TWI419929B - 紫外線硬化型樹脂組成物及光資訊記錄媒體 - Google Patents

紫外線硬化型樹脂組成物及光資訊記錄媒體 Download PDF

Info

Publication number
TWI419929B
TWI419929B TW095125575A TW95125575A TWI419929B TW I419929 B TWI419929 B TW I419929B TW 095125575 A TW095125575 A TW 095125575A TW 95125575 A TW95125575 A TW 95125575A TW I419929 B TWI419929 B TW I419929B
Authority
TW
Taiwan
Prior art keywords
meth
acrylate
ultraviolet curable
information recording
substrate
Prior art date
Application number
TW095125575A
Other languages
English (en)
Other versions
TW200710168A (en
Inventor
Mayumi Aoki
Hirokazu Saito
Original Assignee
Dainippon Ink & Chemicals
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dainippon Ink & Chemicals filed Critical Dainippon Ink & Chemicals
Publication of TW200710168A publication Critical patent/TW200710168A/zh
Application granted granted Critical
Publication of TWI419929B publication Critical patent/TWI419929B/zh

Description

紫外線硬化型樹脂組成物及光資訊記錄媒體
本發明係有關於一種作為光資訊記錄媒體的表面保護層有用的紫外線硬化型樹脂組成物，及具備有由該紫外線硬化型樹脂組成物的硬化膜所構成的表面保護層之光資訊記錄媒體。
光資訊記錄媒體有各種類型。例如有一種光碟，係在形成於基板上的資訊記錄層上，形成用以保護該記錄層之活性能量線硬化型樹脂組成物的硬化膜而成、或是有一種貼合型光碟，係在至少一片光碟用基板上，藉由活性能量線硬化型樹脂組成物的硬化膜貼合形成有資訊記錄層之2片基板而成。
資訊記錄層係由以下所構成之積層體，包含：由在光碟用基板(由聚碳酸酯等合成樹脂所構成)上所形成之稱為坑的凹凸、相變化材料或色料等所構成的層；以及在其上面所形成反射雷射光用以讀取資訊之半透明反射膜或完全反射膜。半透明反射膜及完全反射膜係形成資訊記錄層的最上部之層，通常係由金屬或金屬合金的薄膜所構成的層。
貼合型光碟的代表例有DVD(數位多功能光碟(digital versatile disc)或數位影音光碟(digital video disc))。其中再生專用型DVD存在有各種類型。例如，稱為「DVD－10」之光碟，係在基板的一面設置有對應記錄資訊之稱為坑的凹凸，其上面係作為反射雷射光用以讀取資訊之層，例如具備2片形成有鋁層之光碟用聚碳酸酯基板，將其等以鋁層作為黏著面的方式貼合而成。「DVD－5」係將為了製造「DVD－10」之前述基板、與未設置資訊記錄層之通常的透明的聚碳酸酯基板貼合而成。又，「DVD－9」係使在坑(設置於基板的一面)上面形成有鋁反射膜之基板、與在坑(設置於基板的一面)上形成有由金或金為主成分的合金、銀或銀為主成分的合金、或矽化合物所構成的半透明反射膜之基板，以反射膜間作為黏著面的方式貼合而成。而且，「DVD－18」之結構，係將2片在一面具有2層資訊記錄層之基板貼合而成。目前，記錄容量大、從一面能夠讀取2層資訊的「DVD－9」成為主流。
而且，DVD可大致分為再生專用型及記錄型，記錄型DVD有追記型之稱為DVD－R、DVD＋R的方式、及重寫型之稱為DVD－RW、DVD＋RW、DVD－RAM的方式。此等DVD之中，追記型之稱為DVD－R、DVD＋R的 DVD，與其他DVD不同，其具有的特徵係在記錄層使用有機色料。追記型光碟係在透明基板上，藉由照射雷射光使光學特性產生不可逆性變化、形成凹凸形狀來形成記錄層。該記錄層係使用花青苷系、酞青系、偶氮系有機色料等，藉由例如雷射光照射而加熱分解，其光學常數產生變化之同時、由於體積變化使基板產生變形。
雖然已開發了許多方式，使用連續開發完成的各種記錄方式之光碟，其共同的要求係能夠穩定地讀取記錄於資訊記錄層之信號、能夠極力抑制信號讀取產生錯誤。特別是最近由於黏附在雷射光穿透的聚碳酸酯基板表面之指紋等污染，使雷射光產生散射，記錄於資訊記錄層的信號變為無法讀取，而檢討在聚碳酸酯基板表面上設置容易擦拭污染之保護層。
如此問題的對策，有提案(參照專利文獻1)揭示在硬塗劑中，調配非交聯型氟系界面活性劑。但是，此方法因為氟系界面活性劑只存在保護層表面的一部分，無法達成充分的防止污染功能，希望能夠改善。又，該氟系界面活性劑只是混合而已，經過長期間後或在高溫高濕環境下放置時會有防止污染功能下降的問題。
又，有揭示一種光記錄光碟(參照專利文獻2)作為指紋擦拭性良好的光記錄光碟，在黏附人口指紋液而進行擦拭時之抖動上升率為1.15倍以下。該文獻揭示為了賦與拒水性或滑潤性，在硬塗層中含有活性能量線硬化性之聚矽氧系化合物。但是該揭示之聚矽氧系化合物只有列出通常的聚矽氧系化合物，未記載藉由使用何種化合物能夠以抖動上升率為1.15倍以下的方式來實現光記錄光碟。雖然在實施例有揭示使用在末端具有反應性基之丙烯醯基末端聚二甲基矽氧烷的例子，但是該末端具有反應性基的化合物未能夠充分防止污染、無法得到污染擦拭性，要求進一步改良。又，所列出的聚矽氧化合物多半與形成硬塗層之丙烯酸酯系的聚合性單體未具有相溶性，使用該聚矽氧化合物時，因為在組成物中必須使用溶劑，所以在形成塗膜時會有必須具備除去溶劑的製程之問題。
[專利文獻1]特開平10－110118號公報[專利文獻2]特開2004－335021號公報
本發明欲解決之課題，係提供一種能夠形成表面保護層之紫外線硬化型樹脂組成物，該表面保護層不容易附著指紋等污染，又，即使有污染附著時亦能夠容易地除去、具有優良的防止污染功能、或污染擦拭性。而且，提供一種光資訊記錄媒體，其具備有具有優良的防止污染功能、或污染擦拭性之表面保護層。
本發明之紫外線硬化型組成物，與光硬化性化合物具有適度相溶性，且藉由含有特定結構(具有與光硬化性化合物反應之結構作為側鏈結構)之矽烷化合物，能夠在硬化覆膜表面整體範圍使矽氧烷結構具有高存在機率、堅固地形成固定化的硬化皮膜。藉此，本發明之紫外線硬化型組成物能夠實現優良的防止污染功能、或污染擦拭性，又，即使經過長期間後或在高溫高濕環境下放置時，亦能夠顯現穩定的防污性。
亦即，本發明係提供一種紫外線硬化型樹脂組成物、及使用該紫外線硬化型組成物的硬化膜作為表面保護層之光資訊記錄媒體，該紫外線硬化型樹脂組成物係含有式(1)[化學式1](CH3 )3 Si－o－A－si(CH3 )3 (1)(式中，A係表示式(2) (式中，R1 係表示選自具有藉由醚結合連結(i)碳數1~18之伸烷基及(ii)碳數2~18之複數伸烷基而成的結構之2價基中1種、或是2種以上的基連結而成之2價基，R2 係表示氫原子或甲基)所示n個結構單位、及式(3) 所示m個結構單位以無規則狀或嵌段狀連接而成的結構之基，其中n係1~15之整數，n/m係1/5~1/20，又，式(2)及式(3)所示結構單位，該等的結構單位間、或與分子內其他結構部分未藉由氧-氧結合連結)所示聚矽氧化合物、及與前述聚矽氧化合物反應之光硬化性化合物。
本發明之形成光資訊記錄媒體的表面保護層之紫外線硬化型樹脂組成物，因為含有矽烷化合物其具有能夠與光硬化性化合物反應之反應基之特定結構，顯示優良的防止污染功能。
特別是本發明之光資訊記錄媒體係對設置有表面保護層方向的資訊記錄層進行記錄資訊、或是進行讀取資訊記錄層所記錄的資訊之類型的光資訊記錄媒體時，會產生以下的效果。
光資訊記錄媒體的資訊記錄、或資訊記錄層所記錄的資訊的讀取面側之透明基板的表面有污染黏附時，從透明基板側所照射的雷射光被散射，資訊的記錄或是記錄在資訊記錄層之資訊變為無法讀取。該散射在使用以往的紫外線硬化型樹脂組成物時係顯著的，但是含有具有上述特定結構的聚矽氧化合物作為添加劑之組成物時，表面污染不容易黏附，又，黏附的污染能夠容易地除去，此種因散射造成無法讀取資訊記錄層所記錄資訊之困難不會發生。
以下詳細說明本發明。又，在本說明書，(甲基)丙烯酸係指丙烯酸或甲基丙烯酸，丙烯酸或甲基丙烯酸之衍生物亦相同。
[紫外線硬化型樹脂組成物]
本發明之紫外線硬化型樹脂組成物係含有上述的特定結構之聚矽氧化合物、及與該聚矽氧化合物具有反應性之光硬化性化合物作為必要成分。藉此，所得到的硬化膜在保持良好的光穿透性之同時，在膜整體範圍具有聚矽氧化合物所持有之優良的防污效果及黏附污染的擦拭性。
(聚矽氧化合物)
在本發明之紫外線硬化型樹脂組成物所使用之上述 (1)所示聚矽氧化合物，其側鏈結構以特別比例具有：與光硬化性化合物具有適度相溶性之部位；以及與光硬化性化合物反應之部位。將含有該聚矽氧化合物之紫外線硬化型組成物塗布成膜狀時，可認為在其塗膜表面附近之容易產生相分離之主鏈的矽氧烷結合部位，藉由欲與光硬化性化合物進行相分離的力量產生作用、及具有相溶性之側鏈部位欲與光硬化性化合物進行相溶之力量產生作用，使在表層附近之矽氧烷結構部位的存在機率變高。對該塗膜照射紫外線，光硬化性化合物硬化時，聚矽氧化合物之側鏈的反應基亦產生反應，使矽氧烷結構變成高機率存在於硬化膜的表層。此時，因為相對於一個聚矽氧化合物，複數側鏈部位變為固定錨(anchor)，聚矽氧化合物被堅強地固定於硬化膜。藉此本發明之紫外線硬化型樹脂組成物能夠形成具有優良的防污性、或污染擦拭性之硬化膜，又，該硬化膜即使經過長期間後或在高溫高濕環境下放置時，亦能夠顯現穩定的防污性。相對地未具有如本發明的結構之聚矽氧化合物，因為無法得到複數固定錨效果，會有固定化不充分之情形、或是未具有相溶性不同的部位，無法在表層附近產生高存在機率情形，會成為防污性、或污染擦拭性差之物。
前述式(1)中之A，具有由前述式(2)所示n個結構單位、與前述式(3)所示m個結構單位，以無規則狀或嵌段狀連接而成的結構之基。無規則狀係意指式(2)所示結構單位與式(3)所示結構單位，以順序不同、不規則順序的方式結合而成之結構，嵌段狀係意指式(2)所示結構單位之連續結合而成的部分與式(3)所示結構單位之連續結合而成的部分以交替方式顯現之結構。又，前述n係1~15的整數，以1~10的整數為佳。又，n對m的比(n/m)為1/5~1/20，以1/5~1/15為佳。又，式(2)及式(3)所示結構單位，在此等結構單位間、又與分子內的其他結構部分無藉由氧－氧結合之連結。
前述式(2)中之R1 係選自下述(i)或(ii)所記載的基、或下述(i)或(ii)所記載的基中2種以上的基連結而成的結構之基。
(i)碳數1~18的伸烷基有例如－CH2 －、－CH2 CH2 CH2 －、－CH2 CH(CH3 )－、－CH2 (CH2 )4 CH2 －、－CH2 CH(CH2 CH3 )CH2 CH2 CH2 CH2 －、－CH2 (CH2 )1 0 CH2 －、－CH2 (CH2 )1 6 CH2 －等。
(ii)係碳數2~18之複數伸烷基藉由醚結合連結而成之具有聚氧伸烷基結構之2價基。
(ii)的基以式表示時為－(OR)P －(式中，R係亦可具有分支鏈之碳數2~18的伸烷基、P係1以上的整數)。例如有－(OCH2 CH2 )P －、－(OC3 H6 )P －、－(OCH2 CH2 CH2 CH2 )P －、－(OCH2 (CH2 )1 0 CH2 )P －等。又，具有分子鏈不同長度之－OR－以無規則的方式連接而成的結構之基，例如可以是－OCH2 CH2 －與－OCH2 CH(CH3 )－以無規則的方式結合而成的基。又，R1 係使用(ii)所示的基時，以使用具有複數醚結合之聚醚結構(聚氧伸烷基結構)的基為佳。(ii)所記載的基可從環氧乙烷、環氧丙烷、環氧丁烷等環氧烷、四氫呋喃、烷基取代四氫呋喃等環狀醚的聚合物或此等之2種以上的共聚物得到。
上述之中，R1 以選自碳數1~6的伸烷基、-(OR)t -(式中R係表示伸乙基或伸丙基，t係表示2~20的整數)所示2價基、及環氧乙烷與環氧丙烷以無規則的方式開環加成聚合而成的2價基中1種的基、或是選自此等之2種以上的基連結而成的基為佳。此等之中，以-CH2 CH2 CH2 -、-CH2 CH2 CH2 (OCH2 CH2 )P -(式中，p係2以上的整數)、-CH2 CH2 CH2 Y-(式中，Y係-OC2 H4 -與-OC3 H6 -以無規則的方式結合而成的基)為特佳。(ii)所記載之基與Si間的結合，亦可使氧原子介於中間，其中以使伸氧基介於中間結合而成的結構為佳。又，R1 中的(i)的基之一端，亦可與Si直接結合，亦可使氧原子介於中間而結合，其中以與Si直接結合為佳。又，前述式(2)中的R2 係表示氫原子或甲基，其中以氫原子為佳。
式(1)所示的聚矽氧化合物可以市售品的方式取得，可例示的有例如Degussa公司製的TEGO Rad 2200N。
又，式(1)所示的聚矽氧化合物，數量平均分子量以2000~12000為佳，以3000~8000為更佳。
在紫外線硬化型樹脂組成物所含有式(1)所示聚矽氧化合物的含量，相對於紫外線硬化型樹脂組成物為0.05~5質量份，以0.1~2.0質量份為佳。在上述範圍時，本發明之光資訊記錄媒體的表面保護層，其表面污染不容易黏附，又，黏附的污染能夠容易地擦拭除去，能夠長期間穩 定地賦與優良的防止污染功能。
(光硬化性化合物)
本發明所使用之光硬化性化合物，若與前述聚矽氧化合物具有反應性、藉由紫外線照射可以硬化的成分時，可使用不飽和聚酯型、丙烯酸型、硫醇-烯型、環氧型等各種光硬化性化合物，使用作為光資訊記錄媒體之表面保護層用時，可考慮硬度或彈性模數、與黏著基板之黏著性、塗布時之黏度等而適當地選擇。
其中，作為光資訊記錄媒體用途，以使用透明且耐候性良好之丙烯酸型的光硬化性化合物為佳。此種丙烯酸型的光硬化性化合物，可使用例如下述的聚合性單體及聚合性寡聚物。
單官能(甲基)丙烯酸酯可舉出的例子有(甲基)丙烯酸乙酯、(甲基)丙烯酸丁酯、(甲基)丙烯酸2-乙基己酯、(甲基)丙烯酸壬酯、(甲基)丙烯酸十三酯、(甲基)丙烯酸十六酯、(甲基)丙烯酸十八酯、(甲基)丙烯酸異戊酯、(甲基)丙烯酸異癸酯、(甲基)丙烯酸異硬脂酸酯、(甲基)丙烯酸異2-羥基乙酯、(甲基)丙烯酸3-氯-2-羥基丙酯、(甲基)丙烯酸甲氧基乙酯、(甲基)丙烯酸丁氧基乙酯、(甲基)丙烯酸苄酯、(甲基)丙烯酸壬基苯氧基乙酯、(甲基)丙烯酸四氫糠酯、(甲基)丙烯酸環氧丙酯、(甲基)丙烯酸2-羥基-3-苯氧基丙酯、(甲基)丙烯酸壬基苯氧基乙基四氫糠酯、(甲基)丙烯酸己內酯改性四氫糠酯、丙烯醯基啉、(甲基)丙烯酸苯氧基乙酯等。又，脂環族單體亦可使用(甲基)丙烯酸異莰酯、(甲基)丙烯酸降烷酯、(甲基)丙烯酸2－(甲基)丙烯醯氧基甲基－2－甲基雙環庚烷金剛烷酯、(甲基)丙烯酸二環戊烯酯、(甲基)丙烯酸二環戊酯、(甲基)丙烯酸二環戊烯氧基乙酯、(甲基)丙烯酸四環十二酯、(甲基)丙烯酸環己酯等。
2官能(甲基)丙烯酸酯可舉出的例子有1,4－丁二醇二(甲基)丙烯酸酯、3－甲基－1,5－新戊二醇二(甲基)丙烯酸酯、1,6－己二醇二(甲基)丙烯酸酯、新戊二醇二(甲基)丙烯酸酯、2－甲基－1,8－辛二醇二(甲基)丙烯酸酯、2－丁基－2－乙基－1,3－丙二醇二(甲基)丙烯酸酯、乙二醇二(甲基)丙烯酸酯、聚丙二醇二(甲基)丙烯酸酯、在1莫耳新戊二醇中添加4莫耳以上的環氧乙烷或環氧丙烷而得到的二醇之二(甲基)丙烯酸酯、環氧乙烷改性磷酸(甲基)丙烯酸酯、環氧乙烷改性烷基化磷酸(甲基)丙烯酸酯、二乙二醇二(甲基)丙烯酸酯、二丙二醇二(甲基)丙烯酸酯、三丙二醇二(甲基)丙烯酸酯、聚醚(甲基)丙烯酸酯、(甲基)丙烯酸二乙基胺基乙酯、N－乙烯基吡咯啶酮、N－乙烯基己內醯胺、乙烯基醚單體等。又，脂環族2官能(甲基)丙烯酸酯亦可使用降烷二甲醇二(甲基)丙烯酸酯、降烷二乙醇二(甲基)丙烯酸酯、在降烷二甲醇添加2莫耳環氧乙烷或環氧丙烷而得到的二醇之二(甲基)丙烯酸酯、三環癸烷二甲醇二(甲基)丙烯酸酯、三環癸烷二乙醇二(甲基)丙烯酸酯、在三環癸烷二甲醇中添加2莫耳環氧乙烷或環氧丙烷而得到的二醇之二(甲基)丙烯酸酯、五環十五烷二甲醇二(甲基)丙烯酸酯、五環十五烷二乙醇二(甲基)丙烯酸酯、在五環十五烷二甲醇中添加2莫耳環氧乙烷或環氧丙烷而得到的二醇之二(甲基)丙烯酸酯、在五環十五烷二乙醇中添加2莫耳環氧乙烷或環氧丙烷而得到的二醇之二(甲基)丙烯酸酯、二羥甲基二環戊烷二(甲基)丙烯酸酯等。
為了調整塗布時之黏度、或調整交聯密度，此等單官能及2官能(甲基)丙烯酸酯可適當地使用，(甲基)丙烯酸四氫糠酯、1,6－己二醇二(甲基)丙烯酸酯、新戊二醇二(甲基)丙烯酸酯、(甲基)丙烯酸己內醯胺改性四氫糠酯、丙烯醯啉、(甲基)丙烯酸異莰酯、乙二醇二(甲基)丙烯酸酯、聚丙二醇二(甲基)丙烯酸酯、在1莫耳新戊二醇中添加4莫耳以上環氧乙烷或環氧丙烷而得到的二醇之二(甲基)丙烯酸酯、二乙二醇二(甲基)丙烯酸酯、二丙二醇二(甲基)丙烯酸酯、三丙二醇二(甲基)丙烯酸酯、聚醚二(甲基)丙烯酸酯在使用聚碳酸酯作為層積基板時，因為能夠賦與良好的黏著性，乃是較佳，以使用(甲基)丙烯酸四氫糖酯、1,6－己二醇二(甲基)丙烯酸酯、新戊二醇二(甲基)丙烯酸酯為特佳。
又，具有脂環族結構之物，由於具有剛直的環結構，能夠賦與所得到的硬化物在高溫具有高彈性模數及高玻璃轉移溫度。
3官能以上的(甲基)丙烯酸酯可使用例如三聚異氰酸雙(2－丙烯醯氧基乙基)羥基乙酯、三聚異氰酸雙(2－丙烯醯氧基丙基)羥基丙酯、三聚異氰酸雙(2－丙烯醯氧基丁基)羥基丁酯、三聚異氰酸雙(2－甲基丙烯醯氧基乙基)羥基乙酯、三聚異氰酸雙(2－甲基丙烯醯氧基丙基)羥基丙酯、三聚異氰酸雙(2－甲基丙烯醯氧基丁基)羥基乙酯、三聚異氰酸參(2－丙烯醯氧基乙酯)、三聚異氰酸參(2－丙烯醯氧基丙酯)、三聚異氰酸參(2－丙烯醯氧基丁酯)、三聚異氰酸參(2－甲基丙烯醯氧基乙酯)、三聚異氰酸參(2－甲基丙烯醯氧基丙酯)、三聚異氰酸參(2－甲基丙烯醯氧基丁酯)、三羥甲基丙烷三(甲基)丙烯酸酯、新戊四醇三(甲基)丙烯酸酯、新戊四醇四(甲基)丙烯酸酯、二新戊四醇五(甲基)丙烯酸酯、在1莫耳二新戊四醇六(甲基)丙烯酸酯三羥基丙烷中添加3莫耳以上環氧乙烷或環氧丙烷而得到的三醇之二或三(甲基)丙烯酸酯、二新戊四醇之聚(甲基)丙烯酸酯等多官能(甲基)丙烯酸酯等。
該等3官能以上的(甲基)丙烯酸酯能夠賦與硬化物高彈性模數。其中三聚異氰酸三(2－丙烯醯氧基乙酯)、三聚異氰酸三(2－甲基丙烯醯氧基乙基)、三羥甲基丙烷三(甲基)丙烯酸酯、新戊四醇三(甲基)丙烯酸酯、新戊四醇四(甲基)丙烯酸酯、二新戊四醇五(甲基)丙烯酸酯、二新戊四醇六(甲基)丙烯酸酯，因為夠賦與硬化物特別高的彈性模數，乃是特別適合使用。
又，除了上述(甲基)丙烯酸酯以外，亦可含有具有剛直結構之環氧(甲基)丙烯酸酯。環氧(甲基)丙烯酸酯可舉出的有雙酚A與表氯醇的反應物與(甲基)丙烯酸反應、合成得到的雙酚A型環氧(甲基)丙烯酸酯、雙酚S與表氯醇的反應物與(甲基)丙烯酸反應、合成得到的雙酚S型環氧(甲基)丙烯酸酯、雙酚F與表氯醇的反應物與(甲基)丙烯酸反應、合成得到的雙酚F型環氧(甲基)丙烯酸酯、甲階酚醛樹脂與表氯醇的反應物與(甲基)丙烯酸反應、合成得到的甲階酚醛樹脂型環氧(甲基)丙烯酸酯。此等雙酚型環氧(甲基)丙烯酸酯能夠賦與硬化物高彈性模數。其中以使用雙酚A型環氧(甲基)丙烯酸酯為佳。
而且，聚合性低聚物亦可適合使用，亦可並用聚酯(甲基)丙烯酸酯、聚醚(甲基)丙烯酸酯、聚胺基甲酸酯(甲基)丙烯酸酯等。
本發明之紫外線硬化型組成物亦可含有雙酚型的環氧丙烯酸酯，而且藉由並用3官能(甲基)丙烯酸酯、1官能及/或2官能(甲基)丙烯酸酯，能夠調整硬度、彈性模數、與黏著基板之黏著性、塗布時之黏度等。各自的含量可按照所必要的特別而適當地調整，在紫外線硬化型組成物中，以含有1~30質量%為佳，以含有5~15質量%為更佳。藉由在該範圍含有環氧(甲基)丙烯酸酯，能夠賦與所得到硬化物高硬度之同時，能夠適當地調整塗布時的黏度。又，3官能(甲基)丙烯酸酯的含量，以30~80質量%為佳，以40~70質量%為更佳。而且，1官能及/或2官能(甲基)丙烯酸酯的含量，以5~50質量%為佳，以10~40質量%為更佳。藉由將1~3官能的(甲基)丙烯酸酯之比率調整在上述範圍，能將使塗布時的黏度、硬化後的交聯密度在適當範圍，能夠賦與硬化物高硬度之同時，能夠降低硬化物的翹曲。
(聚合引發劑)
本發明之紫外線硬化型樹脂組成物可按照必要使用光聚合引發劑。光聚合引發劑可以使用任一種眾所周知常用之物，本發明所使用的光聚合引發劑以分子裂開或脫氫型之物為佳。
光聚合引發劑例如可使用苯偶姻異丁基醚、2,4－二乙基噻噸、2－異丙基噻噸、苯偶醯、1－羥基環己基苯基酮、苯偶姻乙基醚、苄基二甲基縮酮、2－羥基－2－甲基－1－苯基丙烷－1－酮、1－(4－異丙基苯基)－2－羥基－2－甲基丙烷－1－酮及2－甲基－1－(4－甲基苯硫基)－2－啉丙烷－1－酮等的分子裂開型、或二苯基酮、4－苯基二苯基酮、間苯二酚、4－苯偶姻－4’－甲基－二苯基硫醚等脫氫型光聚合引發劑。
該光聚合引發劑以不會吸收在對應用的光資訊記錄媒體進行讀取或寫入時之光波長為佳，例如應用於藍光雷射光碟時，以使用在400奈米附近光吸收少之物為佳。
(添加劑)
又，在紫外線硬化型樹脂組成物中添加之任意成分有以下之物，可在不損害本發明之效果的範圍內使用。例如對光聚合引發劑之敏化劑有三甲胺、甲基二甲醇胺、三乙醇胺、對二甲基胺苯乙酮、對二甲基胺苯甲酸乙酯、對二甲胺苯甲酸異戊酯、N,N－二甲基苄胺、及4,4’－雙(二乙胺)二苯基酮等，而且可並用不會與前光聚合性化合物產生附加反應之胺類。當然，此等以選用在紫外線硬化型組成物中之可溶性優良、且不會阻礙紫外線穿透性之物為佳。
又，為了提升硬化物的硬度，亦可含有二氧化矽粒子等無機成分，亦可不使用分散無機粒子之溶劑，又，為了不發生因使用無機粒子所造成的散射等問題，以不含無機粒子為佳。
(黏度)
本發明之紫外線硬化型組成物從製程上之較大優點而言，以製成可藉由塗布形成膜之黏度、特別是能夠藉由旋轉塗布適當地形成膜為佳。該黏度按照膜厚度而適當地調整即可，其中形成光資訊記錄媒體之薄的表面保護層時，以在20~150mPa．s的範圍為佳。
[光資訊記錄媒體]
本發明之光資訊記錄媒體，係在至少一表面上設置有表面保護層之光資訊記錄媒體，其中表面保護層具有由上述紫外線硬化型組成物的硬化膜所構成的層之物。
(表面保護層)
因為本發明之光資訊記錄媒體在表面所具有的保護層，係由上述紫外線硬化型組成物的硬化膜所構成，光可以良好地穿透之同時，具有優良的防污性、或污染擦拭性，又，長期間經過後、即使在高溫高濕環境下放置時亦能夠顯現穩定的防污性。因此，本發明之光資訊記錄媒體在光資訊記錄媒體表面不容易產生光散射。能夠藉由光進行良好的資訊讀取及寫入。
又，為了降低傷害，表面保護層以具有高硬度為佳，表面鉛筆硬度以2H以上為佳，以4H以上為更佳。依據本發明之紫外線硬化型組成物，因為在硬化膜表面附近，能夠提高聚矽氧化合物的存在密度，容易形成滑性良好、且高硬度的覆蓋。
表面保護層的彈性模數在25℃之彈性模數以1000~3000MPa的範圍為佳，以在1500~2500MPa的範圍為更佳。彈性模數在上述範圍係因為彈性模數低時膜變軟，相反地，彈性模數高時膜變脆，乃是不佳。
(層結構)
本發明之光資訊記錄媒體若其結構係最表層之至少一面具有上述表面保護層時，沒有特別限制，可以是(i)其結構係在基板上層積至少一層光反射層、且在前述基板之層積有光反射層的面之相反側的面具有表面保護層，或(ii)其結構係在基板上層積至少一層光反射層、且在與前述基板相對之最表面具有表面保護層等結構中任一種。
上述(i)的結構之例子，可舉出的有在光入射最表層設置有表面保護層之DVD-R或DVD-ROM，上述(ii)的結構之例子有在光入射最表層設置有表面保護層之藍光雷射光碟等。此等光資訊記錄媒體可以是在基板或中間層形成有坑之再生專用光資訊記錄媒體，亦可以是具有相變化型的資訊記錄層之能夠記錄‧再生之光資訊記錄媒體，特別是再生專用的資訊記錄層，具有特別優良的效果。
以下記載製造本發明較佳態樣之「DVD-5」、「DVD-10」、「DVD-9」、「DVD-18」、及「藍光雷射光碟」時之例子，但是本發明之光資訊記錄媒體的例子不限定於此等。
[DVD－9的製造]
準備1片光碟用基板(A)，其係在擔任記錄資訊之稱為坑的凹凸上層積有40~60奈米的金屬薄膜(反射層)而成，及準備1片光碟用基板(B)，其係在擔任記錄資訊之稱為坑的凹凸上層積有10~30奈米的銀或以銀為主成分的合金之半透明膜(半透明反射層)而成，又，前述反射層可使用例如以鋁為主成分之物或以銀或銀為主成分的合金。又，前述光碟用基板可以使用眾所周知之光碟用基板。可舉出的有例如非晶聚烯烴、聚甲基丙烯酸甲酯、聚碳酸酯等，其中以使用聚碳酸酯為特佳。
接著，將紫外線硬化型組成物塗布在前述基板(A)的金屬薄膜上，進而將層積有半透明膜之前述基板(B)以半透明膜的膜面為黏著面之方式、使塗布在金屬薄膜面之紫外線硬化型組成物介於中間而與基板(A)貼合，從該已貼合的2片基板的一面或兩面照射紫外線，使兩者黏著而作為「DVD－9」。進而在穿透雷射光的透明基板表面以膜厚度2~5微米的方式形成表面保護層(由含有式(1)所示化合物之紫外線硬化型組成物的硬化膜所構成)，而得到本發明之光碟。
又，亦可使用形成有溝的基板，作為能夠記錄、再生的光碟(層積有資訊記錄層及光反射層)。資訊記錄層若是能夠記錄、再生資訊即可，可以是相變化型記錄層、光磁記錄層、或是有機色料型記錄層中任一種。
資訊記錄層係相變化型記錄層時，該資訊記錄層通常係由介電體層及相變化膜所構成。介電體層被要求具有緩衝相變化層所產生的熱之功能、及調整光碟的反射係數之功能，可使用ZnS與SiO2 的混合組成。相變化膜係藉由膜的相變化而產生非晶狀態與結晶狀態之反射係數差，可使用Ge－Sb－Te系、Sb－Te系、Ag－In－Sb－Te系合金。
有機色料型記錄層所使用的有機色料，除了偶氮系色料以外，若能夠藉由記錄時所使用的雷射光形成坑時即可使用而沒有特別限制，可舉出的有例如花青苷系、酞青系、萘酞青系、蒽醌系、三苯甲烷系、吡喃鎓或噻吡喃鎓鹽系、斯奈鎓(squarilium)系、克酮鎓(croconium)、甲系、金屬錯合物色料系等。又，亦可在色料混合單態氧淬熄劑而使用。淬熄劑以乙醯丙酮鹽系、雙(二硫代)－α－二酮系或雙苯基二硫醇系等雙(二硫醇)系、硫代兒茶酚系、柳醛肟系、硫代雙酚鹽系等金屬錯合物為佳。又，具有氮的自由基陽離子之胺系化合物或受阻酚等胺系淬熄劑亦佳。在各自資訊記錄層所使用的材料可相同亦可不同。
(DVD－18的製造)
進而在製得前述之DVD－9後，使形成於基板(A)上之金屬薄膜(反射層)殘留在基板(B)側的狀態下，藉由只將基板(A)剝離，來製得依照順序層積有基板(B)/半透明膜(半透明反射層)/紫外線硬化型組成物的硬化膜/金屬薄膜(反射層)之光碟中間體。準備2片如此的光碟中間體。接著。接著，使該2片光碟中間體的金屬薄膜(反射層)作為黏著面，藉由使其等以相向的方式黏著，可得到「DVD－18」。同樣地，藉由以膜厚度2~5微米的方式形成表面保護層(由含有式(1)所示化合物之紫外線硬化型組成物的硬化膜所構成)，而得到本發明之光碟。
(DVD－10的製造)
準備2片光碟用基板(C1)及(C2)，係在擔任記錄資訊之稱為坑的凹凸上層積有40~60奈米的銀或以銀為主成分的合金之薄膜而成。在其中一片基板(C1)的前述薄膜上塗布紫外線硬化型組成物，將另外一片基板(C2)以前述薄膜上的膜面為黏著面的方式，使塗布在基板(C1)的薄膜面之本發明的紫外線硬化型組成物介於中間，與基板(C1)貼合，從該已貼合的2片基板的一面或兩面照射紫外線，使兩者黏著而作為「DVD－10」。同樣地進行，以膜厚度2~5微米的方式形成由含有式(1)所示化合物之紫外線硬化型組成物的硬化膜所構成之表面保護層，而得到本發明之光碟。
(DVD－5的製造)
準備光碟用基板(D)，係在擔任記錄資訊之稱為坑的凹凸上層積有40~60奈米的銀或以銀為主成分的合金之薄膜而成。另外準備未具有坑之光碟用基板(E)。在基板(D)的前述薄膜上塗布紫外線硬化型組成物，使該組成物介於中間貼合基板(D)與基板(E)，從該已貼合的2片基板的一面或兩面照射紫外線，使兩者黏著而作為「DVD－5」。同樣地進行，以膜厚度2~5微米的方式形成由含有式(1)所示化合物之紫外線硬化型組成物的硬化膜所構成之表面保護層，而得到本發明之光碟。
進行照射紫外線時，可藉由使用高壓水銀燈等之連續光照射方式進行，亦可使用USP5904795所記載之閃光照射方式進行。就能夠效率良好地硬化而言，以使用閃光照射為較佳。
在此，照射紫外線之手段可以藉由例如使用高壓水銀燈、鹵化金屬燈等連續照射的方式之紫外線照射裝置或氙氣閃光等閃光照射的方式進行。
(藍光雷射光碟的製造)
再生專用的藍光雷射光碟時可藉由以下步驟來形成，使在擔任記錄資訊之稱為坑的凹凸上層積有40~60奈米的銀或以銀為主成分的合金之薄膜而成、厚度為1.1毫米左右的光碟基板(F)，藉由紫外線硬化型組成物與聚碳酸酯等的薄片(G)貼合，從該已貼合的2片基板的一面或兩面照射紫外線，使兩者黏著後，以膜厚度2~5微米的方式形成由含有式(1)所示化合物之紫外線硬化型組成物的硬化膜所構成之表面保護層，而得到本發明之光碟。又，亦可使用紫外線硬化型組成物的硬化膜形成上述薄片(G)部分，在其表面形成由含有式(1)所示化合物之紫外線硬化型組成物的硬化膜所構成之表面保護層。又，即使形成有2層以上的記錄層之多層結構，亦可使用形成有溝之基板來製造形成有相變化型的資訊記錄層及光反射層之光碟。
[實施例]
接著，舉出實施例來更詳細地說明本發明，但是本發明未限定於此等實施例。以下實施例中的「份」係表示「質量份」
(實施例1~2及比較例1~3) <光碟試樣的製造>
在厚度1.2毫米、直徑120毫米之光碟用聚碳酸酯基板上，以硬化後的保護層硬化膜的厚度為5~8微米的方式塗布實施例及比較例的各組成物，使用120W/cm之聚光型高壓水銀燈(EYE GRAPHICS(股)製H03-L31)，照射光量0.5J/cm2 (同公司的累積光量計UVPF-36)的紫外線作為硬化膜，調製評價用之各光碟試樣。
<人工指紋液的調製>
對10份稀釋劑甲氧基丙醇，添加1份三油酸甘油酯，更而添加0.4份關東土壤(依據JIS Z8901規定之試驗用粉體1第11種)、攪拌，製成人工指紋液。
<模擬指紋圖案轉印用原版>
邊攪拌人工指紋液邊採取約1毫升，藉由旋轉塗布法塗布於聚碳酸酯製基板(直徑120毫米、厚度1.2毫米)上。在60℃加熱該基板3分鐘，除去甲氧基丙醇，得到模擬指紋圖案轉印用原版。
<模擬指紋圖案轉印及擦拭>
使用將No.7的聚矽氧橡膠塞之較小一側的端面(直徑20毫米)使用研磨紙(日本研紙製CC 150-Cw)研磨成一致後之物作為模擬指紋圖案轉印材。將為模擬指紋圖案轉印材 以負荷52N壓觸上述原版10秒，使人工指紋液成分移動至轉印材的前述端面。從形成有紫外線硬化型樹脂組成物之光碟表面的中心至半徑方向37毫米附近，使用負荷52N壓觸黏附有人工指紋液成分之轉印材的前述端面10秒，來使人工指紋液成分轉印。
接著將黏附在各光碟試樣表面之人工指紋液成分，按照以下順序擦拭。將8張重疊之市售面紙(tissue paper)(CORELEX(股)製)，夾在No.7的聚矽氧橡膠塞之較大一側的端面(直徑25毫米)與黏附有人工指紋液成分之光碟表面之間，以5N的力量加壓。在該狀態下，從面紙中央至外周的範圍慢慢地移動橡膠塞，來擦掉黏附的人工指紋液成分。
<PI錯誤之測定>
對各光碟試樣，在黏附人工指紋液前(初期)、及擦試操作2次後之各自時點，測定記錄後之PI錯誤。所得到的結果如表1所示。
PI錯誤係藉由Audio Development公司製「SA-300」來測定。又，藉由計算求得PI錯誤比(試驗後的錯誤數/試驗前的錯誤數)，來進行評價。
PI錯誤比的判定欄係
PI錯誤比小於2時為◎
PI錯誤比為2以上、小於5時為○
PI錯誤比為5以上、小於6時為△
PI錯誤比大於6時為×。
<在高溫高濕環境下之耐久性試驗>
對與實施例1、比較例2及比較例4同樣地製成的光碟試樣，使用ESPEC(股)公司製PR-2PK，在80℃ 85%RH之高溫高濕環境下進行曝光試驗240小時後，測定在黏附人工指紋液前(初期)、及擦試操作2次後之各自時點，測定記錄後之PI錯誤。所得到的結果如表2所示。
表1中的略號係表示以下化合物。
‧PETA：新戊四醇四丙烯酸酯
‧NPGDA：新戊二醇二丙烯酸酯
‧TMPTA：三羥甲基丙烷三丙烯酸酯
‧HCPK：1-羥基環己基苯基酮
‧TEGO Rad 2200N：反應性聚矽氧烷、DEGUSSA製、＊ 在式(1)，n為3、n/m為1/10、R1 係－CH2 CH2 CH2 X1 (式中，X1 係表示平均20個－OC2 H4 －與平均6個－OC3 H6 －係無規則性結合而成的基。又，X1 係與式(1)中丙烯醯基結合。)、R2 係氫原子之化合物，數量平均分子量4000之化合物。．L－7002：聚氧伸烷基．二甲基聚矽氧烷，NIPPON UNICAR製．BY－16－152D：下式(4)所示甲基丙烯酸酯改性矽油、TORAY－DOWCORNING製Y1 －(CH2 )3 －SiO(CH3 )n－Si(CH3 )2 －(CH2 )3 －Y1 (4)Y1 係表示甲基丙烯醯氧基。質量平均分子量386．BY－16－152：上述式(4)所示甲基丙烯酸酯改性矽油，TORAY－DOWCORNING公司製，質量平均分子量5600
從上述表1可以清楚知道，使用本發明之實施例1~2所得到之由紫外線硬化型樹脂組成物所構成的硬化膜作為保護層之光碟，若除去黏附在雷射光穿透的光碟表面之人工指紋液時，顯示與初期同等的PI-錯誤。又，如表2可以清楚知道，即使在高溫高濕環境下的曝露試驗後，錯誤的增加亦極少。
另一方面，比較例1~4的光碟，在光碟表面黏附人工指紋液時，因為光碟保護層的防止污染功能、污染的擦拭性不充分，得知PI-錯誤大幅度上升。又，在比較例5，聚矽氧化合物與光硬化性化合物不相溶。
[產業上之利用可能性]
本發明之紫外線硬化型樹脂組成物，因為含有特定結構的聚矽氧化合物，使用作用光資訊記錄媒體的表面保護層時，能夠發揮優良的防止污染功能及污染擦拭性。藉此，使用本發明的紫外線硬化型樹脂組成物之光資訊記錄媒體，不會有因為從透明基板側所照射的雷射光產生散射，致使記錄資訊、或讀取記錄於資訊記錄層之資訊變為困難之情形。因此，本發明之光資訊記錄媒體即使長期間經過後、或在高溫高濕環境下放置時，亦能夠穩定地顯現防污性，在產業上係極為有用的。

Claims (6)

  1. 一種紫外線硬化型樹脂組成物，其特徵係含有式(1)(CH3 )3 Si-O-A-Si(CH3 )3 (1)(式中，A係表示式(2) (式中，R1 係表示選自具有藉由醚鍵結連結(i)碳數1~18之伸烷基及(ii)碳數2~18之複數伸烷基而成的結構之2價基中1種、或是2種以上的基連結而成之2價基，R1 可直接與Si鍵結、亦可使氧原子介於中間而鍵結，R2 係表示氫原子或甲基)所示n個結構單位、及式(3) 所示m個結構單位係以無規則狀或嵌段狀連接而成的結構之基，其中n係1~15之整數，n/m係1/5~1/20，又，式(2)及式(3)所示結構單位係該等的結構單位間、或與分子內其他結構部分未藉由氧-氧鍵結連結)所示聚矽氧化合物、及與該聚矽氧化合物反應之光硬化性化合物，該光硬化性化合物含有30~80質量%的3官能(甲基)丙烯酸酯，該3官能(甲基)丙烯酸酯為三羥甲基丙烷三(甲基)丙烯酸酯， 該紫外線硬化型樹脂組成物含有0.05~5質量%的該聚矽氧化合物。
  2. 如申請專利範圍第1項之紫外線硬化型樹脂組成物，其中該聚矽氧化合物之數量平均分子量為200~12000。
  3. 如申請專利範圍第1項之紫外線硬化型樹脂組成物，其中該紫外線硬化型樹脂組成物的硬化膜的表面鉛筆硬度為2H以上。
  4. 一種光資訊記錄媒體，其特徵係在至少一表面上設置有表面保護層之光資訊記錄媒體，其中該表面保護層具有由如申請專利範圍第1至3項中任一項之紫外線硬化型樹脂組成物的硬化膜所構成的層。
  5. 如申請專利範圍第4項之光資訊記錄媒體，其中在基板上層積至少一層光反射層，且在該基板之層積有光反射層的面之相反側的面具有表面保護層。
  6. 如申請專利範圍第4項之光資訊記錄媒體，其中在基板上層積至少一層光反射層、且在與該基板相對之最表面具有表面保護層。
TW095125575A 2005-07-15 2006-07-13 紫外線硬化型樹脂組成物及光資訊記錄媒體 TWI419929B (zh)