TW202146285A - 纖維素聚合物的包裝方法和運輸方法以及纖維素聚合物的包裝物 - Google Patents
纖維素聚合物的包裝方法和運輸方法以及纖維素聚合物的包裝物 Download PDFInfo
- Publication number
- TW202146285A TW202146285A TW110113961A TW110113961A TW202146285A TW 202146285 A TW202146285 A TW 202146285A TW 110113961 A TW110113961 A TW 110113961A TW 110113961 A TW110113961 A TW 110113961A TW 202146285 A TW202146285 A TW 202146285A
- Authority
- TW
- Taiwan
- Prior art keywords
- packaging bag
- cellulose polymer
- packaging
- cellulose
- less
- Prior art date
Abstract
本發明之課題係提供一種適合纖維素聚合物之運輸等的包裝方法，進一步的課題係提供抑制纖維素聚合物之黏度降低並且適合運輸的包裝方法。
本發明係以滿足下述條件（1）、（2）及（3）的方式包裝纖維素聚合物。
條件（1）：在具有氣體屏障性的前述包裝袋內填充纖維素聚合物。
條件（2）：將前述包裝袋內的氧濃度調整為0.8%以下並進行密封。
條件（3）：填充有纖維素聚合物的前述包裝袋設置成以最長的長邊L成為水平時，從水平設置面起算的包裝袋之深度D與長邊L滿足關係式：6.1≦L/D≦10。
又，前述包裝袋的最外層表面的靜摩擦係數滿足0.2～0.5且動摩擦係數滿足0.15～0.35的範圍較為合適。
Description
本發明係關於纖維素聚合物的包裝方法及其應用。
由羥乙基纖維素、羧基甲基纖維素、羥基甲基纖維素、羥基丙基纖維素等纖維素而來的聚合物因為其高度的安全性而被應用於醫療、食品等各種領域。例如，羧基甲基纖維素被用於冰淇淋等食品的增黏劑及乳化穩定劑，並且亦被使用於牙膏、瀉藥、瘦身錠、水性印墨、界面活性劑、紙類產品等非食品產品。
以往纖維素聚合物一般係以粉末狀態保管。然而相較於保管前的纖維素聚合物之溶液的黏度，長期保管後的纖維素聚合物之溶液的黏度大幅降低，而具有無法發揮作為黏度調整劑之功能這樣的問題。
因此專利文獻1中提出了藉由使包裝袋內的氧濃度保持在固定值以下來抑制因氧化等導致黏度降低的保管方法。
［先前技術文獻］
［專利文獻］
［專利文獻1］日本特開2012-121957號公報
［發明所欲解決之課題］
然而專利文獻1中，為了最大限度減少黏度降低，而提出了進行氮氣取代以盡量降低包裝袋內之殘氧濃度的方法，若如此最大限度地進行包裝袋內的氮氣取代，包裝袋會因為內壓等而膨脹，而具有難以捆包或是在運輸時難以將包裝袋彼此堆疊這樣的問題。
鑒於以上的狀況，欲解決的一個課題係提供一種適合纖維素聚合物之運輸等的包裝方法。
又，欲解決的另一課題係提供一種抑制纖維素聚合物的黏度降低並且更適合運輸等的包裝方法。
［解決課題之手段］
本揭示中所提出的發明多元地掌握幾個態樣，而包含例如下述內容以作為用以解決課題的手段。亦即本發明為以下的［1］至［20］。
［1］ 一種纖維素聚合物的包裝方法，其係在具有氣體屏障性的包裝袋內填充纖維素聚合物，並將前述包裝袋密封。
［2］ 如上述［1］之纖維素聚合物的包裝方法，其滿足下述條件（1）至（3）。
條件（1）：在具有氣體屏障性的前述包裝袋內填充纖維素聚合物。
條件（2）：將前述包裝袋內的氧濃度調整為0.8%以下並進行密封。
條件（3）：填充有纖維素聚合物的前述包裝袋設置成最長的長邊L成為水平時，從水平面起算的包裝袋之深度D與長邊L滿足6.1≦L/D≦10的關係式。
［3］ 如上述［1］或［2］之纖維素聚合物的包裝方法，其中填充有纖維素聚合物的前述包裝袋的最長之長邊L為700mm以上1100mm以下。
［4］ 如上述［1］至［3］中任一項之纖維素聚合物的包裝方法，其中填充有纖維素聚合物的前述包裝袋中與長邊L正交之短邊W為400mm以上且小於700mm。
［5］ 如上述［1］至［4］中任一項之纖維素聚合物的包裝方法，其中填充有纖維素聚合物的前述包裝袋之深度D小於130mm。
［6］ 如上述［1］至［5］中任一項之纖維素聚合物的包裝方法，其中在滿足最外層表面的靜摩擦係數為0.2～0.5且動摩擦係數為0.15～0.35之範圍的具有氣體屏障性之前述包裝袋中填充纖維素聚合物。
［7］ 如上述［6］之纖維素聚合物的包裝方法，其中前述包裝袋的最外層之平滑度滿足2～10秒的範圍。
［8］ 如上述［6］或［7］之纖維素聚合物的包裝方法，其中前述包裝袋的最外層為紙基材。
［9］ 如上述［6］至［8］中任一項之纖維素聚合物的包裝方法，其中前述包裝袋的最外層滿足基重為50～100g/m2
的範圍。
［10］ 如上述［1］至［9］中任一項之纖維素聚合物的包裝方法，其中前述纖維素聚合物為羧基甲基纖維素。
［11］ 如上述［1］至［10］中任一項之纖維素聚合物的包裝方法，其中在對於前述包裝袋內進行真空處理後，進行氮氣取代而將氧濃度調整至0.8%以下。
［12］ 如上述［1］至［11］中任一項之纖維素聚合物的包裝方法，其中前述包裝袋內的內壓為85KPa以下。
［13］ 一種纖維素聚合物的運輸方法，其係將藉由如上述［1］至［12］中任一項之纖維素聚合物的包裝方法所得之包裝袋積層並運輸至目的地。
［14］ 如上述［13］之纖維素聚合物的運輸方法，其中使前述包裝袋成為2層以上10層以下的積層狀態。
［15］ 一種纖維素聚合物的包裝物，其具備經密封的包裝袋與填充於前述包裝袋內的纖維素聚合物，並滿足下述條件（1）～（3）：
條件（1）：在具有氣體屏障性的前述包裝袋內填充纖維素聚合物；
條件（2）：將前述包裝袋內的氧濃度調整為0.8%以下並進行密封；
條件（3）：填充有纖維素聚合物的前述包裝袋設置成最長的長邊L成為水平時，從水平面起算的包裝袋之深度D與長邊L滿足6.1≦L/D≦10的關係式。
［16］ 如上述［15］之纖維素聚合物的包裝物，其中前述包裝袋滿足最外層表面的靜摩擦係數為0.2～0.5且動摩擦係數為0.15～0.35的範圍。
［17］ 如上述［15］或［16］之纖維素聚合物的包裝物，其中前述纖維素聚合物為羧基甲基纖維素。
［18］ 如上述［15］至［17］中任一項之纖維素聚合物的包裝物，其中前述包裝袋內的氧濃度為大於0.3%且0.8%以下。
［19］ 如上述［15］至［18］中任一項之纖維素聚合物的包裝物，其中前述包裝袋內的內壓為85KPa以下。
［20］ 如上述［15］至［19］中任一項之纖維素聚合物的包裝物，其中前述包裝袋具有2層或3層以上的層結構，前述包裝袋的最外層為紙基材，位於前述最外層之內側的內袋層之中的至少一層為氣體屏障層。
［發明之效果］
根據本發明的一態樣，可提供適用於纖維素聚合物之運輸等的包裝方法。
又，根據本發明的一態樣，可提供一種抑制纖維素聚合物的黏度降低並且適用於運輸纖維素聚合物等的包裝方法。
再者，根據本發明的一態樣，可提供適用於運輸等的纖維素聚合物的包裝物。
又，根據本發明的一態樣，可提供一種抑制纖維素聚合物的黏度降低並且適用於纖維素聚合物的運輸等的包裝物。
以下說明本發明的實施型態。另外，本揭示中若未特別說明，關於數值範圍，「AA～BB」這樣的記載表示「AA以上BB以下」（此處「AA」及「BB」表示任意的數值）。又，下限及上限的單位若未特別說明，則與附於後者（亦即此處為「BB」）之正後方的單位相同。又，本揭示中，「X及/或Y」的表現係指X及Y雙方或是此等之中的任一者。又，本揭示中若未特別說明，則氣體濃度係以容積比例表示。例如，關於氧濃度的單位「%」，係表示氧的容積比（Vol/Vol）的百分率。
1.本發明的第一實施型態
本發明的一個實施型態係提供一種纖維素聚合物的包裝方法，其係在具有氣體屏障性的包裝袋內填充纖維素聚合物，並將前述包裝袋密封，其滿足下述條件（1）～（3）（以下稱為第一實施型態）。
條件（1）：在具有氣體屏障性的包裝袋內填充纖維素聚合物。
條件（2）：將包裝袋內的氧濃度調整為0.8%以下並進行密封。
條件（3）：填充有纖維素聚合物的包裝袋設置成最長的長邊L成為水平時，從水平設置面（水平面）起算的包裝袋之深度D與長邊L滿足6.1≦L/D≦10的關係式。
＜纖維素聚合物＞
本發明的第一實施型態中，纖維素聚合物只要是由纖維素而來的化合物則未特別限定，但較佳為經化學改質者，這樣的化學改質係將官能基導入紙漿，化學改質較佳為陰離子改質，亦即化學改質纖維素較佳係具有陰離子性基。作為陰離子性基，可列舉：羧基、含羧基之基、磷酸基、含磷酸基之基、硫酸酯基等酸基。作為含羧基之基，可列舉：-COOH基、-R-COOH（R為碳數1～3的伸烷基）、-O-R-COOH（R為碳數1～3的伸烷基）。作為含磷酸基之基，可列舉：多磷酸基、亞磷酸基、膦酸基、多膦酸基等。此等的酸基根據反應條件亦會以鹽的型態（例如羧酸酯基（-COOM，M為金屬原子））導入。本發明中化學改質較佳為氧化或醚化。
氧化可以習知的方法進行。可列舉例如：在與選自由N-氧基化合物、溴化物、碘化物及此等混合物所構成之群組的物質存在下，使用氧化劑於水中使原料紙漿氧化的方法。根據此方法，將纖維素表面之哌喃葡萄糖（glucopyranose）環的C6位的一級羥基選擇性氧化，而產生選自由醛基、羧基、及羧酸酯基所構成之群組的基。或可列舉臭氧氧化方法。根據此氧化反應，構成纖維素的哌喃葡萄糖環的至少2位及6位的羥基被氧化並且引起纖維素鏈的分解。
作為醚化，可列舉：羧基甲基（醚）化、甲基（醚）化、乙基（醚）化、氰基乙基（醚）化、羥基乙基（醚）化、羥基丙基（醚）化、乙基羥乙基（醚）化、羥基丙基甲基（醚）化等。其中較佳為羧基甲基化。羧基甲基化例如可藉由下述方法實施：使作為起始原料的原料紙漿進行絲光化（mercerization）之後再進行醚化的方法。其中，特別是羧基甲基化纖維素，可防止作為水溶液時的黏度降低，再者可成為適合進行運輸等的包裝袋。
這樣的羧基甲基化纖維素一般可藉由下述方法製造：以鹼對於纖維素進行處理（絲光化）之後，使所得之絲光化纖維素（亦稱為鹼纖維素）與羧基甲基化劑（亦稱為醚化劑）反應。
本發明的第一實施型態中纖維素意指D-哌喃葡萄糖（亦僅稱為「葡萄糖殘基」、「無水葡萄糖」）由β-1,4鍵連結而成之結構的多糖。纖維素一般由起源、製法等分類成天然纖維素、再生纖維素、微細纖維素、去除非結晶區域的微結晶纖維素等。本發明中，此等纖維素皆可作為絲光化纖維素的原料使用。
作為天然纖維素，可例示漂白紙漿或未漂白紙漿（漂白木材紙漿或未漂白木材紙漿）；棉絨、精製棉絨；藉由乙酸菌等微生物所生產的纖維素等。漂白紙漿或未漂白紙漿的原料並未特別限定，可列舉例如：木材、木棉、稻草、竹、麻、黃麻、洋麻等。又，漂白紙漿或未漂白紙漿的製造方法並未特別限定，可為機械方法、化學方法或是在其之間將二者組合而成的方法。作為根據製造方法分類的漂白紙漿或未漂白紙漿，可列舉例如：機械紙漿（熱磨機械紙漿（TMP）、碎木紙漿）、化學紙漿（針葉樹未漂白亞硫酸鹽紙漿（NUSP）、針葉樹漂白亞硫酸鹽紙漿（NBSP）等亞硫酸紙漿、針葉樹未漂白牛皮（kraft）紙漿（NUKP）、針葉樹漂白牛皮紙漿（NBKP）、廣葉樹未漂白牛皮紙漿（LUKP）、廣葉樹漂白牛皮紙漿（LBKP）等牛皮紙漿）等。再者，除了製紙用紙漿以外亦可使用溶解紙漿。溶解紙漿係經過化學精製的紙漿，主要係溶解於化學藥品以使用，其為人造纖維、賽璐玢等的主原料。
羧基甲基化纖維素的無水葡萄糖每單位的羧基甲基取代度較佳為0.2～1.5的範圍，更佳為0.3～1.2的範圍，再佳為0.5～1.0的範圍。羧基甲基取代度若小於0.2，則在將羧基甲基化纖維素作為水溶液時，不太會展現黏度而限制了本發明的效果。若羧基甲基取代度超過1.5，則即使是本發明的包裝方法也容易引起黏度降低，因此並不合適。
另外，本發明的第一實施型態中無水葡萄糖單元係指構成纖維素的各別的無水葡萄糖（葡萄糖殘基）。又，羧基甲基取代度（亦稱為醚化度），係表示構成纖維素的葡萄糖殘基中的羥基之中被取代為羧基甲醚基的比例（每一個葡萄糖殘基的羧基甲醚基數量）。另外，羧基甲基取代度有時會簡寫成DS。
羧基甲基取代度的測量方法如下：
精秤試料約2.0g，放入300mL的有栓錐形燒瓶。將在1000mL的甲醇中加入特級濃硝酸100mL的液體100mL加入其中，並振盪3小時，以使羧基甲基纖維素的鹽（CMC）轉變成H-CMC（氫型羧基甲基纖維素）。精秤1.5～2.0g的該極乾燥H-CMC，放入300mL的有栓錐形燒瓶。以80%甲醇15mL將H-CMC潤濕，加入100mL的0.1N之NaOH，於室溫振盪3小時。使用酚酞作為指示劑，以0.1N-H2
SO4
對於過剩的NaOH進行反滴定，藉由下式算出羧基甲基取代度（DS值）。
A=［（100×F’-0.1N-H2
SO4
（mL）×F）×0.1］/（H-CMC的極乾燥質量（g））
羧基甲基取代度=0.162×A/（1-0.058×A）
F’：0.1N-H2
SO4
的因子
F：0.1N-NaOH的因子。
作為本發明之第一實施型態中可使用的纖維素聚合物，可直接使用經化學改質之漿狀物的纖維素，亦可藉由粉碎處理等使漿狀物成為粉末狀以使用。又，亦可對於漿狀物進行解纖處理，而使用微纖絲（microfibril）狀的纖維素或奈米纖維狀的纖維素等乾燥物。
纖維素奈米纖維，可藉由將纖維素原料在未改質的狀態下或是對其實施化學改質以後施加強剪切力而加以製造。本發明的第一實施型態中，纖維素原料可為未改質，亦可經過化學改質，但更佳為經過化學改質。推測係使用實施了化學改質的纖維素原料所製造的纖維素奈米纖維，其纖維長度/纖維直徑相對於使用未改質的纖維素原料所製造的纖維素奈米纖維更為均勻，在水中分散性穩定而發揮更優良的效果。化學改質的方法並未特別限制，例如可進行氧化、醚化、磷酸化、酯化、矽烷偶合、氟化、陽離子化等。其中較佳為使用了N-氧基化合物的氧化、羧基甲基化、陽離子化中的任一者，特佳為羧基甲基化或氧化。
又，作為本發明的第一實施型態中可使用的纖維素聚合物，較佳係填充於包裝袋內時的乾燥固體成分量在60重量%以上，更佳為70重量%以上，再佳為80重量%以上。乾燥固體成分量若在此範圍內，則因為在包裝體內平衡水分的乖離量減少，而可抑制因為水分所造成的纖維素聚合物的劣化。
＜包裝袋＞
本發明的第一實施型態中，包裝袋只要是具有氣體屏障性的包裝袋則無特別限制而皆可使用。另外，本發明中具有氣體屏障性係指具有可抑制氧或水分等穿透的功能，作為這種包裝袋，較佳係使用了下述膜的包裝袋：氣體屏障性高的鋁；具有聚丙烯腈、聚乙烯醇、聚二氯亞乙烯系樹脂之塗膜的尼龍膜；在乙烯-乙烯醇共聚物、烯烴系聚合物、烯烴-聚羧酸共聚物或是塑膠製的基材上設置氧化矽、氧化鋁等無機氧化物之蒸鍍層的構成所形成的透明屏障性膜；及設置有鋁等金屬之蒸鍍層的屏障性膜等。
又，包裝袋的最外層為強度高而不易破損者較為合適，較佳為紙基材。作為這種紙基材，可列舉例如：牛皮紙。
因此，本發明的第一實施型態中所使用的包裝袋，較佳係最外層為紙基材且內層具有氣體屏障性層，這樣的氣體屏障層亦可以另外的袋子作為內袋，亦可對於最外層的紙基材進行添附加工（例如層壓加工）等以使用。從操作的簡便性等來看，氣體屏障性層更佳係作為內袋使用。
又，本發明的第一實施型態中所使用的包裝袋，從維持填充之纖維素聚合物之品質的觀點來看，具有紫外線非穿透性、或遮光性者較為合適。
＜纖維素聚合物的填充＞
作為將纖維素聚合物填充於包裝袋內的方法並未特別限制，只要將纖維素聚合物適當填充於包裝袋即可。另外，填充量若太多，則氧濃度的調整以及與第一實施型態相關的後述條件（3）的調整等變得困難，因此纖維素聚合物的填充量較佳為包裝袋內容積的99%以下，更佳為95%以下，再佳為90%以下。
又，包裝袋為具有在前述最外層為紙基材的外袋（或外層）與氣體屏障層之內袋（或內層）的包裝袋的情況中，亦可在將纖維素聚合物填充於內袋之後再捆包外袋，亦可預先將內袋放入外袋之後再填充纖維素聚合物。
＜包裝袋內之氧濃度的調整＞
包裝袋內之氧濃度的調整並未特別限定，較佳係在填充纖維素聚合物後進行，可列舉例如：在填充纖維素聚合物之後， 1）使包裝袋內成為真空的方法，2）以氮氣取代包裝袋內的方法，3）使包裝袋內成為真空後再進行氮氣取代的方法，4）在包裝袋內一起封入吸氧劑的方法等。此等方法之中，使包裝袋內成為真空之後再進行氮氣取代的方法，可抑制纖維素聚合物彼此凝集，因此在本發明的第一實施型態中更合適 。
這樣的本發明之第一實施型態的包裝方法中，將包裝袋內的氧濃度調整為0.8%以下並進行密封係為重要。氧濃度若超過0.8%，則容易引起纖維素聚合物劣化而具有在使纖維素聚合物成為水溶液時黏度降低的疑慮。氧濃度較佳為0.75%以下，更佳為0.7%以下，再佳為0.6%以下。氧濃度的下限並無限制，但從作業性及氮氣取代時調整內壓的觀點來看，較佳為0.1%以上，更佳為0.2%以上，再佳為超過0.3%。
又，較佳係使包裝袋內的內壓為85kPa以下，氣體屏障層內的內壓在85kPa以下尤為合適。若內壓超過85kPa，則包裝袋相對於填充物的膨脹變大，因此難以成為將包裝袋堆疊的積層狀態，而在運輸時等具有問題。這樣的包裝袋的內壓更佳為80kPa以下。
另外，調整包裝袋內之內壓的方法並未特別限制，例如在使包裝袋內成為真空後再進行氮氣取代之方法的情況中，可在真空處理後充入氮氣時，適當調整其氮氣流入量及從原壓力起算的內壓指示值，藉此可適當調整包裝袋內的內壓。
＜經密封之包裝袋的形狀＞
本發明的第一實施型態中，填充纖維素聚合物並調整氧濃度而後密封的包裝袋，其設置於水平設置面（稱為水平面）上而使最長的長邊L成為水平時，從水平面起算的包裝袋之深度D與長邊L滿足6.1≦L/D≦10的關係式，此點係為重要。
圖1係顯示設置在水平面上而使最長的長邊L成為水平的填充有纖維素聚合物的包裝袋。本發明中，填充有纖維素聚合物的包裝袋，在設置為水平之後，進行長邊L與深度D的測量之前，使填充區域沿著水平面均勻填充，此點係為重要。
這樣的長邊L不包含包裝袋的密封口，僅表示包裝袋的填充區域之長度。長邊L較佳為700mm以上1100mm以下的範圍，更佳為700mm以上1000mm以下，再佳為700mm以上900mm以下。
與填充有纖維素聚合物之包裝袋的長邊L正交的短邊W較佳為400mm以上且小於700mm，更佳為450mm以上650mm以下，再佳為450mm以上600mm以下。
填充有纖維素聚合物的包裝袋之深度D較佳為小於130mm，更佳為125mm以下，再佳為120mm以下。
本發明之第一實施型態的纖維素聚合物的包裝方法中，藉由滿足前述的關係式，在將填充有纖維素聚合物的包裝袋積層時取得適當的平衡而容易進行積層。又，藉由使包裝袋的長邊L、深度D及短邊W滿足上述範圍，使得纖維素聚合物的填充變得容易，又包裝袋的積層亦變得容易。
再者，在將該包裝袋積層並運輸時，不易因為振動等而導致積層狀態失去平衡，因此在本發明中係為重要。
本發明的第一實施型態中，在將包裝袋積層時，較佳係成為2層以上10層以下的積層狀態，再佳係成為2層以上8層以下的積層狀態。積層狀態若在此範圍內，則可使包裝袋之積層狀態的平衡更為理想。
2.本發明的第二實施型態
作為本發明的其他實施型態，係提供一種纖維素聚合物的包裝方法，其特徵為在滿足最外層表面的靜摩擦係數為0.2～0.5且動摩擦係數為0.15～0.35之範圍的具有氣體屏障性之包裝袋內填充纖維素聚合物（以下亦稱為第二實施型態）。
首先說明作為第二實施型態之一特徵性部分的包裝袋。
＜包裝袋＞
本發明的第二實施型態中，包裝袋只要是具有氣體屏障性的包裝袋則未特別限制皆可使用。另外，本發明中具有氣體屏障性係指具有可抑制氧或水分等穿透之功能，作為這樣的包裝袋，較佳係使用了下述膜的包裝袋：氣體屏障性高的鋁；具有聚丙烯腈、聚乙烯醇、聚二氯亞乙烯系樹脂之塗膜的尼龍膜；在乙烯-乙烯醇共聚物、烯烴系聚合物、烯烴-聚羧酸共聚物或塑膠製的基材上設置氧化矽、氧化鋁等無機氧化物之蒸鍍層的構成所形成之透明屏障性膜；及設有鋁等金屬之蒸鍍層的屏障性膜等。
又，包裝袋的最外層為強度高而不易破損者較為合適，較佳為紙基材。作為這樣的紙基材，可列舉例如：牛皮紙。
因此，本發明的第二實施型態中所使用的包裝袋較佳係最外層為紙基材且內層具有氣體屏障性層，這樣的氣體屏障性層亦可以另外的袋子作為內袋，亦可對於最外層的紙基材進行添附加工（例如層壓加工）等以使用。從操作的簡便性等來看，氣體屏障性層更佳係作為內袋以使用。
這樣的包裝袋的最外層表面其靜摩擦係數在0.2～0.5的範圍內此點係為重要，較佳為0.2～0.45的範圍，更佳為0.2～0.4的範圍。藉由使最外層表面的靜摩擦係數在此範圍內，即使是在包裝袋內填充纖維素聚合物並且為了運輸而在棧板上等將包裝袋彼此積層的情況，亦不易失去平衡而導致掉落，而且摩擦力亦不會太強，因此可在積層時使包裝袋滑動而容易調整積層狀態。
又包裝袋的最外層表面其動摩擦係數為0.15～0.35的範圍係為重要，較佳為0.2～0.35的範圍，更佳為0.22～0.32的範圍。藉由使最外層表面的動摩擦係數為此範圍，即使在包裝袋內填充纖維素聚合物並且為了運輸而在棧板上等將包裝袋彼此積層的情況，亦可使積層狀態的包裝袋彼此容易平順移動，又包裝袋不易失去平衡而掉落等，此為適當的範圍。另外，包裝袋的最外層表面的靜摩擦係數及動摩擦係數的測量可依據JIS P8147進行測量。
再者，包裝袋的最外層較其藉由王研法所得到的平滑度較佳為2～10秒的範圍，更佳為3～9秒的範圍，再佳為4～8秒的範圍。藉由使平滑度在此範圍，最外層表面的凹凸可在將纖維素聚合物填充於包裝袋並且為了運輸而將包裝袋彼此積層於棧板上等的情況中防止掉落以及在滑動時取得適當的平衡。可依據JIS P8155藉由王研法來測量平滑度。
又，本發明的第二實施型態中，包裝袋的最外層較佳為滿足基重50～100g/m2
的範圍，更佳為滿足60～100g/m2
的範圍，再佳為滿足65～95g/m2
的範圍。藉由使包裝袋的最外層基材滿足上述範圍，即使在填充纖維素聚合物情況中亦可一方面保持強度一方面容易發揮作為前述最外層的最佳平衡。可依據JIS P8124來測量基重。
又，本發明的第一實施型態中所使用的包裝袋，從維持所填充之纖維素聚合物之品質的觀點來看，具有紫外線非穿透性、或遮光性者較為合適。
與第二實施型態相關的其他技術事項，與上述第一實施型態相同。亦即，與下述第一實施型態相關的說明中所述之事項等的說明，在第二實施型態中亦可與第一實施型態相同地採用：纖維素聚合物的定義；氧化的方法；醚化；羧基甲基化纖維素；纖維素；天然纖維素；羧基甲基化纖維素的無水葡萄糖每單位的羧基甲基取代度；無水葡萄糖單元；羧基甲基取代度的測量方法；關於纖維素聚合物的形狀（紙漿狀、粉末狀、微纖絲狀、奈米纖維狀等）；填充於包裝袋內時的乾燥固體成分量；與包裝袋的積層段數相關的狀態。
3.第一實施型態及第二實施型態的組合
作為本發明之其他實施型態，亦可將上述第一實施型態及第二實施型態組合。作為這樣的變形例，可列舉例如下述的實施型態。
＜第一及第二實施型態之組合的例子＞
一種纖維素聚合物的包裝方法，其係在具有氣體屏障性的包裝袋內填充纖維素聚合物並將前述包裝袋密封，其滿足下述條件（1）～（4）：
條件（1）：在具有氣體屏障性的包裝袋內填充纖維素聚合物；
條件（2）：將包裝袋內的氧濃度調整為0.8%以下並進行密封；
條件（3）：填充有纖維素聚合物的包裝袋設置成最長的長邊L成為水平時，從水平面起算的包裝袋之深度D與長邊L滿足6.1≦L/D≦10的關係式；
條件（4）：滿足前述包裝袋的最外層表面的靜摩擦係數為0.2～0.5且動摩擦係數為0.15～0.35的範圍。
第一及第二實施型態之組合的情況中，具體的技術事項或較佳例等，亦可相同地採用上述第一實施型態或第二實施型態中所說明之內容。
4.本發明的第三實施型態
如上所述，本發明的幾個態樣係包裝方法、運輸方法等的方法，根據本發明，提供一種利用此包裝方法之纖維素聚合物的包裝物。作為包裝物的實施型態，根據上述第一實施型態所示的包裝方法而提供如下述之纖維素聚合物的包裝物。
一種纖維素聚合物的包裝物，具備經密封的包裝袋與填充於前述包裝袋內的纖維素聚合物，其滿足下述條件（1）～（3）：
條件（1）：在具有氣體屏障性的包裝袋內填充纖維素聚合物；
條件（2）：將包裝袋內的氧濃度調整為0.8%以下並進行密封；
條件（3）：填充有纖維素聚合物的包裝袋設置成最長的長邊L成為水平時，從水平面起算的包裝袋之深度D與長邊L滿足6.1≦L/D≦10的關係式。
作為包裝物的其他實施型態，根據上述第二實施型態所示的包裝方法，提供如下述之纖維素聚合物的包裝物。
一種纖維素聚合物的包裝物，其具備具有氣體屏障性並且經密封的包裝袋與填充於前述包裝袋內的纖維素聚合物，其中前述包裝袋滿足最外層表面的靜摩擦係數為0.2～0.5且動摩擦係數為0.15～0.35的範圍。
與第三實施型態相關的更具體之技術事項或較佳例等，可相同地採用上述第一實施型態或第二實施型態中所說明之內容。又，亦可作為將第一實施型態及第二實施型態所示的技術事項組合而成的纖維素聚合物的包裝物。
[實施例]
＜第一實施例群＞
［實施例1-1］
將羧基甲基纖維素（日本製紙公司製，產品名稱：MAC500LC）填充至下述包裝袋：該包裝袋處於未填充（空袋）狀態下，長度為850mm，寬度為565mm，最外層為牛皮紙基材，且內裝具有膜基材。
填充後進行真空排氣之後注入氮氣，將包裝體內的氧濃度調整為0.50%，將內壓指示值調整為70kPa，並將密封口密封。
將所得之包裝袋設置於水平面，將包裝袋的內容物均勻分布於填充區域等之後測量包裝袋，結果其最長之長邊L為760mm，從水平面起算的深度D為110mm，與長邊L正交的短邊W為520mm。
［實施例1-2］
使用羧基甲基纖維素（日本製紙公司製，產品名稱：MAC350HC），除此之外與實施例1-1相同地得到包裝袋。
［實施例1-3］
使用羧基甲基纖維素（日本製紙公司製，產品名稱：MAC800LC），除此之外與實施例1相同地得到包裝袋。
［比較例1-1］
使包裝體內的氧濃度為0.3%，並使內壓指示值為90kPa，除此之外，與實施例1相同地得到包裝袋。將所得之包裝袋設置於水平面，在使包裝袋的內容物均勻分布於填充區域之後，測量包裝袋，結果其最長之長邊L為760mm，從水平面起算的深度D為130mm，與長邊L正交的短邊W為520mm。
[表1]
| 包裝袋 | 填充物 | 填充後的包裝袋 | |||||||
| 最外層 | 內層 | 氧濃度 （%） | 內壓 （KPa） | L （mm） | D （mm） | W （mm） | L/D | ||
| 實施例1-1 | 牛皮紙 | 薄膜 | MAC500LC | 0.5 | 70 | 760 | 110 | 520 | 6.9 |
| 實施例1-2 | 牛皮紙 | 薄膜 | MAC350HC | 0.5 | 70 | 760 | 110 | 520 | 6.9 |
| 實施例1-3 | 牛皮紙 | 薄膜 | MAC800LC | 0.5 | 70 | 760 | 110 | 520 | 6.9 |
| 比較例1-1 | 牛皮紙 | 薄膜 | MAC500LC | 0.3 | 90 | 760 | 130 | 520 | 5.8 |
在填充實施例1-1～1-3及比較例1-1的羧基甲基纖維素之後立即測量1%水溶液的黏度，以及在50℃的保管箱內保管1個月、3個月、6個月後測量1%水溶液的黏度。另外，水溶液的調整方法及黏度的測量方法係由後述方法進行。
又，將所得之包裝袋在棧板上堆疊4列6層以進行積層時，以目視確認積層狀態。
＜水溶液的製備＞
以上皿天平量取約10g的試料。在放入有純水880ml的燒杯中，使用溶解用攪拌機，一邊攪拌一邊緩慢投入該試料，攪拌3小時。以使從水分值所計算之純水成為濃度1%的方式進行修正。
＜黏度測量＞
在攪拌3小時後（確認完全溶解）、將溶液的溫度調整為25±0.2℃。使用B型黏度計測量黏度。測量值係讀取在轉子啟動開始3分鐘後的刻度。
［黏度變化率］
以下式（1）計算，包裝後於保管箱內保管於50℃（1個月、3個月、6個月）之後的纖維素聚合物之1%水溶液黏度（黏度2）相對於經過天數0天（包裝前）的纖維素聚合物的1%水溶液黏度（黏度1）的黏度變化率。
［（黏度2-黏度1）/黏度1］×100 （%）･･･（1）
[表2]
| 黏度變化率 | 積層狀態 | ||||
| 經過月數 | |||||
| 0 | 1個月 | 3個月 | 6個月 | ||
| 實施例1-1 | 0 | -1 | -1 | -3 | 各包裝袋緊密地積層，平衡優良。 |
| 實施例1-2 | 0 | -3 | -3 | -4 | 各包裝袋緊密地積層，平衡優良。 |
| 實施例1-3 | 0 | -4 | -1 | -3 | 各包裝袋緊密地積層，平衡優良。 |
| 比較例1-1 | 0 | -1 | -1 | -2 | 各包裝袋膨脹，未緊密地積層而平衡不佳。 |
可知實施例1-1～1-3的包裝袋中，所填充之羧基甲基纖維素在保管後可維持高黏度。再者，包裝袋相對於包裝袋的強度其內壓平衡優良而未發生膨脹，因此在積層時的平衡亦優良。
另一方面，比較例1-1的包裝袋因為將氧濃度抑制地較低，而因此羧基甲基纖維素的黏度維持效果優良，但內壓高而包裝袋膨脹，其在積層狀態下的平衡不佳，並不適合作為運輸型態。
＜第二實施例群＞
［實施例2-1］
將羧基甲基纖維素（日本製紙公司製，產品名稱：MAC500LC）填充於下述包裝袋：該包裝袋的最外層為牛皮紙基材（表面的靜摩擦係數：0.32，動摩擦係數：0.28，王研式平滑度：5秒，基重：85g/m2
），內層具有膜基材。
填充後並進行真空排氣之後注入氮氣，將包裝體內的氧濃度調整為0.50%，將內壓指示值調整為70kPa，將密封口密封，得到填充有羧基甲基纖維素的包裝袋2-1。
［實施例2-2］
將最外層變更為牛皮紙基材（表面的靜摩擦係數：0.30，動摩擦係數：0.28，王研式平滑度：5秒，基重：76g/m2
），除此之外，與實施例1相同地得到填充有羧基甲基纖維素的包裝袋2-2。
［比較例2-1］
不使用牛皮紙基材而將膜基材（表面的靜摩擦係數：0.12，動摩擦係數：0.1，王研式平滑度：無法測量，基重：109g/m2
）作為最外層以進行變更，除此之外，與實施例1相同地得到填充有羧基甲基纖維素的包裝袋3。
[表3]
| 包裝袋 | 填充物 | ||
| 最外層 | 內層 | ||
| 實施例2-1 | 牛皮紙 | 薄膜 | MAC500LC |
| 實施例2-2 | 牛皮紙 | 薄膜 | MAC500LC |
| 比較例2-1 | 薄膜 | - | MAC500LC |
在實施例2-1及2-2中填充了羧基甲基纖維素之後立即測量1%水溶液的黏度，以及在50℃的保管箱內保管1個月、3個月、6個月後測量1%水溶液的黏度。另外，水溶液的調整方法、黏度的測量方法及黏度變化率的計算皆係以與上述第一實施例群所示之方法相同的方法進行。
又，以目視確認將實施例2-1及2-2及比較例2-1的包裝袋在棧板上堆疊成4列6層以進行積層時的積層容易度與積層狀態。
[表4]
| 黏度變化率 | 積層狀態 | ||||
| 經過月數 | |||||
| 0 | 1個月 | 3個月 | 6個月 | ||
| 實施例2-1 | 0 | -1 | -1 | -3 | 各包裝袋可滑動而輕易地調整成緊密的積層狀態。又，積層時的平衡亦為優良。 |
| 實施例2-2 | 0 | -1 | -1 | -3 | 各包裝袋可滑動而輕易地調整成緊密的積層狀態。又，積層時的平衡亦為優良。 |
| 比較例2-1 | - | - | - | - | 各包裝一滑動就失去平衡，無法保持緊密的積層狀態。 |
無
圖1係填充有纖維素聚合物的包裝袋，其係該包裝袋設置成最長的長邊L與水平之設置面（水平面）成為水平的圖，D表示從水平面起算的深度，W表示與L正交之寬度方向的短邊。
Claims (23)
- 一種纖維素聚合物的包裝方法，其係在具有氣體屏障性的包裝袋內填充纖維素聚合物，並將前述包裝袋密封。
- 如請求項1之纖維素聚合物的包裝方法，其滿足下述條件（1）至（3）： 條件（1）：在具有氣體屏障性的前述包裝袋內填充纖維素聚合物； 條件（2）：將前述包裝袋內的氧濃度調整為0.8%以下並進行密封； 條件（3）：填充有纖維素聚合物的前述包裝袋設置成最長的長邊L成為水平時，從水平面起算的包裝袋之深度D與長邊L滿足6.1≦L/D≦10的關係式。
- 如請求項2之纖維素聚合物的包裝方法，其中填充有纖維素聚合物的前述包裝袋的最長之長邊L為700mm以上1100mm以下。
- 如請求項2之纖維素聚合物的包裝方法，其中填充有纖維素聚合物的前述包裝袋中與長邊L正交之短邊W為400mm以上且小於700mm。
- 如請求項2之纖維素聚合物的包裝方法，其中填充有纖維素聚合物的前述包裝袋之深度D小於130mm。
- 如請求項2之纖維素聚合物的包裝方法，其中前述纖維素聚合物為羧基甲基纖維素。
- 如請求項2之纖維素聚合物的包裝方法，其中在對於前述包裝袋內進行真空處理後，以氮氣進行取代而將氧濃度調整至0.8%以下。
- 如請求項2之纖維素聚合物的包裝方法，其中前述包裝袋內的內壓為85KPa以下。
- 如請求項1之纖維素聚合物的包裝方法，其中在滿足最外層表面的靜摩擦係數為0.2～0.5且動摩擦係數為0.15～0.35之範圍的具有氣體屏障性之前述包裝袋中填充纖維素聚合物。
- 如請求項9之纖維素聚合物的包裝方法，其中前述包裝袋的最外層之平滑度滿足2～10秒的範圍。
- 如請求項9之纖維素聚合物的包裝方法，其中前述包裝袋的最外層為紙基材。
- 如請求項9之纖維素聚合物的包裝方法，其中前述包裝袋的最外層滿足基重為50～100g/m2 的範圍。
- 如請求項9之纖維素聚合物的包裝方法，其中前述纖維素聚合物為羧基甲基纖維素。
- 如請求項9之纖維素聚合物的包裝方法，其中在對於前述包裝袋內進行真空處理後，進行氮氣取代而將氧濃度調整至0.8%以下。
- 如請求項9之纖維素聚合物的包裝方法，其中前述包裝袋內的內壓為85KPa以下。
- 一種纖維素聚合物的運輸方法，其係將藉由如請求項1至15中任一項之纖維素聚合物的包裝方法所得之包裝袋積層並運輸至目的地。
- 如請求項16之纖維素聚合物的運輸方法，其中使前述包裝袋成為2層以上10層以下的積層狀態。
- 一種纖維素聚合物的包裝物，其具備經密封的包裝袋與填充於前述包裝袋內的纖維素聚合物，並滿足下述條件（1）～（3）： 條件（1）：在具有氣體屏障性的前述包裝袋內填充纖維素聚合物； 條件（2）：將前述包裝袋內的氧濃度調整為0.8%以下並進行密封； 條件（3）：填充有纖維素聚合物的前述包裝袋設置成最長的長邊L成為水平時，從水平面起算的包裝袋之深度D與長邊L滿足6.1≦L/D≦10的關係式。
- 如請求項18之纖維素聚合物的包裝物，其中前述包裝袋滿足最外層表面的靜摩擦係數為0.2～0.5且動摩擦係數為0.15～0.35的範圍。
- 如請求項18或19之纖維素聚合物的包裝物，其中前述纖維素聚合物為羧基甲基纖維素。
- 如請求項18或19之纖維素聚合物的包裝物，其中前述包裝袋內的氧濃度大於0.3%且在0.8%以下。
- 如請求項18或19之纖維素聚合物的包裝物，其中前述包裝袋內的內壓為85KPa以下。
- 如請求項18或19之纖維素聚合物的包裝物，其中前述包裝袋具有2層或3層以上的層結構，前述包裝袋的最外層為紙基材，位於前述最外層之內側的內袋層之中的至少一層為氣體屏障層。