TW200815288A - Cerium oxide powder, method for preparing the same, and CMP slurry comprising the same - Google Patents
Cerium oxide powder, method for preparing the same, and CMP slurry comprising the same Download PDFInfo
- Publication number
- TW200815288A TW200815288A TW096127623A TW96127623A TW200815288A TW 200815288 A TW200815288 A TW 200815288A TW 096127623 A TW096127623 A TW 096127623A TW 96127623 A TW96127623 A TW 96127623A TW 200815288 A TW200815288 A TW 200815288A
- Authority
- TW
- Taiwan
- Prior art keywords
- cerium oxide
- oxide powder
- cerium
- chemical mechanical
- mechanical polishing
- Prior art date
Description
200815288 九、發明說明: 【發明所屬之技術領域】 本發明係關於一種作為化學機械拋光研磨料之氧化鈽 粉末,於半導體製程之化學機械拋光中,其可改善氧化矽 5 層對比氮化矽層之拋光選擇性及/或晶圓内非均勻性 (WIWNU)。本發明亦關於一種包括該氧化鈽粉末之化學機 械拋光漿料。 【先前技術】 10 一般而言,現今半導體製程已有增加晶圓直徑的趨 勢,以達到特大型積體電路(ULSI)之高積集度(integration) 需求。此外,現今半導體製作已面臨更嚴苛的標準要求, 包括,最小寬度必須等於或小於0.13// m。再者,於晶圓上 形成多路互連(multiple interconnection)或多層互連 15 (multilayer interconnection)結構之步驟已成為改善半導體 裝置品質之必要手段。然而,進行上述其中一項技術後所 導致之晶圓不平坦現象將衍生許多問題,例如,後續步驟 出現的邊緣下降或電晶體或裝置品質劣化的問題。因此, 不同步驟都必.須進行平坦化之程序,以解決此類問題。 20 化學機械拋光(chemical mechanical polishing,CMP) 為平坦化之其中一種技術。於化學機械拋光之製程中,使 晶圓表面對著拋光墊而受壓,拋光塾則相對於晶圓表面旋 轉,而於拋光的過程中,將具化學活性之漿料導入拋光墊 5 200815288 中。化學機械拋光侈藉由化學及物理作用完成晶圓表面平 坦化之技術。 化予機械拋光可應用於淺溝槽隔離(shallow trench isolation’ STI)之製程中,尤其是,於沉積絕緣氧化矽層1〇4 5 後,對絕緣氧化矽層104進行拋光,以使氮化矽蝕刻停止層 102顯露於外,致使晶圓上之溝槽103可嵌埋於其中(請參見 圖1(b)及1(c))。在此,氮化矽層之強度及硬度大約為氧化矽 層之二倍’因此氧化石夕層之拋光速度大於氮化石夕層。較佳 為’氮化矽層未被移除。換言之,理想狀況為,氧化矽層 10 對比於氮化矽層之拋光速度(此後又稱作,,氧化矽層對比於 氮化矽層之拋光選擇性”)為無限大。 然而’習知化學機械拋光漿料具有低的絕緣氧化矽層 對比氮化矽層之拋光選擇性,其大约為4:1。因此,於實際 的化學機械拋光製程中,氮化矽層會被磨到超出可接受之 15 範圍。據此,於化學機械拋光之製程中,氮化矽層圖案將 會依其於晶圓中之位置而被不均勻地移除。因此,氮化矽 蝕刻停止層於整個晶圓中會有明顯的厚度變化。於淺溝槽 隔離(shallow trench isolation,STI)之製程中,上述的問題 會導致形成有溝槽之最終結構的有源區(active region)與場 2〇 區(field region)間出現高度不同的現象,因而導致製作半導 體裝置之後續步驟出現加工邊緣下降現象及電晶體與裝置 品質劣化的問題。尤其是,對同時具有不同密集度圖案之 半導體晶圓而言,上述現象是個嚴重的問題。 200815288 除了上述之局部平坦化問題,習知化學機械拋光製程 還有晶圓内非均勻性(within-wafer non-uniformity,WIWNU) 低的現象。換言之,利用習知化學機械拋光製程進行拋光 的過程中,拋光作用於晶圓之中心處比周圍處更為明顯, 5 如此將導致整體為U型或W型之縱切面。上述現象的原因被 認為是:施加於晶圓及拋光墊之機械壓力分佈不均勻,進 而導致拋光漿料或拋光粒子無法均勻分佈,因而使晶圓之 中心處呈現較高之拋光速度。 為解決上述有關晶圓内非均勻性的問題,實際的半導 10 體製程會採用具有較大加工邊緣的氮化矽層,以確保最終 化學機械拋光之可靠度。例如,氮化矽層具有較大的初始 厚度,用以補償拋光後之晶圓中心處與周圍處的厚度落 差。然而,此法會使製程之經濟效益變差。 15 【發明内容】 本發明係鑑於上述問題而完成。本發明之發明人發 現,當以鍛燒碳酸鈽所獲得之氧化鈽粉末作為化學機械拋 光漿料之研磨料,則碳酸鈽之晶體結構將明顯影響化學機 械拋光製程中之氧化矽對比於氮化矽之拋光選擇性或晶圓 2〇 内非均勻性(within-wafer non-uniformity,WIWNU)。 此外,本發明之發明人發現,當以六方晶體結構之碳 酸鈽作為前驅物,且以其所獲得之氧化鈽粉末作為化學機 械拋光漿料之研磨料時,則化學機械拋光製程中之氧化矽 7 200815288 對比於氮化矽之拋光選擇性及/或晶圓内非均勻性(WIWNU) 可獲改善。 本發明是基於上述發現而成就。 本發明之一態樣係提供一種製備氧化鈽粉末之方法, 5 其係以具有六方晶體結構之碳酸鈽作為前軀物。 本發明之另一態樣係提供:氧化鈽粉末,其包括至少 50%(體積百分比)之六方盤狀粒子,而該些粒子具有至少一 角度為120°±20°的邊緣;化學機械拋光漿料,其包括作為研 磨料之氧化鈽粉末;以及半導體裝置之淺溝槽隔離製程, 10 其特徵在於,以化學機械拋光漿料作為拋光漿料。 本發明之再一態樣係提供一種控制氧化矽對比於氮化 矽之拋光選擇性及/或晶圓内非均勻性(WIWNU)的方法,其 係以氧化鈽粉末作為化學機械拋光漿料之研磨料,而氧化 鈽粉末係由具有六方晶體結構之碳酸鈽所製得。 15 以下將更詳細地解釋本發明。 一般而言,化學機械拋光聚料係包括一研磨料、一分 散劑及水。 至今已有許多研究係使用分散穩定劑或添加劑,藉此 修飾化學機械拋光漿料之化學組成份,企圖改善化學機械 20 拋光漿料之拋光特性,包括氧化矽層對比氮化矽層之拋光 選擇性及晶圓内非均勻性(WIWNU)。 同時,一般認為,藉由習知研磨料(如:氧化鈽)而進行 之拋光步驟係以機械拋光作為其主要之拋光機制,機械拋 光係藉由重複一連串步驟而完成,包括⑴使須拋光之表面 200815288 進行水合反應(據此形成為”si(0H)3,,);(ii)利用研磨料機械 移除水合層;以及(iii)將已移除之水合矽(Si(〇H)4)分散且溶 解於溶液中。 此外,已有論文(journal 0f Non_Crystalline s〇lids, 5 283,2001,pp 129·136)揭示,當以氧化鈽作為研磨料時,氧 化鈽可與氧化矽層起化學作用。意即,氧化鈽可對氧化矽 層進行化學抛光’其所藉由的機制為,氧化鈽與氧化矽間 之高反應性將引起Si-0-Ce之化學鍵結,而氧化鈽可以剝離 氧化矽塊的方式,將氧化矽由氧化矽層表面移除。 10 換言之,當以氧化鈽作為研磨料時,氮化矽層及氧化 矽層之拋光速度可冑b文到氧化鈽之物理化學性質影響。此 外,氧化矽層對比氮化矽層之拋光選擇性及晶圓内非均勻 性(WIWNU)將決定於氧化矽層及氣化矽層之拋光速度。因 此,為了改善氧化矽層對比氮化矽層之拋光選擇性或晶圓 15内非均勻性(WIWNU),改善氧化鈽之物理化學性質是必要 的。 部份改善方式係以改變氧化鈽製程中之鍛燒條件為手 段,其中,氧化鈽係以固相法製備。氧化鈽可藉由高溫下 鍛燒碳酸飾而製付,而所製得之氧化鈽依鍛燒條件的不同 20而具備不同的物理化學性質,例如,锻燒溫度或緞燒步驟。 因此,一般認為,改變碳酸鈽之緞燒條件,藉以調整氧化 矽層及氮化矽層之拋光速度,便可控制氧化矽層對比氮化 石夕層之拋光選擇性及晶圓内非均勻性(WIWNU)。 200815288 然而,本發明之發明人實驗結果顯示,氧化矽層對比 氮化矽層之拋光選擇性及晶圓内非均勻性(WIWNU)係受到 碳酸鈽的晶體結構影響,而非碳酸鈽的緞燒條件。意即, 由實驗結果可發現,當氮化矽層及氧化矽層之拋光速度隨 5 著碳酸鈽的緞燒溫度上升而變快時,氧化矽層對比氮化矽 層之拋光選擇性及晶圓内非均勻性(WIWNU)並沒有明顯隨 著碳酸鈽的緞燒溫度而改變,而是明顯受到碳酸鈽晶體結 構之影響。 因此,本發明之發明人認為,碳酸鈽晶體結構係影響 10 氧化矽層對比氮化矽層之拋光選擇性及晶圓内非均勻性 (WIWNU)的最重要因素,其中,碳酸鈽係作為製備氧化鈽 粉末之前驅物。據此,本發明提供一種氧化鈽粉末作為化 學機械拋光漿料之研磨料,其中,此氧化鈽粉末可提供優 異的氧化矽層對比氮化矽層之拋光選擇性及晶圓内非均勻 15 性(WIWNU)。尤其是,本發明之特徵在於,以氧化鈽粉末 作為化學機械拋光之研磨料,且氧化鈽粉末之製備係以具 有六方晶體結構之碳酸鈽作為前驅物。 作為氧化鈽前驅物之碳酸鈽依其所吸附之碳酸官能基 及氫氧基含量而具有不同之晶體結構。因此,即使係利用 20 相同之氧化步驟來製備氧化鈽,其所製得之氧化鈽可能會 因碳酸鈽之晶體結構而有不同之結晶度、比表面積、孔分 佈、硬度或其他類似特性。 例如,以具有六方晶體結構之碳酸鈽作為前驅物所製 得之氧化鈽包含互相微弱鍵結且具有均一尺寸之粒狀物。 200815288 因此’當以此類之氧化鈽作為研磨料時,拋光墊所提供之 機械力會將該些粒狀物碾壓成均一尺寸,以進行需拋光表 面之抛光動作。如此便可使整個晶圓具有優異之晶圓内非 均勻性(WIWNU)。 10 15 20 此外’一旦用於具有較大硬度之氮化矽層的拋光時, 此類氧化鈽更容易被壓碎,因而變成更小的粒狀物,致使 氮化石夕層之拋光速度明顯下降。同時,由於氧化飾具有寬 的孔徑分佈及優異的化學表面活性,因此用於氧化矽層之 拋光時’可使化學拋光速度變快,維持優異之拋光速度, 且同時不會有氧化矽層拋光速度明顯下降之問題。因此, 以本發明之氧化鈽作為研磨料時,氧化石夕層對比氤化矽層 之拋光選擇性可據此增加。 尤其是’於本發明中,當以具有六方晶體結構之碳酸 鈽作為製備氧化鈽之前驅物,且以該氧化#作為化學機械 拋光漿料之研磨料時,氧化矽層對比氮化矽層之拋光選择 性至少可為30,而△ WIWNU(%)可為10%或小於。相較 於以八方晶體結構之碳酸飾或鋼-飾(Ce)碳酸飾作為前驅物 所製備之氧化鈽粉末進行化學機械拋光之結果’上述之拋 光選擇性及晶圓内非均勻性(WIWNU)已明顯有改善。在 此,△ WIWNU(%)=(拋光後晶圓厚度的標準差)/(拋光後晶 圓厚度的平均值)。一般而言,ΔλνπνΝυ愈小表示平坦度 愈高。 此外,本發明所提供之氧化鈽具有低硬度,且容易被 壓碎,因而可解決粗糙粒子所造成之微刮痕問題。 11 200815288 於本發明中,以具有六方晶體結構之碳酸鈽作為前驅 物所製備之氧化鈽粉末可為六方盤狀粒子。 本發明之發明人研究氧化鈽粉末而發現,以固相法製 備之氧化鈽粉末通常維持為作為前驅物之碳酸鈽的形狀及 5 尺寸。本發明之氧化鈽粉末係以具有六方晶體結構之碳酸 鈽作為前驅物而製得,而具有六方晶體結構之碳酸鈽通常 為六方盤狀粒子。因此,本發明之氧化鈽粉末可為六方盤 狀粒子。 因此,本發明之氧化鈽粉末可包括六方盤狀粒子,而 10 該些粒子具有至少一角度為120420°的邊緣,較佳為,120° ±10°。此外,氧化鈽粉末可包括至少50%體積百分比(以總 體積為基準)之六方盤狀粒子。此比例係藉由掃瞄式電子顯 微鏡(SEM)取得多次圖像後而統計算得。 此外,本發明之氧化鈽粉末較佳係具有5nm〜6Onm之晶 15 徑。若晶徑小於5nm,則拋光速度會下降。若晶徑大於 60nm,則拋光表面可能會有嚴重的刮痕。晶徑係利用X光 繞射儀測得氧化鈽主要峰之半高寬後,以謝樂公式 (Scherrer Equation)算得。 本發明之氧化鈽粉末製備方法並無特殊限制,只要製 20 備方法包括緞燒具有六方晶體結構之碳酸鈽即可。 較佳為,本發明之氧化鈽粉末製備方法包括: (a)使具有六方晶體結構之碳酸鈽進行第一次鍛燒;以 及 12 200815288 (b)於溫度高於第一次鍛燒溫度之條件下,使第一次鍛 燒步驟所獲得之粉末進行第二次鍛燒。 步驟(a)係具有六方晶體結構之碳酸鈽進行第一次鍛 燒(熱處理)之步驟,據此,礙酸鈽相變(phase transition)成 5 氧化鈽。 在此,碳酸鈽並無特殊限制,只要碳酸鈽具有六方晶 體結構即可。所屬技術領域之通常知識者所熟悉之碳酸鈽 皆可使用。碳酸鈽可利用該領域通用之習知方式製備。例 如,碳酸鈽可藉由硝酸鈽與碳酸銨間之沉澱反應或於高壓 10 下進行熱液反應(hydrothermal reaction)而製得。 此外,具有六方晶體結構之碳酸鈽的粒子直徑並無特 殊限制。較佳為,碳酸鈽之平均粒子直徑為0.1〜20μπι。若 碳酸鈽之粒子直徑小於Ο.ίμηι,則最終氧化鈽粉末之平均直 徑小於50nm,如此將導致拋光速度明顯下降。若碳酸鈽之 15 粒子直徑大於20μηι,則第二次緞燒步驟所獲得之粉末需歷 經長時間的研碎及分散,而最終氧化鈽粉末則具有寬的粒 徑分佈。 另外,第一次緞燒步驟可以為,於200〜400°C溫度下, 進行6〜100小時之碳酸鈽熱處理。若第一次緞燒溫度小於 20 200°C,則無法完全將碳酸鈽相變成氧化鈽。若第一次緞燒 溫度大於400°C,則最後形成之氧化鈽將具有不理想之大粒 徑或高硬度,如此可能造成氮化矽層之高拋光速度(氧化矽 層對比於氮化石夕層之抛光選擇性下降),或造成抛光表面之 微刮痕問題。 13 200815288 此外,當第一緞燒步驟所獲得之氡化鈽進行步驟(1>)之 第二次緞燒(熱處理)步驟時,氧化鈽晶體會逐漸增加其晶粒 尺寸,而形成具有寬孔徑分布之粉末。因此,當以所製得 之氧化鈽作為研磨料,則氧化矽層對比氮化矽層之拋光選 5 擇性及/或晶圓内非均勻性(WIWNU)可獲改善。 弟二次锻燒(熱處理)步驟可於600〜1200°C的溫度下進 行,較佳為,於800〜900°C的溫度下進行30分鐘至6小時。 若第二次鍛燒溫度超過上述的範圍,則氮化石夕層之拋光速 度可能增加。 10 雖然第一及第二次鍛燒步驟可於空氣下進行,但較佳 為,於氧氣環境下進行鍛燒。此外,可使用習知加熱器進 行鍛燒步驟’例如’箱式爐(box type furnace)、自動輸送式 連縐爐(automatic conveyance type continuous furnace)、或 叙轉疋連績爐(rotary continuous furnace)。 15 此外,於步驟(a)與0>)之間,氧化鈽之製備方法更可選 擇性包括碎壓第一次鍛燒步驟所得粉末之步驟。 此碎壓步驟係藉由研磨所進行之粗糙粒子預處理步 驟’俾使第二次鍛燒步驟中之後續反應可均勻地進行。藉 由碎壓步驟所獲得之氧化鈽平均直徑為0 03〜m。 20 所屬領域之通常知識者所知悉之任何習知碎壓方法皆 可使用,且無特殊限制,較佳為,乾式碎壓方法。此方法 之無限定實例包括喷射研磨法(jet mill process)、盤磨法 (disk mill process)、珠磨法(beads mill process)或其他類似 方法。 200815288 此外,本發明之化學機械拋光漿料包括一研磨料、一 分散劑及水,其中,研磨料為氧化鈽粉末,其係以具有六 方晶體結構之碳酸鈽作為前驅物而製得。 較佳為,每100重量份之漿料使用有0.1〜50重量份之氧 5 化鈽。若研磨料(即氧化鈽粉末)之使用量少於0.1重量份, 則氧化矽層之拋光速度可能明顯下降。若氧化鈽粉末之使 用量多於50重量份,則所製得之漿料可能具有不甚理想之 高黏度,因而於分散及拋光之步驟中,無法作為穩定的漿 料。 10 本發明可使用之分散劑包括非離子聚合物分散劑或離 子聚合物分散劑。非離子聚合物分散劑包括至少一化合 物,其係選自由聚乙烯醇(polyvinyl alcohol,PVA)、乙二醇 (ethylene glycol,EG)、甘油(glycerin) ·、聚乙二醇 (polyethylene glycol,PEG)、聚丙二醇(polypropylene glycol, 15 PPG)以及聚乙烯基n比洛烧酮(polyvinyl pyrrolidone,PVP)所 組成之群組。離子聚合物分散劑包括至少一化合物,其係 選自由聚丙烯酸、聚丙烯酸銨以及聚丙烯馬林酸 (polyacrylmaleicacid)所組成之群組。然而,本發明範圍並 不侷限於此。 20 較佳為,每100重量份之研磨料使用有0.5〜10重量份之 分散劑。若分散劑之使用量少於0.5重量份,則漿料具有較 低可分散性,因而出現快速沉澱的問題。因此,於施予拋 光漿料時,由於沉澱現象(固液分離)的發生,將因而無法均 15 200815288 勻提供研磨料。若分散劑之使用量多於10重量份,則於進 行拋光步驟時,無法達到足夠程度之拋光選擇性。 較佳為,用水混合氧化鈽粉末及分散劑後,將化學機 械拋光漿料滴定至pH值為6〜8。可使用1N氫氧化鉀(KOH) 5 或1N硝酸(HN〇3)進行滴定。 於滴定完成後’較佳是,進行分散穩定步驟,以改善 分散穩定性及化學機械拋光漿料之貯存穩定性。較佳為, 以濕式碎壓/分散法進行分散穩定步驟,其可精細且準確地 控制粒子尺寸。此法包括球磨法(ball mill process)、碾磨法 10 (attrition mill process)或其他類似方法。 在此,於分散步驟所製得之最後化學機械拋光漿料 中,較佳為,氧化鈽粉末之最大粒徑小於3μηι且平均粒子直 徑為50〜lOOOnm。若氧化鈽粉末之平均粒子直徑小於50 nm,則拋光表面之拋光速度會太慢。若氧化鈽粉末之平均 15 粒子直徑大於lOOOnm,則會有氮化矽層之拋光速度增加(拋 光選擇性下降),表面出現微刮痕,或漿料之貯存穩定性低 的問題發生。上述之粒徑係以粒徑分佈測試儀(Horiba LA-910)測得。 本發明之化學機械拋光漿料包括預定含量之研磨料、 20 分散劑及其他添加劑,且更包括絕大含量的水。 此外,本發明之化學機械拋光漿料更可包括改善拋光 品質之添加劑。該添加劑包括:一單體,其具有500以下之 重量平均分子量,且包含氫氧基(OH)及羧基(COOH)之其中 一者或兩者;一線形聚合物,其具有2000〜50000之重量平 16 200815288 均分子量;或一接枝型聚電解質,其具有1000〜20000之重 量平均分子量,但不限於此。 再者,本發明提供一種淺溝槽隔離(shallow trench isolation,STI)方法,其係以上述之化學機械拋光漿料作為 5 拋光漿料。此淺溝槽隔離法可藉由該領域一般使用的步驟 進行。 例如,此淺溝槽隔離法包括以下步驟: (a) 依序堆疊一墊底氧化矽層(Si02) 101及一氮化矽蝕 • 刻停止層102於半導體晶圓100上,形成一光阻圖案,以及 10 藉由光罩,蝕刻部份該光阻圖案,以形成具有預設深度之 溝槽103 ; (b) 沈積一絕緣氧化矽層104,以使該些溝槽嵌埋其中; (c) 拋光(化學機械拋光)該絕緣氧化矽層104,以使該氮 化矽蝕刻停止層102顯露;以及 15 (d)藉由蝕刻,移除該墊底氧化矽層101及該氮化矽蝕 刻停止層102,以及形成一閘極氧化矽層105於該半導體晶 圓上(請參見圖1)。 再者,本發明提供一種方法,其於使用氧化鈽作為研 磨料之化學機械拋光過程中,可控制氧化矽層對比氮化矽 20 層之拋光選擇性及/或晶圓内非均勻性(WIWNU),該氧化鈽 係由具有六方晶體結構之碳酸鈽製得。在此,氧化矽層對 比氮化矽層之拋光選擇性至少可為30,而△ WIWNU(%)可 為10%以下。 17 200815288 【貫施方式】 本發明所詳述之較佳實施例僅供參考,不受限於以下 所述之例子。 實施例1 5 〈氧化鈽粉末之製備〉 首先,將具有六方晶體結構之lKg碳酸鈽粉末(請參見 圖2之X光繞射分析)置於氧化铭掛鋼中,再藉由提供足夠之 空氣,於氧化氣氛下,進行350°C之12小時鍛燒,並藉由喷 射研磨機進行碎壓。於75〇°C下,將碎壓獲得之粉末再進行 10 2小時之锻燒,以獲得淡黃色之氧化鈽粉末。 以X光繞射分析粉末後可發現,碳酸鈽已完全相變成 氧化錦’如圖3所示。 圖5係掃描式電子顯微鏡(S e M)所擷取之氧化鈽粉末 圖像。 15 〈化學機械拋光漿料之製備〉 乂上述I付之〇.5Kg氧化飾粉末、25g分散劑(由Aldrich 所購得之聚丙烯酸)及5L純水,製備氧化鈽分散物。以氨水 滴定該氧化鈽分散物至pH值為7 5,接著,以球磨機進行分 政穩定及粒徑修飾之步驟。在此,該球磨機係使用尺寸為 20 之氧化锆球,而該球磨機係於25〇rpm之速度下操作2小 時。 違氧化鈽分散物係以Ιμπι之濾器過濾,再加入純水, 以提供氧化鈽漿料,其中,每1〇〇重量份之全部混合物中含 有1重里份之氧化鈽。氧化鈽之平均粒子直徑為180nm,而 18 200815288 粒徑分佈約為70〜300nm,其係以粒徑分佈測試儀(Hodba LA-910)測得。 同時,將氫氧化銨加至1%重量百分比之葡萄糖酸水溶 液中,使pH值為7.2,以形成混合葡萄糖酸溶液。 5 接著,使2重量份之混合葡萄糖酸溶液與100重量份之 氧化鈽粉末混合,以提供最後之化學機械拋光漿料。 實施例2 除了於850°C下進行2小時之第二次鍛燒步驟外,其餘 製備氧化鈽粉末及包含該氧化鈽粉末之化學機械拋光漿料 10 的步驟皆與實施例1相同。分散於化學機械拋光漿料之氧化 飾粉末具有176nm之平均粒子直徑及70〜300nm之粒徑分 佈。 實施例3 除了於950°C下進行2小時之第二次鍛燒步驟外,其餘 15 製備氧化鈽粉末及包含該氧化鈽粉末之化學機械拋光漿料 的步驟皆與實施例1相同。分散於化學機械拋光漿料之氧化 飾粉末具有182ηπι之平均粒子直徑及70〜3OOnm之粒控分 佈。 比較例1 20 除了係以具有八方晶體結構(請參見圖2之X光繞射分 析)之碳酸鈽製被氧化鈽粉末外,其餘製備氧化鈽粉末及包 含該氧化鈽粉末之化學機械拋光漿料的步驟皆與實施例1 相同。 氧化鈽之X光繞射(XRD)分析結果如圖3所示。 19 200815288 同時,分散於化學機械拋光漿料之氧化鈽粉末具有 188nm之平均粒子直徑及70〜300nm之粒徑分佈。 比較例2 除了於850°C下進行2小時之第二次鍛燒步驟外,其餘 5 製備氧化鈽粉末及包含該氧化鈽粉末之化學機械拋光漿料 的步驟皆與比較例1相同。分散於化學機械拋光漿料之氧化 鈽粉末具有181nm之平均粒子直徑及70〜300nm之粒徑分 佈。 比較例3 10 除了於950°C下進行2小時之第二次鍛燒步驟外,其餘 製備氧化鈽粉末及包含該氧化鈽粉末之化學機械拋光漿料 的步驟皆與比較例1相同。分散於化學機械拋光漿料之氧化 飾粉末具有184nm之平均粒子直徑及70〜300nm之粒徑分 佈。 15 比較例4 除了係以鑭-鈽(Ce)碳酸鈽(請參見圖2之X光繞射分析) 製備氧化鈽粉末外,其餘製備氧化鈽粉末及包含該氧化鈽 粉末之化學機械拋光漿料的步驟皆與實施例1相同。 氧化鈽之X光繞射(XRD)分析結果如圖3所示。 20 同時,分散於化學機械拋光漿料之氧化鈽粉末具有 183nm之平均粒子直徑及70〜300nm之粒徑分佈。 比較例5 除了於850°C下進行2小時之第二次鍛燒步驟外,其餘 製備氧化鈽粉末及包含該氧化鈽粉末之化學機械拋光漿料 20 200815288 的步驟皆與比較例4相同。分散於化學機械拋光漿料之氧化 鈽粉末具有180nm之平均粒子直徑及70〜300nm之粒徑分 佈。 比較例6 5 除了於950°C下進行2小時之第二次鍛燒步驟外,其餘 製備氧化鈽粉末及包含該氧化鈽粉末之化學機械拋光漿料 的步驟皆與比較例1相同。分散於化學機械拋光漿料之氧化 鈽粉末具有181nm之平均粒子直徑及70〜300nm之粒徑分 馨佈。 10 實驗例1 於下述條件下,使用實施例1〜3及比較例1〜6之化學機 械拋光漿料,進行1分鐘之拋光步驟。徹底清洗基板,並量 測拋光後之厚度變化,以及評估拋光品質Q其結果如下表1 所示。 15 〔拋光條件〕 拋光系統:GNP POLY 400 (GNP Technology) • 拋光墊:聚氨醋墊 平台轉速(Platen speed): 90 rpm 晶圓載具轉速(Carrier speed): 90 rpm 20 壓力:4 psi 漿料流速:lOOml/min 〔拋光物〕 21 200815288 一氧化矽(Si〇2)晶圓,其中,一氧化矽(Si02)層藉由電 漿辅助化學氣相沉積系統(Plasma-Enhanced Chemical
Vapor Deposition,PECVD)沉積於上,其厚度為 7000 埃。 一氮化矽(SiN)晶圓,其中,一氮化矽(SiN)層藉由低壓 5 化學氣相沉積系統(Low Pressure Chemical Vapor Deposition,LPCVD)沉積於上,其厚度為1500埃。 〔評量〕 以光學厚度量測系統’即Nanospec 6100 (Nanometrics Co.),測得拋光後之每一層厚度變化。 10 △均勻性(△ WIWNU)係以均勻性標準偏差法 (Standard Deviation Uniformity,ASTM)算得。 〔表1〕 項目 石炭酸 鈽之 晶體 結構 第二 次鍛 燒 氧化矽 層之拋 光速度 (A/min) 氮化矽 層之拋 光速度 (A/min) Δ WIWNU (%) 拋 光 選 擇 性 實施例1 六方 750 °C 3444 88 5·14 39 實施例2 六方 850 °C 4099 95 2.78 43 實施例3 六方’ 950 °C 4118 124 6.14 33 比較例1 鑭-鈽 750 °C 3677 108 12.60 34 比較例2 鑭-鈽 850 °C 4327 114 12.14 38 比較例3 鑭-鈽 950 °C 4414 184 16.7 24 比較例4 八方 750 °C 3772 130 12.4 29 22 200815288 比較例5 八方 850 °C 4222 324 17.4 13 比較例6 八方 950 °C 4978 963 26.7 5 由上述實驗結果可發現,氧化石夕層及氮化砍層之拋光 速度隨第二次鍛燒溫度上升而增加。尤其是,對於氧化矽 層及氮化矽層之拋光速度而言,碳酸鈽之晶體結構並未造 5 成明顯影響,而碳酸鈽之第二次緞燒溫度卻有所影響。 同時,對於晶圓内非均勻性(WIWNU)而言,碳酸鈽之 ® 第二次緞燒溫度並未造成明顯影響,而碳酸鈽之晶體結構 卻有明顯影響。尤其是,相較於比較例1〜6之化學機械拋光 漿料,本發明實施例1〜3之化學機械拋光漿料之△ WIWNU 10 已獲約4〜10倍之改善,其係採用六方晶體結構之碳酸鈽所 製得之氧化鈽粉末。 此外,於800°C〜900°C之第二次緞燒溫度下,實施例1〜3 之化學機械拋光漿料呈現最小之氮化矽層拋光速度,因而 獲得最大拋光選擇性。如此表示,相較於以不同晶體結構 _ 15 之碳酸鈽所製得之其他氧化錦粉末,以六方晶體結構之碳 酸鈽作為前驅物而製得之氧化鈽粉末作為研磨料時,氧化 矽層對比氮化矽層之拋光選擇性較不受第二次緞燒溫度影 響。 〔工業上應用〕 20 綜上所述,本發明之氧化鈽粉末係以具有六方晶體結 構之碳酸鈽製備。當以該氧化鈽粉末作為化學機械拋光漿 料之研磨料時,則可提供足夠之氧化矽層拋光速度,並明 23 200815288 顯下降氮化矽層之拋光速度,因而可改善氧化矽層對比氮 化矽層之拋光選擇性及晶圓内非均勻性(WIWNU)。 此外,用於製備半導體裝置之較佳平坦化晶圓可改善 裝置的可靠性及產率,以及超小型半導體裝置之積集度。 雖然本發明列舉數個實施例作具體說明,但熟悉該項 技術之人士皆可加以修改、增加或取代,其皆不脫本案之 專利權範圍。 【圖式簡單說明】 10 圖1係一般淺溝槽隔離方法之流程圖。 圖2係本發明實施例及比較例之碳酸鈽X光繞射(XRD)圖, 其碳酸鈽係作為氧化鈽粉末之前驅物。 圖3係本發明實施例及比較例之氧化鈽粉末X光繞射(XRD) 圖。 15 圖4係本發明實施例1之碳酸鈽粉末之掃描式電子顯微鏡 (SEM)圖像。 圖5係本發明實施例1之氧化鈽粉末之掃描式電子顯微鏡 (SEM)圖像。 20 【主要元件符號說明】 100 半導體晶圓 101 墊底氧化矽層 102 氮化秒餘刻停止層 103 溝槽 104 絕緣氧化矽層 105 閘極氧化石夕層 24
Claims (1)
- 200815288 十、申請專利範圍: 1. 一種製備氧化鈽粉末之方法,其係以具有六方晶體 結構之碳酸鈽作為前驅物。 2·如申請專利範圍第1項所述之方法,其中,該氧化 5 鈽粉末係用於化學機械拋光。 3. 如申請專利範圍第1項所述之方法,其包括: (a) 使具有六方晶體結構之碳酸鈽進行第一次鍛燒;以 及 (b) 於溫度高於第一次鍛燒溫度之條件下,使第一次鍛 10 燒步驟所獲得之粉末進行第二次鍛燒。 4. 如申請專利範圍第1項所述之方法,其中,具有六 方晶體結構之該碳酸鈽具有0.1〜20 /z m之平均粒子直徑。 5. 如申請專利範圍第3項所述之方法,其中,該第一 次鍛燒步驟係於200〜400°C之溫度下,進行6〜100小時。 15 6.如申請專利範圍第3項所述之方法,其中,該第二 次鍛燒步驟係於600〜1200°C之温度下,進行30分鐘〜6小時。 7.如申請專利範圍第3項所述之方法,更包括碎壓該 第一次鍛燒步驟所得粉末之步驟,其係於步驟(a)與(b)之間 進行。 20 8. —種氧化鈽粉末,其包括至少50%體積百分比之六 方盤狀粒子,其中,該些六方盤狀粒子具有至少一角度為 120°±20°的邊緣,且該氧化鈽粉末係以具有六方晶體結構之 碳酸鈽作為前驅物而製得。 25 200815288 9. 如申請專利範圍第8項所述之該氧化飾粉末,其係 利用如申請專利範圍第丨項至第7項之任一項所述之方法製 得。 10. 如申請專利範圍第8項所述之該氧化鈽粉末,其包 5 括平均尺寸為5nm〜6nm之晶粒。 11. 如申请專利範圍第8項所述之該氧化鈽粉末,其提 供至少為30之氧化矽層對比氮化矽層之拋光選擇性。 12. 如申請專利範圍第8項所述之該氧化鈽粉末,其提 擊供10%以下之△ WIWNU(晶圓内非均勻性)(0/〇)。 10 13· 一種化學機械拋光漿料,其包括一研磨料,一分散 劑以及水,其中,該研磨料包括如申請專利範圍第8項所述 之該氧化鈽粉末。 14.如申請專利範圍第π項所述之該化學機械拋光漿 料,其包括0.1〜50重量份之該氧化鈽粉末/每1〇〇重量份之該 15漿料,以及〇·5〜重i份之該分散劑/每1〇〇重量份之該研磨 料。 _ 15·如申請專利範圍第13項所述之該化學機械拋光漿 料,其中,該分散劑為非離子聚合物或離子聚合物。 16·如申請專利範圍第13項所述之該化學機械拋光漿 20 料’其中’該分散劑係選自由聚乙稀醇(polyvinyl alcohol, PVA)、乙二醇(ethylene glycol,EG)、甘油(glycerin)、聚乙 二醇(polyethylene glycol,PEG)、聚丙二醇(polypropylene glycol, PPG)以及聚乙烯基比洛烧酮(polyvinyl pyrrolidone, PVP)所組成之群組。 26 200815288 17· —種半導體裝置之淺溝槽隔離(shallow trench isolation,SΤΙ)方法,其係以如申請專利範圍第13項所述之 該化學機械拋光漿料作為拋光漿料。 18. —種控制氧化矽層對比氮化矽層之拋光選擇性及/ 5 或△ WIWNU(晶圓内非均勻性)之方法,其係以如申請專利 範圍第1項至第7項中任一項所述之該氧化鈽粉末作為化學 機械拋光漿料之研磨料,其中,該氧化鈽粉末係以具有六 方晶體結構之碳酸鈽作為前驅物而製得。 19. 如申請專利範圍第18項所述之方法,其中,氧化矽 10 層對比氮化石夕層之該拋光選擇性至少為30。 20. 如申請專利範圍第18項所述之方法,其中,△ WIWNU(晶圓内非均勻性)(%)為10%以下。 _ 27