TW200537611A - Substrate cleaning liquid for semiconductor device and cleaning method - Google Patents
Substrate cleaning liquid for semiconductor device and cleaning method Download PDFInfo
- Publication number
- TW200537611A TW200537611A TW094103725A TW94103725A TW200537611A TW 200537611 A TW200537611 A TW 200537611A TW 094103725 A TW094103725 A TW 094103725A TW 94103725 A TW94103725 A TW 94103725A TW 200537611 A TW200537611 A TW 200537611A
- Authority
- TW
- Taiwan
- Prior art keywords
- substrate
- component
- acid
- semiconductor device
- cleaning solution
- Prior art date
Description
200537611 (1) 九、發明說明 【發明所屬之技術領域】 本發明係有關半導體裝置用基板洗淨液及其洗淨方法 。特別是,有關金屬線路或低介電率(low-k)絕緣膜等附 著於半導體裝置用基板表面之一部份或全面之微粒子 ‘ (Particle)或將有機污染、金屬污染在不腐蝕金屬線路之短 時間內去除之洗淨液,與使用此洗淨液之方法。 i 【先前技術】 微處理器、記憶體、CCD等之半導體裝置,或TFT 液晶等之平面板顯示裝置之製造步驟,係於矽或二氧化矽 (Si 〇2)、玻璃等之基板表面由亞微米〜亞微微米之尺寸 進行形成圖型或形成薄膜,於製造之各步驟減低該基板表 面之微量污染爲極重要之課題。基板表面之污染中亦特別 以顆粒污染、有機物污染及金屬污染由於降低裝置之電氣 φ 特性或收率’進入次步驟前必要極力減低。如此污染之去 除’ 一般以洗淨液進行基板表面之洗淨。要求該洗淨,於 無副作用’短時間再現性優,低成本洗淨,將表面高淸浄 之。因此’該要求水準,近年與裝置之高積體化、低價格 化愈來愈嚴格。 最近之半導體裝置製造步驟,由於裝置之高速化•高 積體化’導入電阻低的新金屬材料(C11等)作爲線路、低 介電率(Low-k)材料作爲層間絕緣膜。又,爲形成線路, 引進適用之 C Μ P ( C h e m i c a 1 M e c h a n i c a 1 Ρ ο 1 i s h i n g )技術。 200537611 (2) 步驟間之洗淨,向來將酸性或鹼性溶液與過氧化氫混合之 RCA洗淨對線路材料產生腐蝕,不能使用。又由於多數 低介電率絕緣膜表面爲疎水性,排斥洗淨液洗淨有困難。 更於CMP步驟後之洗淨,於CMP使用之漿料(硏磨粒子) 有污染線路或低介電率絕緣膜之表面的問題。爲解決此等 之課題,自向來即嘗試種種適應之洗淨技術。 例如,不腐蝕表面之過渡金屬進行去除顆粒污染或金 屬污染,提案含有具特定構造界面活性劑之洗淨液(日本 特開200 1 -2843 08號公報)。 又,爲去除吸附於具有金屬線路之基板的金屬雜質或 顆粒’提案添加分散劑及/或界面活性劑於有機酸化合物 之洗淨液(日本特開200卜007071號公報)。 又’提案將水滴下時與表面之接觸角爲70度以上基板 之接觸角成爲5 0度以下之含脂肪族聚羧酸類與界面活性劑 之洗淨液(日本特開2 0 0 3 - 3 1 8 1 5 0號公報)。 又’提案不腐蝕金屬線路進行去除顆粒或金屬污染之 含有有機酸與配位化劑之洗淨液(專利第3 2 1 9020號公報) 〇 更提案大幅減低表面缺陷將Cu及Cu合金平坦化之 有效率的方法(日本特開2001-156029號公報)。 又’提案不腐蝕基板表面,爲將附著於基板之微粒子 或有機污染去除,於特定的界面活性劑與水,添加鹼或有 機酸之洗淨液(日本特開20 03 -2 8 9 060號)。 200537611 (3) 【發明內容】 [發明所欲解決之課題] 由於半導體裝置之高速化、高積體化,近年急速導入 C u等所謂低電阻金屬線路材料或低介電率材料之新材料 ~ 。爲解決有關使用此等之半導體裝置製造步驟基板洗淨之 諸問題,雖提案如上述之洗淨法,尙無於短時間充分的去 除疎水性之低介電率絕緣膜或容易腐蝕之Cu膜表面上之 p 種種污染之技術,尋求確實的方法。 爲有效果的洗淨疎水性低介電率絕緣膜表面之污染, 活用界面活性劑提高疎水面之濕潤性極爲重要。但是,向 來的技術,由於該界面活性劑於使用超純水之沖洗步驟不 容易去除(特別是於Cu表面),必要長時間的沖洗,成爲 妨碍洗淨短時間化之問題。 本發明係爲解決上述問題,以提供不腐蝕基板表面, 可同時去除顆粒污染、有機污染及金屬污染,且水沖洗性 φ 良好,可於短時間將基板表面高淸淨化之半導體裝置用基 板及洗淨方法爲目的。 [課題解決手段] 本發明爲解決上述問題經深入硏究的結果,發現含有 機酸、有機鹼成分及界面活性劑具特定pH値之洗淨液, 不腐蝕基板表面,不僅同時去除顆粒污染、有機污染及金 屬污染,可提高水沖洗性,於短時間將基板表面高淸淨化 ,完成本明。 -6 - 200537611 (4) 如此,本發明具下述要旨。 1 ·有關半導體裝置用基板洗淨液,含有以下成分(a)、 (b)、(c)、(d),且PH爲1.5以上低於6.5者爲其特徵之半導 體裝置用基板洗淨液。 成分(a):有機酸 成分(b):有機鹼成分 成分(c):界面活性劑 成分(d):水。 2·如上述第1項,上述半導體裝置用基板其表面具有 金屬線路爲其特徵之半導體裝置用基板洗淨液。 3. 如上述第1或第2項,上述半導體裝置用基板係表面 具有低介電率絕緣膜爲其特徵之半導體裝置用基板洗淨液 〇 4. 如上述第1至第3項中之任一項,上述成分(a)爲具有 1個以上羧基之碳數爲1〜10的有機化合物爲其特徵之半導 體裝置用基板洗淨液。 5. 如上述第4項,上述成分(a)爲至少1種選自由醋酸、 丙酸、草酸、琥珀酸、丙二酸、檸檬酸、酒石酸、及蘋果 酸所成群之有機酸爲其特徵之半導體裝置用基板洗淨液。 6. 如上述第1至第5項中之任一項,上述成分(b)爲以下 一般式(1)所示爲其特徵之半導體裝置用基板洗淨液。 (1) (R1)4N + 〇H· 200537611 (5) (但,R1爲氫原子、或羥基、烷氧 可之烷基,4個R1爲全數相同亦可,互 ,全數同時爲氫原子的情形除外)。 7·如上述第6項,上述成分(b)爲具 或碳數1〜4之羥烷基的氫氧化第4級銨爲 置用基板洗淨液。 8·如上述第1至第7項中之任一項, 陰離子系界面活性劑爲其特徵之半導體 〇 9·如上述第8項,其中上述陰離子 少1種選自由烷基磺酸或其鹽、烷基苯 二苯醚二磺酸或其鹽、烷基甲基牛磺酸 酯或其鹽、烷基醚硫酸酯或其鹽、及磺 鹽所成群之陰離子系界面活性劑爲其特 基板洗淨液。 1 〇 ·如上述第1至第9項中之任一項 之含量爲〇·〇5〜10重量%爲其特徵之半導 液。 1 1 ·如上述第1至第1 0項中之任一項 之含量爲〇·〇1〜10重量%爲其特徵之半導 液。 1 2 ·如上述第1至第1 1項中之任一項 之含量爲0.0003〜0.1重量%爲其特徵之」 洗淨液。 基或由鹵所取代亦 爲相異亦可,但是 碳數1〜4之烷基及/ 其特徵之半導體裝 其中上述成分(c)爲 裝置用基板洗淨液 系界面活性劑爲至 磺酸或其鹽、烷基 或其鹽、烷基硫酸 基琥珀酸二酯或其 徵之半導體裝置用 ,其中上述成分(a) 體裝置用基板洗淨 ,其中上述成分(b) 體裝置用基板洗淨 ’其中上述成分(c) 和導體裝置用基板 200537611 (6) 13. 如上述第1至第12項中之任一項,其中上述成分(a) 與(b)之重量比率[成分(a)/成分(b)]爲0.8以上5以下爲其特 徵之半導體裝置用基板洗淨液。 14. 如上述第1至第13項中之任一項,其中上述成分(c) ' 與(b)之重量比率[成分(c)/成分(b)]爲〇·〇1以上0.2以下爲其 * 特徵之半導體裝置用基板洗淨液。 15. 使用含有以下成分(a)、(b)、(c)、(d),且pH爲 ^ 1 · 5以上低於6 · 5之液將半導體用基板洗淨之半導體裝置用 基板之洗淨方法, 成分(a):有機酸 成分(b广·有機鹼成分 成分(c):界面活性劑 成分(d):水。 16. 如上述第15項,上述半導體裝置用基板,於基板 表面具有C u膜與低介電率絕緣膜,且,於c Μ P處理後洗 φ 淨基板爲其特徵之半導體裝置用基板洗淨方法。 1 7·如上述第1 6項’上述CMP處理係由含唑系防鈾劑 硏磨劑進行爲其特徵之半導體裝置用基板洗淨方法。 18.如上述第15項至第17項中之任一項,上述成分(a) 爲具有1個以上羧基之碳數爲1〜;[〇的有機化合物爲其特徵 之半導體裝置用基板洗淨方法。 19·如上述第18項,上述成分(a)爲至少1種選自由醋酸 、丙酸、草酸、琥珀酸、丙二酸、檸檬酸、酒石酸、及蘋 果酸所成群之有機酸爲其特徵之半導體裝置用基板洗淨方 - 9- 200537611 (7) 法。 2 0 ·如上述第1 5項至第1 9項中之任一 爲以下一般式(1)所示爲其特徵之半導體 方法 (R1)4N + OH' (但,R1爲氫原子、或羥基、烷氧基 可之烷基,4個R1爲全數相同亦可,互爲 ,全數同時爲氫原子的情形除外)。 21·如上述第20項,上述成分(b)爲J 及/或碳數1〜4之經院基的氣氧化第4級銨 體裝置用基板洗淨方法。 22·如上述第15項至第21項中之任一: 爲陰離子系界面活性劑爲其特徵之半導體 方法。 2 3.如上述第22項,上述陰離子系界β 種選自由院基磺酸或其鹽、院基苯擴酸或 醚二磺酸或其鹽、烷基甲基牛磺酸或其鹽 其鹽、院基酸硫酸酯或其鹽、及磺基琥拍 成群之陰離子系界面活性劑爲其特徵之半 洗淨方法。 24·如上述第15項至第23項中之任一〕 之含量爲0.0 5〜1 〇重量%爲其特徵之半導體 項,上述成分(b ) 裝置用基板洗淨 (1) 或由鹵所取代亦 相異亦可,但是 I碳數1〜4之烷基 爲其特徵之半導 項,上述成分(C) 裝置用基板洗淨 0活性劑爲至少1 其鹽、烷基二苯 、烷基硫酸酯或 酸二酯或其鹽所 導體裝置用基板 頁,上述成分(a) 裝置用基板洗淨 -10- 200537611 (8) 方法。 25·如上述第15項至第24項中之任一項,上述 之含量爲0.01〜10重量%爲其特徵之半導體裝置用基 方法。 2 6.如上述第15項至第25項中之任一項,上述 之含量爲0.0003〜0.1重量%爲其特徵之半導體裝置 洗淨方法。 27·如上述第15項至第26項中之任一項,上述 與(b)之重量比率[成分(a) /成分(b)]爲0.8以上5以下 徵之半導體裝置用基板洗淨方法。 2 8 .如上述第1 5項至第2 7項中之任一項,上述 與(b)之重量比率[成分(c)/成分(b)]爲0.01以上0.2以 特徵之半導體裝置用基板洗淨方法。 [發明之效果] 依本發明,於矽等之半導體材料、在其表面之 或全面具有氮化矽、二氧化矽、玻璃、低介電率材 絕緣材料、過渡金屬或過渡金屬化合物等之半導體 基板’不腐蝕基板表面,不僅同時去除顆粒污染、 染及金屬污染,且由於水沖洗性良好,於短時間將 面高淸淨化,本發明係於半導體裝置或顯示器裝置 造步驟作爲污染半導體用基板之洗淨技術,於工業 有用。又,水沖洗性良好,於洗淨後之基板以水沖 洗淨液或微粒子、有機污染、金屬污染容易由基板 成分(b) :板洗淨 成分(Ο 用基板 成分〇) 爲其特 成分(C) 下爲其 一部份 料等之 裝置用 有機污 基板表 等之製 上非常 洗時, 表面去 -11 - 200537611
除。 [用以實施發明之最佳型態] 以下詳細說明本發明之實施型態。 本發明之洗淨液爲含作爲成分(a)之有機酸、作爲成 分(b)之有機鹼成分、作爲成分(c)之界面活性劑、及作爲 成分(d)之水,且pH爲1.5以上低於6.5者。 於本發明成分(a)之有機酸爲在水中顯示酸性(PH<7) 之有機化合物之總稱,具有羧基(-COOH)、磺基(-S03H) 、苯酚性羥基(ArOH : Ar爲苯基等之芳基)、毓基(-SH)等 之酸性官能基者。所使用之有機酸無特別限制,官能基以 具有羧基爲理想。更理想爲具有1以上羧基之碳數1〜1 0之 有機化合物。更理想爲碳數1〜8者,其中亦以碳數1〜6者爲 理想。作爲羧酸以具有1羧基者即可,單羧酸、二羧酸、 三羧酸等可適用。但是通常,羧基爲5以下者。具體的例 可列舉如甲酸、醋酸、丙酸、丁酸、異丁酸、戊酸、乙基 甲基醋酸、三甲基醋酸、草酸、琥珀酸、丙二酸、檸檬酸 、酒石酸、蘋果酸等。理想爲醋酸、丙酸、草酸、琥珀酸 、丙二酸、檸檬酸、酒石酸、蘋果酸,更理想爲醋酸、草 酸、檸檬酸。此等有機酸成分,單獨使用1種亦可,2種以 上以任意比例倂用亦可。 於本發明之洗淨液中成分(a)之含有量,爲能充分進 行去除污染,相對於洗淨液通常爲0.0 1重量%以上,理想 爲0.05重量%以上,更理想爲0.1重量%以上。但是,重視 不腐蝕基板表面或經濟者,成分(a)之含有量以30重量%以 -12- 200537611 (10) 下,理想爲1〇重量%以下’更理想爲2重量%以下。?辰度過 高時亦不能得到更好的效果。 於本發明,於本發明成分(b)之有機酸爲在水中顯示 酸性(p Η > 7 )之有機化合物之總稱,所使用之有機鹼無特別 限制,可列舉如以下一般式(I)所示之氫氧化第4級銨,或 胺類、胺基醇類等。 (R1)4N + OH- (I) (但,R1爲氫原子、或羥基、烷氧基或由鹵所取代亦 可之烷基,4個R1爲全數相同亦可,互爲相異亦可,但是 ,全數同時爲氫原子的情形者除外)。 作爲氫氧化第4級銨,於上述一般式(I),R1爲羥基、 烷氧基、或爲鹵所取代之碳數1〜4之烷基、特別以碳數1〜4 之烷基及/或碳數1〜4之羥烷基者爲理想。R1之烷基爲甲基 、乙基、丙基、丁基等之碳數1〜4之低級院基’經院基如 羥甲基、羥乙基、羥丙基、羥丁基等之碳數1〜4之羥烷基 〇 又’胺類如三乙胺、乙烯二胺等,胺基醇如單乙醇胺 、二乙醇胺、三甲醇胺等。 理想的成分(b)爲一般式(I)所示之氫氧化第4級銨。該 氫氧化第4級銨之具體例,可列舉如四甲基銨氫氧化物 (TM A H)、四乙基銨氫氧化物、三甲基(羥乙基)銨氫氧化 物(通稱:膽鹼)、三乙基(羥乙基)銨氫氧化物等。 -13- 200537611 (11) 上述(b)之有機鹼成分中亦以洗淨效果、金屬殘留少 ,由經濟性、洗淨液安定性等之理由,有機鹼成分以四甲 基銨氫氧化物(TMAH)、三甲基(羥乙基)銨氫氧化物(通稱 :膽鹼)等特別理想。此等之有機鹼成分,可單獨使用1種 ,2種以上以任意比例倂用亦可。又,氨與金屬線路所使 用之銅容易形成配位化合物,成爲腐蝕之原因不理想。 於本發明洗淨液相關成分(b)之含有量,爲充分良好 之水沖洗性,相對洗淨液通常爲〇.〇〇1重量%以上,理想爲 0.01重量%以上,更理想爲0.05重量%以上。但是,重視不 腐蝕基板表面或經濟者,成分(b)之含有量以30重量%以下 ,理想爲10重量%以下,更理想爲2重量%以下。濃度過高 時亦不能得到更好的效果。 於本發明,作爲成分(c)使用之界面活性劑無特別限 制,可列舉如陰離子界面活性劑、無離子界面活性劑、陽 離子界面活性劑、兩性界面活性劑。 陰離子界面活性劑,可列舉如烷基磺酸或其鹽、烷基 苯磺酸或其鹽、烷基甲基牛磺酸或其鹽、烷基硫酸酯或其 鹽、烷基醚硫酸酯或其鹽、磺基琥珀酸二酯或其鹽等。無 離子界面活性劑可列舉如聚氧基聚環氧乙烷烷醚、聚環氧 乙烷脂肪酸酯等之環氧乙烷型界面活性劑。陽離子界面活 性劑可列舉如胺鹽型界面活性劑或第4級銨鹽型界面活性 劑。兩性界面活性劑可列舉如胺基酸型兩性界面活性劑或 甜菜鹼型兩性界面活性劑。其中亦以使用陰離子系界面活 性劑爲理想。更理想爲碳數8〜1 2之烷基苯磺酸或其鹽、碳 -14- 200537611 (12) 數8〜12之烷基二苯醚二磺酸或其鹽、碳數8〜12之烷基甲基 牛磺酸或其鹽、碳酸8〜1 2之磺基琥珀酸二酯或其鹽。此等 之界面活性劑成分,可單獨使用1種,2種以上以任意比例 倂用亦可。 有關本發明洗淨液中成分(c)之含有量,爲充分得到 顆粒污染去除性能,相對於洗淨液通常爲0.000 1重量%以 上,理想爲0.0003重量%以上,更理想爲0.001重量%以上 。但是,過度抑制起泡或重視減輕廢液處理之負荷,成分 (c)之含有量通常爲1重量%以下,理想爲0.1重量%以下, 更理想爲〇 . 0 5重量%以下。濃度過高時亦不能得到更好的 效果。 又,作爲成分(Ο的界面活性劑,又,於通常市售之 型態通常有1〜數千重量ppm程度之Na、K、Fe等金屬等 金屬雜質的情形,此時,成分(c)成爲金屬污染源。因此 ,於作爲成分(c)使用之界面活性劑含有金屬雜質時,將 各各金屬雜質之含有量純化至通常爲10PPm以下,理想爲 1 ppm,更理想爲0.3 ppm以下使用爲理想。該純化方法, 例如將界面活性劑溶解於水後’流經離子交換樹脂,由樹 脂捕捉金屬雜質之方法爲合適。使用如此純化之成分(c) 時,可得到金屬雜質含有量極爲減低之洗淨液。 於本發明使用水作爲(d)成分。用水不能得到高淸淨 基板表面時,通常使用脫離子水’以使用超純水爲理想。 又,由電分解所得之電解離子水’或亦可使用溶存氫氣之 氫水等。 -15 - 200537611 (13) 本發明洗淨液之ρ Η,爲抑制腐鈾基板表面以i . 5以上 ,理想爲2以上,更理想爲3以上。但爲能充分去除金屬污 染,p Η爲6.5以下,理想爲6以下,更理想爲5以下。 於本發明之洗淨液,成分(a)之有機酸與成分(b)之有 % 機鹼成分之重量比率[成分(a)/成分(b)] ’爲能充分去除金 屬污染以0.8以上爲理想,更理想爲1以上。但是,重視基 板表面之腐鈾時,該重量比率以5以下爲理想,更理想爲4 B 以下。重量比率過大時不能得到更好的效果。 又,於發明之洗淨液,有機鹼具有促進基板表面之界 面活性劑之脫離效果,爲充分得到提高水沖洗性效果與界 面活性劑比較以含較多有機鹼成分爲理想。所以成分(c) 之界面活性劑與成分(b)之有機鹼成分之重量比率[成分 (c)/成分(b)]以0.2以下爲理想,更理想爲〇·15以下,由於 有機鹼過多時效果亦不會更好,重視經濟時,該重量比率 以0.01以上爲理想,更理想爲〇.〇5以上者。 φ 如此含有成分(a)〜(d)之本發明洗淨液,洗淨液中之金 屬雜質中,至少Na、K、Al、Ca、Fe、Cu、Pb、Zn之各 各的含有量爲20ppb以下,其中亦以5 ppb,特別以0.1 ppb以下者,可防止因洗淨時半導體裝置用基板之金屬污 染爲理想。特別是,此等之金屬雜質之合計含有量以 20ppb以下爲理想,其中亦以5 ppb以下,特別以O.lppb 以下爲理想。 於本發明洗淨液,成分U)〜(d)以外’更依必要可含有 配位化劑。配位化劑,可減低基板表面金屬污染之效果。 -16- 200537611 (14) 作爲配位化劑,可使用向來公知之任意者。配位化劑之種 類,依基板表面之污染水準、金屬種類、基板表面要求之 淸淨度水準、配位化劑成本、化學安定性等之總合判斷而 選擇即可,例如可列舉如以下(1)〜(4)所示者。 (1) 具有供體(donor)原子之氮與羧基及/或膦酸基之化 合物:例如,可列舉如甘氨酸等之氨基酸;亞胺基2醋酸 、硝基3醋酸、乙撐二胺4醋酸[ETDA]、反-1,2-二胺基環 己烷4醋酸[CyDTA]、二乙撐三胺5醋酸[DPTA]、三乙撐四 胺6醋酸[TTHA]等之含氮羧酸類;乙撐二胺四(甲撐膦酸 )[ED 丁 PO]、硝基三(甲撐膦酸)[ΝΤΡΟ]、丙撐二胺四(甲撐 膦酸)[PDTMP]等之含氮膦酸類等。 (2) 具有芳香族烴環且與構成芳香族烴、環之碳原子直 接結合之ΟΗ基及/或具有2個以上0_基之化合物:例如隣 苯二酚、間苯二酚、間苯二酚-3,5-二磺酸鈉等之酚類,其 衍生物等。 (3 )倂持上述(1 )、( 2 )之構造之化合物:例如以下(3 - 1 ) 、(3-2)。 (3-1)乙撐二胺二隣羥基苯醋酸[EDDHA]或其衍生物: 可舉例如乙撐二胺二鄰羥苯醋酸[EDDHA]、乙撐二胺_ Ν,Ν’-雙[(2-羥基·5 -甲苯)醋酸][EDDHMA]、乙撐二胺-N,N’-雙[(2-羥基-5-氯苯)醋酸][EDDHCA]、乙撐二胺-N,N’-雙[(2-羥基-5磺苯)醋酸][EDDHSA]等之芳香族含羧 酸類·,乙撐二胺·Ν,Ν,-雙[(2-羥基·5-甲苯)膦酸、乙撐二 胺-Ν,Ν’-雙[(2-羥基-5-膦苯)磺酸等之芳香族含氮膦酸類。 -17- 200537611 (15) (3-2)1^,1^’-雙(2-羥苄)乙撐二胺->^川’-2醋酸[1^£0]或 其衍生物:N,N’-雙(2-羥苄)乙撐二胺-N,N’-2醋酸[HBED] 、N,N’-雙(2-羥基-5-甲苄)乙撐二胺-N,N’-2醋酸[HMBED] 、N,N’-雙(2-羥基-5-氯苄)乙撐二胺-N,N’-2醋酸等。 (4)其他:可列舉如乙撐二胺、8-喹啉酚、〇-菲繞啉等 之胺類;甲酸、醋酸、草酸、酒石酸等之羧酸類;氫氫酸 、鹽酸、溴化氫、碘化氫之鹵化氫、其鹽;磷酸、縮合磷 酸等之羰基酸類、此等之鹽等。 上述配位化劑,以酸的型態使用亦可,以銨鹽等之鹽 型態使用亦可。 上述配位化劑中,依洗淨效果、化學安定性等之理由 ,亦以乙撐二胺4醋酸[ETDA]、二乙撐三胺5醋酸[DPTA] 等含氮羧酸類;乙撐二胺四(甲撐膦酸)[ED TP 0]、丙撐二 胺四(甲撐膦酸)[PDTMP]等之含氮膦酸類;乙撐二胺二隣 羥基苯醋酸[EDDHA]或其衍生物;N,N’-雙(2-羥苄)乙撐二 胺-N,N’-2醋酸[HBED]等爲理想。其中依洗淨效果觀點亦 以乙撐二胺二隣羥基苯醋酸[EDDHA]、乙撐二胺-N,N5-雙 [(2 -羥基-5 -甲苯)醋酸][EDDHMA]、二乙撐三胺5醋酸 [DPTA]、乙撐二胺4醋酸[ETDA]、丙撐二胺四(甲撐膦酸 )[PDTMP]爲理想。 上述配位化劑可單獨使用,亦可2種以上以任意比例 倂用。 本發明之洗淨液中配位化劑之濃度,依洗淨對象之半 導體裝置用基板之污染金屬雜質之種類與量、基板表面要 -18- 200537611 (16) 求之淸淨度水準任意選擇即可。爲充分得到去除污染或防 止附著效果,通常爲1 P P m以上、理想爲5 P P m以上、更理 想爲lOppm以上者。但是,重視爲減少於基板表面附著配 位劑經表面處理後殘留之慮或經濟面,配位化劑之濃度, % 通常爲lOOOOppm以下、理想爲lOOOppm以下,更理想爲 200ppm 以下 0 又,配位化劑,通常販賣的配位化劑含有1〜數千ppm φ 程度之Fe、Al、Zn等金屬雜質,在初期與配位化劑安定 的形成配位化合物存在,洗淨液長時間使用時配位化劑分 解’由配位化劑遊離,附著於洗淨對象之基板表面。因此 於本發明使用配位化劑,以預先純化再使用爲理想,由純 化各各的金屬雜質含有量,通常爲5ppm以下,理想爲 1 ppm以下,更理想以成爲〇.lppm以下者爲理想。其純化 方法例如,於酸性或鹼性溶液溶解配位化劑後,將不溶性 雜質過濾分離取出,再以中和析出結晶將該結晶與液分離 φ 的方法爲合適。 又’本發明之洗淨液,在不損及其性能之範圍,可含 _ ί壬思tt例之其他成分。其他成分可列舉如含硫有機化合 物(2-疏基噻唑、2-锍基咪唑啉、厂酼基乙醇、硫代甘油等 )、含氮有機化合物(苯井三唑、3-胺基三唑、N(R2)3(R2爲 相互爲同一或相異亦可之碳數1〜4之烷基及/或碳數1〜4之 經院基)、尿素、硫代尿素等)、水溶性聚合物(聚乙二醇 、聚乙燒醇等)、烷醇系化合物(R3OH(R3爲碳數1〜4之烷基 )等之防鈾劑、硫酸、鹽酸、甲烷磺酸等之酸、胼等之還 -19-
200537611 (17) 元劑、氫、氬、氣等之溶存氣體、氟酸、 緩衝氟酸)等之乾蝕刻後堅固附著之聚合牛 除效果的促進劑等。 於本發明之洗淨液所含有之其他成分瓦 氫、臭氣、氧等之氧化劑。在半導體裝置用 驟,洗淨無氧化膜之矽(裸矽)基板表面時, 合、可抑制因基板表面蝕刻之表面荒亂爲理 洗淨液含有過氧化氫等時,洗淨液中之過孽 常爲〇.〇1重量%以上,理想爲0.1重量%以上 %以下,理想爲1重量%以下。 可是,欲洗淨之基板表面,與過氧化氫 金屬材料所成之半導體裝置有露出線路或裝 形。如此之金屬材料,例如,C u或W等之 渡金屬化合物。此時,於洗淨時所使用之洗 以不含過氧化氫爲理想。本發明之洗淨; CPM相同,實質上不含過氧化氫,對此等 發生不良影響,顯示充分之洗淨性能。 又’於本發明之洗淨液,「實質上不含 係意味由過氧化氫對須洗淨基板上之材料, 等之線路材料或電極材料,及低介電率膜, 變質等之不良影響。即,意味此等之材料爲 ’具充分機能作爲線路或電極等。爲此,於 液不含過氧化氫,含有過氧化氫時其含有量 爲理想。其含有量例如爲1 〇 ρ ρ ηι以下,理范 氟化銨、BHF( 等可期待其去 ‘列舉如過氧化 基板之洗淨步 由氧化劑之配 想。於本發明 化氫濃度,通 ,通常爲5重量 反應由溶解之 置元件電極情 過渡金屬或過 淨液,實質上 夜,與向來之 之金屬材料不 有過氧化氫」 例如Cii或W 不產生腐蝕或 半導體裝置時 本發明之洗淨 以抑制於少量 丨爲1 p p m以下 - 20- 200537611 (18) ,更理想爲lOppb以下者。 本發明之洗淨液之調製方法,依向來公知之方法即可 。本發明之構成成分(有機酸、有機鹼成分,界面活性劑 ,水,因應必要之配位化劑等,其他成分)之中,任何2成 分或3成分預先配合’其後將殘餘之成分混合亦可,一次 將全部混合亦可。 本發明之洗淨液,使用於金屬污染或顆粒污染爲問題 之半導體、玻璃、金屬、陶瓷、樹脂、磁性物、超導體等 之半導體裝置用基板表面之洗淨。特別是,製造要求高淸 淨之基板表面’半導體元件或顯示器裝置用等之半導體裝 置用基板之步驟’適合於半導體裝置用基板表面之洗淨使 用。此等基板之表面上,存在線路、電極等亦可。作爲線 路或電極之材料,可列舉如Si、Ge、GaAs等之半導體材 料;S i Ο2、氮化矽、玻璃、低介電率材料、氧化鋁、過渡 金屬氧化物(氧化鈦、氧化鉅、氧化飴、氧化鉻等)、(B a 、S〇Ti 02(BST)、聚醯亞胺、有機熱硬化性樹脂等之絕緣 材料;W、Cu、A1等之金屬或此等之合金、矽化物、氮 化物等。此處低介電率材料,係比介電率爲3 . 5以下材料 之總稱。Si02之比介電率爲3.8〜3.9。 特別是,本發明之洗淨液,不腐蝕金屬表面,且容易 將殘留於金屬表面之界面活性劑,可在短時間沖洗去除, 由於產量可提高,適合使用於表面具有過渡金屬或過渡金 屬化合物之半導體裝置用基板之洗淨。此處過渡金屬可列 舉如 W、Cu、Ti、Cr、Co、Zr、Hf、Mo、Ru、Au、Pt、 -21 - 200537611 (19) A g等,過渡金屬化合物,可列舉如此等金過渡金屬之氮 化物、氧化物、矽化物等。其中,以W及/或Cu爲理想 〇 又,本發明之洗淨液,亦適合使用於表面具有低介電 % 率層間絕緣膜之半導體裝置用基板之洗淨。低介電率材料 ',可列舉如聚醯亞胺、BCB(苯并環丁烯)、Flare( Honeywell 公司)、SiLK(Dow Chemical 公司)等之有機聚 φ 合物材料或 FSG(氟化矽玻璃)等之無機聚合物材料、 BLACK DIAMOND(Applied Materials 公司)、Aurora(日 本 ASM公司)等之 SiOC系材料。其中,Flare、SiLK、 BLACK DIAMOND、Aurora等疎水性強之低介電率絕緣膜 使用本洗淨液時,基板表面之污染亦可於短時間去除。 進行表面具有Cii或低介電率絕緣膜之基板之洗淨步 驟,特別是,對 Cu 膜進行 CMP(Chemical Mechanical Polishing )後之洗淨步驟,列舉如線路上之層間絕緣膜由 φ 乾蝕刻開控孔穴後之洗淨步驟,適合使用本發明之洗淨液 可發揮上述效果。 CMP步騾,係使用硏磨劑將基板於墊上磨擦進行硏 磨。硏磨劑成分含硏磨粒子、氧化劑、分散劑或其他添加 劑。硏磨粒子列舉如膠質二氧化矽(S i Ο 2 )、煙霧狀二氧化 矽(Si〇2)、氧化鋁(Al2〇3)、二氧化鈽(Ce02)等。氧化劑可 列舉如過氫化氫、過硫酸銨、硝酸鐵、碘酸鉀等。分散劑 列舉如界面活性劑、KOH、氨、胺等。特別是,Cu膜之 C Μ P硏磨,C u膜容易腐蝕,加入防蝕劑爲重要者,防蝕 -22 - 200537611 (20) 劑中亦以使用防蝕效果高之重氮系防蝕劑爲理3。重氮係 含2個以上雜原子之5員環芳香族化合物,雜原子至少1個 爲氮原子之化合物之總稱。氮原子以外之雜原子,熟知者 如氧或硫。僅氮之複數環可列舉如二重氮系或三重.氮系、 四重氮系。氮與氧之複數環列舉如噁唑系或異噁唑系、噁 二唑系,氮與硫之複數環列舉如噻唑系、異噻唑系、噻二 唑系。其中特別以使用防蝕效果優之苯并三唑(BTA)系之 B 防蝕劑爲理想。又,硏磨劑依其組成有酸性、中性、鹼性 之種種pH物,可因應目的而選擇。 本發明之洗淨液,適用於該含防蝕劑之硏磨劑硏磨後 之表面,此等防蝕劑來源之污染可有效果的去除的觀點爲 極優良。即,硏磨劑中存在於此等防蝕劑時,可抑制C u 膜表面之腐蝕,另外一面與硏磨時溶出之Cu子反應,產 生大量不溶性析出物。本發明之洗淨液,可將如此之析出 物有效率的溶解去除。又,於金屬表面容易殘留之界面活 φ 性劑,可於短時間沖洗去除,可提高產量。特別是,適合 使用於加入噁唑系防蝕劑之硏磨劑,將Cu膜與低介電率 絕緣膜共存之表面以CMP處理後之半導體裝置用基板之 洗淨。 本發明之洗淨方法,係將本發明之洗淨液直接與基板 接觸之方法進行。洗淨液對基板之接觸方法,列舉如於滿 裝洗淨液之洗淨槽將基板浸漬之浸漬方式,由噴嘴將洗淨 液流於基板上再高速旋轉之旋轉方式,於基板上噴霧洗淨 之噴霧方式等。爲進行此洗淨之裝置,有將收容於卡匣之 -23- 200537611 (21) 複數片基板同時洗淨之批次.方式洗淨裝置,井 夾具洗淨之葉片式洗淨裝置等。 本發明之洗淨液可適用於上述之任一方法 有效率的去除污染觀點,以使用旋轉方式或噴 % 淨爲理想。期望縮短洗淨時間,削減洗淨液使 片式洗淨裝置可解決此問題爲理想。 又,本發明之洗淨方法,由物理力之洗淨 φ 是倂用使用洗淨刷之擦拭洗淨或頻率0.5MHz 波洗淨,顆粒污染之去除性更爲提高,亦關聯 縮短爲理想。特別是,CMP後之洗淨,以使 刷子進行擦拭洗淨爲理想。樹脂刷材質之選擇 擇,例如以使用 PVA(聚乙烯醇)爲理想。又, 淨之前及/或後,由水之電分解所得之電解離 存氫之氫水組合洗淨亦可。 洗淨液之溫度,通常爲室溫,在不損及性 A 加溫至40〜70°C程度。 【實施方式】 以下舉實施例及比較例更具體的說明本發 越其要旨本發明不限於實施例。 又,於表1〜表6,金屬雜質之濃度,任一 淨劑中所含之Na、Mg、A卜K、Ca、Cu、Pb 。又,下述縮寫記號各意味如下。再者,於彥 性之單位爲濃度X 1 〇 1 9 a t 〇 m s / c m 2。 I 1基板挾於 。由短時間 霧方式之洗 用量使用葉 方式,特別 以上之超音 洗淨時間之 用塑膠製之 ,得任意選 由本發明洗 子水,或溶 能範圍,可 明,在不超 者均表示洗 > Zn各濃度 t 5金屬去除 -24- 200537611 (22) T M A Η :四甲基銨氫氧化物 N(Et)3 :三乙胺 膽鹼:三甲基(羥乙基)銨氫氧化物 DBS :十二烷基二苯磺酸 DPDSA :十二烷基二苯醚二磺酸銨鹽 MMTA : N-十四烷醯基甲磺酸銨 M S A :甲烷磺酸 IPA :異丙醇 <實施例1〜12及比較例1〜6> (由括板式洗淨之顆粒污染的洗淨性評價) 將附Cu膜的8吋矽基板,以加入苯并三唑系 CMP用漿料(酸性,含Si02粒子)硏磨1分鐘後,進 水硏磨。將該CMP硏磨後的基板,使用表1所示配 淨液,由 Multi spinner(曰本(股)Kaijio 製「KSSP. ,使用PVA製之刷子進行刷括洗淨,去除顆粒。 液之洗淨於室溫實施3 0秒鐘,其後,將基板以超純 1 〇秒或3 0秒,旋轉乾燥,得到洗淨後的基板。 其後,使用雷射表面檢查裝置(日本日立電子 司製「LS-6600」測定附著於基板表面之顆粒數(粒 // m以上)’結果如表1所不。 表1,知悉由本發明的半導體基板用基板洗淨 防止以添加苯并三唑系防蝕劑CMP用漿料(酸性 Si〇2粒子)硏磨後的Cu膜上的顆粒污染,可高淸淨 防蝕劑 行17秒 合的洗 201」) 以洗淨 水沖洗 工程公 徑 0 · 3 5 液,可 ,含有 的洗淨 -25- 200537611 (23) ,且沖洗時間亦短縮至1 0秒。 又,成分(a)之有機酸使用醋酸與草酸時,亦可提高 沖洗性,確認可得到同樣的效果。 <實施例13〜14> (由括板式洗淨之顆粒污染的洗淨性評價) 將附 Cu膜的8吋矽基板,以加入苯并三唑系防蝕劑 CMP用漿料(鹼性,含Si02粒子)硏磨1分鐘後,進行17秒 水硏磨。將該CMP硏磨後的基板,使用表2所示配合的洗 淨液,由 Multi spinner(日本(股)Kaijio 製「KSSP-201」) ,使用 PVA製之刷子進行刷括洗淨,去除顆粒。以洗淨 液之洗淨於室溫實施3 0秒鐘,其後,將基板以超純水沖洗 3 0秒,旋轉乾燥,得到洗淨後的基板。 其後,使用雷射表面檢查裝置(日本日立電子工程公 司製「LS-6600」測定附著於基板表面之顆粒數(粒徑0.35 # m以上),結果如表2所示。 如表2,Cii膜上之顆粒殘留數非常少,知悉由本發明 的半導體基板用基板洗淨液,可防止以添加苯并三唑系防 蝕劑CMP用漿料(鹼性,含有Si02粒子)硏磨後的Cu膜上 的顆粒污染,可高淸淨的洗淨。 <實施例1 5〜1 6> (由括板式洗淨之顆粒污染的洗淨性評價) 將附C11膜的8吋矽基板,以加入苯并三唑系防蝕劑 -26- 200537611 (24) CMP用漿料(酸性,含Si02粒子)硏磨1分鐘後,不進行水 硏磨將硏磨終了之基板取出。硏磨墊上殘留Cu污染之狀 態,接著將附有 Low-k膜(BLACK DIAMOND)膜之8吋矽 基板,以加入苯并三唑系防蝕劑CMP用漿料(酸性,含 Si02粒子)硏磨1分鐘後,進行17秒水硏磨。該CMP硏磨 後之附有Low-k膜(BLACK DIAMOND)膜之基板,使用表 3所示配合的洗淨液,由Multi spinner(日本(股)Kaijio製 「KSSP-201」),使用PVA製之刷子進行刷括洗淨,去除 顆粒。以洗淨液之洗淨於室溫實施3 0秒鐘,其後,將基板 以超純水沖洗3 0秒或60秒,旋轉乾燥,得到洗淨後的基板 〇 其後,使用雷射表面檢查裝置(日本日立電子工程公 司製「LS-6600」測定附著於基板表面之顆粒數(粒徑〇.2 // in以上),結果如表3所示。 如表3,知悉由本發明的半導體基板用基板洗淨液, 亦可防止通常不易洗淨之Low-k膜以添加苯并三唑系防蝕 劑CMP用漿料(酸性,含有Si02粒子)硏磨後的顆粒污染 ,可高淸淨的洗淨。 <實施例17〜18> (由括板式洗淨之顆粒污染的洗淨性評價) 將附C u膜的8吋矽基板,以加入苯并三唑系防蝕劑 CMP用漿料(鹼性,含Si02粒子)硏磨1分鐘後,不進行水 硏磨將硏磨終了之基板取出。硏磨墊上殘留C u污染之狀 -27- 200537611 (25) 態,接著將附有Low-k膜(BLACK DIAMOND)膜之8吋矽 基板,以加入苯并三唑系防蝕劑CMP用漿料(鹼性,含 Si02粒子)硏磨1分鐘後,進行17秒水硏磨。該CMP硏磨 後之附有Low-k膜(BLACK DIAMOND)膜之基板,使用表 4所不配合的洗淨液,由Multi spinner(日本(股)Kaijio製 「KSSP-201」),使用PVA製之刷子進行刷括洗淨,去除 顆粒。以洗淨液之洗淨於室溫實施3 0秒鐘,其後,將基板 以超純水沖洗3 0秒,旋轉乾燥,得到洗淨後的基板。 其後,使用雷射表面檢查裝置(日本日立電子工程公 司製「LS-6600」測定附著於基板表面之顆粒數(粒徑0.2 # m以上),結果如表4所示。 如表4,知悉由本發明的半導體基板用基板洗淨液, 亦可防止通常不易洗淨之Low-k膜以添加苯并三唑系防蝕 劑CMP用漿料(鹼性,含有Si02粒子)硏磨後的顆粒污染 ,可高淸淨的洗淨。 由表1〜4,知悉由本發明的半導體基板用基板洗淨液 ,不論對Cu膜及Low-k膜之任一者,以添加苯并三唑系 防蝕劑CMP用漿料(酸性,含有Si02粒子)及添加苯并三 唑系防鈾劑C Μ P用漿料(鹼性,含有S i Ο 2粒子)之任一者 硏磨後的顆粒污染,均可高淸淨的洗淨。又知悉本發明的 半導體裝置用基板洗淨液,沖洗時間亦可比向來縮短。 <實施例1 9 > (由括板式洗淨之顆粒污染的洗淨性評價) -28- 200537611 (26) 將附Cii膜的8吋矽基板,以加入苯并三唑系防蝕劑 CMP用漿料(酸性,含Si02粒子)硏磨1分鐘後,不進行水 硏磨將硏磨終了之基板取出。硏磨墊上殘留Cu污染之狀 態,接著將附有TEOS(四乙氧基矽烷)膜之8吋矽基板,以 加入苯并三唑系防蝕劑CMP用漿料(酸性,含Si02粒子) • 硏磨1分鐘後,進行17秒水硏磨。該CMP硏磨後之附有 TEOS膜基板使用表5所示洗淨液,由Multi spinner(日本( φ 股)Kaijio製「KSSP-201」),使用PVA製之刷子進行刷 括洗淨,去除顆粒。以洗淨液之洗淨於室溫實施3 0秒鐘, 其後,將基板以超純水沖洗6 0秒,旋轉乾燥,得到洗淨後 的基板。 該基板上之殘留污染金屬(F e、C u),依以下的方法分 析,結果如表5所示。 (殘留污染金屬之分析方法) ^ 將基板表面之金屬,以含有0.1重量%氟酸與1重量% 過氧化氫之水溶液,將基板處理而回收,使用感應結合電 漿質量分析計(ICP-MS)測定該金屬量,換算爲基板表面之 金屬濃度(X 1 〇1Gatoms/cm2)。 如表5 ’知悉依本發明之半導體裝置用基板洗淨液, 可防止金屬污染,可高淸淨洗淨。 <實施例20及比較例7> (Cii膜蝕刻率之評價) -29- 200537611 (27) 將附Cu膜的8吋矽基板片((1.5 cm x 2cm),以表6所示 之洗淨液浸漬3小時。浸漬後的洗淨液之Cii濃度(ppb)使 用感應結合電漿質量分析計(ICP-MS)測定,由下式計算洗 淨液之Cuf虫刻率(nm/min)
Cu 倉虫亥丨J 率(nm/min) = CxL><G/S/100/H C :洗淨液之Cu濃度(ppb) L :洗淨液量(c m3) G : Cu 之密度(8.95g/cm3) S : Cu基板片面積(cm2) Η :浸漬時間(180min) 由表6,知悉由本發明之半導體基板用洗淨液對Cu之 鈾刻率非常低,可防止基板上之線路之腐蝕,且可高淸淨 的洗淨。 由以上之結果,知悉本發明之洗淨液,對添加防蝕劑 CMP用漿料硏磨後微粒子(particle)之去除性優,且短時 間沖洗之洗淨性亦優。又,金屬污染之去除性或防止金屬 線路之腐蝕亦顯現優洗淨效果。 又,作爲本申請之優先權張之基礎引用日本特許願 2004-032222號(於2004年2月9日向日本特許廳申請)之全 說明書內容,採用作爲本發明之說明書之揭示。 -30- 200537611(28)
一 « U b §ffl a ® o 鷗1 (N m (N ON 对 rn m <N ro m (N iT) fN (N rn 沖洗時間 (sec) 〇 ο 〇 〇 O ο o ο ο ο o 〇 ο O O o O O 洗淨時間 (sec) 〇 ο m o m o o m Ο m o m Ο m Ο m ο: o ro o m ο m 〇 m o r〇 o ro 〇 rn o ΓΟ 成分⑷/ 成分(b) <N Ο Ο ο 'sD 〇 d d 00 o d ro 5 卜 d g d \D Ο Ο g d g d g O' g d • 1 1 1 1 1 s d 1 1 1 1 1 1 11 Φ炎 对 卜 卜 (N oc ro o »〇 <Ν ΟΝ 卜 rs <N (N 1 1 1 1 1 1 o 1 1 1 1 1 1 对· 对· o 对· o 寸 m ON (N 卜 <N rn 对 rn m 对· rn oc Os 二 口 00 ΓΜ S£) (N <N 金屬雜質 濃度※1 CX V -D Ο. Cl V Cu V JD^ D. V 兰 D. V -D o. V Q. V *§· Q. V 兰 Cl V Xi o. V X) a. CU V 兰 a. V 兰 D- V x> D. o- V Cu V 兰 O- V Cl V CX V 含有量 wt% 1 翁 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 隹 1 1 1 ft 1 K 1 1 1 1 1 1 1 1 1 t 1 1 1 1 1 1 1 1 1 1 1 o (N 〇 S d 其他 成分 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 1 t 1 1 1 I 1 1 1 1 1 » 1 1 1 1 1 MSA < Oh I 1 1 1^ 超純水 超純水 超純水 超純水 超純水 超純水 超純水 1超純水1 I超純水I 1超純水1 超純水 超純水 1超純水1 超純水 超純水 超純水 超純水 超純水: 含有量 wt% 0.007 0.017 卜 ο d 卜 ο Ο 卜 ο Ο 卜 ο 〇· 卜 ο Ο 卜 ο ο 卜 ο Ο 卜 ο ο 卜 CD 〇 卜 ο ο 卜 Ο Ο 卜 ο d 卜 ο ο 卜 ο d 卜 ο d 卜 Ο d 成分⑷ 界面活性劑 00 CQ Ο C/D CQ Q CQ D CO CQ Q GC CQ Q CO CQ Q in 0D D ΟΟ CQ Q C/D CQ Q DPDSA DPDSA ΜΜΤ ! in 0Q Ο 00 CQ Q CQ Q C/D DD Q 00 CQ O 00 CQ Q 含有量 wt% ΓΟ m d 卜 m d Os (N d 0's <N d o ΓΜ o m o ο ο ο ΓΜ Ο 卜 (N d ON (N 〇 o (N 〇 ο (Ν ο ο CM d 1 1 1 1 1 1 O 1 1 1 1 1 1 e灸 Φ链 但繼 TWAH jTWAH TWAH TWAH TWAH TWAH TWAH m S 纒 m TWAH TWAH TWAH m X z 1 1 1 1 1 1 TWAH 1 1 翁 1 1 1 含有量 wt% d o d o d d Ο ο in d 〇 in d IT) d in 〇· 〇 d in o 〇 d 成分(a) 有機酸 檸檬酸 檸檬酸 檸檬酸 檸檬酸 檸檬酸 檸檬酸 檸檬酸 1檸檬酸1 I檸檬酸I 1檸檬酸1 檸檬酸 1檸檬酸1 1檸檬酸1 檸檬酸 檸檬酸 檸檬酸 檸檬酸 檸檬酸 實施例1 實施例2 實施例3 實施例4 實施例5 實施例6 實施例7 實施例8 實施例9 實施例10 實施例Π 實施例〗2 比較例1 比較例2 比較例3 比較例4 比較例5 比較例6 sfsi^^uN, qcu, nu, £ , BU.M, IV , 3S , BMW邻旮蘅衡«濉迥«»漶酲領stl^^: 一※ tN« Μ ^ m ^ S d 鼷A ΓΜ CN 二 沖洗時間 (sec) 〇 ΓΟ 〇 m 洗淨時間 (sec) 〇 m 〇 m Sf 00 〇 〇 g ο 成分(a)/ 成分(b) «〇 (N ΟΟ ΓΟ rn ο 寸· 金屬雜質 濃度※1 V χ> S \/ 1超純水1 1超純水1 含有量 wt% 0.008 0.008 成分(C) 界面活性劑 00 CQ Q DPDSA 含有量 wt% 〇 〇 Ο e炎 链繼 TWAH TWAH 含有量 wt% (N 〇 CM Ο 成分(a) 有機酸 1檸檬酸1 1檸檬酸1 實施例13 實施例14 fe(«^*Nez , qd , nu, £ , Βυ, Μ1V ,ΟΙΙΙΛί , —^舶*0-観耻«濉迥«»裁||領濉长鉅:1糸 -31 - 200537611(29)
e« & B §ffl ^ 歡10 Μ 2 r- 沖洗時間 (sec) 洗淨時間 ! (sec) 成分(C)/ 成分(b) 0.06 0.06 成分⑷/ 成分(b) 卜 卜 〇 对· 〇 对· 金屬雜質 濃度※1 JO D. V 〇. V 成分(d) ί水— 超純水 超純水 含有量 wt% 0.017 0.017 成分(C) 界面活性劑 DBS DBS 含有量 wt% 0.29 0.29 成分(b) 驗成分 TWAH TWAH i含有量 wt% d d 成分(a) 有機酸 檸檬酸 檸檬酸 實施例〗5 實施例16 fessl^^uN, , nu, 3U-, Bo.M-lv ,32, 1^)邻-B-f歡$:铝濉秘»»漶1|^減长矻:一※
Tt« S言 Si ^ 起2 VO 173 沖洗時間 (sec) 洗淨時間 (sec) 成分(c)/ 成分(b) 0.08 0.06 成分⑷/ 成分(b) <Ν 00 ΓΟ 〇 对· |金屬雜質 濃度※1 〇. V CL V 1成分(d) 超純水| 超純水 1含有量 wt% 0.008 0.008 1成分(C) 界面活性劑 DBS DPDSA 含有量 wt% 0.10 0.14 成分(b) 驗成分 TWAH TWAH |含有量 wt% 0.25 0.25 成分(a) 有機酸 檸檬酸 檸檬酸 實施例17 實施例18 fessl^^uz , qcu, Π3,3d ;u,y,lv ,32, —-N<rnfl-E$:S脏鹋觸»羰 B領 ffil^yul: »o* 金屬去除性※2 P U (N 〇 (N 沖洗時間 (sec) S 洗淨時間 (sec) 成分(C)/ 成分(b) 0.06 成分⑷/ 成分(b) 卜 a 〇 寸· 金屬雜質 濃度※1 JO ο ν 成分(d) 超純水 含有量 wt% 0.017 成分(C) 界面活性劑 DBS 含有量 wt% 0.29 成分(b) 驗成分 TWAH 含有量 wt% d 成分(a) 有機酸 檸檬酸 實施例】9 9* zi/iloolx®_m®® :⑺※ 魃_砟^UN, qDH, nu, £ , BU, >1 ,1V ,32, —^<ro-fi-sa垢脏««MSB領輯长踣:一※ 蝕刻率 (mm/min) 0.05 0.17 洗淨時間 (小時) m m 成分(C)/ 成分(b) 0.08 1 1 1 成分⑷/ 成分(b) <N 1 1 1 q 金屬雜質 濃度※1 cx V -Ο ο. V 成分(d) 水 超純水 超純水 含有量 wt% 0.008 0.008 成分(c) i界面活性劑 DBS DBS 含有量 wt% 0.10 參 1 1 成分(b) 驗成分 TWAH 1 1 1 含有量 wt% 0.25 0.25 成分(a) 有機酸 擰檬酸 檸檬酸 實施例20 比較例7 ««^•Νυζ , qd , nuLJ , ΰ , >1 , IV ,32, m^)邻旮豪班铝*®»»羰β領脏长矻:一※ -32-
Claims (1)
- 200537611 (1) 十、申請專利範圍 1 · 一種半導體裝置用基板洗淨液,其特徵爲含有以下 成分(a)、(b)、(c)、(d),且pH爲1.5以上低於6.5者: 成分(a):有機酸 成分(b):有機鹼成分 成分(Ο :界面活性劑 成分(d):水。 2 ·如申請專利範圍第1項之半導體裝置用基板洗淨液 ,其中上述半導體裝置用基板其表面具有金屬線路者。 3·如申請專利範圍第1或第2項之半導體裝置用基板洗 淨液,其中上述半導體裝置用基板係表面具有低介電率絕 緣膜者。 4 .如申請專利範圍第1至第3項中任一項之半導體裝置 用基板洗淨液,其中上述成分(a)爲具有1個以上羧基之碳 數爲1〜1 0的有機化合物者。 5 ·如申請專利範圍第4項之半導體裝置用基板洗淨液 ,其中上述成分(a)爲至少1種選自由醋酸、丙酸、草酸、 號珀酸、丙二酸、檸檬酸、酒石酸、及蘋果酸所成群之有 機酸。 6 .如申請專利範圍第1至第5項中任一項之半導體裝置 用基板洗淨液,其中上述成分(b)爲以下一般式(1)所示者 (1) (R1)4N + OH- -33- 200537611 (2) (但,R 1爲氫原子、或經基、院氧基或由鹵素所取代 亦可之烷基,4個R1爲全數相同亦可,互爲相異亦可,但 是,全數同時爲氫原子的情形除外)。 7.如申請專利範圍第6項之半導體裝置用基板洗淨液 ,其中上述成分(b)爲具碳數1〜4之烷基及/或碳數1〜4之羥 烷基的氫氧化第4級銨者。 8·如申請專利範圍第1至第7項中任一項之半導體裝置 用基板洗淨液,其中上述成分(c)爲陰離子系界面活性劑 者。 9·如申請專利範圍第8項之半導體裝置用基板洗淨液 ,其中上述陰離子系界面活性劑爲至少1種選自由烷基磺 酸或其鹽 '烷基苯磺酸或其鹽、烷基二苯醚二磺酸或其鹽 、烷基甲基牛磺酸或其鹽、烷基硫酸酯或其鹽、烷基醚硫 酸酯或其鹽、及磺基琥珀酸二酯或其鹽所成群之陰離子系 界面活性劑。 1 〇 ·如申請專利範圍第1至第9項中任一項之半導體裝 置用基板洗淨液,其中上述成分(a)之含量爲〇.05〜10重量 % 〇 1 1 .如申請專利軸圍第1至第1 〇項中任一 I旨之半導體裝 置用基板洗淨液’其中上述成分(b)之含量爲〇.〇1〜10重量 %。 1 2 ·如申請專利範圍第1至第1】項中任一項之半導體裝 置用基板洗淨液’其中上述成分(C)之含量爲〇 〇〇〇3〜〇.]重 -34- 200537611 (3) 量% 〇 13.如申請專利範圍第1至第12項中任一項之半導體裝 置用基板洗淨液,其中上述成分(a)與(b)之重量比率[成分 (a)/成分(b)]爲0.8以上5以下者。 1 4 ·如申請專利範圍第1至第1 3項中任一項之半導體裝 '置用基板洗淨液,其中上述成分(c)與(b)之蔞量比率[成分 (〇/成分(b)]爲0.01以上0.2以下者。 _ 15.—種半導體裝置用基板之洗淨方法,其特徵爲使 用含有以下成分(a)、(b)、(〇、(d),且pH爲丨.5以上低於 6.5之液洗淨半導體用基板者: 成分(a):有機酸 成分(b):有機鹼成分 成分(c):界面活性劑 成分(d):水。 1 6 .如申請專利範圍第1 5項之半導體裝置用基板洗淨 φ 方法,其中上述半導體裝置用基板,係於基板表面具有 C u膜與低介電率絕緣膜,且,於C μ P處理後洗淨基板者 〇 1 7 ·如申請專利範圍第1 6項之半導體裝置用基板洗淨 方法,其中上述CMP處理係由含唑(Azole)系防蝕劑之硏磨 劑進行者。 -35- 200537611 七、指定代表圖: (一) 、本案指定代表圖爲:無 (二) 、本代表圖之元件代表符號簡單說明:無本案若有化學式時,請揭示最能顯示發明特徵之化學式:無