RU2430895C1 - Mass for production of enamel coating - Google Patents
Mass for production of enamel coating Download PDFInfo
- Publication number
- RU2430895C1 RU2430895C1 RU2010124919/03A RU2010124919A RU2430895C1 RU 2430895 C1 RU2430895 C1 RU 2430895C1 RU 2010124919/03 A RU2010124919/03 A RU 2010124919/03A RU 2010124919 A RU2010124919 A RU 2010124919A RU 2430895 C1 RU2430895 C1 RU 2430895C1
- Authority
- RU
- Russia
- Prior art keywords
- enamel coating
- mass
- production
- frit
- mullite
- Prior art date
Abstract
Description
Изобретение относится к составам масс для получения эмалевого покрытия на изделиях из чугуна, стали.The invention relates to compositions of the masses to obtain an enamel coating on products made of cast iron, steel.
Известна масса для получения эмалевого покрытия, состава, мас.%: фритта 75,0-96,0; муллит 2,0-15,0; глина 1,0-2,0 [1].Known mass to obtain an enamel coating, composition, wt.%: Frit 75.0-96.0; mullite 2.0-15.0; clay 1.0-2.0 [1].
Задачей изобретения является повышение термостойкости эмалевого покрытия.The objective of the invention is to increase the heat resistance of the enamel coating.
Технический результат достигается тем, что масса для получения эмалевого покрытия, содержащая фритту, муллит, глину, дополнительно содержит силлиманит при следующем соотношении компонентов, мас.%: фритта 82,0-83,0; муллит 4,0-10,0; силлиманит 4,0-10,0; глина 3,0-4,0.The technical result is achieved in that the mass to obtain an enamel coating containing frit, mullite, clay, additionally contains sillimanite in the following ratio of components, wt.%: Frit 82,0-83,0; mullite 4.0-10.0; sillimanite 4.0-10.0; clay 3.0-4.0.
В таблице приведены составы массы для получения эмалевого покрытия.The table shows the composition of the mass to obtain an enamel coating.
Термостойкость эмалевого покрытия составит 4-6 теплосмен (при 450°С нагрева) для любого состава, приведенного в таблице.The heat resistance of the enamel coating will be 4-6 heat exchange (at 450 ° C heating) for any composition shown in the table.
Для приготовления эмалевого покрытия используют выпускаемые промышленностью фритты: 24/70, ДМ-2, В-9, ЛГ-19. Фритту, муллит, силлиманит и глину размалывают до полного прохождения через сетку №0056. После помола компоненты дозируют в требуемых количествах и смешивают. Из полученной массы готовят суспензию с влажностью 45-55%. Суспензию наносят на подготовленную поверхность металлических изделий и закрепляют обжигом (температуру и продолжительность обжига подбирают экспериментальным путем в зависимости от состава и свойств используемой фритты и толщины эмалируемых изделий).To prepare the enamel coating, the frits produced by the industry are used: 24/70, DM-2, V-9, LG-19. Frit, mullite, sillimanite and clay are ground until they pass completely through mesh No. 0056. After grinding, the components are dosed in the required quantities and mixed. A suspension with a moisture content of 45-55% is prepared from the resulting mass. The suspension is applied to the prepared surface of metal products and fixed by firing (the temperature and duration of firing are selected experimentally, depending on the composition and properties of the frit used and the thickness of the enameled products).
Источники информацииInformation sources
1. JP 9169543, С03С 3/072, 1997.1. JP 9169543, C03C 3/072, 1997.
Claims (1)