RU2537735C1 - Mixture for making enamel coating - Google Patents
Mixture for making enamel coating Download PDFInfo
- Publication number
- RU2537735C1 RU2537735C1 RU2013155355/03A RU2013155355A RU2537735C1 RU 2537735 C1 RU2537735 C1 RU 2537735C1 RU 2013155355/03 A RU2013155355/03 A RU 2013155355/03A RU 2013155355 A RU2013155355 A RU 2013155355A RU 2537735 C1 RU2537735 C1 RU 2537735C1
- Authority
- RU
- Russia
- Prior art keywords
- enamel coating
- mixture
- frit
- mullite
- zircon
- Prior art date
Abstract
Description
Изобретение относится к составам масс для получения эмалевого покрытия на керамических изделиях, в том числе хозяйственно-бытового назначения.The invention relates to compositions of the masses to obtain an enamel coating on ceramic products, including domestic purposes.
Известна масса для получения эмалевого покрытия, содержащая, мас.%: фритта 75,0-96,0; муллит 2,0-15,0 [1].Known mass to obtain an enamel coating, containing, wt.%: Frit 75.0-96.0; mullite 2.0-15.0 [1].
Задачей изобретения является повышение термостойкости эмалевого покрытия.The objective of the invention is to increase the heat resistance of the enamel coating.
Технический результат достигается тем, что масса для получения эмалевого покрытия, содержащая фритту и муллит, дополнительно содержит циркон и сподумен при следующем соотношении компонентов, мас.%: фритта 63,0-67,0; муллит 7,0-10,0; циркон 16,0-20,0; сподумен 4,0-6,0.The technical result is achieved in that the mass to obtain an enamel coating containing frit and mullite, additionally contains zircon and spodumene in the following ratio of components, wt.%: Frit 63.0-67.0; mullite 7.0-10.0; zircon 16.0-20.0; spodumene 4.0-6.0.
В таблице приведены составы массы для получения эмалевого покрытия.The table shows the composition of the mass to obtain an enamel coating.
Используют типовой состав фритты В 1 с, используемой в производстве изделий санитарной керамики.Use a typical composition of frits B 1 s, used in the manufacture of sanitary ceramics.
Фритту В 1 с получают сплавлением следующих компонентов, мас.%: полевой шпат 15,6; песок кварцевый 15,5; мел 23,0; тальк 10,4; оксид цинка 2,0; барий углекислый 4,1; цирконовый концентрат 29,4 [2].Frit B 1 s is obtained by fusion of the following components, wt.%: Feldspar 15.6; quartz sand 15.5; chalk 23.0; talcum 10.4; zinc oxide 2.0; barium carbonate 4.1; zircon concentrate 29.4 [2].
Фритту, муллит, циркон, сподумен дозируют в требуемых количествах, загружают в шаровую мельницу, добавляют воду и размалывают до полного прохождения через сетку 0056. Из полученной массы готовят суспензию с влажностью 45-60%. Суспензию наносят на поверхность керамических изделий и закрепляют обжигом при температуре 1250°C. Термостойкость эмалевого покрытия составит ~25 теплосмен (нагрев до 450°C - охлаждение на воздухе) для любого состава, приведенного в таблице.Frit, mullite, zircon, spodumene are dosed in the required quantities, loaded into a ball mill, water is added and milled until it passes through the 0056 mesh. A suspension with a moisture content of 45-60% is prepared from the resulting mass. The suspension is applied to the surface of ceramic products and fixed by firing at a temperature of 1250 ° C. The heat resistance of the enamel coating will be ~ 25 heat exchange (heating to 450 ° C - cooling in air) for any composition shown in the table.
Источники информацииInformation sources
1. JP 9169543.1.JP 9169543.
2. Канаев В.К. Новая технология строительной керамики. - М.: Стройиздат, 1990. - С.63.2. Kanaev V.K. New technology for building ceramics. - M .: Stroyizdat, 1990. - P.63.
Claims (1)