RU2496743C1 - Ceramic mixture for making buttons - Google Patents
Ceramic mixture for making buttons Download PDFInfo
- Publication number
- RU2496743C1 RU2496743C1 RU2012121085/03A RU2012121085A RU2496743C1 RU 2496743 C1 RU2496743 C1 RU 2496743C1 RU 2012121085/03 A RU2012121085/03 A RU 2012121085/03A RU 2012121085 A RU2012121085 A RU 2012121085A RU 2496743 C1 RU2496743 C1 RU 2496743C1
- Authority
- RU
- Russia
- Prior art keywords
- ceramic
- buttons
- kaolin
- ceramic mixture
- sodium oleate
- Prior art date
Abstract
Description
Изобретение относится к составам керамических масс, которые могут быть использованы для изготовления пуговиц.The invention relates to compositions of ceramic masses that can be used for the manufacture of buttons.
Известна керамическая масса, содержащая, мас.%: каолин 0-70,0; керамический бой 0-15,0; глинистый песок - остальное [1].Known ceramic mass containing, wt.%: Kaolin 0-70,0; ceramic battle 0-15,0; clay sand - the rest [1].
Задача изобретения состоит в повышении прочности пуговиц, полученных из керамической массы.The objective of the invention is to increase the strength of buttons obtained from ceramic mass.
Технический результат достигается тем, что керамическая масса для изготовления пуговиц, включающая каолин и керамический бой, дополнительно содержит маршалит и олеат натрия при следующем соотношении компонентов, мас.%: каолин 75,5-80,5; керамический бой 3,0-4,0; маршалит 16,0-20,0; олеат натрия 0,5-0,6.The technical result is achieved in that the ceramic mass for the manufacture of buttons, including kaolin and ceramic fight, additionally contains marshalite and sodium oleate in the following ratio of components, wt.%: Kaolin 75.5-80.5; ceramic battle 3.0-4.0; marshallite 16.0-20.0; sodium oleate 0.5-0.6.
В таблице приведены составы керамической массы для изготовления пуговиц.The table shows the compositions of the ceramic mass for the manufacture of buttons.
Для приготовления керамической массы могут быть использованы каолины любых месторождений, например каолин Просяновского месторождения, характеризующийся следующим химическим составом, мас.%: SiO2 46,02-46,5; TiO2 0,47-0,52; Al2O3 38,69-40,17; Fe2O3 0,55-0,92; CaO 0,05-0,19; п.п.п. 13,34-13,97; бой любых керамических изделий, в том числе и глазурованных.To prepare the ceramic mass, kaolins of any deposits can be used, for example, kaolin of the Prosyanovskoye deposit, characterized by the following chemical composition, wt.%: SiO 2 46.02-46.5; TiO 2 0.47-0.52; Al 2 O 3 38.69-40.17; Fe 2 O 3 0.55-0.92; CaO 0.05-0.19; p.p.p. 13.34-13.97; the battle of any ceramic products, including glazed ones.
Компоненты дозируют в требуемых количествах. Керамический бой, каолин загружают в шаровые мельницы и по отдельности размалывают и просеивают через сетку 008. Размолотые керамический бой и каолин смешивают, добавляют просеянный через сетку 008 маршалит, олеат натрия и готовят керамическую массу с влажностью 20-25%. Керамическую массу раскатывают в пласт требуемой толщины, из которого прессуют пуговицы. Изделия сушат до влажности не более 5% и при температуре 1650-1670°С проводят обжиг. Поверхность обожженных пуговиц может быть покрыта легкоплавкой эмалью или глазурью с последующим ее оплавлением, металлизирована. The components are dosed in the required amounts. Ceramic fight, kaolin are loaded into ball mills and individually grinded and sieved through a 008 grid. The ground ceramic fight and kaolin are mixed, mixed with marshalite sifted through a 008 grid, sodium oleate and a ceramic mass with a moisture content of 20-25% is prepared. The ceramic mass is rolled into a layer of the required thickness, from which the buttons are pressed. Products are dried to a moisture content of not more than 5% and firing is carried out at a temperature of 1650-1670 ° C. The surface of the burnt buttons can be coated with low-melting enamel or glaze with its subsequent melting, metallized.
Источник информацииThe source of information
1. BG 103628, 2001.1. BG 103628, 2001.
Claims (1)