RU2304100C1 - Enamel - Google Patents

Enamel Download PDF

Info

Publication number
RU2304100C1
RU2304100C1 RU2006108637/03A RU2006108637A RU2304100C1 RU 2304100 C1 RU2304100 C1 RU 2304100C1 RU 2006108637/03 A RU2006108637/03 A RU 2006108637/03A RU 2006108637 A RU2006108637 A RU 2006108637A RU 2304100 C1 RU2304100 C1 RU 2304100C1
Authority
RU
Russia
Prior art keywords
enamel
mgo
zno
sio
moo
Prior art date
Application number
RU2006108637/03A
Other languages
Russian (ru)
Inventor
Юли Алексеевна Щепочкина (RU)
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2006108637/03A priority Critical patent/RU2304100C1/en
Application granted granted Critical
Publication of RU2304100C1 publication Critical patent/RU2304100C1/en

Abstract

FIELD: enamel compositions used for coating of articles made from steel, cast iron and other alloys.
SUBSTANCE: enamel composition contains the following components, wt%: SiO2 50.0-54.0; B2O3 8.0-12.0; Al2O3 6.0-10.0; MgO 0.5-1.5; ZnO 2.0-3.0; K2O 0.5-1.5; TiO2 5.0-6.0; Cr2O3 1.5-2.5; ZrO2 14.0-20.0; MoO3 0.5-1.5.
EFFECT: increased acid resistance of enamel.
1 tbl

Description

Изобретение относится к технологии силикатов, в частности к составам эмалей, используемых для нанесения на изделия из стали, чугуна и других сплавов.The invention relates to the technology of silicates, in particular to compositions of enamels used for application to steel products, cast iron and other alloys.

Известна эмаль, содержащая SiO2, B2O3, Al2O3, MgO, ZnO, K2O и другие компоненты /1/.Known enamel containing SiO 2 , B 2 O 3 , Al 2 O 3 , MgO, ZnO, K 2 O and other components / 1 /.

Известна эмаль, содержащая следующие компоненты, мас.%: SiO2 41,0-52,0; B2O3 15,0-18,0; Al2O3 4,0-7,0; Fe2O3 3,5-7,5; MgO 0,4-0,5; CaO 1,2-4,0; ZnO 4,0-6,0; Na2O 13,0-18,5; K2O 0,2-0,5; TiO 0,1-1,0; Cr2O3 1,5-3,5 /2/.Known enamel containing the following components, wt.%: SiO 2 41,0-52,0; B 2 O 3 15.0-18.0; Al 2 O 3 4.0-7.0; Fe 2 O 3 3.5-7.5; MgO 0.4-0.5; CaO 1.2-4.0; ZnO 4.0-6.0; Na 2 O 13.0-18.5; K 2 O 0.2-0.5; TiO 0.1-1.0; Cr 2 O 3 1.5-3.5 / 2 /.

Целью изобретения является повышение кислостойкости эмали.The aim of the invention is to increase the acid resistance of enamel.

Цель достигается тем, что в состав эмали дополнительно вводят ZrO2 и MoO3 при следующем соотношении компонентов, мас.%: SiO2 50,0-54,0; B2O3 8,0-12,0; Al2O3 6,0-10,0; MgO 0,5-1,5; ZnO 2,0-3,0; K2O 0,5-1,5; TiO2 5,0-6,0; Cr2O3 1,5-2,5; ZrO2 14,0-20,0; MoO3 0,5-1,5.The goal is achieved in that the composition of the enamel is additionally introduced ZrO 2 and MoO 3 in the following ratio of components, wt.%: SiO 2 50,0-54,0; B 2 O 3 8.0-12.0; Al 2 O 3 6.0-10.0; MgO 0.5-1.5; ZnO 2.0-3.0; K 2 O 0.5-1.5; TiO 2 5.0-6.0; Cr 2 O 3 1.5-2.5; ZrO 2 14.0-20.0; MoO 3 0.5-1.5.

В таблице приведены составы эмали.The table shows the composition of the enamel.

ТаблицаTable СоставStructure Компоненты, мас.%Components, wt.% Потеря массы в 4% мг/см2 Weight loss of 4% mg / cm 2 SiO2 SiO 2 B2O3 B 2 O 3 Al2O3 Al 2 O 3 MgOMgO ZnOZno K2OK 2 O TiO2 TiO 2 Cr2O3 Cr 2 O 3 ZrO2 ZrO 2 MoO3 Moo 3 1one 50,050,0 12,012.0 10,010.0 0,50.5 3,03.0 1,51,5 6,06.0 1,51,5 14,014.0 1,51,5 0,005-0,050.005-0.05 22 52,052.0 10,010.0 8,08.0 1,01,0 2,52,5 1,01,0 5,55.5 2,02.0 17,017.0 1,01,0 0,005-0,050.005-0.05 33 54,054.0 8,08.0 6,06.0 1,51,5 2,02.0 0,50.5 5,05,0 2,52,5 20,020,0 0,50.5 0,005-0,050.005-0.05

Температура варки эмали 1300°С, температура обжига 950°С. Эмаль наносят на предварительно загрунтованные металлические поверхности.The enamel cooking temperature is 1300 ° С, the firing temperature is 950 ° С. Enamel is applied to pre-primed metal surfaces.

Эмаль может быть эффективно использована для покрытия оборудования химической, текстильной промышленности, изделий хозяйственно-бытового назначения. Повышается качество и расширяется область применения эмалированных изделий.Enamel can be effectively used to cover equipment of the chemical, textile industry, household products. Enhanced quality and expanded scope of enameled products.

Источники информацииInformation sources

1. Авторское свидетельство СССР №923980, С03С 7/06, 1982.1. USSR author's certificate No. 923980, С03С 7/06, 1982.

2. Авторское свидетельство СССР №1632956, С03С 8/04, 1991.2. USSR Author's Certificate No. 1632956, С03С 8/04, 1991.

Claims (1)

Эмаль, содержащая SiO2, B2O3, Al2O3, MgO, ZnO, K2O, TiO2, Cr2O3, отличающаяся тем, что дополнительно содержит ZrO2 и МоО3 при следующем соотношении компонентов, мас.%:Enamel containing SiO 2 , B 2 O 3 , Al 2 O 3 , MgO, ZnO, K 2 O, TiO 2 , Cr 2 O 3 , characterized in that it additionally contains ZrO 2 and MoO 3 in the following ratio of components, wt. %: SiO2 SiO 2 50,0-54,050.0-54.0 B2O3 B 2 O 3 8,0-12,08.0-12.0 Al2O3 Al 2 O 3 6,0-10,06.0-10.0 MgO MgO 0,5-1,50.5-1.5 ZnO Zno 2,0-3,02.0-3.0 K2O K 2 O 0,5-1,50.5-1.5 TiO TiO 5,0-6,05.0-6.0 Cr2O3 Cr 2 O 3 1,5-2,51.5-2.5 ZrO2 ZrO 2 14,0-20,014.0-20.0 MoO3 Moo 3 0,5-1,50.5-1.5
RU2006108637/03A 2006-03-20 2006-03-20 Enamel RU2304100C1 (en)