RU2307094C1

RU2307094C1 - Enamel paint

Info

Publication number: RU2307094C1
Application number: RU2006112655/03A
Authority: RU
Inventors: Юли Алексеевна Щепочкина (RU); Юлия Алексеевна Щепочкина
Original assignee: Юлия Алексеевна Щепочкина
Priority date: 2006-04-17
Filing date: 2006-04-17
Publication date: 2007-09-27

Abstract

FIELD: application coats on articles made from cast iron, steel and alloys.

SUBSTANCE: proposed enamel paint contains the following components, mass-%: B₂O₃, 16.0-22.0; CoO, 0.3-7.0; Na₂O, 1.5-2.5; CaO, 4.0-8.0; Al₂O₃, 5.7-6.3; NiO, 2.0-4.0; MnO₂, 4.0-6.0; TiO₂, 3.0-5.0; Fe₂O₃, 3.5-4.5; V₂O₅, 4.0-6.0; MgF₂, 18.0-22.0; the remainder being SiO₂.

EFFECT: improved quality; extended field of application.

1 tbl

Description

Изобретение относится к составам эмалей, используемых для покрытия изделий из чугуна, стали и других сплавов.The invention relates to compositions of enamels used for coating articles made of cast iron, steel and other alloys.

Известна эмаль, получаемая из фритты, содержащая B₂O₃, Na₂O, CaO, Al₂O₃, SiO₂ и другие компоненты [1].Known enamel obtained from frit containing B ₂ O ₃ , Na ₂ O, CaO, Al ₂ O ₃ , SiO ₂ and other components [1].

Известна эмаль следующего состава, мас.%: B₂O₃ 16,0-25,0; CoO 0,3-0,7; Na₂O 16,0-25,0; CaO 2,1-4,0; Al₂O₃ 1,5-6,5; NiO 0,3-2,0; MnO₂ 1,5-8,7; TiO₂ 1,1-5,5; Zi₂O 0,05-0,5; Fe₂O₃0,3-4,5; SiO₂ - остальное [2]. Прочность такой эмали на удар 1,5-1,6 Дж.Known enamel of the following composition, wt.%: B ₂ O ₃ 16,0-25,0; CoO 0.3-0.7; Na ₂ O 16.0-25.0; CaO 2.1-4.0; Al ₂ O ₃ 1.5-6.5; NiO 0.3-2.0; MnO ₂ 1.5-8.7; TiO ₂ 1.1-5.5; Zi ₂ O 0.05-0.5; Fe ₂ O ₃ 0.3-4.5; SiO ₂ - the rest [2]. The strength of such an enamel on impact is 1.5-1.6 J.

Цель изобретения состоит в повышении прочности эмали на удар.The purpose of the invention is to increase the enamel's impact strength.

Цель достигается тем, что в состав эмали дополнительно вводят V₂O₅ и MgF₂, при следующем соотношении компонентов, мас.%: B₂O₃ 16,0-22,0; CoO 0,3-0,7; Na₂O 1,5-2,5; CaO 4,0-8,0; Al₂O₃ 5,7-6,3; NiO 2,0-4,0; MnO₂ 4,0-6,0; TiO₂ 3,0-5,0; Fe₂O₃ 3,5-4,5; V₂O₅ 4,0-6,0; MgF₂ 18,0-22,0; SiO₂ - остальное.The goal is achieved by the fact that V ₂ O ₅ and MgF ₂ are additionally introduced into the enamel, in the following ratio of components, wt.%: B ₂ O ₃ 16.0-22.0; CoO 0.3-0.7; Na ₂ O 1.5-2.5; CaO 4.0-8.0; Al ₂ O ₃ 5.7-6.3; NiO 2.0-4.0; MnO ₂ 4.0-6.0; TiO ₂ 3.0-5.0; Fe ₂ O ₃ 3.5-4.5; V ₂ O ₅ 4.0-6.0; MgF ₂ 18.0-22.0; SiO ₂ - the rest.

В таблице приведены со станы эмали.The table shows the enamel mill.

ТаблицаTable СоставStructure Компоненты, мас.%:Components, wt.%: B₂O₃ B ₂ O ₃ CoOCoo Na₂ONa ₂ O CaOCao Al₂O₃ Al ₂ O ₃ NiONio MnO₂ MnO ₂ TiO₂ TiO ₂ Fe₂O₃ Fe ₂ O ₃ V₂O₅ V ₂ O ₅ MgF₂ MgF ₂ SiO₂ SiO ₂ 1one 16,016,0 0,70.7 1,51,5 8,08.0 6,36.3 2,02.0 4,04.0 5,05,0 4,54,5 4,04.0 22,022.0 26,026.0 22 22,022.0 0,30.3 2,52,5 4,04.0 5,75.7 4,04.0 6,06.0 3,03.0 3,53,5 6,06.0 18,018.0 25,025.0 33 19,019.0 0,50.5 2,02.0 6,06.0 6,06.0 3,03.0 5,05,0 4,04.0 4,04.0 5,05,0 20,020,0 25,025.0

Прочность эмали на удар составит ~2,5 Дж для всех составов, приведенных в таблице.The enamel's impact strength will be ~ 2.5 J for all compositions listed in the table.

Температура варки эмали 1300°С, температура обжига 1000°С.The enamel cooking temperature is 1300 ° С, the firing temperature is 1000 ° С.

Источники информацииInformation sources

1. Патент США №4446241, кл.501-14, 1984.1. US patent No. 4446241, CL 501-14, 1984.

2. Авторское свидетельство СССР №1255598, С03С 8/02, 1986.2. USSR copyright certificate No. 1255598, С03С 8/02, 1986.

Claims

An enamel containing B ₂ O ₃ , Na ₂ O, CoO, CaO, Al ₂ O ₃ , NiO, MnO ₂ , TiO ₂ , Fe ₂ O ₃ , SiO ₂ , characterized in that it further comprises V ₂ O ₅ and MgF ₂ in the following ratio of components, wt.%: In ₂ About ₃ 16,0-22,0; CoO 0.3-0.7; Na ₂ O 1.5-2.5; CaO 4.0-8.0; Al ₂ O ₃ 5.7-6.3; NiO 2.0-4.0; MnO ₂ 4.0-6.0; TiO ₂ 3.0-5.0; Fe ₂ O ₃ 3.5-4.5; V ₂ O ₅ 4.0-6.0; MgF ₂ 18.0-22.0; SiO ₂ - the rest.