RU2019116177A - Новый способ производства высокоуглеродистых материалов и полученные высокоуглеродистые материалы - Google Patents

Новый способ производства высокоуглеродистых материалов и полученные высокоуглеродистые материалы Download PDF

Info

Publication number
RU2019116177A
RU2019116177A RU2019116177A RU2019116177A RU2019116177A RU 2019116177 A RU2019116177 A RU 2019116177A RU 2019116177 A RU2019116177 A RU 2019116177A RU 2019116177 A RU2019116177 A RU 2019116177A RU 2019116177 A RU2019116177 A RU 2019116177A
Authority
RU
Russia
Prior art keywords
production
paragraphs
carbon material
fibers
parts
Prior art date
Application number
RU2019116177A
Other languages
English (en)
Other versions
RU2019116177A3 (ru
RU2765203C2 (ru
Inventor
Александр Корженко
Селья МЕРКАДЕ
Original Assignee
Аркема Франс
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Аркема Франс filed Critical Аркема Франс
Publication of RU2019116177A publication Critical patent/RU2019116177A/ru
Publication of RU2019116177A3 publication Critical patent/RU2019116177A3/ru
Application granted granted Critical
Publication of RU2765203C2 publication Critical patent/RU2765203C2/ru

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/71—Ceramic products containing macroscopic reinforcing agents
    • C04B35/78—Ceramic products containing macroscopic reinforcing agents containing non-metallic materials
    • C04B35/80—Fibres, filaments, whiskers, platelets, or the like
    • C04B35/83—Carbon fibres in a carbon matrix
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
    • B01D53/02—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols by adsorption, e.g. preparative gas chromatography
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
    • B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
    • B01J20/20—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising free carbon; comprising carbon obtained by carbonising processes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
    • B01J20/28—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties
    • B01J20/28014—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties characterised by their form
    • B01J20/28023—Fibres or filaments
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
    • B01J20/30—Processes for preparing, regenerating, or reactivating
    • B01J20/32—Impregnating or coating ; Solid sorbent compositions obtained from processes involving impregnating or coating
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/62204—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products using waste materials or refuse
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/62204—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products using waste materials or refuse
    • C04B35/62209—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products using waste materials or refuse using woody material, remaining in the ceramic products
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/62227—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products obtaining fibres
    • C04B35/62272—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products obtaining fibres based on non-oxide ceramics
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C04B35/628—Coating the powders or the macroscopic reinforcing agents
    • C04B35/62844—Coating fibres
    • C04B35/62857—Coating fibres with non-oxide ceramics
    • C04B35/62873—Carbon
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B38/00—Porous mortars, concrete, artificial stone or ceramic ware; Preparation thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B38/00—Porous mortars, concrete, artificial stone or ceramic ware; Preparation thereof
    • C04B38/0022—Porous mortars, concrete, artificial stone or ceramic ware; Preparation thereof obtained by a chemical conversion or reaction other than those relating to the setting or hardening of cement-like material or to the formation of a sol or a gel, e.g. by carbonising or pyrolysing preformed cellular materials based on polymers, organo-metallic or organo-silicon precursors
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F11/00—Chemical after-treatment of artificial filaments or the like during manufacture
    • D01F11/10—Chemical after-treatment of artificial filaments or the like during manufacture of carbon
    • D01F11/14—Chemical after-treatment of artificial filaments or the like during manufacture of carbon with organic compounds, e.g. macromolecular compounds
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F9/00—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments
    • D01F9/08—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments of inorganic material
    • D01F9/12—Carbon filaments; Apparatus specially adapted for the manufacture thereof
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F9/00—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments
    • D01F9/08—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments of inorganic material
    • D01F9/12—Carbon filaments; Apparatus specially adapted for the manufacture thereof
    • D01F9/14—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments
    • D01F9/16—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from products of vegetable origin or derivatives thereof, e.g. from cellulose acetate
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F9/00—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments
    • D01F9/08—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments of inorganic material
    • D01F9/12—Carbon filaments; Apparatus specially adapted for the manufacture thereof
    • D01F9/14—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments
    • D01F9/16—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from products of vegetable origin or derivatives thereof, e.g. from cellulose acetate
    • D01F9/17—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from products of vegetable origin or derivatives thereof, e.g. from cellulose acetate from lignin
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/052—Li-accumulators
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
    • H01M4/133—Electrodes based on carbonaceous material, e.g. graphite-intercalation compounds or CFx
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/13—Electrodes for accumulators with non-aqueous electrolyte, e.g. for lithium-accumulators; Processes of manufacture thereof
    • H01M4/139—Processes of manufacture
    • H01M4/1393—Processes of manufacture of electrodes based on carbonaceous material, e.g. graphite-intercalation compounds or CFx
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/362—Composites
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/58—Selection of substances as active materials, active masses, active liquids of inorganic compounds other than oxides or hydroxides, e.g. sulfides, selenides, tellurides, halogenides or LiCoFy; of polyanionic structures, e.g. phosphates, silicates or borates
    • H01M4/583—Carbonaceous material, e.g. graphite-intercalation compounds or CFx
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/02—Electrodes composed of, or comprising, active material
    • H01M4/36—Selection of substances as active materials, active masses, active liquids
    • H01M4/58—Selection of substances as active materials, active masses, active liquids of inorganic compounds other than oxides or hydroxides, e.g. sulfides, selenides, tellurides, halogenides or LiCoFy; of polyanionic structures, e.g. phosphates, silicates or borates
    • H01M4/583—Carbonaceous material, e.g. graphite-intercalation compounds or CFx
    • H01M4/587—Carbonaceous material, e.g. graphite-intercalation compounds or CFx for inserting or intercalating light metals
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M4/00—Electrodes
    • H01M4/86—Inert electrodes with catalytic activity, e.g. for fuel cells
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
    • C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
    • C04B2111/0081—Uses not provided for elsewhere in C04B2111/00 as catalysts or catalyst carriers
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
    • C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
    • C04B2111/00853—Uses not provided for elsewhere in C04B2111/00 in electrochemical cells or batteries, e.g. fuel cells
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/40—Metallic constituents or additives not added as binding phase
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/40—Metallic constituents or additives not added as binding phase
    • C04B2235/404—Refractory metals
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/40—Metallic constituents or additives not added as binding phase
    • C04B2235/405—Iron group metals
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/42—Non metallic elements added as constituents or additives, e.g. sulfur, phosphor, selenium or tellurium
    • C04B2235/422—Carbon
    • C04B2235/424—Carbon black
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/42—Non metallic elements added as constituents or additives, e.g. sulfur, phosphor, selenium or tellurium
    • C04B2235/422—Carbon
    • C04B2235/425—Graphite
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/42—Non metallic elements added as constituents or additives, e.g. sulfur, phosphor, selenium or tellurium
    • C04B2235/428—Silicon
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/48—Organic compounds becoming part of a ceramic after heat treatment, e.g. carbonising phenol resins
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/52—Constituents or additives characterised by their shapes
    • C04B2235/5208—Fibers
    • C04B2235/5264—Fibers characterised by the diameter of the fibers
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/52—Constituents or additives characterised by their shapes
    • C04B2235/5284—Hollow fibers, e.g. nanotubes
    • C04B2235/5288—Carbon nanotubes
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/54—Particle size related information
    • C04B2235/5418—Particle size related information expressed by the size of the particles or aggregates thereof
    • C04B2235/5454—Particle size related information expressed by the size of the particles or aggregates thereof nanometer sized, i.e. below 100 nm
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/60—Aspects relating to the preparation, properties or mechanical treatment of green bodies or pre-forms
    • C04B2235/616—Liquid infiltration of green bodies or pre-forms
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/65—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes
    • C04B2235/656—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes characterised by specific heating conditions during heat treatment
    • C04B2235/6567—Treatment time
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/74—Physical characteristics
    • C04B2235/77—Density
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/10—Energy storage using batteries
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/30—Hydrogen technology
    • Y02E60/50—Fuel cells

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Ceramic Engineering (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Manufacturing & Machinery (AREA)
  • Materials Engineering (AREA)
  • General Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Structural Engineering (AREA)
  • Inorganic Chemistry (AREA)
  • Electrochemistry (AREA)
  • Textile Engineering (AREA)
  • Composite Materials (AREA)
  • Analytical Chemistry (AREA)
  • Nanotechnology (AREA)
  • Dispersion Chemistry (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Wood Science & Technology (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Carbon And Carbon Compounds (AREA)
  • Inorganic Fibers (AREA)
  • Moulding By Coating Moulds (AREA)
  • Artificial Filaments (AREA)
  • Nonwoven Fabrics (AREA)
  • Woven Fabrics (AREA)
  • Battery Electrode And Active Subsutance (AREA)

Claims (42)

1. Способ производства (1) высокоуглеродистого материала (2), отличающийся тем, что он содержит объединение (100) структурированного прекурсора (10), содержащего волокно или набор волокон, и неструктурированного прекурсора (15) в форме текучей среды, имеющей вязкость меньше чем 45000 мПа/с при температуре стадии объединения и содержащей по меньшей мере одно циклическое органическое или ароматическое соединение в расплавленном состоянии или в растворе в концентрации меньше или равной 65 мас.%, для того, чтобы получить объединенный прекурсор (20), соответствующий структурированному прекурсору (10), покрытому неструктурированным прекурсором (15), причем этот процесс дополнительно содержит следующие стадии:
- стадию (200) термической и размерной стабилизации объединенного прекурсора (20) для того, чтобы получить волокно или набор волокон, покрытых циклическим или ароматическим органическим соединением (30), и
- стадию (300) карбонизации волокна или набора волокон, покрытых циклическим или ароматическим органическим соединением (30), для того, чтобы получить высокоуглеродистый материал (2).
2. Способ производства по п. 1, отличающийся тем, что циклическое или ароматическое органическое соединение выбирается из получаемых из биоисточников продуктов, выбираемых из: лигнина, целлюлозы, крахмала, гликогена, амилозы, амилопектина, декстрана, гемицеллюлозы, фруктозы или глюкоза, а также их производных; из продуктов, получаемых из нефти или ископаемых ресурсов, выбираемых из: пека, нафталина, фенантрена, антрацена, пирена или нафталинсульфата; а также из синтетических продуктов, выбираемых из фенольной смолы, смолы фенопласта или полиэпоксидной смолы.
3. Способ производства по одному из пп. 1 или 2, отличающийся тем, что неструктурированный прекурсор (15) содержит от 5 до 50 мас.% циклического органического или ароматического соединения.
4. Способ производства по любому из пп. 1-3, отличающийся тем, что текучая среда представляет собой водный раствор, или органический раствор, или их смесь.
5. Способ производства по любому из пп. 1-3, отличающийся тем, что текучая среда является расплавом.
6. Способ производства по любому из предшествующих пунктов, отличающийся тем, что циклическое органическое или ароматическое соединение имеет молекулярную массу больше чем 500 г/моль.
7. Способ производства по любому из предшествующих пунктов, отличающийся тем, что неструктурированный прекурсор (15) дополнительно содержит по меньшей мере одно дополнительное соединение, выбираемое из: металлических наполнителей, богатых углеродом соединений и органических частиц.
8. Способ производства по п. 7, отличающийся тем, что металлические наполнители содержат металлы, выбираемые из: бора, кремния, германия, мышьяка, лития, натрия, калия, титана, ванадия, марганца, железа, кобальта, никеля, молибдена, алюминия и свинца.
9. Способ производства по п. 7, отличающийся тем, что богатые углеродом соединения выбираются из: активированного угля, натурального антрацита, синтетического антрацита, сажи, натурального графита или синтетического графита.
10. Способ производства по п. 7, отличающийся тем, что органические частицы выбираются из: наноцеллюлозы, таннинов, хитозана или других биополимеров, которые не являются ни плавкими, ни растворимыми.
11. Способ производства по любому из предшествующих пунктов, отличающийся тем, что структурированный прекурсор (10) содержит по меньшей мере одно регулярное волокно (11) с диаметром от 0,5 до 300 мкм, предпочтительно от 1 мкм до 50 мкм.
12. Способ производства по любому из предшествующих пунктов, отличающийся тем, что структурированный прекурсор (10) содержит скрученный комплекс несвязанных между собой элементарных непрерывных волокон, нескрученный комплекс несвязанных между собой элементарных непрерывных волокон, набор нетканых волокон или набор тканых волокон.
13. Способ производства по любому из предшествующих пунктов, отличающийся тем, что структурированный прекурсор (10) содержит целлюлозные волокна, волокна гидроцеллюлозы, волокна лигнина, волокна пека или волокна PAN.
14. Способ производства по любому из предшествующих пунктов, отличающийся тем, что структурированный прекурсор (10) и/или неструктурированный прекурсор (15) содержат углеродсодержащие нанонаполнители в концентрации от 0,0001 до 30 мас.%, предпочтительно от 0,01 до 5 мас.%.
15. Способ производства по любому из предшествующих пунктов, отличающийся тем, что стадия (100) объединения и стадия (200) термической и размерной стабилизации повторяются один или более раз.
16. Способ производства по любому из предшествующих пунктов, отличающийся тем, что он дополнительно содержит стадию (400) формообразования высокоуглеродистого материала (2) с помощью любого процесса формования, такого как экструдирование, прессование, каландрирование, вытягивание или формовка, при температуре окружающей среды или с термической обработкой.
17. Процесс производства по любому из предшествующих пунктов, отличающийся тем, что он дополнительно содержит стадию (500) графитизации.
18. Волокно или набор волокон, покрытых органическим покрытием (30) в качестве промежуточного продукта, отличающиеся тем, что это органическое покрытие содержит по меньшей мере одно циклическое или ароматическое органическое соединение, выбираемое из:
- лигнина или производных лигнина, полисахаридов, таких как целлюлоза, крахмал, гликоген, амилоза, амилопектин, декстран, гемицеллюлоза, или фруктоза или глюкоза и их производные,
- пека, нафталина, фенантрена, антрацена, пирена или замещенных полициклических ароматических углеводородов, таких как нафталинсульфат, и
- фенольной смолы, смолы фенопласта или полиэпоксидной смолы,
и отличающиеся тем, что отношение массы волокна к массе циклического органического или ароматического соединения составляет от 1/5 до 100/1.
19. Высокоуглеродистый материал (2), отличающийся тем, что он является биструктурным и содержит структурированную часть, содержащую карбонизированное волокно или набор карбонизированных волокон, и неструктурированную часть, содержащую карбонизированное циклическое органическое или ароматическое соединение, а также тем, что он имеет общую пористость больше чем 5%, предпочтительно больше чем 10%.
20. Высокоуглеродистый материал (2) по п. 19, отличающийся тем, что структурированная часть имеет пористость меньше чем 40%, предпочтительно меньше чем 30%, в то время как неструктурированная часть имеет пористость больше чем 7%, предпочтительно больше чем 10%.
21. Высокоуглеродистый материал (2) по любому из пп. 19 или 20, отличающийся тем, что отношение объема структурированной части к объему неструктурированной части составляет от 1/5 до 100/1.
22. Высокоуглеродистый материал (2) по любому из пп. 19-21, отличающийся тем, что он содержит добавки, такие как металлические наполнители и/или соли металла, введенные в его неструктурированную часть в соответствии с процессом по пп. 1-8.
23. Высокоуглеродистый материал (2) по любому из пп. 19-22, отличающийся тем, что он имеет форму углеродного волокна, скрученного комплекса несвязанных между собой элементарных непрерывных волокон, множества нескрученных непрерывных элементарных волокон, набора нетканых углеродных волокон или набора тканых углеродных волокон.
24. Применение высокоуглеродистого материала по любому из пп. 19-23 для производства деталей из композиционного материала термопластичного или термореактивного типа.
25. Применение высокоуглеродистого материала по любому из пп. 19-23 для производства деталей, которые могут использоваться в качестве электрода в электрохимических процессах.
26. Применение высокоуглеродистого материала по любому из пп. 19-23 для производства деталей, которые могут использоваться в качестве анода для катодной защиты.
27. Применение высокоуглеродистого материала по любому из пп. 19-23 для производства деталей, которые могут использоваться в качестве электрода для топливных ячеек.
28. Применение высокоуглеродистого материала по любому из пп. 19-23 для производства деталей, которые могут использоваться в качестве электродного элемента для батарей и аккумуляторов.
29. Применение высокоуглеродистого материала по любому из пп. 19-23 для производства деталей, которые могут использоваться в качестве коллектора электрического тока для анодов или катодов литиевых или натриевых батарей.
30. Применение высокоуглеродистого материала по любому из пп. 19-23 для производства деталей, которые могут использоваться в качестве коллектора электрического тока для литиево-серных батарей.
31. Применение высокоуглеродистого материала по любому из пп. 19-23 для производства деталей, которые могут использоваться в качестве коллектора электрического тока для литиево-полимерных батарей.
32. Применение высокоуглеродистого материала по любому из пп. 19-23 для производства деталей, которые могут использоваться в качестве электродного элемента для свинцово-кислотных батарей, в частности для свинцовых или свинцово-углеродных ультрабатарей.
33. Применение высокоуглеродистого материала по любому из пп. 19-23 для производства деталей, которые могут использоваться в качестве электродного элемента для перезаряжаемых литиевых батарей.
34. Применение высокоуглеродистого материала по любому из пп. 19-23 для производства деталей, которые могут использоваться в качестве суперконденсаторного электродного элемента.
35. Применение высокоуглеродистого материала по любому из пп. 19-23 для производства деталей, которые могут использоваться в качестве каталитической подложки, в частности для очистки воздуха.
36. Применение высокоуглеродистого материала по любому из пп. 19-23 для производства деталей, которые могут использоваться в качестве каталитической подложки для литиево-воздушных батарей.
RU2019116177A 2016-10-28 2017-10-26 Новый способ производства высокоуглеродистых материалов и полученные высокоуглеродистые материалы RU2765203C2 (ru)