RU2017105280A - Покрытия с гибкими гиперразветвленными полиолами - Google Patents
Покрытия с гибкими гиперразветвленными полиолами Download PDFInfo
- Publication number
- RU2017105280A RU2017105280A RU2017105280A RU2017105280A RU2017105280A RU 2017105280 A RU2017105280 A RU 2017105280A RU 2017105280 A RU2017105280 A RU 2017105280A RU 2017105280 A RU2017105280 A RU 2017105280A RU 2017105280 A RU2017105280 A RU 2017105280A
- Authority
- RU
- Russia
- Prior art keywords
- groups
- carboxylic acid
- epoxy
- dicarboxylic acid
- polyol
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D167/00—Coating compositions based on polyesters obtained by reactions forming a carboxylic ester link in the main chain; Coating compositions based on derivatives of such polymers
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B05—SPRAYING OR ATOMISING IN GENERAL; APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
- B05D—PROCESSES FOR APPLYING FLUENT MATERIALS TO SURFACES, IN GENERAL
- B05D7/00—Processes, other than flocking, specially adapted for applying liquids or other fluent materials to particular surfaces or for applying particular liquids or other fluent materials
- B05D7/50—Multilayers
- B05D7/52—Two layers
- B05D7/53—Base coat plus clear coat type
- B05D7/532—Base coat plus clear coat type the two layers being cured or baked together, i.e. wet on wet
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G63/00—Macromolecular compounds obtained by reactions forming a carboxylic ester link in the main chain of the macromolecule
- C08G63/02—Polyesters derived from hydroxycarboxylic acids or from polycarboxylic acids and polyhydroxy compounds
- C08G63/12—Polyesters derived from hydroxycarboxylic acids or from polycarboxylic acids and polyhydroxy compounds derived from polycarboxylic acids and polyhydroxy compounds
- C08G63/16—Dicarboxylic acids and dihydroxy compounds
- C08G63/18—Dicarboxylic acids and dihydroxy compounds the acids or hydroxy compounds containing carbocyclic rings
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G63/00—Macromolecular compounds obtained by reactions forming a carboxylic ester link in the main chain of the macromolecule
- C08G63/02—Polyesters derived from hydroxycarboxylic acids or from polycarboxylic acids and polyhydroxy compounds
- C08G63/12—Polyesters derived from hydroxycarboxylic acids or from polycarboxylic acids and polyhydroxy compounds derived from polycarboxylic acids and polyhydroxy compounds
- C08G63/16—Dicarboxylic acids and dihydroxy compounds
- C08G63/20—Polyesters having been prepared in the presence of compounds having one reactive group or more than two reactive groups
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G63/00—Macromolecular compounds obtained by reactions forming a carboxylic ester link in the main chain of the macromolecule
- C08G63/66—Polyesters containing oxygen in the form of ether groups
- C08G63/668—Polyesters containing oxygen in the form of ether groups derived from polycarboxylic acids and polyhydroxy compounds
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
- C08G63/00—Macromolecular compounds obtained by reactions forming a carboxylic ester link in the main chain of the macromolecule
- C08G63/78—Preparation processes
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D201/00—Coating compositions based on unspecified macromolecular compounds
- C09D201/005—Dendritic macromolecules
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Engineering & Computer Science (AREA)
- Wood Science & Technology (AREA)
- Life Sciences & Earth Sciences (AREA)
- Health & Medical Sciences (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Materials Engineering (AREA)
- Paints Or Removers (AREA)
- Polyesters Or Polycarbonates (AREA)
- Application Of Or Painting With Fluid Materials (AREA)
- Epoxy Resins (AREA)
- Polyurethanes Or Polyureas (AREA)
Claims (21)
1. Композиция покрытия, включающая гибкий гиперразветвленный полиол, который получают путем
(а) реакции полиола, включающего как минимум три карбоксильных группы, с алифатической дикарбоновой кислотой, имеющей от 6 до 36 атомов углерода, или эстерифицируемой производной алифатической дикарбоновой кислоты для образования гидроксил-функционального первого промежуточного продукта;
(б) реакции первого промежуточного продукта с циклическим ангидридом карбоновой кислоты для образования карбоновокислотного второго функционального промежуточного продукта; и
(в) реакции второго промежуточного продукта с эпоксидным функциональным соединением, имеющим одну эпоксидную группу, для образования гиперразветвленного полиола.
2. Композиция покрытия по п. 1, отличающаяся тем, что соотношение на этапе (а) молей полиола с молями дикарбоновой кислоты или эстерифицируемой производной алифатической дикарбоновой кислоты составляет от приблизительно 2,0 до приблизительно 2,2 моль полиола на моль дикарбоновой кислоты или эстерифицируемой производной алифатической дикарбоновой кислоты.
3. Композиция покрытия по п. 1 или 2, отличающаяся тем, что эквивалентное соотношение на этапе (б) гидроксильных групп первого промежуточного продукта с ангидридными группами циклического ангидрида карбоновой кислоты составляет от приблизительно 1,0 до приблизительно 1,25 эквивалентов гидроксильных групп на карбоксильную ангидридную группу.
4. Композиция покрытия по любому из пп. 1-3, отличающаяся тем, что эквивалентное соотношение на этапе (в) карбоновокислотных групп второго промежуточного продукта с эпоксидными группами эпоксидного функционального соединения составляет от приблизительно 1,0 до приблизительно 2,5 эквивалентов карбоновокислотных групп на эквивалент эпоксидных групп.
5. Композиция покрытия по любому из пп. 1-3, отличающаяся тем, что композиция покрытия является водной и тем, что эквивалентное соотношение на этапе (в) карбоновокислотных групп второго промежуточного продукта с эпоксидными группами эпоксидного функционального соединения составляет от приблизительно 1,1 до приблизительно 2,5 эквивалента карбоновокислотных групп на эквивалент эпоксидных групп, и непрореагировавшие карбоновокислотные группы как минимум частично нейтрализуются основанием.
6. Способ покрытия основы, включающий нанесение на основу композиции покрытия по любому из пп. 1-5 для образования слоя покрытия и отверждение слоя покрытия.
7. Способ по п. 6, отличающийся тем, что слой покрытия является пигментным.
8. Способ по п. 7, отличающийся тем, что поверх слоя покрытия наносят лаковую композицию для образования лакового слоя, и слой покрытия и лаковый слой отверждают вместе.
9. Способ по п. 6, отличающийся тем, что слой покрытия является непигментированным.
10. Способ по любому из пп. 5-9, отличающийся тем, что слой покрытия наносят на основу в качестве реставрационного покрытия.
11. Способ получения гибкого гиперразветвленного полиола, включающий:
(а) реакцию полиола, включающего как минимум три карбоксильных группы, с алифатической дикарбоновой кислотой, имеющей от 6 до 36 атомов углерода, или эстерифицируемой производной алифатической дикарбоновой кислоты для образования гидроксил-функционального первого промежуточного продукта;
(б) реакцию первого промежуточного продукта с циклическим ангидридом карбоновой кислоты для образования карбоновокислотного второго функционального промежуточного продукта; и
(в) реакцию второго промежуточного продукта с эпоксидным функциональным соединением, имеющим одну эпоксидную группу, для образования гиперразветвленного полиола.
12. Способ по п. 11, отличающийся тем, что соотношение на этапе (а) молей полиола с молями дикарбоновой кислоты или эстерифицируемой производной алифатической дикарбоновой кислоты составляет от приблизительно 2,0 до приблизительно 2,2 моль полиола на моль дикарбоновой кислоты или эстерифицируемой производной алифатической дикарбоновой кислоты.
13. Способ по п. 11 или 12, отличающийся тем, что эквивалентное соотношение на этапе (б) гидроксильных групп первого промежуточного продукта с ангидридными группами циклического ангидрида карбоновой кислоты составляет от приблизительно 1,0 до приблизительно 1,25 эквивалентов гидроксильных групп на карбоксильную ангидридную группу.
14. Способ по любому из пп. 11-13, отличающийся тем, что эквивалентное соотношение на этапе (в) карбоновокислотных групп второго промежуточного продукта с эпоксидными группами эпоксидного функционального соединения составляет от приблизительно 1,0 до приблизительно 2,5 эквивалентов карбоновокислотных групп на эквивалент эпоксидных групп.
15. Способ по любому из пп. 11-13, отличающийся тем, что эквивалентное соотношение на этапе (в) карбоновокислотных групп второго промежуточного продукта с эпоксидными группами эпоксидного функционального соединения составляет от приблизительно 1,1 до приблизительно 2,5 эквивалента карбоновокислотных групп на эквивалент эпоксидных групп и непрореагировавшие карбоновокислотные группы как минимум частично нейтрализуются основанием, и гиперразветвленный полиол диспергируют в водной среде.