RU2013147375A - Горячекатаный стальной лист и соответствующий способ изготовления - Google Patents

Горячекатаный стальной лист и соответствующий способ изготовления Download PDF

Info

Publication number
RU2013147375A
RU2013147375A RU2013147375/02A RU2013147375A RU2013147375A RU 2013147375 A RU2013147375 A RU 2013147375A RU 2013147375/02 A RU2013147375/02 A RU 2013147375/02A RU 2013147375 A RU2013147375 A RU 2013147375A RU 2013147375 A RU2013147375 A RU 2013147375A
Authority
RU
Russia
Prior art keywords
steel
steel sheet
composition
less
sheet according
Prior art date
Application number
RU2013147375/02A
Other languages
English (en)
Other versions
RU2551727C2 (ru
Inventor
Астрид Перлад
Орели АМАР
Флоранс ПЕШНО
Эрик СТАНБАК
Жан Марк ПИПАР
Фарид Э. ХАССАНИ
Original Assignee
Арселормитталь Инвестигасьон И Десарролло Сл
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Арселормитталь Инвестигасьон И Десарролло Сл filed Critical Арселормитталь Инвестигасьон И Десарролло Сл
Publication of RU2013147375A publication Critical patent/RU2013147375A/ru
Application granted granted Critical
Publication of RU2551727C2 publication Critical patent/RU2551727C2/ru

Abstract

1. Горячекатаный стальной лист с пределом упругости более 690 МПа и менее или равным 840 МПа, с пределом прочности 780-950 МПа, относительным удлинением при разрыве более 10% и коэффициентом (Ас) раздачи отверстия более или равном 50%, химический состав которого включает, масс.%:0,040%≤55С≤0,065%1,4%≤Mn≤1,9%0,1%≤Si≤0,55%0,095%≤Ti≤0,145%0,025%≤Nb≤0,045%0,005%≤Al≤0,1%0,002%≤N≤0,007%S≤0,004%P≤0,020%необязательноCr≤0,7%Cu≤0,1%Ni≤0,25%В≤0,003%Са≤0,005%Mg≤0,005%остальное железо и неизбежные технологические примеси, микроструктура листа состоит из зернистого бейнита, феррита, цементита с процентной долей площади менее 1,5% и карбонитридов титана и ниобия, причем плотность нитридов титана со средним размером более 6 мкм менее или равна 3/мм, и отношение размера Dзерна, измеренного параллельно направлению прокатки, и размера Dзерна, измеренного перпендикулярно направлению прокатки, менее или равно 1,4.2. Стальной лист по п.1, характеризующийся тем, что отношение размера Dзерна, измеренного параллельно направлению прокатки, и размера Dзерна, измеренного перпендикулярно направлению прокатки, менее или равно 1,3.3. Стальной лист по п.1, характеризующийся тем, что химический состав включает, масс.%:0,045%≤С≤0,065%1,6%≤Mn≤1,9%0,1%≤Si≤0,55%0,095%≤Ti≤0,125%0,025%≤Nb≤0,045%0,01%≤Al≤0,1%0,002%≤N≤0,007%S≤0,004%P≤0,020%необязательноCu≤0,1%Ni≤0,25%В≤0,003%Са≤0,005%Mg≤0,005%причем указанная композиция не содержит хрома.4. Стальной лист по п.2, характеризующийся тем, что химический состав включает, масс.%:0,045%≤С≤0,065%1,6%≤Mn≤1,9%0,1%≤Si≤0,55%0,095%≤Ti≤0,125%0,025%≤Nb≤0,045%0,01%≤Al≤0,1%0,002%≤N≤0,007%S≤0,004%P≤0,020%необязательноCu≤0,1%Ni≤0,25%В≤0,003%Са≤0,005%Mg≤0,005%причем указанная композиция не содержит хрома.5. Стальной лист по любому из пп.1-4, характеризующийся тем, что состав стали �

Claims (26)

1. Горячекатаный стальной лист с пределом упругости более 690 МПа и менее или равным 840 МПа, с пределом прочности 780-950 МПа, относительным удлинением при разрыве более 10% и коэффициентом (Ас) раздачи отверстия более или равном 50%, химический состав которого включает, масс.%:
0,040%≤55С≤0,065%
1,4%≤Mn≤1,9%
0,1%≤Si≤0,55%
0,095%≤Ti≤0,145%
0,025%≤Nb≤0,045%
0,005%≤Al≤0,1%
0,002%≤N≤0,007%
S≤0,004%
P≤0,020%
необязательно
Cr≤0,7%
Cu≤0,1%
Ni≤0,25%
В≤0,003%
Са≤0,005%
Mg≤0,005%
остальное железо и неизбежные технологические примеси, микроструктура листа состоит из зернистого бейнита, феррита, цементита с процентной долей площади менее 1,5% и карбонитридов титана и ниобия, причем плотность нитридов титана со средним размером более 6 мкм менее или равна 3/мм2, и отношение размера DL зерна, измеренного параллельно направлению прокатки, и размера DN зерна, измеренного перпендикулярно направлению прокатки, менее или равно 1,4.
2. Стальной лист по п.1, характеризующийся тем, что отношение размера DL зерна, измеренного параллельно направлению прокатки, и размера DN зерна, измеренного перпендикулярно направлению прокатки, менее или равно 1,3.
3. Стальной лист по п.1, характеризующийся тем, что химический состав включает, масс.%:
0,045%≤С≤0,065%
1,6%≤Mn≤1,9%
0,1%≤Si≤0,55%
0,095%≤Ti≤0,125%
0,025%≤Nb≤0,045%
0,01%≤Al≤0,1%
0,002%≤N≤0,007%
S≤0,004%
P≤0,020%
необязательно
Cu≤0,1%
Ni≤0,25%
В≤0,003%
Са≤0,005%
Mg≤0,005%
причем указанная композиция не содержит хрома.
4. Стальной лист по п.2, характеризующийся тем, что химический состав включает, масс.%:
0,045%≤С≤0,065%
1,6%≤Mn≤1,9%
0,1%≤Si≤0,55%
0,095%≤Ti≤0,125%
0,025%≤Nb≤0,045%
0,01%≤Al≤0,1%
0,002%≤N≤0,007%
S≤0,004%
P≤0,020%
необязательно
Cu≤0,1%
Ni≤0,25%
В≤0,003%
Са≤0,005%
Mg≤0,005%
причем указанная композиция не содержит хрома.
5. Стальной лист по любому из пп.1-4, характеризующийся тем, что состав стали включает, масс.%:
0,1%≤Si≤0,3%.
6. Стальной лист по п.1, характеризующийся тем, что химический состав включает, масс.%:
0,040%≤С≤0,065%
1,4%≤Mn≤1,9%
0,1%≤Si≤0,4%
0,095%≤Ti≤0,145%
0,025%≤Nb≤0,045%
0,01%≤Al≤0,1%
0,002%≤N≤0,007%
0,2%≤Cr≤0,7%
S≤0,004%
P≤0,020%
необязательно
Cu≤0,1%
Ni≤0,25%
В≤0,003%
Са≤0,005%
Mg≤0,005%
7. Стальной лист по любому из пп.1, 2, 6, характеризующийся тем, что состав стали включает, масс.%:
0,4%≤Cr≤0,6%.
8. Стальной лист по любому из пп.1-4, 6, характеризующийся тем, что процентная доля площади зернистого бейнита составляет 80-95% и процентная доля площади феррита составляет менее 20%.
9. Стальной лист по п.5, характеризующийся тем, что процентная доля площади зернистого бейнита составляет 80-95% и процентная доля площади феррита составляет менее 20%.
10. Стальной лист по п.7, характеризующийся тем, что процентная доля площади зернистого бейнита составляет 80-95% и процентная доля площади феррита составляет менее 20%.
11. Стальной лист по любому из пп.1-4, 6, 9, 10, характеризующийся тем, что состав стали включает, масс.%:
0,0005%≤Са≤0,005%.
12. Стальной лист по п.5, характеризующийся тем, что состав стали включает, масс.%:
0,0005%≤Са≤0,005%.
13. Стальной лист по п.7, характеризующийся тем, что состав стали включает, масс.%:
0,0005%≤Са≤0,005%.
14. Стальной лист по п.8, характеризующийся тем, что состав стали включает, масс.%:
0,0005%≤Са≤0,005%.
15. Стальной лист по любому из пп.1-4, 6, 9, 10, 12-14, характеризующийся тем, что состав стали включает, масс.%:
0,0005%≤Mg≤0,005%.
16. Стальной лист по п.5, характеризующийся тем, что состав стали включает, масс.%:
0,0005%≤Mg≤0,005%.
17. Стальной лист по п.7, характеризующийся тем, что состав стали включает, масс.%:
0,0005%≤Mg≤0,005%.
18. Стальной лист по п.8, характеризующийся тем, что состав стали включает, масс.%:
0,0005%≤Mg≤0,005%.
19. Стальной лист по п.11, характеризующийся тем, что состав стали включает, масс.%:
0,0005%≤Mg≤0,005%.
20. Способ изготовления горячекатаного стального листа с пределом упругости более 690 МПа и менее или равным 840 МПа, пределом прочности 780-950 МПа и относительным удлинением при разрыве более 10%, характеризующийся тем, что жидкую сталь получают в форме жидкого металла, состав которого включает, масс.%:
0,040≤С≤0,065%
1,4%≤Mn≤1,9%
0,1%≤Si≤0,55%
0,095%≤Ti≤0,145%
0,025%≤Nb≤0,045%
0,005%≤Al≤0,1%
0,002%≤N≤0,007%
S≤0,004%
P≤0,020%
необязательно
Cr≤0,7%
Cu≤0,1%
Ni≤0,25%
В≤0,003%
Mg≤0,005%
остальное железо и неизбежные примеси,
проводят обработку вакуумом или SiCa; причем в последнем случае композиция включает также, масс%.
0,0005%≤Са≤0,005%;
количество титана [Ti] и азота [N], растворенного в жидком металле, удовлетворяет соотношению %[Ti]%[N]≤6·10-4%2, сталь разливают для получения отлитого полуфабриката;
указанный полуфабрикат необязательно нагревают до температуры 1160-1300°С, затем,
указанный отлитый полуфабрикат, подвергают горячей прокатке с температурой конца прокатки 880-930°С, со степенью обжатия предпоследнего прохода менее 0,25, степенью обжатия последнего прохода менее 0,15, с суммой двух степеней обжатия менее 0,37, с начальной температурой в начале предпоследнего прохода менее 960°С, для получения горячекатаного продукта, затем
указанный горячекатаный продукт охлаждают со скоростью 50-150°С/с для получения горячекатаного стального листа и затем указанный лист наматывают при температуре намотки 470-625°С.
21. Способ по п.20, характеризующийся тем, что сталь включает, масс.%:
0,045%≤С≤0,065%
1,6%≤Mn≤1,9%
0,1%≤Si≤0,3%
0,095%≤Ti≤0,125%
0,025%≤Nb≤0,045%
0,01%≤Al≤0,1%
0,002%≤N≤0,007%
S≤0,004%
P≤0,020%
необязательно
Cu≤0,1%
Ni≤0,25%
В≤0,003%
Mg≤0,005%
причем указанная композиция не содержит хрома.
22. Способ по п.21, характеризующийся тем, что намотку листа проводят при температуре между 515°С и строго 620°С.
23. Способ по любому из пп.20-22, характеризующийся тем, что лист наматывают при температуре намотки 515-560°С, затем
лист протравливают, затем
протравленный лист нагревают до температуры 600-750°С, затем протравленный лист охлаждают со скоростью 5-20°С/с,
и полученный лист покрывают цинком в подходящей ванне цинкования.
24. Способ по п.20, характеризующийся тем, что сталь включает, масс.%:
0,040%≤С≤0,065%
1,4%≤Mn≤1,9%
0,1%≤Si≤0,4%
0,095%≤Ti≤0,145%
0,025%≤Nb≤0,045%
0,005%≤Al≤0,1%
0,002%≤N≤0,007%
0,2%≤Cr≤0,7%
S≤0,004%
P≤0,020%
необязательно
Cu≤0,1%
Ni≤0,25%
В≤0,003%
Са≤0,005%
Mg≤0,005%
и лист наматывают при температуре 470-580°С.
25. Способ по п.20, характеризующийся тем, что сталь включает, масс.%:
0,4%≤Cr≤0,6%.
26. Способ по пп.24-25, характеризующийся тем, что, когда суммарное содержание Mn, Si и Cr составляет менее 2,35%, лист наматывают при температуре 520-580°С.
RU2013147375/02A 2011-03-24 2012-03-23 Горячекатаный стальной лист и соответствующий способ изготовления RU2551727C2 (ru)