UA113404C2 - Гарячекатаний сталевий лист та спосіб його виготовлення - Google Patents

Гарячекатаний сталевий лист та спосіб його виготовлення

Info

Publication number
UA113404C2
UA113404C2 UAA201312424A UAA201312424A UA113404C2 UA 113404 C2 UA113404 C2 UA 113404C2 UA A201312424 A UAA201312424 A UA A201312424A UA A201312424 A UAA201312424 A UA A201312424A UA 113404 C2 UA113404 C2 UA 113404C2
Authority
UA
Ukraine
Prior art keywords
sheet
mpa
equal
hot
less
Prior art date
Application number
UAA201312424A
Other languages
English (en)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed filed Critical
Publication of UA113404C2 publication Critical patent/UA113404C2/uk

Abstract

Винахід стосується головним чином гарячекатаного сталевого листа з межею текучості, більшою 690 МПа і меншоюм або рівною 840 МПа, з міцністю 780-950 MПa, відносним подовженням при розриві, більшим 10 % і коефіцієнтом (Ас) роздачі отвору, більшим або рівним 50 %.Хімічний склад листа винаходу включає, в мас. %: 0,040≤С≤0,065, 1,4≤Mn≤1,9, 0,1≤Si≤0,55, 0,095≤Ті≤0,145, 0,025≤Nb≤0,045, 0,005≤Аl≤0,1, 0,002≤N≤0,007, S≤0,004, Р<0,020.Мікроструктура листа за винаходом також складається з зернистого бейніту, фериту, цементиту в процентній частці площі, меншій 1,5 %, карбонітридів титану та ніобію, що приводить до коефіцієнта (Ас) роздачі отвору більшого або рівного 50 % і відношення розміру Dзерна, виміряного паралельно напрямку прокатки, і розміру Dзерна, виміряного перпендикулярно напрямку прокатки, меншого або рівного 1,4.Винахід також стосується способів виготовлення вищеописаного листа, зокрема, залежно від того, включає композиція хром або ні.
UAA201312424A 2011-03-24 2012-03-23 Гарячекатаний сталевий лист та спосіб його виготовлення UA113404C2 (xx)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/FR2011/000173 WO2012127125A1 (fr) 2011-03-24 2011-03-24 Tôle d'acier laminée à chaud et procédé de fabrication associé
PCT/FR2012/000104 WO2012127136A2 (fr) 2011-03-24 2012-03-23 Tôle d'acier laminée à chaud et procédé de fabrication associé

Publications (1)

Publication Number Publication Date
UA113404C2 true UA113404C2 (xx) 2017-01-25

Family

ID=44626377

Family Applications (1)

Application Number Title Priority Date Filing Date
UAA201312424A UA113404C2 (xx) 2011-03-24 2012-03-23 Гарячекатаний сталевий лист та спосіб його виготовлення

Country Status (16)

Country Link
US (1) US9540719B2 (uk)
EP (1) EP2689045B1 (uk)
JP (2) JP6182522B2 (uk)
KR (1) KR101544298B1 (uk)
CN (1) CN103534365B (uk)
BR (1) BR112013024416B8 (uk)
CA (1) CA2830853C (uk)
ES (1) ES2648787T3 (uk)
HU (1) HUE035730T2 (uk)
MA (1) MA35008B1 (uk)
MX (1) MX355871B (uk)
PL (1) PL2689045T3 (uk)
RU (1) RU2551727C2 (uk)
UA (1) UA113404C2 (uk)
WO (2) WO2012127125A1 (uk)
ZA (1) ZA201307002B (uk)

Families Citing this family (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012127125A1 (fr) * 2011-03-24 2012-09-27 Arcelormittal Investigatión Y Desarrollo Sl Tôle d'acier laminée à chaud et procédé de fabrication associé
KR101749948B1 (ko) 2013-04-15 2017-06-22 제이에프이 스틸 가부시키가이샤 고강도 열연 강판 및 그의 제조 방법
CN103602895B (zh) * 2013-11-29 2016-08-24 宝山钢铁股份有限公司 一种抗拉强度780MPa级高扩孔钢板及其制造方法
CN106103749A (zh) * 2014-01-24 2016-11-09 罗奇钢铁公司 热轧超高强度钢带产品
CN104018087B (zh) * 2014-04-04 2016-03-30 首钢总公司 屈服强度700MPa以上汽车大梁用钢的制造方法
WO2016005780A1 (fr) * 2014-07-11 2016-01-14 Arcelormittal Investigación Y Desarrollo Sl Tôle d'acier laminée à chaud et procédé de fabrication associé
WO2016016676A1 (fr) * 2014-07-30 2016-02-04 ArcelorMittal Investigación y Desarrollo, S.L. Procédé de fabrication de tôles d'acier, pour durcissement sous presse, et pièces obtenues par ce procédé
KR20170134729A (ko) 2015-04-10 2017-12-06 더 나노스틸 컴퍼니, 인코포레이티드 금속 합금에서의 에지 성형성의 개선
US10465260B2 (en) 2015-04-10 2019-11-05 The Nanosteel Company, Inc. Edge formability in metallic alloys
CN109689910B (zh) 2016-09-13 2021-08-27 日本制铁株式会社 钢板
WO2018096387A1 (en) * 2016-11-24 2018-05-31 Arcelormittal Hot-rolled and coated steel sheet for hot-stamping, hot-stamped coated steel part and methods for manufacturing the same
KR101899674B1 (ko) 2016-12-19 2018-09-17 주식회사 포스코 저온역 버링성이 우수한 고강도 강판 및 이의 제조방법
MX2019011711A (es) * 2017-03-31 2019-11-21 Nippon Steel Corp Lamina de acero laminada en caliente, pieza forjada de acero y metodo de produccion.
KR102098478B1 (ko) 2018-07-12 2020-04-07 주식회사 포스코 고강도, 고성형성, 우수한 소부경화성을 갖는 열연도금강판 및 그 제조방법
KR102098482B1 (ko) 2018-07-25 2020-04-07 주식회사 포스코 내충돌 특성이 우수한 고강도 강판 및 이의 제조방법
CN110066966B (zh) * 2019-05-22 2020-10-30 武汉钢铁有限公司 一种低内应力含钛高强钢及生产方法
CN112522597B (zh) * 2019-09-19 2022-10-21 宝山钢铁股份有限公司 一种含硼高扩孔钢及其生产方法
CN112575267A (zh) * 2019-09-27 2021-03-30 宝山钢铁股份有限公司 一种高扩孔复相钢及其制造方法
CN113122770B (zh) * 2019-12-31 2022-06-28 宝山钢铁股份有限公司 低碳低成本超高强复相钢板/钢带及其制造方法
DE102021104584A1 (de) * 2021-02-25 2022-08-25 Salzgitter Flachstahl Gmbh Hochfestes, warmgewalztes Stahlflachprodukt mit hoher lokaler Kaltumformbarkeit sowie ein Verfahren zur Herstellung eines solchen Stahlflachprodukts
CN114214559B (zh) * 2021-11-18 2022-06-24 湖南华菱涟源钢铁有限公司 热轧钢板材料及其制造方法和制品
CN114978926B (zh) * 2022-05-17 2023-09-19 电子科技大学 一种适用于确定性网络协议的仿真方法及设备
WO2024179680A1 (de) * 2023-03-02 2024-09-06 Thyssenkrupp Steel Europe Ag Warmgewalztes stahlflachprodukt und verfahren zur herstellung eines warmgewalzten stahlflachprodukts

Family Cites Families (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3417878B2 (ja) * 1999-07-02 2003-06-16 株式会社神戸製鋼所 伸びフランジ性および疲労特性に優れた高強度熱延鋼板およびその製法
JP4306078B2 (ja) * 2000-02-15 2009-07-29 Ｊｆｅスチール株式会社 焼付け硬化性および耐衝撃性に優れた高張力熱延鋼板およびその製造方法
JP3945180B2 (ja) * 2000-04-13 2007-07-18 住友金属工業株式会社 穴広げ性および延性が優れた高強度合金化溶融亜鉛めっき鋼板および高強度鋼板と、それらの製造方法
US6364968B1 (en) * 2000-06-02 2002-04-02 Kawasaki Steel Corporation High-strength hot-rolled steel sheet having excellent stretch flangeability, and method of producing the same
DE10161465C1 (de) * 2001-12-13 2003-02-13 Thyssenkrupp Stahl Ag Verfahren zum Herstellen von Warmband
FR2845694B1 (fr) * 2002-10-14 2005-12-30 Usinor Procede de fabrication de toles d'acier durcissables par cuisson, toles d'acier et pieces ainsi obtenues
JP4411005B2 (ja) 2003-04-04 2010-02-10 株式会社神戸製鋼所 成形性に優れた高強度熱延鋼板
JP4317417B2 (ja) 2003-10-17 2009-08-19 新日本製鐵株式会社 穴拡げ性と延性に優れた高強度薄鋼板
JP4305216B2 (ja) * 2004-02-24 2009-07-29 Ｊｆｅスチール株式会社 溶接部の靭性に優れる耐サワー高強度電縫鋼管用熱延鋼板およびその製造方法
KR20090078807A (ko) 2006-10-06 2009-07-20 엑손모빌 업스트림 리서치 캄파니 탁월한 변형 시효 저항성을 갖는 낮은 항복비의 복합조직강 라인파이프
EP2020451A1 (fr) 2007-07-19 2009-02-04 ArcelorMittal France Procédé de fabrication de tôles d'acier à hautes caractéristiques de résistance et de ductilité, et tôles ainsi produites
JP5304435B2 (ja) 2008-06-16 2013-10-02 新日鐵住金株式会社 穴広げ性に優れた熱延鋼板及びその製造方法
WO2012127125A1 (fr) * 2011-03-24 2012-09-27 Arcelormittal Investigatión Y Desarrollo Sl Tôle d'acier laminée à chaud et procédé de fabrication associé

Also Published As

Publication number Publication date
KR20130135972A (ko) 2013-12-11
JP2016047963A (ja) 2016-04-07
JP6182522B2 (ja) 2017-08-16
EP2689045B1 (fr) 2017-09-13
US9540719B2 (en) 2017-01-10
ZA201307002B (en) 2014-05-28
WO2012127136A3 (fr) 2012-11-15
WO2012127125A1 (fr) 2012-09-27
PL2689045T3 (pl) 2018-02-28
WO2012127136A2 (fr) 2012-09-27
RU2013147375A (ru) 2015-04-27
HUE035730T2 (en) 2018-05-28
KR101544298B1 (ko) 2015-08-12
US20140230970A1 (en) 2014-08-21
BR112013024416A2 (pt) 2016-12-20
RU2551727C2 (ru) 2015-05-27
ES2648787T3 (es) 2018-01-08
MX355871B (es) 2018-05-03
EP2689045A2 (fr) 2014-01-29
WO2012127125A8 (fr) 2012-11-29
CA2830853A1 (en) 2012-09-27
JP2014514443A (ja) 2014-06-19
CN103534365B (zh) 2015-04-15
BR112013024416B1 (pt) 2019-11-12
BR112013024416B8 (pt) 2020-01-28
MX2013010887A (es) 2013-12-16
MA35008B1 (fr) 2014-04-03
CN103534365A (zh) 2014-01-22
CA2830853C (en) 2016-01-12

Similar Documents

Publication Publication Date Title
UA113404C2 (xx) Гарячекатаний сталевий лист та спосіб його виготовлення
WO2016198940A3 (fr) Acier à haute résistance et procédé de fabrication
MX2016007664A (es) Acero de elevada resistencia y procedimiento de fabricacion.
MX2015017874A (es) Lamina de acero enrollada en frio, metodo de fabricacion y vehiculo.
MX2016009745A (es) Lamina de acero laminada en frio de alta resistencia y metodo para la fabricacion de la misma.
MX2016001013A (es) Hoja de acero que tiene propiedades mecanicas de resistencia y ductibilidad muy altas, metodo de fabricacion y uso de tales hojas.
MX356054B (es) Lámina de acero laminada en frío, de alta resistencia y método para la fabricación de la misma.
MY174201A (en) A high strength thin cast strip product and method for making the same
MX359273B (es) Lámina de acero laminada en caliente y método de fabricación de la misma.
MX2019001794A (es) Lamina de acero laminada en frio de alta resistencia y el metodo para su produccion.
UA107519C2 (uk) Гаряче- або холоднокатаний сталевий лист, спосіб його виготовлення та його застосування в автомобільній промисловості
UA92039C2 (uk) Композиція високоміцної пластичної сталі, лист сталі та його застосування, спосіб одержання гарячекатаного та холоднокатаного листа сталі
MX2017000496A (es) Hoja de acero laminada en caliente y metodo de fabricacion relacionado.
MX2018007641A (es) Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida.
UA99827C2 (uk) Сталь низької щільності з хорошою здатністю до штампування, сталевий лист, спосіб його виготовлення та застосування
MX2015007724A (es) Lamina de acero laminada en frio de alta resistencia con bajo limite de elasticidad y metodo para la fabricacion de la misma.
IN2014DN07404A (uk)
WO2013179115A8 (fr) Acier lamine a chaud ou a froid a faible densite, son procede de mise en oeuvre et son utilisation
MX2016014990A (es) Hoja de acero doblemente recocida que tiene resistencia mecanica alta y caracteristicas de ductilidad, metodo de fabricacion y uso de tales hojas.
MX2018009735A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
MX2020006703A (es) Placa de acero laminada en caliente y metodo para fabricar la misma.
MX340869B (es) Lamina de acero laminada en caliente para lamina de acero laminada en frio, lamina de acero laminada en caliente para lamina de acero galvanizada, y metodo para la fabricacion de las mismas.
MY176614A (en) Steel sheet for cans and method for manufacturing steel sheet for cans
PH12015502714A1 (en) Steel sheet for can and method for manufacturing the same
WO2009145562A3 (ko) 연성이 우수하고 에지부 균열이 없는 고강도 강판, 용융아연도금강판 및 그 제조방법