MX2016014990A - Hoja de acero doblemente recocida que tiene resistencia mecanica alta y caracteristicas de ductilidad, metodo de fabricacion y uso de tales hojas. - Google Patents

Hoja de acero doblemente recocida que tiene resistencia mecanica alta y caracteristicas de ductilidad, metodo de fabricacion y uso de tales hojas.

Info

Publication number
MX2016014990A
MX2016014990A MX2016014990A MX2016014990A MX2016014990A MX 2016014990 A MX2016014990 A MX 2016014990A MX 2016014990 A MX2016014990 A MX 2016014990A MX 2016014990 A MX2016014990 A MX 2016014990A MX 2016014990 A MX2016014990 A MX 2016014990A
Authority
MX
Mexico
Prior art keywords
double
steel sheet
sheets
manufacture
annealed steel
Prior art date
Application number
MX2016014990A
Other languages
English (en)
Inventor
Kegel Frédéric
Arlazarov Artem
Christophe HELL Jean-
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MX2016014990A publication Critical patent/MX2016014990A/es

Abstract

La invención se refiere a una hoja de acero doblemente recocida, cuya composición incluye, expresa en porcentaje en peso, 0.20% = C = 0.40%, 0.8% = Mn = 1.4%, 1.60% = Si = 3.00%, 0.015 = Nb = 0.150%, Al = 0.1 %, Cr = 1.0 %, S = 0.006%, P = 0.030%, Ti = 0.05%, V = 0.05%, B = 0.003%, N = 0.01%, el restante de la composición siendo constituido por hierro e impurezas inevitables que resultan del proceso, la microestructura siendo constituida, en porcentaje de área, de 10 a 30% de austenita residual, 30 a 60% de martensita recocida, 5 a 30% de bainita, 10 a 30% de martensita fresca y menos de 10% de ferrita.
MX2016014990A 2014-05-20 2015-05-07 Hoja de acero doblemente recocida que tiene resistencia mecanica alta y caracteristicas de ductilidad, metodo de fabricacion y uso de tales hojas. MX2016014990A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/IB2014/000785 WO2015177582A1 (fr) 2014-05-20 2014-05-20 Tôle d'acier doublement recuite à hautes caractéristiques mécaniques de résistance et ductilité, procédé de fabrication et utilisation de telles tôles
PCT/IB2015/000651 WO2015177615A1 (fr) 2014-05-20 2015-05-07 Tôle d'acier doublement recuite a hautes caracteristiques mecaniques de resistance et de ductilite, procede de fabrication et utilisation de telles tôles

Publications (1)

Publication Number Publication Date
MX2016014990A true MX2016014990A (es) 2017-03-31

Family

ID=50981580

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2016014990A MX2016014990A (es) 2014-05-20 2015-05-07 Hoja de acero doblemente recocida que tiene resistencia mecanica alta y caracteristicas de ductilidad, metodo de fabricacion y uso de tales hojas.

Country Status (16)

Country Link
US (1) US10995386B2 (es)
EP (1) EP3146083B1 (es)
JP (1) JP6433512B2 (es)
KR (2) KR101846116B1 (es)
CN (1) CN106604999B (es)
BR (1) BR112016026883B1 (es)
CA (1) CA2949855C (es)
ES (1) ES2692848T3 (es)
HU (1) HUE039794T2 (es)
MA (1) MA39417B1 (es)
MX (1) MX2016014990A (es)
PL (1) PL3146083T3 (es)
RU (1) RU2667947C2 (es)
TR (1) TR201815496T4 (es)
UA (1) UA114877C2 (es)
WO (2) WO2015177582A1 (es)

Families Citing this family (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101786318B1 (ko) * 2016-03-28 2017-10-18 주식회사 포스코 항복강도와 연성이 우수한 고강도 냉연강판, 도금강판 및 이들의 제조방법
WO2019092481A1 (en) 2017-11-10 2019-05-16 Arcelormittal Cold rolled steel sheet and a method of manufacturing thereof
WO2019092483A1 (en) * 2017-11-10 2019-05-16 Arcelormittal Cold rolled and heat treated steel sheet and a method of manufacturing thereof
WO2019092482A1 (en) 2017-11-10 2019-05-16 Arcelormittal Cold rolled heat treated steel sheet and a method of manufacturing thereof
WO2019111029A1 (en) * 2017-12-05 2019-06-13 Arcelormittal Cold rolled and annealed steel sheet and method of manufacturing the same
WO2019111028A1 (en) * 2017-12-05 2019-06-13 Arcelormittal Cold rolled and annealed steal sheet and method of manufacturing the same
DE102017223633A1 (de) * 2017-12-21 2019-06-27 Voestalpine Stahl Gmbh Kaltgewalztes Stahlflachprodukt mit metallischer Korrosionsschutzschicht und Verfahren zur Herstellung eines solchen
RU2768717C1 (ru) * 2018-11-30 2022-03-24 Арселормиттал Холоднокатаный отожжённый стальной лист с высокой степенью раздачи отверстия и способ его изготовления
WO2020229877A1 (en) * 2019-05-15 2020-11-19 Arcelormittal A cold rolled martensitic steel and a method for it's manufacture
KR102653635B1 (ko) * 2019-06-28 2024-04-03 닛폰세이테츠 가부시키가이샤 강판
CN110438407B (zh) * 2019-09-16 2020-11-03 益阳紫荆福利铸业有限公司 一种合金钢及其制备方法和应用
EP4043596B1 (en) * 2019-10-09 2024-03-13 Nippon Steel Corporation Steel sheet and method for manufacturing same
DE102021128327A1 (de) 2021-10-29 2023-05-04 Voestalpine Stahl Gmbh Kaltgewalztes stahlflachprodukt mit metallischer korrosionsschutzschicht und verfahren zur herstellung eines solchen

Family Cites Families (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5110611A (ja) 1974-07-16 1976-01-28 Kunimasa Ooide Kenchikuyoshitajizai
JPS5821260B2 (ja) 1974-08-23 1983-04-28 京セラミタ株式会社 フクシヤシサイダンキコウニオケル カミヅマリオボウシシタフクシヤキ
JPH01272720A (ja) 1988-04-22 1989-10-31 Kobe Steel Ltd 高延性高強度複合組織鋼板の製造法
EP1146132B1 (en) 1999-10-22 2007-02-21 JFE Steel Corporation Hot-dip galvanized steel sheet having high strength and also being excellent in formability and galvanizing property
CN1145709C (zh) 2000-02-29 2004-04-14 川崎制铁株式会社 应变时效硬化特性优良的高强度冷轧钢板及其制造方法
WO2002061161A1 (fr) 2001-01-31 2002-08-08 Kabushiki Kaisha Kobe Seiko Sho Feuillard en acier a haute resistance ayant une excellente formabilite, et son procede de production
JP4188581B2 (ja) 2001-01-31 2008-11-26 株式会社神戸製鋼所 加工性に優れた高強度鋼板およびその製造方法
EP1288322A1 (en) 2001-08-29 2003-03-05 Sidmar N.V. An ultra high strength steel composition, the process of production of an ultra high strength steel product and the product obtained
JP4400079B2 (ja) * 2002-03-29 2010-01-20 Ｊｆｅスチール株式会社 超微細粒組織を有する冷延鋼板の製造方法
JP4681290B2 (ja) 2004-12-03 2011-05-11 本田技研工業株式会社 高強度鋼板及びその製造方法
CN101120114B (zh) 2005-03-31 2013-11-06 株式会社神户制钢所 涂膜附着性、加工性及耐氢脆化特性优异的高强度冷轧钢板和机动车用钢零件
JP5095958B2 (ja) * 2006-06-01 2012-12-12 本田技研工業株式会社 高強度鋼板およびその製造方法
WO2008007785A1 (fr) * 2006-07-14 2008-01-17 Kabushiki Kaisha Kobe Seiko Sho Feuilles d'acier très résistantes et procédés de production de celles-ci
JP5402007B2 (ja) 2008-02-08 2014-01-29 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5418047B2 (ja) 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5400484B2 (ja) * 2009-06-09 2014-01-29 株式会社神戸製鋼所 伸び、伸びフランジ性および溶接性を兼備した高強度冷延鋼板
ES2719930T3 (es) * 2010-06-14 2019-07-16 Nippon Steel Corp Artículo moldeado estampado en caliente, proceso para la producción de chapa de acero para estampación en caliente y proceso para la producción de artículo moldeado estampado en caliente
JP5821260B2 (ja) * 2011-04-26 2015-11-24 Ｊｆｅスチール株式会社 成形性及び形状凍結性に優れた高強度溶融亜鉛めっき鋼板、並びにその製造方法
UA112771C2 (uk) 2011-05-10 2016-10-25 Арселормітталь Інвестігасьон І Десароло Сл Сталевий лист з високою механічною міцністю, пластичністю і формованістю, спосіб виготовлення та застосування таких листів
EP2524970A1 (de) * 2011-05-18 2012-11-21 ThyssenKrupp Steel Europe AG Hochfestes Stahlflachprodukt und Verfahren zu dessen Herstellung
US9745639B2 (en) * 2011-06-13 2017-08-29 Kobe Steel, Ltd. High-strength steel sheet excellent in workability and cold brittleness resistance, and manufacturing method thereof
US10174392B2 (en) 2011-07-06 2019-01-08 Nippon Steel & Sumitomo Metal Corporation Method for producing cold-rolled steel sheet
CN103781932B (zh) * 2011-07-06 2016-05-25 新日铁住金株式会社 冷轧钢板
JP5413539B2 (ja) 2011-09-30 2014-02-12 新日鐵住金株式会社 焼付硬化性に優れた高強度溶融亜鉛めっき鋼板、高強度合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
JP5764549B2 (ja) 2012-03-29 2015-08-19 株式会社神戸製鋼所 成形性および形状凍結性に優れた、高強度冷延鋼板、高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板、ならびにそれらの製造方法
WO2015011511A1 (fr) 2013-07-24 2015-01-29 Arcelormittal Investigación Y Desarrollo Sl Tôle d'acier à très hautes caractéristiques mécaniques de résistance et de ductilité, procédé de fabrication et utilisation de telles tôles

Also Published As

Publication number Publication date
CA2949855A1 (fr) 2015-11-26
JP6433512B2 (ja) 2018-12-05
EP3146083B1 (fr) 2018-07-25
US20170101695A1 (en) 2017-04-13
EP3146083A1 (fr) 2017-03-29
WO2015177582A1 (fr) 2015-11-26
WO2015177615A1 (fr) 2015-11-26
MA39417A1 (fr) 2017-04-28
CN106604999A (zh) 2017-04-26
KR20170002652A (ko) 2017-01-06
RU2016149784A (ru) 2018-06-21
TR201815496T4 (tr) 2018-11-21
JP2017519107A (ja) 2017-07-13
CN106604999B (zh) 2018-04-10
BR112016026883B1 (pt) 2021-02-09
RU2016149784A3 (es) 2018-06-21
RU2667947C2 (ru) 2018-09-25
MA39417B1 (fr) 2017-12-29
PL3146083T3 (pl) 2019-05-31
KR101846116B1 (ko) 2018-04-05
HUE039794T2 (hu) 2019-02-28
KR101987572B1 (ko) 2019-06-10
UA114877C2 (uk) 2017-08-10
ES2692848T3 (es) 2018-12-05
CA2949855C (fr) 2018-05-01
KR20170126512A (ko) 2017-11-17
US10995386B2 (en) 2021-05-04

Similar Documents

Publication Publication Date Title
MX2016014990A (es) Hoja de acero doblemente recocida que tiene resistencia mecanica alta y caracteristicas de ductilidad, metodo de fabricacion y uso de tales hojas.
MX2017015841A (es) Acero de alta resistencia y metodo de fabricacion.
MX2022004076A (es) Acero para conformado en caliente y pieza conformada en caliente fabricada de tal acero.
MX2016001013A (es) Hoja de acero que tiene propiedades mecanicas de resistencia y ductibilidad muy altas, metodo de fabricacion y uso de tales hojas.
MX2019003282A (es) Lamina de acero de alta resistencia y alta conformabilidad laminada en frio y tratada termicamente y metodo de fabricacion.
MX2017001374A (es) Procedimiento para la fabricacion de laminas de acero para el endurecimiento por presion y piezas obtenidas por este procedimiento.
MX2019007165A (es) Lamina de acero templada y recubierta que tiene excelente conformabilidad y metodo para fabricar la misma.
MX2016016129A (es) Hoja de acero galvanizada multifasica de alta resistencia, metodo de produccion y uso.
MX2016007664A (es) Acero de elevada resistencia y procedimiento de fabricacion.
MX2019007169A (es) Hoja de acero revestida y templada con excelente capacidad de formacion y un metodo para fabricar la misma.
MX2018008561A (es) Lamina de acero de alta resistencia que tiene excelente conformabilidad y un metodo de fabricacion de la misma.
MX2017000496A (es) Hoja de acero laminada en caliente y metodo de fabricacion relacionado.
MX2016009745A (es) Lamina de acero laminada en frio de alta resistencia y metodo para la fabricacion de la misma.
MX2015011027A (es) Hoja de acero laminada en caliente y metodo para fabricar la misma.
WO2008145871A3 (fr) Procede de fabrication de tôles d'acier laminees a froid et recuites a tres haute resistance, et tôles ainsi produites
MX350016B (es) Lámina de acero con altas propiedades de resistencia mecánica, ductilidad y de formación, método de producción de la misma y uso de dichas láminas.
IN2014DN09576A (es)
WO2015162939A8 (ja) 厚鋼板及びその製造方法
PH12017500557A1 (en) Steel sheet for cans and method for manufacturing steel sheet for cans
MX2016009530A (es) Producto plano de acero de alta resistencia con estructura bainitica-martensitica y procedimiento para la fabricacion de un producto plano de acero de este tipo.
MX2016014963A (es) Tira de acero que tiene alta resistencia y alta plasticidad, la tira de acero tiene un recubrimiento a base de zinc en caliente.
MX2017008296A (es) Laminas de acero galvanizado de alta resistencia y metodos para fabricar las mismas.
MX2017016905A (es) Acero resistente a la corrosion, metodo para producir dicho acero y uso del mismo.
FI20125063L (fi) Menetelmä sääkestävän kuumavalssatun ultralujan rakenneterästuotteen valmistamiseksi ja sääkestävä kuumavalssattu ultraluja rakenneterästuote
MX2017012242A (es) Partes con una estructura bainitica que tiene propiedades de alta resistencia y proceso de fabricacion.

Legal Events

Date Code Title Description
FG Grant or registration