MX355871B - Lamina de acero laminada en caliente y metodo asociado de fabricacion. - Google Patents

Lamina de acero laminada en caliente y metodo asociado de fabricacion.

Info

Publication number
MX355871B
MX355871B MX2013010887A MX2013010887A MX355871B MX 355871 B MX355871 B MX 355871B MX 2013010887 A MX2013010887 A MX 2013010887A MX 2013010887 A MX2013010887 A MX 2013010887A MX 355871 B MX355871 B MX 355871B
Authority
MX
Mexico
Prior art keywords
mpa
equal
hot
less
rolled steel
Prior art date
Application number
MX2013010887A
Other languages
English (en)
Other versions
MX2013010887A (es
Inventor
Perlade Astrid
Amard Aurélie
Pechenot Florence
Stenback Erik
Marc Pipard Jean
E Hassani Farid
Original Assignee
Arcelormittal Investigacion Y Desarrollo Sl
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal Investigacion Y Desarrollo Sl filed Critical Arcelormittal Investigacion Y Desarrollo Sl
Publication of MX2013010887A publication Critical patent/MX2013010887A/es
Publication of MX355871B publication Critical patent/MX355871B/es

Abstract

La invención se refiere principalmente a una lámina de acero laminada en caliente con un límite de elasticidad mayor de 690 MPa y menor de o igual a 840 MPa, con resistencia de entre 780 MPa y 950 MPa, alargamiento en la falla mayor de 10% y una proporción de expansión de agujero (Ac) mayor de o igual a 50%. La composición química de la lámina reivindicada por la invención contiene, por lo que los contenidos se expresan en por ciento en peso: 0.040% = C = 0.065%, 1.4% = Mn = 1.9%, 0.1% = Si = 0.55%, 0.095% = Ti = 0.145%, 0.025% = Nb = 0.045%, 0.005% = Al = 0.1%, 0.002% = N = 0.007%, S = 0.004%, P= 0.020. La microestructura de la lámina reivindicada por la invención consiste de vainita granular, ferrita, cementita en un porcentaje de área menor de 1.5%, y carbonitruros de titanio y niobio, que da por resultado una proporción de expansión de agujero (Ac) mayor de o igual a 50% y la relación entre el tamaño de grano DL medido paralelo a la dirección de laminación y el tamaño de grano DN medido perpendicular a la dirección de laminación es menor que o igual a 1.4. La invención también se refiere a métodos para la fabricación de la lámina descrita anteriormente, en particular dependiendo de si la composición incluye cromo o no.
MX2013010887A 2011-03-24 2012-03-23 Lamina de acero laminada en caliente y metodo asociado de fabricacion. MX355871B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/FR2011/000173 WO2012127125A1 (fr) 2011-03-24 2011-03-24 Tôle d'acier laminée à chaud et procédé de fabrication associé
PCT/FR2012/000104 WO2012127136A2 (fr) 2011-03-24 2012-03-23 Tôle d'acier laminée à chaud et procédé de fabrication associé

Publications (2)

Publication Number Publication Date
MX2013010887A MX2013010887A (es) 2013-12-16
MX355871B true MX355871B (es) 2018-05-03

Family

ID=44626377

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2013010887A MX355871B (es) 2011-03-24 2012-03-23 Lamina de acero laminada en caliente y metodo asociado de fabricacion.

Country Status (16)

Country Link
US (1) US9540719B2 (es)
EP (1) EP2689045B1 (es)
JP (2) JP6182522B2 (es)
KR (1) KR101544298B1 (es)
CN (1) CN103534365B (es)
BR (1) BR112013024416B8 (es)
CA (1) CA2830853C (es)
ES (1) ES2648787T3 (es)
HU (1) HUE035730T2 (es)
MA (1) MA35008B1 (es)
MX (1) MX355871B (es)
PL (1) PL2689045T3 (es)
RU (1) RU2551727C2 (es)
UA (1) UA113404C2 (es)
WO (2) WO2012127125A1 (es)
ZA (1) ZA201307002B (es)

Families Citing this family (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012127125A1 (fr) * 2011-03-24 2012-09-27 Arcelormittal Investigatión Y Desarrollo Sl Tôle d'acier laminée à chaud et procédé de fabrication associé
WO2014171062A1 (ja) * 2013-04-15 2014-10-23 Ｊｆｅスチール株式会社 高強度熱延鋼板およびその製造方法
CN103602895B (zh) * 2013-11-29 2016-08-24 宝山钢铁股份有限公司 一种抗拉强度780MPa级高扩孔钢板及其制造方法
WO2015110585A1 (en) * 2014-01-24 2015-07-30 Rautaruukki Oyj Hot-rolled ultrahigh strength steel strip product
CN104018087B (zh) * 2014-04-04 2016-03-30 首钢总公司 屈服强度700MPa以上汽车大梁用钢的制造方法
WO2016005780A1 (fr) 2014-07-11 2016-01-14 Arcelormittal Investigación Y Desarrollo Sl Tôle d'acier laminée à chaud et procédé de fabrication associé
WO2016016676A1 (fr) * 2014-07-30 2016-02-04 ArcelorMittal Investigación y Desarrollo, S.L. Procédé de fabrication de tôles d'acier, pour durcissement sous presse, et pièces obtenues par ce procédé
JP7059010B2 (ja) 2015-04-10 2022-04-25 ザ・ナノスティール・カンパニー・インコーポレーテッド 金属合金における端部形成能の改善
US10465260B2 (en) 2015-04-10 2019-11-05 The Nanosteel Company, Inc. Edge formability in metallic alloys
KR102226684B1 (ko) * 2016-09-13 2021-03-12 닛폰세이테츠 가부시키가이샤 강판
WO2018096387A1 (en) * 2016-11-24 2018-05-31 Arcelormittal Hot-rolled and coated steel sheet for hot-stamping, hot-stamped coated steel part and methods for manufacturing the same
KR101899674B1 (ko) 2016-12-19 2018-09-17 주식회사 포스코 저온역 버링성이 우수한 고강도 강판 및 이의 제조방법
WO2018179391A1 (ja) * 2017-03-31 2018-10-04 新日鐵住金株式会社 熱間圧延鋼板および鋼製鍛造部品ならびにそれらの製造方法
KR102098478B1 (ko) * 2018-07-12 2020-04-07 주식회사 포스코 고강도, 고성형성, 우수한 소부경화성을 갖는 열연도금강판 및 그 제조방법
KR102098482B1 (ko) * 2018-07-25 2020-04-07 주식회사 포스코 내충돌 특성이 우수한 고강도 강판 및 이의 제조방법
CN110066966B (zh) * 2019-05-22 2020-10-30 武汉钢铁有限公司 一种低内应力含钛高强钢及生产方法
CN112522597B (zh) * 2019-09-19 2022-10-21 宝山钢铁股份有限公司 一种含硼高扩孔钢及其生产方法
CN112575267A (zh) * 2019-09-27 2021-03-30 宝山钢铁股份有限公司 一种高扩孔复相钢及其制造方法
CN113122770B (zh) * 2019-12-31 2022-06-28 宝山钢铁股份有限公司 低碳低成本超高强复相钢板/钢带及其制造方法
DE102021104584A1 (de) * 2021-02-25 2022-08-25 Salzgitter Flachstahl Gmbh Hochfestes, warmgewalztes Stahlflachprodukt mit hoher lokaler Kaltumformbarkeit sowie ein Verfahren zur Herstellung eines solchen Stahlflachprodukts
CN114214559B (zh) * 2021-11-18 2022-06-24 湖南华菱涟源钢铁有限公司 热轧钢板材料及其制造方法和制品
CN114978926B (zh) * 2022-05-17 2023-09-19 电子科技大学 一种适用于确定性网络协议的仿真方法及设备

Family Cites Families (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3417878B2 (ja) * 1999-07-02 2003-06-16 株式会社神戸製鋼所 伸びフランジ性および疲労特性に優れた高強度熱延鋼板およびその製法
JP4306078B2 (ja) 2000-02-15 2009-07-29 Ｊｆｅスチール株式会社 焼付け硬化性および耐衝撃性に優れた高張力熱延鋼板およびその製造方法
JP3945180B2 (ja) 2000-04-13 2007-07-18 住友金属工業株式会社 穴広げ性および延性が優れた高強度合金化溶融亜鉛めっき鋼板および高強度鋼板と、それらの製造方法
US6364968B1 (en) * 2000-06-02 2002-04-02 Kawasaki Steel Corporation High-strength hot-rolled steel sheet having excellent stretch flangeability, and method of producing the same
DE10161465C1 (de) * 2001-12-13 2003-02-13 Thyssenkrupp Stahl Ag Verfahren zum Herstellen von Warmband
FR2845694B1 (fr) * 2002-10-14 2005-12-30 Usinor Procede de fabrication de toles d'acier durcissables par cuisson, toles d'acier et pieces ainsi obtenues
JP4411005B2 (ja) 2003-04-04 2010-02-10 株式会社神戸製鋼所 成形性に優れた高強度熱延鋼板
JP4317417B2 (ja) 2003-10-17 2009-08-19 新日本製鐵株式会社 穴拡げ性と延性に優れた高強度薄鋼板
JP4305216B2 (ja) * 2004-02-24 2009-07-29 Ｊｆｅスチール株式会社 溶接部の靭性に優れる耐サワー高強度電縫鋼管用熱延鋼板およびその製造方法
WO2008045631A2 (en) 2006-10-06 2008-04-17 Exxonmobil Upstream Research Company Low yield ratio dual phase steel linepipe with superior strain aging resistance
EP2020451A1 (fr) 2007-07-19 2009-02-04 ArcelorMittal France Procédé de fabrication de tôles d'acier à hautes caractéristiques de résistance et de ductilité, et tôles ainsi produites
JP5304435B2 (ja) * 2008-06-16 2013-10-02 新日鐵住金株式会社 穴広げ性に優れた熱延鋼板及びその製造方法
WO2012127125A1 (fr) * 2011-03-24 2012-09-27 Arcelormittal Investigatión Y Desarrollo Sl Tôle d'acier laminée à chaud et procédé de fabrication associé

Also Published As

Publication number Publication date
WO2012127125A1 (fr) 2012-09-27
CA2830853C (en) 2016-01-12
HUE035730T2 (en) 2018-05-28
BR112013024416B8 (pt) 2020-01-28
WO2012127125A8 (fr) 2012-11-29
ZA201307002B (en) 2014-05-28
KR20130135972A (ko) 2013-12-11
EP2689045A2 (fr) 2014-01-29
CA2830853A1 (en) 2012-09-27
KR101544298B1 (ko) 2015-08-12
RU2551727C2 (ru) 2015-05-27
RU2013147375A (ru) 2015-04-27
CN103534365B (zh) 2015-04-15
WO2012127136A3 (fr) 2012-11-15
US20140230970A1 (en) 2014-08-21
CN103534365A (zh) 2014-01-22
PL2689045T3 (pl) 2018-02-28
JP2016047963A (ja) 2016-04-07
WO2012127136A2 (fr) 2012-09-27
UA113404C2 (xx) 2017-01-25
EP2689045B1 (fr) 2017-09-13
JP2014514443A (ja) 2014-06-19
JP6182522B2 (ja) 2017-08-16
ES2648787T3 (es) 2018-01-08
US9540719B2 (en) 2017-01-10
MA35008B1 (fr) 2014-04-03
BR112013024416B1 (pt) 2019-11-12
MX2013010887A (es) 2013-12-16
BR112013024416A2 (pt) 2016-12-20

Similar Documents

Publication Publication Date Title
MX355871B (es) Lamina de acero laminada en caliente y metodo asociado de fabricacion.
MY174201A (en) A high strength thin cast strip product and method for making the same
MX359273B (es) Lámina de acero laminada en caliente y método de fabricación de la misma.
IN2012DE00320A (es)
MX2014001501A (es) Lamina de acero laminada en caliente de alta proporcion de rendimiento, que tiene excelente absorcion de energia de impacto a baja temperatura y resistencia al reblandecimiento de la haz y metodo de produccion de la misma.
MX2018007649A (es) Metodo para producir una lamina de acero recubierta de alta resistencia que tenga ductilidad y conformabilidad mejorada, y lamina de acero recubierta obtenida.
MX2016013898A (es) Placa de acero laminada en caliente para una pieza en blanco laminada a la medida, pieza en blanco laminada a la medida y metodos para producirlas.
MX2016001013A (es) Hoja de acero que tiene propiedades mecanicas de resistencia y ductibilidad muy altas, metodo de fabricacion y uso de tales hojas.
MX2019001794A (es) Lamina de acero laminada en frio de alta resistencia y el metodo para su produccion.
MX356054B (es) Lámina de acero laminada en frío, de alta resistencia y método para la fabricación de la misma.
MX2016007664A (es) Acero de elevada resistencia y procedimiento de fabricacion.
UA92039C2 (ru) Композиция высокопрочной пластичной стали, лист стали и его применение, способ получения горячекатанного и холоднокатанного листа из стали
MX2011012371A (es) Lamina de acero de alta resistencia, lamina de acero bañada en caliente, y lamina de acero bañada en caliente aleada que tienen excelentes caracteristicas a la fatiga, alargamiento y colision y metodo de fabricacion para tales laminas de acero.
MX2016009745A (es) Lamina de acero laminada en frio de alta resistencia y metodo para la fabricacion de la misma.
MX2013002893A (es) Chapa delgada de acero laminada en caliente de alta resistencia que tiene excelente resistencia a la fatiga y metodo para fabricar la misma.
MX357839B (es) Hoja de acero platinada con zinc de alta resistencia y lámina de acero de alta resistencia que tiene maleabilidad superior y método para producir cada una de ellas.
MX2013002906A (es) Lamina de acero de alta resistencia y lamina de acero revestida con zinc de alta resistencia que tiene excelente ductilidad y capacidad de embridado por estiramiento y metodo de fabricacion de las mismas.
WO2010011791A3 (en) Hot rolled dual phase steel sheet, and method of making the same
UA107519C2 (uk) Гаряче- або холоднокатаний сталевий лист, спосіб його виготовлення та його застосування в автомобільній промисловості
MX2017000496A (es) Hoja de acero laminada en caliente y metodo de fabricacion relacionado.
IN2014DN09576A (es)
BR112014015715A8 (pt) tubo de aço de alta resistência e chapa de aço de alta resistência excelentes em capacidade de deformação e tenacidade a baixa temperatura, e método de produção da chapa de aço
IN2015DN00772A (es)
MY168642A (en) High tensile strength steel for container and producing method of the same
MX356410B (es) Chapa de acero laminada en frio.

Legal Events

Date Code Title Description
FG Grant or registration