RU2008151942A - Способ нанесения покрытия на металлический субстрат - Google Patents
Способ нанесения покрытия на металлический субстрат Download PDFInfo
- Publication number
- RU2008151942A RU2008151942A RU2008151942/04A RU2008151942A RU2008151942A RU 2008151942 A RU2008151942 A RU 2008151942A RU 2008151942/04 A RU2008151942/04 A RU 2008151942/04A RU 2008151942 A RU2008151942 A RU 2008151942A RU 2008151942 A RU2008151942 A RU 2008151942A
- Authority
- RU
- Russia
- Prior art keywords
- component
- aiii
- composition
- aqueous composition
- meth
- Prior art date
Abstract
1. Способ нанесения покрытия на металлический субстрат, включающий нанесение неводной композиции непосредственно на металлический субстрат, в котором неводная композиция содержит ! А) от около 10 до 99,9 мас.% ненасыщенного (мет)акрилатного полимера или олигомера, состоящего из: ! а) ненасыщенного уретан метакрилатного полимера или олигомера, полученного взаимодействием: ! ai) одного или более органических полиизоцианатов и ! aii) одного или более -NH или -ОН функциональных соединений, имеющих среднечисловую молекулярную массу от около 60 до около 600, и ! aiii) 1) от 0 до около 100 мас.% моно-, ди-, три- или поли-гидроксил-C1-С10-алкил или С6-С10-арил(мет)акрилата, ! 2) от 0 до 100 мас.% ненасыщенного полимерного простоэфирного или сложноэфирного (мет)акрилат полиола, имеющего ОН число от около 30 до около 500 и полученного взаимодействием полимерного простоэфирного или полимерного сложноэфирного ди- или полиола с акриловой и/или метакриловой кислотой, и ! 3) или комбинацией aiii) 1) и aiii) 2), в которой массовые проценты компонентов aiii)1), aiii)2) рассчитаны относительно общей массы компонентов aiii)1) и aiii)2), и в сумме составляют 100% при эквивалентном соотношении изоцианата и гидроксила от около 0.9:1 до около 1:0.9, ! и ! D) от 0,1 до 10 мас.% одного или более фотоинициаторов, где мас.% компонента D) рассчитывается относительно общего количества компонентов А), В) и С), и где процентные доли компонентов А), В) и С) в сумме составляют 100%. ! 2. Способ по п.1, в котором наносится неводная композиция, при этом указанная композиция дополнительно содержит ! В) до 90 мас.% ненасыщенного эпокси(мет)акрилата, практически не содержащего эпоксидных групп и получаемого взаимодействием ! b
Claims (31)
1. Способ нанесения покрытия на металлический субстрат, включающий нанесение неводной композиции непосредственно на металлический субстрат, в котором неводная композиция содержит
А) от около 10 до 99,9 мас.% ненасыщенного (мет)акрилатного полимера или олигомера, состоящего из:
а) ненасыщенного уретан метакрилатного полимера или олигомера, полученного взаимодействием:
ai) одного или более органических полиизоцианатов и
aii) одного или более -NH или -ОН функциональных соединений, имеющих среднечисловую молекулярную массу от около 60 до около 600, и
aiii) 1) от 0 до около 100 мас.% моно-, ди-, три- или поли-гидроксил-C1-С10-алкил или С6-С10-арил(мет)акрилата,
2) от 0 до 100 мас.% ненасыщенного полимерного простоэфирного или сложноэфирного (мет)акрилат полиола, имеющего ОН число от около 30 до около 500 и полученного взаимодействием полимерного простоэфирного или полимерного сложноэфирного ди- или полиола с акриловой и/или метакриловой кислотой, и
3) или комбинацией aiii) 1) и aiii) 2), в которой массовые проценты компонентов aiii)1), aiii)2) рассчитаны относительно общей массы компонентов aiii)1) и aiii)2), и в сумме составляют 100% при эквивалентном соотношении изоцианата и гидроксила от около 0.9:1 до около 1:0.9,
и
D) от 0,1 до 10 мас.% одного или более фотоинициаторов, где мас.% компонента D) рассчитывается относительно общего количества компонентов А), В) и С), и где процентные доли компонентов А), В) и С) в сумме составляют 100%.
2. Способ по п.1, в котором наносится неводная композиция, при этом указанная композиция дополнительно содержит
В) до 90 мас.% ненасыщенного эпокси(мет)акрилата, практически не содержащего эпоксидных групп и получаемого взаимодействием
bi) одного или более органических соединений, содержащих по меньшей мере одну эпоксидную группу и имеющих среднечисловую молекулярную массу от около 130 до около 1000,
bii) от 1,3 до 3,0 карбоксильных эквивалентов органической двухосновной кислоты или ангидрида, имеющих среднечисловую молекулярную массу от около 98 до около 166,
biii) 1 гидрокси эквивалента продукта реакции, содержащего гидроксильную группу, полученного при эквивалентом соотношении карбокси к гидроксилу от 0.6:1 до 0.95:1 взаимодействием
1) (мет)акриловой кислоты и
2) три- или тетрагидрокси простоэфирного спирта, имеющего среднечисловую молекулярную массу от около 180 до около 1000 и содержащего по меньшей мере два этилен- и/или пропилен-оксидных фрагмента как часть простоэфирной структуры,
при этом соотношение реакционноспособных эквивалентов компонентов от bii) до biii) к эпоксидным эквивалентам компонента bi) составляет по меньшей мере около 1:1.
3. Способ по п.1, в котором наносится неводная композиция, при этом указанная композиция дополнительно содержит
С) до 100 мас.% реакционноспособных разбавителей, выбранных из моно-, ди-, три- или поли-С1-С10-алкил или С1-С10-арил{(мет)акрилатов}, или виниловых эфиров, или их смесей, где мас.% компонента С) рассчитывается относительно общего количества компонентов А) и В).
4. Способ по п.1, в котором наносится неводная композиция, при этом указанная композиция дополнительно содержит
Е) до 90 мас.% растворителя или смеси растворителей, где мас.% компонента Е) рассчитывается относительно общего количества компонентов А), В) и С).
5. Способ по любому из пп.1-4, в котором наносится композиция, содержащая от 10 до 85 мас.% компонента А), от 5 до 80 мас.% компонента В) и от 10 до 90 мас.% компонента С) и/или Е).
6. Способ по любому из пп.1-4, в котором наносится композиция, содержащая от 25 до 65 мас.% компонента А), от 10 до 50 мас.% компонента В) и от 25 до 75 мас.% компонента С) и/или Е).
7. Способ по п.1, в котором компонент aii)1) имеет ОН число от около 100 до около 400.
8. Способ по п.7, в котором компонент aii)1) имеет ОН число от около 100 до около 300.
9. Способ по п.1, в котором соотношение эквивалентов изоцианата к гидроксилу составляет около 1:1.
10. Способ по п.1, в котором в реакцию вступают от около 1,8 до около 2,2 карбокси эквивалентов органической двухосновной кислоты или ангидрида (компонент bii)).
11. Способ по п.10, в котором в реакцию вступают от около 1,9 до около 2,1 карбокси эквивалентов органической двухосновной кислоты или ангидрида (компонент bii)).
12. Способ по п.1, в котором компонент bi) содержит в среднем от 1,5 до 6 эпоксидных групп на молекулу.
13. Способ по п.12, в котором компонент bi) содержит в среднем от 1.5 до 2 эпоксидных групп на молекулу.
14. Способ по п.1, в котором соотношение эквивалентов карбокси к гидроксилу (компонент biii)) составляет от 0,65:1 до 0,9:1.
15. Способ по п.1, в котором металлический субстрат представляет собой свежеполученную или подвергшуюся воздействию окружающей среды оцинкованную сталь.
16. Способ по п.1, в котором металлический субстрат представляет собой обработанную или необработанную сталь.
17. Способ по п.1, в котором металлический субстрат представляет собой алюминий.
18. Способ по п.1, в котором металлический субстрат представляет собой металлический сплав.
19. Способ по п.1, дополнительно включающий отверждение композиции под действием УФ-излучения.
20. Способ по п.19, в котором излучение имеет длину волны 200 нм или больше.
21. Способ по п.19, в котором излучение имеет длину волны от 200 до 450 нм.
22. Способ по п.19, в котором излучение имеет длину волны от 320 до 420 нм.
23 Способ по п.19, в котором источником излучения является солнечный свет.
24. Способ по п.19, дополнительно включающий нанесение двухкомпонентной полиуретан-образующей композиции на затвердевшую неводную композицию.
25. Способ по п.24, в котором двухкомпонентная полиуретан-образующая композиция наносится после того, как неводная композиция подверглась обработке УФ-излучением.
26. Способ по п.24, в котором двухкомпонентная полиуретан-образующая композиция наносится до того или одновременно с тем, как неводная композиция подвергается обработке УФ-излучением.
27. Способ по п.24, в котором двухкомпонентная полиуретан-образующая композиция содержит полиизоцианатный компонент и реагирующий с изоцианатом компонент.
28. Способ по п.27, дополнительно включающий нанесение на субстрат -ОН или -NH-функционального соединения во время стадии нанесения на субстрат неводной композиции.
29. Способ по п.28, в котором двухкомпонентная полиуретан-образующая композиция имеет соотношение изоцианатных групп к группам, реагирующим с изоцианатами, равное единице или больше единицы.
30. Способ по п.27, дополнительно включающий нанесение на субстрат NCO-функционального соединения во время стадии нанесения на субстрат неводной композиции.
31. Способ по п.30, в котором двухкомпонентная полиуретан-образующая композиция имеет соотношение изоцианатных групп к группам, реагирующим с изоцианатами, от 20:1 до 1:20.