MX378702B - Metodo para producir una lamina de acero recubierta de alta resistencia que tiene resistencia y ductilidad mejoradas y lamina obtenida. - Google Patents

Metodo para producir una lamina de acero recubierta de alta resistencia que tiene resistencia y ductilidad mejoradas y lamina obtenida.

Info

Publication number
MX378702B
MX378702B MX2016017398A MX2016017398A MX378702B MX 378702 B MX378702 B MX 378702B MX 2016017398 A MX2016017398 A MX 2016017398A MX 2016017398 A MX2016017398 A MX 2016017398A MX 378702 B MX378702 B MX 378702B
Authority
MX
Mexico
Prior art keywords
temperature
strength
sheet
producing
coated steel
Prior art date
Application number
MX2016017398A
Other languages
English (en)
Other versions
MX2016017398A (es
Inventor
Dongwei Fan
Hyun Jo Jun
Rashmi Ranjan Mohanty
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=53269687&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=MX378702(B) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MX2016017398A publication Critical patent/MX2016017398A/es
Publication of MX378702B publication Critical patent/MX378702B/es

Abstract

Un método para producir una lámina de acero recubierta de alta resistencia que tiene un límite elástico YS de al menos 800 MPA, una resistencia a la tracción TS de > 1180 MPa, un alargamiento total > 14% y una proporción de expansión de orificio HER > 30%. El acero contiene en % en peso: 0.13% = C = 0.22%, 1.2% = Si = 1.8%, 1.8% = Mn = 2.2%, 0.10% = Mo = 0.20%, Nb = 0.05%, Al = 0.5%, siendo el resto Fe e impurezas inevitables. La lámina es templada a una temperatura TA mayor que Ac3 pero menor que 1000°C para más de 30 s, entonces se extinguió mediante temperatura de enfriamiento QT entre 325°C y 375°C, a una velocidad de enfriamiento suficiente para obtener una estructura que consiste de austenita y al menos 60% de martensita, siendo el contenido de austenita tal que la estructura final puede contener entre 3% y 15% de austenita residual y entre 85 y 97% de la suma de martensita y bainita, sin ferrita, entonces se calentó a una temperatura de partición PT entre 430°C y 480°C y se mantuvo a esta temperatura durante un tiempo de partición Pt entre 10 s y 90 s, entonces se recubrió con inmersión caliente y se enfrió a la temperatura ambiente. Se obtuvo la lámina recubierta.
MX2016017398A 2014-07-03 2015-07-03 Metodo para producir una lamina de acero recubierta de alta resistencia que tiene resistencia y ductilidad mejoradas y lamina obtenida. MX378702B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/IB2014/003249 WO2016001710A1 (en) 2014-07-03 2014-07-03 Method for producing a high strength coated steel having improved strength and ductility and obtained sheet
PCT/IB2015/055035 WO2016001891A1 (en) 2014-07-03 2015-07-03 Method for producing a high strength coated steel sheet having improved strength and ductility and obtained sheet

Publications (2)

Publication Number Publication Date
MX2016017398A MX2016017398A (es) 2017-05-01
MX378702B true MX378702B (es) 2025-03-10

Family

ID=53269687

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2016017398A MX378702B (es) 2014-07-03 2015-07-03 Metodo para producir una lamina de acero recubierta de alta resistencia que tiene resistencia y ductilidad mejoradas y lamina obtenida.

Country Status (16)

Country Link
US (2) US10995383B2 (es)
EP (1) EP3164512B1 (es)
JP (2) JP6515119B2 (es)
KR (1) KR102455376B1 (es)
CN (1) CN106536782B (es)
BR (1) BR112017000023B1 (es)
CA (1) CA2954140C (es)
ES (1) ES2701837T3 (es)
HU (1) HUE041424T2 (es)
MX (1) MX378702B (es)
PL (1) PL3164512T3 (es)
RU (1) RU2687284C2 (es)
TR (1) TR201818939T4 (es)
UA (1) UA118699C2 (es)
WO (2) WO2016001710A1 (es)
ZA (1) ZA201608672B (es)

Families Citing this family (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016001702A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength coated steel sheet having improved strength, ductility and formability
WO2016001700A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength steel sheet having improved strength, ductility and formability
WO2016001706A1 (en) * 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength steel sheet having improved strength and formability and obtained sheet
WO2016001710A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength coated steel having improved strength and ductility and obtained sheet
CN105886750A (zh) * 2016-04-18 2016-08-24 河北钢铁股份有限公司 1180MPa级Q&P钢的连续热镀锌方法
WO2018203111A1 (en) * 2017-05-05 2018-11-08 Arcelormittal Method for producing a high strength steel sheet having high ductility, formability and weldability, and obtained steel sheet
WO2019166852A1 (en) * 2018-02-27 2019-09-06 Arcelormittal Method for producing a press-hardened laser welded steel part and press-hardened laser welded steel part
CN109988969B (zh) * 2019-04-01 2021-09-14 山东钢铁集团日照有限公司 一种具有不同屈强比的冷轧q&p1180钢及其生产方法
CN109972036B (zh) * 2019-04-01 2021-09-10 山东钢铁集团日照有限公司 一种具有不同屈强比的热轧q&p1180钢及其制造方法
JP2021034838A (ja) 2019-08-22 2021-03-01 株式会社オートネットワーク技術研究所 出力装置
CN110964969B (zh) * 2019-11-27 2021-09-21 本钢板材股份有限公司 一种高强度热镀锌淬火配分钢及其生产方法
US20230243007A1 (en) * 2020-06-12 2023-08-03 Arcelormittal Cold rolled and heat-treated steel sheet and method of manufacturing thereof
WO2022206912A1 (zh) * 2021-04-02 2022-10-06 宝山钢铁股份有限公司 抗拉强度≥980MPa的低碳低合金TRIP钢或热镀锌TRIP钢及其制造方法

Family Cites Families (49)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5236145A (en) 1975-09-18 1977-03-19 Nippon Shokubai Kagaku Kogyo Co Ltd Molding resin composition
US4159218A (en) * 1978-08-07 1979-06-26 National Steel Corporation Method for producing a dual-phase ferrite-martensite steel strip
JP4608822B2 (ja) 2001-07-03 2011-01-12 Ｊｆｅスチール株式会社 プレス成形性と歪時効硬化特性に優れた高延性溶融亜鉛めっき鋼板およびその製造方法
US6746548B2 (en) * 2001-12-14 2004-06-08 Mmfx Technologies Corporation Triple-phase nano-composite steels
WO2004022794A1 (en) 2002-09-04 2004-03-18 Colorado School Of Mines Method for producing steel with retained austenite
KR100884104B1 (ko) 2004-01-14 2009-02-19 신닛뽄세이테쯔 카부시키카이샤 도금 밀착성 및 구멍 확장성이 우수한 용융 아연 도금 고강도 강판과 그 제조 방법
JP4510488B2 (ja) 2004-03-11 2010-07-21 新日本製鐵株式会社 成形性および穴拡げ性に優れた溶融亜鉛めっき複合高強度鋼板およびその製造方法
JP4367300B2 (ja) 2004-09-14 2009-11-18 Ｊｆｅスチール株式会社 延性および化成処理性に優れる高強度冷延鋼板およびその製造方法
JP4716358B2 (ja) 2005-03-30 2011-07-06 株式会社神戸製鋼所 強度と加工性のバランスに優れた高強度冷延鋼板およびめっき鋼板
US7887648B2 (en) 2005-12-28 2011-02-15 Kobe Steel, Ltd. Ultrahigh-strength thin steel sheet
JP4174592B2 (ja) 2005-12-28 2008-11-05 株式会社神戸製鋼所 超高強度薄鋼板
EP1832667A1 (fr) 2006-03-07 2007-09-12 ARCELOR France Procédé de fabrication de tôles d'acier à très hautes caractéristiques de résistance, de ductilité et de tenacité, et tôles ainsi produites
GB2439069B (en) 2006-03-29 2011-11-30 Kobe Steel Ltd High Strength cold-rolled steel sheet exhibiting excellent strength-workability balance and plated steel sheet
JP4974341B2 (ja) 2006-06-05 2012-07-11 株式会社神戸製鋼所 成形性、スポット溶接性、および耐遅れ破壊性に優れた高強度複合組織鋼板
JP4291860B2 (ja) 2006-07-14 2009-07-08 株式会社神戸製鋼所 高強度鋼板およびその製造方法
JP4411326B2 (ja) 2007-01-29 2010-02-10 株式会社神戸製鋼所 リン酸塩処理性に優れた高強度合金化溶融亜鉛めっき鋼板
EP1990431A1 (fr) 2007-05-11 2008-11-12 ArcelorMittal France Procédé de fabrication de tôles d'acier laminées à froid et recuites à très haute résistance, et tôles ainsi produites
EP2020451A1 (fr) 2007-07-19 2009-02-04 ArcelorMittal France Procédé de fabrication de tôles d'acier à hautes caractéristiques de résistance et de ductilité, et tôles ainsi produites
ATE516380T1 (de) 2007-08-15 2011-07-15 Thyssenkrupp Steel Europe Ag Dualphasenstahl, flachprodukt aus einem solchen dualphasenstahl und verfahren zur herstellung eines flachprodukts
ES2387040T3 (es) 2007-08-15 2012-09-12 Thyssenkrupp Steel Europe Ag Acero de doble fase, producto plano de un acero de doble fase de este tipo y procedimiento para la fabricación de un producto plano
MX2010002581A (es) * 2007-09-10 2010-04-30 Pertti J Sippola Metodo y aparato para la conformabilidad mejorada de acero galvanizado con resistencia a la traccion mejorada.
KR101399741B1 (ko) 2007-10-25 2014-05-27 제이에프이 스틸 가부시키가이샤 가공성이 우수한 고강도 용융 아연 도금 강판 및 그 제조 방법
KR101018131B1 (ko) * 2007-11-22 2011-02-25 주식회사 포스코 저온인성이 우수한 고강도 저항복비 건설용 강재 및 그제조방법
JP2009173959A (ja) 2008-01-21 2009-08-06 Nakayama Steel Works Ltd 高強度鋼板およびその製造方法
CN101225499B (zh) 2008-01-31 2010-04-21 上海交通大学 低合金超高强度复相钢及其热处理方法
JP5402007B2 (ja) * 2008-02-08 2014-01-29 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5418047B2 (ja) * 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5315956B2 (ja) 2008-11-28 2013-10-16 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5412182B2 (ja) 2009-05-29 2014-02-12 株式会社神戸製鋼所 耐水素脆化特性に優れた高強度鋼板
JP5703608B2 (ja) * 2009-07-30 2015-04-22 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5807368B2 (ja) 2010-06-16 2015-11-10 新日鐵住金株式会社 圧延方向に対して４５°の方向の均一伸びが極めて高い高強度冷延鋼板及びその製造方法
JP5136609B2 (ja) 2010-07-29 2013-02-06 Ｊｆｅスチール株式会社 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
EP2683839B1 (en) * 2011-03-07 2015-04-01 Tata Steel Nederland Technology B.V. Process for producing high strength formable steel and high strength formable steel produced therewith
JP5821260B2 (ja) * 2011-04-26 2015-11-24 Ｊｆｅスチール株式会社 成形性及び形状凍結性に優れた高強度溶融亜鉛めっき鋼板、並びにその製造方法
UA112771C2 (uk) 2011-05-10 2016-10-25 Арселормітталь Інвестігасьон І Десароло Сл Сталевий лист з високою механічною міцністю, пластичністю і формованістю, спосіб виготовлення та застосування таких листів
EP2524970A1 (de) 2011-05-18 2012-11-21 ThyssenKrupp Steel Europe AG Hochfestes Stahlflachprodukt und Verfahren zu dessen Herstellung
JP2012240095A (ja) 2011-05-20 2012-12-10 Kobe Steel Ltd 高強度鋼板の温間成形方法
JP5824283B2 (ja) 2011-08-17 2015-11-25 株式会社神戸製鋼所 室温および温間での成形性に優れた高強度鋼板
JP5834717B2 (ja) 2011-09-29 2015-12-24 Ｊｆｅスチール株式会社 高降伏比を有する溶融亜鉛めっき鋼板およびその製造方法
RU2474623C1 (ru) 2011-10-31 2013-02-10 Валентин Николаевич Никитин Способ производства высокопрочной листовой стали мартенситного класса и деформационно-термический комплекс для его осуществления
JP5632904B2 (ja) * 2012-03-29 2014-11-26 株式会社神戸製鋼所 加工性に優れた高強度冷延鋼板の製造方法
JP2013237923A (ja) 2012-04-20 2013-11-28 Jfe Steel Corp 高強度鋼板およびその製造方法
JP2014019928A (ja) 2012-07-20 2014-02-03 Jfe Steel Corp 高強度冷延鋼板および高強度冷延鋼板の製造方法
KR20150029736A (ko) 2012-07-31 2015-03-18 제이에프이 스틸 가부시키가이샤 성형성 및 형상 동결성이 우수한 고강도 용융 아연 도금 강판, 그리고 그의 제조 방법
JP5857909B2 (ja) * 2012-08-09 2016-02-10 新日鐵住金株式会社 鋼板およびその製造方法
WO2016001710A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength coated steel having improved strength and ductility and obtained sheet
WO2016001706A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength steel sheet having improved strength and formability and obtained sheet
WO2016001700A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength steel sheet having improved strength, ductility and formability
WO2016001702A1 (en) 2014-07-03 2016-01-07 Arcelormittal Method for producing a high strength coated steel sheet having improved strength, ductility and formability

Also Published As

Publication number Publication date
JP2017524823A (ja) 2017-08-31
US20210095357A1 (en) 2021-04-01
RU2016151388A3 (es) 2018-11-22
WO2016001891A1 (en) 2016-01-07
KR102455376B1 (ko) 2022-10-14
JP6843176B2 (ja) 2021-03-17
RU2687284C2 (ru) 2019-05-13
HUE041424T2 (hu) 2019-05-28
EP3164512B1 (en) 2018-09-12
RU2016151388A (ru) 2018-06-26
BR112017000023B1 (pt) 2021-03-23
JP2019151933A (ja) 2019-09-12
ZA201608672B (en) 2019-10-30
CA2954140C (en) 2022-06-07
UA118699C2 (uk) 2019-02-25
CN106536782A (zh) 2017-03-22
EP3164512A1 (en) 2017-05-10
KR20170026406A (ko) 2017-03-08
BR112017000023A2 (pt) 2017-11-07
CN106536782B (zh) 2020-04-03
JP6515119B2 (ja) 2019-05-15
WO2016001710A1 (en) 2016-01-07
PL3164512T3 (pl) 2019-02-28
ES2701837T3 (es) 2019-02-26
US20170130290A1 (en) 2017-05-11
CA2954140A1 (en) 2016-01-07
MX2016017398A (es) 2017-05-01
TR201818939T4 (tr) 2019-01-21
US10995383B2 (en) 2021-05-04

Similar Documents

Publication Publication Date Title
MX385499B (es) Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida.
MX389187B (es) Metodo para producir una hoja de acero de alta resistencia que tiene resistencia y capacidad de formacion mejoradas y hoja obtenida.
MX2016017399A (es) Metodo para producir una hoja de acero recubierta de alta resistencia con una resistencia, ductilidad y capacidad de formacion mejoradas.
WO2016001898A3 (en) Method for producing a high strength steel sheet having improved strength, ductility and formability
MX377793B (es) Metodo para producir una hoja de acero recubierta que tiene resistencia, ductilidad y conformabilidad mejoradas.
MX2016017398A (es) Metodo para producir una lamina de acero recubierta de alta resistencia que tiene resistencia y ductilidad mejoradas y lamina obtenida.
UA119459C2 (uk) Спосіб виготовлення високоміцного сталевого листа і одержаний лист
MX380198B (es) Método para producir una chapa de acero revestida o no revestida de resistencia ultra alta y chapa obtenida.
UA117865C2 (uk) Високоміцна багатофазна сталь, спосіб її одержання та застосування
MX2019006862A (es) Producto de acero plano laminado en caliente y metodo para la produccion del mismo.
MX380199B (es) Método para producir una hoja de acero de alta resistencia que tiene capacidad de formación mejorada y hoja obtenida por dicho método.
MX378118B (es) Metodo para producir un producto de acero plano laminado en frio con alto limite elastico y producto de acero plano laminado en frio.
MX375454B (es) Metodo para la fabricacion de una hoja de acero de alta resistencia que tiene formabilidad y ductilidad mejoradas y hoja obtenida.
MX2016014963A (es) Tira de acero que tiene alta resistencia y alta plasticidad, la tira de acero tiene un recubrimiento a base de zinc en caliente.
UA118793C2 (uk) Спосіб виготовлення високоміцного сталевого листа і одержаний лист
MX386813B (es) Método para producir una hoja de acero galvano-recocido de ultra alta resistencia y hoja de acero galvano-recocido obtenida.
MX390428B (es) Método de producción de lámina de acero revestida de alta resistencia con resistencia y conformabilidad mejoradas.
MX2024009382A (es) Metodo para producir una lamina de acero de alta resistencia que tiene alta ductilidad, formabilidad y soldadura y lamina de acero obtenida.
MX393745B (es) Metodo para producir una hoja de acero que tiene resistencia, ductilidad y formabilidad mejoradas.
MX2017008296A (es) Laminas de acero galvanizado de alta resistencia y metodos para fabricar las mismas.
MX2015013579A (es) Lamina de acero recocida despues de galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MX2019009600A (es) Lamina de acero laminada en frio y metodo para fabricar la misma.
TH2401007863A (th) วิธีการผลิต แผ่นเหล็กกล้าเคลือบ หรือไม่เคลือบ ความแข็งแรงสูงยิ่งยวดและแผ่นเหล็กกล้าได้จากการนั้น
TH1601006097A (th) วิธีการสำหรับการผลิตผลิตภัณฑ์เหล็กกล้าแบนรีดเย็นที่มีความแข็งแรงครากสูง และผลิตภัณฑ์เหล็กกล้ารีดเย็นชนิดแบน
TH170799A (th) แผ่นเหล็กกล้ากัลวาไนซ์ทนแรงสูง และ วิธีการสำหรับการผลิตสิ่งเดียวกันนี้