CN110964969B - 一种高强度热镀锌淬火配分钢及其生产方法 - Google Patents
一种高强度热镀锌淬火配分钢及其生产方法 Download PDFInfo
- Publication number
- CN110964969B CN110964969B CN201911178880.0A CN201911178880A CN110964969B CN 110964969 B CN110964969 B CN 110964969B CN 201911178880 A CN201911178880 A CN 201911178880A CN 110964969 B CN110964969 B CN 110964969B
- Authority
- CN
- China
- Prior art keywords
- steel
- dip galvanized
- quenching
- temperature
- hot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (7)