MX378469B - Artìculo moldeado por estampado en caliente, làmina de acero enrollada en frio, y mètodo para manufacturar el artìculo moldeado por estampado en caliente. - Google Patents

Artìculo moldeado por estampado en caliente, làmina de acero enrollada en frio, y mètodo para manufacturar el artìculo moldeado por estampado en caliente.

Info

Publication number
MX378469B
MX378469B MX2015013878A MX2015013878A MX378469B MX 378469 B MX378469 B MX 378469B MX 2015013878 A MX2015013878 A MX 2015013878A MX 2015013878 A MX2015013878 A MX 2015013878A MX 378469 B MX378469 B MX 378469B
Authority
MX
Mexico
Prior art keywords
stamp
molded article
hot
area ratio
martensite
Prior art date
Application number
MX2015013878A
Other languages
English (en)
Other versions
MX2015013878A (es
Inventor
Koichi Sato
Manabu NARUSE
Toshiki Nonaka
Yasunori Iwasa
Yoshifumi Kobayashi
Yoshihiro Suwa
Original Assignee
Nippon Steel Corp Star
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp Star filed Critical Nippon Steel Corp Star
Publication of MX2015013878A publication Critical patent/MX2015013878A/es
Publication of MX378469B publication Critical patent/MX378469B/es

Abstract

Un acero estampado en caliente de acuerdo con la presente invención comprende componentes químicos específicos, en donde se cumple con fa relación representada por la fórmula: (5 x [Si] + [Mn])/[C]> 10 en la cual [C], [Si] y [Mo] representan respectivamente los contenidos, en % en masa de C, Si y Mn, una ferrita y una martensita están contendías respectivamente en una relación de área de 40 a 95% inclusive y de 5 a 60% inclusive, la suma total de la relación de área de la ferrita y la relación del área de la martensita es de 60% o más, por lo menos uno de una perlita a una relación de área de 10% o menos, una austenita retenida a una relación en volumen de 5% o menos y una bainita a una relación de área de menos de 40% puede estar contenido, la dureza de la martensita como se mide en un nanoindentador cumple con una relación representada por la fórmula H2/H1<1.l0 y una relación representada por la fórmula: dHM<20, y un valor de TSx?, que es un producto de una resistencia a la tensión (TS) y una relación de expansión de orificio (?), cumple con 50000 MPa % o más.
MX2015013878A 2013-04-02 2014-03-27 Artìculo moldeado por estampado en caliente, làmina de acero enrollada en frio, y mètodo para manufacturar el artìculo moldeado por estampado en caliente. MX378469B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013076835 2013-04-02
PCT/JP2014/058950 WO2014162984A1 (ja) 2013-04-02 2014-03-27 ホットスタンプ成形体、冷延鋼板、及びホットスタンプ成形体の製造方法

Publications (2)

Publication Number Publication Date
MX2015013878A MX2015013878A (es) 2015-12-11
MX378469B true MX378469B (es) 2025-03-11

Family

ID=51658282

Family Applications (2)

Application Number Title Priority Date Filing Date
MX2015013878A MX378469B (es) 2013-04-02 2014-03-27 Artìculo moldeado por estampado en caliente, làmina de acero enrollada en frio, y mètodo para manufacturar el artìculo moldeado por estampado en caliente.
MX2020010051A MX2020010051A (es) 2013-04-02 2015-09-30 Articulo moldeado por estampado en caliente, lamina de acero enrollada en frio, y metodo para manufacturar el articulo moldeado por estampado en caliente.

Family Applications After (1)

Application Number Title Priority Date Filing Date
MX2020010051A MX2020010051A (es) 2013-04-02 2015-09-30 Articulo moldeado por estampado en caliente, lamina de acero enrollada en frio, y metodo para manufacturar el articulo moldeado por estampado en caliente.

Country Status (13)

Country Link
US (2) US10544475B2 (es)
EP (2) EP3456855B1 (es)
JP (1) JP6225988B2 (es)
KR (1) KR101687931B1 (es)
CN (1) CN105074038B (es)
BR (1) BR112015024777B1 (es)
CA (1) CA2908356C (es)
ES (1) ES2712379T3 (es)
MX (2) MX378469B (es)
PL (1) PL2982772T3 (es)
RU (1) RU2627313C2 (es)
TW (1) TWI515310B (es)
WO (1) WO2014162984A1 (es)

Families Citing this family (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101417260B1 (ko) * 2012-04-10 2014-07-08 주식회사 포스코 재질 균일성이 우수한 고탄소 열연강판 및 이의 제조방법
WO2016103682A1 (ja) * 2014-12-25 2016-06-30 新日鐵住金株式会社 パネル状成形品及びパネル状成形品の製造方法
CN105479116B (zh) * 2015-12-30 2018-01-30 浙江吉利汽车研究院有限公司 一种高强度扭力梁横梁的制作方法
CN106399837B (zh) * 2016-07-08 2018-03-13 东北大学 热冲压成形用钢材、热冲压成形工艺及热冲压成形构件
KR20180011004A (ko) * 2016-07-22 2018-01-31 현대제철 주식회사 핫 스탬핑용 강재 및 이의 제조방법, 핫스탬핑 부품 및 이에 의해 제조 방법
TWI613300B (zh) * 2016-09-06 2018-02-01 新日鐵住金股份有限公司 高強度冷軋鋼板
WO2018096387A1 (en) * 2016-11-24 2018-05-31 Arcelormittal Hot-rolled and coated steel sheet for hot-stamping, hot-stamped coated steel part and methods for manufacturing the same
KR101949027B1 (ko) * 2017-07-07 2019-02-18 주식회사 포스코 초고강도 열연강판 및 그 제조 방법
CN107675077B (zh) * 2017-09-21 2019-01-29 燕山大学 一种中碳纳米贝氏体超高强度钢、钢棒及其制备方法
US11208705B2 (en) 2017-11-15 2021-12-28 Nippon Steel Corporation High-strength cold-rolled steel sheet
MX2020009944A (es) * 2018-03-27 2020-10-16 Kobe Steel Ltd Placa de acero para estampado en caliente.
JP6460287B1 (ja) * 2018-03-29 2019-01-30 新日鐵住金株式会社 ホットスタンプ用鋼板
TWI667351B (zh) * 2018-03-29 2019-08-01 日商日本製鐵股份有限公司 Hot stamping
CN110760765B (zh) * 2018-07-27 2021-03-12 宝山钢铁股份有限公司 超低成本、高延伸率及抗应变时效脆化600MPa级调质钢板及其制造方法
JP7151878B2 (ja) * 2019-04-01 2022-10-12 日本製鉄株式会社 ホットスタンプ成形品およびホットスタンプ用鋼板、並びにそれらの製造方法
KR102633542B1 (ko) * 2019-04-01 2024-02-06 닛폰세이테츠 가부시키가이샤 핫 스탬프 성형품 및 그 제조 방법
CN110257702B (zh) * 2019-06-24 2021-04-27 鞍钢股份有限公司 一种热冲压成形用钢及其热成形方法
CN110295325A (zh) * 2019-07-22 2019-10-01 唐山不锈钢有限责任公司 Ti微合金化540MPa级高扩孔钢钢带及其生产方法
JP7235621B2 (ja) * 2019-08-27 2023-03-08 株式会社神戸製鋼所 低強度ホットスタンプ用鋼板、ホットスタンプ部品およびホットスタンプ部品の製造方法
EP4079913A4 (en) * 2019-12-20 2023-02-22 Posco STEEL FOR HOT FORMING, HOT FORMED ELEMENT AND METHOD OF MANUFACTURE THEREOF
WO2021145445A1 (ja) 2020-01-16 2021-07-22 日本製鉄株式会社 ホットスタンプ成形体
WO2021145442A1 (ja) * 2020-01-16 2021-07-22 日本製鉄株式会社 ホットスタンプ成形体
EP4208576A1 (de) 2020-09-01 2023-07-12 ThyssenKrupp Steel Europe AG Durch warmumformen eines stahlflachprodukts hergestelltes stahlbauteil, stahlflachprodukt und verfahren zur herstellung eines stahlbauteils
KR102399887B1 (ko) * 2020-12-09 2022-05-20 현대제철 주식회사 핫 스탬핑 부품 및 이의 제조 방법
WO2022195024A1 (en) * 2021-03-17 2022-09-22 Tata Steel Ijmuiden B.V. Steel strip, sheet or blank and method for producing a hot-formed part or a heat-treated pre-formed part
JP2023538796A (ja) 2021-07-30 2023-09-12 ヒュンダイ スチール カンパニー 熱間プレス用鋼板及びそれを用いて製造されたアルミニウム系メッキブランク
WO2023041954A1 (en) * 2021-09-14 2023-03-23 Arcelormittal High strength high slenderness part having excellent energy absorption
CN116837285B (zh) * 2023-06-09 2026-01-30 河北河钢材料技术研究院有限公司 一种490MPa级双相钢外板及其生产方法
CN118668139B (zh) * 2024-08-23 2024-11-05 乌海市包钢万腾钢铁有限责任公司 含Ce厚壁热轧S275J0钢桩的生产工艺及制备方法

Family Cites Families (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH01189842A (ja) 1988-01-25 1989-07-31 Mitsubishi Electric Corp 画像表示装置
JPH06128688A (ja) 1992-10-20 1994-05-10 Sumitomo Metal Ind Ltd 疲労特性に優れた熱延鋼板およびその製造方法
JP3755301B2 (ja) 1997-10-24 2006-03-15 Ｊｆｅスチール株式会社 耐衝撃特性、強度−伸びバランス、耐疲労特性および穴拡げ性に優れた高強度高加工性熱延鋼板およびその製造方法
JP3769143B2 (ja) 1999-05-06 2006-04-19 新日本製鐵株式会社 疲労特性に優れた加工用熱延鋼板およびその製造方法
CA2353492C (en) * 1999-10-22 2004-10-26 Jfe Steel Corporation Hot-dip galvanized high-strength steel sheet having superior workability and galvanizability and method for producing the same
JP4414563B2 (ja) 2000-06-12 2010-02-10 新日本製鐵株式会社 成形性並びに穴拡げ性に優れた高強度鋼板およびその製造方法
FR2830260B1 (fr) * 2001-10-03 2007-02-23 Kobe Steel Ltd Tole d'acier a double phase a excellente formabilite de bords par etirage et procede de fabrication de celle-ci
US8084143B2 (en) * 2003-09-30 2011-12-27 Nippon Steel Corporation High-yield-ratio and high-strength thin steel sheet superior in weldability and ductility, high-yield-ratio high-strength hot-dip galvanized thin steel sheet, high-yield ratio high-strength hot-dip galvannealed thin steel sheet, and methods of production of same
JP4317418B2 (ja) 2003-10-17 2009-08-19 新日本製鐵株式会社 穴拡げ性と延性に優れた高強度薄鋼板
JP4293020B2 (ja) 2004-03-15 2009-07-08 Ｊｆｅスチール株式会社 穴広げ性に優れる高強度鋼板の製造方法
JP4445365B2 (ja) * 2004-10-06 2010-04-07 新日本製鐵株式会社 伸びと穴拡げ性に優れた高強度薄鋼板の製造方法
JP2007016296A (ja) 2005-07-11 2007-01-25 Nippon Steel Corp 成形後の延性に優れたプレス成形用鋼板及びその成形方法、並びにプレス整形用鋼板を用いた自動車用部材
KR20080017244A (ko) * 2006-08-21 2008-02-26 가부시키가이샤 고베 세이코쇼 고장력 후강판 및 그 제조 방법
WO2008110670A1 (fr) * 2007-03-14 2008-09-18 Arcelormittal France Acier pour formage a chaud ou trempe sous outil a ductilite amelioree
JP5223360B2 (ja) * 2007-03-22 2013-06-26 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
BRPI0805832B1 (pt) * 2007-10-29 2014-11-25 Nippon Steel & Sumitomo Metal Corp Aço não-tratado termicamente para uso em forjamento a quente do tipo martensita e peça de aço não-tratada termicamente forjada a quente
JP5119903B2 (ja) 2007-12-20 2013-01-16 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板の製造方法
JP5365217B2 (ja) * 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
US8128762B2 (en) * 2008-08-12 2012-03-06 Kobe Steel, Ltd. High-strength steel sheet superior in formability
JP5347392B2 (ja) 2008-09-12 2013-11-20 Ｊｆｅスチール株式会社 延性に優れたホットプレス部材、そのホットプレス部材用鋼板、およびそのホットプレス部材の製造方法
JP4962594B2 (ja) * 2010-04-22 2012-06-27 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
WO2012081666A1 (ja) * 2010-12-17 2012-06-21 新日本製鐵株式会社 溶融亜鉛メッキ鋼板およびその製造方法
ES2569190T3 (es) * 2011-06-10 2016-05-09 Kabushiki Kaisha Kobe Seiko Sho Articulo moldeado por estampación en caliente, método para producir el mismo, y lámina de acero fina para el moldeado por estampación en caliente
KR101304621B1 (ko) * 2011-06-28 2013-09-05 주식회사 포스코 영역별로 상이한 강도를 갖는 프레스 성형품의 제조방법
CN104040007B (zh) * 2012-01-13 2016-08-24 新日铁住金株式会社 冷轧钢板及其制造方法

Also Published As

Publication number Publication date
MX2020010051A (es) 2020-10-15
JP6225988B2 (ja) 2017-11-08
RU2627313C2 (ru) 2017-08-07
EP3456855B1 (en) 2020-12-09
BR112015024777A2 (pt) 2017-07-18
KR101687931B1 (ko) 2016-12-19
US20160060722A1 (en) 2016-03-03
ES2712379T3 (es) 2019-05-13
KR20150121163A (ko) 2015-10-28
US20200109458A1 (en) 2020-04-09
PL2982772T3 (pl) 2019-03-29
RU2015141478A (ru) 2017-05-11
US10544475B2 (en) 2020-01-28
EP2982772A1 (en) 2016-02-10
TW201443249A (zh) 2014-11-16
CN105074038B (zh) 2016-12-14
CN105074038A (zh) 2015-11-18
JPWO2014162984A1 (ja) 2017-02-16
CA2908356C (en) 2017-11-28
BR112015024777B1 (pt) 2020-05-12
CA2908356A1 (en) 2014-10-09
TWI515310B (zh) 2016-01-01
US11371110B2 (en) 2022-06-28
EP2982772A4 (en) 2017-01-04
EP2982772B1 (en) 2018-10-10
EP3456855A1 (en) 2019-03-20
WO2014162984A1 (ja) 2014-10-09
MX2015013878A (es) 2015-12-11

Similar Documents

Publication Publication Date Title
MX378469B (es) Artìculo moldeado por estampado en caliente, làmina de acero enrollada en frio, y mètodo para manufacturar el artìculo moldeado por estampado en caliente.
MX373607B (es) Artículo moldeado estampado en caliente y método para la producción del mismo.
MX357148B (es) Lamina de acero laminada en frio y metodo para la produccion de la misma.
MX368564B (es) Lamina de acero laminada en frio, metodo para producir la misma y articulo moldeado mediante estampado en caliente.
MX376693B (es) Lamina de acero laminada en frio y metodo para producir lamina de acero laminada en frio.
MX356054B (es) Lámina de acero laminada en frío, de alta resistencia y método para la fabricación de la misma.
MX2016006777A (es) Componente de lamina de acero formada en caliente y metodo para producir el mismo asi como la lamina de acero para formacion en caliente.
MX373588B (es) LÁMINA DE ACERO GALVANIZADA POR INMERSIÓN EN CALIENTE, DE ALTA RESISTENCIA, Y LÁMINA DE ACERO GALVANIZADA POR INMERSIÓN EN CALIENTE, ALEADA, DE ALTA RESISTENCIA, QUE TIENE EXCELENTE ADHESIÓN DE ENCHAPADO, FORMABILIDAD, Y CAPACIDAD DE EXPANSIÓN DE AGUJERO CON RESISTENCIA A LA TRACCIÓN DE 980 MPa O MÁS Y MÉTODO DE FABRICACIÓN DE LAS MISMAS.
MX366776B (es) Lamina de acero, laminada en caliente, recocida y galvanizada por inmersion en caliente, y proceso para producir la misma.
MX2016007664A (es) Acero de elevada resistencia y procedimiento de fabricacion.
MX2016007954A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MY183438A (en) High-strength cold-rolled steel sheet and method for manufacturing the same
IN2014DN11262A (es)
MX385554B (es) Lamina de acero laminada en frio, de alta resistencia, que tiene excelente trabajabilidad y resistencia al impacto, y metodo para manufacturar la misma.
MX381461B (es) Lamina de acero laminada en frio de alta resistencia y alto limite de fluencia y metodo de produccion para la misma.
GB201315448D0 (en) High-strength steel sheet exerting excellent deep drawability at room temperature and warm temperatures and method for warm working same
MX2020003923A (es) Lamina de acero laminada en caliente de alta resistencia y metodo para la fabricacion de la misma.
MX385499B (es) Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida.
UA113404C2 (xx) Гарячекатаний сталевий лист та спосіб його виготовлення
MX378613B (es) Lamina de acero laminada en frio de alta resistencia con bajo limite de elasticidad y metodo para la fabricacion de la misma.
MX356410B (es) Chapa de acero laminada en frio.
MX2019004000A (es) Lamina de acero recubierta de metal, metodo de fabricacion de lamina de acero galvanizada por inmersion en caliente, y metodo de fabricacion de lamina de acero galvanizada-recocida aleada.
IN2014KN01170A (es)
MX2014002021A (es) Lamina de acero laminada en caliente para lamina de acero laminada en frio, lamina de acero laminada en caliente para lamina de acero galvanizada, y metodo para la fabricacion de las mismas.
MY170336A (en) High carbon steel wire rod having excellent wire drawability