KR970703392A - 열탄성 블렌드 조성물(thermoelastic blend compositions) - Google Patents
열탄성 블렌드 조성물(thermoelastic blend compositions) Download PDFInfo
- Publication number
- KR970703392A KR970703392A KR1019960706825A KR19960706825A KR970703392A KR 970703392 A KR970703392 A KR 970703392A KR 1019960706825 A KR1019960706825 A KR 1019960706825A KR 19960706825 A KR19960706825 A KR 19960706825A KR 970703392 A KR970703392 A KR 970703392A
- Authority
- KR
- South Korea
- Prior art keywords
- composition
- styrene
- storage modulus
- ethylene
- weight
- Prior art date
Abstract
본 발명은 하나 이상의 스티렌성 블록 공중합체를 포함하는 두가지 이상의 성분으로 된 열가소성 탄성중합체성 블렌드 조성물이다. 여기서, 상기 조성물은 필수적으로 조성물의 개질되지 않고 회석되지 않은(순수한) 블록 공중합체 부분과 동일하게 필적할만한 탄성, 고온 가공성 및 경성을 갖는다, 조성물은 또한 향상된 열적 안정성 및 가공성을 나타내고, 아스팔트, 접착제 및 밀봉제와 배합하기에 적합할뿐 아니라 탄성 성형제품, 필름 및 섬유를 제조하기에 매우 적합하다. 신규한 열가소성 탄성중합체성 블렌드 조성물은 (a) 하나 이상의 스티렌성 블록 공중합체를 99 내지 50중량%; 및 (b) 0.855 내지 0.895g/cc의 밀도를 갖는 하나 이상의 균일하게 분지된 에털렌 공중합체(이때, 사용된 양의 에틸렌 공중합체는 스티렌성 블록 공중합체의 실질적으로 불활성인 중량제이다)를 1 내지 50중량%로 포함하고, 상기 조성물은 (i) -26℃ 내지 24℃에서 3.5×109dyne/㎠ 미만의 저장 모듈러스를 갖고, (b) -26℃에서의 저장 모듈러스 대 24℃에서의 저장 모듈러스의 비가 3미만이고, (c) 조성물의 순수한 블록 공중합체 부분의 -26℃ 및 24℃에서의 저장 모듈러스보다 각각 0.2 내지 3배가 더 큰 -26℃ 및 24℃에서의 저장 모듈러스를 가짐을 특징으로 한다.
Description
열탄성 블렌드 조성물(THERMOELASTIC BLEND COMPOSITIONS)
[도면의 간단한 설명]
제1도는 유동학적 고체 분석기(RSA-II)를 사용하여 결정한, 본 발명의 실시예 6 및 8 및 비교예 7, 9 및 10의 동적 저장 모듈러스 대 온도의 도면이다.
제2도는 성분 물질의 평균 중량 분포도를 기준으로 예상한, 본 발명의 실시예 6 및 8 및 비교예 7,9 및 10의 동적 저장 모듈러스 대 온도의 도면이다.
제3도는 190℃에서 유동학적 유동계 RMS-800를 사용하여 결정한, 본 발명의 실시예 6 및 8 및 비교예 7,9 및 10의 동적 복합 점성 대 전단 속도의 도면이다.
제4도는 유동학적 고체 분석기(RSA-II)를 사용하여 결정한, 실시예 6 내지 10의 동적 저장 모듈러스 대 온도의 도면이다.
제5도는 성분 물질의 중량 평균 분포도를 기준으로 예상한, 실시예 6 내지 10의 동적 저장 모듈러스 대 온도의 도면이다.
제6도는 190℃에서 유동학적 유동계 RMS-800를 사용하여 결정한, 실시예 6 내지 10의 동적 복합 점성 대 전단 속도의 도면이다.
제7도는 유동학적 고체 분석기 RSA-II를 사용하여 결정한, 본 발명의 실시예 16 및 18 및 비교예 17,19 및 20의 동적 저장 모듈러스 대 온도의 도면이다.
제8도는 190℃에서 유동학적 유동계 RMS-800를 사용하여 결정한, 실시예 11 내지 15의 동적 복합 점성 대 전단 속도의 도면이다.
제9도는 유동학적 고체 분석기 RSA-II를 사용하여 결정한, 본 발명의 실시예 11, 12 및 23, 및 비교예 12, 24 및 25의 동적 저장 모듈러스 대 온도의 도면이다.
제10도는 240℃에서 하케(Haake) 토크(torque) 혼합기를 사용하여 결정한, 비교예 17의 하케 토크 반응 대 시간의 도면이다.
제11도는 240℃에서 하케 토크 혼합기를 사용하여 결정한, 본 발명의 실시예 16의 하케 토크 반응 대 시간의 도면이다.
제12도는 240℃에서 하케 토크 혼합기를 사용하여 결정한, 실시예 22의 하케 토크 반응 대 시간의 도면이다.
제13도는 유동학적 고체 분석기 RSA-II 를 사용하여 결정한, 실시예 7, 23 내지 26의 동적 저장 모듈러스 대 온도의 도면이다.
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (22)
- (a) 하나 이상의 스티렌성 블록 공중합체(copolymer)를 총 조성물의 50 내지 99중량%; 및 (b) 하나 이상의 C3-C20α-올레핀을 갖고, (i) 0.855g/cc 내지 0.905g/cc의 밀도, (ii) 50%보다 큰 단쇄 분지 분포 지수(SCBDI), (iii) 시차주사열계량법(DSC)을 이용하여 결정될때 단일 융점, (iv) 5.63 이상의 용융유동비(I10/I2), (v) Mw/Mn≤(I10/I2)-4.63의 식에 따라 결정된 분자량 분포(Mw/Mn) 및 (vi) 거의 동일한 I2및 Mw/Mn을 갖는 선형 에틸렌/C3-C20α-올레핀 공중합체(interpolymer)의 표면 용융파괴가 개시될때의 임계전단속도보다 50%이상 더 큰 표면 용융 파괴가 개시될때의 임계전단속도를 가짐을 특징으로 하는 하나 이상의 실질적으로 선형인 에틸렌/α-올레핀 공중합체를 총 조성물의 1 내지 50중량%로 포함함을 특징으로 하는 열가소성 탄성중합체성 블렌드 조성물.
- 제1항에 있어서, 상기 실질적으로 선형인 에틸렌/α-올레핀 공중합체가 스티렌성 블록 공중합체의 실질적으로 불활성인 중량제이고; (i) -26℃ 내지 24℃에서 3.5×109dyne/㎠ 미만의 저장 모듈러스를 갖고, (b) -26℃에서의 저장 모듈러스 대 24℃에서의 저장 모듈러스의 비가 4 미만이고, (c) 조성물의 순수한 블록 공중합체 부분의 -26℃ 및 24℃에서의 저장 모듈러스보다 각각 0.2 내지 3배가 더 큰 -26℃ 및 24℃에서의 저장 모듈러스를 가짐을 특징으로 하는 조성물.
- 제1항에 있어서, 상기 실질적으로 선형인 에틸렌 공중합체가 중합체 골격을 따라 탄소 1000개당 0.01개 내지 3개의 장쇄 분지를 가짐을 또한 특징으로 하는 조성물.
- 제1항에 있어서, 상기 하나 이상의 C3-C20α-올레핀이 1-프로필렌, 1-부텐, 4-메틸-1-펜텐, 1-헥센 및 1-옥텐으로 이루어진 군으로부터 선택된 조성물.
- 제4항에 있어서, 상기 에틸렌 공중합체가 에틸렌과 1-옥텐의 공중합체인 조성물.
- 제1항에 있어서, 상기 실질적으로 선형인 에틸렌/α-올레핀 공중합체가 0.86g/cc 내지 0.89g/cc의 밀도를 갖는 조성물.
- 제1항에 있어서, 상기 스티렌성 분절이 스티렌인 조성물.
- 제1항에 있어서, 상기 스티렌성 블록 공중합체가 스티렌/부타디엔/스티렌, 스티렌/이소프렌/스티렌, 스티렌/에틸렌-부텐/스티렌 및 스티렌/에틸렌-프로필렌/스티렌으로 이루어진 군으로부터 선택된 조성물.
- 제1항에 있어서, 상기 스티렌성 블록 공중합체가 하나 이상의 고무 단량체 분절을 갖는 조성물.
- 제9항에 있어서, 상기 고무 단량체 분절이 불포화된 조성물.
- 제10항에 있어서, 상기 고무 분절이 부타디엔 및 이소프렌으로 이루어진 군으로부터 선택된 조성물.
- 제9항에 있어서, 상기 고무 단량체 분절이 포화된 조성물.
- 제12항에 있어서, 상기 고무 분절이 에틸렌-부텐 및 에틸렌-프로필렌으로 이루어진 군으로부터 선택된 조성물.
- 제1항에 있어서, 상기 스티렌성 블록 공중합체가 선형 이원블록(diblock) 중합체, 선형 삼원블록(triblock) 중합체, 방사상 이원블록 중합체 및 방사상 삼원블록 중합체로 이루어진 군으로부터 선택된 조성물.
- 제1항에 있어서, 총 조성물의 60 내지 95중량%의 스티렌성 블록 공중합체 및 총 조성물의 5 내지 40중량%의 에틸렌 공중합체를 포함하는 조성물.
- (a) 10 내지 35중량%의 스티렌을 함유하는 스티렌/부타디엔/스티렌 블록 공중합체(copolymer)를 총 조성물의 70 내지 90중량%; 및 (b) (i) 0.855 내지 0.885g/cc의 밀도, (ii) 50%보다 큰 단쇄 분지 분포 지수 (SCBDI), (iii) 시차주사열계량법(DSC)을 이용하여 결정될때 단일 융점, (iv) 5.63 이상의 용융유동비(I10/I2), (v) Mw/Mn≤(I10/I2)-4.63의 식에 따라 결정된 분자량 분포(Mw/Mn) 및 (vi) 거의 동일한 I2및 Mw/Mn을 갖는 선형 에틸렌/C3-C20α-올레핀 공중합체(interpolymer)의 표면 용융파괴가 개시될때의 임계전단속도보다 50%이상 더 큰 표면 용융 파괴가 개시될때의 임계전단속도를 가짐을 특징으로 하는 하나 이상의 실질적으로 선형인 에틸렌/1-올레핀 공중합체를 총 조성물의 10 내지 30중량%로 포함하고, (i) -26℃ 내지 24℃에서 3.5×109dyne/㎠ 미만의 저장 모듈러스를 갖고, (b) -26℃에서의 저장 모듈러스 대 24℃에서의 저장 모듈러스의 비가 3 미만이고, (c) 조성물의 순수한 블록 공중합체 부분의 -26℃ 및 24℃에서의 저장 모듈러스보다 각각 0.4 내지 2.2배가 더 큰 -26℃ 및 24℃에서의 저장 모듈러스를 가짐을 특징으로 하는 열가소성 탄성중합체성 블렌드 조성물.
- 제15항에 있어서, 총 조성물의 25중량%가 스티렌/부타디엔/스티렌 블록 공중합체인 조성물.
- 제15항에 있어서, 총 조성물의 25중량%가 스티렌/이소프렌/스티렌 블록 공중합체인 조성물.
- 제15항에 있어서, 총 조성물의 25중량%가 스티렌/에틸렌-부텐/스티렌 블록 공중합체인 조성물.
- 제15항에 있어서, 총 조성물의 25중량%가 스티렌/에틸렌-프로필렌/스티렌 블록 공중합체인 조성물.
- (a) 하나 이상의 스티렌성 블록 공중합체(copolymer)를 총 조성물의 50 내지 99중량%; 및 (b) 하나 이상의 C3-C20α-올레핀을 포함하고, (i) 0.855 내지 0.905g/cc의 밀도, (ii) 50%보다 큰 단쇄 분지 분포지수(SCBDI) 및 (iii) 시차주사열계량법(DSC)을 이용하여 결정될때 단일 융점을 가짐을 특징으로 하는 하나 이상의 균일하게 분지된 선형 에틸렌/α-올레핀 공중합체(interpolymer)를 총 조성물의 1 내지 50중량%로 포함함을 특징으로 하는 열가소성 탄성중합체성 블렌드 조성물.
- (A) (a) 하나 이상의 스티렌성 블록 공중합체를 총 조성물의 99 내지 50중량%; 및 (b) 하나 이상의 C3-C20α-올레핀을 포함하고 (i) 0.855 내지 0.905g/cc의 밀도, (ii) 약 50%보다 큰 단쇄 분지 분포 지수(SCBDI), (iii) 시차주사열계량법(DSC)을 이용하여 결정될때 단일 융점, (iv) 5.63 이상의 용융유동비(I10/I2), (v) Mw/Mn≤(I10/I2)-4.63의 식에 따라 결정된 분자량 분포(Mw/Mn) 및 (vi) 거의 동일한 I2및 Mw/Mn을 갖는 선형 에틸렌/C3-C20α-올레핀 공중합체의 표면 용융파괴가 개시될때의 임계전단속도보다 50%이상 더 큰 표면 용융 파괴가 개시될때의 임계전단속도를 가짐을 특징으로 하는, 하나 이상의 실질적으로 선형인 에틸렌/α-올레핀 공중합체를 총 조성물의 1 내지 50중량%로 포함하는 조성물을 제공하는 단계; (B) 조성물을 제품으로 제조시키기에 충분한 온도로 가열시키는 단계; (C) 가열된 조성물을 필름, 섬유 또는 성형된 제품으로 제조시키는 단계; 및 (D) 필름, 섬유 또는 성형된 제품을 수거하거나 필름, 섬유 또는 성형된 제품을 추가로 가공시키기 위해 이동시키는 단계를 포함하는 특징으로 하는, 필름, 섬유 또는 성형품 형태의 제품을 제조하는 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.