CN104846692A - 用于压纹离型纸的制造方法 - Google Patents
用于压纹离型纸的制造方法 Download PDFInfo
- Publication number
- CN104846692A CN104846692A CN201510205379.4A CN201510205379A CN104846692A CN 104846692 A CN104846692 A CN 104846692A CN 201510205379 A CN201510205379 A CN 201510205379A CN 104846692 A CN104846692 A CN 104846692A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixture
- embossing
- film
- release paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种用于压纹离型纸的制造方法，包括以下步骤：将高密度聚乙烯100份、低密度聚乙烯120~180份、苯乙烯-异戊二烯-苯乙烯嵌段共聚物10份~30份、苯乙烯与丁二烯的嵌段共聚物5份~15份、石蜡0.5~1.5份、甘油0.1~0.5份、POE聚烯烃弹性体5~10份，偶联剂0.3-0.8份放入搅拌器内搅；将混合物通过淋膜机进料口的双螺杆进行加热架桥获得熔化后混合物；将熔化后混合物在进料螺杆处再次对熔化后混合物进一步加热至220~250℃，从而获得流体状混合物，同时进行加压至5~15Mpa；将流体状混合物在螺杆出口处再次加热至260~280℃加热并变成布状被挤出。本发明获得的压纹淋膜离型膜网状纹路压纹清晰、深浅统一，分布线均匀，形成的压纹淋膜离型纸在与压敏胶贴合时两者之间不会产生气泡。
Description
技术领域
本发明涉及一种用于压纹离型纸的制造方法，属于离型材料技术领域。
背景技术
通常离型膜是指在聚酯薄膜表面涂布有机硅油，起到防粘的作用；离型膜表面可以有光面和哑面，但这种传统的离型膜制作的压敏胶胶带及标签胶带时，胶面美化效果不理想，普通的离型膜与压敏胶胶带贴合时，两者之间容易产生气泡。采用压纹离型纸，虽然可以达到排气泡的效果，但是由于离型纸容易吸水、抗撕裂强度不高，不易观察胶面、模切后，边缘有纸屑等缺点，不能被高端产品所使用。
发明内容
本发明目的是提供一种用于压纹离型纸的制造方法，该制作方法获得压纹淋膜离型纸网状纹路压纹清晰、深浅统一，分布线均匀，形成的压纹淋膜离型纸在与压敏胶贴合时两者之间不会产生气泡，从而不会影响到使用效果。
为达到上述目的，本发明采用的技术方案是：一种用于压纹离型纸的制造方法，包括以下步骤：
步骤一：淋膜涂覆层的制备工艺如下：
步骤1、将高密度聚乙烯100份、低密度聚乙烯120~180份、苯乙烯-异戊二烯-苯乙烯嵌段共聚物10份~30份、苯乙烯与丁二烯的嵌段共聚物5份~15份、石蜡0.5~1.5份、甘油0.1~0.5份、POE聚烯烃弹性体 5~10份，偶联剂 0.3~0.8份放入搅拌器内进行混合搅拌20~30min形成混合物；
步骤2、将步骤一获得的混合物通过淋膜机进料口的双螺杆进行加热架桥获得熔化后混合物，此加热架桥的温度为150~200℃；
步骤3、将步骤二获得的熔化后混合物在进料螺杆处再次对熔化后混合物进一步加热至220~250℃，从而获得流体状混合物，同时进行加压至5~15Mpa；
步骤4、将步骤三获得流体状混合物在螺杆出口处再次加热至260~280℃加热并变成布状被挤出；
步骤二：将基纸装到淋膜机的放卷轴上，通过导辊将基纸引入，引入的过程中，淋膜机对基纸表面进行电晕抛毛处理，当基纸进入淋膜机上带压纹的复合轮时，挤出的淋膜涂覆层通过复合轮淋膜至基纸表面，并且通过有压纹的复合轮对其进行加压复合压纹、压纹轮的压纹面与淋膜涂覆层接触，复合后冷却至30~40℃，再进过低温冷却轮冷却至10~15℃，从而在淋膜涂覆层与基纸相背的表面形成压纹图案区，然后对基纸进行分切；
步骤三：在淋膜涂覆层的具有压纹图案区的表面涂布有机硅离型剂层，制备成所述压纹淋膜离型膜。
上述技术方案中进一步改进的方案如下：
1、上述方案中，所述POE聚烯烃弹性体为乙烯和辛烯的高聚物。
2、上述方案中，所述苯乙烯-异戊二烯-苯乙烯嵌段共聚物与苯乙烯与丁二烯的嵌段共聚物的比例为2：0.9~1。
3、上述方案中，所述偶联剂为硅烷偶联剂。
4、上述方案中，所述双螺杆挤出机9节加温区域温度分别为150℃、180℃、190、,220℃、230℃、250℃、2500℃、260℃和280℃，真空度为0.05~0.07。
由于上述技术方案运用，本发明与现有技术相比具有下列优点和效果：
本发明制作方法获得的压纹淋膜离型膜，其形成的网状纹路压纹清晰、深浅统一，分布线均匀，形成的压纹淋膜离型纸在与压敏胶贴合时两者之间不会产生气泡，从而不会影响到使用效果；其次，其加入苯乙烯-异戊二烯-苯乙烯嵌段共聚物10份~30份、苯乙烯与丁二烯的嵌段共聚物5份~15份和POE聚烯烃弹性体 5~10份，偶联剂0.3~0.8份使得离型剂层与基纸间的粘结力更加紧密，并大大改善了残余接着率，离型层不易脱落，并目还改善了膜的防静电性能。
附图说明
附图1为本发明压纹离型膜结构示意图。
以上附图中：1、基纸；2、淋膜涂覆层；3、压纹图案区；4、有机硅离型剂层。
具体实施方式
下面结合实施例对本发明作进一步描述：
实施例1~5：一种用于压纹离型纸的制造方法，包括以下步骤：
步骤一：淋膜涂覆层的制备工艺如下：
步骤1、将高密度聚乙烯100份、低密度聚乙烯120~180份、苯乙烯-异戊二烯-苯乙烯嵌段共聚物10份~30份、苯乙烯与丁二烯的嵌段共聚物5份~15份、石蜡0.5~1.5份、甘油0.1~0.5份、POE聚烯烃弹性体 5~10份，偶联剂0.3-0.8份放入搅拌器内进行混合搅拌20~30min形成混合物；
步骤2、将步骤一获得的混合物通过淋膜机进料口的双螺杆进行加热架桥获得熔化后混合物，此加热架桥的温度为150~200℃；
步骤3、将步骤二获得的熔化后混合物在进料螺杆处再次对熔化后混合物进一步加热至220~250℃，从而获得流体状混合物，同时进行加压至5~15Mpa；
步骤4、将步骤三获得流体状混合物在螺杆出口处再次加热至260~280℃加热并变成布状被挤出；
步骤二：将基纸1装到淋膜机的放卷轴上，通过导辊将基纸1引入，引入的过程中，淋膜机对基纸1表面进行电晕抛毛处理，当基纸1进入淋膜机上带压纹的复合轮时，挤出的淋膜涂覆层2通过复合轮淋膜至基纸1表面，并且通过有压纹的复合轮对其进行加压复合压纹、压纹轮的压纹面与淋膜涂覆层2接触，复合后冷却至30~40℃，再进过低温冷却轮冷却至10~15℃，从而在淋膜涂覆层2与基纸1相背的表面形成压纹图案区3，然后对基纸1进行分切；
步骤三：在淋膜涂覆层2的具有压纹图案区3的表面涂布有机硅离型剂层4，制备成所述压纹淋膜离型膜。
上述双螺杆挤出机9节加温区域温度分别为150℃、180℃、190℃、,220℃、230℃、250℃、250℃、260℃和280℃，真空度为0.05~0.07。
实施例1~5中所述淋膜涂覆层由下列重量份的组分组成：
表1
上述POE聚烯烃弹性体，实施例1为乙烯和辛烯的高聚物，实施例2为乙烯和辛烯的高聚物，实施例2为乙烯和丁烯的高聚物，实施例2为乙烯和丁烯的高聚物，实施例2为乙烯和辛烯的高聚物。
上述苯乙烯-异戊二烯-苯乙烯嵌段共聚物与苯乙烯与丁二烯的嵌段共聚物的比例为：实施例1为2：1、实施例2为2：1.05、实施例3为2：0.9、实施例4为2：1、实施例4为2：0.95。
对比例1：一种用于压纹离型纸的制造方法，包括以下步骤：
步骤一、在淋膜涂覆层2与基纸1相背的表面形成压纹图案区3，然后对纸张进行分切；
步骤二、在淋膜涂覆层2的具有压纹图案区3的表面涂布有机硅离型剂层4，制备成所述压纹淋膜离型纸，所述淋膜涂覆层由下列重量份的组分组成，高密度聚乙烯100份、低密度聚乙烯125份。
对比例2：一种用于压纹离型纸的制造方法，包括以下步骤：
步骤一、在淋膜涂覆层2与基纸1相背的表面形成压纹图案区3，然后对纸张进行分切；
步骤二、在淋膜涂覆层2的具有压纹图案区3的表面涂布有机硅离型剂层4，制备成所述压纹淋膜离型纸，所述淋膜涂覆层由下列重量份的组分组成，高密度聚乙烯100份、低密度聚乙烯150份。
将实施例1~5和对比例方法获得的压纹淋膜离型纸进行测试，如表2所示：
表2
采用上述制作方法获得的压纹淋膜离型纸，其形成的网状纹路压纹清晰、深浅统一，分布线均匀，形成的压纹淋膜离型纸在与压敏胶贴合时两者之间不会产生气泡，从而不会影响到使用效果；其次，其加入苯乙烯-异戊二烯-苯乙烯嵌段共聚物10份~30份、苯乙烯与丁二烯的嵌段共聚物5份~15份和POE聚烯烃弹性体 5~10份，偶联剂0.3~0.8份使得离型剂层与基纸间的粘结力更加紧密，并大大改善了残余接着率，离型层不易脱落，并目还改善了膜的防静电性能。
上述实施例只为说明本发明的技术构思及特点，其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施，并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰，都应涵盖在本发明的保护范围之内。
Claims (4)
1. 一种用于压纹离型纸的制造方法，其特征在于：包括以下步骤：
步骤一：淋膜涂覆层的制备工艺如下：
步骤1、将高密度聚乙烯100份、低密度聚乙烯120~180份、苯乙烯-异戊二烯-苯乙烯嵌段共聚物10份~30份、苯乙烯与丁二烯的嵌段共聚物5份~15份、石蜡0.5~1.5份、甘油0.1~0.5份、POE聚烯烃弹性体 5~10份，偶联剂 0.3~0.8份放入搅拌器内进行混合搅拌20~30min形成混合物；
步骤2、将步骤一获得的混合物通过淋膜机进料口的双螺杆进行加热架桥获得熔化后混合物，此加热架桥的温度为150~200℃；
步骤3、将步骤二获得的熔化后混合物在进料螺杆处再次对熔化后混合物进一步加热至220~250℃，从而获得流体状混合物，同时进行加压至5~15Mpa；
步骤4、将步骤三获得流体状混合物在螺杆出口处再次加热至260~280℃加热并变成布状被挤出；
步骤二：将基纸（1）装到淋膜机的放卷轴上，通过导辊将基纸（1）引入，引入的过程中，淋膜机对基纸（1）表面进行电晕抛毛处理，当基纸（1）进入淋膜机上带压纹的复合轮时，挤出的淋膜涂覆层（2）通过复合轮淋膜至基纸（1）表面，并且通过有压纹的复合轮对其进行加压复合压纹、压纹轮的压纹面与淋膜涂覆层（2）接触，复合后冷却至30~40℃，再进过低温冷却轮冷却至10~15℃，从而在淋膜涂覆层（2）与基纸（1）相背的表面形成压纹图案区（3），然后对基纸（1）进行分切；
步骤三：在淋膜涂覆层（2）的具有压纹图案区（3）的表面涂布有机硅离型剂层（4），制备成所述压纹淋膜离型纸。
2. 根据权利要求1所述的用于压纹离型纸的制造方法，其特征在于：所述POE聚烯烃弹性体为乙烯和辛烯的高聚物。
3. 根据权利要求1所述的用于压纹离型纸的制造方法，其特征在于：所述苯乙烯-异戊二烯-苯乙烯嵌段共聚物与苯乙烯与丁二烯的嵌段共聚物的比例为2：0.9~1。
4. 根据权利要求1所述的用于压纹离型纸的制造方法，其特征在于：所述双螺杆挤出机9节加温区域温度分别为150℃、180℃、190℃、,220℃、230℃、250℃、250℃、260℃和280℃，真空度为0.05~0.07。