KR960010748A - 폴리올레핀 조성물의 제조방법 및 폴리올레핀 필름용 조성물의 제조방법 - Google Patents
폴리올레핀 조성물의 제조방법 및 폴리올레핀 필름용 조성물의 제조방법 Download PDFInfo
- Publication number
- KR960010748A KR960010748A KR1019950031145A KR19950031145A KR960010748A KR 960010748 A KR960010748 A KR 960010748A KR 1019950031145 A KR1019950031145 A KR 1019950031145A KR 19950031145 A KR19950031145 A KR 19950031145A KR 960010748 A KR960010748 A KR 960010748A
- Authority
- KR
- South Korea
- Prior art keywords
- polyolefin
- weight
- average particle
- particle diameter
- composition
- Prior art date
Abstract
본 발명은 평균 입자 직경이 50 내지 500㎛이고 직경이 100㎛이하인 미세 입자를 10중량% 이상 함유하는 폴리올레핀 입자를, 평균 입자 직경이 1.0 내지 4.0㎛이고 겉보기 밀도가 0.25 내지 0.50g/㎤인 무기 미세 분말 3.0 내지 25.0중량%와 혼합하고, 생성된 혼합물을 혼련기로 용융혼련시키면 무기 미세 분말의 함량이 높은 마스터뱃치를 수득할 수 있으며, 이는 무기 미세 분말(Ⅱ)이 잘 분산되고 외관 및 내스크랫치성을 포함하는 우수한 필름 특성을 가지면서도 폴리올레핀 필름 고유의 바람직한 특성을 유지시키는 폴리올레핀 필름의 제조에 유용하다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (14)
- (a)평균 입자 직경이 50 내지 500㎛이고 직경이 100㎛ 이하인 미세 입자를 10중량% 이상 함유하는 폴리올레핀 입자(Ⅰ) 97 내지 75중량%와, 평균 입자 직경이 1.0 내지 4.0㎛이고 겉보기 밀도가 0.25 내지 0.50g/㎤인 무기 미세 분말(Ⅱ) 3 내지 25중량%를 혼합하여 혼합물을 형성하는 단계 및 (b) 이 혼합물을 용융 혼련시키는 단계를 포함하는, 폴리올레핀 조성물의 제조방법.
- 제1항에 있어서, 폴리올레핀 입자(Ⅰ)가 70 내지 300㎛의 평균 입자 직경을 갖고, 100㎛ 이하의 직경을 갖는 미세 입자를 15중량% 이상 함유하는 방법.
- 제1항 또는 제2항에 있어서, 폴리올레핀 입자(Ⅰ)가 폴리프로필렌 입자인 방법.
- 제1항 또는 제2항에 있어서, 무기 미세 분막(Ⅱ)의 평균 입자 직경이 1.5 내지 4.0㎛이고 겉보기 밀도가 0.25 내지 0.45g/㎤인 방법.
- 제3항 또는 제4항에 있어서, 단계(a)가 폴리올레핀 입자(Ⅰ) 96 내지 80중량%를 무기 미세 분말(Ⅱ) 4 내지 20중량%의 혼합하는 단계를 포함하는 방법.
- 제4항에 있어서, 무기 미세 분말(Ⅱ)이 이산화규소인 방법.
- (a)평균 입자 직경이 50 내지 500㎛이고 직경이 100㎛ 이하인 미세 입자를 10중량% 이상 함유하는 폴리올레핀 입자(Ⅰ) 97 내지 75중량%와, 평균 입자 직경이 1.0 내지 4.0㎛이고 겉보기 밀도가 0.25 내지 0.50g/㎤인 무기 미세 분말(Ⅱ) 3 내지 25중량%를 혼합하여 혼합물을 형성하는 단계, (b)이 혼합물을 용융혼련시켜 폴리올레핀 조성물을 수득하는 단계, (c)폴리올레핀 조성물 0.1 내지 10중량부를 폴리올레핀(Ⅲ) 100중량부와 혼합하여 예비 혼합물을 형성하는 단계 및 (d)이러한 예비 혼합물을 용융혼련하는 단계를 포함하는, 폴리올레핀 필름용 조성물의 제조방법.
- 제7항에 있어서, 폴리올레핀(Ⅲ)이 프로필렌 단독중합체인 방법.
- 제7항에 있어서, 폴리올레핀(Ⅲ)이 프로필렌과 탄소수 4 내지 10의 하나 이상의 α-올리핀과의 공중합체인 방법.
- 제7항에 있어서, 폴리올레핀(Ⅲ)이 프로필렌-에틸렌랜덤 공중합체인 방법.
- 제7항에 있어서, 폴리올레핀(Ⅲ)이 프로필렌, 에틸렌 및 탄소수 4 내지 10의 α-올레핀으로 이루어진 랜덤 삼원공중합체인 방법.
- 제7항에 있어서, 폴리올레핀 필름용 조성물 중에서의 무기 미세 분말(Ⅱ)의 함량이 0.05 내지 1중량%인 방법.
- 제8항 또는 제9항에 있어서, 폴리올레핀(Ⅲ)이 500 내지 1300㎛의 평균 입자 직경을 갖고 300㎛이하의 직경을 갖는 미세 입자를 10중량% 이하 함유하는 방법.
- (a)평균 입자 직경이 50 내지 500㎛이고 직경이 100㎛이하인 미세 입자를 10중량% 이상 함유하는 폴리올레핀 입자(Ⅰ) 97 내지 75중량%와, 평균 입자 직경이 1.0 내지 4.0㎛이고 겉보기 밀도가 0.25 내지 0.50g/㎤인 무기 미세 분말(Ⅱ) 3 내지 25중량%를 혼합하여 혼합물을 형성하는 단계, (b)이 혼합물을 용융혼련시켜 폴리올레핀 조성물을 수득하는 단계, (c)폴리올레핀 조성물 0.1 내지 10중량부를 폴리올레핀(Ⅲ) 100 중량부와 혼합하여 예비 혼합물을 형성하는 단계, (d)이러한 예비 혼합물을 용융혼련하여 폴리올레핀 필름용 조성물을 형성하는 단게 및 (e)폴리올레핀 필름을 제조하기 위하여 폴리올레핀 필름용 조성물을 사용하는 단계를 포함하는, 폴리올레핀 필름에 외관, 투명도, 내블록킹성 및 내스크랫치성을 균형이 잘 잡히게 부여하는 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.