KR920016481A - 필름성형용 고결정성 폴리프로필렌 - Google Patents
필름성형용 고결정성 폴리프로필렌 Download PDFInfo
- Publication number
- KR920016481A KR920016481A KR1019920001501A KR920001501A KR920016481A KR 920016481 A KR920016481 A KR 920016481A KR 1019920001501 A KR1019920001501 A KR 1019920001501A KR 920001501 A KR920001501 A KR 920001501A KR 920016481 A KR920016481 A KR 920016481A
- Authority
- KR
- South Korea
- Prior art keywords
- crystalline polypropylene
- film
- film forming
- highly crystalline
- polypropylene
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (18)
- 입체규칙성 촉매하에서 프로필렌을 종합하여 얻어진 프로필렌 단일 중합체의 분자량을 감소시켜서 얻고, (a)ASTM-D-1238을 통해 측정된 용융유동율 (MFR)이 1내지 10g/10분이고, (b)수평균분자량의 MN에 대한 무게 평균 분자량 MN의비율 (Mw/MN)인 Q비율이 2.5 내지 4.0의 범위이며, (c) 밀도가 적어도 0.9070g/㎠이고, (d)냉각된 코실렌 용해성물질(CXS)이 최고 2.5중량%의 범위에 있는 필름성형용 고결정성 폴리프로필렌.
- 제1항에 잇어서, 입체규칙성 촉매는 ( A)주성분이 마그네슘,티탄, 할로겐 원소와 전자 공여체로 이루어진 고체촉매성분과 (B)유기알루미늄 화합물 성분이 조합된 필름 성형용 고결정성 폴리프로필렌.
- 제2항에 있어서, 고체촉매성분(A)에서 티탄, 미그네슘 및 할로겐은 마그네슘의 디할로겐화물, 할로겐 원소및/또는 알콕시기를 갖는 4가 티탄 그리고 마그네슘과 티탄을 도입하기 위해 사용된 마그네슘 화합물 및/또는 티탄 화합물들을 통해 도입시켜서 되는 필름성형용 고결정성 폴리프로필렌.
- 제2항에 있어서, 고체촉매성분(A)에서 전자 공여체 화합물은 유기산 에스테르, 유기산 할로겐화물 또는 유기 유기실리콘 화합물을 통해 도입시켜서 되는 필름성형용 고결정성 폴리프로필렌.
- 제4항에 있어서, 유기산 에스테르 또는 유기산 할로겐화물의 유기산은 방향족 카르복실산인 필름성형용 고결성 폴리프로필렌.
- 제4항에 있어서, 유기 실리콘 화합물은 식 R1R2 3-nSi(OR3)n을 필름성형용 고결정성 폴리프로필렌, 윗 식중, R1은 탄소수가 약 3내지 12인 분지된 사슬 또는 탄소수가 3 내지 12인 지환족카르빌기를 갖는 하이드로카르빌기이고, R2는 R1과 같거나 다르며, 탄소수가 3내지 12인 하이드로카르빌기이며, R3는 산소수가 1내지 4인 하이드로카르빌기이고, n은 1≤n≤3인 수이다.
- 제6항에 있어서, 치환체 R1은 α위치에 분지사슬과 2급 또는 3급 α-탄소를 갖는 탄소수가 3내지 10인 지방족 또는 지환족 하이드로카르빌기인 필름성형용 고결정성 폴리프로필렌.
- 제6항에 있어서, 치환제 R1은 3급 α-탄소를 갖으며 탄소수가 4내지 10인 지방족 하이드로 카르빌기인 필름성형용 고결정성 폴리프로필렌.
- 제1항에 있어서, 분자량 감소는 레디칼발생제 존재하에 프로필렌 단일중합체를 가열하면서혼합시켜서 되는 필름성형용 고결정성 폴리프로필렌.
- 제9항에 있어서, 레디칼발생제는 유기 과산화물인 필름성형용 고결정성 폴리프로필렌.
- 제10항에 있어서, 유기 과산화물은 과산화물, 수산화과산화물 및 과산물로 이루어진 그룹에서 선택하여서 되는 필름성형용 고결정성 폴리프로필렌.
- 제10항에 있어서, 유기 과산화물은 1분의 반감시간을 갖도록 하기 위해 70내지 300℃의 온도를 가지는 필름성형용 고결정성 폴리프로필렌.
- 제9항에 있어서 분자량 감소는 170내지 300℃에서 프로필렌 단일중합체를 혼합시켜서 되는 필름성형용 고결정성 폴리프로필렌.
- 제9항에 있어서, 레디칼발생제의 양은 프로필렌 단일중합체에 대해 0.001내지 2중량%로 하여서 되는 필름성형용 고결정성 폴리프로필렌.
- 제1항에 있어서, MFR은 2내지 8g/10분인 필름성형용 고결정성 폴리프로필렌.
- 제1항에 있어서, Q치는 2.8내지 3.8인 필름성형용 고결정성 폴리프로필렌.
- 제1항에 있어서, 밀도는 0.9070내지 0.9150g/㎤ 인 필름성형 고결정성 폴리프로필렌.
- 제1항에 있어서, 밀도는 0.9075지 0.9150㎤ 인 필름성형 고결정성 폴리프로필렌.※ 참고사항 : 최초출원 내용에 의하여 공개되는 것임.