KR950018115A - 지방족 반응 사출 성형(rim) 탄성중합체 - Google Patents
지방족 반응 사출 성형(rim) 탄성중합체 Download PDFInfo
- Publication number
- KR950018115A KR950018115A KR1019940034959A KR19940034959A KR950018115A KR 950018115 A KR950018115 A KR 950018115A KR 1019940034959 A KR1019940034959 A KR 1019940034959A KR 19940034959 A KR19940034959 A KR 19940034959A KR 950018115 A KR950018115 A KR 950018115A
- Authority
- KR
- South Korea
- Prior art keywords
- component
- weight
- group
- amount
- present
- Prior art date
Abstract
본 발명은 RIM방법에 의하여 제조된 폴리우레탄 성형물에 관한 것이다. 본 발명에 따른 폴리우레탄 성형물은 반응성 및 탈형 특성(30초의 탈형 시간에서)이 우수하고 신장률 및 인렬 강도가 양호하며, 촉매의 존재하에 25℃에서의 점도가 약 20,000mPa·s이고 NCO 관능도가 2.3내지 4.0인 지방족 폴리이소시아네이트를, (b1) 히드록시기와 아민기로 이루어진 군으로부터 선택된 하나 이상의 기를 함유하는 비교적 고분자량의 유기 화합물 및 (b2) 다올, 트리올, 1차 아민, 2차 아민, 아미노알코올 및 그의 혼합물로 이루어진 군으로부터 선택된 저분자량의 연쇄 신장제를 함유하는 이소시아네이트 반응성 화합물과 반응시켜 얻어진 반응 생성물로 이루어진다. 연쇄 신장제의 OH:NH비율는 1:1 내지 25:1이다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (10)
- (A) 25℃에서의 점도가 약 20,000mPa·s 미만이고, NCO 관능도가 2.3 내지 4.0이며, (a1) 이소시아누레이트기 함유 폴리이소시아네이트, (a2) 바이우레트기 함유 폴리이소시아네이트, (a3) 우레티디온디이소시아네이트, (a4) 우레탄기 함유 폴리이소시아네이트, (a5) 알로파네이트기 함유 폴리이소시아네이트, (a6) 이소시아누레이트기와 알로파네이트기를 함유하는 폴리이소시아네이트, (a7) 카르보디이미드기 및(또는) 우레톤이민기 함유 폴리이소시아네이트, (a8) 옥사디아진트리온기 함유 폴리이소시아네이트, 및 (a9) 그의 혼합물로 이루어진 군으로부터 선택된 지방족 폴리이소시아네이트, (B) (b1) 평균 관능도가 1내지 4이고 분자량이 약 500내지 10,000이며, 히드록시기와 아민기로 이루어진 군으로부터 선택된 1개 이상의 기를 함유하고, 성분(B)와 성분(C)의 중량을 기준으로 약 30 내지 94.9중량%의 양으로 존재하는 화합물 1종 이상, 및 (b2) 분자량이 61 내지 500이고, 디올, 트리올, 1차 아민, 2차 아민, 아미노알코올 및 그의 혼합물로 이루어진 군으로부터 선택되며, OH와 NH의 당량비는 1:1 내지 25:1이고, 성분(B)와 성분(C)의 중량을 기준으로 약 5내지 60중량%의 양으로 존재하는 유기 연쇄신장제를 함유하는 이소시아네이트 반응성 성분, (C) 성분(B)와 성분(C)의 중량을 기준으로 0.1내지 10중량%의 양으로 존재하는 1종 이상의 촉매, 및 임의로, (D) 보조제 및(또는) 첨가제로 이루어지며, 성분(B)와 성분(C)의 양은 총 100%이고, 이들 성분은 이소시아네이트 지수 80 내지 130에서 완샷 공정으로 가공되며, 지방족 폴리이소시아네이트는 10중량% 미만의 이소포론디이소시아네이트를 함유하는 것을 반응 혼합물로부터 반응 사출 성형법(RIM Process)에 의하여 폴리우레탄 성형물을 제조하는 방법.
- 제1항에 있어서, 이소시아네이트 반응성 성분(B)가 성분(B)가 성분(C)의 중량을 기준으로 약 0.5내지 25중량%의 양으로 존재하는 분자량이 32내지 500인 1종 이상의 유기 1관능성 알코올을 더 함유하는 것이 특징인 방법.
- 제1항에 있어서, 성분(C)가 (c1) 성분(B)와 성분(C)의 중량을 기준으로 0.1내지 10중량%의 양으로 존재하며, 금속카르복실레이트, 금속할라이드, 암모늄카르복실레이트, 및 그의 혼합물로 이루어진 군으로부터 선택된 1종 이상의 촉매, (c2) 이소시아네이트 반응성 성분의 중량을 기준으로 0내지 10중량%의 양으로 존재하는 1종 이상의 주석-황 촉매, 및 (c3) 이소시아네이트 반응성 성분의 중량을 기준으로 0내지 10중량%의 양으로 존재하는 1종 이상의 3차 아민 촉매를 함유하며, 성분(c1),(c2) 및 (c3)의 양은 성분(B)와 성분(C)의 중량을 기준으로 총 0.1내지 10중량%인 것이 특징인 방법.
- 제2항에 있어서, 성분(B)가 (ⅰ) 성분(B)와 성분(C)의 중량을 기준으로 45내지 92.5중량%의 성분(b1) 및 (ⅱ) 성분(B)와 성분(C)의 총중량을 기준으로 7내지 50중량%의 성분(b2)를 함유하는 것이 특징인 방법.
- 제4항에 있어서, 성분(B)가 (ⅰ) 성분(B)와 성분(C)의 중량을 기준으로 66내지 92중량%의 성분(b1) 및 (ⅱ) 성분(B)와 성분(C)의 총중량을 기준으로 7내지 30중량%의 성분(b2)를 함유하는 것이 특징인 방법.
- 제3항에 있어서, 성분(C)가 (c1) 성분(B)와 성분(C)의 중량을 기준으로 0.5내지 5.0중량%의 양으로 존재하며, 금속카르복실레이트, 금속할라이드, 암모늄카르복실레이트, 및 그의 혼합물로 이루어진 군으로부터 선택된 1종 이상의 촉매, (c2) 성분(B)와 성분(C)의 중량을 기준으로 0내지 5.0중량%의 양으로 존재하는 1종 이상의 주석-황 촉매 및 (c3) 성분(B)와 성분(C)의 중량을 기준으로 0내지 5.0중량%의 양으로 존재하는 1종 이상의 3차 아민 촉매를 함유하며, 성분(c1),(c2) 및 (c3)의 양은 성분(B)와 성분(C)의 중량을 기준으로 총 0.5내지 5.0중량%인 것이 특징인 방법.
- 제6항에 있어서, 촉매(C)가 (c1) 성분(B)와 성분(C)의 중량을 기준으로 1내지 4.0중량%의 양으로 존재하며, 금속카르복실레이트, 금속할라이드, 암모늄카르복실레이트, 및 그의 혼합물로 이루어진 군으로부터 선택된 1종 이상의 촉매, (c2) 성분(B)와 성분(C)의 중량을 기준으로 0내지 4.0중량%의 양으로 존재하는 1종 이상의 주석-황 촉매 및 (c3) 성분(B)와 성분(C)의 중량을 기준으로 0내지 4.0중량%의 양으로 존재하는 1종 이상의 3차 아민 촉매를 함유하며, 성분(c1),(c2) 및 (c3)의 양은 성분(B)와 성분(C)의 중량을 기준으로 총 1내지 4중량%인 것이 특징인 방법.
- 제3항, 제6항 및 제7항 중 어느 한 항에 있어서, 성분(C1)는 디메틸주석디라우레이트, 비스무스트리네오데카노에이트, 디메틸주석디클로라이드, 트리메틸히드록시에틸암모늄-2-에틸헥사노에이트 및 그의 혼합물로 이루어진 군으로부터 선택되며, 성분(C2)는 디메틸주석디라우릴메르캅티드, 디부틸주석디라우릴메르캅티드, 및 그의 혼합물로 이루어진 군으로부터 선택되는 것이 특징인 방법.
- 제2항, 제4항 및 제5항 중 어느 한 항에 있어서, (b1) 폴리히드록시 화합물이 폴리에테르 폴리에테르 폴리올이고, (b2) 유기 연쇄 신장제가 1, 4 -부탄디올, 2- 메틸 -1,3- 프로판디올, 시클로 헥실아민, 디부틸아민,모노에탈올아민, 디에탄올아민, 및 그의 혼합물로 이루어진 군으로부터 선택되는 것이 특징인방법.
- 1내지 7항중 어느 한 항에 있어서,(a1) 1,6-헥사메틸렌디이소시아네이트로부터 제조되고, 이소시아네이트 함량이 약 21.6중량%이며, 단량체성 디이소시아네이트 함량이 0.2% 미만이며, 25℃에서의 점도가 약 3,000mPa·s인 이소시아누레이트기 함유 폴리이소시아네이트, (a2) 1,6-헥사메틸렌디이소시아네이트로부터 제조되고, 이소시아네이트 함량이 약 23%이며, 단량체성 디이소시아네이트 함량이 0.7% 미만이며, 25℃에서의 점도가 1,300 내지 2,200mPa·s인 바이우레트기 함유 폴리이소시아네이트, 및 (a3) 1,6-헥사메틸렌디이소시아네이트로부터 제조되고, 이소시아네이트 함량이 약 18내지 21%이며, 25℃에서의 점도가 500내지 1,500mPa·s이고, 단량체성 이소시아네이트 함량이 0.7중량% 미만인 이소시아누레이트기와 알로파네이트기를 함유하는 폴리이소시아네이트로 이루어진 군으로부터 선택되는 것이 특징인 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.