KR930021673A - 가요성 폴리우레탄 발포체의 제조 방법 - Google Patents
가요성 폴리우레탄 발포체의 제조 방법 Download PDFInfo
- Publication number
- KR930021673A KR930021673A KR1019930005350A KR930005350A KR930021673A KR 930021673 A KR930021673 A KR 930021673A KR 1019930005350 A KR1019930005350 A KR 1019930005350A KR 930005350 A KR930005350 A KR 930005350A KR 930021673 A KR930021673 A KR 930021673A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- prepolymer
- isocyanate
- prepolymers
- prepared
- Prior art date
Abstract
본 발명은 유리 NCO 함량이 2 내지 15중량%인 이소시아네이트 에비중합체, 유리 NCO 함량이 25 내지 31중량%인 이소시아네이트 예비중합체, 및 물을 함유하는 이소시아네이트-반응성 조성물을 반응시키는 가요성 발포체의 제조 방법에 관한 것이다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (10)
- 에틸렌 옥사이드 함량이 30중량% 이하인 폴리옥시알킬렌 폴리올로부터 제조된 유리 NCO 함량이 2 내지 15중량%인 이소시아네이트 예비중합체(제1예비중합체0 및 에틸렌 옥사이드 함량이 50중량% 이상인 폴리옥시알킬렌 폴리올로부터 제조된 유리 NCO 함량이 25 내지 31중량%인 다른 이소시아네이트 예비중합체(제2예비중합체)를 1.5-19:1(제1예비중합체 : 제2예비중합체)의 중량비로 하여 40중량% 이상의 물을 함유하는 이소시아네이트 반응성 조성물과 반응시키는 것을 특징으로 하는 가요성 폴리우레탄 발포체의 제조 방법.
- 제1항에 있어서, 제1 및 제2예비중합체의 총중량을 기준으로 하여 계산해서 60 내지 95중량%의 제1예비중합체와 5 내지 40중량%의 제2예비중합체를 함유하는 폴리이소시아네이트 조성물 100 중량부를 이소시아네이트 반응성 조성물 1 내지 20중량부와 반응시키는 것을 특징으로 하는 방법.
- 제1항에 있어서, 제1 및 제2예비중합체를 각각 독립적으로 이소시아네이트 반응성 조성물과 접촉시키는 것을 특징으로 하는 방법.
- 제1항에 있어서, 제2예비종합체가 이소시아네이트 관능가 2.5 내지 3.0의 폴리메틸렌 폴리페닐렌 폴리이소시아네이트와 평균 공칭 히드록실 관능가 2 내지 6 및 수평균당량 250 내지 3000의 폴리옥시알킬렌 폴리올로부터 제조된 것임을 특징으로 하는 방법.
- 제1항에 있어서, 제1 및 제2예비중합체의 총중량을 기준으로 하여 계산해서 60 내지 95중량%의 제1예비중합체와 5 내지 40중량%의 제2예비중합체를 함유하는 폴리이소시아네이트 조성물 100중량부를 이소시아네이트 반응성 조성물 1 내지 20중량부와 반응시키고, 제1 및 제2예비중합체를 각각 독립적으로 이소시아네이트 반응성 조성물과 접촉시키고, 제2예비중합체가 이소시아네이트 관응가 2.5 내지 3.0의 폴리메틸렌 폴리페닐렌 폴리이소시아네이트와 평균 공칭 히드록실 관능가 2 내지 6 및 수평균 당량 250 내지 3000의 폴리옥시알킬렌 폴리올로부터 제조된 것임을 특징으로 하는 방법.
- 제1 및 제2예비중합체의 총중량을 기준으로 하여 계산할 때 60 내지 95중량%의 유리 NCO 함량이 2 내지 15중량%이고 에틸렌 옥사이드 함량 30중량% 이하의 폴리옥시알킬렌 폴리올로부터 제조된 제1이소시아네이트 예비중합체, 및 5 내지 40중량%의 유리 NCO 함량이 25 내지 31중량%이고 에틸렌 옥사이드 함량 50중량% 이상의 폴리옥시알킬렌 폴리올로부터 제조된 제2 이소시아네이트 예비중합체로 이루어진 폴리이소시아네이트 조성물.
- 제6항에 있어서, 제2예비중합체가 이소시아네이트 관능가 2.5 내지 3.0의 폴리메틸렌 폴리페닐렌 폴리이소시아네이트와 평균 공칭 히드록실 관능가 2 내지 6 및 수평균 당량 250 내지 3000의 폴리옥시알킬렌 폴리올로부터 제조된 것임을 특징으로 하는 폴리이소시아네이트 조성물.
- (A)에틸렌 옥사이드 함량이 30중량% 이하인 폴리옥시알킬렌 폴리올로부터 제조된 유리 NCO 함량이 2 내지 15중량%인 이소시아네이트 예비중합체(제1예비중합체) 및 (B)에틸렌 옥사이드 함량이 50중량% 이상인 폴리옥시알킬렌 폴리올로부터 제조된 유리 NCO 함량이 25 내지 31중량% 이상인 폴리옥시알릴렌 폴리올로부터 제조된 유리 NCO 함량이 25 내지 31중량%인 다른 이소시아네이트 예비중합체(제2예비중합체)를 1.5-19:1(제1예비중합체 : 제2예비중합체)의 중량비로 함유하고 (C)40중량% 이상의 물을 함유하는 이소시아네이트-반응성 조성물을 함유하는 반응체.
- 제8항에 있어서, 반응계가 제1 및 제2예비중합체를 기준으로 하여 계산해서 60 내지 95중량%의 제1예비중합체 및 5 내지 40중량%의 제2예비중합체를 함유하고, 제1 및 제2예비중합체 100중량부에 대하여 이소시아네이트-반응성 조성물을 1 및 제2예비중합체 100중량부에 대하여 이소시아네이트-반응성 조성물을 1 내지 20중량부 함유하는 것을 특징으로 하는 반응계.
- 제8항 또는 제9항에 있어서, 제2예비중합체가 이소시아네이트 관능가 2.5 내지 3.0의 폴리메틸렌 폴리페닐렌 폴리이소시아네이트와 평균 공칭 히드록실 관능가 2 내지 6 및 수평균 당량 250 내지 3000의 폴리옥시알킬렌 폴리올로부터 제조된 것임을 특징으로 하는 반응계.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.