KR940018501A - 에어백용 폴리에스테르 필라멘트 직물 - Google Patents
에어백용 폴리에스테르 필라멘트 직물 Download PDFInfo
- Publication number
- KR940018501A KR940018501A KR1019940000177A KR19940000177A KR940018501A KR 940018501 A KR940018501 A KR 940018501A KR 1019940000177 A KR1019940000177 A KR 1019940000177A KR 19940000177 A KR19940000177 A KR 19940000177A KR 940018501 A KR940018501 A KR 940018501A
- Authority
- KR
- South Korea
- Prior art keywords
- yarn
- polyester
- fabric
- uncoated
- polyester filament
- Prior art date
Abstract
건열 또는 습열 노화 후에도 공기 투과도가 낮은, 에어백용으로 유용한 비코우팅 및 비칼렌더링 폴리에스테르 필라멘트 직물은 (1)초기 하중 0.08g/데니어 하에서 150℃/분의 가열속도로, 길이를 50mm로 고정한 시편 얀을 실온에서 얀의 용융 온도까지 가열함으로써 측정한 최대 열 응력이 0.8g/데니어 이하이고, (2)초기 하중 0.08g/데니어 하에서 150℃/분의 가열 속도로, 시편 얀의 열 수축을 제한하지 않으면서 길이 50mm의 시편 얀을 실온에서 얀의 용융온도까지 가열함으로써 측정한 최대 열 수축율이 25% 이하이며, (3)25℃의 o-클로로페놀 중에서 1.2g/100ml농도로 측정한 제한 점도수가 0.80~0.95dl/g이고 (4)말단 카르복실기의 함량이 5~35당량/톤인 다수의 폴리에스테르 멀티필라멘트 경사 및 위사를 함유한다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (13)
- 각각 서로 독립적으로 (1)초기 하중 0.08g/데니어 하에서 150℃/분의 가열 속도로, 길이를 50mm로 고정한 시편 얀을 실온에서 얀의 용융 온도까지 가열함으로써 측정한 최대 열 응력이 0.8g/데니어 이하이고, (2)초기하중 0.08g/데니어 하에서 150℃/분의 가열 속도로, 시편 얀의 열 수축을 제한하지 않으면서 길이 50mm의 시편 얀을 실온에서 얀의 용융 온도까지 가열함으로써 측정한 최대 열 수축율이 25% 이하이며, (3)25℃의 o-클로로페놀 중에서 1.2g/100ml농도로 측정한 제한 점도수가 0.80~0.95dl/g이고, (4)말단 카르복실기의 함량이 5~35당량/톤인 다수의 폴리에스테르 멀티필라멘트 경사 및 위사를 함유함을 특징으로 하는 에어 백용 비코우팅 및 비칼렌더링 폴리에스테르 필라멘트 직물.
- 제 1 항에 있어서, 폴리에스테르 멀티필라멘트 경사 및 위사가 각각 서로 독립적으로 잔류의 디에틸렌글리콜 함량이 0.1~1.5중량%이고 이산화티타늄 안료의 함량이 0.2% 이하인 비코우팅 및 비칼렌더링 폴리에스테르 필라멘트 직물.
- 제 1 항에 있어서, 폴리에스테르 멀티필라멘트 경사 및 위사가 각각 서로 독립적으로 결정화도가 45~65중량%이고, 결정의 격자망(100)전면에 대하여 직각에서 측정한 결정 크기가 3.0~9.0nm이 비코우팅 및 비칼렌더링 폴리에스테르 필라멘트 직물.
- 제 1 항에 있어서, 폴리에스테르 멀티필라멘트 경사 및 위사가 각각 서로 독립적으로 연계수가 2500이하이고 인터레이스 수가 10~50/m인 비코우팅 및 비칼렌더링 폴리에스테르 필라멘트 직물.
- 제 1 항에 있어서, 폴리에스테르 멀티필라멘트 경사 및 위삭 각각 서로 독립적으로 각각의 두께가 0.5~3.0데니어인 폴리에스테르 필라멘트로 구성된 비코우팅 및 비칼렌더링 폴리에스테르 필라멘트 직물.
- 제 1 항에 있어서, 120℃에서 500시간 동안의 건열 노화후 측정한 공기 투과도가 0.5ml/㎠/sec/0.5인지 Aq 이하인 비코우팅 및 비칼렌더링 폴리에스테르 필라멘트 직물.
- 제 1 항에 있어서, 직물을 지름이 700mm인 2개의 원형 조각으로 절단하고; 원형 조각을 서로 겹쳐놓고; 겹쳐진 조각의 둥근 모서리 부분을 더블 스레드 체인 스티치로 서로 연결시켜 겹쳐진 원형 조각에 대하여 중심이 같고 지름이 670mm인 원형의 솔기를 형성하여 원형의 백을 만들고; 이 백을 120℃에서 500시간 동안 건열 노화시키거나 상대 습도 95%의 85℃에서 500시간 동안 습열 노화시키고; 노화된 백의 한 조각면의 중심에 지름이 106mm인 원형의 구멍을 형성하고; 40kg/㎠G의 압력하에서 압축된 고압의 공기 40ℓ를 중앙의 구멍을 통해 백으로 즉시 불어 넣어 노화된 백의 파열 강도를 측정하고; 직물의 파열 강도 유지도를 비노화 백에 대한 노화된 백의 파열 강도의 비율(%)로 나타내는 방법으로 측정한 직물의 파열 강도 유지도가 70% 이상인 비코우딩 및 비칼렌더링 폴리에스테르 필라멘트 직물.
- 각각 서로 독립적으로 150℃에서의 열 수축율이 3~13%인 다수의 폴리에스테르 멀티필라멘트 경사 및 위사를 위빙하여 경사 및 위사 방향의 커버 팩터가 1000~1200이고 경사 방향 및 위사 방향간의 커버 팩터의 차가 200이하인 회색의 직물을 제공하고; 생성된 열고정 직물의 공기 투과도가 0.5ml/㎠/sec0.5인치 Aq 이하일 정도의 장력하에서 열고정 금속 로울러 표면과 접촉시킴으로써 직물을 건열 고정시켜 제조된 비코우팅 및 비칼렌더링 폴리에스테르 필라멘트 직물.
- 제 8 항에 있어서, 회색 직물 중의 폴리에스테르 멀티필라멘트사의 극한 신장율이 20% 이하인 비코우팅 및 바칼렌더링 폴리에스테르 필라멘트 직물.
- 제 8 항에 있어서, 폴리에스테르 멀티필라멘트 경사 및 위사가 각각 서로 독립적으로 잔류의 디에틸렌 글리콘의 함량이 0.1∼1.5중량%이고 이산화 티타늄 인료의 함량이 0.2% 이하인 비코우팅 및 비칼렌더링 폴리에스테르 필라멘트 직물.
- 제 8 항 있어서, 폴리에스테르 멀티필라멘트 경사 및 위사가 각각 서로 독립적으로 결정화도가 45~65중량%이고 결정의 격자망(100)전면에 대하여 직각에서 측정한 결정 크기가 3.0~9.0nm인 비코우팅 및 비칼렌더링 폴리에스테르 필라멘트 직물.
- 제 8 항에 있어서, 폴리에스테르 멀티필라멘트 경사 및 위사가 각각 서로 독립적으로 연계수가 2500이하이고 인터레이스수가 10-50/m인 비코우팅 및 비칼렌더링 폴리에스테르 필라멘트 직물.
- 제 8 항에 있어서, 폴리에스테르 멀티필라멘트 경사 및 위사가 각각 서로 독립적으로 두께가 0.5~3.0데니어인 다수외 폴리에스테르 필라멘트로 구성된 비코우팅 및 비칼렌더링 폴리에스테르 필라멘트 직물.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.