KR860003361A - 에나멜 코우팅용 냉연강판과 그 제조 방법 - Google Patents

에나멜 코우팅용 냉연강판과 그 제조 방법 Download PDF

Info

Publication number
KR860003361A
KR860003361A KR1019850007885A KR850007885A KR860003361A KR 860003361 A KR860003361 A KR 860003361A KR 1019850007885 A KR1019850007885 A KR 1019850007885A KR 850007885 A KR850007885 A KR 850007885A KR 860003361 A KR860003361 A KR 860003361A
Authority
KR
South Korea
Prior art keywords
less
enamel
cold rolled
steel sheet
iron
Prior art date
Application number
KR1019850007885A
Other languages
English (en)
Other versions
KR890003664B1 (ko
Inventor
아끼라 야쓰다 (외 4)
히라 준코 이게
겐지 이또
준스께 다까사끼
고조우 쓰노야마
Original Assignee
노다로우 헤이
가와사끼 세이데쓰 가부시기 가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP59223780A external-priority patent/JPS61104051A/ja
Priority claimed from JP60117294A external-priority patent/JPS61276958A/ja
Application filed by 노다로우 헤이, 가와사끼 세이데쓰 가부시기 가이샤 filed Critical 노다로우 헤이
Publication of KR860003361A publication Critical patent/KR860003361A/ko
Application granted granted Critical
Publication of KR890003664B1 publication Critical patent/KR890003664B1/ko

Abstract

내용 없음

Description

에나멜 코우팅용 냉연강판과 그 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 실시예(1)에서 제공된 연속적으로 가열 냉각된 강판 견본으로 생성되는 희박산수(Pickling products)의 생성물량과 에나멜 밀착성을 그래프로 설명하는 도표이다.
제2도는 실시예(2)에서 제공된 연속적으로 박스가열 냉각된(box annealed)강판 견본으로 생성되는 희박산수의 생성물량과 에나멜밀착성을 그래프로 설명하는 도표이다.

Claims (64)

  1. 하기의 중량비의 각 성분과 As, Sb,Bid으로 구성되는 그루우프에서 선정된 0.003 내지 0.03%인 최소한 하나의 원서와 불가피적으로 잔여철로 구성되는 에나멜 피복용 냉연강판.
  2. C 0.005% 이하
  3. P 0.02% 이하
  4. S 0.03% 이하
  5. N 0.005% 내지 0.012%
  6. Ti 0.15% 이하 Ti(48/12C+48/14N+4832S)%
  7. Cu 0.08% 이하
  8. 프레스 성형성, 에나멜밀착성, 스케일링 저항성이 우수한 에나멜 피복용 냉연강판을 제조함에 있어서 하기의 각 성분과 As, Sb, Bi으로 구성되는 그루우프에서 선정된 0.003 내지 0.03%인 최소한 하나의 원소와 잔여물은 불가피하게 철로 형성되는 용강을 연속주조하고 열간압연 냉간압연후에 재결정온도이상 Ac3점 이하의 온도역에서 연속 아니일링을 실시함을 특징으로 하는 에나멜 피복용 냉연강판의 제조법.
  9. C 0.005% 이하
  10. P 0.02% 이하
  11. S 0.03% 이하
  12. N 0.005% 내지 0.012%
  13. Ti 0.15% 이하 Ti(48/12C+48/14N+4832S)%
  14. Cu 0.08% 이하
  15. 프레스 성형성, 에나멜 밀착성, 스케일링 저항성이 우수한 에나멜 피복용 냉연강판을 제조함에 있어서 하기의 각 성분과 As, Sb, Bi으로 구성된 그루우프에서 선택된 0.003 내지 0.03%인 최소한 하나의 원소와 잔여물은 불가피하게 철로 형성되는 용강을 연속주조하고, 열간압연 냉강압연후에 재결정온도이상, 800℃ 이하의 온도역에서 박스아니일링함을 특징으로 하는 에나멜 피복용 냉연강판의 제조방법.
  16. C 0.005% 이하
  17. P 0.02% 이하
  18. S 0.03% 이하
  19. N 0.005% 내지 0.012%
  20. Ti 0.15% 이하 Ti(48/12C+48/14N+4832S+0.03)%
  21. Cu 0.08% 이하
  22. 하기의 중량비를 가지는 우성분과 Se와 Te로 구성된 그루우프에서 0.003 내지 0.05%인 최소한 하나의 원소를 선택하고 잔여물은 불가피하게 철로 형성되는 에나멜 피복용 냉연강판.
  23. C 0.005% 이하
  24. P 0.02% 이하
  25. S 0.03% 이하
  26. N 0.005% 내지 0.012%
  27. Ti 0.15% 이하 Ti(48/12C+48/14N+4832S)%
  28. Cu 0.08% 이하
  29. 프레스 성형성, 에나멜 밀착성, 스케일링 저항성이 우수한 에나멜 피복용 냉연강판을 제조함에 있어서 하기의 각 성분과 Se와 Te로 구성되는 그 루우프에서 선택한 0.003 내지 0.05%인 최소한 하나의 원소와 잔여물은 불가피하게 철로 구성되는 용강을 연속주조하고 열간압연, 냉각압연후에 재결정온도이상, Ac3점 이하의 온도역에서 아니일링을 실시함을 특징으로 하는 에나멜 피복용 냉연강판의 제조방법.
  30. C 0.005% 이하
  31. P 0.02% 이하
  32. S 0.03% 이하
  33. N 0.005% 내지 0.012%
  34. Ti 0.15% 이하 Ti(48/12C+48/14N+4832S)%
  35. Cu 0.08% 이하
  36. 프레스 성형성, 에나멜 밀착성, 스케일링 저항성이 우수한 에나멜 피복용 냉연강판을 제조함에 있어서 하기의 각 성분과 Se와 Te로 형성되는 그 루우프에서 선택한 중량비 합계가 0.003 내지 0.05%인 최소한 하나의 원소와 잔여물은 불가피하게 철로 형성되는 용강을 연속적으로 주조하고, 열간압연, 냉각압연후에 재결정온도 이상 800℃이하의 온도역에서 박스아니일링을 실시함을 특징으로 하는 에나멜 피복용 냉연강판의 제조방법.
  37. C 0.005% 이하
  38. P 0.02% 이하
  39. S 0.03% 이하
  40. N 0.005% 내지 0.012%
  41. Ti 0.15% 이하 Ti(48/12C+48/14N+4832S+0.03)%
  42. Cu 0.08% 이하
  43. 하기의 중량비의 각 성분과 As, Sb 및 Bi으로 형성되는 그루우프에서 최소한 한가지와 Se 및 또는 Te와의 합계가 0.002 내지 0.05이고, 잔여분은 불가피하게 철로 형성되는 에나멜 피복용 냉연강판.
  44. C 0.005% 이하
  45. P 0.02% 이하
  46. S 0.03% 이하
  47. N 0.005% 내지 0.012%
  48. Ti 0.15% 이하 Ti(48/12C+48/14N+4832S)%
  49. Cu 0.08% 이하
  50. 프레스 성형성, 에나멜 밀착성, 스케일링 저항성이 우수한 에나멜 피복용 냉연강판을 제조함에 있어서 하기의 각 성분과 As, Sb, Bi으로 형성되는 그루우프에서 최소한 한가지와 Se와 Te로 형성되는 그루우프중에서 선정된 하나의 원소의 합계가 0.002 내지 0.05%이고, 잔여분은 불가피하게 철로 구성되는 용강을 계속 주조하고 열간압연 냉간압연후에 재결정온도 이상 Ac3점 이하의 온도역에서 아니일링을 실시하는 것을 특징으로 하는 에나멜 피복용 냉연강판의 제조방법.
  51. C 0.005% 이하
  52. P 0.02% 이하
  53. S 0.03% 이하
  54. N 0.005% 내지 0.012%
  55. Ti 0.15% 이하 Ti(48/12C+48/14N+4832S)%
  56. Cu 0.08% 이하
  57. 프레스 성형성, 에나멜 밀착성, 스케일링 저항성이 우수한 에나멜 피복용 냉연강판을 제조함에 있어서 하기의 각 성분과 As, Sb, Bi으로 형성되는 그루우프에서 최소한 한가지와 Se와 Te로 형송되는 그루우프에서 선택되는 한지의 원소의 합계가 0.002 내지 0.05%이고, 잔여분은 불가피하게 철로 구성되는 용강을 계속 주조하고, 열간압연, 냉간압연후에 재결정온도 이상, 800℃이하의 온도역에서 박스아니일링을 실시하는 것을 특징으로 하는 에나멜 피복용 냉연강판의 제조방법.
  58. C 0.005% 이하
  59. P 0.02% 이하
  60. S 0.03% 이하
  61. N 0.005% 내지 0.012%
  62. Ti 0.15% 이하 Ti(48/12C+48/14N+4832S+0.03)%
  63. Cu 0.08% 이하
  64. ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019850007885A 1984-10-24 1985-10-23 에나멜 코우팅용 냉연강판과 그 제조방법 KR890003664B1 (ko)