KR20040104542A - 정공 수송 중합체 및 이 중합체로 만들어진 장치 - Google Patents
정공 수송 중합체 및 이 중합체로 만들어진 장치 Download PDFInfo
- Publication number
- KR20040104542A KR20040104542A KR10-2004-7015072A KR20047015072A KR20040104542A KR 20040104542 A KR20040104542 A KR 20040104542A KR 20047015072 A KR20047015072 A KR 20047015072A KR 20040104542 A KR20040104542 A KR 20040104542A
- Authority
- KR
- South Korea
- Prior art keywords
- polymer
- layer
- groups
- hole transport
- polymers
- Prior art date
Abstract
본 발명은 일반적으로 융합 방향족 고리 기를 포함하는 다수의 치환체가 연결된 중합체 주쇄를 포함하는 정공 수송 중합체에 관한 것이며, 단 이 중합체는 트리아릴아민 및 카르바졸 기중에서 선택되는 기를 함유하지 않는다. 본 발명은 또한 이 중합체로 만들어진 장치에 관한 것이다.
Description
표시장치를 구성하는 발광 다이오드와 같은, 빛을 방출하는 유기 전자 장치는 많은 상이한 종류의 전자 설비에 존재한다. 이러한 장치에서, 유기 활성층은 두 전기 접촉층 사이에 끼여 있다. 이들 전기 접촉층중 하나 이상은 광투과성이어서 전기 접촉층을 통해 빛이 통과할 수 있다. 유기 활성층은 전기 접촉층을 가로질러 전기가 가해지면 광투과성 전기 접촉층을 통해 빛을 방출한다.
발광 다이오드에서 활성 성분으로서 유기 전계발광성 화합물을 사용하는 것은 널리 공지되어 있다. 안트라센, 티아디아졸 유도체 및 쿠마린 유도체와 같은 간단한 유기 분자가 전계발광성을 나타내는 것으로 알려져 있다. 반도전성 공액 중합체도 또한 전계발광성 성분으로서 사용되었다. 홀메스(Holmes) 등의 미국 특허 제5,653,914호에 스틸베닐 또는 옥사디아졸 측쇄를 갖는 중합체 물질이 보고된 바 있다.
많은 전계발광성 물질은 불량한 전하 수송 특성을 갖는다. 이러한 특성을 개선시키기 위하여, 추가의 전하 수송 물질이 발광층에 부가되거나 또는 발광층과 전극 사이의 분리층으로서 부가될 수 있다. 정공 수송 물질이 자주 사용되어 왔다. 공지의 정공 수송 물질로는 N,N'-디페닐-N,N'-비스(3-메틸페닐)-[1,1'-비페닐]-4,4'-디아민(TPD) 및 비스[4-(N,N-디에틸아미노)-2-메틸페닐] (4-메틸페닐)메탄(MPMP)과 같은 간단한 분자, 및 폴리비닐카르바졸(PVK), (페닐메틸)폴리실란, 폴리(3,4-에틸렌디옥시티오펜)(PEDOT) 및 폴리아닐린(PANI)과 같은 중합체 물질이 있다. 전자 및 정공 수송 물질(예: 4,4'-N,N'-디카르바졸 비페닐(BCP)); 또는 우수한 전자 및 정공 수송 특성을 갖는 발광 물질(예: 킬레이트화된 옥시노이드 화합물, 예를 들어 트리스(8-히드록시퀴놀레이토)알루미늄(Alq3))을 사용하는 것도 또한 공지되어 있다. 펜타센과 같은 융합 방향족 고리 화합물은 전자 수송 물질로서 공지되어 있다. 2개의 상이한 방향족 측기를 갖는 공중합체는 미국 특허 제6,007,928호에 발광 물질로서 개시되었다.
신규한 정공 수송 물질이 계속적으로 필요하다.
발명의 요약
본 발명은 하나 이상의 융합 방향족 고리 기를 포함하는 다수의 치환체가 연결된 중합체 주쇄를 포함하는 정공 수송 중합체에 관한 것으로, 단 이 중합체는 트리아릴아민 및 카르바졸 기중에서 선택된 기를 함유하지 않는다.
본 발명은 또한 양극과 음극 사이에 활성층을 갖는 유기 전자 장치에 관한것으로, 이 장치는 하나 이상의 융합 방향족 고리 기를 포함하는 다수의 치환체가 연결된 중합체 주쇄를 포함하는 하나 이상의 제1 정공 수송 중합체를 추가로 가지며, 단 이 중합체는 트리아릴아민 및 카르바졸 기중에서 선택된 기를 함유하지 않는다.
본원에 사용된 바와 같이, "정공 수송 물질"이란 용어는 양극으로부터 양전하를 받아서 비교적 고효율 및 저손실의 물질의 두께를 통해 양전하를 이동시킬 수 있는 물질을 뜻한다. "정공 수송 중합체"란 용어는 중합체성 정공 수송 물질을 뜻하는 것이다. "중합체"란 용어는 단독중합체, 및 둘 이상의 상이한 반복 단위를 갖는 공중합체를 포함한다. "관능화된 중합체"란 용어는 중합체 주쇄에 융합 방향족 고리 기를 결합시키도록 반응할 수 있는 하나 이상의 관능기(들)를 갖는 중합체를 뜻한다. "관능화된 융합 방향족 고리 화합물"이란 용어는 중합체 주쇄에 결합시키도록 반응할 수 있는 하나 이상의 관능기(들)를 갖는 융합 방향족 고리 화합물을 뜻한다. "광활성"이란 용어는 전계발광성 및(또는) 감광성을 나타내는 임의의 물질을 가리킨다. "(메트)아크릴"이란 용어는 아크릴, 메타크릴 또는 이들의 혼합물을 뜻한다. "(메트)아크릴레이트"란 용어는 아크릴레이트, 메타크릴레이트 또는 이들의 혼합물을 뜻한다. 또한, 처음부터 끝까지 IUPAC 번호부여 시스템이 사용되는데, 주기율표의 족은 왼쪽부터 오른쪽으로 1에서 18로 번호매긴다(문헌[CRC Handbook of Chemistry and Physics, 81st Edition, 2000]).
본 발명은 유용한 정공 수송 특성을 갖는 중합체 물질에 관한 것이다. 이 중합체는 또한 전계발광성일 수 있다. 본 발명은 또한 활성층이 이러한 중합체 물질을 포함하는 전자 장치에 관한 것이다.
도 1은 발광 장치(LED)의 개략도이다.
도 2는 실시예 5의 장치에 해당하는 전류 대 전압 곡선이다.
도 3은 실시예 9의 장치에 해당하는, 전류 대 전압 곡선 및 발광 대 전압 곡선이다.
중합체 주쇄에 결합된 치환체의 하나 이상의 융합 방향족 고리 기는 일반적으로 탄소수가 10 내지 50이고 2 내지 8개, 바람직하게는 2 내지 4개의 융합 방향족 고리를 함유한다. 융합 방향족 고리 기는 임의로 탄소수 1 내지 20의 알킬 또는 아릴 기로 치환될 수 있다. 적합한 융합 방향족 고리 기의 예로는 나프틸, 안트라실, 페난트릴, 페날레닐, 플루오레닐, 피레닐, 기타 테트라세닐 및 펜타세닐 기가 있다. 본 발명에 따라, 정공 수송 특성은 일반적으로 정공 수송 특성을 제공하기 위해 사용되는 기, 예를 들어 트리아릴아민 기 및 카르바졸 기의 부재하에 달성된다.
정공 수송 중합체는 제1 유형의 반응성 기를 갖는 중합체("관능화된 중합체")와 제2 유형의 반응성 기를 갖는 융합 방향족 고리 화합물("관능화된 융합 방향족 고리 화합물")을 반응시킴으로써 얻을 수 있다. 이를 하기 반응식 1에 개략적으로 나타내었다.
상기 식에서,
Pol은 중합체 주쇄를 나타내고,
Ar은 융합 방향족 고리를 나타내고,
R1및 R2는 각각 제1 유형 및 제2 유형의 반응성 기를 나타내고,
R3은 R1과 R2의 반응으로부터 생성된 연결기를 나타내고,
S는 반응에서 형성될 수 있는 임의의 부산물을 나타낸다.
중합체에 작은 분자를 결합시키는 기법은 라텍스 입자에 대한 생화학적 리간드의 커플링에서와 같이 널리 공지되어 있다. 이는, 예를 들어 뱅스(L. B. Bangs)의 문헌[Uniform Latex Particles](미국 인디애나주 인디애나폴리스 소재의 세라젠 다이아그노스틱스 인코포레이티드(Seragen Diagnostics, Inc.)사의 서식 #1661-84)에 논의되어 있다. 예를 들어, 카르복실산 관능기를 갖는 중합체는 아미노 관능기를 갖는 융합 방향족 고리 화합물과 반응하여 아미드 연결기를 형성할 수 있다. 또 다르게는, 카르복실산 기는 중합체의 융합 방향족 고리 및 아미노 기상에 있을 수 있다. 유사하게, 히드록실 기는 산 염화물 기와 반응하여, 에스테르 연결기를 형성한다. 다른 유형의 반응짝으로는 히드록실 및 클로로메틸 기; 히드록실 및 카르복실산 기; 이소시아네이트 및 히드록실 또는 아민 기; 에폭시 및 아민 기; 산 염화물 및 아민 기; 술폰산 및 아민 기; 술폰산 염화물 및 히드록실 기; 알데하이드 및 아미노 기; 알데하이드 및 카르복실 기; 알데하이드 및 히드록실 기; 및 알데하이드 및 메틸케톤 기가 있다. 연결을 제공할 다양한 반응은 합성 유기 화학 문헌에서 입수할 수 있다.
또 다르게는, 정공 수송 중합체는, 하기 반응식 2에 나타낸 바와 같이, 융합 방향족 고리 기가 결합된 한 유형 이상의 단량체("관능화된 단량체")를 중합함으로써 얻을 수 있다.
상기 식에서,
Mon은 중합성 화합물을 나타내고,
R4는 연결기를 나타내고,
Ar 및 Pol은 상기 반응식 1에 정의된 바와 같다.
I. 관능화된 중합체
본 발명에 유용한 관능화된 중합체 화합물은 일반적으로 (a) 중합체 주쇄; (b) 다수의 제1형 관능기; 임의로 (c) 중합체 주쇄와 제1형 관능기 사이의 간격기; 및 임의로 (d) 서로 동일하거나 상이한 다수의 제2형 관능기(들)를 갖는 것으로 기술될 수 있다. 중합체 주쇄는 바람직한 특성 및 가공성을 갖는 중합체 또는 공중합체일 수 있고, 융합 방향족 고리 기가 결합될 수 있다. 몇몇 종류의 유용한 중합체 주쇄로는 폴리아크릴레이트; 폴리메타크릴레이트; 폴리아라미드; 폴리스티렌; 폴리아릴렌; 폴리비닐렌; 폴리비닐 에테르; 및 폴리비닐 에스테르가 있다.
융합 방향족 고리 기를 결합시키기에 유용한 제1형의 관능기는 반응짝의 일부로서 상기 논의된 것중 임의의 것이다.
"융합 방향족 기의 밀도"로 기술될 수도 있는, 중합체 주쇄상의 융합 방향족 기의 수는 정공 수송 물질로서의 중합체의 효율에 영향을 줄 것이다. 그러나, 중합체를 선택할 때, 가공성 및 막 형성능과 같은 그밖의 인자도 고려하여야 한다. 본 발명의 중합체 물질에 있어서, 융합 방향족 기의 밀도는 제1형 관능기를 갖는 단량체("제1형 단량체") 대 중합체내 제1형 관능기를 갖지 않는 다른 단량체에 대한 상대적 비율에 의해 결정된다. 일반적으로, 제1 관능성 단량체 대 다른 단량체에 대한 비는 약 5:95 내지 95:5의 범위일 수 있다.
제1형 관능기는, 예를 들어 폴리아크릴산 중합체의 카르복실 기로서 중합체 주쇄에 직접 결합될 수 있다. 그러나, 제1형 관능기와 중합체 주쇄 사이에 간격기를 갖는 것도 가능하다. 유용한 간격기는 화학적으로 안정하고 중합체의 수송 특성에 해로운 영향을 주지 않는 것이다. 간격기는 포화 또는 불포화 지방족 기, 또는 방향족 기일 수 있다. 간격기는 헤테로원자, 특히 산소 및 질소를 함유할 수 있다. 일부 경우에서, 임의의 제1 관능기로 가장 쉽게 이용가능한 단량체는 간격기를 가지기 때문에, 간격기가 존재한다. 간격기는 일반적으로 탄소수가 1 내지 50, 바람직하게는 5 내지 15이다. 간격기는 간단히 중합체 주쇄와 제1 관능기 사이에 거리를 제공할 수 있거나, 이후 논의되는 바와 같이 관능성을 제공할 수 있다.
관능화된 중합체는 또한 하나 이상의 제2형 관능기를 가질 수 있다. 제2형 관능기는 최종 중합체의 물성을 개질시키기 위하여 존재할 수 있다. 이러한 유형의 기의 예로는 가소화기(예: 알킬렌 옥사이드 기), 및 반응성 및(또는) 가교결합성 기(예: 말단 비닐 기 및 에폭시 기)가 있다. 제2형 관능기는 중합체 주쇄내에, 제1형 관능기에 결합된 간격기에, 또는 제1형 관능기로부터 떨어진 측기에 존재할 수 있다.
관능화된 중합체는 통상적인 중합 기법을 사용하여, 바람직한 관능기(들)를 갖는 단량체(들)를 사용하여 제조될 수 있다. 적합한 단량체의 예로는 (메트)아크릴산(카르복실 관능성); 4-스티렌카르복실산(카르복실 관능성); 아미노알킬 아크릴레이트 및 메타크릴레이트(아미노 관능성); 히드록시알킬 (메트)아크릴레이트(히드록시 관능성); 글리시딜 (메트)아크릴레이트(에폭시 관능성); 및 바람직한 관능기를 갖는 유사 단량체가 있다.
관능화된 중합체는 단독중합체 또는 공중합체일 수 있다. 공중합체는 불규칙, 교호, 블록 또는 빗형 공중합체이도록 제조될 수 있다. 이들 상이한 구조적 공중합체를 형성하기 위한 방법은 당업계에 널리 공지되어 있으며, 예를 들어 죠지 오디안(George Odian)의 문헌[Principles of Polymerization, 3rd Edition(John Wiley & Sons, New York, NY, 1991)]; 라자르(M. Lazar) 등의 문헌[Chemical Reactions of Natural and Synthetic Polymers]; 베남(Benham) 및 킨슬(Kinstle)의 문헌[Chemical Reactions on Polymers(1988)]에 논의되어 있다.
II. 관능화된 융합 방향족 고리 화합물
관능화된 융합 방향족 고리 화합물은 상기 논의된 바와 같이 관능화된 중합체상의 기와 반응할 수 있는 반응성 기를 갖는다. 유용한 유형의 관능화된 융합 방향족 고리 화합물로는 방향족 아민, 방향족 술포닐 클로라이드, 방향족 이소티오시아네이트, 방향족 숙시닐 에스테르, 방향족 알데하이드, 및 방향족 알콜 또는 페놀이 있다. 이들 화합물중 일부, 예를 들어 1-(1-나프틸)에틸아민; 1-피렌메틸아민; 1-피렌프로필아민; 4'-(아미노메틸)플루오레신; 로다민 B 에틸렌 디아민; 로다민 B 술포닐 클로라이드; 및 5-디메틸아미노나프틸렌-1-술포닐 클로라이드는 상업적으로 입수가능하다. 그밖의 적합한 관능화된 융합 방향족 고리 화합물은 표준의 합성 화학 기법을 사용하여 제조될 수 있다.
III. 관능화된 단량체
일반적으로, 관능화된 단량체는 전술한 바와 같은 커플링 화학을 사용하여, 관능기를 단량체에 커플링시킴으로써 제조할 수 있다. 관능화된 단량체로부터 정공 수송 중합체를 제조하는 경우, 더 구조적으로 명확한 중합체 물질을 얻는 것이 가능하다. 관능화된 단량체는 블록 공중합체, 교호 공중합체, 빗형 중합체 및 그밖에 공지된 중합체 구조와 같은 상이한 구조를 생성하는 방법을 사용하여 중합될 수 있다. 관능화된 중합체 및 관능화된 융합 방향족 고리 화합물로부터 정공 수송 중합체를 제조하는 경우, 반응은 더 불규칙이고, 통계적으로 제어되는 방식으로 일어난다.
IV. 장치
본 발명은 또한 두 전기 접촉층 사이에 끼여 있는 유기 활성층, 양극 및 음극을 포함하는 전자 장치에 관한 것으로, 이 장치는 본 발명의 정공 수송 중합체를 추가로 포함한다. 전형적인 구조는 도 1에 나타나 있다. 장치(100)는 양극층(110) 및 음극층(150)을 갖는다. 양극에 인접하여 정공 수송 물질을 포함하는 임의층(120)이 있다. 음극에 인접하여 전자 수송 물질을 포함하는 임의층(140)이 있다. 양극과 음극(또는 임의의 전하 수송 층들) 사이에는 유기 활성층(130)이 있다. 본 발명의 정공 수송 중합체는 유기 활성층(130), 및(또는) 정공 수송층(120)에 존재한다. 각각의 작용성 층은 하나보다 많은 층으로 구성될 수 있는 것으로 이해된다.
장치는 일반적으로 또한 양극 또는 음극에 인접할 수 있는 지지체를 포함한다. 가장 빈번하게는, 지지체는 양극에 인접한다. 지지체는 가요성이거나 단단하고, 유기 또는 무기일 수 있다. 일반적으로, 유리 또는 가요성 유기 필름이 지지체로서 사용된다.
양극(110)은 양전하 운반체를 주입하거나 모으기에 특히 효율적인 전극이다. 이것은, 예를 들어 금속, 혼합 금속, 합금, 금속 산화물 또는 혼합 금속 산화물을 함유하는 물질로 이루어질 수 있거나, 또는 도전성 중합체일 수 있다. 적합한 금속으로는 원소 주기율표(현 IUPAC 형식)에 나타난 바와 같이 11족 금속, 4족, 5족 및 6족 금속, 및 8 내지 10족 전이금속이 있다. 양극이 광투과성이려면, 2족, 3족, 4족, 13족 및 14족 금속의 혼합 금속 산화물(예: 인듐-주석 산화물)이 사용된다. 폴리(3,4-에틸렌디옥시티오펜)(PEDOT) 및 폴리아닐린(PANI)과 같은 도전성 중합체는 전도성이 10-2S/㎝보다 클 때 사용될 수 있다. 양극과 음극중 하나 이상은 빛을 장치의 활성층 내로 또는 활성층 밖으로 통과시키도록 일부 이상 투과성이어야 한다.
무기 양극층은 일반적으로 물리증착 공정에 의해 적용될 수 있다. "물리증착"이란 용어는 진공중에서 수행되는 다양한 침착 방법을 가리킨다. 따라서, 예를 들어 물리증착은 이온 빔 스퍼터링(ion beam sputtering)을 포함한 모든 형태의 스퍼터링, 및 e-빔 증발과 같은 모든 형태의 증착을 포함한다. 유용한 특별한 형태의 물리증착은 고주파 마그네트론 스퍼터링이다. 도전성 중합체 양극층은 스핀-코팅(spin-coating), 주조 및 인쇄(예: 그라비어 인쇄, 잉크젯(ink jet) 인쇄 또는 열패턴화)를 포함한 임의의 통상의 수단을 사용하여 적용될 수 있다.
본 발명의 정공 수송 중합체는 분리층(120)으로서, 또는 층(130)내의 방출 물질과 함께 존재할 수 있다. 중합체 층은 전술한 바와 같은 임의의 통상의 적용 수단을 사용하여 적용될 수 있다. 중합체는 일반적으로 디메틸 술폭사이드, N-메틸 피롤리돈, 디메틸 포름아미드, 아세토니트릴, 프로필렌 카르보네이트, 프로필렌 글리콜 모노메틸 에테르, 디메틸 아세트아미드 및 테트라히드로푸란과 같은 유기 용매내 용액 또는 분산액으로서 적용된다. 용액 또는 분산액이 코팅되어 연속 막을 형성할 수 있다면, 용매내 중합체의 농도는 특별히 중요하지 않다. 일반적으로, 중합체 1 내지 5중량%를 갖는 용액 또는 분산액이 사용될 수 있다.
일부 경우에서, 다른 정공 수송 물질로부터 만들어진 추가의 정공 수송층(도시되지 않음)을 갖는 것이 바람직할 수 있다. 층에 적합한 다른 정공 수송 물질의 예는 왕(Y. Wang)의 문헌[Kirk-Othmer Encyclopedia of Chemical Technology, Fourth Edition, Vol. 18, p. 837-860, 1996]에 요약되어 있다. 정공 수송 분자 및 중합체 모두가 사용될 수 있다. 일반적으로 사용되는 정공 수송 분자는 N,N'-디페닐-N,N'-비스(3-메틸페닐)-[1,1'-비페닐]-4,4'-디아민(TPD); 1,1-비스[(디-4-톨릴아미노)페닐]시클로헥산(TAPC); N,N'-비스(4-메틸페닐)-N,N'-비스(4-에틸페닐)-[1,1'-(3,3'-디메틸)비페닐]-4,4'-디아민(ETPD); 테트라키스-(3-메틸페닐)-N,N,N',N'-2,5-페닐렌디아민(PDA); α-페닐-4-N,N-디페닐아미노스티렌(TPS); p-(디에틸아미노)벤즈알데하이드 디페닐히드라존(DEH); 트리페닐아민(TPA); 비스[4-(N,N-디에틸아미노)-2-메틸페닐](4-메틸페닐)메탄(MPMP); 1-페닐-3-[p-(디에틸아미노)스티릴]-5-[p-(디에틸아미노)페닐] 피라졸린(PPR 또는 DEASP); 1,2-트랜스-비스(9H-카르바졸-9-일)시클로부탄(DCZB); N,N,N',N'-테트라키스(4-메틸페닐)-(1,1'-비페닐)-4,4'-디아민(TTB); 및 포르피린산 화합물(예: 구리 프탈로시아닌)이다. 일반적으로 사용되는 정공 수송 중합체는 폴리비닐카르바졸(PVK) 및 (페닐메틸)폴리실란이다. 전도성이 10-2S/㎝ 미만일 경우, 폴리(3,4-에틸렌디옥시티오펜)(PEDOT) 및 폴리아닐린(PANI)과 같은 도전성 중합체가 사용될 수 있다. 상기 언급한 것과 같은 정공 수송 분자를 중합체(예: 폴리스티렌 및 폴리카르보네이트)내로 도핑(doping)함으로써 정공 수송 중합체를 얻는 것도 또한 가능하다.
많은 경우에서, 양극 및 정공 수송층은 패턴화된다. 패턴은 경우에 따라 변할 수 있는 것으로 이해된다. 층은, 예를 들어 제1 전기 접촉층 물질을 적용하기 전에 제1 가요성 복합 차단 구조상에 패턴화된 마스크 또는 포토레지스트를 위치시킴으로써 패턴으로 적용될 수 있다. 또 다르게는, 층은 전체 층으로서 적용된 후, 예를 들어 포토레지스트 및 습식 화학 에칭을 사용하여 패턴화될 수 있다. 상기논의된 바와 같이, 도전성 중합체 층도 또한 잉크젯(ink jet) 인쇄, 리쏘그래피(lithography), 스크린 인쇄 또는 열전사 패턴화에 의해 패턴으로 적용될 수 있다. 당업계에 널리 공지된 그밖의 패턴화 공정이 또한 사용될 수 있다.
장치(100)의 용도에 따라, 활성층(130)은 인가된 전압에 의해 활성화되는 발광층(예: 발광 다이오드 또는 조명 장치에서와 같이), 방사 에너지에 반응하여여 인가된 바이어스 전압이 있거나 없이 신호를 생성하는 물질 층(예: 광검파기에서와 같이), 또는 방사 에너지를 전기 에너지로 변환시키는 층(예: 광전지 또는 태양전지)일 수 있다. 전기 장치의 예로는 광전도 전지, 포토레지스터, 광스위치, 광트랜지스터 및 광전관, 및 광전지가 있고, 이들 용어는 마르쿠스(Markus, John)의 문헌[Electronics and Nucleonics Dictionary, 470 및 476(McGraw-Hill, Inc. 1966)]에 기술되어 있다.
활성층이 발광성인 경우, 층은 전기 접촉층에 충분한 바이어스 전압이 인가될 때 빛을 방출할 것이다. 발광 활성층은 임의의 유기 전계발광성 물질 또는 다른 유기 발광 물질을 함유할 수 있다. 이러한 물질은, 예를 들어 탕(Tang)의 미국 특허 제4,356,429호, 반 슬리케(Van Slyke) 등의 미국 특허 제4,539,507호(이들의 관련 부분은 본원에 참조로 인용됨)에 기술된 것과 같은 소분자 물질일 수 있다. 발광 물질은, 예를 들어 미국 특허출원 공개공보 US 2001/0019782호 및 PCT 특허출원 공개공보 WO 00/70655호 및 WO 01/41512호에 기술된 바와 같이 유기-금속 착체일 수 있다. 또 다르게는, 이러한 물질은 프렌드(Friend) 등의 미국 특허 제5,247,190호, 히거(Heeger) 등의 미국 특허 제5,408,109호, 나카노(Nakano) 등의미국 특허 제5,317,169호에 기술된 것과 같은 중합체 물질일 수 있다. 바람직한 전계발광성 물질은 반도전성 공액 중합체이다. 이러한 중합체의 예는 PPV로 불리는 폴리(p-페닐렌비닐렌)이다.
발광 물질은 단독 층을 형성할 수 있거나, 또는 다른 물질의 매트릭스에 분산될 수 있거나, 또는 본 발명의 정공 수송 중합체와 혼합될 수 있다. 전하 수송 물질의 농도는 전도 경로가 만들어질 수 있도록 약 15체적%의 퍼컬레이션(percolation) 한계치 이상이어야 한다. 물질의 밀도가 1에 가까울 경우, 퍼컬레이션 한계치에 도달한다면 15중량%가 조건에 맞다. 본 발명의 정공 수송 중합체는 일반적으로 발광층의 전체 중량을 기준으로 약 15 내지 99중량%, 바람직하게는 25 내지 80중량%의 양으로 존재한다.
활성 유기층은 일반적으로 두께가 50 내지 500㎚이다.
활성층이 광검파기에 도입되는 경우, 층은 방사 에너지에 반응하여 바이어스 전압이 있거나 없이 신호를 생성한다. 방사 에너지에 반응하고 바이어스 전압의 존재하에 신호를 생성할 수 있는 물질(예: 광전도 전지, 포토레지스터, 광스위치, 광트랜지스터 및 광전관의 경우에서)의 예로는 많은 공액 중합체 및 전계발광성 물질이 있다. 방사 에너지에 반응하고 바이어스 전압의 부재하에 신호를 생성할 수 있는 물질(예: 광전도 전지 또는 광전지의 경우에서)으로는 빛과 화학 반응하여 신호를 생성하는 물질이 있다. 이러한 감광성 화학 반응성 물질의 예로는 많은 공액 중합체, 및 전계발광 및 광자발광 물질이 있다. 구체적인 예로는 MEH-PPV(유(G. Yu), 파크바즈(K. Pakbaz) 및 히거(A. J. Heeger)의 문헌["Optocoupler made fromsemiconducting polymers",Journal of Electronic Materials, Vol. 23, pp. 925-928(1984)]); 및 CN-PPV와의 MEH-PPV 복합체(홀스(J. J. M. Halls) 등(캠브리지 그룹)의 문헌["Efficient Photodiodes from Interpenetrating Polymer Networks"Nature, Vol. 376, pp. 498-500, 1995])가 있으나, 이에 제한되지 않는다.
활성 유기 물질을 함유하는 활성층(130)은 스핀-코팅, 주조 및 인쇄를 포함한 임의의 통상의 수단에 의해 용액으로부터 적용될 수 있다. 활성 유기 물질은 물질의 성질에 의존하여, 증착 공정에 의해 직접 적용될 수 있다. 활성 중합체 전구체를 적용한 다음, 전형적으로는 가열에 의하여 중합체로 변환시키는 것도 가능하다.
음극(150)은 전자 또는 음전하 운반체를 주입하거나 모으기에 특히 효율적인 전극이다. 음극은 제1 전기 접촉층(이 경우에서 양극)보다 낮은 작업 기능을 갖는 임의의 금속 또는 비금속일 수 있다. 제2 전기 접촉층을 위한 물질은 1족의 알칼리 금속(예컨대, Li, Cs), 2족 (알칼리 토)금속, 12족 금속, 희토류, 란탄족 및 악틴족중에서 선택될 수 있다. 알루미늄, 인듐, 칼슘, 바륨 및 마그네슘, 및 이들의 혼합물과 같은 물질이 사용될 수 있다. Li-함유 유기금속 화합물이 또한 유기층과 음극층 사이에 침착되어 작동 전압을 낮출 수 있다.
음극층은 일반적으로 물리 증착 공정에 의해 적용된다. 일반적으로, 음극층은 양극층(110) 및 도전성 중합체층(120)에 대하여 상기 논의된 바와 같이 패턴화될 것이다. 유사한 가공 기법을 사용하여 음극층을 패턴화할 수 있다.
임의층(140)은 전자 수송을 용이하게 하고, 또한 층 계면에서의 반응 정지를방지하기 위하여 완충층 또는 구속층으로서 작용하는 기능을 할 수 있다. 바람직하게는, 이 층은 전자 이동성을 촉진하고 반응 정지를 감소시킨다. 임의층(140)을 위한 전자 수송 물질의 예로는 금속 킬레이트화된 옥시노이드 화합물(예: 트리스(8-히드록시퀴놀레이토)알루미늄(Alq3)); 플루오르-함유 치환체를 갖는 페닐-피리딘 리간드와의 시클로금속화된 이리듐 착체(예: 동시 계류중인 미국 특허출원 제09/879014호에 개시된 것); 페난트롤린계 화합물(예: 2,9-디메틸-4,7-디페닐-1,10-페난트롤린(DDPA) 또는 4,7-디페닐-1,10-페난트롤린(DPA)); 아졸 화합물(예: 2-(4-비페닐릴)-5-(4-t-부틸페닐)-1,3,4-옥사디아졸(PBD) 및 3-(4-비페닐릴)-4-페닐-5-(4-t-부틸페닐)-1,2,4-트리아졸(TAZ))이 있다.
임의층(140)은 또한 중합체 물질로 만들어질 수 있다. 그 예로는 폴리(플루오렌-옥사디아졸)(동시 계류중인 미국 특허출원 제09/546512호에 개시된 바와 같이), 및 일부 폴리페닐렌비닐렌 중합체(PPV)(예: 시아노-치환된 PPV)가 있다.
유기 전자 장치에 다른 층을 갖는 것은 공지되어 있다. 예를 들어, 층들의 양전하 수송 및(또는) 띠간격 정합을 촉진하거나 또는 보호층으로서 기능하기 위하여 전도성 중합체층(120)과 활성층(130) 사이에 층(도시되지 않음)이 있을 수 있다. 유사하게는, 활성층(130)과 음극층(150) 사이에, 층들 사이의 음전하 수송 및(또는) 띠간격 정합을 촉진하거나 또는 보호층으로서 기능하기 위한 추가의 층(도시되지 않음)이 있을 수 있다. 당업계에 공지된 층들이 사용될 수 있다. 또한, 임의의 전술된 층들은 둘 이상의 층으로 이루어질 수 있다. 또 다르게는, 무기 양극층(110), 전도성 중합체층(120), 활성층(130) 및 음극층(150)중 일부 또는 전부는 전하 운반체 수송 효율을 증가시키기 위하여 표면처리될 수 있다. 각각의 성분층을 위한 물질의 선택은 바람직하게는 장치를 제공하는 목적과 높은 장치 효율을 비교함으로써 결정된다.
장치는 적합한 기재위에 개별 층들을 순차적으로 침착함으로써 제조될 수 있다. 유리 및 중합체 막과 같은 기재가 사용될 수 있다. 대부분의 경우에서, 양극이 기재에 적용되고, 그 위에 층들이 적층된다. 그러나, 먼저 기재에 음극을 적용하고 역순으로 층들을 부가하는 것이 가능하다. 일반적으로, 상이한 층들은 다음과 같은 범위의 두께를 가질 것이다: 무기 양극(110), 500-5000Å, 바람직하게는 1000-2000Å; 임의의 정공 수송층(120), 50-2500Å, 바람직하게는 200 내지 2000Å; 광활성층(130), 10-1000Å, 바람직하게는 100-800Å; 임의의 전자 수송층(140), 50 내지 1000Å, 바람직하게는 200 내지 800Å; 음극(150), 200-10000Å, 바람직하게는 300-5000Å.
하기 실시예는 본 발명의 임의의 특징 및 이점을 설명한다. 이들은 본 발명을 설명하려는 것이지, 제한하려는 것이 아니다. 달리 나타내지 않는 한, 모든 비율은 중량 기준이다.
실시예 1 및 2
이들 실시예는 관능화된 중합체의 형성을 설명한다.
물질
CN-PPV는 폴리(페닐렌-비닐렌)의 시아노-유도체이다. 이것은 유(Gang Yu) 및 히거(Alan J. Heeger)의 문헌[J. Applied Physics 78, 4510(1995)]에 기술된 것과 유사하다.
그린(Green) PPV및 기타 PPV는 요한슨(D. M. Johansson), 스르다노브(G. Srdanov), 유, 틴더(M. Theander), 인가나스(O. Inganas) 및 앤더슨(M. R. Andersson)의 문헌["Synthesis and Characterization of Highly Soluble Phenyl-Substituted Poly(p-phenylenevinylene)",Macromolecules33, 2525(2000)]에 기술된 것과 유사한 폴리(페닐렌-비닐렌)의 유도체이다.
C60은 미국 플로리다주 소재의 버키 유에스에이 인코포레이티드(Bucky USA Inc.)사로부터 구입한 풀러렌 분자이다. PCBM[6,6]은 휴멜렌(J. C. Hummelen), 나이트(B. W. Knight), 레펙(F. Lepec) 및 우들(F. Wudl)의 문헌[J. Org. Chem.60, 532(1995)]에 공개된 과정을 따라 합성된, 관능성 측쇄를 갖는 풀러렌 유도체이다. 그의 물성에 대한 상세한 내용은 사리시프치(N. S. Sariciftci) 및 히거의 문헌[Intern. J. Mod. Phys.B8, 237(1994)]에서 찾을 수 있다.
PFO는 다음과 같이, 플루오렌-디카르복실산으로부터 제조된 폴리(플루오렌-옥사디아졸)이다:
9,9-디-(2-에틸헥실)-플루오렌-2,7-디카르복실산의 합성
500㎖들이 플라스크에 마그네슘 7g을 넣고, 무수 질소하에 100℃로 예열하였다. 요오드 5㎎을 첨가한 후, 무수 THF 100㎖내 2,7-디브로모-9,9-디-(2-에틸헥실)-플루오렌 50g의 용액(20㎖)의 제1 부분을 첨가하였다. 반응이 개시된 후(용액에서 색이 사라짐으로 알 수 있음), 나머지 용액을 주사기로 적가하였다. 적가 후, 반응 혼합물을 1시간동안 환류시키고, 추가의 무수 THF 100㎖를 첨가하였다. 그 다음, 반응 혼합물을 실온으로 냉각하였다. 반응 혼합물에 드라이아이스 500g을 첨가하고, 드라이아이스가 잘 혼합될 때까지 플라스크를 흔들어 주었다. 여분의 드라이아이스가 증발된 후, 잔류물에 18% 염산 800㎖를 첨가하였다. 산성화된 잔류물을 에틸 아세테이트로 3회 추출하였다(3×200㎖). 유기층을 합하여 물 400㎖로 세척한 다음, MgSO4상에서 건조시켰다. 용매를 증발시킨 후, 헥산 200㎖를 첨가하였다. 생성물은 백색 고체로서 침전되었고, 이를 여과에 의해 단리하였다. 메탄올로부터의 재결정화에 의해 추가 정제하여 백색 고체로서 생성물 25g을 얻었다. 생성물의 수율은 57%이었다.
양성자 NMR에 의해 하기 구조를 확인하였다:
1H-NMR(500㎒, THF-d8)δppm: 8.17(t, J=6.5㎐, 2H, 플루오렌 고리), 8.06(d, 2H, J=8㎐, 플루오렌 고리), 7.89(d, J=8㎐, 2H, 플루오렌 고리), 2.13(d, J=5㎐, 4H, H-알킬), 0.65-0.95(m, 22H, H-알킬), 0.45-0.54(m, 8H, H-알킬).
폴리(9,9-디-(2-에틸헥실)-플루오렌-옥사디아졸)의 합성
질소의 보호하에 110℃의 오일 가열욕중에서 교반하면서 메틸황산 500㎖에오산화인 3.0g을 용해시켰다. 이 용액에 9,9-디-(2-에틸헥실)-플루오렌-2,7-디카르복실산 2.0g 및 히드라진 염산염 286㎎의 혼합물을 첨가하였다. 현탁액을 5시간에 걸쳐 교반하여, 균질한 점성 용액이 형성되었다. 용액을 실온으로 냉각시킨 후, 용맥을 물 500㎖에 부었다. 중합체가 백색 섬유로서 침전되었고, 이를 여과에 의해 단리하였다. 조질의 중합체를 탄산나트륨 수용액에 이어서 물, 그 다음 메탄올에 의해 세척하고, 실온에서 진공 건조시켰다. 조질의 중합체를 THF 25㎖에 용해시켰다. 용액을 5㎛의 여과기를 통해 여과한 다음, 중합체를 물로부터 침전시켰다. 중합체를 단리하고, 물에 이어서 메탄올에 의해 세척하고, 실온에서 진공 건조시켰다. 이 정제 공정을 3회 반복하고, 중합체를 백색 섬유로서 얻었다. 이 생성물의 수득량은 1.5g(78%)이었다.
양성자 NMR에 의해 하기 구조를 확인하였다:
1H-NMR(500㎒, THF-d8)δppm: 8.42(s, 2H, 플루오렌 고리), 8.26(d, 2H, 플루오렌 고리), 8.13(d, J=8㎐, 2H, 플루오렌 고리), 2.2-2.5(br, 4H, H-알킬), 0.8-1.1(br, 16H, H-알킬), 0.59-0.65(br, 14H, H-알킬).
실시예 1
정공 수송을 위한 융합 방향족 화합물의 후속 결합에 사용되는 아민 관능화된 아크릴 공중합체는 하기 과정을 사용하여 제조되었다:
깨끗한 반응 용기에 다음을 첨가하였다:
단계 I | 양(g) |
이소부틸 메타크릴레이트(IBMA) | 21.81 |
2-(3급부틸아미노) 에틸 메타크릴레이트(IBAEMA) | 18.94 |
아세톤 | 250.25 |
생성된 용액을 환류 온도로 가열하고, 교반하면서 그 온도를 유지시켰다.
그 다음, 질소하에 미리 15분동안 혼합시킨, 하기 두 용액을 동시에 첨가하였다:
단계 II-용액(A) | 양(g) |
아세톤 | 176.63 |
바조(Vazo, 등록상표) 52 촉매2,2'-아조비스(2,4-디메틸펜탄 니트릴) | 14.78 |
단계 III-용액(B) | 양(g) |
이소부틸 메타크릴레이트(IBMA) | 196.24 |
2-(3급부틸아미노) 에틸 메타크릴레이트(IBAEMA) | 170.46 |
용액(A)을 90분에 걸쳐 54.8% 및 330분에 걸쳐 45.2%가 첨가되도록 공급하고, 용액(B)을 120분에 걸쳐 67% 및 120분에 걸쳐 33%가 첨가되도록 공급하였다. 공급이 완료된 후, 반응괴를 120분동안 교반하면서 환류 온도에서 유지시켰다. 질소 스윕(sweep)을 사용하여 대부분의 용매를 증발시킨 후, 중합체 용액의 일부(250g)를 진공 오븐에서 밤새 건조시켰다. IMBA/IBAEMA의 중합체 수율은 100%이었다.
실시예 2
정공 수송을 위한 융합 방향족 화합물의 후속 결합에 사용되는 히드록실 관능화된 아크릴 공중합체는 하기 과정을 사용하여 제조되었다:
깨끗한 반응 용기에 다음을 첨가하였다:
단계 I | 양(g) |
아세톤 | 600.0 |
생성된 용액을 환류 온도로 가열하고, 교반하면서 그 온도를 유지시켰다.
그 다음, 질소하에 미리 15분동안 혼합시킨, 하기 두 용액을 동시에 첨가하였다:
단계 II-용액(A) | 양(g) |
아세톤 | 176.63 |
바조 52 촉매 2,2'-아조비스(2,4-디메틸펜탄 니트릴) | 4.5 |
단계 3-용액(B) | 양(g) |
메틸 메타크릴레이트(MMA) | 540.0 |
2-히드록시에틸 메타크릴레이트(HEMA) | 180.0 |
용액(A) 및 용액(B)을 각각 330분 및 240분에 걸쳐 균일하게 공급하였다. 공급이 완료된 후, 반응괴를 60분동안 교반하면서 환류 온도에서 유지시켰다. 질소 스윕을 사용하여 대부분의 용매를 증발시킨 후, 중합체 용액의 일부(250g)를 진공 오븐에서 밤새 건조시켰다. HEMA/MMA의 중합체 수율은 100%이었다. 분자량은 GPC에 의해 측정하였다. 수평균(Mn) 및 중량평균 분자량은 각각 30,308 및 93,195이어서, 3.07의 다분산도(Pd)가 얻어졌다.
실시예 3 및 4
이들 실시예는 관능화된 중합체에 대한 융합 방향족 고리의 결합을 설명한다.
실시예 3
이 실시예는 실시예 2의 관능화된 중합체에 대한 나프틸 고리의 결합을 설명한다.
깨끗한, 오븐 건조된 반응 용기에 다음을 첨가하였다:
단계 1 | 양(g) |
실시예 2에서 얻은 HEMA/MMA 공중합체 | 20.0 |
무수 테트라히드로푸란(THF) | 444.5 |
중합체가 완전히 용해될 때까지 생성된 용액을 아르곤하에 실온에서 교반하였다.
그 다음, 하기 시약을 단일 분량으로 첨가하였다:
단계 2 | 양(g) |
1,1'-카르보닐디이미다졸(CDI) | 7.50 |
생성된 용액을 1시간동안 아르곤하에 실온에서 교반하였다.
그 다음, 하기 용액을 20분에 걸쳐 적가하였다:
단계 3 | 양(g) |
1-(1-나프틸)에틸아민 | 7.90 |
무수 테트라히드로푸란(THF) | 66.7 |
생성된 용액을 48시간동안 아르곤하에 실온에서 교반하였다. 그 다음, 용액을 그의 원래 체적의 1/3까지 진공 농축하였다. 농축된 용액을 큰 체적의 물(200㎖)에 붓고, 생성된 침전물을 여과에 의해 수획하였다. 조질의 중합체 생성물을 블렌더에서 물(200㎖)로 5회 추출한 다음, 48시간동안 50℃에서 진공하에 오븐 건조시켰다. 중합체 수율은 84중량%이었다.
중합체는 하기 화학식 I을 가짐을 특징으로 하였다:
<랜덤 공중합체: a=25몰%; b=75몰%>
1H-NMR(DMSO-d6)δ: 6.7-8.1(나프틸렌 측기의 방향족 양성자); 방향족 H:지방족 H의 비=0.20(이론치=0.19); 자외선-가시광선(UV-vis)(DMSO): λ최대=305㎚.
중합체 분자량은 비개질된 중합체와 매우 유사할 것이므로 측정하지 않았다.
실시예 4
이 실시예는 실시예 1의 관능화된 중합체에 대한 피렌 기의 결합을 설명한다.
깨끗한, 오븐 건조된 반응 용기에 다음을 첨가하였다:
단계 1 | 양(g) |
1-피렌카르복실산 | 2.25 |
염화 티오닐 | 90.2 |
생성된 용액을 2시간동안 가열 환류시켰다. 그 다음, 남아 있는 염화 티오닐을 증류에 의해 제거하여 조질의 황색 고체를 얻었다. 이 고체를 무수 헥산으로 반복하여 세척한 다음, 12시간동안 50℃에서 진공 건조시켰다. 1-피렌카르보닐 클로라이드의 수율은 95%이었다.
제2의 깨끗한, 오븐 건조된 반응 용기에 다음을 첨가하였다:
단계 2 | 양(g) |
실시예 1에서 얻은 IBMA/IBAEMA 공중합체 | 10.0 |
무수 테트라히드로푸란(THF) | 147.8 |
중합체가 완전히 용해될 때까지 중합체 용액을 아르곤하에 실온에서 교반하였다. 그 다음, 단계 1에서 제조된 생성물을 첨가하였다.
생성된 용액을 실온에서 12시간동안 아르곤하에 교반하였다. 용액을 추가로 개질하였다:
단계 3 | 양(g) |
트리에틸아민 | 2.93 |
생성된 용액을 5분동안 아르곤하에 교반하였다. 용액을 추가로 개질하였다:
단계 4 | 양(g) |
시클로헥사노일 클로라이드 | 2.26 |
생성된 용액을 12시간동안 아르곤하에 실온에서 교반하였다. 그 다음, 용액을 그의 원래 체적의 1/2까지 진공 농축하였다. 농축된 용액을 큰 체적의 물(300㎖)에 붓고, 생성된 침전물을 여과에 의해 수획하였다. 조질의 중합체 생성물을 블렌더에서 물(200㎖)로 5회 추출한 다음, 48시간동안 50℃에서 진공하에 오븐 건조시켰다. 중합체 수율은 79중량%이었다.
UV-vis(DMSO): λ최대=340㎚.
중합체 분자량은 비개질된 중합체와 매우 유사할 것이므로 측정하지 않았다.
실시예 5
이 실시예는 관능화된 단량체로부터 본 발명의 정공 수송 중합체의 제조를 설명한다.
정공 수송 물질로서 사용되는, 피렌 측기를 갖는 폴리아라미드를 다음과 같이 다단계 방식으로 제조하였다:
깨끗한, 오븐 건조된 반응 용기에 다음을 첨가하였다:
단계 1 | 양(g) |
1-피렌카르복실산 | 4.07 |
염화 티오닐 | 163.1 |
생성된 용액을 2시간동안 가열하여 환류시켰다. 그 다음, 잔여 염화 티오닐을 증류에 의해 제거하여 조질의 황색 고체를 얻었다. 고체를 무수 헥산으로 반복하여 세척한 다음, 50℃에서 12시간동안 진공 건조시켰다. 1-피렌카르보닐 클로라이드의 수율은 95%이었다.
1-피렌카르보닐 클로라이드를 추가로 개질하였다. 깨끗한, 오븐 건조된 반응 용기에 다음을 첨가하였다:
단계 2 | 양(g) |
5-아미노이소프탈산 | 3.03 |
N,N-디메틸아세트아미드(DMAC) | 93.7 |
생성된 용액을 아르곤하에 실온에서 교반하였다. 그 다음, 아르곤하에 5분동안 미리 혼합시킨 하기 용액을 15분에 걸쳐 적가하였다:
단계 3 | 양(g) |
1-피렌카르보닐 클로라이드 | 4.16 |
N,N-디메틸아세트아미드(DMAC) | 46.9 |
생성된 용액을 8시간동안 아르곤하에 실온에서 교반하였다. 그 다음, DMAC 용매를 진공 증류에 의해 제거하여 조질의 황갈색 고체를 얻었다. 이 고체를 메탄올로 2회 세척한 다음, 50℃에서 24시간동안 진공 건조시켰다. 생성물 수율은 92%이었다.
단계 3에서 단리한 생성물을 하기 화학식 II의 피렌 이산을 사용하여 추가로 개질하였다:
깨끗한, 오븐 건조된 반응 용액에 다음을 첨가하였다:
단계 4 | 양(g) |
화학식 I의 화합물 | 4.50 |
염화 티오닐 | 326.2 |
생성된 용액을 12시간동안 가열하여 환류시켰다. 그 다음, 잔여 염화 티오닐을 증류에 의해 제거하여 하기 화학식 III의 조질의 황색-녹색 고체를 얻었다:
이 고체를 무수 헥산으로 반복하여 세척한 다음, 50℃에서 12시간동안 진공 건조시켰다.
그 다음, 화학식 II의 피렌-이산 클로라이드를 사용하여 정공 수송 중합체를 제조하였다. 깨끗한, 오븐 건조된 반응 용기에 다음을 첨가하였다:
단계 5 | 양(g) |
화학식 II의 화합물 | 2.0 |
1,3-페닐렌디아민 | 0.47 |
N,N-디메틸아세트아미드(DMAC) | 37.5 |
생성된 용액을 12시간동안 아르곤하에 실온에서 교반하였다. 그 다음, 용액을 물에 부어 황색-황갈색 침전물을 얻었다. 이 침전물을 수획하여 메탄올로 추출하였다. 생성된 폴리아라미드를 50℃에서 48시간동안 진공 건조시켰다. 중합체 수율은 중량%이었다.
중합체는 하기 화학식 IV를 가짐을 특징으로 하였다:
1H-NMR(DMSO-d6)δ: 11.1-11.3(m, 1H); 10.6-10.7(s, 2H); 7.9-8.7(m, 16H). UV-vis(DMSO): λ최대=345㎚. 고유 점도(0.5중량%, H2SO4, 25℃)=0.61dL/g.
실시예 6 내지 12
이들 실시예는 2단자의 박막 장치에서 본 발명의 중합체의 용도를 설명한다.
실시예 6
무기 금속 또는 유기 도전성 중합체로 만들어진 두 도전성 전극 사이에 중합체 층을 위치시켰다. 다음과 같이 1조의 장치를 만들었다. 1000Å의 금층을 유기 기재상으로 열증발시켰다. 그 다음, 폴리(3,4-에틸렌디옥시티오펜)(PEDOT)의 도전성 층을 상부에 코팅하였다. Au/PEDOT 층은 이 장치의 양극(110)을 형성하였다. 0.45μpp의 필터를 통해 여과시킨 디메틸아세트아미드(DMAC)내 2% 용액으로부터 실시예 5의 중합체를 코팅하였다. 생성된 막의 두께는 텐코어(TENCOR) 500 표면 측정기에 의해 측정하였을 때 ~500Å이었다. 음극 전극은 약 3×10-6토르의 진공하에활성층의 위에 증착된, Ba(30Å)/Al(3000Å) 이층 구조이었다. 장치의 활성 면적은 2개의 전극에 의해 한정되고, 이 실험에서는 ~0.15㎠이었다. 키쓸리(Keithley) 236 쏘스-메저-유닛(Source-Measure-Unit)을 사용하여 건조 상자내에서 장치 성능을 시험하였다.
전류 대 전압(V) 특징은 도 2에 나타낸 바와 같다. 이 2단자 장치는 우수한 정류 효과를 나타내었다. 곡선(200)은 역방향 바이어스가 인가되었을 때의 전류를 도시하고, 곡선(210)은 순방향 바이어스가 인가되었을 때의 전류를 도시한다. 15V의 순방향 바이어스에서, 순방향 바이어스는 50㎃(330㎃/㎠)로서, -5V 바이어스하의 전류보다 5000배 컸다. 이러한 장치는 전기 스위치로서 사용될 수 있다. "ON(켜짐)" 상태가 14V 바이어스이고, "OFF(꺼짐)" 상태가 0 바이어스로 정해질 때, 스위치 비(Ion/Ioff)는 107보다 크다.
양극 전극으로서 Au, Pt, Ag, Ni, Cu, Se, 폴리아닐린(PANI), 및 폴리피롤을 사용하여 유사한 장치를 제조하였다. 유사한 결과가 관찰되었다. 음극 전극으로서 Ba, Li, Ce, Cs, Eu, Rb, Sm, Al, In, LiF/Al, BaO/Al 및 CsF/Al을 사용하여 유사한 장치를 제조하였고, 유사한 I-V 특징이 관찰되었다.
이 실시예는 본 발명에서 개시한 중합체를 사용하여 우수한 정류 효과를 갖는 2단자 박막 장치를 제작할 수 있음을 나타낸다. 이러한 장치를 고체 상태 전기 스위치로서 사용할 수 있다.
실시예 7
실시예 6에 주어진 것과 동일한 물질 및 유사한 과정을 사용하여 장치를 제작하였다. 이 경우에서, 음극 및 양극 전극을 섀도 마스크(shadow mask)로 패턴화되었다. 10×10의 다이오드 어레이(array)가 제작되었다. 각 화소의 피치(pitch) 크기는 0.3㎜이고, 두 접촉 전극의 폭에 의해 한정되었다. 각각의 화소의 I-V 특징을 분석하였고, 도 1에 나타낸 것과 유사한 행태가 관찰되었다.
이 실시예는 본 발명에서 개시된 중합체를 사용하여 마이크로스위치(microswitch) 어레이를 제작할 수 있음을 나타내었다.
실시예 8
실시예 6에 주어진 것과 유사한 과정을 사용하여 장치를 제작하였다. 이 경우에서, 활성 중합체는 실시예 3의 중합체이었다. 용매로서 THF를 사용하였다. I-V 특징은 실시예 6과 유사하였다. 장치 순방향 전류는 ~20V에서 330㎃/㎠에 도달하였다.
실시예 6 뿐만 아니라 이 실시예는 본 발명의 중합체를 2단자 스위치 장치의 활성층으로서 사용할 수 있음을 나타낸다.
실시예 9
실시예 6에 기술된 과정에 따라 박막 발광 장치를 제작하였다. 이들 장치에서, 투명 ITO 전극을 양극(도 1에 최상으로 나타낸 층(110))으로서 사용하였다. 폴리(비닐카르바졸) 층을 정공 수송층(도 1에 최상으로 나타낸 층(120))으로서 사용하였다. 이 층의 상부에, 실시예 4의 중합체를 EL 층(도 1에 최상으로 나타낸 층(130))으로서 적용하였다. 이것은 실시예 8에 기술된 것과 유사한 과정을 사용하여 THF 용액으로부터 스핀 코팅되었다. 생성된 막의 두께는 약 950Å이었다. 약 3×10-6토르의 진공하에 EL 층의 상부에 Ba 및 Al 층을 증착시켰다. Ba 및 Al 층의 두께는 각각 30Å 및 3000Å이었다. 교정된 Si 광다이오드 및 키쓸리 236 쏘스-메져-유닛을 사용하여 건조 상자내에서 장치 성능을 시험하였다.
도 3은 이 장치의 전류 대 전압("I-V")(곡선 230) 및 발광 대 전압("L-V")(곡선 240) 특징을 나타낸다. 순방향 바이어스에서 청색의 발광이 관찰되었다. 방출은 40V에서 ~50cd/㎡이었다. 외부 양자 효율은 넓은 전압 범위에서 0.2% ph/el이었다. EL 방출 스펙트럼은 방출이 실시예 4에 개시된 중합체에 의한 것임을 나타내었다(동일한 물질의 광발광 스펙트럼과 비교하여).
장치는 또한 ITO 및 PVK 층 사이에 PEDOT 층(~1000Å)을 갖는 유사한 형태로 제작되었다. 이들 장치의 성능 변수는 도 3에 나타낸 것과 유사하다.
이 실시예는 본 발명에서 개시된 중합체를 중합체 발광 장치의 발광 물질로서 사용할 수 있음을 나타내었다.
실시예 10
실시예 9에 기술된 과정에 따라 박막 발광 장치를 제작하였다. 이들 장치에서, ITO를 양극(층(110))으로서 사용하였다. 실시예 5의 중합체 층을 정공 수송층(120)으로서 사용하였다. 정공 수송층상에 ~1000Å의 폴리(플루오렌-옥사디아졸)(PFO)을 스핀-코팅하였다(층(130)). Ca/Al을 음극 전극(150)으로서 사용하였다. PFO의 청색 발광 특징은 ~1% ph/el의 외부 양자 효율로 관찰되었다. CIE 색상 좌표는 x=0.18, y=0.15로서, 색 표시 적용에 있어서 CIE가 권장하는 숫자에 가까왔다. 이들 장치는 낮은 바이어스 전압에서 작동될 수 있었다. 발광은 전형적으로 4볼트 이상에서 관찰되었고, ~8V에서 ~100cd/㎡에 도달하였고, 10V에서 103cd/㎡를 초과하였다.
층(130)으로서 알킬 측쇄를 갖는 폴리(페닐렌 비닐렌) 유도체를 사용하여 과정을 반복하였다. 4V보다 큰 전압에서 5 내지 10cd/A의 EL 효율로 녹색 발광이 관찰되었다.
층(130)으로서 알콕시 측쇄를 갖는 폴리(페닐렌 비닐렌) 유도체를 사용하여 과정을 반복하였다. 4V보다 큰 전압에서 2 내지 3cd/A의 EL 효율로 오렌지색-적색 발광이 관찰되었다.
이 실시예는 본 발명에서 개시된 중합체를 청색, 녹색 및 적색 발광 장치를 위한 정공 수송 물질로서 사용할 수 있음을 나타낸다. 이러한 장치는 자연색 발광 표시장치의 화소로서 사용할 수 있다.
비교예 A
정공 수송층(120)으로서 PVK(미국 위스콘신주 밀워키 소재의 시그마-알드리흐(Sigma-Aldrich)사)를 사용한 것을 제외하고, 실시예 10에 기술된 것과 동일한 과정에 따라 실험을 수행하였다. 실시예 10에 기술된 것(본 발명에서 개시된 정공 수송 중합체를 사용하여)과 유사한 결과가 관찰되었다.
실시예 10과 함께, 이 실시예는 본 발명에서 개시된 중합체를 청색, 녹색 및적색 발광 장치를 위한 정공 수송 물질로서 사용할 수 있음을 나타낸다. 이러한 장치는 자연색 발광 표시장치의 화소로서 사용할 수 있다.
실시예 11
실시예 5(100㎚)/Ba(3㎚)/Al(100㎚)의 ITO/중합체의 형태로 박막 장치를 제작하였다. 백색 등 조명하에 전류 전압 특징을 측정하였다. 광발전 효과는 UV 조명하에 관찰되었다. 개방회로 전압은 ~2V이었다. 336㎚에서의 광전 감도는 약 1㎃/와트이었다.
이 실시예는 본 발명에서 개시된 중합체를 자외선 검출을 위한 광검파기를 제작하는데 사용할 수 있음을 나타낸다.
실시예 12
실시예 3 및 5의 중합체, 및 유사한 광학 에너지 간격을 갖는 추가의 중합체 또는 분자를 함유하는 중합체 블렌드로 이루어진 활성층을 가짐을 제외하고, 실시예 11의 과정을 반복하였다. 이들 장치에 대하여 광반응을 측정하였다. 하기 표는 이 블렌드로부터 얻어진 스펙트럼 반응의 범위를 제공한다.
첨가제 | 스펙트럼 범위 |
PFO | 400㎚ |
그린 PPV 유도체 | 500㎚ |
CN-PPV | 600㎚ |
C60, PCBM[6,6] | 710㎚ |
이 실시예는 본 발명에서 개시된 중합체를 상이한 스펙트럼의 반응 범위를 갖는 광검파기의 제작을 위한 호스트(host) 물질로서 사용할 수 있음을 나타낸다. 근적외선 또는 적외선 스펙트럼 범위에 반응하는 블렌드도 또한 태양 전지와 같은에너지 전환 장치에 적합하다.
Claims (11)
- 하나 이상의 융합 방향족 고리 기를 포함하는 다수의 치환체가 연결된 중합체 주쇄를 포함하고, 트리아릴아민 기 및 카르바졸 기중에서 선택된 기를 함유하지 않는 정공 수송 중합체.
- 제1항에 있어서, 중합체 주쇄가 폴리아크릴레이트, 폴리메타크릴레이트, 폴리아라미드, 폴리스티렌, 폴리아릴렌, 폴리에스테르, 폴리비닐렌, 폴리비닐 에테르 및 폴리비닐 에스테르중에서 선택되는 정공 수송 중합체.
- 제1항에 있어서, 융합 방향족 고리 기가 나프틸, 안트라실, 페난트릴, 페날레닐, 플루오레닐, 피레닐, 테트라세닐 및 펜타세닐 기중에서 선택되는 정공 수송 중합체.
- 융합 방향족 고리 기를 포함하는 다수의 치환체가 연결된 중합체 주쇄를 포함하고 트리아릴아민 및 카르바졸 기중에서 선택된 기를 함유하지 않는 하나 이상의 정공 수송 중합체를 추가로 포함하는, 양극과 음극 사이에 활성층을 포함하는 유기 전자 장치.
- 제4항에 있어서, 정공 수송 중합체가 양극과 활성층 사이에 놓인 층에 존재하는 장치.
- 제4항에 있어서, 발광 장치인 장치.
- 제4항에 있어서, 광검파기인 장치.
- 제4항에 있어서, 광전지인 장치.
- 정공 수송 중합체가 융합 방향족 고리 기를 포함하는 다수의 치환체가 연결된 중합체 주쇄를 포함하고, 이때 중합체가 트리아릴아민 및 카르바졸 기중에서 선택되는 기를 함유하지 않는, 제1 도전층, 정공 수송 중합체, 제2 도전층을 포함하는 2단자 전기 스위치.
- 제9항에 있어서, 중합체 주쇄가 폴리아크릴레이트, 폴리메타크릴레이트, 폴리아라미드, 폴리스티렌, 폴리아릴렌, 폴리에스테르, 폴리비닐렌, 폴리비닐 에테르 및 폴리비닐 에스테르중에서 선택되는 전기 스위치.
- 제9항에 있어서, 융합 방향족 고리 기가 나프틸, 안트라실, 페난트릴, 페날레닐, 플루오레닐, 피레닐, 테트라세닐 및 펜타세닐 기중에서 선택되는 전기 스위치.