KR102210135B1 - 용접 구조 부재용 고강도 도금 강판 및 이의 제조법 - Google Patents

용접 구조 부재용 고강도 도금 강판 및 이의 제조법 Download PDF

Info

Publication number
KR102210135B1
KR102210135B1 KR1020157030683A KR20157030683A KR102210135B1 KR 102210135 B1 KR102210135 B1 KR 102210135B1 KR 1020157030683 A KR1020157030683 A KR 1020157030683A KR 20157030683 A KR20157030683 A KR 20157030683A KR 102210135 B1 KR102210135 B1 KR 102210135B1
Authority
KR
South Korea
Prior art keywords
welding
steel sheet
less
phase
plated steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
KR1020157030683A
Other languages
English (en)
Korean (ko)
Other versions
KR20150133838A (ko
Inventor
겐타로 히라타
유키오 가타기리
시게루 모리카와
마사아키 우라나카
Original Assignee
닛테츠 닛신 세이코 가부시키가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 닛테츠 닛신 세이코 가부시키가이샤 filed Critical 닛테츠 닛신 세이코 가부시키가이샤
Publication of KR20150133838A publication Critical patent/KR20150133838A/ko
Application granted granted Critical
Publication of KR102210135B1 publication Critical patent/KR102210135B1/ko
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment 
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C22C18/04—Alloys based on zinc with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Organic Chemistry (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
KR1020157030683A 2013-03-26 2014-03-13 용접 구조 부재용 고강도 도금 강판 및 이의 제조법 Active KR102210135B1 (ko)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JPJP-P-2013-064370 2013-03-26
JP2013064370A JP6049516B2 (ja) 2013-03-26 2013-03-26 溶接構造部材用高強度めっき鋼板およびその製造法
PCT/JP2014/056620 WO2014156671A1 (ja) 2013-03-26 2014-03-13 溶接構造部材用高強度めっき鋼板およびその製造法

Publications (2)

Publication Number Publication Date
KR20150133838A KR20150133838A (ko) 2015-11-30
KR102210135B1 true KR102210135B1 (ko) 2021-02-01

Family

ID=51623654

Family Applications (1)

Application Number Title Priority Date Filing Date
KR1020157030683A Active KR102210135B1 (ko) 2013-03-26 2014-03-13 용접 구조 부재용 고강도 도금 강판 및 이의 제조법

Country Status (10)

Country Link
US (2) US10100395B2 (https=)
EP (1) EP2980237A4 (https=)
JP (1) JP6049516B2 (https=)
KR (1) KR102210135B1 (https=)
CN (1) CN105121681B (https=)
CA (1) CA2905623A1 (https=)
MX (1) MX2015013538A (https=)
MY (1) MY171301A (https=)
TW (1) TWI618816B (https=)
WO (1) WO2014156671A1 (https=)

Families Citing this family (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102075182B1 (ko) 2015-12-24 2020-02-10 주식회사 포스코 도금성이 우수한 고강도 용융 아연계 도금 강재 및 그 제조방법
JP2017115205A (ja) * 2015-12-24 2017-06-29 日新製鋼株式会社 めっき密着性に優れた溶融Ｚｎ−Ａｌ−Ｍｇ合金めっき鋼板の製造方法
JP2017145441A (ja) * 2016-02-16 2017-08-24 日新製鋼株式会社 黒色表面被覆高強度鋼板およびその製造方法
WO2017169939A1 (ja) * 2016-03-31 2017-10-05 Ｊｆｅスチール株式会社 薄鋼板およびめっき鋼板、並びに、熱延鋼板の製造方法、冷延フルハード鋼板の製造方法、熱処理板の製造方法、薄鋼板の製造方法およびめっき鋼板の製造方法
KR101858853B1 (ko) * 2016-12-19 2018-06-28 주식회사 포스코 용접성이 우수한 전봉강관용 열연강판 및 이의 제조방법
JP6816550B2 (ja) * 2017-02-17 2021-01-20 日本製鉄株式会社 曲げ加工性に優れた黒色表面被覆高強度溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板及びその製造方法
CN113366126B (zh) * 2019-01-29 2023-09-22 杰富意钢铁株式会社 高强度钢板及其制造方法
JP7288184B2 (ja) 2019-03-22 2023-06-07 日本製鉄株式会社 溶融Ｚｎ－Ａｌ－Ｍｇ系めっき鋼板の製造方法
JP7059979B2 (ja) * 2019-04-25 2022-04-26 Ｊｆｅスチール株式会社 スポット溶接部材
JP2021042419A (ja) * 2019-09-10 2021-03-18 日本電産株式会社 亜鉛合金及びその製造方法
UA127573C2 (uk) * 2019-12-18 2023-10-11 Арселорміттал Холоднокатаний і відпалений сталевий лист і спосіб його виготовлення
MX2022009482A (es) * 2020-02-13 2022-08-22 Nippon Steel Corp Componente de union y metodo de fabricacion del mismo.
KR102451005B1 (ko) * 2020-10-23 2022-10-07 주식회사 포스코 열적 안정성이 우수한 고강도 강판 및 이의 제조방법
CN113388796B (zh) * 2021-08-16 2021-11-02 天津市新宇彩板有限公司 钢材表面热镀锌铝镁镀液及使用该镀液的镀覆方法
WO2023181429A1 (ja) * 2022-03-24 2023-09-28 Ｊｆｅ鋼板株式会社 溶融Ａｌ－Ｚｎ系めっき鋼板及びその製造方法
KR102818628B1 (ko) * 2023-01-18 2025-06-10 주식회사 포스코 가스 실드 아크 용접용 와이어
WO2024154855A1 (ko) * 2023-01-20 2024-07-25 주식회사 포스코 가스 실드 아크 용접 금속
KR102887144B1 (ko) * 2023-01-20 2025-11-17 주식회사 포스코 가스 실드 아크 용접 금속
CN121046729B (zh) * 2025-11-04 2026-02-24 鞍钢股份有限公司 一种应变时效性能良好的高强耐蚀海工钢板及其制造方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010235989A (ja) * 2009-03-30 2010-10-21 Nisshin Steel Co Ltd 耐溶融金属脆化特性に優れた高強度Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板およびその製造方法
JP2011132602A (ja) * 2009-11-30 2011-07-07 Nippon Steel Corp 高強度冷延鋼板、高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板
JP2011153361A (ja) * 2010-01-28 2011-08-11 Nisshin Steel Co Ltd 曲げ性および耐溶融金属脆化特性に優れた高強度Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板
WO2012026419A1 (ja) 2010-08-23 2012-03-01 住友金属工業株式会社 冷延鋼板およびその製造方法
JP2012193452A (ja) * 2011-02-28 2012-10-11 Nisshin Steel Co Ltd 溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板および製造方法

Family Cites Families (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4085583B2 (ja) * 2001-02-27 2008-05-14 Ｊｆｅスチール株式会社 高強度冷延溶融亜鉛メッキ鋼板およびその製造方法
US6677058B1 (en) * 2002-07-31 2004-01-13 Nisshin Steel Co., Ltd. Hot-dip Zn plated steel sheet excellent in luster-retaining property and method of producing the same
JP2004315848A (ja) * 2003-02-27 2004-11-11 Nisshin Steel Co Ltd 溶融金属脆化による溶接加工割れのないＺｎ−Ａｌ−Ｍｇ系溶融めっき鋼板
JP2006307260A (ja) * 2005-04-27 2006-11-09 Toyo Kohan Co Ltd プラズマディスプレイ固定板用鋼板、プラズマディスプレイ固定用鋼板の製造方法及びプラズマディスプレイ固定板
JP4665692B2 (ja) * 2005-09-29 2011-04-06 Ｊｆｅスチール株式会社 曲げ剛性に優れた高強度薄鋼板およびその製造方法
JP4542515B2 (ja) 2006-03-01 2010-09-15 新日本製鐵株式会社 成形性と溶接性に優れた高強度冷延鋼板、高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板、並びに、高強度冷延鋼板の製造方法、高強度溶融亜鉛めっき鋼板の製造方法、高強度合金化溶融亜鉛めっき鋼板の製造方法
JP5082432B2 (ja) * 2006-12-26 2012-11-28 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法
JP4692519B2 (ja) * 2007-06-11 2011-06-01 Ｊｆｅスチール株式会社 高強度溶融亜鉛メッキ鋼板およびその製造方法
JP4377955B2 (ja) * 2007-12-27 2009-12-02 新日本製鐵株式会社 亜鉛めっき鋼板溶接用ステンレス鋼フラックス入り溶接ワイヤおよびこれを用いた亜鉛めっき鋼板のアーク溶接方法
JP5194841B2 (ja) * 2008-01-31 2013-05-08 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5264234B2 (ja) 2008-03-24 2013-08-14 日新製鋼株式会社 耐溶融金属脆化割れ性に優れたＺｎ−Ａｌ−Ｍｇ系めっき鋼板およびその製造方法
JP5320798B2 (ja) * 2008-04-10 2013-10-23 新日鐵住金株式会社 時効性劣化が極めて少なく優れた焼付け硬化性を有する高強度鋼板とその製造方法
KR20160136468A (ko) * 2009-03-10 2016-11-29 닛신 세이코 가부시키가이샤 내용융금속취화균열성이 우수한 아연계 합금 도금 강재

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010235989A (ja) * 2009-03-30 2010-10-21 Nisshin Steel Co Ltd 耐溶融金属脆化特性に優れた高強度Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板およびその製造方法
JP2011132602A (ja) * 2009-11-30 2011-07-07 Nippon Steel Corp 高強度冷延鋼板、高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板
JP2011153361A (ja) * 2010-01-28 2011-08-11 Nisshin Steel Co Ltd 曲げ性および耐溶融金属脆化特性に優れた高強度Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板
WO2012026419A1 (ja) 2010-08-23 2012-03-01 住友金属工業株式会社 冷延鋼板およびその製造方法
JP2012193452A (ja) * 2011-02-28 2012-10-11 Nisshin Steel Co Ltd 溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板および製造方法

Also Published As

Publication number Publication date
JP6049516B2 (ja) 2016-12-21
US20160032438A1 (en) 2016-02-04
EP2980237A4 (en) 2016-11-30
MY171301A (en) 2019-10-08
MX2015013538A (es) 2016-02-05
EP2980237A1 (en) 2016-02-03
KR20150133838A (ko) 2015-11-30
US20190010596A1 (en) 2019-01-10
JP2014189812A (ja) 2014-10-06
TWI618816B (zh) 2018-03-21
CN105121681B (zh) 2017-04-26
TW201443280A (zh) 2014-11-16
CA2905623A1 (en) 2014-10-02
WO2014156671A1 (ja) 2014-10-02
CN105121681A (zh) 2015-12-02
US10100395B2 (en) 2018-10-16

Similar Documents

Publication Publication Date Title
KR102210135B1 (ko) 용접 구조 부재용 고강도 도금 강판 및 이의 제조법
JP6777173B2 (ja) スポット溶接用高強度亜鉛めっき鋼板
CN111433380B (zh) 高强度镀锌钢板及其制造方法
US10526676B2 (en) High-strength steel sheet and method for producing the same
JP4791992B2 (ja) スポット溶接用合金化溶融亜鉛めっき鋼板の製造方法
KR102099588B1 (ko) 용융 Ｚｎ-Ａｌ-Ｍｇ계 도금 강판 및 제조방법
CN109790592B (zh) 钢铁零件及其制造方法和钢铁零件用的钢板
WO2019189842A1 (ja) 高強度亜鉛めっき鋼板、高強度部材およびそれらの製造方法
WO2016199922A1 (ja) 合金化溶融亜鉛めっき鋼板およびその製造方法
KR20190022769A (ko) 박강판 및 그의 제조 방법
KR20160101095A (ko) 고강도 용융 아연 도금 강판 및 그의 제조 방법
JP5641741B2 (ja) 曲げ性および耐溶融金属脆化特性に優れた高強度Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板
JPWO2018038045A1 (ja) 抵抗溶接部を有する自動車用部材
EP4316718B1 (en) AUTOMOTIVE COMPONENT AND RESISTANCE SPOT WELDING PROCESS FOR IT
JP6950826B2 (ja) 高強度鋼板、熱延鋼板の製造方法、冷延フルハード鋼板の製造方法および高強度鋼板の製造方法
CN102369303A (zh) 耐熔融金属脆化裂纹性优异的锌系合金镀敷钢材
KR102747858B1 (ko) 접합 부품 및 그 제조 방법
KR20060047587A (ko) 스폿 용접성 및 재질안정성이 우수한 고강도용융아연도금강판
JP5264234B2 (ja) 耐溶融金属脆化割れ性に優れたＺｎ−Ａｌ−Ｍｇ系めっき鋼板およびその製造方法
WO2018062342A1 (ja) 高強度めっき鋼板及びその製造方法
KR20240007934A (ko) 고강도 아연 도금 강판 및 부재 그리고 그들의 제조 방법
JP2010235989A (ja) 耐溶融金属脆化特性に優れた高強度Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板およびその製造方法
JP7722606B1 (ja) 鋼板、抵抗スポット溶接方法、抵抗スポット溶接部材、および鋼板の製造方法

Legal Events

Date Code Title Description
PA0105 International application

Patent event date: 20151023

Patent event code: PA01051R01D

Comment text: International Patent Application

PG1501 Laying open of application
A201 Request for examination
PA0201 Request for examination

Patent event code: PA02012R01D

Patent event date: 20181029

Comment text: Request for Examination of Application

E902 Notification of reason for refusal
PE0902 Notice of grounds for rejection

Comment text: Notification of reason for refusal

Patent event date: 20191119

Patent event code: PE09021S01D

E902 Notification of reason for refusal
PE0902 Notice of grounds for rejection

Comment text: Notification of reason for refusal

Patent event date: 20200513

Patent event code: PE09021S01D

E701 Decision to grant or registration of patent right
PE0701 Decision of registration

Patent event code: PE07011S01D

Comment text: Decision to Grant Registration

Patent event date: 20201023

GRNT Written decision to grant
PR0701 Registration of establishment

Comment text: Registration of Establishment

Patent event date: 20210126

Patent event code: PR07011E01D

PR1002 Payment of registration fee

Payment date: 20210127

End annual number: 3

Start annual number: 1

PG1601 Publication of registration
PR1001 Payment of annual fee

Payment date: 20240119

Start annual number: 4

End annual number: 4