KR101974182B1 - 열간 프레스용 도금 강판 및 도금 강판의 열간 프레스 방법 - Google Patents

열간 프레스용 도금 강판 및 도금 강판의 열간 프레스 방법 Download PDF

Info

Publication number
KR101974182B1
KR101974182B1 KR1020167017057A KR20167017057A KR101974182B1 KR 101974182 B1 KR101974182 B1 KR 101974182B1 KR 1020167017057 A KR1020167017057 A KR 1020167017057A KR 20167017057 A KR20167017057 A KR 20167017057A KR 101974182 B1 KR101974182 B1 KR 101974182B1
Authority
KR
South Korea
Prior art keywords
steel sheet
hot
compound
coated steel
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
KR1020167017057A
Other languages
English (en)
Korean (ko)
Other versions
KR20160078521A (ko
Inventor
신타로 야마나카
준 마키
마사오 구로사키
가즈히사 구스미
Original Assignee
닛폰세이테츠 가부시키가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 닛폰세이테츠 가부시키가이샤 filed Critical 닛폰세이테츠 가부시키가이샤
Publication of KR20160078521A publication Critical patent/KR20160078521A/ko
Application granted granted Critical
Publication of KR101974182B1 publication Critical patent/KR101974182B1/ko
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D22/00—Shaping without cutting, by stamping, spinning, or deep-drawing
    • B21D22/02—Stamping using rigid devices or tools
    • B21D22/022—Stamping using rigid devices or tools by heating the blank or stamping associated with heat treatment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D—WORKING OR PROCESSING OF SHEET METAL OR METAL TUBES, RODS OR PROFILES WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21D22/00—Shaping without cutting, by stamping, spinning, or deep-drawing
    • B21D22/20—Deep-drawing
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/12—Aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/14—Removing excess of molten coatings; Controlling or regulating the coating thickness
    • C23C2/16—Removing excess of molten coatings; Controlling or regulating the coating thickness using fluids under pressure, e.g. air knives
    • C23C2/18—Removing excess of molten coatings from elongated material
    • C23C2/20—Strips; Plates
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/265—After-treatment by applying solid particles to the molten coating
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/60—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using alkaline aqueous solutions with pH greater than 8
    • C23C22/66—Treatment of aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/68—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous solutions with pH between 6 and 8
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
    • C23C28/32—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer
    • C23C28/322—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer only coatings of metal elements only
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
    • C23C28/34—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/62—Quenching devices
    • C21D1/673—Quenching devices for die quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y10T428/12556—Organic component
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y10T428/12556—Organic component
    • Y10T428/12569—Synthetic resin
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y10T428/12611—Oxide-containing component

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Inorganic Chemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Coating With Molten Metal (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
  • Chemical Treatment Of Metals (AREA)
  • Laminated Bodies (AREA)
  • Heat Treatment Of Articles (AREA)
  • Shaping Metal By Deep-Drawing, Or The Like (AREA)
KR1020167017057A 2012-02-14 2013-02-08 열간 프레스용 도금 강판 및 도금 강판의 열간 프레스 방법 Active KR101974182B1 (ko)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2012029396 2012-02-14
JPJP-P-2012-029396 2012-02-14
PCT/JP2013/053070 WO2013122004A1 (ja) 2012-02-14 2013-02-08 熱間プレス用めっき鋼板及びめっき鋼板の熱間プレス方法

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
KR1020147022750A Division KR20140119738A (ko) 2012-02-14 2013-02-08 열간 프레스용 도금 강판 및 도금 강판의 열간 프레스 방법

Publications (2)

Publication Number Publication Date
KR20160078521A KR20160078521A (ko) 2016-07-04
KR101974182B1 true KR101974182B1 (ko) 2019-04-30

Family

ID=48984116

Family Applications (2)

Application Number Title Priority Date Filing Date
KR1020167017057A Active KR101974182B1 (ko) 2012-02-14 2013-02-08 열간 프레스용 도금 강판 및 도금 강판의 열간 프레스 방법
KR1020147022750A Ceased KR20140119738A (ko) 2012-02-14 2013-02-08 열간 프레스용 도금 강판 및 도금 강판의 열간 프레스 방법

Family Applications After (1)

Application Number Title Priority Date Filing Date
KR1020147022750A Ceased KR20140119738A (ko) 2012-02-14 2013-02-08 열간 프레스용 도금 강판 및 도금 강판의 열간 프레스 방법

Country Status (15)

Country Link
US (1) US10092938B2 (enExample)
EP (1) EP2816139B1 (enExample)
JP (3) JP5582254B2 (enExample)
KR (2) KR101974182B1 (enExample)
CN (1) CN104093880B (enExample)
BR (1) BR112014019984B1 (enExample)
CA (1) CA2864392C (enExample)
ES (1) ES2765101T3 (enExample)
IN (1) IN2014DN06844A (enExample)
MX (2) MX365687B (enExample)
PL (1) PL2816139T3 (enExample)
RU (1) RU2584105C2 (enExample)
TW (1) TWI470118B (enExample)
WO (1) WO2013122004A1 (enExample)
ZA (1) ZA201405948B (enExample)

Families Citing this family (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101974182B1 (ko) * 2012-02-14 2019-04-30 닛폰세이테츠 가부시키가이샤 열간 프레스용 도금 강판 및 도금 강판의 열간 프레스 방법
CA2940304C (en) * 2012-04-18 2018-11-27 Nippon Steel & Sumitomo Metal Corporation Al-plated steel sheet, method for hot-pressing al-plated steel sheet, and automotive part
BR112016012467B1 (pt) * 2013-12-12 2020-12-29 Nippon Steel Corporation chapa de aço chapeada de alumínio usada para prensagem a quente e método para fabricação da mesma
CN105090222B (zh) * 2014-12-31 2017-06-20 铜陵爱阀科技有限公司 一种高碳钢、不锈钢复合型精密垫片的制作方法
WO2016132165A1 (fr) * 2015-02-19 2016-08-25 Arcelormittal Procede de fabrication d'une piece phosphatable a partir d'une tole revetue d'un revetement a base d'aluminium et d'un revetement de zinc
WO2017017485A1 (en) * 2015-07-30 2017-02-02 Arcelormittal A method for the manufacture of a phosphatable part starting from a steel sheet coated with a metallic coating based on aluminium
WO2017017483A1 (en) 2015-07-30 2017-02-02 Arcelormittal Steel sheet coated with a metallic coating based on aluminum
WO2017017484A1 (en) 2015-07-30 2017-02-02 Arcelormittal Method for the manufacture of a hardened part which does not have lme issues
CN106148830A (zh) * 2016-08-10 2016-11-23 安徽禹王铸业有限公司 货运列车专用铁轨
EP3564409A4 (en) 2016-12-28 2020-01-01 Nippon Steel Corporation PLATED STEEL SHEET FOR HOT PRESSING, METHOD FOR PRODUCING A PLATED STEEL SHEET FOR HOT PRESSING, METHOD FOR PRODUCING A HESSPRESS SHAPED ARTICLE AND METHOD FOR PRODUCING A VEHICLE
JP6424989B1 (ja) * 2017-03-27 2018-11-21 新日鐵住金株式会社 Ａｌ系めっき鋼板
US20200238357A1 (en) * 2017-09-28 2020-07-30 Nippon Steel Corporation Coated steel sheet, coated steel sheet coil, method of producing hot-press formed article, and automobile part
WO2019073274A1 (en) 2017-10-12 2019-04-18 Arcelormittal PROCESS FOR PROCESSING METAL SHEET AND METAL SHEET TREATED USING THE SAME
WO2019073273A1 (en) 2017-10-12 2019-04-18 Arcelormittal PROCESS FOR PROCESSING METAL SHEET AND METAL SHEET TREATED WITH THIS METHOD
EP4186611B1 (en) 2018-04-13 2024-05-29 Nippon Steel Corporation Production method for hot press molded articles, press molded article, die mold, and mold set
CN112236243B (zh) * 2018-07-04 2023-04-04 日本制铁株式会社 热压成型品的制造方法、压制成型品、冲模模具及模具套件
JP6648874B1 (ja) 2018-07-04 2020-02-14 日本製鉄株式会社 熱間プレス成形品の製造方法、プレス成形品、ダイ金型、及び金型セット
CN111434402A (zh) * 2019-07-30 2020-07-21 苏州普热斯勒先进成型技术有限公司 表面具有含锰涂层的热冲压件的制造方法
MX2022014404A (es) 2020-05-18 2022-12-07 Nippon Steel Corp Material de acero estampado en caliente enchapado con al.
CN115874132A (zh) * 2021-09-26 2023-03-31 上海梅山钢铁股份有限公司 长点焊寿命高耐蚀性能的冷轧热镀铝锌钢板及其制造方法
CN116949439B (zh) 2022-04-15 2025-09-09 宝山钢铁股份有限公司 热冲压用镀层钢板及其所用的水性表面处理液
CN119194330A (zh) * 2024-10-18 2024-12-27 首钢集团有限公司 一种镀铝钢板及其制备方法和应用

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001220690A (ja) * 2000-02-01 2001-08-14 Nippon Steel Corp 自動車用Ａｌ系めっき鋼板
JP2007302982A (ja) * 2006-05-15 2007-11-22 Nippon Steel Corp 昇温特性、加工性、塗装後耐食性に優れたホットプレス用Ａｌめっき鋼材
WO2010089273A1 (de) * 2009-02-06 2010-08-12 Thyssenkrupp Steel Europe Ag Verfahren zum herstellen eines beschichteten stahlbauteils durch warmformen und durch warmformen hergestelltes stahlbauteil

Family Cites Families (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4707415A (en) 1985-03-30 1987-11-17 Sumitomo Metal Industries, Ltd. Steel strips with corrosion resistant surface layers having good appearance
DE68917332T2 (de) * 1988-02-19 1994-12-08 Nippon Steel Corp Verwendung eines Zink oder Zinklegierung-plattierten Stahlblechs mit ausgezeichneten Punktschweisseigenschaften.
US5525431A (en) * 1989-12-12 1996-06-11 Nippon Steel Corporation Zinc-base galvanized sheet steel excellent in press-formability, phosphatability, etc. and process for producing the same
FR2780984B1 (fr) 1998-07-09 2001-06-22 Lorraine Laminage Tole d'acier laminee a chaud et a froid revetue et comportant une tres haute resistance apres traitement thermique
JP3346338B2 (ja) * 1999-05-18 2002-11-18 住友金属工業株式会社 亜鉛系めっき鋼板およびその製造方法
CA2352158C (en) * 1999-10-08 2010-09-21 Kawasaki Steel Corporation Steel sheet having surface-treated zinc-based plating
JP2001214280A (ja) * 2000-01-28 2001-08-07 Nippon Steel Corp 潤滑性に優れたＣｒを使用しない皮膜を被覆するＳｎ系，Ａｌ系めっき鋼板
JP3749487B2 (ja) * 2002-01-18 2006-03-01 Ｊｆｅスチール株式会社 加工性と加工部耐食性に優れた表面処理鋼板及びその製造方法
KR20070119096A (ko) * 2001-06-15 2007-12-18 신닛뽄세이테쯔 카부시키카이샤 고강도 알루미늄계 합금 도금 강판
WO2003035280A2 (de) * 2001-10-22 2003-05-01 Henkel Kommanditgesellschaft Auf Aktien Oberflächenbeschichtete al/zn-stahlbleche und oberflächenbeschichtungsmittel
JP3582511B2 (ja) 2001-10-23 2004-10-27 住友金属工業株式会社 熱間プレス成形用表面処理鋼とその製造方法
FR2843130B1 (fr) * 2002-08-05 2004-10-29 Usinor Procede de revetement de la surface d'un materiau metallique, dispositif pour sa mise en oeuvre et produit ainsi obtenu
JP4167046B2 (ja) * 2002-11-29 2008-10-15 日本パーカライジング株式会社 金属表面処理剤、金属表面処理方法及び表面処理金属材料
JP2004211151A (ja) 2002-12-27 2004-07-29 Nippon Steel Corp 潤滑性に優れた高温プレス成形性用Ａｌ系めっき鋼板
JP2005048200A (ja) 2003-07-29 2005-02-24 Jfe Steel Kk 耐食性および皮膜外観に優れる表面処理鋼板
JP4447270B2 (ja) 2003-08-29 2010-04-07 豊田鉄工株式会社 熱間プレス用めっき鋼板の加熱処理方法
JP2007231375A (ja) * 2006-03-01 2007-09-13 Jfe Steel Kk 合金化溶融亜鉛めっき鋼板
JP4919427B2 (ja) * 2006-10-03 2012-04-18 日新製鋼株式会社 溶融めっき鋼板の温間加工方法
JP2008189965A (ja) 2007-02-02 2008-08-21 Nisshin Steel Co Ltd 塗装鋼板
JP4616854B2 (ja) 2007-03-13 2011-01-19 新日本製鐵株式会社 熱間プレス用Ａｌめっき鋼板
JP5071065B2 (ja) 2007-11-22 2012-11-14 Ｊｆｅスチール株式会社 合金化溶融亜鉛めっき鋼板の製造方法および合金化溶融亜鉛めっき鋼板
JP4590025B2 (ja) * 2008-04-22 2010-12-01 新日本製鐵株式会社 めっき鋼板及びめっき鋼板の熱間プレス方法
JP4616900B2 (ja) * 2008-05-27 2011-01-19 新日本製鐵株式会社 塗装後耐食性に優れた高強度自動車部品
JP4724780B2 (ja) * 2008-07-11 2011-07-13 新日本製鐵株式会社 急速加熱ホットプレス用アルミめっき鋼板、その製造方法、及びこれを用いた急速加熱ホットプレス方法
JP5353105B2 (ja) 2008-07-31 2013-11-27 新日鐵住金株式会社 熱処理用鋼材の表面処理液および熱処理用鋼材の製造方法
JP5338226B2 (ja) 2008-09-26 2013-11-13 Ｊｆｅスチール株式会社 熱間プレス用亜鉛系めっき鋼板
JP5573195B2 (ja) * 2010-01-25 2014-08-20 新日鐵住金株式会社 昇温特性に優れた熱間プレス用Ａｌめっき鋼板及びその製造方法
DE102011001140A1 (de) * 2011-03-08 2012-09-13 Thyssenkrupp Steel Europe Ag Stahlflachprodukt, Verfahren zum Herstellen eines Stahlflachprodukts und Verfahren zum Herstellen eines Bauteils
KR101974182B1 (ko) * 2012-02-14 2019-04-30 닛폰세이테츠 가부시키가이샤 열간 프레스용 도금 강판 및 도금 강판의 열간 프레스 방법

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001220690A (ja) * 2000-02-01 2001-08-14 Nippon Steel Corp 自動車用Ａｌ系めっき鋼板
JP2007302982A (ja) * 2006-05-15 2007-11-22 Nippon Steel Corp 昇温特性、加工性、塗装後耐食性に優れたホットプレス用Ａｌめっき鋼材
WO2010089273A1 (de) * 2009-02-06 2010-08-12 Thyssenkrupp Steel Europe Ag Verfahren zum herstellen eines beschichteten stahlbauteils durch warmformen und durch warmformen hergestelltes stahlbauteil

Also Published As

Publication number Publication date
CA2864392C (en) 2018-01-02
JP2014139350A (ja) 2014-07-31
TWI470118B (zh) 2015-01-21
ES2765101T3 (es) 2020-06-05
JP6028761B2 (ja) 2016-11-16
CN104093880A (zh) 2014-10-08
EP2816139B1 (en) 2019-10-09
JP6048525B2 (ja) 2016-12-21
CA2864392A1 (en) 2013-08-22
RU2584105C2 (ru) 2016-05-20
MX365687B (es) 2019-06-11
TW201335425A (zh) 2013-09-01
PL2816139T3 (pl) 2020-04-30
JPWO2013122004A1 (ja) 2015-05-11
EP2816139A1 (en) 2014-12-24
KR20160078521A (ko) 2016-07-04
ZA201405948B (en) 2015-11-25
JP2015165049A (ja) 2015-09-17
EP2816139A4 (en) 2015-12-09
MX2014009731A (es) 2014-11-10
US10092938B2 (en) 2018-10-09
BR112014019984B1 (pt) 2021-03-09
CN104093880B (zh) 2016-12-21
BR112014019984A2 (pt) 2017-06-13
US20150020562A1 (en) 2015-01-22
MX2019003385A (es) 2019-07-08
RU2014137101A (ru) 2016-04-10
JP5582254B2 (ja) 2014-09-03
WO2013122004A1 (ja) 2013-08-22
KR20140119738A (ko) 2014-10-10
IN2014DN06844A (enExample) 2015-05-22

Similar Documents

Publication Publication Date Title
KR101974182B1 (ko) 열간 프레스용 도금 강판 및 도금 강판의 열간 프레스 방법
CN105829578B (zh) 汽车部件以及汽车部件的制造方法
KR101679492B1 (ko) Al계 도금 강판, Al계 도금 강판의 열간 프레스 방법 및 자동차 부품
JP6042445B2 (ja) 熱間プレス用めっき鋼板、めっき鋼板の熱間プレス方法及び自動車部品
JP5692148B2 (ja) 熱間プレス用Ａｌ系めっき鋼板及びその熱間プレス方法
WO2019066063A1 (ja) めっき鋼板、めっき鋼板コイル、熱間プレス成形品の製造方法、及び自動車部品

Legal Events

Date Code Title Description
A107 Divisional application of patent
PA0104 Divisional application for international application

Comment text: Divisional Application for International Patent

Patent event code: PA01041R01D

Patent event date: 20160624

Application number text: 1020147022750

Filing date: 20140814

PG1501 Laying open of application
A201 Request for examination
PA0201 Request for examination

Patent event code: PA02012R01D

Patent event date: 20180208

Comment text: Request for Examination of Application

E902 Notification of reason for refusal
PE0902 Notice of grounds for rejection

Comment text: Notification of reason for refusal

Patent event date: 20180504

Patent event code: PE09021S01D

E701 Decision to grant or registration of patent right
PE0701 Decision of registration

Patent event code: PE07011S01D

Comment text: Decision to Grant Registration

Patent event date: 20190212

GRNT Written decision to grant
PR0701 Registration of establishment

Comment text: Registration of Establishment

Patent event date: 20190424

Patent event code: PR07011E01D

PR1002 Payment of registration fee

Payment date: 20190425

End annual number: 3

Start annual number: 1

PG1601 Publication of registration
PR1001 Payment of annual fee

Payment date: 20220331

Start annual number: 4

End annual number: 4

PR1001 Payment of annual fee

Payment date: 20240401

Start annual number: 6

End annual number: 6