KR101821876B1 - 지르코니아로부터 이루어진 유색, 특히 오렌지색 아이템을 생산하는 방법 및 이 방법에 따라 획득되는 지르코니아로부터 이루어진 장식용의 유색 아이템 - Google Patents

지르코니아로부터 이루어진 유색, 특히 오렌지색 아이템을 생산하는 방법 및 이 방법에 따라 획득되는 지르코니아로부터 이루어진 장식용의 유색 아이템 Download PDF

Info

Publication number
KR101821876B1
KR101821876B1 KR1020157034424A KR20157034424A KR101821876B1 KR 101821876 B1 KR101821876 B1 KR 101821876B1 KR 1020157034424 A KR1020157034424 A KR 1020157034424A KR 20157034424 A KR20157034424 A KR 20157034424A KR 101821876 B1 KR101821876 B1 KR 101821876B1
Authority
KR
South Korea
Prior art keywords
oxide
mixture
weight
zirconia
producing
Prior art date
Application number
KR1020157034424A
Other languages
English (en)
Other versions
KR20160004382A (ko
Inventor
아르노 악티스-다타
Original Assignee
코마도 쏘시에떼 아노님
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 코마도 쏘시에떼 아노님 filed Critical 코마도 쏘시에떼 아노님
Publication of KR20160004382A publication Critical patent/KR20160004382A/ko
Application granted granted Critical
Publication of KR101821876B1 publication Critical patent/KR101821876B1/ko

Abstract

본 발명은, 제 1 혼합물을 생성하는 단계로서, 상기 제 1 혼합물은, ㆍ 지르코니아 분말, ㆍ 단독으로 또는 조합으로 산화 이트륨, 산화 마그네슘 및 산화 칼슘을 포함하는 산화물 군으로부터 선택된 3 내지 20 중량% 의 적어도 하나의 안정화제, ㆍ 유리질 상을 생성하기 위한 그리고 단독으로 또는 조합으로 산화 규소, 산화 알루미늄, 산화 리튬 및 산화 이트륨을 포함하는 군으로부터 선택된 0.1 내지 5 중량% 의 적어도 하나의 원소, ㆍ 1 내지 6 중량% 의 산화 세륨 분말을 포함하는, 상기 제 1 혼합물을 생성하는 단계; 상기 제 1 혼합물 및 바인더를 포함하는 제 2 혼합물을 생성하는 단계; 상기 제 2 혼합물을 과립화하여, 과립화된 혼합물을 생성하는 단계; 과립화된 상기 제 2 혼합물에 소망하는 물품의 형상을 부여하여 생형체를 형성하는 단계; 1,250 내지 1,500 ℃ 의 온도에서 적어도 30 분 동안에 공기-소결을 행하는 단계; 환원 분위기하에서 30 분 내지 20 시간의 기간 동안에 700 내지 1,350 ℃ 의 온도에서 소망하는 물품을 어닐링하는 단계; 및 소결된 상기 생형체를 연마하는 단계로 이루어지는 일련의 단계들을 포함하는, 밝은 오렌지색 지르코니아계 물품의 제조 방법에 관한 것이다.

Description

지르코니아로부터 이루어진 유색, 특히 오렌지색 아이템을 생산하는 방법 및 이 방법에 따라 획득되는 지르코니아로부터 이루어진 장식용의 유색 아이템{METHOD FOR PRODUCING A COLOURED ITEM, IN PARTICULAR ORANGE, MADE FROM ZIRCONIA, AND COLOURED DECORATIVE ITEM MADE FROM ZIRCONIA OBTAINED ACCORDING TO THIS METHOD}
본 발명은, 특히 밝은 오렌지색으로부터 구리빛 갈색까지의 범위에 포함되는 색을 나타내며 소결에 의해 획득되는 물품과 같은 유색 지르코니아계 물품의 제조 방법에 관한 것이다. 그러한 물품을 이하의 설명에서 편의상 "오렌지색 물품" 이라 칭한다.
또한, 본 발명은 특히 전술한 방법에 따라 획득되는 장식용의 지르코니아계 오렌지색 물품에 관한 것이다.
예컨대 에나멜, 글레이즈 및 가정용이나 바닥재용 용기를 형성하는데 사용되는 오렌지색/적색 세라믹 물품을 획득하기 위해 세라믹 재료에 황화 카드뮴 (CdSe), 셀렌화 카드뮴 및 카드뮴 황셀레나이드 (cadmium sulfoselenide) 와 같은 착색제를 혼입하는 것이 이미 알려져 있다.
산업적 세라믹, 특히 소결된 지르코니아계 세라믹에서 이러한 타입의 착색제의 혼입이 곧 바람직하므로, 이러한 타입의 착색제의 사용은 여러 단점이 있다.
실제로, 이러한 착색제는 고온에서 불안정하고, 단지 1,000 또는 2,000 ℃ 까지 착색 특성을 나타낸다. 이는 이러한 타입의 착색제의 사용을 크게 제한하고, 특히, 지르코니아의 소결 온도가 어쨌든 1,100 ℃ 보다 높으므로, 소결된 지르코니아 물품의 형성을 허용하지 않는다.
더욱이, 시계 케이스와 같이 사용자의 피부와 접촉할 물체에 중금속을 함유하는 이러한 타입의 착색제의 사용은, 법에 의해 금지되지 않는다면, 적어도 강하게 막아야 한다.
더욱이, 이러한 타입의 상업적으로 입수가능한 착색제는 지르코니아 분말로 균질 혼합물을 획득하는 것과 양립할 수 없는 큰 결정립 크기를 갖는다.
그러므로, 본 발명의 주된 목적은, 한편으로, 밝은 오렌지색의 소결된 지르코니아계 물품의 제조 방법을 제공하고, 다른 한편으로, 이 방법에 따라 획득되는 그러한 물품으로서, 표면으로부터 적어도 5 ㎜ 의 깊이에 걸쳐 밝은 오렌지색을 나타내면서 만족스러운 기계적 특성을 갖는 상기 물품을 제공하는 것이다.
이를 위해, 본 발명은,
제 1 혼합물을 생성하는 단계로서, 상기 제 1 혼합물은
ㆍ 지르코니아 분말,
ㆍ 단독으로 또는 조합으로 산화 이트륨, 산화 마그네슘 및 산화 칼슘을 포함하는 산화물 군으로부터 선택된 3 내지 20 중량% 의 적어도 하나의 안정화제,
ㆍ 유리질 상 (vitreous phase) 을 생성하기 위한 그리고 단독으로 또는 조합으로 산화 규소, 산화 알루미늄, 산화 리튬 및 산화 이트륨을 포함하는 군으로부터 선택된 0.1 내지 5 중량% 의 적어도 하나의 원소,
ㆍ 1 내지 6 중량% 의 산화 세륨 분말
을 포함하는, 상기 제 1 혼합물을 생성하는 단계,
상기 제 1 혼합물 및 바인더를 포함하는 제 2 혼합물을 생성하는 단계,
상기 제 2 혼합물을 과립화하여, 과립화된 혼합물을 생성하는 단계,
과립화된 상기 제 2 혼합물에 소망하는 물품의 형상을 부여하여 생형체 (green body) 를 형성하는 단계,
1,250 내지 1,500 ℃ 의 온도에서 적어도 30 분 동안에 공기-소결을 행하는 단계,
10-6 내지 10-1 기압 (atmospheres) 의 산소 분압을 갖는 환원 분위기하에서 30 분 내지 20 시간의 기간 동안에 700 내지 1,350 ℃ 의 온도에서 상기 소망하는 물품을 어닐링하는 단계, 및
소결된 상기 생형체를 연마하는 단계
로 이루어지는 일련의 단계들을 포함하는, 밝은 오렌지색 지르코니아계 물품의 제조 방법에 관한 것이다.
본 발명의 방법은, 소결될 혼합물에 산화세륨 분말 (CeO2) 을 혼입함으로써 소결 온도를 낮추는 것을 가능하게 한다. 산화세륨은 물품에 주어져야 하는 오렌지색의 결정적인 요소들 중의 하나로서 또한 작용한다.
실제로, CeO2 의 존재 하에서의 소결 작업 후의 물품의 색은 유백색 (ivory white) 이다. 그러면, 본 발명의 방법의 후속 단계, 이른바 소결 단계 동안에, 이를 Ce2O3 (+3 산화 상태) 로 환원시키기 위해 CeO2 (+4 산화 상태) 의 존재의 이점이 취해진다. 이 소결 단계 후에, 물품은 결정립계에 존재하는 +4 및 +3 산화 상태의 세륨의 개별 양에 따라 옐로-오렌지색으로부터 밝은 오렌지색까지의 범위의 색을 갖는다. +4 산화 상태의 산화세륨 (CeO2) 의 색은 유백색이고, +3 산화 상태의 산화세륨 (Ce2O3) 의 색은 밝은 오렌지색이다.
결정립계에 존재하는 +4 및 +3 산화 상태의 산화세륨의 개별 양은 어닐링 조건에 의해, 더 구체적으로는 어닐링이 일어나는 오븐의 분위기에서 산소 분압을 변경함으로써 결정된다.
일 실시형태에 따르면, 제 1 혼합물은 유리질 상을 위한 0.1 내지 1 중량% 의 분말, 바람직하게는 4 내지 5 중량% 의 산화 세륨 분말 (Ce+4 O2) 을 포함한다.
또한, 본 발명은, 전술한 방법에 따라 얻어진 장식용의 밝은 오렌지색 지르코니아계 물품에 관한 것으로서, 상기 물품은 지르코니아 매트릭스, 단독으로 또는 조합으로 산화 이트륨, 산화 마그네슘 및 산화 칼슘을 포함하는 산화물 군으로부터 선택된 3 내지 20 중량% 의 적어도 하나의 안정화제, 단독으로 또는 조합으로 산화 규소, 산화 알루미늄, 산화 리튬 및 산화 이트륨을 포함하는 군으로부터 선택된 적어도 하나의 원소를 포함하는 0.1 내지 5 중량% 의 유리질 상, 및 1 내지 6 중량% 의 산화 세륨을 본질적으로 포함하는 성형 부분으로 제조된 소결 부분으로 형성되는 것을 특징으로 한다.
그러한 물품은 연마 후에 강한 광택을 나타낸다는 이점을 갖고, 따라서 시계 케이스의 구성 부품, 보석류, 팔찌, 브로치, 타이 핀, 목걸이, 핸드백, 전화기, 가구, 또는 가정용품과 같은 장식용 물품의 제조에 특히 적합하다.
본 발명의 다른 특징 및 이점은 본 발명의 방법의 실시예에 대한 이하의 설명으로부터 분명해질 것이다.
이제 상세하게 설명될 본 발명의 제조 방법은 손목시계의 구성 부품을 제조하거나 임의의 다른 장식용 물품을 제조하기에 특히 적합한 외관 및 기계적 특성을 갖는 밝은 오렌지색의 소결 지르코니아계 물품의 생성을 허용하는 것이다.
이 방법에 따라 획득되는 밝은 오렌지색 지르코니아 물품은 89 내지 98.9 중량% 의 안정화된 지르코니아 및 중량 기준 잔부, 즉 단독으로 또는 조합으로 산화 규소, 산화 알루미늄, 산화 이트륨 및 산화 리튬으로 형성된 0.1 내지 5 중량% 의 유리질 상, 및 1 내지 6 중량% 의 산화 세륨을 포함한다.
단독으로 또는 조합으로 지르코니아는 산화 이트륨, 산화 마그네슘 및 산화 칼슘을 포함하는 산화물 군으로부터 선택된 적어도 하나의 안정화제에 의해 정방정 상 (tetragonal phase) 에서 통상적으로 안정화되며, 이 안정화제는 지르코니아에 대해 3 내지 20 중량% 의 양이다.
본 발명의 방법의 실시예에 따라, 이러한 물품을 제조하기 위해, 다음과 같이 진행한다:
3 중량% 의 산화 이트륨과 함께 943 g 의 안정화된 지르코니아 분말을 칭량한다. 사용되는 분말은 대략 마이크로미터, 전형적으로 0.1 내지 0.5 마이크로미터의 평균 결정립 크기를 갖는다. 이 분말은 일본 Tosoh Corporation 에 의해 참조번호 TZ-3 Y 로 판매된다.
그리고 나서, 후속 소결 동안에 유리질 상을 형성하도록, 산화 규소, 산화 알루미늄과 산화 리튬 분말의 혼합물 7 g 을 칭량한다.
바람직하게는, 유리질 상은 내림차순으로 산화 규소, 산화 알루미늄 및 산화 리튬의 혼합물 또는 조합을 중량 기준으로 각각 47 %, 40 % 및 13 % 포함한다.
사용된 규소 분말은 1 마이크로미터 미만, 전형적으로 40 나노미터의 평균 결정립 크기를 갖고, 독일 Cerdec 에 의해 명칭 Aerosil OX50 으로 판매된다.
사용된 알루미늄 분말은 대략 마이크로미터 또는 서브마이크로미터, 전형적으로 0.5 마이크로미터의 평균 결정립 크기를 갖고, 프랑스 Baikowski 에 의해 명칭 CR30 으로 판매된다.
사용된 리튬 분말은 대략 마이크로미터 또는 서브마이크로미터, 전형적으로 2.4 마이크로미터의 평균 결정립 크기를 갖고, 스위스 Sigma-Aldrich Chemicals 에 의해 참조번호 374725 로 판매된다. 필요하다면, 분말은 희망 결정립 크기를 얻도록 밀링된다.
마지막으로, 50 g 의 산화 세륨 (Ce4 +O) 을 칭량한다; 사용된 분말은 대략 마이크로미터 또는 서브마이크로미터, 전형적으로 0.5 마이크로미터의 결정립 크기를 갖고, 스위스 Sigma-Aldrich Chemicals 에 의해 참조번호 202975 로 판매된다.
이러한 분말들은 모두 95 % 초과의 순도를 갖는 것이 바람직하다고 할 수 있다.
일단 분말들이 칭량되고 나면, 상기 분말들 모두는 습식 매체 (wet medium) 에서 혼합되고 균질화된다. 균질화의 최종 단계에서, 대략 50 g 의 바인더, 예컨대 폴리비닐 알코올이 추가된다.
그리고 나서, 혼합물은 예컨대 통상적인 애터마이저 (atomiser) 에서 건조된다.
따라서 획득되는 과립은 200 마이크로미터 미만의 결정립 크기를 갖는 입자들을 유지하기 위해 체질된다.
그리고 나서, 체질된 과립은 생형체를 획득하기 위해 획득하고자 하는 물품의 형상을 갖는 몰드 내로 가압된다.
거의 최종의 대략적인 형상의 물품이 소결로 내에 위치된다. 이와 관련하여, 소결이 공기 중에서 행해질 수 있다는 것을 인식할 것이다. 그리고, 물품은 제 1 단계에서 시간당 30°의 속도로 대략 1,000 ℃ 까지 가열된 후, 제 2 단계에서 시간당 50°의 속도로 1,250 ℃ 의 온도까지 가열된다. 물품은 적어도 30 분 동안, 바람직하게는 1 시간 동안 이 온도에서 유지된다.
물론 1,100 ℃ 이상 1,600 ℃ 미만의 임의의 다른 온도에서 소결이 행해질 수 있다는 것을 인식할 것이다.
소결 동안에, 산화 규소, 산화 알루미늄, 산화 이트륨 및 산화 리튬은 결정립계에서 +4 산화 상태의 산화 세륨으로 농축되는 유리질 상을 형성하고, 이는 소결 후에 물품에 아이보리색을 제공한다.
산화 리튬의 존재가 유리하게는, 소결 온도를 낮추고 밝은 오렌지색이 획득될 수 있게 하는 산화 세륨 색의 변환을 제한한다는 것을 인식할 것이다.
이러한 소결 단계 후에, 물품은 분위기를 선택할 수 있는 어닐링로 내에 위치된다. 원하는 물품은 수소 분위기 (H2) 중에서 또는 질소와 수소의 혼합물 (N2/H2) 또는 아르곤과 수소의 혼합물을 포함하는 분위기 중에서 어닐링된다.
이러한 어닐링 작업 동안에, 노 내의 산소 분압은 10-6 내지 10-1 기압이고, 어닐링 온도는 700 ℃ 내지 1250 ℃ 이고, 어닐링 시간은 일반적으로 30 분 내지 20 시간이다.
본 발명의 방법의 바람직한 실시예에 따르면, 어닐링로 내의 분위기는 수소이고, 산소 분압은 10-4 내지 10-1 기압이고, 어닐링 온도는 900 내지 1,150 ℃ 이고, 어닐링 시간은 4 내지 6 시간이다. 물품 내부의 색의 농도가 어닐링 시간에 비례하여 변한다는 것을 이해할 것이다.
어닐링 작업 후에 획득되는 물품의 색은 어닐링 조건에 따라 오렌지색과 구리빛 갈색 사이에 포함되는 색상 또는 밝은 오렌지색이다.
그리고 나서, 물품은 최종 용도에 적합한 형상을 획득하도록 냉각 및 기계가공된다. 착색이 물품 내측으로 깊어서 물품의 기계가공이 어떤 식으로도 그 색을 변경하시 않는다는 것을 인식할 것이다.
마지막으로, 물품은 예컨대 다이아몬드 페이스트를 이용하여 연마되고, 따라서 획득되는 물품은 어닐링 조건에 따라 상기한 색들 사이에 포함된 색상 또는 밝은 오렌지색의 광택있는 외관을 가지므로, 특히 시계제조 분야에의 적용을 위한 매력적이고 흥미로운 심미적 특징들을 갖는다.
본 발명의 방법의 다른 실시예에 따르면, 직경이 45 ㎜ 이고 두께가 4 ㎜ 인 원형 시계 베즐을 형성하기 위해 전술한 작업 방법을 따른다. 이 예는 총 조성물의 중량 기준으로 비율이 0.7 % 인 컴파운드를 형성하는 SiO2 (47%), Al2O3 (40%), 및 Li2O (13%) 의 조합, 유리질 상을 형성하는 혼합물, 6 중량% 의 CeO2, 및 잔부, 즉 93.3 중량% 의 안정화된 ZrO2 를 사용하였다. 일단 원하는 최종 형상으로 구성되고 나서, 베즐은 1,450 ℃ 에서 2 시간 동안 공기 중에서 소결되었다. 그리고 나서, 이 베즐은 5 % 수소 및 95 % 아르곤을 포함하는 분위기 중에서 1,000 ℃ 에서 12 시간 동안 어닐링되었다. 그리고 나서, 베즐은 냉각되었고, 경면 연마되었다. 획득된 베즐은 밝은 오렌지색의 광택있는 외관을 가졌다. 또한, 베즐의 파괴 후에, 물품 속 깊게 착색이 달성되었음이 관찰되었다.

Claims (10)

  1. 제 1 혼합물을 생성하는 단계로서, 상기 제 1 혼합물은
    ㆍ 지르코니아 분말,
    ㆍ 단독으로 또는 조합으로 산화 이트륨, 산화 마그네슘 및 산화 칼슘을 포함하는 산화물 군으로부터 선택된 3 내지 20 중량% 의 적어도 하나의 안정화제,
    ㆍ 유리질 상을 생성하기 위한 그리고 단독으로 또는 조합으로 산화 규소, 산화 알루미늄, 산화 리튬 및 산화 이트륨을 포함하는 군으로부터 선택된 0.1 내지 5 중량% 의 적어도 하나의 원소,
    ㆍ 1 내지 6 중량% 의 산화 세륨 분말
    을 포함하는, 상기 제 1 혼합물을 생성하는 단계,
    상기 제 1 혼합물 및 바인더를 포함하는 제 2 혼합물을 생성하는 단계,
    상기 제 2 혼합물을 과립화하여, 과립화된 혼합물을 생성하는 단계,
    과립화된 상기 제 2 혼합물에 소망하는 물품의 형상을 부여하여 생형체 (green body) 를 형성하는 단계,
    1,250 내지 1,500 ℃ 의 온도에서 적어도 30 분 동안에 공기-소결을 행하는 단계,
    환원 분위기하에서 30 분 내지 20 시간의 기간 동안에 700 내지 1,350 ℃ 의 온도에서 상기 소망하는 물품을 어닐링하는 단계, 및
    소결된 상기 생형체를 연마하는 단계
    로 이루어지는 일련의 단계들을 포함하는, 밝은 오렌지색 지르코니아계 물품의 제조 방법.
  2. 제 1 항에 있어서,
    상기 제 1 혼합물은 상기 유리질 상을 형성하기 위한 0.1 내지 1 중량% 의 분말을 포함하는 것을 특징으로 하는 밝은 오렌지색 지르코니아계 물품의 제조 방법.
  3. 제 1 항에 있어서,
    유리질 상을 형성하기 위한 분말들은 내림차순으로 산화 규소, 산화 알루미늄, 산화 리튬 및 산화 이트륨의 중량에 의한 양을 포함하는 것을 특징으로 하는 밝은 오렌지색 지르코니아계 물품의 제조 방법.
  4. 제 3 항에 있어서,
    내림차순으로 산화 규소, 산화 알루미늄 및 산화 리튬의 중량의 양은 각각 47%, 40% 및 13% 인 것을 특징으로 하는 밝은 오렌지색 지르코니아계 물품의 제조 방법.
  5. 제 1 항에 있어서,
    상기 제 1 혼합물은 1 내지 6 중량% 의 산화 세륨 분말을 포함하는 것을 특징으로 하는 밝은 오렌지색 지르코니아계 물품의 제조 방법.
  6. 제 1 항에 있어서,
    상기 제 1 혼합물은 4 내지 5 중량% 의 산화 세륨 분말을 포함하는 것을 특징으로 하는 밝은 오렌지색 지르코니아계 물품의 제조 방법.
  7. 제 1 항에 있어서,
    상기 안정화제는 산화 이트륨인 것을 특징으로 하는 밝은 오렌지색 지르코니아계 물품의 제조 방법.
  8. 제 1 항에 있어서,
    어닐링 온도는 700 내지 1,350℃ 이고, 상기 환원 분위기는 10-6 내지 10-1 기압의 산소 분압을 갖는 것을 특징으로 하는 밝은 오렌지색 지르코니아계 물품의 제조 방법.
  9. 제 1 항 내지 제 8 항 중 어느 한 항의 방법에 따라 얻어진 장식용의 밝은 오렌지색 지르코니아계 물품으로서,
    상기 물품은 지르코니아 매트릭스, 산화 이트륨, 산화 마그네슘, 산화 세륨 및 산화 칼슘 그리고 이들의 혼합물을 포함하는 산화물 군으로부터 선택된 3 내지 20 중량% 의 적어도 하나의 안정화제, 산화 규소, 산화 알루미늄, 산화 리튬 및 산화 이트륨 그리고 이들의 혼합물을 포함하는 0.1 내지 5 중량% 의 유리질 상, 및 1 내지 6 중량% 의 산화 세륨을 본질적으로 포함하는 성형 부분으로 제조된 소결 부분으로 형성되는, 장식용의 밝은 오렌지색 지르코니아계 물품.
  10. 제 9 항에 있어서,
    상기 물품은 제 1 항에 따라 얻어지는 것을 특징으로 하는 장식용의 오렌지색 지르코니아계 물품.
KR1020157034424A 2013-05-03 2014-05-05 지르코니아로부터 이루어진 유색, 특히 오렌지색 아이템을 생산하는 방법 및 이 방법에 따라 획득되는 지르코니아로부터 이루어진 장식용의 유색 아이템 KR101821876B1 (ko)