KR100784020B1 - 내피로균열성이 우수한 고 Cr 주철 및 그 제조 방법 - Google Patents
내피로균열성이 우수한 고 Cr 주철 및 그 제조 방법 Download PDFInfo
- Publication number
- KR100784020B1 KR100784020B1 KR1020060048912A KR20060048912A KR100784020B1 KR 100784020 B1 KR100784020 B1 KR 100784020B1 KR 1020060048912 A KR1020060048912 A KR 1020060048912A KR 20060048912 A KR20060048912 A KR 20060048912A KR 100784020 B1 KR100784020 B1 KR 100784020B1
- Authority
- KR
- South Korea
- Prior art keywords
- cast iron
- martensite
- hardness
- fatigue
- carbide
- Prior art date
Abstract
Description
Claims (8)
- 질량%로 C: 2.5 내지 3.5%, Si: 0.2 내지 1.0%, Mn: 0.6 내지 2.0%, Cr: 13 내지 22%, Mo: 1.0 내지 3.0%, N: 0.01 내지 0.15%를 함유하고, 또한,이들의 함유량이, [Cr]/[C]= 4.5 내지 6.5, [Mn]×[Mo]= 1.8 내지 2.5의 관계를 각각 만족시키며,잔부가 Fe 및 불가피적 불순물로 이루어지는 조성을 갖고,100배의 광학 현미경에서의 주철 조직 관찰에 있어서의 마르텐사이트의 크기가, 탄화물에 둘러싸인 마르텐사이트의 1개당 평균 면적으로서 6000μm2 이하이며,마르텐사이트와 잔류 오스테나이트 및 탄화물에 있어서의, X선 회절 피크 강도비에 의한 잔류 오스테나이트의 평균 부피 분율이 5 내지 40%인 조직을 갖는 것을 특징으로 하는,내피로균열성이 우수한 고 Cr 주철.
- 제 1 항에 있어서,상기 고 Cr 주철이 추가로 Ni 1.0질량% 이하를 포함하는 내피로균열성이 우수한 고 Cr 주철.
- 제 1 항에 있어서,상기 고 Cr 주철이 추가로 Ti, V, Zr, Nb 중에서 선택되는 1종 또는 2종 이상을 합계로 1.0 내지 5.0질량% 함유하는 내피로균열성이 우수한 고 Cr 주철.
- 제 1 항 내지 제 3 항 중 어느 한 항에 있어서,상기 고 Cr 주철의 경도가 800 Hv 이상이고, 인성이 샤르피 충격치로 2.0 J/cm2 이상인 내피로균열성이 우수한 고 Cr 주철.
- 질량%로 C: 2.5 내지 3.5%, Si: 0.2 내지 1.0%, Mn: 0.6 내지 2.0%, Cr: 13 내지 22%, Mo: 1.0 내지 3.0%, N: 0.01 내지 0.15%를 함유하고, 또한,이들의 함유량이, [Cr]/[C]= 4.5 내지 6.5, [Mn]×[Mo]= 1.8 내지 2.5의 관계를 각각 만족시키며,잔부가 Fe 및 불가피적 불순물로 이루어지는 조성의 주철을, 냉각 속도가 5℃/s 이상에서 주조하고, 이어서,900 내지 1050℃의 범위에서 3시간 이상 유지하는 가열 유지 후에,냉각 속도 0.05 내지 5℃/s의 범위에서 담금질 처리하여,100배의 광학 현미경에서의 주철 조직 관찰에 있어서의 마르텐사이트의 크기가, 탄화물에 둘러싸인 마르텐사이트의 1개당 평균 면적으로서 6000μm2 이하이며,마르텐사이트와 잔류 오스테나이트 및 탄화물에 있어서의, X선 회절 피크 강도비에 의한 잔류 오스테나이트의 평균 부피 분율이 5 내지 40%인 조직을 얻는 것을 특징으로 하는,내피로균열성이 우수한 고 Cr 주철의 제조 방법.
- 제 5 항에 있어서,상기 고 Cr 주철이 추가로 Ni 1.0질량% 이하를 포함하는 내피로균열성이 우수한 고 Cr 주철의 제조 방법.
- 제 5 항에 있어서,상기 고 Cr 주철이 추가로 Ti, V, Zr, Nb 중에서 선택되는 1종 또는 2종 이상을 합계로 1.0 내지 5.0질량% 함유하는 내피로균열성이 우수한 고 Cr 주철의 제조 방법.
- 제 5 항 내지 제 7 항 중 어느 한 항에 있어서,상기 고 Cr 주철의 경도가 800 Hv 이상이고, 인성이 샤르피 충격치로 2.0 J/cm2 이상인 내피로균열성이 우수한 고 Cr 주철의 제조 방법.