KR100528377B1 - 부분도장 방법 - Google Patents
부분도장 방법 Download PDFInfo
- Publication number
- KR100528377B1 KR100528377B1 KR1020050040918A KR20050040918A KR100528377B1 KR 100528377 B1 KR100528377 B1 KR 100528377B1 KR 1020050040918 A KR1020050040918 A KR 1020050040918A KR 20050040918 A KR20050040918 A KR 20050040918A KR 100528377 B1 KR100528377 B1 KR 100528377B1
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- partial coating
- coating method
- transfer film
- transparent coating
- Prior art date
Abstract
본 발명은 부분도장 방법에 관한 것으로, 보다 구체적으로는 투명도장을 한 기재면에 홀로그램 등의 무늬가 인쇄된 전사필름을 부착시킨 후 열처리하여 인쇄층을 전사시킨 후 기재필름을 제거함으로써, 기재면에 인쇄층이 완벽하게 전사되는 것을 특징으로 하는 도장방법에 관한 것으로, 본 발명의 전사된 표면은 인쇄층이 완벽하게 전사되어 투명도장 내로 함침되므로 단차가 발생하지 않으며, 용제에 의해 지워지지 않는 특징이 있다.
Description
본 발명은 부분도장 방법에 관한 것으로, 보다 구체적으로는 투명도장을 한 기재면에 홀로그램 등의 무늬가 인쇄된 전사필름을 부착시킨 후 열처리하여 인쇄부분을 전사시킨 후 기재필름층을 제거하는 방법에 관한 것으로, 본 발명의 전사된 표면은 인쇄무늬가 완벽하게 전사되어 투명도장 내로 함침되므로 단차가 발생하지 않으며, 굴곡진 면에도 쉽게 부착 가능하고, 완벽하게 접착되어 용제를 사용하여도 지워지지 않는 특징이 있다.
자동차 도장은 베이스도장, 안료 도장, 클리어 도장의 3단계로 구성되는 데, 이중 클리어 도장은 차체 표면의 미관상 광택을 주기 위하여 도장시키는 것으로, 먼지 또는 오물 등으로부터 차체를 보호하는 역할도 한다.
근래에 자동차의 외관을 아름답게 하기위하여 전사필름을 부착시키거나 스티커를 부착시키고 있으나, 종래 전사필름을 사용하는 경우, 상온에서 점착성이 있어 전사시킨 후 물리적인 힘을 가하거나 용제를 사용하는 경우 벗겨지는 등의 내구성이 떨어지는 단점이 있었으며, 이밖에 통상적인 스티커 장식을 붙이는 경우, 단차가 발생하여 이물질이 끼거나, 쉽게 탈리되므로 내구성이 떨어지는 단점이 있으며, 다양하고 규격화된 일정한 모양 또는 문자를 도장시키는 것이 불가능하였다.
상기와 같은 문제점을 해결하기 위한 본 발명은, 전사필름의 인쇄층을 투명도장을 한 기재면에 완벽하게 전사시켜 함침시키는 신규한 부분도장 방법을 제공하고자 한다.
또한 기재면에 완벽하게 전사시킬 수 있는 상기의 전사필름의 조성물을 제공하고자 한다.
본 발명은 부분도장 방법에 관한 것으로, 보다 구체적으로는 투명도장을 한 기재면에 홀로그램 등의 무늬가 인쇄된 전사필름을 부착시킨 후 열처리하여 인쇄층을 전사시킨 후 기재필름을 제거함으로써, 기재면에 인쇄층이 완벽하게 전사되는 것을 특징으로 하는 도장방법에 관한 것으로, 본 발명의 전사된 표면은 인쇄층이 완벽하게 전사되어 투명도장 내로 함침되므로 단차가 발생하지 않으며, 용제로도 지워지지 않는다.
본 발명에서 상기 기재면은 금속면, 목재면, 플라스틱면에서 선택되는 어느 하나이며, 상기 금속면은 자동차외장, 냉장고, 세탁기, 전자렌지, 에어컨, 철재가구, 알루미늄제품, 엘리베이터에서 선택되는 어느 하나이나 여기에 제한되는 것은 아니다.
본 발명에서 사용하는 전사필름은 그 두께가 얇고, 일반 점착층이 아닌 상온에서는 접착성이 없으나, 열을 가하는 경우 투명도장이 경화됨과 동시에 인쇄층과 함께 투명도장면에 완벽하게 전사되어 함침되는 것이다. 따라서 본 발명의 전사필름을 이용하여 부분 도장시키는 경우, 물리적인 힘을 가하여도 인쇄면이 벗겨지지 않는 특징이 있으며, 용제 등에 의해서도 지워지지 않는 신규한 도장방법에 관한 것이다.
본 발명에 따른 부분도장 방법은 다음과 같다.
1) 기재면에 투명도장을 하고 예비 건조시키는 단계;
2) 기재필름층, 인쇄층의 순으로 적층된 전사필름의 인쇄층면을 상기 투명도장면에 부착시키는 단계;
3) 상기 부착시킨 전사필름과 투명도장면을 함께 50 ~ 200 ℃로 열처리하는 단계;
4) 전사필름과 투명도장면을 냉각시킨 후 상기 전사필름의 기재필름층을 제거시키는 단계; 로 이루어진다.
본 발명에서 상기 예비건조단계는 투명도장의 도장면이 끈적이지 않을 정도로 건조시키는 것을 의미하는 것으로, 일반적으로 속건형 도장의 경우 30분 이상, 지건형의 경우 2시간 이상 건조시키는 것이 바람직하다. 상기 예비 건조단계에서는 끈적이지 않을 정도로 건조시키나 완전히 경화시키는 것이 아니기 때문에 얇은 두께의 전사필름이 접착제 없이도 잘 부착되며, 굴곡진 곳에도 잘 접착이 된다.
또한 상기 투명도장을 한 후 예비건조 단계에서 오랜 시간이 지난 경우에는 전사필름이 잘 부착되지 않으므로, 상기 2)단계인 전사필름을 부착시키기 전에 부착면을 40 ~ 70 ℃로 가열하거나 또는 유기용제를 스프레이하는 단계를 추가할 수 있다. 이때 사용되는 유기용제는 에탄올, 메탄올, 이소프로판올 등과 같은 알콜류, 초산에틸, 초산부틸 등과 같은 에스테르류, 에틸셀로솔브, 부틸셀로솔브 등과 같은 에테르류, 아세톤, 메틸에틸케톤, 메틸이소부틸케톤 등과 같은 케톤류, 톨루엔, 크실렌 등과 같은 방향족 탄화수소류에서 선택되는 어느 하나이상의 용제를 사용할 수 있다. 또는 일반적으로 사용되는 희석제인 신나를 이용하는 것도 가능하다.
투명도장을 하고 오랜 시간이 경과된 경우 기재면이 경화된 상태에서 기재면이 금속면인 경우에는 전사필름을 부착시킨 후 고무자석판 또는 고무판을 부착시킨 후 열을 가할 수 있으나, 금속면이 아닌 경우에는 상기한 바와 같이 가열하거나 유기용제를 스프레이하여 투명도장면이 약간 점성을 갖도록 하여 전사필름을 부착시키는 것이 바람직하다.
상기와 같은 본 발명은 투명도장면에 기재필름을 부착시킨 후 열처리 하는 경우, 투명도장이 경화되면서 인쇄층이 투명도장면에 함침되므로 냉각시킨 후 부착면 상부의 기재필름을 제거시키는 경우 힘을 들이지 않고도 쉽게 제거가 된다.
본 발명에서 투명도장은 열에 의해 경화되는 열경화성 수지를 사용하는 것이 바람직하며, 아미노알키드수지, 열경화성아크릴수지, 멜라민 수지, 불소수지에서 선택되는 어느 하나 이상을 사용할 수 있으나 이에 한정되는 것은 아니다.
상기 열경화성 아크릴수지는 아크릴 및 메타크릴산 에스테르, 스티렌, 비닐톨루엔 등 공중합쇄의 골격에 각종의 활성 작용기를 펜단트 그룹으로 한 구조를 갖고 있어서, 상기 펜단트 그룹이 열 또는 촉매의 존재에서 아크릴 수지끼리 또는 다른 도료용 수지와 반응해 무한대의 분자량의 3차원 망목구조를 형성하는 것이다.
또한 본 발명에서 투명도장은 기재면이 자동차의 외관인 경우 클리어 도장을 의미하는 것으로, 자동차 클리어도장에 사용되는 도료는 아미노알키드계, 열경화성 아크릴계가 통상적으로 사용된다.
또한 상기 투명도장은 안료를 사용하여 색상을 구현하는 것도 가능하다. 이때 사용되는 안료는 탈크, 탄산칼슘 등과 같은 체질안료, 크롬산아연, 아연분말, 황산바륨 등과 같은 방청안료, 산화티탄, 산화철, 암석 등과 같은 무기안료, 프탈로시아닌블루, 퀴나크리돈레드 등과 같은 유기안료, 이 밖의 착색 안료에서 선택되는 어느 하나 이상을 사용할 수 있다.
본 발명에서는 상기 3)단계의 열처리 시 고무자석판 또는 고무판을 전사필름의 일부 또는 전면을 수용하도록 붙인 후 간접 가열시킬 수 있는 방법을 제공한다. 상기한 바와 같이 고무자석판 또는 고무판을 붙인 후 가열하는 경우, 열이 골고루 전달되므로 전사 후 기재필름을 제거시킬 때 인쇄면이 고루 부착되는 효과가 있으며, 직접 가열하는 경우 온도가 너무 높은 경우에는 기재필름이 용융되는 현상이 발생할 수 있으나 고무자석판 또는 고무판을 부착시킨 후 가열하는 경우에는 이러한 것을 방지하여 주므로 안전하고, 균일하게 열을 가할 수 있어서 바람직하다.
상기 가열은 50 ~ 200 ℃가 바람직하며, 이는 투명도장면이 경화되도록 하는 온도이며, 전사필름의 인쇄면이 전사되는 온도를 기재한 것으로 조성물에 따라 그 온도를 선택적으로 사용할 수 있다.
또한, 본 발명에서는 상기 4)단계 후 투명도장을 추가로 수행하는 것도 가능하다. 상기와 같이 기재필름을 제거시킨 후 완성하여도 전사가 되어 바람직하나, 보다 바람직하게는 전사시킨 후 투명도장을 하여 마무리하면, 보다 깨끗하게 마무리 할 수 있다.
본 발명의 부분 도장에 사용되는 전사필름의 구성은 도 1 및 도2에 나타내었으며, 이에 대하여 자세하게 설명하면 다음과 같다.
도 1에는 기재필름의 상부에 인쇄층이 구비되는 본 발명에 따른 전사필름을 나타내었으며, 도 2에는 기재필름, 열경화성수지로 구성되는 보호층, 인쇄층, 열가소성수지로 구성되는 열균착층의 순으로 이루어진 본 발명에 전사필름의 또 다른 일예를 나타내었다. 본 발명에서는 상기 예시된 기재필름의 구성 중 어느 하나이상을 갖는 것이라면 모두 포함되며, 이하는 도 2를 참고하여 각 구성에 대하여 설명하도록 한다.
본 발명의 기재필름(1)은 투명한 수지 필름을 사용하는 것이 바람직하며, 예를 들면, 폴리에스테르필름, 폴리비닐클로라이드필름, 폴리에틸렌필름, 폴리프로필렌필름 등을 사용할 수 있으며, 바람직하게는 폴리프로필렌필름을 사용하는 것이 좋다. 재질의 두께는 유연성, 전이성 등을 고려할 때 10 내지 200 ㎛가 바람직하나 여기에 한정되는 것은 아니다.
상기 보호층(2)은 상기 기재필름(1)의 상부에 형성되는 것으로, 투명도장에 사용된 수지와 유사한 것을 사용하는 것이 바람직하다. 투명도장은 통상적으로 열경화성 아미노알키드계 또는 열경화성 아크릴계를 사용하므로 이와 동일하거나 유사한 열경화성 수지를 사용하는 것이 전사시킨 후 투명도장면에 완벽하게 함침되므로 바람직하다. 예를 들면, 아미노알키드계, 열경화성 아크릴계, 에폭시계, 우레탄계 수지에서 선택되는 어느 하나이상의 수지를 사용한다. 상기 보호층(2)은 기재필름층으로부터 인쇄층이 쉽게 분리되는 역할을 함과 동시에, 전사되는 경우 인쇄층의 바깥쪽에 위치하여 인쇄층의 표면을 보호하고, 긁힘을 방지하는 역할을 하며, 본 발명에서 선택적으로 사용할 수 있다.
상기 인쇄층(3)은 안료, 투명수지를 혼합하여 그라비아 인쇄, 실크스크린인쇄 등으로 형성시키거나, 상기 조성물에 금속파우더, 결합제를 추가로 혼합시켜 그라비아 인쇄, 실크인쇄 등으로 형성한 후 홀로그램패턴을 가지도록 금속막을 가공시킨 홀로그램박막도 가능하다. 상기 안료는 통상적으로 사용되는 안료라면 사용가능하고, 투명수지는 열가소성 투명수지를 사용하는 것이 바람직하다. 예를 들면, 폴리비닐클로라이드계수지, 아크릴로니트릴-부타디엔-스티렌 수지 등이 있으며 여기에 한정되는 것은 아니다. 상기 결합제는 금속파우더가 기재에 접착하도록 하는 역할을 하는 것으로, 예를 들면, visprox사의 V2000, TCI8700 시리즈, TCP9900 시리즈 등을 사용한다. 상기 금속파우더는 통상적으로 홀로그램에 사용되는 금속 분말을 사용하며, 금, 은, 알루미늄, 아연, 니켈, 크롬 등이 통상적으로 사용된다. 이와 같은 홀로그램은 입체무늬를 부여하는 효과가 있다. 홀로그램 문양 등의 패턴이 형성되는 금속박의 경우에는 먼저 기재층의 상부에 보호층을 형성한 후, 그 상부에 금속 파우더가 혼합된 금속박을 형성하고, 홀로그램 패턴을 가지도록 통상적인 방법에 의하여 금속막을 가공시킨다.
본 발명에서 상기 인쇄층(3)에 사용되는 상기 조성물들은 통상적으로 당업자가 사용하는 수준의 조성비를 사용하는 것이며, 사용자가 필요에 따라 변형 가능한 것이다.
본 발명에서 상기 인쇄층(3)은 0.1 ~ 150 ㎛의 두께로 얇은 박으로 형성시키는 것이 단차가 발생하지 않으며, 투명도장면으로 함침되므로 바람직하다.
본 발명은 열균착층(4)을 더 구비하는 것도 가능하며, 상기 열균착층(4)은 접착면에 해당하는 것으로, 상온에서 점착성을 갖는 일반 접착층과는 다르게, 열을 가하는 경우 접착성을 갖는 것이 바람직하다. 통상적으로 사용하는 핫멜트 수지를 사용하는 것도 가능하며, 보다 바람직하게는 폴리에틸렌비닐아세테이트수지 또는 아크릴수지를 사용하는 것이 투명도장면과의 접착성이 우수하므로 바람직하다.
본 발명에 따른 부분도장 방법을 사용하는 경우 인쇄층이 투명도장을 한 기재면에 완벽하게 전사되어 함침되므로 단차가 발생하지 않으며, 굴곡진 면에도 쉽게 전사시킬 수 있으며, 용제를 사용해도 지워지지 않는 특징이 있는 신규한 부분도장을 할 수 있다.
또한 본 발명에 따른 전사필름은 투명도장면에 완벽하게 전사되는 특징이 있으며, 홀로그램 등으로 입체 효과를 부여할 수 있는 효과가 있다.
도 1은 본 발명의 부분 도장에 사용되는 전사필름의 일예를 나타낸 단면도이다.
도 2는 본 발명의 부분 도장에 사용되는 전사필름의 또 다른 일예를 나타낸 단면도이다.
- 도면의 주요부분에 대한 설명 -
1 - 기재필름층 2 - 보호층
3 - 인쇄층 4 - 열균착층
Claims (13)
1) 기재면에 투명도장을 하고 예비 건조시키는 단계;
2) 상기 예비건조 후 전사필름을 부착시키기 전에 부착면을 40 ~ 70 ℃로 가열하거나 유기용제를 스프레이하는 단계;
3) 기재필름층, 인쇄층의 순으로 적층된 전사필름의 인쇄층면을 상기 투명도장면에 부착시키는 단계;
4) 상기 부착시킨 전사필름과 투명도장면을 함께 50 ~ 200 ℃로 열처리하는 단계;
5) 전사필름과 투명도장면을 냉각시킨 후 상기 전사필름의 기재필름층을 제거시키는 단계;
를 포함하는 것을 특징으로 하는 부분도장 방법.
제 1항에 있어서,
상기 기재면은 금속면, 목재면, 플라스틱면에서 선택되는 어느 하나인 것을 특징으로 하는 부분도장 방법.
제 2항에 있어서,
상기 금속면은 자동차외장, 냉장고, 세탁기, 전자렌지, 에어컨, 철재가구, 알루미늄제품, 엘리베이터에서 선택되는 어느 하나인 것을 특징으로 하는 부분도장 방법.
삭제
제 1항에 있어서,
상기 투명도장은 아미노알키드수지, 열경화성아크릴수지, 멜라민 수지, 불소수지에서 선택되는 어느 하나 이상인 것을 특징으로 하는 부분도장 방법.
제 1항에 있어서,
상기 투명도장에 안료를 첨가시키는 것을 특징으로 하는 부분도장 방법.
제 1항에 있어서,
상기 인쇄층은 홀로그램박막인 것을 특징으로 하는 부분도장 방법.
제 7항에 있어서,
상기 인쇄층은 0.1 ~ 150 ㎛의 두께의 박막형태인 것을 특징으로 하는 부분도장 방법.
제 1항에 있어서,
상기 전사필름은 인쇄층의 상부에 열가소성수지로 된 열균착층을 더 구비하는 것을 특징으로 하는 부분도장 방법.
제 9항에 있어서,
상기 열균착층은 폴리에틸렌비닐아세테이트수지 또는 아크릴수지인 것을 특징으로 하는 부분도장 방법.
제 1항에 있어서,
상기 4)단계의 열처리 시 고무자석판 또는 고무판을 전사필름의 일부 또는 전면을 수용하도록 붙인 후 간접가열시키는 것을 특징으로 하는 부분도장 방법.
제 1항에 있어서,
상기 5)단계 후 투명도장을 추가로 수행하는 것을 특징으로 하는 부분도장 방법.
제 1항 내지 제 3항 또는 제 5항 내지 제 12항에서 선택되는 어느 한 항에 있어서,
상기 기재필름층과 인쇄층의 사이에 아미노알키드계, 열경화성 아크릴계, 에폭시계, 우레탄계에서 선택되는 어느 하나이상의 열경화성수지로 된 보호층이 구비되는 것을 특징으로 하는 부분도장 방법.