KR100425949B1 - 광기록매체 - Google Patents

광기록매체 Download PDF

Info

Publication number
KR100425949B1
KR100425949B1 KR10-2001-0051890A KR20010051890A KR100425949B1 KR 100425949 B1 KR100425949 B1 KR 100425949B1 KR 20010051890 A KR20010051890 A KR 20010051890A KR 100425949 B1 KR100425949 B1 KR 100425949B1
Authority
KR
South Korea
Prior art keywords
substrate
adhesive layer
recording medium
optical recording
layer
Prior art date
Application number
KR10-2001-0051890A
Other languages
English (en)
Other versions
KR20030018272A (ko
Inventor
민경선
마명근
허영재
Original Assignee
주식회사 비올디벨로퍼즈
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 비올디벨로퍼즈 filed Critical 주식회사 비올디벨로퍼즈
Priority to KR10-2001-0051890A priority Critical patent/KR100425949B1/ko
Priority to JP2003522923A priority patent/JP2005501363A/ja
Priority to EP01974906A priority patent/EP1421581A1/en
Priority to PCT/KR2001/001543 priority patent/WO2003019549A1/en
Priority to CNA018237460A priority patent/CN1559069A/zh
Priority to US10/488,046 priority patent/US20050118417A1/en
Publication of KR20030018272A publication Critical patent/KR20030018272A/ko
Application granted granted Critical
Publication of KR100425949B1 publication Critical patent/KR100425949B1/ko

Abstract

본 발명은 보호막없이 2장의 기판을 자외선 경화가 가능한 접착제로 접착시켜 줌으로써 공정을 단순화하고, 우수한 특성을 얻을 수 있는 광기록매체에 관한 것이다.
본 발명의 광기록매체는 안내골이 형성되어 있고 그 위에 색소층 및 반사층이 적층되어 있는 기판과 더미기판을 접착시켜 주기 위한 접착층을 구비한다.
상기 접착층은 자외선에 의해 경화가능하며, 10-80㎛ 두께를 갖는다. 접착층을 위한 접착체는 경화후 유리전이온도 30℃ 이상, 경화시 수축율 7.0%이내, 경화후 경도가 H이상인 특성을 갖는다. 상기 광기록매체는 상기 디스크 내측과 외측에 상기 기판과 더미기판이 접착층을 통해 직접 접착되는 접착강화영역을 구비한다.
상기 더미 디스크는 그의 상면에 반사막이 있을 수도 있으며 상기 기판상의 반사막과 접착층에 의해 접착되며, 상기 반사막은 Ag, Au, Al, Cu 또는 이들의 합금으로 이루어진다. 상기 색소층은 시아닌계 색소, 헤미시아닌계 색소, 아조계 색소, 트리페닐메탄계 색소 또는 이들의 혼합물로 이루어진 군으로부터 선택된다.

Description

광기록매체{Optical recording medium}
본 발명은 광기록매체에 관한 것으로서, 보다 상세하게는 공정이 단순화되고, 우수한 특성을 얻을 수 있는 DVD-R 또는 DVD+R(Digital Versatile Disc -/+Recordable)디스크에 관한 것이다.
DVD-R/+R 디스크는 1회에 한하여 기록이 가능한 추기형 디스크로 도 1과 같은 단면구조를 갖는다. 즉, 종래의 광기록매체(100)인 DVD-R/+R 디스크는 기록 및 재생시 레이저광을 안내하기 위한 안내골(도면상에는 도시되지 않음)을 구비한 0.6mm 두께의 PC(polycarbonate)기판(10)상에 색소층(11), 반사막(12) 및 보호막(13)이 순차 적층된 디스크(110)를 더미 디스크(120)와 접착층(14)을 통해 접착시켜 제작한다. 이때, 더미 디스크(120)는 더미기판(15)상에 반사막(16), 색소층(17) 및 보호막(18)이 형성되어 제1디스크와 동일구조를 갖거나, 색소층 또는 색소층과 반사막이 없는 구조를 갖는다.
상기 색소층(11), (17)은 기판(10), (15)상에 유기색소를 코팅하여 형성하는 것으로서, 기록광을 흡수하여 발열하므로 색소자체의 분해 또는 변형 및 기판의 변형을 유도하는 기록층의 역할을 한다. 상기 반사막(12), (16)은 기록 및 재생광을 반사시키기 위한 것으로, 기록신호의 변조도가 광검출기를 통해 검출되도록 충분한 광량을 제공하는 역할을 한다.
또한, 상기 보호막(13), (18)은 상기 반사막(12), (16)을 보호하기 위한 것으로, 기록시 반사막(12), (16)의 변형을 방지하고 접착층(14)으로부터 반사막(12), (16)을 분리시켜 색소층 또는 반사막의 화학적 손상을 방지하는 역할을 한다. 상기 접착층(14)은 0.6mm두께의 기판 또는 디스크 두장을 접착시켜, 1.2mm 두께를 갖는 DVD-R/+R 디스크의 광기록매체(100)을 제작하기 위한 것으로, 강한 접착력이 요구된다.
두 장의 디스크(110), (120)를 접착하는 방식으로는 접착제의 종류 및 접착방식에 따라 고용융(high melt) 접착법, 카티온 UV 접착제(cationic UV adhesive)를 사용한 스크린 인쇄방법 그리고 자유라디칼 UV 접착제(free radical UV adhesive)를 스핀코팅하는 방법이 이용되고 있다. 두 장의 디스크(110), (120)를 접착층(13)을 통해 접착할 때, 고려할 요소는 다음과 같다.
첫번 째 고려해야할 요소는 내습성 및 내열성이다. 경화후 반응하지 않은 소량의 모노머가 보호막 및 반사막을 손상시켜 디스크 특성을 손상시킬 수 있으며, 습기 및 열에 의해 손상이 가속화될 수 있다. 습기와 열에 의한 손상을 방지하기 위하여 반사막에 대한 보호기능이 뛰어난 보호막을 반사막위에 형성하여야 하는데, 이를 위하여 특수재질의 반사막을 사용하거나 또는 유기색소층(11), (13)에 안정한 색소를 사용하는 등의 다양한 방법이 사용되고 있다.
두번 째 고려해야할 요소는 접착성이다. 두 장의 디스크가 기계적 충격에 안정하기 위해서는 충분한 접착력을 가져야 한다.
상기한 바와같은 특성을 고려하여, 일본특허 특개평10-27383의 광정보매체는 기판/보호막/접착층/보호막/기판의 순서로 형성하여 색소층이 없는 영역을 확보함으로써 접착력을 갖도록 제작되었으며, 내충격성 및 내습성을 개선하여 시도하였다.
또한, 일본특허 특개평 10-106037의 광정보매체는 도 1과 같은 디스크구조에서 색소층과 반사층의 외측단부를 안쪽으로 후퇴시켜 노출면을 만들고, 이 노출면에서 양쪽기판의 측면에 이르는 영역에 대해 표면가공을 실시하고, 상기 영역에 보호층을 접합하는 방법을 사용하기도 하였다.
그러나 종래의 모든 DVD-R/+R 다스크에서는 도 1에 도시된 바와같이, 두 장의 디스크를 접착하기 위하여 보호층(13), (18)을 필히 사용하였다. 디스크를 보호하기 위한 보호층은 UV 경화수지를 코팅한 다음 UV광을 조사하여 경화시켜 주어야 하기 하기 때문에, 제조공정이 복잡하고 UV경화시 열에 의한 디스크의 휨이 발생하는 등의 문제가 있다.
본 발명은 상기한 바와같은 종래 기술의 문제점을 해결하기 위한 것으로서, 보호층없이 두 장의 디스크를 접착시켜도 기계적 충격, 내충격성 및 내구성이 우수한 DVD-R/+R를 얻을 수 있는, 제조공정이 단순하고 우수한 특성을 갖는 광기록매체를 제공하는 데 그 목적이 있다.
도 1은 종래의 광기록매체의 단면구조도,
도 2는 본 발명의 일실시예에 따른 광기록매체의 단면구조도,
도 3은 본 발명의 다른 실시예에 따른 광기록매체의 단면구조도,
도 4는 본 발명의 광기록매체의 제조방법을 설명하기 위한 단면구조도,
도 5는 본 발명의 광기록매체의 제조방법을 설명하기 위한 또 다른 단면구조도,
*도면의 주요부분에 대한 부호의 설명*
20, 30, 40, 50 : 기판 25, 35, 45, 55 : 더미기판
21, 31, 41, 51 : 색소층 22, 32, 34, 42, 52 : 반사막
23, 33, 43, 53 : 접착층
200, 300, 400, 500 : 광기록매체 210, 310 : 디스크
이와 같은 목적을 달성하기 위한 본 발명은 안내골이 형성되어 있고 그 위에 색소층과 반사막이 적층되어 있는 기판과 더미기판을 접착시켜 주기 위한 접착층을 구비하는 광기록매체를 제공하는 것을 특징으로 한다.
상기 접착층은 자외선에 의해 경화가능하며, 상기 접착층은 10-80㎛ 두께를 갖는다. 접착층을 위한 접착체는 경화후 유리전이온도 30℃ 이상, 경화시 수축율 7.0%이내, 경화후 경도가 H이상인 특성을 갖는다.
상기 광기록매체는 상기 디스크 내측과 외측에 상기 기판과 더미기판이 접착층을 통해 직접 접착되는 접착강화영역을 구비한다.
상기 더미 디스크는 그의 상면에 특수 목적으로 얇은 반사막이 있을수도 있으며 상기 기판상의 반사막과 접착층에 의해 접착되며, 상기 반사막은 Ag, Au, Al, Cu 또는 이들의 합금으로 이루어진다.
상기 색소층은 시아닌계 색소, 헤미시아닌계 색소, 아조계 색소, 트리페닐메탄계 색소 또는 이들의 혼합물로 이루어진 군으로부터 선택된다.
이하, 본 발명을 보다 구체적으로 설명하기 위하여 본 발명에 따른 일 실시예를 첨부 도면을 참조하면서 보다 상세하게 설명하고자 한다.
도 2는 본 발명의 일실시예에 따른 광기록매체의 단면구조를 나타낸 것이다. 도 2를 참조하면, 본 발명의 일실시예에 따른 광기록매체(200)는 기판(20)상에 색소층(21) 및 반사막(22)이 형성된 디스크(210)를 더미기판(25)과 접착층(23)을 통해 접착시켜 제작된 DVD-R/+R 디스크이다.
상기 기판(20)은 기록 또는 재생시 광을 안내하기 위한 안내골(pregroove) (도면상에는 도시되지않음)이 형성되어 있으며, 스탬퍼를 이용하여 사출하여 제작한다. 상기 기판(20)은 그의 두께가 0.5 내지 0.7mm이며, 폴리카보네이트, 폴리메틸메타크릴레이트, 에폭시수지, 폴리에스테르, 비정질 폴리올레핀으로 이루어진 군에서 선택되는 물질로 이루어진다.
상기 색소층(21)은 유기색소를 유기용매에 용해시키고 기판(20)상에 스핀코팅방법으로 도포한다. 상기 색소층(21)은 시아닌(cyanine)계 색소, 헤미시아닌(hemicyanine)계 색소, 아조(azo)계 색소，트리페닐메탄(triphenylmethane)계 색소 또는 이들의 혼합물로 이루어진 군으로부터 선택되는 것이 바람직하다.
상기 반사막(22)은 건조된 색소층(21)상에 금속박막을 스퍼터링방법으로 60-100nm의 두께로 형성한다. 상기 반사막(22)을 위한 금속박막으로는 Au, Ag, Al, Cu 및 이들의 합금막이 사용된다.
기판(20)상에 색소층(21)과 반사막(22)이 순차 적층된 디스크(210)와 더미기판(25)을 접착시키기 위한 접착층(23)는 상기 기판(20)상에 형성된 반사막(22)상에 접착제를 도포하고, 그위에 더미기판(25)을 덮은 다음 고속회전시켜 스핀코팅하고 자외선을 조사하여 경화시킴으로써 디스크(210)와 더미기판(25)을 접착시킨다. 이때, 주변온도, 접착제의 점도 및 스핀코팅시 회전속도에 의해 접착층(23)의 두께가 조절된다.
상기 접착층(23)은 다음과 같은 특성을 가져야 한다.
1. 점도(viscosity) : 25℃에서 300 - 900 cps
2. 경화후 유리 전이온도(Tg after curing) : 30℃ 이상
3. 경화시 수축율(shrinkage on curing) : 7.0% 이내
4. 경화후 경도(hardness) : H 이상
5. 경화후 모노머잔량 : 10%이내
본 발명에서는 접착제 도포공정을 간단히 하기 위해 스핀코팅방법을 사용하는데, 상기 점도는 충분한 접착층 두께를 갖기 위한 점도로서, 300cps 보다 작으면 접착층 두께가 작아 접착력이 작은 문제가 있고, 900cps 보다 크면 스핀코팅의 어려움이 있다.
경화후 유리전이온도는 기록시 반사막의 변형을 방지하여 DVD-R/+R 디스크의 기록특성을 우수하게 하며 DVD-R/+R 디스크의 기록후 내열성을 위한 것으로서, 유리전이온도가 30℃보다 낮으면 기록특성이 저하되고, 내열성이 열약할 가능성이 있다.
본 발명의 광기록매체인 DVD-R/+R 디스크(200)에 있어서, 각층간 계면중 계면접착력이 가장 약한 곳은 색소층(21)과 반사막(22)의 계면으로서, 반사막(22)상의 접착층(23)이 자외선 경화시 크게 수축하면 색소층(21)과 반사막(22)의 계면접착력이 약화되어 기록특성이 저하되거나, 기계적 충격에 의해 이 계면에서 디스크(200)가 분리될 수 있다. 따라서, 접착제의 자외선 경화시 접착층(23)의 수축에 의한 색소층(21)과 반사막(22)의 계면 접착력의 손상을 줄이기 위하여, 접착제의 수축율이 7.0% 이하인 것이 바람직하다.
경화후 경도는 레이저로 기록시 기록특성을 위한 것으로서, 경도가 H보다 작으면 기록시 기록특성이 저하된다. 경화후 모노머의 잔량은 내화학성을 위한 것으로서, 잔량이 10%이상일 경우 반사막(22) 및 색소층(21)을 손상시켜 디스크의 내구성이 약화될 수 있다. 보호층(23)의 두께는 약 10-80㎛가 적당하며 이보다 작을 경우 접착력이 약화되며, 두꺼울 경우 경화시 수축력에 의해 반사막(21)과 색소층(22)의 계면이 손상될 수 있다.
도 3은 본 발명의 다른 실시예에 따른 광기록매체(300)의 단면구조를 도시한 것이다. 다른 실시예에 따른 광기록매체(300)에 있어서, 디스크(300)의 구조는 도 2의 일 실시예에 따른 디스크(200)와 그 구조가 동일하다. 다만, 일 실시예의 광기록매체(200)에서는 더미 디스크(25)가 직접 디스크(200)에 접착층(23)을 통해 접착되는 구조이지만, 다른 실시예의 광기록매체(300)에서는 더미기판(35)상에 반사막(34)이 형성되어 디스크(310)와 접착층(33)을 통해 접착되는 구조를 갖는다.
상기 더미기판(35)에 형성된 반사막(34)으로 Au, Ag, Cu, Al 또는 이들의 합금을 사용한다.
도 2 및 도 3에 도시된 바와같은 본 발명의 광기록매체(200), (300)인 DVD-R/+R 디스크에 따르면, 보호층없이 디스크와 더미기판을 접착시켜 줌으로써, 보호층의 제조를 위한 스핀코팅 및 경화단계가 생략되어 다음과 같은 장점이 있다.
첫째, 광기록매체를 제조하기 위한 생산설비의 필요면적을 줄일 수 있다. 둘째, 제조공정이 간단하여 생산수율이 향상시킬 수 있다. 셋째, 보호층의 경화시 자외선 조사에 의한 디스크 휘어짐의 원인을 제거하여 디스크 특성을 향상시킬수 있다. 넷째, 보호층을 사용하지 않으므로 제조비가 저렴하다. 다섯째, 자외선 경화수지로 기판과 디스크를 접착하므로 매우 접착력이 뛰어나며, 내열성이 우수한 접착력의 사용에 따라 우수한 내구성을 얻을 수 있다.
상기한 바와같은 구조를 갖는 본 발명의 광기록매체를 제조하는 방법을 설명하면 다음과 같다.
실시예 1
도 4를 참조하여 본 발명의 실시예 1에 따른 광기록매체의 제조방법을 설명하면 다음과 같다.
먼저, 트랙피치 0.74㎛, 깊이 150nm, 폭 350nm 의 안내골을 갖는 두께 0.6mm폴리카보네이트기판(40)을 제공한다. 상기 기판(40)상에 일본 하야시바라(Hayashibara)사의 시아닌계 색소인 NK 4499를 0.25g/10ml TFP 용액을 사용하여 3000rpm으로 스핀코팅하여 유기색소층(41)을 형성한다.
유기색소층(41)을 형성한 다음, 80℃의 열풍건조기에서 20분 건조한 후 은(Ag)을 스퍼터링법으로 약 100nm의 두께로 증착하여 반사막(42)을 형성한다.
상기 반사막(42)상에 DSM 사의 디솔라이트(desolite) 660-006 UV 접착제(점도 300cps, 유리전이온도 32℃, 수축율 5.4%, 접착후 경도 H)를 도포하고, 0.6mm두께의 더미기판(45)을 덮고 2000rpm으로 스핀코팅한다. 그후 자외선을 조사하여 접착제를 경화시키면, 더미디스크(45)와 기판(40)이 접착층(44)에 의해 접착되어 본 발명의 광기록매체인 DVD-R/+R디스크(400)가 제조된다. 이때, 접착층(43)의 두께는 약 25㎛이다.
본 발명에서는, 접착층(43)의 접착력을 강화시키기 위해서, 기판(40)상에 코팅된 색소층(41)중 디스크 외주부위의 색소층은 식각하여 제거하고, 반사막(42)을 위한 금속박막이 색소층 전체를 덮을 수 있도록 형성한다. 또한, 접착층(43)이 반사막(42) 전체를 덮도록 형성하여, 기판(40)과 더미기판(45)이 접착층(43)에 의해 직접 접착되는 접착강화영역(47)이 디스크 내측과 외측에 모두 존재하여 접착력을 강화시킨다
실시예 1에 따라 제조된 DVD-R/+R 디스크(400)를 DVD-R 레코더(recorder) 예를 들어 파이오니어사의 DVR-2000 으로 동영상을 기록하여 DVD 재생기, 예를 들어 엘지의 DVD 3030, 삼성의 DVD 909, 또는 파이오니어사의 DV-535K 로 재생한 결과,모두 재생가능하였다. 기록특성을 펄스텍(pulstec.)사의 DVD 평가설비인 DDU-1000 시스템으로 평가시 신호의 균일성을 나타내는 지터가 7.8%, 반사율 48.0%, 에러율(PI) 80 으로 국제표준규격을 만족하였다.
또한, 상기 디스크(400)를 60℃, 80% 상대습도에서 6일동안 가혹후 기록특성을 측정한 결과, 지터가 8.0%, 반사율 48.5%, PI는 90으로 크게 변화되지 않는 특성을 나타내어 내열성 및 내습성이 우수함으로 보여주었다. 게다가, 내충격실험을 위해 10개의 디스크를 1.5m 높이에서 수직낙하하여 디스크의 쪼개짐을 검사한 결과 10 디스크모두 변화가 없어 내충격성이 우수함을 보여 주었다.
실시예 2
실시예 2에 따른 디스크 제조방법은 접착제를 MK 1010 (자체제조, 점도 650cps, 유리전이온도 125℃, 수축율 6.3%, 접착후 경도 H)을 사용하고 반사막으로 Ag-Cu-Au의 합금을 사용한 것 이외에는 실시예 1과 동일방법으로 디스크를 제조하여 평가하였다. 이때, 접착층의 두께는 약 40㎛이었다.
실시예 2에 따라 제조된 디스크의 기록특성은 지터 7.5%, 반사율 48.5%, PI는 50으로 재생성에 문제가 없었으며, 60℃, 80%의 상대습도에서 6일동안 가혹후 지터가 7.8%, 반사율 49.0%, PI는 60으로 우수한 내열성 및 내습성을 나타내었다. 또한, 내충격실험을 위해 1.5m 높이에서 수직낙하하여 디스크의 쪼개짐을 검사한 결과 10개의 디스크 모두 변화가 없어 내충격성이 우수함을 보여 주었다.
비교예 1
비교예 1에 따른 디스크의 제조방법은 반사막(42)위에 보호막으로 소니 케마칼사의 SK 3200을 도포한 후 자외선 경화하여 보호막을 제조후 접착제를 사용하여 더미디스크와 접착한 것을 제외하고는 실시예 2와 동일하다. 디스크의 기록특성은 지터 8%, 반사율 48.5%, PI는 100으로 재생성에 문제가 없었으며, 60℃, 80% 상대습도에서 6일동안 가혹후 지터 8.5%, 반사율 49%, PI 150으로 보호층이 없는 경우보다 약한 내열성, 내습성을 나타내었다. 그러나 내충격실험은 10 디스크 모두 변화가 없어 우수한 접착력을 나타내었다. 실시예 2와 비교시, 보호층의 유무에 관계없이 유사한 특성을 보여주었다.
비교예 2
비교예 2에 따른 디스크 제조방법은 접착제로 소니 케미칼사의 SK 6000(점도 300cps, 유리전이온도 89℃, 수축율 8.3%, 접착후 경도 1H)를 사용하고, 반사막(42)위에 보호층으로 소니 케미칼사의 SK 3200을 도포한 후 자외선 경화한 것을 제외하고는 실시예 2와 동일방법으로 제조평가하였다.
디스크의 기록특성은 지터 8.4%, 반사율 48.5%, PI는 120으로 실시예 2보다 특성이 저하되었다. 60℃, 80% 상대습도에서 6일동안 가혹후 지터 10.0%, 반사율 53.0%, PI는 500으로, 실시예 2보다 내열 내습성이 약한 것으로 보여 주었다. 내충격실험에서 10 디스크중 2개의 디스크가 분리되어 내충격성도 약함을 보여주어 자외선 경화시 큰 수축에 의한 색소층(41)와 반사막(42) 계면의 힘이 약화되었음을 간접적으로 보여 주었다.
비교예 3
비교예 3에 따른 제조방법은 도 5에 도시된 바와같이, 접착제 도포시 도 5에도시된 바와같이 내측의 접착강화영역없이 외측의 접착강화영역만을 구비한 디스크를 제조하는 것이외에는 실시예 2와 동일하다.
디스크의 기록특성은 지터 7.5%, 반사율 48.5%, PI는 50으로 실시예 2와 동일하였으나, 60℃, 80% 상대습도에서 6일동안 가혹후 디스크 내측에서 지터 10.8%, 반사율 52.0%, PI는 600으로 특성이 매우 악화되어 내열, 내습성에 문제가 있음을 보여주었다. 또, 내충격실험을 위해 1.5m높이에서 수직낙하여 디스크의 쪼개짐을 검사한 결과 10 디스크중 4개의 디스크가 쪼개지는 특성을 나타내어 내측과 외측의 접착강화영역의 필요성을 보여주었다.
비교예 4
비교예 4에 따른 디스크제조방법은 접착제로 디솔라이트 650-002(점도 10cps, 유리전이온도 26℃, 수축율 7.0)을 사용하여 디스크를 접착하고, 접착제 두께가 8㎛ 인 것을 제외하고는 실시예 2와 동일방법으로 제조하였다.
디스크의 기록특성은 지터 8.8%, 반사율 48.5%, PI는 200으로 실시예 2보다 기록특성이 저하되었으며, 또 내충격실험을 위해 높이 1.5m높이에서 수직낙하하여 디스크의 쪼개짐을 검사한 결과 10 디스크중에서 7개의 디스크가 쪼개지는 특성을 나타내어 접착층의 두께가 약하여 접착력이 약함을 보여주었다.
상기한 바와같은 본 발명의 광기록매체에 따르면, 보호막없이 2장의 기판을 자외선에 의해 경화가 가능한 접착제를 사용하여 접착시켜 줌으로써, 공정을 단순화하고 우수한 특성을 얻을 수 있다. 또한, 디스크의 내외측에 2장의 기판을 직접접착층에 의해 접착시키는 접착강화영역을 형성하여 접착력을 향상시킬 수 있는 이점이 있다.
상기에서는 본 발명의 바람직한 실시예를 참조하여 설명하였지만, 해당 기술 분야의 숙련된 당업자는 하기의 특허 청구의 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.

Claims (7)

  1. 안내골이 형성되어 있는 기판과;
    내측 및 외측을 제외한 기판상에 형성된 색소층과;
    내측 및 외측을 제외한 기판상에, 상기 색소층 전체를 덮도록 형성된 반사막과;
    더미기판과;
    상기 기판과 더미기판을 접착시켜 주기 위한 접착층을 구비하며,
    상기 기판은 상기 디스크 내측과 외측에 상기 기판과 더미기판이 접착층을 통해 직접 접착시켜 주기위한 접착강화영역을 더 구비하고,
    상기 접착층은 자외선에 의해 경화가능하며, 접착층을 위한 접착체는 경화후 유리전이온도 30℃ 이상, 경화시 수축율 7.0%이내, 경화후 경도가 1H이상인 특성을 갖는 것을 특징으로 하는 광기록매체.
  2. 삭제
  3. 삭제
  4. 제 1 항에 있어서, 상기 더미 디스크는 그의 상면에 반사막이 형성되어 상기 기판상의 반사막과 접착층에 의해 접착되는 것을 특징으로 하는 광기록매체.
  5. 제 1 항에 있어서, 상기 반사막은 Ag, Au, Al, Cu 또는 이들의 합금으로 이루어지는 것을 특징으로 하는 광기록매체.
  6. 제 1 항에 있어서, 상기 색소층은 시아닌계 색소, 헤미시아닌계 색소, 아조계 색소, 트리페닐메탄계 색소 또는 이들의 혼합물로 이루어진 군으로부터 선택되는 것을 특징으로 하는 광기록매체.
  7. 제 1 항에 있어서, 상기 접착층은 10-80㎛ 두께를 갖는 것을 특징으로 하는 광기록매체.
KR10-2001-0051890A 2001-08-27 2001-08-27 광기록매체 KR100425949B1 (ko)