KR100410725B1 - 등속조인트용 그리스조성물 - Google Patents

등속조인트용 그리스조성물 Download PDF

Info

Publication number
KR100410725B1
KR100410725B1 KR1019950031601A KR19950031601A KR100410725B1 KR 100410725 B1 KR100410725 B1 KR 100410725B1 KR 1019950031601 A KR1019950031601 A KR 1019950031601A KR 19950031601 A KR19950031601 A KR 19950031601A KR 100410725 B1 KR100410725 B1 KR 100410725B1
Authority
KR
South Korea
Prior art keywords
constant velocity
grease composition
weight
carbon atoms
velocity joint
Prior art date
Application number
KR1019950031601A
Other languages
English (en)
Other versions
KR960014311A (ko
Inventor
하따케야마꼬
곤도신야
Original Assignee
교도유시 가부시끼가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 교도유시 가부시끼가이샤 filed Critical 교도유시 가부시끼가이샤
Publication of KR960014311A publication Critical patent/KR960014311A/ko
Application granted granted Critical
Publication of KR100410725B1 publication Critical patent/KR100410725B1/ko

Abstract

본 발명은 등속조인트용 그리스 조성물에 관한 것으로서, 더욱 상세하게는 자동차에 사용되는 등속조인트 특히 트리포드형(tripod type) 등속조인트에 유용한 그리스 조성물에 관한 것이다.

Description

등속조인트용 그리스 조성물
본 발명은 등속조인트용 그리스 조성물에 관한 것으로서, 더욱 상세하게는 자동차에 사용되는 등속조인트 특히 트리포드형(tripod type) 등속조인트에 유용한 그리스 조성물에 관한 것이다.
등속조인트(constant velocity joint)는 일반 자동차의 최종 감속장치에서부터 차축(車軸)으로 구동력(驅動力)을 전달하는 역활을 하는 회전축(回轉軸)에 사용되는 것으로서, 특히 트리포드형(tripod type)으로 불리어지는 등속조인트는 3개의 축을 갖는 트리포드(tripod)와 그리고 각각의 축에 여러개의 니들(needle)을 끼운 3개의 로울러와 이들 로울러를 안내하는 3개의 원형통 그루브(cylindrical groove)를 갖는 외측 레이스(outer race)로 이루어져 있다. 트리포드형 등속조인트에 있어서, 특정 각도조건하에서 조인트를 회전시켰을때 구성부품들은 복잡한 롤링(rolling) 및 슬라이딩(sliding) 운동을 하는 바, 조인트 회전수의 3배 주기(period)에 해당하는 슬라이드 저항(slide resistance) 즉, 회전3차축력(軸力)이 축방향으로 생기며, 이에 의해 자동차의 진동이 야기되는 것으로 알려져 있다.
종래에는 트리포드형 등속조인트용 윤활그리스로서 칼슘착비누(calciumcomplex soap)를 증감제(thickening agent)로 함유하는 그리스 ; 또는 리튬비누(lithium soap)를 증감제로 하고, 유화유지(sulfurized fats and oils), 트리클레실 포스페이트 및 아연 디알킬디티오포스페이트 중에서 선택된 황-인계 극압제를 함유한 그리스 등을 사용하였다. 이들 그리스는 윤활유를 기본 오일로 사용하였다. 그러나 상기 종래의 그리스를 사용할 경우 회전3차축력이 발생하는데, 이는 트리포드형 등속조인트 구조의 복잡한 롤링(rolling) 및 슬라이딩(sliding) 운동에 의해 생긴 내부 마찰에 의한 것이다.
따라서, 본 발명은 종래의 그리스보다 낮은 마찰계수를 갖고 등속조인트의 내부 마찰을 감소시켜 등속조인트의 진동운동을 감소시킬 수 있는 새로운 등속조인트용 그리스 조성물을 제공하는데 그 목적이 있다.
또한, 본 발명은 트리포드형 등속조인트를 효과적으로 윤활시켜 마찰력을 효율적으로 감소시키고 어떠한 진동운동도 발생하지 않도록 효율적으로 억제할 수 있는 트리포드형 등속조인트용 그리스 조성물을 제공하는데 또 다른 목적이 있다.
이에 본 발명의 발명자들은 등속조인트 특히, 트리포드형 등속조인트의 마찰을 감소시키고 어떠한 진동운동도 방지할 수 있는 그리스 조성물을 개발하기 위해 연구 노력하였으며, 그리스의 성능평가는 SRV(Schwingungs Reibung und Verschleiss) 시험기로 호칭되고 있는 진동마찰마모 시험기를 사용하였다.
그 결과 본 발명자들은 특정 진동 및 마찰 조건하에서 SRV 측정기에 의해 측정한 마찰계수와 진동발생원으로서 실제 적용되고 있는 등속조인트에 의해 발생된 진동사이에는 일정한 상관관계가 있음을 발견하였다. 또한, 본 발명자들은 상기 관계를 고려하여 증감제(리튬비누 또는 리튬착비누)와 극압제 등의 첨가제의 배합비율의 변화에 대해 연구하였고, 또한 선택된 각 성분 화합물의 특정 배합비율에 의해 상기 본 발명의 목적을 달성할 수 있음을 알게됨으로써 본 발명을 완성하였다.
따라서, 본 발명은 (a) 기본유 ; (b) 리튬비누 및 리튬착비누 중에서 선택된 리튬 함유 증감제 ; (c) 몰리브데늄 디티오포스페이트 및 몰리브데늄 디티오카바메이트 중에서 선택된 유기 몰리브데늄 화합물 ; (d) 아연 디티오포스페이트 ; (e) 금속을 함유 하지않는 황-인계 극압제 ; 그리고 (f) 산화왁스의 칼슘염, 석유술폰산의 칼슘염 및 알킬 방향족술폰산의 칼슘염 중에서 선택된 칼슘염으로 이루어진 등속조인트용 그리스 조성물에 관한 것이다.
본 발명의 그리스 조성물은 상기 성분들이 특정 배합 비율로 이루어짐으로써 마찰계수를 감소시키고, 또한 실제 조인트에 그리스 조성물을 적용하여 진동 시험기로 측정한 결과 회전3차축력을 현저하게 감소시킴을 알 수 있었다.
이하, 본 발명을 상세히 설명하면 다음과 같다.
본 발명의 등속조인트용 그리스 조성물은 성분(a)로서 기본오일을 사용하는 바, 그 종류로는 광물유, 탄화수소계 합성유, 에스테르계 합성유, 에테르계 합성유 및 이들의 혼합물 중에서 선택된 윤활유를 사용함이 바람직하지만 본 발명이 이에 의해 한정되는 것은 아니다.
성분(b)로서 일반적인 용도로 광범위하게 사용되고 있는 리튬비누 등의 리튬함유 증감제를 사용하는 바, 그 종류로는 12-히드록시스테아르산 리튬염 및 스테아르산 리튬염 등의 리튬염(lithium salt), 그리고 12-히드록시스테아르산 리튬비누및 이염기산(예를들면 아젤라산) 리튬비누 등의 리튬착비누(lithium complex soap) 중에서 선택된 것이다. 내열성이 요구되는 그리스 조성물의 경우 리튬착비누를 사용하는 것이 바람직하다.
성분(c)로서 몰리브데늄 디티오포스페이트, 보다 바람직하기로는 다음 구조식(Ⅰ)로 표시되는 유기 몰리브데늄 화합물을 사용한다.
상기식에서, R1, R2, R3및 R4는 각각 같거나 다른 것으로서 탄소원자수 1 ~ 24 바람직하기로는 3 ∼ 20의 일차 또는 이차 알킬기, 탄소원자수 6 ∼ 30 바람직하기로는 8 ∼ 18의 아릴기, 또는 몰리브데늄 디티오카바메이트 바람직하기로는 다음 구조식(Ⅱ)로 표시되는 화합물이다.
상기식에서, R5및 R6은 각각 같거나 다른 것으로서 탄소원자수 1 ∼ 24 바람직하기로는 3 ∼ 18의 알킬기이고 ; m은 0 ∼ 3이고, n은 4 ∼ 1이며, 단 m + n = 4이다.
상기 유기 몰리브데늄 화합물은 단독 또는 2종 이상을 함께 사용할 수도 있다.
성분(d)로서 다음 구조식(Ⅲ)으로 표시되는 아연 디티오포스페이트를 극압제로 사용한다.
상기식에서, R7, R8, R9및 R10은 각각 같거나 다른 것으로서 탄소원자수 1 ∼ 24 바람직하기로는 3 ∼ 20 의 알킬기, 또는 탄소원자수 6 ∼ 30 바람직하기로는 8 ~ 18의 아릴기이다. 이때, 알킬기는 일차 또는 이차 알킬기이며, 특히 R7, R8, R9및 R10각각이 탄소원자수 3 ∼ 8의 일차 또는 이차 알킬기일때 뛰어난 효과를 나타낼 수 있다.
성분(e)로서 금속을 함유하지 않는 황-인계 극압제를 사용하는 바, 이는 15 ~ 35 중량%의 황(S)성분과 0.5 ~ 3 중량%의 인(P)성분으로 이루어져 있고, 황과 인의 성분함량비를 적절히 조절하면 내마모효과(wear-resistant effect) 및 시저억제효과(seizure-inhibitory effect)을 얻을 수 있다. 만약 황 성분의 함량이 상기의 범위를 초과하면 그리스 조성물에 함유된 금속이 쉽게 부식될 수 있고, 인 성분의 함량이 상기의 범위를 초과하면 금속이 마모되어 내마모효과를 얻을 수 없다. 또한 이들이 상기의 범위 미만으로 함유되면 본 발명에서 요구하는 효과를 얻을 수 없다.
그리고, 성분(f)로서 사용될 수 있는 칼슘염으로는 산화왁스의 칼슘염, 윤활유 성분 중의 방향족 탄화수소를 황산화하여 얻은 석유술포네이트의 칼슘염, 알킬방향족술포네이트의 칼슘염 (예를들면 디노닐나프탈렌술폰산 및 알킬벤젠술폰산 등의 합성 술폰산의 칼슘염), 그리고 이밖에 과염기성 합성술폰산의 칼슘염이 있다. 상기 나열된 칼슘염들은 녹방지제(rust inhibitor)로 잘 알려져 있으며, 특히 산화왁스의 칼슘염을 사용하면 아주 우수한 효과를 얻을 수 있다.
또한, 본 발명에서는 (a) 기본유 ; (b) 리튬함유 증감제 ; (c) 유기 몰리브데늄 화합물 ; (d) 아연 디티오포스페이트 ; (e) 금속을 함유하지 않는 황-인계 극압제 ; 그리고 (f) 칼슘염이 특정 비율로 배합되어 있어서 각각의 성분을 단독으로 사용하여 얻은 효과에 비교하여 현저하게 우수한 효과를 발휘할 수 있도록 하였고 이로써 본 발명의 목적을 만족스럽게 달성할 수 있다.
상기 본 발명의 그리스 조성물에 의해 성취될 수 있는 효과가 나타나는 이유는 다음과 같은 바, 이는 어떠한 확증(確證)으로 나타나는 것은 아니다. (c) 유기 몰리브데늄 화합물과 (d) 아연 디티오포스페이트는 윤활부에서 자기분해(self-decomposition)되어 점탄성의 고분자막을 형성하고, 이러한 고분자막은 윤활부의 금속부분을 피복한다. 이로써 윤활부에 대한 마찰력 감소 및 진동 흡수는 서로간의 상승효과를 보이는데, 이는 상기의 고분자막이 윤활부의 복잡한 롤링과 슬라이딩 운동에 의해 쉽게 절단되기 때문이다. 상기 효과 이외에도 성분(c)의 유기 몰리브데늄 화합물이 황(S)성분의 존재하에서 자기분해하여 몰리브데늄 디설파이드를 쉽게 생성하고, 이에 고면압(high surface pressure)하에서의 어떠한 마찰 또는 이 부분에 생기는 마찰력을 감소시키는 효과를 나타낸다.
성분(e)는 황성분과 인성분이 적절한 비율로 배합되어 있음으로써 성분(c)와 성분(d)가 보다 뚜렷한 마찰력 감소효과를 나타내도록 하고, 또한 상기 고분자막의생성 등을 촉진하는데 도움을 준다.
성분(f) 즉, 산화왁스의 칼슘염, 석유술폰산의 칼슘염 및 알킬방향족술폰산의 칼슘염 중에서 선택된 칼슘염은 일반적으로 녹방지제(rust inhibitor)로 사용되고 있고, 이러한 녹방지효과는 칼슘염이 윤활부의 금속 표면에 흡착되어 금속표면을 보호함으로써 나타나게 된다. 본 발명에 있어서 상기의 (f) 칼슘염은 윤활부에 균일하게 분산되고, 또한 칼슘 화합물의 칼슘원자가 마모방지효과를 갖기때문에 상기의 다른 성분들에 의해 성취될 어떠한 효과의 감소없이 칼슘염은 다른 성분들이 보다 효과적으로 마찰력 감소 효과를 갖도록 하는 것으로 추정된다.
본 발명의 등속조인트용 그리스 조성물은 조성물의 총량에 대하여 성분(a)의 기본유가 60 ~ 96 중량% 바람직하기로는 77 ~ 91 중량%, 성분(b)의 리튬함유 증감제가 2 ∼ 15 중량% 바람직하기로는 5 ~ 10 중량%, 성분(c)의 유기 몰리브데늄 화합물은 0.5 ∼ 10 중량% 바람직하기로는 2 ~ 5 중량%, 성분(d)의 아연 디티오포스페이트가 0.5 ~ 5 중량 바람직하기로는 1 ~ 3 중량%, 성분(e)의 금속이 함유되지 않은 황-인계 극압제가 0.1 ∼ 5 중량% 바람직하기로는 0.3 ∼ 2 중량%, 그리고 성분(f)의 칼슘염이 0.5 ~ 5 중량% 바람직하기로는 1 ~ 3 중량% 함유되어 있다.
상기 그리스 조성물에 있어서 성분(b)의 함량이 2 중량% 미만이면 증감제로서 작용할 수 없고 본 발명에서 목적으로 하는 그리스 조성물은 얻을 수 없으며, 15 중량%를 초과하면 너무 딱딱해서 그리스 조성물에 요구되는 효과를 얻을 수 없다.
성분(c)의 함량이 0.5 중량% 미만, 성분(d)의 함량이 0.5 중량% 미만,성분(e)의 함량이 0.1 중량%미만 그리고 성분(f)의 함량이 0.5 중량% 미만이면 본 발명의 그리스 조성물에 요구되는 효과를 나타낼 수 없다. 또한, 성분(c)의 함량이 10 중량%를 초과, 성분(d)의 함량이 5 중량%를 초과, 성분(e)의 함량이 5중량%를 초과, 그리고 성분(f)의 함량이 5 중량%를 초과하면 더 이상의 개선된 효과를 기대할 수 없다.
또한, 본 발명의 그리스 조성물은 필요에따라 산화방지제, 녹방지제 및 부식방지제 중에서 선택된 하나 또는 그 이상의 것을 상기 필수성분에 첨가하여 사용할 수도 있다.
상기와 같은 본 발명은 다음의 실시예와 비교예에 의해 더욱 상세히 설명하면 다음과 같은바, 본 발명이 이에 한정되는 것은 아니다.
실시예 1 ~ 4, 6 ~ 9 및 비교예 1 ~ 3
기본유(2500 g)와 12-히드록시스테아르산(500 g)을 혼합한 다음, 80℃까지 가열하였다. 50% 수산화나트륨 수용액(140 g)을 혼합물에 첨가하고 30분동안 교반하여 비누화반응 시킨다음, 혼합물을 210 ℃까지 가열한 후 160 ℃까지 냉각시켰다. 여기에 기본유(1930 g)을 추가로 투입하고 100 ℃미만으로 반응온도가 내려가지않도록 하면서 교반하여 베이스 리튬그리스(base lithium grease)를 제조하였다.
다음 표1 또는 표2에 제시된 배합비율로 첨가제를 상기의 베이스 리튬그리스에 첨가하고, 임의로 기본유를 첨가한 다음, 쓰리-스테이지 롤 밀(three-stage roll mill)에서 혼합하여 혼합물의 조도(consistency)가 No. 1 등급인 그리스 조성물을 제조하였다.
실시예 5
기본유(500 g), 12-히드록시스테아르산(90 g) 및 아젤라산(30 g)을 혼합한 다음, 65∼75 ℃까지 가열하였다. 50% 수산화나트륨 수용액(55 g)을 혼합물에 첨가하고 10분동안 반응시킨다음, 혼합물을 95∼120℃에서 30분동안 가열반응시키고, 210 ℃까지 승온하여 10분동안 유지시킨다음 냉각시켰다. 여기에 기본유(352.5 g)을 추가로 투입하고 교반 냉각하여 베이스 리튬착그리스(base lithium complex grease)를 제조하였다.
다음 표1 또는 표2에 제시된 배합비율로 첨가제를 상기의 베이스 리튬착그리스에 첨가하고, 쓰리-스테이지 롤 밀(three-stage roll mill)에서 혼합하여 혼합물의 컨시스텐시(consistency)가 No. 1 등급인 그리스 조성물을 제조하였다.
상기 실시예와 비교예의 그리스 조성물 제조시 사용된 기본유는 다음과 같은 조성을 갖는다.
기본유의 종류 : 광물유 (mineral oil)
점도(Viscosity) : 60.6 ㎟/s (40℃에서)
7.7 ㎟/s (100℃에서)
점도지수(Viscosity Index) : 88
또한, 비교예4는 시판되고 있는 황-인계 극압제를 함유하는 리튬그리스이고, 비교예5는 시판되고 있는 칼슘착그리스이다.
다음의 측정방법에 의해 그리스의 물리적 성질을 측정하였고, 그 결과는 다음 표 1과 2에 나타내었다.
[조도(Consistency)] ISO 2137에 제시된 방법에 의함.
[SRV 시험]
시험편 : 볼(ball) 직경 10 mm (SUJ-2)
원통형판 직경 24 mm × 7.85 mm (SUJ-2)
측정조건 :
·하중 : 50N, 100N, 200N, 300N, 400N, 500N (50N의 하중에서 1분동안 운전한후 100N씩 하중을 증가시키고, SRV시험기는 각 하중에서 1분동안 운전시킴.)
· 주파수 : 15 Hz
· 진폭 : 1000 ㎛
· 시간 : 6분
· 측정온도 : 상온
· 측정항목 : 각 하중에서 마찰계수의 총평균값
[축력측정시험]
실제 조인트의 진동을 측정하기 위하여 트리포드형 등속조인트의 경우, 회전운동시 축방향으로의 슬라이드 저항을 측정하였고, 이에의해 축력을 결정하였다. 비교예 5의 시판 칼슘착그리스(calcium complex grease)에서 측정한 값을 기준으로하여 각 각도(angle)에서의 축력감소율을 구하였고,세각도(three angle)에서의 평균치가 평균 축력 감소율이다.
측정조건
회전수 : 300 rpm
토크(torque) : 637 N·m
조인트 각도 : 6° , 8° , 10°
측정시간 : 10분동안 운전후
표1.
표2.
* 시판 황-인계 극압제를 함유하는 리튬그리스
** 시판 칼슘착그리스
(1) 베이스 리튬그리스(base lithium grease)
(2) 베이스 리튬착그리스(base lithium complex grease)
(3) 몰리브데늄 디티오포스페이트(상품명 : Molyvan L ; R.T. VanderbiltCompany의 제품)
(4) 몰리브데늄 디티오카바메이트(상품명 : Molyvan A ; R.T. Vanderbilt Company의 제품)
(5) 몰리브데늄 디티오카바메이트(상품명 : Molyvan 822 ; R.T. Vanderbilt Company의 제품)
(6) 아연 디티오포스페이트 Ⅰ(상품명 : Lubrizol 1360 ; Nippon Lubrizol Co., Ltd.의 제품)
(7) 아연 디티오포스페이트 Ⅱ(상품명 : TLA 111 ; Texaco Company의 제품)
(8) 아연 디티오포스페이트 Ⅲ[(상품명 : TLA 252 ; Texaco Company의 제품)
(9) 황-인계 극압제(상품명 : Mobilad G-305 ; Mobil Chemical Company의 제품)
(10) 산화왁스의 칼슘염(상품명 : Alox 165 ; Alox Corporation의 제품)
(11) 석유술폰산의 칼슘염(상품명 : Sulfo Ca-45 ; Matsumura Petroleum Laboratory Co., Ltd.의 제품)
(12) 디노닐나프탈렌술폰산 칼슘염(상품명 : NA-SUL 729 ; KING INDUSTRIES Co., Ltd.의 제품)
(13) 과염기성 알킬벤젠술폰산 칼슘염(상품명 : BRYTON C-400 ; WITCO CHEMICAL Company 제품)
(14) 조도(Consistency) : 60 W
(15) SRV 시험 : 평균 마찰계수
(16) 축력측정시험 : 평균 축력감소율(%)
상기에서 설명된 바와 같이, 본 발명의 등속조인트용 그리스 조성물은 (a) 기본유 ; (b) 리튬비누 및 리튬착비누 중에서 선택된 리튬함유 증감제 ; (c) 몰리브데늄 디티오포스페이트 및 몰리브데늄 디티오카바메이트 중에서 선택된 유기 몰리브데늄 화합물 ; (d) 아연 디티오포스페이트 ; (e) 금속을 함유하지 않는 황-인계 극압제 ; (f) 산화왁스의 칼슘염, 석유술폰산의 칼슘염 및 알킬방향족술폰산의 칼슘염 중에서 선택된 칼슘염을 특정 배합비율로 함유하고 있어서, 상기 표 1 과 표 2에 제시된 실시예와 비교예의 시험결과로부터 알 수 있듯이 본 발명의 그리스 조성물은 현저한 마찰계수의 감소효과 및 현저한 회전3차축력의 감소효과가 있다.

Claims (12)

  1. (a) 기본유 60~96 중량% ;
    (b) 리튬비누 및 리튬착비누 중에서 선택된 리튬함유 증감제 2~15 중량% ;
    (c) 몰리브데늄 디티오포스페이트 및 몰리브데늄 디티오카바메이트 중에서 선택된 유기 몰리브데늄 화합물 0.5~10 중량% ;
    (d) 아연 디티오포스페이트 0.5~5 중량% ;
    (e) 금속을 함유하지 않는 황-인계 극압제 0.1~5 중량% ; 그리고
    (f) 산화왁스의 칼슘염, 석유술폰산의 칼슘염 및 알킬방향족술폰산의 칼슘염 중에서 선택된 칼슘염 0.5~5 중량%으로 이루어진 것을 특징으로 하는 등속조인트용 그리스 조성물.
  2. 제 1 항에 있어서, 상기 조성물은 (a) 기본유 77∼91 중량% ; (b) 리튬함유 증감제 5~10중량% ; (c) 유기 몰리브데늄 화합물 2 ~ 5 중량% ; (d) 아연 디티오포스페이트 1 ∼ 3 중량% ; (e) 금속을 함유하지 않는 황-인계 극압제 0.3 ∼ 2 중량% ; 그리고 (f) 칼슘염 1 ∼ 3 중량%으로 이루어진 것을 특징으로 하는 등속조인트용 그리스 조성물.
  3. 제 1 항에 있어서, 상기 몰리브데늄 디티오포스페이트는 다음 구조식(Ⅰ)로 표시되는 화합물 중에서 선택된 것임을 특징으로 하는 등속조인트용 그리스 조성물.
    상기 식에서 R1, R2, R3및 R4는 각각 같거나 다른 것으로서 탄소원자수 1 ∼ 24의 1 차 또는 2차 알킬기 또는 탄소원자수 6 ∼ 30의 아릴기이다.
  4. 제 3 항에 있어서, 상기 R1, R2, R3및 R4는 각각 같거나 다른 것으로서 탄소원자수 3 ∼ 20의 1 차 또는 2차 알킬기 또는 탄소원자수 8 ∼ 18의 아릴기임을 특징으로 하는 등속조인트용 그리스 조성물.
  5. 제 1 항에 있어서, 상기 몰리브데늄 디티오카바메이트는 다음 구조식(Ⅱ)로 표시되는 화합물 중에서 선택된 것임을 특징으로 하는 등속조인트용 그리스 조성물.
    상기 식에서, R5및 R6은 각각 같거나 다른 것으로서 탄소원자수 1 ∼ 24의 알킬기이고 ; m은 0 ∼ 3이고, n은 4 ∼ 1이며, 단 m + n = 4이다.
  6. 제 5항에 있어서, 상기 R5및 R6은 각각 같거나 다른 것으로서 탄소원자수 3∼ 18의 알킬기임을 특징으로는 등속조인트용 그리스 조성물.
  7. 제 1 항에 있어서, 상기 아연 디티오포스페이트는 다음 구조식(Ⅲ)으로 표시되는 화합물 중에서 선택된 극압제임을 특징으로는 등속조인트용 그리스 조성물.
    상기 식에서, R7, R8, R9및 R10은 각각 같거나 다른 것으로서 탄소원자수 1 ∼ 24의 알킬기 또는 탄소원자수 6 ∼ 30의 아릴기이다.
  8. 제 7 항에 있어서, 상기 R7, R8, R9및 R10은 각각 같거나 다른 것으로서 탄소원자수 3 ∼ 20 의 알킬기 또는 탄소원자수 8 ∼ 18의 아릴기임을 특징으로는 등속조인트용 그리스 조성물.
  9. 제 7 항에 있어서, 상기 R7, R8, R9및 R10은 각각 탄소원자수 3 ∼ 8의 1차 또는 2차 알킬기임을 특징으로는 등속조인트용 그리스 조성물.
  10. 제 1 항에 있어서, 상기 유기 몰리브데늄 화합물은 몰리브데늄 디티오포스페이트와 몰리브데늄 디티오카바메이트 혼합물임을 특징으로 하는 등속조인트용 그리스 조성물.
  11. 제 1 항에 있어서, 상기 금속을 함유하지 않는 황-인계 극압제는 황(sulfur) 성분 15 ∼ 35 중량%와 인(phosphorus)성분 0.5 ∼ 3 중량%를 함유하고 있는 것을 특징으로 하는 등속조인트용 그리스 조성물.
  12. 제 1 항에 있어서, 상기 칼슘염은 산화왁스의 칼슘염임을 특징으로 하는 등속조인트용 그리스 조성물.
KR1019950031601A 1994-10-21 1995-09-25 등속조인트용 그리스조성물 KR100410725B1 (ko)