JPWO2019244971A1 - 金属端子用接着性フィルム、接着性フィルム付き金属端子、及び電池 - Google Patents
金属端子用接着性フィルム、接着性フィルム付き金属端子、及び電池 Download PDFInfo
- Publication number
- JPWO2019244971A1 JPWO2019244971A1 JP2019571089A JP2019571089A JPWO2019244971A1 JP WO2019244971 A1 JPWO2019244971 A1 JP WO2019244971A1 JP 2019571089 A JP2019571089 A JP 2019571089A JP 2019571089 A JP2019571089 A JP 2019571089A JP WO2019244971 A1 JPWO2019244971 A1 JP WO2019244971A1
- Authority
- JP
- Japan
- Prior art keywords
- adhesive film
- layer
- metal
- metal terminals
- polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
項1. 電池素子の電極に電気的に接続された金属端子と、前記電池素子を封止する包装材料との間に介在される、金属端子用接着性フィルムであって、
前記金属端子用接着性フィルムは、少なくとも1層のポリオレフィン骨格を有する樹脂層を備えており、
前記金属端子用接着性フィルムを示差走査熱量計で測定した場合に、120℃以上156℃以下の範囲に融解ピークが観察される、金属端子用接着性フィルム。
項2. 前記ポリオレフィン骨格を有する樹脂層は、断面を電子顕微鏡で観察した際に海島構造が観察される層を含んでいる、項1に記載の金属端子用接着性フィルム。
項3. 以下の測定方法で測定される、前記金属端子用接着性フィルムの厚さ残存率が、40%以上である、項1または2に記載の金属端子用接着性フィルム。
厚さ100μmのアルミニウム板と、前記金属端子用接着性フィルムを用意する。
前記金属端子用接着性フィルムの厚さA(μm)を測定する。
前記アルミニウム板及び前記金属端子用接着性フィルムの長さ方向及び幅方向が一致するようにして、前記アルミニウム板の中心部分に前記金属端子用接着性フィルムを重ねる。さらに、前記金属端子用接着性フィルムの上に厚み12μmのポリエチレンテレフタレートフィルムを配置する。
前記アルミニウム板の長さより長く、幅7mmの金属板を2枚用意し、前記金属端子用接着性フィルムの全面を覆うようにして、前記アルミニウム板と前記金属端子用接着性フィルムの上下から、温度190℃、面圧1.27MPa、時間3秒間の条件で、前記金属板で加熱及び加圧を行い、前記ポリエチレンテレフタレートフィルムを金属接着性フィルムから剥し前記アルミニウム板と前記金属端子用接着性フィルムの積層体を得る。
当該積層体の加熱及び加圧が行われた部分の厚さB(μm)を測定する。
以下の式によって、前記金属端子用接着性フィルムの厚さ残存率を算出する。
金属端子用接着性フィルムの厚さ残存率(%)=(厚さB−100)/厚さA×100
項4. 前記金属端子用接着性フィルムの流れ方向の熱収縮率が、40%以上95%以下である、項1〜3のいずれかに記載の金属端子用接着性フィルム。
項5. 前記金属端子用接着性フィルムを赤外分光法で分析すると、無水マレイン酸に由来するピークが検出される、項1〜4のいずれかに記載の金属端子用接着性フィルム。
項6. 前記ポリオレフィン骨格を有する樹脂層は、ポリプロピレン層を含んでいる、項1〜5のいずれかに記載の金属端子用接着性フィルム。
項7. 前記ポリプロピレン層は、ブロックポリプロピレンを含んでいる、項6に記載の金属端子用接着性フィルム。
項8. 前記ポリプロピレン層は、ランダムポリプロピレンを含んでいる、項6又は7に記載の金属端子用接着性フィルム。
項9. 前記ポリプロピレン層は、未延伸ポリプロピレンにより構成されている、項6〜8のいずれかに記載の金属端子用接着性フィルム。
項10. 前記ポリプロピレン層は、ランダムポリプロピレンにより構成された層と、ブロックポリプロピレンにより構成された層と、ランダムポリプロピレンにより構成された層とがこの順に積層された積層構成を有している、項6〜9のいずれかに記載の金属端子用接着性フィルム。
項11. 前記ポリプロピレン層は、断面を電子顕微鏡で観察した際に海島構造が観察され、当該海島構造において、島の部分の面積の割合が、5%以上である、項6〜10のいずれかに記載の金属端子用接着性フィルム。
項12.前記ポリオレフィン骨格を有する樹脂層は、酸変性ポリプロピレン層を含んでいる、項1〜11のいずれかに記載の金属端子用接着性フィルム。
項13. 前記酸変性ポリプロピレン層は、ランダムベースの酸変性ポリプロピレンを含んでいる、項12に記載の金属端子用接着性フィルム。
項14. 前記金属端子用接着性フィルムの一方側の表面粗さが0.5μm以上である、項1〜13のいずれかに記載の金属端子用接着性フィルム。
項15. 前記包装材料が、少なくとも、基材層、バリア層、及び熱融着性樹脂層をこの順に備える積層シートから構成されており、
前記熱融着性樹脂層と前記金属端子との間に前記金属端子用接着性フィルムが介在される、項1〜13のいずれかに記載の金属端子用接着性フィルム。
項16. 少なくとも、正極、負極、及び電解質を備えた電池素子と、当該電池素子を封止する包装材料と、前記正極及び前記負極のそれぞれに電気的に接続され、前記包装材料の外側に突出した金属端子とを備える電池であって、
前記金属端子と前記包装材料との間に、項1〜15のいずれかに記載の金属端子用接着性フィルムが介在される、電池。
項17. 金属端子と、前記金属端子の一部を被覆している項1〜15のいずれかに記載の金属端子用接着性フィルムとを備える、接着性フィルム付き金属端子。
本発明の金属端子用接着性フィルムは、電池素子の電極に電気的に接続された金属端子と、電池素子を封止する包装材料との間に介在されるものである。具体的には、例えば図1〜3に示されるように、本発明の金属端子用接着性フィルム1は、電池素子4の電極に電気的に接続されている金属端子2と、電池素子4を封止する包装材料3との間に介在されている。また、金属端子2は、包装材料3の外側に突出しており、ヒートシールされた包装材料3の周縁部3aにおいて、金属端子用接着性フィルム1を介して、包装材料3に挟持されている。なお、本発明において、包装材料をヒートシールする際の熱としては、通常160〜220℃程度の範囲、圧力としては、通常0.5〜2.0MPa程度の範囲である。
厚さ100μmのアルミニウム板(純アルミニウム系、JIS H4160−1994 A1N30H−O)と、金属端子用接着性フィルムを用意する。金属端子用接着性フィルムの厚さA(μm)をマイクロゲージで測定する。アルミニウム板及び金属端子用接着性フィルムの長さ方向及び幅方向が一致するようにして、アルミニウム板の中心部分に金属端子用接着性フィルムを重ねる。このとき、金属端子用接着性フィルムの表面とアルミニウム板とが接するように配置する。さらに、金属端子用接着性フィルムの上に厚み12μmのポリエチレンテレフタレートフィルムを配置する。アルミニウム板の長さより長く、幅7mmの金属板を2枚用意し、金属端子用接着性フィルムの全面を覆うようにして、アルミニウム板と金属端子用接着性フィルムの上下から、温度190℃、面圧1.27MPa、時間3秒間の条件で、加熱及び加圧を行い、ポリエチレンテレフタレートフィルムを金属接着性フィルムから剥しアルミニウム板と金属端子用接着性フィルムの積層体を得る。当該積層体の加熱及び加圧が行われた部分の厚さB(μm)をマイクロゲージで測定する。以下の式によって、前記金属端子用接着性フィルムの厚さ残存率を算出する。
金属端子用接着性フィルムの厚さ残存率(%)=(厚さB−100)/厚さA×100
金属端子用接着性フィルムを長さ50mm(MD)×幅4mm(TD)のサイズに切り出して試験片とする。次に、金尺にて試験片の長さM(mm)を計測する。次に、試験片の長さ方向の端部(約1mm)を金網にテープで固定し、試験片を金網から吊るした状態にする。この状態で、190℃に加熱されたオーブン内に120秒置いた後、試験片を金網ごと取出して、室温(25℃)環境で自然冷却する。次に、室温まで自然冷却した試験片の長さN(mm)を金尺にて測定する。下の式により、金属端子用接着性フィルムの熱収縮率を算出する。
熱収縮率(%)=(1−(長さN/長さM))×100
本発明において、ポリオレフィン骨格を有する樹脂層は、ポリプロピレン層11を含んでいることが好ましい。ポリプロピレン層11は、ポリプロピレンにより構成された層である。
熱硬化性のエポキシ樹脂内に金属端子用接着性フィルムを包埋し硬化させる。市販品の回転式ミクロトーム(例えば、LEICA製 EM UC6)と、ガラスナイフを用いて目的とする方向の断面(TDに沿った断面)を作製する。包埋樹脂ごと四酸化ルテニウムにて一晩染色する。染色すると、樹脂が膨張し断面付近では海島構造を確認できないため、膨張部分をミクロトームでトリミングする。そして、1μmから2μmほどダイヤモンドナイフで切り進めた後の断面を観察する。染色した断面は、電界放出形走査型電子顕微鏡(例えば、日立ハイテクノロジーズ社製 S−4800 TYPE1,測定条件:3kV 20mA High WD6mm 検出器(Upper))で観測して画像(倍率は10000倍)を取得する。次に、画像を二値化できる画像処理ソフト(例えば、三谷商事製画像解析ソフトWinROOF(Ver7.4)を用い、当該画像について、海島構造の島の部分と海の部分とを二値化して、島の部分の占める面積の割合(島の部分の合計面積/画像の測定範囲の面積)を求める。具体的な画像処理の条件については、例えば実施例に記載の条件を採用する。
本発明において、酸変性ポリプロピレン層12は、酸変性ポリプロピレンにより構成された層である。酸変性ポリプロピレン層12についても、断面を電子顕微鏡で観察した際に海島構造が観察されることが好ましい。なお、酸変性ポリプロピレン層12における海島構造の確認方法は、前述のポリプロピレン層11における確認方法と同様である。
走査型熱顕微鏡(Anasys社製のNanoTA)を用い、サーマルプローブのカンチレバーのモデルはEX−AN2−200、昇温速度5℃/sの条件で測定された値である。また、軟化点は、ピークトップ温度とした。
金属端子用接着性フィルム1全体に含まれている滑剤の含有量は、ガスクロマトグラフ質量分析計(GC−MS)を用いて測定した値である。具体的には、沸騰還流させたメタノール中にて、金属端子用接着性フィルム内の添加剤をメタノール中に抽出し、得られたメタノール抽出液を、GC−MSで分析して、金属端子用接着性フィルム全体に含まれる滑剤量を測定する。
図示を省略するが、本発明の金属端子用接着性フィルム1は、ポリオレフィン骨格を有する樹脂層10に加えて、さらに、支持部材を有していてもよい。支持部材は、金属端子用接着性フィルム1の支持体として機能する層である。
本発明の金属端子用接着性フィルム1は、金属端子2と包装材料3との間に介在させて使用される。金属端子2(タブ)は、電池素子4の電極(正極または負極)に電気的に接続される部材であり、金属材料により構成されている。金属端子2を構成する金属材料としては、特に制限されず、例えば、アルミニウム、ニッケル、銅などが挙げられる。例えば、リチウムイオン電池の正極に接続される金属端子2は、通常、アルミニウムなどにより構成されている。また、リチウムイオン電池の負極に接続される金属端子は、通常、銅、ニッケルなどにより構成されている。
本発明の接着性フィルム付き金属端子は、金属端子2と、金属端子2の一部を被覆している金属端子用接着性フィルム1とを備える。前記の通り、金属端子用接着性フィルムは、金属端子2と包装材料3との間に介在させて使用される。本発明の接着性フィルム付き金属端子においては、予め金属端子2の一部が金属端子用接着性フィルム1で被覆されている。金属端子2を金属端子用接着性フィルム1で被覆する部分は、金属端子2が包装材料3によって挟持される部分に対応する位置とする。金属端子用接着性フィルム1は、金属端子2に巻き付けられていることが好ましい。
包装材料3としては、少なくとも、基材層31、バリア層33、及び熱融着性樹脂層34をこの順に有する積層シートからなる積層構造を有するものが挙げられる。図6に、包装材料3の断面構造の一例として、基材層31、接着剤層32、バリア層33、接着層35、及び熱融着性樹脂層34がこの順に積層されている態様について示す。接着剤層32は、基材層31とバリア層33との密着性を高めることなどを目的として、必要に応じて設けられる層である。また、接着層35は、バリア層33と熱融着性樹脂層34の密着性を高めることなどを目的として、必要に応じて設けられる層である。
包装材料3において、基材層31は、包装材料の基材として機能する層であり、最外層側を形成する層である。
包装材料3において、接着剤層32は、基材層31に密着性を付与させるために、基材層31上に必要に応じて配置される層である。即ち、接着剤層32は、基材層31とバリア層33の間に必要に応じて設けられる。
包装材料において、バリア層33は、電池用包装材料の強度向上の他、電池内部に水蒸気、酸素、光などが侵入することを防止する機能を有する層である。バリア層33を構成する金属としては、具体的には、アルミニウム、ステンレス、チタンなどが挙げられ、好ましくはアルミニウムが挙げられる。バリア層33は、例えば、金属箔や金属蒸着膜、無機酸化物蒸着膜、炭素含有無機酸化物蒸着膜、これらの蒸着膜を設けたフィルムなどにより形成することができ、金属箔により形成することが好ましく、アルミニウム合金箔により形成することがさらに好ましい。電池用包装材料の製造時に、バリア層33にしわやピンホールが発生することを防止する観点からは、バリア層は、例えば、焼きなまし処理済みのアルミニウム(JIS H4160:1994 A8021H−O、JIS H4160:1994 A8079H−O、JIS H4000:2014 A8021P−O、JIS H4000:2014 A8079P−O)など軟質アルミニウム合金箔により形成することがより好ましい。
包装材料3において、接着層35は、熱融着性樹脂層34を強固に接着させるために、バリア層33と熱融着性樹脂層34の間に、必要に応じて設けられる層である。
包装材料3において、熱融着性樹脂層34は、最内層に該当し、電池の組み立て時に熱融着性樹脂層同士が熱融着して電池素子を密封する層である。
本発明の電池40は、少なくとも、正極、負極、及び電解質を備えた電池素子4と、当該電池素子4を封止する包装材料3と、正極及び負極のそれぞれに電気的に接続され、包装材料3の外側に突出した金属端子2とを備えている。本発明の電池40においては、金属端子2と包装材料3との間に、本発明の金属端子用接着性フィルム1が介在されることを特徴とする。
示差走査熱量計(DSC)を用いて金属端子用接着性フィルムを測定した。装置としては、島津製作所の「DSC−60 Plus」を用いた。また、測定条件は、昇温速度を10℃/min、温度測定範囲を−50〜200℃とし、サンプルパンとしてアルミニウムパンを使用した。
金属端子用接着性フィルムを長さ50mm(MD)×幅4mm(TD)のサイズに切り出して試験片とした。次に、金尺にて試験片の長さM(mm)を計測した。次に、試験片の長さ方向の端部(約1mm)を金網にテープで固定し、試験片を金網から吊るした状態にした。この状態で、190℃に加熱されたオーブン内に120秒置いた後、試験片を金網ごと取出して、室温(25℃)環境で自然冷却した。次に、室温まで自然冷却した試験片の長さN(mm)を金尺にて測定した。以下の式により、金属端子用接着性フィルムの熱収縮率を算出した。
熱収縮率(%)=(1−(長さN/長さM))×100
金属端子用接着性フィルムを15mm(MD)×100mm(TD)のサイズに切り出して試験片とした。次に、試験片を電解液(1M LiPF6の溶液(エチレンカーボネート:ジメチルカーボネート:ジエチルカーボネート=1:1:1、体積比)に浸漬し、85℃のオーブン内で24時間保管した。次に、試験片を取り出し、水で洗浄した後、試験片を目視で観察した。試験片の層間が剥離していなかった場合を「A」とし、試験片の層間が剥離していた場合を「C」とした。
金属端子用接着性フィルム1を長さ50mm(MD)×幅10mm(TD)のサイズに切り出した。また、金属端子2(アルミニウム板、長さ60mm、幅22.5mm、厚み0.3mm)を用意した。次に、図7の模式図に示すように、ホットプレート25の上に、厚さ2mmのアルミニウム板24を載せ、さらにその上に金属端子2を載せた。次に、ホットプレート25を加熱することにより、金属端子2を190℃に加熱した。次に、図7に示すように、真鍮製ブロック21とシリコーンゴム22とテフロン(登録商標)クロス23の積層体を用いて、金属端子2の上に、面圧0.0082MPa、10秒間の条件で、金属端子用接着性フィルム1を押しつけることにより、金属端子2の表面に金属端子用接着性フィルム1を熱融着させて積層体を得た。次に、積層体を電解液(1M LiPF6の溶液(エチレンカーボネート:ジメチルカーボネート:ジエチルカーボネート=1:1:1の体積比、水分1000ppm)に浸漬し、85℃のオーブン内で72時間保管した。次に、電解液から積層体を取り出し水洗し乾燥させた。その後、図8の模式図に示すように、得られた積層体の金属端子2から、金属端子用接着性フィルム1を、引張速度175mm/mimで長さ方向(MD)に剥離して、電解液浸漬後のシール強度(N/10mm)を測定した。結果を表1に示す。
長さ60mm、幅25mm、厚さ100μmのアルミニウム板(純アルミニウム系、JIS H4160−1994 A1N30H−O)と、長さ70mm、幅5mmの前記金属端子用接着性フィルムを用意した。次に、金属端子用接着性フィルムの厚さA(μm)をマイクロゲージで測定した。次に、アルミニウム板及び金属端子用接着性フィルムの長さ方向及び幅方向が一致するようにして、アルミニウム板の中心部分に金属端子用接着性フィルムを重ねた。さらに、金属端子用接着性フィルムの上に厚み12μmのポリエチレンテレフタレートフィルムを配置する。次に、アルミニウム板の長さよりも長く、幅7mmの金属板を2枚用意し、次に、金属端子用接着性フィルムの全面を覆うようにして、金属端子用接着性フィルムの上下から、温度190℃、面圧1.27MPa、時間3秒間の条件で、加熱及び加圧を行い、ポリエチレンテレフタレートフィルムを積層体から剥し、アルミニウム板と金属端子用接着性フィルムの積層体を得た。次に、当該積層体の加熱及び加圧が行われた部分の厚さB(μm)をマイクロゲージで測定した。以下の式によって、金属端子用接着性フィルムの厚さ残存率を算出した。このとき、厚さBは、積層体の中心部1箇所と、積層体の長さ方向の両端部(アルミニウム板と金属端子用接着性フィルムとが積層されている部分の両端部)から前記中心部に向かって10mmの2箇所の合計3箇所の平均値とした。
金属端子用接着性フィルムの厚さ残存率(%)=(厚さB−100)/厚さA×100
熱硬化性のエポキシ樹脂内に金属端子用接着性フィルムを包埋し硬化させた。市販品の回転式ミクロトーム(LEICA製 EM UC6)と、ガラスナイフを用いて目的とする方向の断面(TDに沿った断面)を作製する。包埋樹脂ごと四酸化ルテニウムにて一晩染色した。染色すると、樹脂が膨張し断面付近では海島構造を確認できないため、膨張部分をミクロトームでトリミングした。そして、1μmから2μmほどダイヤモンドナイフで切り進めた後の断面を観察した。染色した断面について、電界放出形走査型電子顕微鏡(日立ハイテクノロジーズ社製 S−4800 TYPE1,測定条件:3kV 20mA High WD6mm 検出器(Upper))で観測して画像(倍率は10000倍)を取得した。次に、画像を二値化できる画像処理ソフト(三谷商事製画像解析ソフトWinROOF(Ver7.4)を用い、当該画像について、海島構造の島の部分と海の部分とを二値化して、島の部分の占める面積の割合(島の部分の合計面積/画像の測定範囲の面積)を求めた。具体的な画像処理の条件は、以下の通りである。なお、本測定では、島部分が海部分よりも染色されたため、島部分が海部分よりも明るく観察された。
[画像処理条件]
3×3pix 平均化
二値化:自動二値化
孤立点除去:1画素から成り立っている物体または背景を除去する。
削除:形状特徴値、または、濃度特徴値を求めて粒子を削除(0.005μm2の面積をノイズとして認識)
JIS B 0601:2013に規定された方法により、金属端子用接着性フィルムの一方側の表面について、算術平均粗さRaを測定した。
(実施例1)
ポリプロピレン層として、ブロックポリプロピレン層(60μm、融解ピーク温度121℃、159℃)の未延伸ポリプロピレンフィルム(CPP)を用意した。次に、この未延伸ポリプロピレンフィルムの両面に、それぞれ、ブロックベースの無水マレイン酸変性ポリプロピレン(20μm、融解ピーク温度157℃)を押出しラミネート法により積層して、酸変性ポリプロピレン層(20μm)/ポリプロピレン層(60μm)/酸変性ポリプロピレン層(20μm)が順に積層された金属端子用接着性フィルムを製造した。
ポリプロピレン層として、ランダムポリプロピレン層(4μm)/ブロックポリプロピレン層(22μm)/ランダムポリプロピレン層(4μm)が順に積層されている3層構成の未延伸ポリプロピレンフィルム(CPP,合計厚さ30μm、融解ピーク温度155℃)を用意した。次に、未延伸ポリプロピレンフィルムの両面に、それぞれ、ブロックベースの無水マレイン酸変性ポリプロピレン(16μm、融解ピーク温度157℃)を押出しラミネート法により積層して、酸変性ポリプロピレン層(16μm)/ポリプロピレン層(30μm)/酸変性ポリプロピレン層(16μm)が順に積層された金属端子用接着性フィルムを製造した。
液晶ポリマー製不織布(目付14g/m2)を用意した。次に、液晶ポリマー製不織布の両面に、それぞれ、ランダムベースの無水マレイン酸変性ポリプロピレン(44μm、融解ピーク温度140℃)を押出しラミネート法により積層して、酸変性ポリプロピレン層(44μm)/液晶ポリマー製不織布(目付14g/m2)/酸変性ポリプロピレン層(44μm)が順に積層された金属端子用接着性フィルム(総厚100μm)を製造した。
ポリプロピレン層として、ブロックポリプロピレン層(80μm、融解ピーク温度121℃、159℃、未延伸ポリプロピレンフィルム(CPP))を用意した。次に、この未延伸ポリプロピレンフィルムの両面に、それぞれ、ブロックベースの無水マレイン酸変性ポリプロピレン(35μm、融解ピーク温度140℃)を押出しラミネート法により積層して、酸変性ポリプロピレン層(35μm)/ポリプロピレン層(80μm)/酸変性ポリプロピレン層(35μm)が順に積層された金属端子用接着性フィルムを製造した。
ランダムベースの酸変性ポリプロピレン(融解ピーク温度140℃)とランダムポリプロピレン(融解ピーク温度142℃)を、Tダイ型の製膜機を用いて、酸変性ポリプロピレン層(25μm)/ポリプロピレン層(100μm)/酸変性ポリプロピレン層(25μm)が順に積層されるようにして共押出して、金属端子用接着性フィルムを製造した。
ランダムベースの酸変性ポリプロピレン(融解ピーク温度135℃)とランダムポリプロピレン(融解ピーク温度142℃)を、Tダイ型の製膜機を用いて、酸変性ポリプロピレン層(25μm)/ポリプロピレン層(100μm)/酸変性ポリプロピレン層(25μm)が順に積層されるようにして共押出して、金属端子用接着性フィルムを製造した。
ランダムベースの酸変性ポリプロピレン(融解ピーク温度140℃)とホモポリプロピレン(融解ピーク温度160℃)を、Tダイ型の製膜機を用いて、酸変性ポリプロピレン層(25μm)/ホモポリプロピレン層(100μm)/酸変性ポリプロピレン層(25μm)が順に積層されるようにして共押出して、金属端子用接着性フィルムを製造した。
酸変性ポリプロピレン(融解ピーク温度140℃)とブロックポリプロピレン(融解ピーク温度164℃)を、Tダイ型の製膜機を用いて、酸変性ポリプロピレン層(35μm)/ポリプロピレン層(80μm)/酸変性ポリプロピレン層(35μm)が順に積層されるようにして共押出して、金属端子用接着性フィルムを製造した。
ポリプロピレン層として、延伸ポリプロピレンフィルム(OPP,ホモポリプロピレン、厚さ50μm、融解ピーク温度165℃)を用意した。次に、延伸ポリプロピレンフィルムの両面に、それぞれ、ブロックベースの無水マレイン酸変性ポリプロピレン(融解ピーク温度157℃)を押出しラミネート法により積層して、酸変性ポリプロピレン層(25μm)/ポリプロピレン層(50μm)/酸変性ポリプロピレン層(25μm)が順に積層された金属端子用接着性フィルムを製造した。
フェノール樹脂、フッ化クロム(三価)化合物、リン酸の3成分からなる化成処理液で両面を化成処理(リン酸クロメート処理)したアルミニウム箔(厚み40μm)を用意した。次に、このアルミニウム箔の一方の面と、二軸延伸ナイロンフィルム(厚み25μm)とをウレタン系接着剤を介して積層した。次に、アルミニウム箔の他方の面と、未延伸ポリプロピレンフィルム(厚み30μm)とを酸変性ポリプロピレン樹脂(厚み15μm、不飽和カルボン酸でグラフト変性したポリプロピレン)でサンドイッチラミネートすると共に、熱風により酸変性ポリプロピレン樹脂の軟化点以上の温度に加熱して、二軸延伸ナイロンフィルム(25μm)/アルミニウム箔(厚み40μm)/酸変性ポリプロピレン樹脂(厚み15μm)/未延伸ポリプロピレンフィルム(15μm)が順に積層された包装材料を製造した。
2 金属端子
3 包装材料
3a 包装材料の周縁部
4 電池素子
10 ポリオレフィン骨格を有する樹脂層
11 ポリプロピレン層
12 酸変性ポリプロピレン層
21 真鍮製ブロック
22 シリコーンゴム
23 テフロン(登録商標)クロス
24 アルミニウム板
25 ホットプレート
31 基材層
32 接着剤層
33 バリア層
34 熱融着性樹脂層
35 接着層
40 電池
Claims (17)
- 電池素子の電極に電気的に接続された金属端子と、前記電池素子を封止する包装材料との間に介在される、金属端子用接着性フィルムであって、
前記金属端子用接着性フィルムは、少なくとも1層のポリオレフィン骨格を有する樹脂層を備えており、
前記金属端子用接着性フィルムを示差走査熱量計で測定した場合に、120℃以上156℃以下の範囲に融解ピークが観察される、金属端子用接着性フィルム。 - 前記ポリオレフィン骨格を有する樹脂層は、断面を電子顕微鏡で観察した際に海島構造が観察される層を含んでいる、請求項1に記載の金属端子用接着性フィルム。
- 以下の測定方法で測定される、前記金属端子用接着性フィルムの厚さ残存率が、40%以上である、請求項1または2に記載の金属端子用接着性フィルム。
厚さ100μmのアルミニウム板と、前記金属端子用接着性フィルムを用意する。
前記金属端子用接着性フィルムの厚さA(μm)を測定する。
前記アルミニウム板及び前記金属端子用接着性フィルムの長さ方向及び幅方向が一致するようにして、前記アルミニウム板の中心部分に前記金属端子用接着性フィルムを重ねる。さらに、前記金属端子用接着性フィルムの上に厚み12μmのポリエチレンテレフタレートフィルムを配置する。
前記アルミニウム板の長さより長く、幅7mmの金属板を2枚用意し、前記金属端子用接着性フィルムの全面を覆うようにして、前記アルミニウム板と前記金属端子用接着性フィルムの上下から、温度190℃、面圧1.27MPa、時間3秒間の条件で、前記金属板で加熱及び加圧を行い、前記ポリエチレンテレフタレートフィルムを金属接着性フィルムから剥し前記アルミニウム板と前記金属端子用接着性フィルムの積層体を得る。
当該積層体の加熱及び加圧が行われた部分の厚さB(μm)を測定する。
以下の式によって、前記金属端子用接着性フィルムの厚さ残存率を算出する。
金属端子用接着性フィルムの厚さ残存率(%)=(厚さB−100)/厚さA×100 - 前記金属端子用接着性フィルムの流れ方向の熱収縮率が、40%以上95%以下である、請求項1〜3のいずれかに記載の金属端子用接着性フィルム。
- 前記金属端子用接着性フィルムを赤外分光法で分析すると、無水マレイン酸に由来するピークが検出される、請求項1〜4のいずれかに記載の金属端子用接着性フィルム。
- 前記ポリオレフィン骨格を有する樹脂層は、ポリプロピレン層を含んでいる、請求項1〜5のいずれかに記載の金属端子用接着性フィルム。
- 前記ポリプロピレン層は、ブロックポリプロピレンを含んでいる、請求項6に記載の金属端子用接着性フィルム。
- 前記ポリプロピレン層は、ランダムポリプロピレンを含んでいる、請求項6又は7に記載の金属端子用接着性フィルム。
- 前記ポリプロピレン層は、未延伸ポリプロピレンにより構成されている、請求項6〜8のいずれかに記載の金属端子用接着性フィルム。
- 前記ポリプロピレン層は、ランダムポリプロピレンにより構成された層と、ブロックポリプロピレンにより構成された層と、ランダムポリプロピレンにより構成された層とがこの順に積層された積層構成を有している、請求項6〜9のいずれかに記載の金属端子用接着性フィルム。
- 前記ポリプロピレン層は、断面を電子顕微鏡で観察した際に海島構造が観察され、当該海島構造において、島の部分の面積の割合が、5%以上である、請求項6〜10のいずれかに記載の金属端子用接着性フィルム。
- 前記ポリオレフィン骨格を有する樹脂層は、酸変性ポリプロピレン層を含んでいる、請求項1〜11のいずれかに記載の金属端子用接着性フィルム。
- 前記酸変性ポリプロピレン層は、ランダムベースの酸変性ポリプロピレンを含んでいる、請求項12に記載の金属端子用接着性フィルム。
- 前記金属端子用接着性フィルムの一方側の表面粗さが0.5μm以上である、請求項1〜13のいずれかに記載の金属端子用接着性フィルム。
- 前記包装材料が、少なくとも、基材層、バリア層、及び熱融着性樹脂層をこの順に備える積層シートから構成されており、
前記熱融着性樹脂層と前記金属端子との間に前記金属端子用接着性フィルムが介在される、請求項1〜14のいずれかに記載の金属端子用接着性フィルム。 - 少なくとも、正極、負極、及び電解質を備えた電池素子と、当該電池素子を封止する包装材料と、前記正極及び前記負極のそれぞれに電気的に接続され、前記包装材料の外側に突出した金属端子とを備える電池であって、
前記金属端子と前記包装材料との間に、請求項1〜15のいずれかに記載の金属端子用接着性フィルムが介在される、電池。 - 金属端子と、前記金属端子の一部を被覆している請求項1〜15のいずれかに記載の金属端子用接着性フィルムとを備える、接着性フィルム付き金属端子。