JPWO2018186412A1 - 光透過性導電フィルムの可視化の分析方法、及び光透過性導電フィルム - Google Patents
光透過性導電フィルムの可視化の分析方法、及び光透過性導電フィルム Download PDFInfo
- Publication number
- JPWO2018186412A1 JPWO2018186412A1 JP2018519987A JP2018519987A JPWO2018186412A1 JP WO2018186412 A1 JPWO2018186412 A1 JP WO2018186412A1 JP 2018519987 A JP2018519987 A JP 2018519987A JP 2018519987 A JP2018519987 A JP 2018519987A JP WO2018186412 A1 JPWO2018186412 A1 JP WO2018186412A1
- Authority
- JP
- Japan
- Prior art keywords
- light
- measurement object
- film
- transmitting conductive
- conductive film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Lab表色系
ΔL*=第1の測定対象物のL値−第2の測定対象物のL値
Δa*=第1の測定対象物のa値−第2の測定対象物のa値
Δb*=第1の測定対象物のb値−第2の測定対象物のb値
Lab表色系
ΔL*=第1の測定対象物のL値−第2の測定対象物のL値
Δa*=第1の測定対象物のa値−第2の測定対象物のa値
Δb*=第1の測定対象物のb値−第2の測定対象物のb値
Lab表色系
ΔL*=第1の測定対象物のL値−第2の測定対象物のL値
Δa*=第1の測定対象物のa値−第2の測定対象物のa値
Δb*=第1の測定対象物のb値−第2の測定対象物のb値
Lab表色系
ΔL*=第1の測定対象物のL値−第2の測定対象物のL値
Δa*=第1の測定対象物のa値−第2の測定対象物のa値
Δb*=第1の測定対象物のb値−第2の測定対象物のb値
基材の全体の厚みは、好ましくは23μm以上、より好ましくは50μm以上、好ましくは300μm以下、より好ましくは200μm以下である。
基材フィルムは、高い光透過性を有することが好ましい。従って、基材フィルムの材料としては、特に限定されないが、例えば、ポリオレフィン、ポリエーテルサルフォン、ポリスルホン、ポリカーボネート、シクロオレフィンポリマー、ポリアリレート、ポリアミド、ポリメチルメタクリレート、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート、トリアセチルセルロース、及びセルロースナノファイバー等が挙げられる。但し、本発明に係る光透過性導電フィルムでは、上記基材フィルムは、ポリカーボネート基材フィルム、又は、シクロオレフィンポリマー基材フィルムである。光透過性導電フィルムの可視化をより一層正確に判別する観点からは、本発明に係る光透過性導電フィルムの可視化の分析方法では、上記基材フィルムは、ポリカーボネート基材フィルム、又は、シクロオレフィンポリマー基材フィルムであることが好ましい。
第1及び第2のハードコート層はそれぞれ、バインダー樹脂により構成されていることが好ましい。上記バインダー樹脂は、硬化樹脂であることが好ましい。上記硬化樹脂としては、熱硬化樹脂、及び紫外線硬化樹脂等の活性エネルギー線硬化樹脂等が挙げられる。生産性及び経済性を良好にする観点から、上記硬化樹脂は、紫外線硬化樹脂であることが好ましい。
アンダーコート層は、例えば、屈折率調整層である。アンダーコート層を設けることで、導電層と、第2のハードコート層又は基材フィルムとの間の屈折率の差を小さくすることができるので、光透過性導電フィルムの光透過性をより一層高めることができる。
導電層は、光透過性を有する導電性材料により形成されている。上記導電性材料としては、特に限定されないが、例えば、IZO(インジウム亜鉛酸化物)及びITO(インジウムスズ酸化物)などのIn系酸化物、SnO2及びFTO(フッ素ドープ酸化スズ)などのSn系酸化物、AZO(アルミニウム亜鉛酸化物)及びGZO(ガリウム亜鉛酸化物)などのZn系酸化物、ナトリウム、ナトリウム−カリウム合金、リチウム、マグネシウム、アルミニウム、マグネシウム−銀混合物、マグネシウム−インジウム混合物、アルミニウム−リチウム合金、Al/Al2O3混合物、Al/LiF混合物、金等の金属、CuI、Agナノワイヤー(AgNW)、カーボンナノチューブ(CNT)並びに導電性透明ポリマーなどが挙げられる。上記導電性材料は、単独で用いてもよく、複数を併用してもよい。
保護フィルムは、基材シート及び粘着剤層により構成されていることが好ましい。
シクロオレフィンポリマー(COP)基材フィルムB(厚み50μm、日本ゼオン社製「ZF16」)
ポリカーボネート(PC)基材フィルムA(厚み100μm、帝人社製「C110」)
基材フィルムとして、上記COP基材フィルムAを用意した。
光硬化性モノマーとしてのウレタンアクリレートオリゴマー100重量部と、希釈溶剤としてのトルエン及びメチルイソブチルケトン(MIBK)の混合溶剤140重量部と、光開始剤としてのイルガキュア194(チバスペシャルティケミカル社製)7重量部とを混合撹拌して、塗工液を調製した。
第1のハードコート層上に、保護フィルム(厚み50μm)を、粘着剤層側から貼り合わせた。
第2のハードコート層上に、Si純度99.9%の多結晶をSiターゲット材として用いて、ACマグネトロンスパッタリング法により、SiO2膜を形成した。具体的には、チャンバー内を5×10−4Pa以下となるまで真空排気した後に、チャンバー内にArガス:95%及び酸素ガス:5%の混合ガスを導入し、厚さ10nmのSiO2膜を堆積させて、アンダーコート層を形成した。
上記アンダーコート層上に、酸化インジウム:93重量%及び酸化スズ:7重量%の焼結体材料をターゲット材として用いて、DCマグネトロンスパッタリング法により、アンダーコート層の全面を覆う導電層を形成した。具体的には、チャンバー内を5×10−4Pa以下となるまで真空排気した後に、チャンバー内にArガス:95%及び酸素ガス:5%の混合ガスを導入し、厚さ20nmのITO層(導電層)を形成した。ITO層を堆積したフィルムをオーブンにて140℃で、60分加熱し、光透過性導電フィルム(第1の測定対象物)を得た。得られた光透過性導電フィルムを、全面エッチング、洗浄、乾燥の各工程をこの順に行い、光透過性導電フィルムからITO層を除去した。それによって、光透過性導電フィルムから導電層を取り除いたフィルム(第2の測定対象物)を得た。
基材フィルムの種類、保護フィルムの厚み、ITO層の厚み、及びSiO2膜の厚みを下記の表1,2に示すように変更したこと以外は実施例1と同様にして、光透過性導電フィルム、及びパターン状の導電層を有する光透過性導電フィルムを得た。
(1)ΔE*rw/ΔE*t
得られた光透過性導電フィルム(第1の測定対象物)、及び、光透過性導電フィルムから導電層を取り除いたフィルム(第2の測定対象物)について、保護フィルムを剥離した後、上述した方法で、ΔE*tの値と、ΔE*rwの値とを求めた。
得られた光透過性導電フィルムについて、以下の基準で骨見えの評価を行った。
光透過性導電フィルムを5cm角に切り出し、導電層の上に200μm幅のラインアンドスペースのレジストパターンを露光現像し、ITOエッチング液(関東化学社製「ITO−06N」)に1分間浸漬し、リンス及び乾燥後にレジストパターンを除去して、パターニングされた導電層(パターン状の導電層)を有する光透過性導電フィルムを得た。
○○…LED光、蛍光灯及び白色灯のいずれを照射した場合においても、目視で導電層のパターンが視認されない
○…LED光を照射した場合には、目視で導電層パターンがわずかに視認されるが、蛍光灯を照射した場合には、目視で導電層のパターンが視認されない
△…LED光を照射した場合には、目視で導電層パターンが視認されるが、蛍光灯を照射した場合には、目視で導電層のパターンが視認されない
×…LED光、蛍光灯のいずれを照射した場合においても、目視で導電層パターンが視認される
得られた透明導電フィルムの導電層の表面抵抗値(シート抵抗値)を、抵抗率計(三菱化学アナリテック社製「ロレスタAX MCP−T370」)を用いて、JIS K7105に基づいて、測定した。
2,2A…基材
2a…第1の表面
2b…第2の表面
3…パターン状の導電層
3X…導電層
4…保護フィルム
11…基材フィルム
12…第1のハードコート層
13…第2のハードコート層
14…アンダーコート層
21…測定対象物
22…光源
23…受光部
24…白色板
Claims (6)
- 基材フィルムと、前記基材フィルムの一方の表面側に配置された導電層とを備える光透過性導電フィルムを第1の測定対象物とし、前記光透過性導電フィルムの前記導電層を除くフィルム部分を第2の測定対象物として、
前記第1の測定対象物及び前記第2の測定対象物のそれぞれについて、分光光度計を用いて、測定対象物に光を照射し、該測定対象物を透過した透過光を測定することで、下記式で表されるΔE*をΔE*tとして得て、
前記第1の測定対象物及び前記第2の測定対象物のそれぞれについて、測定対象物の光源側とは反対側に白色板が配置された状態で、分光光度計を用いて、測定対象物に光を照射し、該測定対象物及び該白色板により反射された反射光を測定することで、下記式で表されるΔE*をΔE*rwとして得て、
ΔE*tの値とΔE*rwの値とから、光透過性導電フィルムの可視化を判別する、光透過性導電フィルムの可視化の分析方法。
ΔE*=(ΔL*2+Δa*2+Δb*2)1/2
Lab表色系
ΔL*=第1の測定対象物のL値−第2の測定対象物のL値
Δa*=第1の測定対象物のa値−第2の測定対象物のa値
Δb*=第1の測定対象物のb値−第2の測定対象物のb値 - 前記基材フィルムが、ポリカーボネート基材フィルム、又は、シクロオレフィンポリマー基材フィルムである、請求項1に記載の光透過性導電フィルムの可視化の分析方法。
- 基材フィルムと、前記基材フィルムの一方の表面側に配置された導電層とを備える光透過性導電フィルムであり、
前記基材フィルムが、ポリカーボネート基材フィルム、又は、シクロオレフィンポリマー基材フィルムであり、
前記基材フィルムが、前記ポリカーボネート基材フィルムである場合に、下記の測定により求められるΔE*rw/ΔE*tが0.5以上であり、
前記基材フィルムが、前記シクロオレフィンポリマー基材フィルムである場合に、下記の測定により求められるΔE*rw/ΔE*tが1.0以上である、光透過性導電フィルム。
ΔE*rw/ΔE*tの測定方法:前記光透過性導電フィルムを第1の測定対象物とし、前記光透過性導電フィルムの前記導電層を除くフィルム部分を第2の測定対象物とする。前記第1の測定対象物及び前記第2の測定対象物のそれぞれについて、分光光度計を用いて、測定対象物に光を照射し、測定対象物を透過した透過光を測定することで、下記式で表されるΔE*をΔE*tとして得る。前記第1の測定対象物及び前記第2の測定対象物のそれぞれについて、測定対象物の光源側とは反対側に白色板が配置された状態で、分光光度計を用いて、測定対象物に光を照射し、該測定対象物及び該白色板により反射された反射光を測定することで、下記式で表されるΔE*をΔE*rwとして得る。ΔE*tの値とΔE*rwの値とから、ΔE*rw/ΔE*tを求める。
ΔE*=(ΔL*2+Δa*2+Δb*2)1/2
Lab表色系
ΔL*=第1の測定対象物のL値−第2の測定対象物のL値
Δa*=第1の測定対象物のa値−第2の測定対象物のa値
Δb*=第1の測定対象物のb値−第2の測定対象物のb値 - 前記基材フィルムが、前記ポリカーボネート基材フィルムであり、
前記ΔE*rw/ΔE*tが0.5以上である、請求項3に記載の光透過性導電フィルム。 - 前記基材フィルムが、前記シクロオレフィンポリマー基材フィルムであり、
前記ΔE*rw/ΔE*tが1.0以上である、請求項3に記載の光透過性導電フィルム。 - 前記導電層の材料が、インジウムスズ酸化物であり、
前記導電層の厚みが、15nm以上、30nm未満である、請求項3〜5のいずれか1項に記載の光透過性導電フィルム。