JPWO2017033681A1 - 表面保護フィルム - Google Patents
表面保護フィルム Download PDFInfo
- Publication number
- JPWO2017033681A1 JPWO2017033681A1 JP2016550286A JP2016550286A JPWO2017033681A1 JP WO2017033681 A1 JPWO2017033681 A1 JP WO2017033681A1 JP 2016550286 A JP2016550286 A JP 2016550286A JP 2016550286 A JP2016550286 A JP 2016550286A JP WO2017033681 A1 JPWO2017033681 A1 JP WO2017033681A1
- Authority
- JP
- Japan
- Prior art keywords
- protective film
- surface protective
- styrene
- weight
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
(1)粘着層と基材層を有する表面保護フィルムであって、粘着層がエチレン・酢酸ビニル共重合体および低密度ポリエチレンからなる群から選ばれる一つ以上を主成分として70重量%超、および、ガラス転移温度が−40℃以上であるスチレン系エラストマーを5〜25重量%含有してなる組成物である表面保護フィルム。
(2)前記スチレン系エラストマーが、スチレン・エチレン・ブチレン・スチレン共重合体である上記(1)に記載の表面保護フィルム。
(3)粘着層の主成分に低密度ポリエチレンが含まれ、該低密度ポリエチレンが、0.90〜0.93g/cm3の密度の直鎖状低密度ポリエチレンである上記(1)または(2)に記載の表面保護フィルム。
(4)粘着層同士を貼り合わせたときの剥離力が0.75N/15mm以下である上記(1)〜(3)のいずれかに記載の表面保護フィルム。
(5)アクリル板に対する貼り込み温度50℃、70℃×15分間の加熱調整後の粘着層の粘着力が0.2〜5.0N/50mmの範囲である上記(1)〜(4)のいずれかに記載の表面保護フィルム。
(6)導光板保護用である上記(1)〜(5)のいずれかに記載の表面保護フィルム。
(1)本発明の表面保護フィルムは、加熱による粘着力の昂進が抑えられ、表面保護フィルムの剥離が容易となる。
(2)本発明の表面保護フィルムは、粘着層同士の剥離性に優れており、粘着層同士の剥離に大きな力を必要としない。
(3)本発明の表面保護フィルムは、剥離後の粘着面表面に凝集破壊痕がなく、若しくは破壊痕があっても軽微であり、被着体への再貼付を容易に行うことができる。
表面保護フィルムを、作成後3日以上、室温23℃、湿度50RH%雰囲気下で保管し、しかる後に予め50℃に加熱しておいた厚さ20mm・幅50mmの三菱レイヨン株式会社製「アクリライトS」アクリル板に、貼込圧力9,100N/m、貼込速度300cm/分で貼付した。しかる後に予め70℃に保温しておいた熱風乾燥機内に15分間保管し、熱風乾燥機より試料を取り出した後、23℃雰囲気下で24時間保管後、引張試験機を用い、引張速度300mm/分、剥離角度180°にて表面保護フィルムを剥離し粘着力を測定した。
前記(1)にて粘着力を測定した後、剥離した表面保護フィルムを再度アクリル板に手指で圧着させ、貼着するかどうかを目視観察し、次の判定を行った。
◎:手指で圧着した部分から、周辺に向かって自発的に粘着していく
○:手指で圧着した部分が粘着する
×:手指で強く圧着しても粘着しない。
前記(1)にて粘着力を測定した後、剥離した表面保護フィルムの粘着層同士を、貼込圧力9,100N/m、貼込速度300cm/分で貼付した。しかる後に23℃雰囲気下で24時間保管後、試料幅が15mmとなるよう断裁し、引張試験機を用い、引張速度300mm/分、剥離角度90°で表面保護フィルム同士を剥離し、粘着層同士を貼り合わせたときの剥離力を測定した。
酢酸ビニルの含有率が10重量%であるエチレン・酢酸ビニル共重合体93重量%とガラス転移温度が−27℃であるスチレン・エチレン・ブチレン・スチレン共重合体(SEBS)7重量%からなる組成物を粘着層として、密度0.97g/cm3の高密度ポリエチレン85重量%と230℃下のメルトフローレート40g/10分、融点145℃のエチレン・プロピレンランダム共重合体12重量%と190℃下でのメルトフローレート2g/10分の低密度ポリエチレン3重量%からなる組成物を基材層としてTダイ型複合製膜機を用い、基材層厚さ比率が80%、粘着層厚さ比率が20%、総厚さが70μmとなるよう共押出し表面保護フィルムを作成した。
粘着層として、密度が0.91g/cm3であるシングルサイト触媒(メタロセン触媒)を用いて得られた直鎖状低密度ポリエチレン樹脂(LLDPE−1)93重量%とガラス転移温度が−27℃であるスチレン・エチレン・ブチレン・スチレン共重合体(SEBS)7重量%からなる組成物を用いる以外は、実施例1と同様に共押出し表面保護フィルムを作成した。
粘着層の組成物のうち、酢酸ビニルの含有率が10重量%であるエチレン・酢酸ビニル共重合体90重量%と、ガラス転移温度が−21℃であるスチレン・エチレン・ブチレン・スチレン共重合体(SEBS)を10重量%とした以外は実施例1と同様とし、表面保護フィル
<実施例4>
粘着層の組成物のうち、ガラス転移温度が−27℃であるスチレン・エチレン・ブチレン・スチレン共重合体(SEBS)を10重量%とした以外は実施例2と同様とし、表面保護フィルムを作成した。
粘着層として、密度が0.92g/cm3であるマルチサイト触媒(チーグラーナッタ触媒)を用いて得られた直鎖状低密度ポリエチレン樹脂(LLDPE−2)80重量%とガラス転移温度が−27℃であるスチレン・エチレン・ブチレン・スチレン共重合体(SEBS)20重量%からなる組成物を用い、基材層として、実施例1と同様の高密度ポリエチレンを用い、更に粘着層とは反対側にホモポリプロピレン80重量%、230℃下のメルトフローレート40g/10分、融点145℃のエチレン・プロピレンランダム共重合体16重量%、190℃下でのメルトフローレート2g/10分の低密度ポリエチレン4重量%の組成からなる背面層を有する2層構成とし、基材層厚さ比率が80%、粘着層厚さ比率が20%、総厚さが70μmとなるよう共押出し表面保護フィルムを作成した。
ここで、基材層の高密度ポリエチレンからなる層と、主としてホモポリプロピレンからなる背面層との厚さ比率は90/10とした。
粘着層として、酢酸ビニルの含有率が10重量%であるエチレン・酢酸ビニル共重合体55重量%、密度0.92g/cm3の低密度ポリエチレンを20重量%およびガラス転移温度が−20℃であるスチレン・イソブチレン・スチレントリブロック共重合体(SIBS)25重量%からなる組成物を用いる以外は実施例5と同様に共押出し表面保護フィルムを作成した。
粘着層の組成物のうち、酢酸ビニルの含有率が10重量%であるエチレン・酢酸ビニル共重合体55重量%、低密度ポリエチレン40重量%、ガラス転移温度が−20℃であるスチレン・イソブチレン・スチレントリブロック共重合体(SIBS)を5重量%とした以外は実施例6同様とし、表面保護フィルムを作成した。
粘着層として、酢酸ビニルの含有率が10重量%であるエチレン・酢酸ビニル共重合体30重量%と、マルチサイト触媒による密度0.92g/cm3の直鎖状低密度ポリエチレン50重量%とガラス転移温度が−27℃であるスチレン・エチレン・ブチレン・スチレン共重合体(SEBS)を20重量%とした以外は実施例6と同様とし、表面保護フィルムを作成した。
密度が0.92g/cm3である直鎖状低密度ポリエチレン樹脂(LLDPE−2)73重量%とガラス転移温度が−27℃であるスチレン・エチレン・ブチレン・スチレン共重合体(SEBS)20重量%、及びガラス転移温度が−50℃である水添スチレン・ブタジエン共重合体(HSBR)7重量%からなる組成物を粘着層として、基材層は実施例5と同一構成として、表面保護フィルムを作成した。
酢酸ビニルの含有率が10重量%であるエチレン・酢酸ビニル共重合体からなる組成物を粘着層とする以外は実施例1と同様に表面保護フィルムを作成した。
酢酸ビニルの含有率が10重量%であるエチレン・酢酸ビニル共重合体を95重量%とロジンエステルが5重量%からなる組成物を粘着層とする以外は実施例1と同様に共押出し表面保護フィルムを作成した。
酢酸ビニルの含有率が10重量%であるエチレン・酢酸ビニル共重合体を93重量%とガラス転移温度が−50℃であるスチレン・エチレン・ブチレン・スチレン共重合体(SEBS)が7重量%からなる組成物を粘着層とする以外は実施例5と同様に共押出し表面保護フィルムを作成した。
密度が0.91g/cm3である直鎖状低密度ポリエチレン樹脂(LLDPE−1)を85重量%とガラス転移温度が−50℃であるスチレン・エチレン・ブチレン・スチレン共重合体(SEBS)が15重量%からなる組成物を粘着層とする以外は実施例5と同様に表面保護フィルムを作成した。
密度が0.92g/cm3である直鎖状低密度ポリエチレン(LLDPE−2)80重量%とガラス転移温度が−54℃であるスチレン・エチレン・ブチレン・スチレン共重合体(SEBS)が20重量%からなる組成物を粘着層とする以外は実施例5と同様に表面保護フィルムを作成した。
酢酸ビニルの含有率が10重量%であるエチレン・酢酸ビニル共重合体を60重量%とガラス転移温度が−50℃である水添スチレン・ブタジエン共重合体(HSBR)が40重量%からなる組成物を粘着層とする以外は実施例5と同様に共押出し表面保護フィルムを作成した。
Claims (6)
- 粘着層および基材層を有する表面保護フィルムであって、粘着層がエチレン・酢酸ビニル共重合体および低密度ポリエチレンからなる群から選ばれる一つ以上を主成分として70重量%超、および、ガラス転移温度が−40℃以上であるスチレン系エラストマーを5〜25重量%含有してなる組成物であることを特徴とする表面保護フィルム。
- 前記スチレン系エラストマーが、スチレン・エチレン・ブチレン・スチレン共重合体である請求項1に記載の表面保護フィルム。
- 粘着層の主成分に低密度ポリエチレンが含まれ、該低密度ポリエチレンが、密度0.90〜0.93g/cm3の直鎖状低密度ポリエチレンである請求項1または2に記載の表面保護フィルム。
- 粘着層同士を貼り合わせたときの剥離力が0.75N/15mm以下である請求項1から3のいずれかに記載の表面保護フィルム。
- アクリル板に対する貼り込み温度50℃、70℃×15分間の加熱調整後の粘着層の粘着力が0.2〜5.0N/50mmの範囲である請求項1から4のいずれかに記載の表面保護フィルム。
- 導光板保護用である請求項1から5のいずれかに記載の表面保護フィルム。