JPWO2016002725A1 - 粉体塗料用組成物、粉体塗料および塗装物品 - Google Patents
粉体塗料用組成物、粉体塗料および塗装物品 Download PDFInfo
- Publication number
- JPWO2016002725A1 JPWO2016002725A1 JP2015544268A JP2015544268A JPWO2016002725A1 JP WO2016002725 A1 JPWO2016002725 A1 JP WO2016002725A1 JP 2015544268 A JP2015544268 A JP 2015544268A JP 2015544268 A JP2015544268 A JP 2015544268A JP WO2016002725 A1 JPWO2016002725 A1 JP WO2016002725A1
- Authority
- JP
- Japan
- Prior art keywords
- powder
- resin
- composition
- powder coating
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
耐候性に優れる粉体塗料としては、フッ素樹脂を用いたフッ素樹脂系粉体塗料も開発されている。
(1)融点が150℃以下、結晶化度が35%以下および質量平均分子量が1×104〜5×105であるビニリデンフルオリド共重合体の粉体と、ガラス転移温度が110℃以下および質量平均分子量が1×104〜5×105であるメチルメタクリレート共重合体の粉体とをドライブレンドした粉体塗料;または前記ビニリデンフルオリド共重合体の水性分散液中にて前記メチルメタクリレート共重合体を形成し得る単量体をシード重合し、得られた水性分散液をスプレードライした粉体塗料(特許文献1)。
しかし、本発明者らの知見によれば、(1)の粉体塗料から形成される塗膜であっても、折り曲げ加工性は充分に満足できるものではない。たとえば、(1)の粉体塗料から形成される塗膜を有するアルミニウム板を折り曲げ加工した場合、折り曲げた箇所の塗膜に割れ、アルミニウム板からのはがれが発生することがある。
[1]下記ポリビニリデンフルオリド(A)と、アクリル樹脂、ポリエステル樹脂およびエポキシ樹脂からなる群から選択される少なくとも1種の樹脂(B)とを含み、下記ポリビニリデンフルオリド(A)の含有量が、ポリビニリデンフルオリド(A)と前記樹脂(B)との合計100質量部のうち、30〜90質量部であることを特徴とする粉体塗料用組成物。
ポリビニリデンフルオリド(A):融点が151〜170℃であり、下記方法で求めた異種シーケンス比率が11〜37%である、ポリビニリデンフルオリド。
(異種シーケンス比率の求め方)
異種シーケンス比率は、溶媒として重N,N−ジメチルホルムアミド、内部標準としてCFCl3を用いてポリビニリデンフルオリドの19F−NMRを測定し、得られたスペクトルにおいて−85〜−98ppm付近に現れる正規シーケンス由来のシグナルの積分値(I1)と−113〜−120ppm付近に現れる異種シーケンス由来のシグナルの積分値(I2)とから下式(1)によって算出する。
異種シーケンス比率(%)={I2/(I1+I2)}×100・・・(1)
[2]前記粉体塗料用組成物が含む樹脂成分が、前記ポリビニリデンフルオリド(A)と前記樹脂(B)のみからなる、[1]の粉体塗料用組成物。
[3]さらに、顔料を含む、[1]または[2]の粉体塗料用組成物。
[5]前記[1]〜[3]のいずれかの粉体塗料用組成物からなる第1の粉体と、アクリル樹脂、ポリエステル樹脂、ウレタン樹脂、エポキシ樹脂およびシリコーン樹脂からなる群から選択される少なくとも1種の樹脂(C)を含み、フッ素樹脂を含まない粉体塗料用組成物からなる第2の粉体とを含む、粉体塗料。
[6]前記第1の粉体と前記第2の粉体との混合比(第1の粉体/第2の粉体)が、10/90〜90/10(質量比)である、[5]の粉体塗料。
[8]前記基材の材質が、化成処理薬剤で表面処理されたアルミニウムまたはアルミニウム合金である、[7]の塗装物品。
[9]前記化成処理薬剤が、クロムを含まない、ジルコニウム系処理薬剤またはチタニウム系処理薬剤である、[8]の塗装物品。
[10]基材の表面と、前記粉体塗料から形成されてなる塗膜の間に、さらに、アクリル樹脂、ポリエステル樹脂およびエポキシ樹脂からなる群から選択される少なくとも一種のプライマーからなるプライマー層を有する、[7]の塗装物品。
本発明の粉体塗料によれば、耐候性、折り曲げ加工性に優れた塗膜を形成できる。
本発明の塗装物品は、耐候性、折り曲げ加工性に優れた塗膜を表面に有する。
ポリビニリデンフルオリドにおいて、CF2とCH2が交互に規則正しく結合している部分(−CF2CH2−CF2CH2−)を「正規シーケンス」というのに対し、CF2同士が隣接して結合している部分(−CH2CF2−CF2CH2−)を「異種シーケンス」という。異種シーケンス比率は、19F−NMRから求めることができ、具体的には、溶媒として重N,N−ジメチルホルムアミド(以下、重DMFとも記す。)、内部標準としてCFCl3を用いてポリビニリデンフルオリドの19F−NMRを測定し、図1に示すように、得られたスペクトルにおいて−85〜−98ppm付近に現れる正規シーケンス由来のシグナルの積分値(I1)と−113〜−120ppm付近に現れる異種シーケンス由来のシグナルの積分値(I2)とから下式(1)によって算出する。
異種シーケンス比率(%)={I2/(I1+I2)}×100・・・(1)
樹脂の「融点」とは、示差走査熱量測定(DSC)法で測定した融解ピークにおける温度を意味する。
樹脂の「ガラス転移温度」とは、示差走査熱量測定(DSC)法で測定した中間点ガラス転移温度を意味する。
「ドライブレンド」とは、粉体を溶融することなく、また、溶媒を添加することなく、2種以上の粉体を混合することを意味する。
「溶融膜」とは、粉体塗料を塗装して形成された該粉体塗料の溶融物からなる膜を意味する。
「塗膜」とは、前記溶融膜を冷却し、場合によっては硬化することにより形成される膜を意味する。
「単位」とは、重合体中に存在して重合体を構成する、単量体に由来する部分を意味する。また、ある単位の構造を重合体形成後に化学的に変換したものも単位という。
なお、以下、場合により、個々の単量体に由来する単位をその単量体名に「単位」を付した名称で呼ぶ。
本発明の粉体塗料用組成物は、ポリビニリデンフルオリド(A)(以下、PVDF(A)とも記す。)と、アクリル樹脂、ポリエステル樹脂およびエポキシ樹脂からなる群から選択される少なくとも1種の樹脂(B)とを含み、PVDF(A)の含有量が、PVDF(A)と樹脂(B)との合計100質量部のうち、30〜90質量部である粉体塗料用組成物(以下、組成物(α)とも記す。)である。
組成物(α)を用いることによって、第一の粉体を製造できる。第1の粉体をそのまま後述する粉体塗料(I)として用いてもよく、第1の粉体と後述する第2の粉体を混合した後述する粉体塗料(II)として用いてもよい。
なお、以下、本発明における第1の粉体を粉体(X)ともいい、本発明における第2の粉体を粉体(Y)ともいう。
PVDF(A)は、融点が151〜170℃、かつ異種シーケンス比率が11〜37%のPVDFである。
PVDF(A)は、ビニリデンフルオリド(以下、VDFとも記す。)の単独重合体、またはVDF単位の80モル%以上100モル%未満と、VDF以外の単量体由来の単位の0モル%超20モル%以下とからなる共重合体である。VDF以外の単量体由来の単位の割合が20モル%を超えると、塗膜の耐候性が劣る。粉体(X)を熱硬化性の粉体塗料として用いる場合は、PVDF(A)は、カルボキシ基、水酸基、スルホ基等の硬化剤と反応し得る反応性基を有していてもよい。
PVDF(A)の溶融粘度は、回転式レオメータを用いて、昇温速度:10℃/分の条件にて測定する。
PVDF(A)の結晶化度は、EXSTAR DSC7020(SIIナノテクノロジー社製)を用い、試料の10mgについて、温度範囲:−25〜200℃、昇温速度:10℃/分で熱収支を測定し、得られたチャートの吸熱ピークの面積および試料量から融解熱量M1(J/g)を算出し、PVDFの完全結晶体の融解熱量M2(EXPRESS Polymer Letters,第4巻,第5号、2010年,p.284−291に記載の文献値:104.5J/g)とから下式(2)によって算出する。
結晶化度(%)=(M1/M2)×100 ・・・(2)
急冷時の結晶化度は、試料について、300℃で完全に溶解させた後、冷却速度:10℃/分で300℃から室温まで冷却し、再結晶化させ、示差走査熱量測定により、再結晶化させた試料の10mgを昇温速度:10℃/分で室温から200℃まで昇温し、得られたチャートの吸熱ピークの面積および試料量から融解熱量M1(J/g)を算出し、PVDFの完全結晶体の融解熱量M2(EXPRESS Polymer Letters,第4巻,第5号,2010年,p.284−291に記載の文献値:104.5J/g)とから前記式(2)によって算出する。
徐冷時の結晶化度は、再結晶化条件である冷却速度を0.5℃/分に変更した以外は、急冷時の結晶化度と同様にして算出する。
フッ素系界面活性剤としては、構造中にフッ素原子を含み界面活性能をもつ化合物の1種または2種以上の混合物が挙げられる。具体的には、X(CF2)nCOOH(ただし、nは、6〜20の整数であり、Xは、FまたはHである。)で表される酸、またはそのアルカリ金属塩、アンモニウム塩、アミン塩もしくは第四級アンモニウム塩;Y(CH2CF2)mCOOH(ただし、mは、6〜13の整数であり、Yは、FまたはClである。)で表される酸、またはそのアルカリ金属塩、アンモニウム塩、アミン塩もしくは第四級アンモニウム塩;Z(CF2OCF2)pCOOH(ただし、pは、1〜10の整数であり、Zは、F、Cl、HまたはCF3である。)で表される酸、またはそのアルカリ金属塩、アンモニウム塩、アミン塩もしくは第四級アンモニウム塩が挙げられる。
ノニオン性非フッ素系界面活性剤としては、ポリオキシエチレンアルキルエーテル類、ポリオキシエチレンアルキルフェニルエーテル類、ポリオキシエチレンアルキルエステル類、ソルビタンアルキルエステル類、ポリオキシエチレンソルビタンアルキルエステル類、グリセリンエステル類およびその誘導体が挙げられる。
乳化剤として前記好ましいものを選択し、かつ添加量をVDFの100質量部に対して0.05〜10質量部とすることによって、PVDF(A)の異種シーケンス比率を前記範囲内に制御できる。
重合開始剤として前記好ましいものを選択し、添加量をVDFの100質量部に対して0.05〜5質量部とし、重合開始剤の添加のタイミングを連続添加とし、かつ重合温度を40〜90℃とすることによって、ラジカル種の発生を一定にし、過剰のラジカル種供給による、PVDF(A)の異種シーケンス比率の増加を抑制し、前記範囲内に制御することができる。
樹脂(B)は、アクリル樹脂、ポリエステル樹脂およびエポキシ樹脂からなる群から選択される少なくとも1種である。アクリル樹脂およびポリエステル樹脂は、熱可塑性であってもよく、熱硬化性であってもよい。
樹脂(B)の溶融粘度は、回転式レオメータを用いて、昇温速度:10℃/分の条件にて測定する。
アクリル樹脂は、アクリレートまたはメタクリレートに由来する単位を有する重合体である。粉体(X)を熱硬化性の粉体塗料として用いる場合は、カルボキシ基、水酸基、スルホ基等の硬化剤と反応し得る反応性基を有していてもよい。
ポリエステル樹脂としては、多価カルボン酸化合物に由来する単位と多価アルコール化合物に由来する単位とを有し、必要に応じて、これら2種の単位以外の単位(たとえば、ヒドロキシカルボン酸化合物に由来する単位等)を有するものが挙げられる。
多価アルコール化合物としては、エチレングリコール、ジエチレングリコール、トリエチレングリコール、1,2−プロパンジオール、1,3−プロパンジオール、1,3−ブタンジオール、1,4−ブタンジオール、1,2−ペンタンジオール、1,5−ペンタンジオール、ネオペンチルグリコール、スピログリコール、1,10−デカンジオール、1,4−シクロヘキサンジメタノール、トリメチロールエタン、トリメチロールプロパン、グリセリン、ペンタエリスリトール等が挙げられる。
多価アルコールとしては、ネオペンチルグリコール、1,2−ペンタンジオール、1,5−ペンタンジオール、トリメチロールプロパン等が好ましく、入手容易の点で、ネオペンチルグリコール、またはトリメチロールプロパンが特に好ましい。
エポキシ樹脂としては、ビスフェノールA型エポキシ樹脂、ビスフェノールF型エポキシ樹脂、2,2−ビス(ヒドロキシメチル)−1−ブタノールの1,2−エポキシ−4−(2−オキシラニル)シクロヘキサン付加物等が挙げられる。
エポキシ樹脂の市販品としては、三菱化学社製の「エピコート(登録商標) 1001」、「エピコート(登録商標) 1002」、「エピコート(登録商標) 4004P」、DIC社製の「エピクロン(登録商標) 1050」、「エピクロン(登録商標) 3050」、新日鉄住金化学社製の「エポトート(登録商標) YD−012」、「エポトート(登録商標) YD−014」、ナガセケムテックス社製の「デナコール(登録商標) EX−711」、ダイセル社製の「EHPE3150」等が挙げられる。
組成物(α)は、顔料を含むことが好ましい。
顔料としては、光輝顔料、防錆顔料、着色顔料および体質顔料からなる群から選ばれる少なくとも1種が好ましい。
粉体(X)を熱硬化性の粉体塗料として用いる場合は、組成物(α)は硬化剤を含んでいてもよい。
硬化剤は、樹脂(PVDF(A)、樹脂(B)等)の反応性基と反応して樹脂を架橋したり高分子量化して、樹脂を硬化させる化合物である。硬化剤は、樹脂が有する反応性基(水酸基、カルボキシ基等)に反応し得る反応性基を2個以上有する。硬化剤の反応性基は、常温で樹脂の反応性基に反応しやすいものは好ましくない点から、粉体塗料が加熱溶融された際に反応し得る反応性基であることが好ましい。たとえば、常温で高い反応性基を有するイソシアナート基よりもブロック化イソシアナート基が好ましい。ブロック化イソシアナート基は、粉体塗料が加熱溶融された際にブロック剤が脱離してイソシアナート基となり、該イソシアナート基が反応性基として作用する。
硬化剤は、1種を単独で用いてもよく、2種以上を併用してもよい。
ブロック化イソシアナート系硬化剤としては、脂肪族、芳香族または芳香脂肪族のジイソシアナートと、活性水素を有する低分子化合物とを反応させて得たポリイソシアナートを、ブロック剤と反応させ、マスキングすることによって製造したものが好ましい。
粉体(X)を熱硬化性の粉体塗料として用いる場合は、組成物(α)は硬化触媒を含んでいてもよい。
硬化触媒は、硬化反応を促進し、塗膜に優れた化学性能および物理性能を付与するものである。
ブロック化イソシアナート系硬化剤を用いる場合、硬化触媒としては、スズ触媒(オクチル酸スズ、トリブチルスズラウレート、ジブチルスズジラウレート等)が好ましい。
硬化触媒は、1種を単独で用いてもよく、2種以上を併用してもよい。
組成物(α)は、必要に応じて、顔料、硬化剤および硬化触媒以外の添加剤(以下、他の添加剤とも記す。)を含んでいてもよい。
他の添加剤としては、たとえば、紫外線吸収剤、光安定剤、つや消し剤(超微粉合成シリカ等)、界面活性剤(ノニオン系界面活性剤、カチオン系界面活性剤、またはアニオン系界面活性剤)、レベリング剤、表面調整剤(塗膜の表面平滑性を向上させる)、脱ガス剤(粉体に巻き込まれる空気、硬化剤から出てくるブロック剤、水分等が塗膜内に留まらないよう、溶融膜外へ出す作用がある。なお、通常は、固体だが、溶融すると非常に低粘度になる。)、充填剤、熱安定剤、増粘剤、分散剤、帯電防止剤、防錆剤、シランカップリング剤、防汚剤、低汚染化剤等が挙げられる。
紫外線吸収剤としては、有機系紫外線吸収剤、無機系紫外線吸収剤のいずれの紫外線吸収剤も用いることができる。
紫外線吸収剤は、1種を単独で用いてもよく、2種以上を組み合わせて用いてもよい。
無機系紫外線吸収剤としては、酸化亜鉛と酸化チタンの複合粒子、酸化セリウムと酸化チタンの複合粒子、酸化亜鉛と酸化セリウムの複合粒子、酸化チタンと酸化亜鉛と酸化セリウムの複合粒子等が好ましい。
光安定剤は、紫外線から塗膜中の樹脂(PVDF(A)、樹脂(B)等)を保護するものである。
光安定剤としては、粉体塗料の塗装時に溶融膜中に均一に拡散していくという点からは、分子量が300〜5,000であり、かつ融点が50〜250℃であるヒンダードアミン系光安定剤が好ましい。組成物の溶融混練時に組成物中に均一に拡散していくという点からは、分子量が400〜4,000であり、かつ融点が60〜200℃であるヒンダードアミン系光安定剤がより好ましい。
光安定剤は、1種を単独で用いてもよく、2種以上を併用してもよい。
組成物(α)中のPVDF(A)の含有量は、PVDF(A)と樹脂(B)との合計100質量部のうち、30〜90質量部であり、35〜90質量部が好ましく、40〜85質量部が特に好ましい。PVDF(A)の含有量が前記下限値以上であれば、塗膜の耐候性にさらに優れる。PVDF(A)の含有量が前記上限値以下であれば、塗膜の折り曲げ加工性にさらに優れる。
硬化剤がブロック化イソシアナート系硬化剤の場合、組成物(α)中のブロック化イソシアナート系硬化剤の含有量は、組成物(α)中の水酸基に対するイソシアナート基のモル比が0.05〜1.5となる量が好ましく、0.8〜1.2となる量が特に好ましい。該モル比が前記範囲の下限値以上であれば、粉体塗料の硬化度が高くなり、基材への塗膜の密着性、塗膜の硬度および耐薬品性等に優れる。該モル比が前記範囲の上限値以下であれば、塗膜が脆くなりにくく、しかも、塗膜の耐熱性、耐薬品性、耐湿性等に優れる。
以上説明した本発明の粉体塗料用組成物(組成物(α))にあっては、異種シーケンス比率が35%以下のPVDF(A)を含むため、耐候性に優れた塗膜を形成できる粉体塗料を得ることができる。
また、以上説明した本発明の粉体塗料用組成物(組成物(α))にあっては、樹脂(B)を含み、かつPVDF(A)の異種シーケンス比率が11%以上であるため、折り曲げ加工性に優れた塗膜を形成できる粉体塗料を得ることができる。
本発明の粉体塗料は、下記の粉体塗料(I)と粉体塗料(II)とに分けられる。
粉体塗料(I):本発明の粉体塗料用組成物(組成物(α))からなる第1の粉体(粉体(X))を含む。
粉体塗料(II):本発明の粉体塗料用組成物(組成物(α))からなる第1の粉体(粉体(X))、アクリル樹脂、ポリエステル樹脂、ウレタン樹脂、エポキシ樹脂およびシリコーン樹脂からなる群から選択される少なくとも1種の樹脂(C)を含み、フッ素樹脂を含まない粉体塗料用組成物からなる第2の粉体(粉体(Y))とを含む。
なお、「樹脂(C)を含み、フッ素樹脂を含まない粉体塗料用組成物」を、以下、「組成物(β)」という。
以下、粉体塗料(I)および粉体塗料(II)のそれぞれについて説明する。
粉体塗料(I)は、粉体(X)の少なくとも1種を含む。
粉体塗料(I)中の粉体(X)の含有量は、50〜100質量%が好ましく、70〜100質量%がより好ましく、80〜100質量%がさらに好ましく、90〜100質量%が特に好ましい。粉体塗料(I)が、粉体(X)のみからなる塗料であってもよい。
粉体塗料(I)は、たとえば、下記工程(a)、工程(b)および工程(c)を有する製造方法によって製造できる。
(a)PVDF(A)と樹脂(B)とを含み、必要に応じて前記添加剤を含んでもよい混合物を溶融混練して組成物(α)からなる混練物を得る工程。
(b)組成物(α)からなる混練物を粉砕して粉体(X)を得る工程。
(c)必要に応じて、粉体(X)の分級を行う工程。
各成分を混合し混合物を調製した後、該混合物を溶融混練して各成分が均一化された混練物を得る。
各成分は、あらかじめ粉砕して粉末状にすることが好ましい。
混合に用いる装置としては、高速ミキサ、V型ミキサ、反転ミキサ等が挙げられる。
溶融混練に用いる装置としては、1軸押出機、2軸押出機、遊星ギア等が挙げられる。
混練物は、冷却後、ペレットとすることが好ましい。
粉砕に用いる装置としては、ピンミル、ハンマーミル、ジェットミル等の粉砕機が挙げられる。
粒子径の大きすぎる粉体や粒子径の小さすぎる粉体を除去するために、粉砕後に分級を行うことが好ましい。分級を行う場合、粒子径が10μm未満の粒子および粒子径が100μmを超える粒子の少なくともいずれかを除去することが好ましい。
分級方法としては、ふるい分けによる方法、空気分級法等が挙げられる。
以上説明した粉体塗料(I)にあっては、本発明の粉体塗料用組成物(組成物(α))からなる粉体を含むため、耐候性、折り曲げ加工性に優れた塗膜を形成できる。
粉体塗料(II)は、粉体(X)の少なくとも1種および下記粉体(Y)の少なくとも1種を含む。
粉体(Y):組成物(β)からなる粉体。組成物(β)は、必要に応じて添加剤を含んでいてもよい。
樹脂(C)は、アクリル樹脂、ポリエステル樹脂、ウレタン樹脂、エポキシ樹脂およびシリコーン樹脂からなる群から選択される少なくとも1種である。
アクリル樹脂、ポリエステル樹脂、エポキシ樹脂としては、組成物(α)で例示したものと同様のものが挙げられ、好ましい態様も同様である。
ウレタン樹脂としては、ポリオール(アクリルポリオール、ポリエステルポリオール、ポリエーテルポリオール、多価アルコール等)と、イソシアナート化合物とを混合した混合物、または反応させた樹脂が挙げられる。粉末状のポリオール(アクリルポリオール、ポリエステルポリオール、ポリエーテルポリオール等)と粉末状のイソシアナート化合物やブロック化イソシアナート化合物とからなる粉体塗料を用いることが好ましい。
シリコーン樹脂としては、分岐構造を有し、反応活性基としてシラノール基(Si−OH)を有しており、互いに脱水縮合することで硬化し、硬化後は三次元架橋構造の塗膜を形成し得るものが挙げられる。また、比較的低分子量のシリコーン樹脂(変性用シリコーン樹脂中間体)と他の熱硬化性樹脂(アルキッド樹脂、ポリエステル樹脂、エポキシ樹脂、アクリル樹脂等)とを併用してもよい。
シリコーン樹脂の市販品としては、JSR社製の「グラスカ HPC−7506」、カネカ社製の「ゼムラック(登録商標)」、エボニック社製の「SILIKOPON(登録商標) EF」、「SILIKOPON(登録商標) EW」、「SILIKOPON(登録商標) EC」、「SILIKOPON(登録商標) ED」等が挙げられる。
添加剤としては、組成物(α)で例示したものと同様のものが挙げられ、好ましい態様も同様である。
組成物(β)中の樹脂(C)の含有量は、組成物(β)(100質量%)のうち、20〜85質量%が好ましく、30〜80質量%がより好ましく、40〜75質量%が特に好ましい。
硬化剤がブロック化イソシアナート系硬化剤の場合、組成物(β)中のブロック化イソシアナート系硬化剤の含有量は、組成物(β)中の水酸基に対するイソシアナート基のモル比が0.05〜1.5となる量が好ましく、0.8〜1.2となる量が特に好ましい。該モル比が前記範囲の下限値以上であれば、粉体塗料の硬化度が高くなり、基材への塗膜の密着性、塗膜の硬度および耐薬品性等が優れる。該モル比が前記範囲の上限値以下であれば、塗膜が脆くなりにくく、しかも、塗膜の耐熱性、耐薬品性、耐湿性等が優れる。
組成物(α)中の樹脂(B)および組成物(β)中の樹脂(C)の合計の含有量は、組成物(α)中のPVDF(A)および樹脂(B)と組成物(β)中の樹脂(C)との合計の100質量部に対して、10〜90質量部が好ましく、20〜80質量部がより好ましく、25〜75質量部が特に好ましい。樹脂(B)および樹脂(C)の合計の含有量が前記下限値以上であれば、塗膜のコストを抑えることができる。樹脂(B)および樹脂(C)の合計の含有量が前記上限値以下であれば、塗膜の耐候性がさらに優れる。
粉体塗料(II)は、たとえば、下記工程(a)〜(g)を有する製造方法によって製造できる。
(a)PVDF(A)と樹脂(B)とを含み、必要に応じて添加剤を含んでもよい混合物を溶融混練して組成物(α)からなる混練物を得る工程。
(b)組成物(α)からなる混練物を粉砕して粉体(X)を得る工程。
(c)必要に応じて、粉体(X)の分級を行う工程。
(d)樹脂(C)を含み、フッ素樹脂を含まず、必要に応じて添加剤を含んでもよい、混合物を溶融混練して組成物(β)からなる混練物を得る工程。
(e)前記組成物(β)からなる混練物を粉砕して粉体(Y)を得る工程。
(f)必要に応じて、粉体(Y)の分級を行う工程。
(g)粉体(X)と粉体(Y)とをドライブレンドする工程。
各成分を混合し混合物を調製した後、該混合物を溶融混練して各成分が均一化された混練物を得る。
各成分は、あらかじめ粉砕して粉末状にすることが好ましい。
混合に用いる装置としては、高速ミキサ、V型ミキサ、反転ミキサ等が挙げられる。
溶融混練に用いる装置としては、1軸押出機、2軸押出機、遊星ギア等が挙げられる。
混練物は、冷却後、ペレットとすることが好ましい。
粉砕に用いる装置としては、ピンミル、ハンマーミル、ジェットミル等の粉砕機が挙げられる。
粒子径の大きすぎる粉体や粒子径の小さすぎる粉体を除去するために、粉砕後に分級を行うことが好ましい。分級を行う場合、粒子径が10μm未満の粒子および粒子径が100μmを超える粒子の少なくともいずれかを除去することが好ましい。
分級方法としては、ふるい分けによる方法、空気分級法等が挙げられる。
ドライブレンドに用いる装置としては、ハイスピードミキサ、ダブルコーンミキサ、ニーダ、ダンプラーミキサ、ミキシングシェーカ、ドラムシェーカ、ロッキングシェーカ等が挙げられる。
粉体(X)と粉体(Y)との混合比(粉体(X)/粉体(Y))は、10/90〜90/10(質量比)が好ましく、20/80〜80/20(質量比)がより好ましく、25/75〜75/25(質量比)が特に好ましい。粉体(X)の割合が前記下限値以上であれば、塗膜の耐候性がさらに優れる。粉体(Y)の割合が前記下限値以上であれば、塗膜のコストを抑えることができる。
以上説明した粉体塗料(II)にあっては、粉体(X)と粉体(Y)とを含むため、耐候性、折り曲げ加工性に優れた塗膜を形成できる。
本発明の塗装物品は、基材の表面に、粉体塗料(I)または粉体塗料(II)(以下、粉体塗料(I)および粉体塗料(II)をまとめて粉体塗料とも記す。)から形成されてなる塗膜を有する。
基材と前記塗膜との密着性を高めるために、基材と前記塗膜の間にプライマーを含むプライマー層を有していてもよい。
プライマーとしては、アクリル樹脂、ポリエステル樹脂およびエポキシ樹脂からなる群から選択される少なくとも一種の樹脂を適宜用いることができる。
プライマー層の膜厚は、1〜60μmが好ましく、5〜40μmがより好ましい。
基材の材質としては、アルミニウム、鉄、マグネシウム等の金属類が好ましく、防食性に優れ、軽量で、建築材料用途に優れた性能を有する点から、アルミニウムまたはアルミニウム合金が特に好ましい。アルミニウム合金としては、アルミニウムと、銅、マンガン、ケイ素、マグネシウム、亜鉛およびニッケルからなる群から選ばれる少なくとも一種との合金が挙げられる。
基材の形状、サイズ等は、特に限定されない。
化成処理薬剤としては、6価クロム系処理薬剤、3価クロム系処理薬剤、ジルコニウム系処理薬剤、チタニウム系処理薬剤などが挙げられる。環境への配慮の点から、ジルコニウム系処理薬剤、チタニウム系処理薬剤が好ましい。
具体的に、ジルコニウム系処理薬剤としては、日本シー・ビー・ケミカル社製の「ケミボンダ―(商品名)5507、5703、5705、5706」、日本パーカライジング社製の「パルコート3762、3796、20X」、ヘンケル社製の「アロジン(商品名)5200、4707」、日本ペイント社製の「アルサーフ(商品名)320、375」、バルクケミカル社製の「E−CLPS(商品名)1700、1900」等が挙げられ、チタニウム系処理薬剤としては、日本ペイント社製の「アルサーフ(商品名)CX4707」、バルクケミカル社製の「E−CLPS(商品名)2100、2900」等が挙げられる。
本発明の塗装物品は、下記工程(h)および工程(i)を有する製造方法によって製造できる。
(h)粉体塗料を基材に塗装し、粉体塗料の溶融物からなる溶融膜を形成する工程。
(i)溶融膜を冷却して塗膜を形成する工程。
粉体塗料を基材に塗装して基材上に粉体塗料の溶融物からなる溶融膜を形成する。
粉体塗料の溶融物からなる溶融膜は、基材への粉体塗料の塗装と同時に形成してもよく、基材に粉体塗料の粉体を付着させた後に基材上で粉体を加熱溶融させて形成してもよい。粉体塗料が熱硬化性の場合、粉体塗料が加熱溶融されるとほぼ同時に、組成物中の反応成分の硬化反応が開始するため、粉体塗料の加熱溶融と基材への付着はほぼ同時に行うか、粉体塗料の基材への付着の後に粉体塗料の加熱溶融を行う必要がある。
粉体塗装ガンからの粉体塗料の吐出量は、50〜200g/分が好ましい。
粉体塗装ガンのガン部分の先端から基材までの距離は、塗着効率の点から、150〜400mmが好ましい。
摩擦帯電型塗装ガンを用いる場合、摩擦帯電処理による粉体塗料の内部発生電流値は、塗着効率と塗膜の外観に優れる点から、1〜8μAが好ましい。
流動浸漬法においては、空気等のガスに担持されて流動している粉体塗料が収容されている流動槽中に、粉体塗料の溶融温度以上の温度に塗装面が加熱されている基材を浸漬し、粉体を基材の塗装面に付着させるとともに溶融し、基材上に所定の厚さの溶融膜を形成した後、塗装された基材を流動槽から取り出し、場合により所定時間溶融膜の溶融状態を維持し、その後溶融状態の塗膜を冷却し、場合によっては硬化して、塗膜が形成された基材とすることが好ましい。
溶融状態の溶融膜を室温(20〜25℃)まで冷却し、場合によっては硬化させて塗膜を形成する。
焼付け後の冷却は、急冷、徐冷のいずれでもよく、基材から塗膜がはがれにくい点で、徐冷が好ましい。
塗膜の厚さは、特に制限されないが、100〜1,000μmが好ましい。アルミカーテンウォール等の高層ビル用の部材等の用途では、20〜90μmが好ましい。海岸沿いに設置してあるエアコンの室外機、信号機のポール、標識等の耐候性の要求が高い用途では、100〜200μmが好ましい。なお、上述したように、厚さが厚い場合には、流動浸漬法を選択することで達成できる。
例1〜3は実施例であり、例4〜6は比較例であり、例7,8は参考例である。
[測定方法、評価方法]
測定方法および評価方法を以下に示す。
PVDFの19F−NMRを下記条件にて測定した。
測定装置:日本電子社製、ECP−400、
測定法:シングルパルス法(パルス幅45度、待ち時間4秒)、
測定溶媒:重DMF、
内部標準:CFCl3、
測定温度:60℃、
試料管外径:5mm。
得られたスペクトルにおいて−85〜−98ppm付近に現れる正規シーケンス由来のシグナルの積分値(I1)と−113〜−120ppm付近に現れる異種シーケンス由来のシグナルの積分値(I2)とから異種シーケンス比率を下式(1)によって算出した。
異種シーケンス比率(%)={I2/(I1+I2)}×100・・・(1)
Thermal Analysis System(パーキンエルマー社製)を用い、試料の10mgについて、温度範囲:−25〜200℃、昇温速度:10℃/分で熱収支を測定し、得られたチャートの融解ピークを融点とした。
試料の0.5質量%テトラヒドロフラン(以下、THFと記す。)溶液を、キャリア(THF)の流量を1.0mL/分とし、カラムとしてTSKgel G4000XL(東ソー社製)を用いて、スチレン換算の数平均分子量および質量平均分子量を求めた。
PVDF(A)の結晶化度は、EXSTAR DSC7020(SIIナノテクノロジー社製)を用い、試料の10mgを昇温速度:10℃/分で室温から200℃まで昇温し、得られたチャートの吸熱ピークの面積および試料量から融解熱量M1(J/g)を算出し、PVDFの完全結晶体の融解熱量M2(EXPRESS Polymer Letters,第4巻,第5号,2010年,p.284−291に記載の文献値:104.5J/g)とから下式(2)によって算出した。
結晶化度(%)=(M1/M2)×100 ・・・(2)
急冷時の結晶化度は、試料について、300℃で完全に溶解させた後、冷却速度:10℃/分で300℃から室温まで冷却し、再結晶化させ、EXSTAR DSC7020(SIIナノテクノロジー社製)を用い、再結晶化させた試料の10mgを昇温速度:10℃/分で室温から200℃まで昇温し、得られたチャートの吸熱ピークの面積および試料量から融解熱量M1(J/g)を算出し、PVDFの完全結晶体の融解熱量M2(EXPRESS Polymer Letters,第4巻,第5号,2010年,p.284−291に記載の文献値:104.5J/g)とから式(2)によって算出した。
徐冷時の結晶化度は、再結晶化条件である冷却速度を0.5℃/分に変更した以外は、急冷時の結晶化度と同様にして算出した。
樹脂の190℃における溶融粘度は、回転式レオメータ(アントンパール・ジャパン社製、レオメータMCR302)を用いて、昇温速度:10℃/分の条件にて測定した。
Thermal Analysis System(パーキンエルマー社製)を用い、試料の10mgについて、温度範囲:−25〜200℃、昇温速度:10℃/分で熱収支を測定し、得られたチャートの変曲点から中点法によってガラス転移温度を求めた。
粉体の平均粒子径は、レーザー回折式粒度分布測定機(Sympatec社製、Helos−Rodos)で測定し、50%平均体積粒度分布により求めた。
塗膜の表面の状態を目視し、以下の基準で判定した。
○(良好):塗膜の表面平滑性に優れ、表面凹凸、はじき、濡れ性の不良等が確認されなかった。
×(不良):塗膜の表面平滑性が悪く、表面凹凸、はじき、濡れ性の不良等が確認された。
光沢計(日本電色工業社製、PG−1M)を用い、JIS K 5600−4−7:1999年(ISO 2813:1994年)に準拠して塗膜の表面の60度鏡面光沢度を測定した。
JIS K 5600−5−1:1999年(ISO 1519:1973年)に準拠して試験片の折り曲げ試験を行い、以下の基準で折り曲げ加工性を評価した。
○(良好):塗膜の割れおよび基材からの塗膜のはがれは確認されなかった。
×(不良):塗膜の割れまたは基材からの塗膜のはがれが確認された。
キセノンウェザーメーター(スガ試験機社製)を用い、試験直前の硬化膜の表面の60度鏡面光沢度と、試験100時間後における硬化膜の表面の60度鏡面光沢度を、光沢計(日本電色工業社製、PG−1M)を用い、JIS K 5600−4−7:1999年(ISO 2813:1994年)に準拠して測定した。試験直前の60度鏡面光沢度の値を100%としたときの、試験100時間後の60度鏡面光沢度の値の割合を光沢保持率(単位:%)として算出し、下記基準で促進耐候性を判定した。なお、促進耐候試験では、通常は水を噴霧するが、水を噴霧する代わりに、1%の過酸化水素水を用いた。
<試験条件>
相対湿度:70%RH、
温度:50℃、
光源:80W/m2(300〜400nm)。
<判定基準>
○(良好):光沢保持率が50%以上であり、硬化膜の変色等は見られなかった。
×(不良):光沢保持率が50%未満であり、硬化膜の変色等が見られた。
沖縄県那覇市の屋外に試験片を設置し、設置直前の塗膜の表面の60度鏡面光沢度と、3年後における塗膜の表面の60度鏡面光沢度を、光沢計(日本電色工業社製、PG−1M)を用い、JIS K 5600−4−7:1999年(ISO 2813:1994年)に準拠して測定した。試験直前の60度鏡面光沢度の値を100%としたときの、3年後の60度鏡面光沢度の値の割合を光沢保持率(単位:%)として算出し、下記基準で促進耐候性を判定した。
<判定基準>
○(良好):光沢保持率が60%以上であり、変色はしなかった。
△(可):光沢保持率が40%以上60%未満であり、変色はしなかった。
×(不良):光沢保持率が40%未満であった、または黄色に変色した。
(PVDF(A−1)の製造)
撹拌機を備えた3Lの重合槽を脱気し、CF3CF2OCF2CF2OCF2COONH4の3gを溶解したイオン交換水の600g、アセトンの1.2g、過硫酸アンモニウムの0.3g、VDFの40gを仕込み、毎分300回転で36時間撹拌した。重合槽内を65℃に昇温して重合を開始させた。重合圧力は2.0MPaであった。重合中圧力が一定になるようにVDFを連続的に仕込み、VDFの連続仕込みが180gになった時点で重合槽内を室温に冷却し、未反応の単量体をパージした。重合槽を開放し、得られた水性乳化液を凍結させて、破壊して重合体を析出させた後、1,000mLのイオン交換水(25℃)で洗浄を3回繰り返した。150℃で12時間乾燥させて、PVDF(A−1)の170gを得た。PVDF(A−1)の異種シーケンス比率、融点、数平均分子量、質量平均分子量、分子量分布、結晶化度、溶融粘度を表1に示す。
(PVDF(Z−1)の製造)
撹拌機を備えた3Lの重合槽を脱気し、ペルフルオロオクタン酸アンモニウム塩の0.75g、ポリオキシエチレンアルキルエステル型の乳化剤(日光ケミカルズ社製、MYS40)の0.01g、アセトンの1.2g、過硫酸アンモニウムの0.3g、VDFの40gを仕込み、毎分300回転で36時間撹拌した。以降、重合槽内の温度を100℃に変更した以外は、製造例1と同様にしてPVDF(Z−1)の170gを得た。PVDF(Z−1)の異種シーケンス比率、融点、数平均分子量、質量平均分子量、分子量分布、結晶化度、溶融粘度を表1に示す。
なお、表1中のPVDF(Z−2)は、後述の市販PVDFである。
(樹脂(B−1)の製造)
冷却管、温度計を備えた1Lの四つ口フラスコに、脱イオン水の200mL、反応性乳化剤(三洋化成工業社製、エレミノール(登録商標) JS−2、コハク酸エステル誘導体)の2g、ポリオキシエチレンノニルフェニルエーテル(エチレンオキシド10モル付加)の2gを仕込んだ。窒素気流下において温浴中で80℃に達したところで、過硫酸アンモニウムの2質量%水溶液の10mLを添加した。MMAの140.2g、EMAの80.0gおよび連鎖移動剤としてのn−ラウリルメルカプタンの0.2gの混合物を1時間かけて滴下した。直後に過硫酸アンモニウムの2質量%水溶液の2mLを添加し、反応を開始した。3時間後に、フラスコ内の温度を85℃に上げ、1時間保持した後、300メッシュの金網でろ過して、青白色の水性分散液を得た。水性分散液を−25℃で凍結凝析し、脱水洗浄した後、80℃で真空乾燥し、白色のパウダーのMMA共重合体(MMA単位/EMA単位=2/1(モル比))である樹脂(B−1)の209.2gを得た。樹脂(B−1)のガラス転移温度は55℃、数平均分子量は53,000、質量平均分子量は92,000、分子量分布は1.75であった。また、190℃における溶融粘度は、0.314Pa・sであった。
(Z−2):ライニング用PVDF(Arkema社製、Kynar 761A)。異種シーケンス比率、融点、数平均分子量、質量平均分子量、分子量分布を表1に示す。
(B−2):ポリエステル樹脂(ダイセル・オルネクス社製、CRYLCOAT(登録商標) 4890−0、数平均分子量:2,500、質量平均分子量:4,400、水酸基価:30mgKOH/g、190℃における溶融粘度:5.25Pa・s)。
(B−3):エポキシ樹脂(ダイセル社製、EHPE3150、2,2−ビス(ヒドロキシメチル)−1−ブタノールの1,2−エポキシ−4−(2−オキシラニル)シクロヘキサン付加物、190℃における溶融粘度:0.254Pa・s)。
(D−1):酸化チタン顔料(デュポン社製、Ti−Pure(登録商標) R960、酸化チタン含有量:89質量%)。
(D−2):有機系紫外線吸収剤(BASF社製、Tinuvin(登録商標) 405、分子量:583.8、融点:76.3℃、揮発温度:348.5℃)。
(D−3):脱ガス剤(ベンゾイン)。
(D−4):粉体塗料用レベリング剤(ビックケミー社製、BYK(登録商標)−360P)。
表2に記載の各成分を、高速ミキサー(佑崎有限公司社製)を用いて、10〜30分程度混合し、粉末状の混合物を得た。該混合物を2軸押出機(サーモプリズム社製、16mm押出し機)を用いて、120℃のバレル設定温度にて溶融混練を行い、粉体塗料用組成物からなるペレットを得た。該ペレットを粉砕機(FRITSCH社製、ロータースピードミルP14)を用いて常温で粉砕し、200メッシュによる分級を行い、平均粒子径が約20μmの粉体を得た。
一方、PVDF(A−1)の含有量が、PVDF(A−1)と樹脂(B)との合計100質量部のうち、30質量部未満である粉体塗料用組成物からなる粉体塗料を用いた例4においては、得られた塗膜の耐候性が不充分であった。異種シーケンス比率が37%を超えるPVDF(Z−1)を含む粉体塗料用組成物からなる粉体塗料を用いた例5においては、得られた塗膜の耐候性が不充分であった。異種シーケンス比率が11〜37%であっても、融点が170℃を超えるPVDF(Z−2)を含む粉体塗料用組成物からなる粉体塗料を用いた例6においては、得られた塗膜の折り曲げ加工性が不充分であった。
[例7]
クロメート処理を行ったアルミニウム板に代えて、ヘンケル社製のクロム(VI)を含まない化成処理薬剤(商品名:「アロジン5200」)で処理したアルミニウム板を用い、プライマーとしてペルノックス社製エポキシ樹脂(商品名:「ペルパウダーPCE−900」)を、膜厚が30μmになるように静電塗装してから、例1で得られた粉体塗料を静電塗装した以外は例1と同様に塗膜が付いたアルミニウム板を得た。
プライマーとしてペルノックス社製エポキシ樹脂粉体塗料を用いなかった以外は例8と同様にして塗膜が付いたアルミニウム板を得た。
例1、例7および例8で得られた塗膜が付いたアルミニウム板を試験片として、腐食性および耐候性の評価を行った。結果を表3に記す。
JIS K 5600−7−1(1999年)に準拠し、アルミニウム板の腐食性を、以下の基準で評価した。
○(良好):塗膜のクロスカット部に、塗膜のふくれやアルミニウムの白錆の発生が確認されない。
×(不良):塗膜のクロスカット部に、塗膜のふくれやアルミニウムの白錆の発生が確認される。
なお、2014年7月1日に出願された日本特許出願2014−136305号の明細書、特許請求の範囲、要約書および図面の全内容をここに引用し、本発明の明細書の開示として、取り入れるものである。
Claims (10)
- 下記ポリビニリデンフルオリド(A)と、
アクリル樹脂、ポリエステル樹脂およびエポキシ樹脂からなる群から選択される少なくとも1種の樹脂(B)とを含み、
下記ポリビニリデンフルオリド(A)の含有量が、ポリビニリデンフルオリド(A)と前記樹脂(B)との合計100質量部のうち、30〜90質量部である
ことを特徴とする粉体塗料用組成物。
ポリビニリデンフルオリド(A):融点が151〜170℃であり、下記方法で求めた異種シーケンス比率が11〜37%である、ポリビニリデンフルオリド。
(異種シーケンス比率の求め方)
異種シーケンス比率は、溶媒として重N,N−ジメチルホルムアミド、内部標準としてCFCl3を用いてポリビニリデンフルオリドの19F−NMRを測定し、得られたスペクトルにおいて−85〜−98ppm付近に現れる正規シーケンス由来のシグナルの積分値(I1)と−113〜−120ppm付近に現れる異種シーケンス由来のシグナルの積分値(I2)とから下式(1)によって算出する。
異種シーケンス比率(%)={I2/(I1+I2)}×100・・・(1) - 前記粉体塗料用組成物が含む樹脂成分が、前記ポリビニリデンフルオリド(A)と前記樹脂(B)のみからなる、請求項1に記載の粉体塗料用組成物。
- さらに、顔料を含む、請求項1または2に記載の粉体塗料用組成物。
- 請求項1〜3のいずれか一項に記載の粉体塗料用組成物からなる粉体を含む、粉体塗料。
- 請求項1〜3のいずれか一項に記載の粉体塗料用組成物からなる第1の粉体と、
アクリル樹脂、ポリエステル樹脂、ウレタン樹脂、エポキシ樹脂およびシリコーン樹脂からなる群から選択される少なくとも1種の樹脂(C)を含み、フッ素樹脂を含まない粉体塗料用組成物からなる第2の粉体と
を含む、粉体塗料。 - 前記第1の粉体と前記第2の粉体との混合比(第1の粉体/第2の粉体)が、10/90〜90/10(質量比)である、請求項5に記載の粉体塗料。
- 基材の表面に、請求項4〜6のいずれか一項に記載の粉体塗料から形成されてなる塗膜を有する、塗装物品。
- 前記基材の材質が、化成処理薬剤で表面処理されたアルミニウムまたはアルミニウム合金である、請求項7に記載の塗装物品。
- 前記化成処理薬剤が、クロムを含まない、ジルコニウム系処理薬剤またはチタニウム系処理薬剤である、請求項8に記載の塗装物品。
- 基材の表面と、前記粉体塗料から形成されてなる塗膜の間に、さらに、アクリル樹脂、ポリエステル樹脂およびエポキシ樹脂からなる群から選択される少なくとも一種のプライマーからなるプライマー層を有する、請求項7に記載の塗装物品。