JPWO2011007700A1 - 太陽電池用裏面保護シート及びその製造方法 - Google Patents
太陽電池用裏面保護シート及びその製造方法 Download PDFInfo
- Publication number
- JPWO2011007700A1 JPWO2011007700A1 JP2010549368A JP2010549368A JPWO2011007700A1 JP WO2011007700 A1 JPWO2011007700 A1 JP WO2011007700A1 JP 2010549368 A JP2010549368 A JP 2010549368A JP 2010549368 A JP2010549368 A JP 2010549368A JP WO2011007700 A1 JPWO2011007700 A1 JP WO2011007700A1
- Authority
- JP
- Japan
- Prior art keywords
- layer
- functional group
- reactive functional
- film
- base film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
前記コート層が、反応性官能基(Y)を有する金属アルコキシドと、前記反応性官能基(Y)と反応する反応性の官能基(X)を有するアクリル系モノマーと、反応性の官能基(X)を有さないアクリル系モノマーとからなる樹脂成分を有する液状体の塗膜を硬化してなる三元共重合体層である太陽電池用裏面保護シート。
[2] 基材フィルムがフィルムを2層以上にシラン系の接着剤で貼り合わせた積層フィルムであることを特徴とする[1]に記載の太陽電池用裏面保護シート。
[3] 前記基材フィルムが1層からなり、該1層が無機酸化物蒸着膜付きフィルムであることを特徴とする、上記[1]に記載の太陽電池用裏面保護シート。
[4] 前記基材フィルムが2層以上からなり、その少なくとも1層が無機酸化物蒸着膜付きフィルムであることを特徴とする、上記[1]又は[2]に記載の太陽電池用裏面保護シート。
[5] 基材フィルムの材質が、ポリエステル系樹脂、ポリオレフィン系樹脂、ポリスチレン系樹脂、ポリアミド樹脂、ポリカーボネート樹脂、及びポリアクリロニトリル樹脂から選ばれる少なくとも一種であることを特徴とする[1]〜[4]のいずれか1つに記載の太陽電池用裏面保護シート。
[6] 前記コート層が1層構成である場合はその1層に、多層構成である場合はその少なくとも1層に、紫外線散乱剤又は/及び紫外線吸収剤が混合されていることを特徴とする、上記[1]〜[5]のいずれか1つに記載の太陽電池用裏面保護シート。
[7] 少なくとも1層からなる基材フィルムを用意する工程と、
反応性官能基(Y)を有する金属アルコキシドと、前記反応性官能基(Y)と反応する反応性の官能基(X)を有するアクリル系モノマーと、反応性の官能基(X)を有さないアクリル系モノマーとからなる樹脂成分を有する液状体を用意する工程と、
前記基材フィルムの片面又は両面に、前記液状体を塗布することにより少なくとも1層の塗膜を形成する工程と、
前記少なくとも1層の塗膜を硬化させて少なくとも1層の三元共重合体層からなるコート層を形成する工程と、
を有する太陽電池用裏面保護シートの製造方法。
[8] 前記液状体は、反応性官能基(Y)を有する金属アルコキシドと、前記反応性官能基(Y)と反応する反応性の官能基(X)を有するアクリル系モノマーと、反応性の官能基(X)を有さないアクリル系モノマーとからなる樹脂成分を水系溶媒に分散させたエマルションであることを特徴とする、上記[7]に記載の太陽電池用裏面保護シートの製造方法。
[9] 前記液状体は、反応性官能基(Y)を有する金属アルコキシドと、前記反応性官能基(Y)と反応する反応性の官能基(X)を有するアクリル系モノマーと、反応性の官能基(X)を有さないアクリル系モノマーとからなる樹脂成分を非水系溶媒に溶解させた樹脂溶液であることを特徴とする、上記[7]に記載の太陽電池用裏面保護シートの製造方法。
[10] 前記基材フィルムは、フィルムを2層以上にシラン系の接着剤で貼り合わせた積層フィルムであることを特徴とする、上記[7]〜[9]のいずれか1つに記載の太陽電池用裏面保護シートの製造方法。
[11] 前記基材フィルムは、1層からなり、該1層が無機酸化物蒸着膜付きフィルムであることを特徴とする、上記[7]〜[10]のいずれか1つに記載の太陽電池用裏面保護シートの製造方法。
[12] 前記基材フィルムは、2層以上からなり、その少なくとも1層が無機酸化物蒸着膜付きフィルムであることを特徴とする、上記[7]〜[10]のいずれか1つに記載の太陽電池用裏面保護シートの製造方法。
[13] 基材フィルムの材質が、ポリエステル系樹脂、ポリオレフィン系樹脂、ポリスチレン系樹脂、ポリアミド樹脂、ポリカーボネート樹脂、及びポリアクリロニトリル樹脂から選ばれる少なくとも一種であることを特徴とする、上記[7]〜[12]のいずれか1つに記載の太陽電池用裏面保護シートの製造方法。
[14] 前記液状体を用意する工程において、前記三元共重合体層が1層構成である場合はその1層を構成するための液状体に、前記三元共重合体層が多層構成である場合はその少なくとも1層を構成するための液状体に、紫外線散乱剤又は/及び紫外線吸収剤を混合することを特徴とする、上記[7]〜[13]のいずれか1つに記載の太陽電池用裏面保護シートの製造方法。
また、上記少なくとも1層からなる基材フィルムの少なくとも1層は無機酸化物蒸着膜付きフィルムとすることが好ましい。すなわち、基材フィルムが1層からなる場合は、その1層のフィルムが無機酸化物蒸着膜付きフィルムであることが好ましい。そして、基材フィルムを多層構成とする場合は、その内の少なくとも1層を無機酸化物蒸着膜付きフィルムとすることが好ましく、その場合は各層間にシラン系接着剤を介装して各層を接着する。
基材フィルム1としては、太陽電池モジュールを形成する際の熱プレスにおいて、加温されるため所定の加熱時間内で適宜調整しながら溶融軟化しない範囲内で成形加工可能な樹脂フィルムを用いることができる。かかる基材フィルムの材質としては、ポリエステル系樹脂、ポリオレフィン系樹脂、ポリスチレン系樹脂、ポリアミド樹脂、ポリカーボネート樹脂、及びポリアクリロニトリル樹脂から選ばれる少なくとも一種を挙げることができる。換言すれは、基材フィルム1の種類としては、例えば、ポリエチレンテレフタレート(PET)、ポリエチレンナフタレート(PEN)などのポリエステル系フィルム、ポリエチレン、ポリプロピレン等のポリオレフィン系フィルム、ポリスチレン系フィルム、ポリアミドフィルム、ポリカーボネートフィルム、ポリアクリロニトリルフィルム、ポリイミドフィルム等のエンプラフィルムが用いられる。
基材フィルム1の厚さは3〜300μmの範囲とする。
基材フィルム1の片面又は両面(図1では両面)に、厚さ5〜300μmの範囲で、コート層2を形成するが、該コート層2は、反応性官能基(Y)を有する金属アルコキシド、反応性官能基(X)を有するアクリル系モノマー、反応性の官能基(X)を有さないアクリル系モノマーからなる樹脂成分を有する液状体の塗膜を硬化させた三元共重合体層である。ここでいう液状体とは、反応性官能基(Y)を有する金属アルコキシドと、前記反応性官能基(Y)と反応する反応性の官能基(X)を有するアクリル系モノマーと、反応性の官能基(X)を有さないアクリル系モノマーとの3種のモノマーのみからなる樹脂成分を所定の濃度(好ましくは、最終的に濃度50重量%)で含む水系エマルションであるか、前記3種のモノマーのみからなる樹脂成分を非水系の溶媒に溶解した樹脂溶液である。
かかる反応性官能基(X)を有さないアクリルモノマーしては、α,β−エチレン性不飽和モノマーとして、(メタ)アクリル酸エステル[例えば(メタ)アクリル酸メチル、(メタ)アクリル酸エチル、(メタ)アクリル酸n−プロピル、(メタ)アクリル酸イソプロピル、(メタ)アクリル酸n−ブチル、(メタ)アクリル酸イソブチル、(メタ)アクリル酸t−ブチル、(メタ)アクリル酸2−エチルヘキシル、メタクリル酸ラウリル、アクリル酸フェニル、(メタ)アクリル酸イソボルニル、メタクリル酸シクロヘキシル、(メタ)アクリル酸t−ブチルシクロヘキシル、(メタ)アクリル酸ジシクロペンタジエニル、(メタ)アクリル酸ジヒドロジシクロペンタジエニル等]、重合性芳香族化合物(例えば、スチレン、α−メチルスチレン、ビニルケトン、t−ブチルスチレン、パラクロロスチレン及びビニルナフタレン等)、重合性ニトリル(例えば、アクリロニトリル、メタクリロニトリル等)、α−オレフィン(例えば、エチレン、プロピレン等)、ビニルエステル(例えば、酢酸ビニル、プロピオン酸ビニル等)、ジエン(例えば、ブタジエン、イソプレン等)、重合性芳香族化合物、重合性ニトリル、α−オレフィン、ビニルエステル、及びジエンなどが挙げられる。
水系溶媒としては、イオン交換水などを用いる。必要に応じてアルコールなどのような有機溶剤を含む水性媒体中に、慣用の分散剤を加えて分散性を向上させることもできる。その後、前記水系溶媒に対して、慣用のホモジナイザー(例えば、マイクロテック・ニチオン社製、商品名「NR-300」)を用いて、均一に分散させ、加熱撹拌下、上述組み合わせで3種、または予め2種の組み合わせでモノマーおよび重合開始剤を滴下することにより重合を行うことができる。樹脂成分の濃度としては、30〜60重量%とすることが好ましい。
非水系溶媒としては、トルエンや酢酸エチルなどの有機溶剤が用いられる。非水系溶媒としては、その他に、キシレン、N−メチルピロリドン、ブチルアセテート、比較的高沸点の脂肪族及び/もしくは芳香族、ブチルジグリコールアセテート、アセトン等などを適宜用いることもできる。
基材フィルム1の片面又は両面(図1では両面)に、乾燥後の膜厚が6〜350μmとなるように、前記液状体の塗膜を形成する。液状体の塗布方法としては、一般に用いられるディッピング法、ロールコーティング法、スクリーン印刷法、スプレー法などの従来公知の手段を用いることができる。また、厚さを均一にコントロールするために、薄いコーティング層を多重に積層して所定の膜厚としてもよい。多重に積層する場合は、先に塗布した層を乾燥させた後に次の層を塗布し、その層を乾燥させて、さらに次の層を塗布することを繰り返す。
この工程には、塗膜を乾燥させる塗膜乾燥工程と、乾燥後、最終的に三元共重合体から構成される硬化膜(三元共重合体層)にする乾燥塗膜硬化工程とが、含まれる。
この塗膜乾燥工程では、上記液状体の塗膜から溶媒を気化させて、塗膜の形状を安定化させる。乾燥の温度は80℃〜120℃が好ましい。80℃未満では溶媒の気化が不十分になり、100℃を超えると、塗膜中の未反応モノマーの重合反応が開始される。乾燥時間は、乾燥温度に依存するが、例えば、好ましくは、100℃で、10分〜15分である。
乾燥により形状が安定化した塗膜を、塗膜中の未反応モノマーを重合させることにより、硬化させる。未反応モノマーの重合温度は、80℃〜120℃が好ましい。80℃未満では、重合が不十分となり、120℃を超えると、PET上に膜形成させる上で、PETの収縮が始まり、塗膜も密着性等に悪影響を与えるという不都合が生じる。重合時間は、重合温度に依存するが、例えば、好ましくは、100℃で、10分〜15分である。
上記三元共重合体層からなるコート層2は柔軟性を保ちながらガスバリア性及び耐侯性を有しているので、得られるシートは、太陽電池用裏面保護シートとして、長期信頼性に優れたものとなる。
本発明の実施例1では、液状体として、シャラスターMKの主剤15重量部に対して、3−グリシドキシプロピルトリエトキシシラン(1重量部)を配合したものを用意した。
得られた乾燥塗膜を100℃10分間加熱して、塗膜を構成する未反応モノマーを重合させて、三元共重合体層(コート層)を得た。得られた膜の厚みは、20μmであった。
以上により、厚さ125μmの基材フィルムの両面に20μm厚のコート層(三元共重合体層)が積層されてなるシート(太陽電池用裏面保護シート)を得た。
本発明の実施例2では、下記(表2)に示すように、基材フィルムとして、厚さ75μmのポリエチレンテレフタレート(PET)フィルムと、酸化珪素や酸化アルミを数十nm蒸着された厚さ12μmのポリエチレンテレフタレート(PET)フィルム(東洋紡績株式会社製、商品名「エコシアールVE500」)とを、厚さ5μmのアルコキシシラン系接着(3−メタクリロキシプロピルトリエトキシシラン)層を設けて接着した多層フィルムを用いた。また、液状体としては、実施例1で用いた液状体と同一の液状体を用意した。
得られた乾燥塗膜を100℃、10分間加熱して、塗膜を構成する未反応モノマーを重合させて、三元共重合体層(コート層)を得た。得られた膜の厚みは、20μmであった。
以上により、厚さ92μmの基材フィルムの両面に20μm厚のコート層(三元共重合体層)が積層されてなるシート(太陽電池用裏面保護シート)を得た。
本発明の実施例3では、下記(表2)に示すように、基材フィルムとして、厚さ75μmのポリエチレンテレフタレート(PET)フィルムと、厚さ50μmのポリエチレンテレフタレート(PET)フィルムとを、厚さ5μmのアルコキシシラン系接着(3−メタクリロキシプロピルトリエトキシシラン)層を介して接着した多層フィルムを用いた。また、液状体としては、実施例1で用いた液状体と同一の液状体を用意した。
得られた乾燥塗膜を100℃、10分間加熱して、塗膜を構成する未反応モノマーを重合させて、三元共重合体層(コート層)を得た。得られた膜の厚みは、20μmであった。
以上により、厚さ130μmの基材フィルムの両面に20μm厚のコート層(三元共重合体層)が積層されてなるシート(太陽電池用裏面保護シート)を得た。
本発明の実施例4では、下記(表2)に示すように、基材フィルムとして厚さ125μmのポリエチレンテレフタレート(PET)フィルムを用意した。
液状物としては、シャラスターMKの主剤15重量部に対して、3−イソシアネートプロピルトリエトシキシラン(1重量部)を配合したものを用意した。
得られた乾燥塗膜を100℃10分間加熱して、塗膜を構成する未反応モノマーを重合させて、三元共重合体層(コート層)を得た。得られた膜の厚みは、20μmであった。
以上により、厚さ125μmの基材フィルムの両面に20μm厚のコート層(三元共重合体層)が積層されてなるシート(太陽電池用裏面保護シート)を得た。
また、比較例1として市販されている太陽電池裏面保護シートを用いた。比較例1のシートは、下記(表3)に示すように、厚さ125μmのPETフィルムの片面にガスバリア層として厚さ20nmのSiO2蒸着膜が形成された積層フィルム(基材)の両面に接着剤を用いて厚さ25μmのフッ素樹脂フィルム(PVF)を貼り合わせた構成である。
実施例1〜4及び比較例1の各太陽電池用裏面保護シートの性能評価として、サンシャインカーボンアーク灯式耐侯性試験機(スガ試験機株式会社製、商品名「WEL−300L」)による紫外線照射前後における水蒸気透過量、引っ張り強度保持率、及び絶縁耐電圧を測定した。さらに下記R曲げ(柔軟性)耐久試験後の水蒸気透過量、引っ張り強度保持率、及び絶縁耐電圧についても測定した。その結果を(表2、3)に併記した。
上記方法で作成されたシート状サンプル(A4サイズ)から15cm角を切り取り、切り取ったシートの向かい合う両端部を持って両端部が着き合わさるところまで、シート中央部をR曲げる。この屈曲を100回繰り返す。
2 コート層
かかる反応性官能基(X)を有さないアクリルモノマーしては、α,β−エチレン性不飽和モノマーとして、(メタ)アクリル酸エステル[例えば(メタ)アクリル酸メチル、(メタ)アクリル酸エチル、(メタ)アクリル酸n−プロピル、(メタ)アクリル酸イソプロピル、(メタ)アクリル酸n−ブチル、(メタ)アクリル酸イソブチル、(メタ)アクリル酸t−ブチル、(メタ)アクリル酸2−エチルヘキシル、メタクリル酸ラウリル、アクリル酸フェニル、(メタ)アクリル酸イソボルニル、メタクリル酸シクロヘキシル、(メタ)アクリル酸t−ブチルシクロヘキシル、(メタ)アクリル酸ジシクロペンタジエニル、(メタ)アクリル酸ジヒドロジシクロペンタジエニル等]などが挙げられる。
前記コート層が、反応性官能基(Y)を有する金属アルコキシドと、前記反応性官能基(Y)と反応する反応性の官能基(X)を有するアクリル系モノマーと、反応性の官能基(X)を有さないアクリル系モノマーとからなる樹脂成分を有する液状体の塗膜を硬化してなる三元共重合体層である太陽電池用裏面保護シート。
[2] 基材フィルムがフィルムを2層以上にシラン系の接着剤で貼り合わせた積層フィルムであることを特徴とする[1]に記載の太陽電池用裏面保護シート。
[3] 前記基材フィルムが1層からなり、該1層が無機酸化物蒸着膜付きフィルムであることを特徴とする、上記[1]に記載の太陽電池用裏面保護シート。
[4] 前記基材フィルムが2層以上からなり、その少なくとも1層が無機酸化物蒸着膜付きフィルムであることを特徴とする、上記[1]又は[2]に記載の太陽電池用裏面保護シート。
[5] 基材フィルムの材質が、ポリエステル系樹脂、ポリオレフィン系樹脂、ポリスチレン系樹脂、ポリアミド樹脂、ポリカーボネート樹脂、及びポリアクリロニトリル樹脂から選ばれる少なくとも一種であることを特徴とする[1]〜[4]のいずれか1つに記載の太陽電池用裏面保護シート。
[6] 前記コート層が1層構成である場合はその1層に、多層構成である場合はその少なくとも1層に、紫外線散乱剤又は/及び紫外線吸収剤が混合されていることを特徴とする、上記[1]〜[5]のいずれか1つに記載の太陽電池用裏面保護シート。
[7] 少なくとも1層からなる基材フィルムを用意する工程と、
反応性官能基(Y)を有する金属アルコキシドと、前記反応性官能基(Y)と反応する反応性の官能基(X)を有するアクリル系モノマーと、反応性の官能基(X)を有さないアクリル系モノマーとからなる樹脂成分を有する液状体を用意する工程と、
前記基材フィルムの片面又は両面に、前記液状体を塗布することにより少なくとも1層の塗膜を形成する工程と、
前記少なくとも1層の塗膜を硬化させて少なくとも1層の三元共重合体層からなるコート層を形成する工程と、
を有する太陽電池用裏面保護シートの製造方法。
[8] 前記液状体は、反応性官能基(Y)を有する金属アルコキシドと、前記反応性官能基(Y)と反応する反応性の官能基(X)を有するアクリル系モノマーと、反応性の官能基(X)を有さないアクリル系モノマーとからなる樹脂成分を水系溶媒に分散させたエマルションであることを特徴とする、上記[7]に記載の太陽電池用裏面保護シートの製造方法。
[9] 前記液状体は、反応性官能基(Y)を有する金属アルコキシドと、前記反応性官能基(Y)と反応する反応性の官能基(X)を有するアクリル系モノマーと、反応性の官能基(X)を有さないアクリル系モノマーとからなる樹脂成分を非水系溶媒に溶解させた樹脂溶液であることを特徴とする、上記[7]に記載の太陽電池用裏面保護シートの製造方法。
[10] 前記基材フィルムは、フィルムを2層以上にシラン系の接着剤で貼り合わせた積層フィルムであることを特徴とする、上記[7]〜[9]のいずれか1つに記載の太陽電池用裏面保護シートの製造方法。
[11] 前記基材フィルムは、1層からなり、該1層が無機酸化物蒸着膜付きフィルムであることを特徴とする、上記[7]〜[9]のいずれか1つに記載の太陽電池用裏面保護シートの製造方法。
[12] 前記基材フィルムは、2層以上からなり、その少なくとも1層が無機酸化物蒸着膜付きフィルムであることを特徴とする、上記[7]〜[10]のいずれか1つに記載の太陽電池用裏面保護シートの製造方法。
[13] 基材フィルムの材質が、ポリエステル系樹脂、ポリオレフィン系樹脂、ポリスチレン系樹脂、ポリアミド樹脂、ポリカーボネート樹脂、及びポリアクリロニトリル樹脂から選ばれる少なくとも一種であることを特徴とする、上記[7]〜[12]のいずれか1つに記載の太陽電池用裏面保護シートの製造方法。
[14] 前記液状体を用意する工程において、前記三元共重合体層が1層構成である場合はその1層を構成するための液状体に、前記三元共重合体層が多層構成である場合はその少なくとも1層を構成するための液状体に、紫外線散乱剤又は/及び紫外線吸収剤を混合することを特徴とする、上記[7]〜[13]のいずれか1つに記載の太陽電池用裏面保護シートの製造方法。
Claims (14)
- 少なくとも1層からなる基材フィルムと、該基材フィルムの片面又は両面に形成された少なくとも1層からなるコート層とを有してなる太陽電池用裏面保護シートであって、
前記コート層が、反応性官能基(Y)を有する金属アルコキシドと、前記反応性官能基(Y)と反応する反応性の官能基(X)を有するアクリル系モノマーと、反応性の官能基(X)を有さないアクリル系モノマーとからなる樹脂成分を有する液状体の塗膜を硬化してなる三元共重合体層である太陽電池用裏面保護シート。 - 前記基材フィルムがフィルムを2層以上にシラン系の接着剤で貼り合わせた積層フィルムであることを特徴とする請求項1に記載の太陽電池用裏面保護シート。
- 前記基材フィルムが1層からなり、該1層が無機酸化物蒸着膜付きフィルムであることを特徴とする請求項1に記載の太陽電池用裏面保護シート。
- 前記基材フィルムが2層以上からなり、その少なくとも1層が無機酸化物蒸着膜付きフィルムであることを特徴とする請求項1又は2に記載の太陽電池用裏面保護シート。
- 前記基材フィルムの材質が、ポリエステル系樹脂、ポリオレフィン系樹脂、ポリスチレン系樹脂、ポリアミド樹脂、ポリカーボネート樹脂、及びポリアクリロニトリル樹脂から選ばれる少なくとも一種であることを特徴とする請求項1〜4のいずれか1項に記載の太陽電池用裏面保護シート。
- 前記コート層が1層構成である場合はその1層に、多層構成である場合はその少なくとも1層に、紫外線散乱剤又は/及び紫外線吸収剤が混合されていることを特徴とする請求項1〜5のいずれか1項に記載の太陽電池用裏面保護シート。
- 少なくとも1層からなる基材フィルムを用意する工程と、
反応性官能基(Y)を有する金属アルコキシドと、前記反応性官能基(Y)と反応する反応性の官能基(X)を有するアクリル系モノマーと、反応性の官能基(X)を有さないアクリル系モノマーとからなる樹脂成分を有する液状体を用意する工程と、
前記基材フィルムの片面又は両面に、前記液状体を塗布することにより少なくとも1層の塗膜を形成する工程と、
前記少なくとも1層の塗膜を硬化させて少なくとも1層の三元共重合体層からなるコート層を形成する工程と、
を有する太陽電池用裏面保護シートの製造方法。 - 前記液状体は、反応性官能基(Y)を有する金属アルコキシドと、前記反応性官能基(Y)と反応する反応性の官能基(X)を有するアクリル系モノマーと、反応性の官能基(X)を有さないアクリル系モノマーとからなる樹脂成分を水系溶媒に分散させたエマルションであることを特徴とする請求項7に記載の太陽電池用裏面保護シートの製造方法。
- 前記液状体は、反応性官能基(Y)を有する金属アルコキシドと、前記反応性官能基(Y)と反応する反応性の官能基(X)を有するアクリル系モノマーと、反応性の官能基(X)を有さないアクリル系モノマーとからなる樹脂成分を非水系溶媒に溶解させた樹脂溶液であることを特徴とする請求項7に記載の太陽電池用裏面保護シートの製造方法。
- 前記基材フィルムは、フィルムを2層以上にシラン系の接着剤で貼り合わせた積層フィルムであることを特徴とする請求項7〜9のいずれか1項に記載の太陽電池用裏面保護シートの製造方法。
- 前記基材フィルムは、1層からなり、該1層が無機酸化物蒸着膜付きフィルムであることを特徴とする請求項7〜10のいずれか1項に記載の太陽電池用裏面保護シートの製造方法。
- 前記基材フィルムは、2層以上からなり、その少なくとも1層が無機酸化物蒸着膜付きフィルムであることを特徴とする請求項7〜10のいずれか1項に記載の太陽電池用裏面保護シートの製造方法。
- 前記基材フィルムの材質が、ポリエステル系樹脂、ポリオレフィン系樹脂、ポリスチレン系樹脂、ポリアミド樹脂、ポリカーボネート樹脂、及びポリアクリロニトリル樹脂から選ばれる少なくとも一種であることを特徴とする請求項7〜12のいずれか1項に記載の太陽電池用裏面保護シートの製造方法。
- 前記液状体を用意する工程において、前記三元共重合体層が1層構成である場合はその1層を構成するための液状体に、前記三元共重合体層が多層構成である場合はその少なくとも1層を構成するための液状体に、紫外線散乱剤又は/及び紫外線吸収剤を混合することを特徴とする請求項7〜13のいずれか1つに記載の太陽電池用裏面保護シートの製造方法。