JPS6330291A - 光記録媒体 - Google Patents

光記録媒体

Info

Publication number
JPS6330291A
JPS6330291A JP61174496A JP17449686A JPS6330291A JP S6330291 A JPS6330291 A JP S6330291A JP 61174496 A JP61174496 A JP 61174496A JP 17449686 A JP17449686 A JP 17449686A JP S6330291 A JPS6330291 A JP S6330291A
Authority
JP
Japan
Prior art keywords
layer
recording
selenium
fluoride
nitrogen
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP61174496A
Other languages
English (en)
Other versions
JPH0533675B2 (ja
Inventor
Masaki Ito
雅樹 伊藤
Katsuji Nakagawa
活二 中川
Akio Morimoto
昭男 森本
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NEC Corp
Original Assignee
NEC Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NEC Corp filed Critical NEC Corp
Priority to JP61174496A priority Critical patent/JPS6330291A/ja
Priority to US07/043,626 priority patent/US4839208A/en
Priority to EP87106262A priority patent/EP0243958B1/en
Priority to DE8787106262T priority patent/DE3781926T2/de
Publication of JPS6330291A publication Critical patent/JPS6330291A/ja
Publication of JPH0533675B2 publication Critical patent/JPH0533675B2/ja
Granted legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 ［産業上の利用分野］ 本発明はレーザ光によって情報を記録再生することので
きる光記録媒体に関するものである。
［従来の技術］ レーザ光によって情報を媒体に記録し、かつ再生する光
デイスクメモリは、記録密度が高いことから大容量記録
装置として優れた特徴を有している。この光記録媒体材
料としては、テルル（丁ｅ）等゛のカルコゲン元素又は
これらの化合物が使用されている（特公昭４７−２６８
９７号公報）。とくに耐候性の良いテルル−セレン系合
金はよく使用されている（特公昭５４−４１９０２＠公
報、特公昭５７−７９１９号公報、特公昭５７−５６０
５８号公報）。
近年、記録装置を小型化するため、レーザ光源としては
半導体レーザが使用されてきている。半導体レーデは発
振波長がａｏｏｏ八前後へあるが、テルル−セレン系合
金はこの波長帯にも比較的よく適合し、適度な反射率と
適度な吸収率が得られる（フィジカ・スティタス・ソリ
ダイ、　７，１８９．１９６４（ｐｈｙｓ、　５ｔａｔ
、　ｓｏｌ、　７．１８９．１９６４）　）。
このテルル−セレン系合金を光記録層として用いた光記
録媒体は第２図に示すような構成になっている。すなわ
ち基板１に隣接してテルル−セレン系合金よりなる記録
層２１が設けられている。記録用レーザ光は基板１を通
して記録層２１に集光照射され、ピット２２が形成され
る。基板１としてはポリカーボネート、ポリオレフィン
、ポリメチルペンテン、アクリル、エポキシ樹脂等の合
成樹脂やガラスが使用され、基板１にはピットが同心円
状あるいはスパイラル状に一定間隔で精度よく記録され
るように通常案内溝が設けられている。
レーザビーム径程度の幅の溝に光が入射すると光は回折
され、ビーム中心が溝からずれるにつれて回折光強度の
空間分布が変化するので、これを検出してレーザビーム
を溝の中心に入射させるようにサーボ系が構成されてい
る。溝の幅は通常０．３〜１．３卯であり、溝の深さは
使用するレーザ波長の１７１２から１７４の範囲に設定
される。集光に関しても同様にサーボ系が構成されてい
る。情報の読み出しは、記録のときよりも弱いパワーの
レーザ光をピット上を通過するように照射することによ
り、ピットの有無に起因する反射率の変化を検出して行
なう。
［発明が解決しようとする問題点］ しかしながら、テルル−セレン系合金層のみを記録層と
して用いた光記録媒体では信号品質が充分に良好ではな
かった。
一方、本発明者らは記録層をテルルとセレンと窒素を主
成分とすることにより、信号品質が良好となることを見
出し、すでに提案している。本発明はこれをさらに改善
したものであり、耐候性がよくかつ高感度で信号品質の
良好な光記録媒体を提供することを目的とする。
［問題点を解決するための手段］ 本発明は基板と、レーザ光によって一部が選択的に除去
されて情報を記録する前記基板上に形成された記録層と
からなる光記録媒体において、前記記録層がフッ化物を
主成分とする前記基板側に形成された層と、この層に隣
接して前記基板の外方に形成されたテルル、セレンおよ
び窒素を主成分とする層とを少なくとも有していること
を特徴とする光記録媒体である。
本発明においては例えば第１図に示すように基板１上に
フッ化物を主成分とする層２およびテルル、セレンおよ
び窒素を主成分とする層（以下テて記録層を形成する。
基板１とテルル−セレン−窒素層３との間にフッ化物層
２を設けることにより、記録により形成されるピットが
大きく拡がらないようになる。したがって、ピットをつ
めて記録できるので゛高密度記録が可能となる。又、記
録パワー変動に対する余裕度も大きくなるので実用的な
光記録媒体となる。ざらに又、大きなピットが形成され
ないためトラッキングやフォーカスサーボが不安定にな
らないので実用的な光記録媒体となる。
フッ化物層としては種々のフッ化物を使用することがで
きるが、その中ではフッ化セリウム、フッ化ランタンな
どの希土類元素との化合物ヤノッ化マグネシウム等が望
ましい。膜の内部応力が小さくなるように作製すること
が膜のクランクを防止する点で重要である。フッ化物層
の膜厚は、５八から２５００への範囲が望ましい。フッ
化物層の屈折率が基板の屈折率よりも小さい場合には膜
中波長の１７４か３７４の厚さに設定することにより媒
体反則率を極大にすることができる。フッ化物層で・１ の屈折率が基板の屈折率よりも大きい場合には膜中波長
の１７２の厚さに設定することにより媒体反射率が小さ
くなることを防ぐことができる。逆に、膜中波長の１７
４或いは３／４の厚さに設定すれば、媒体反射率は小さ
くなるものの記録膜での吸収は最大となるので高感度化
することができる。
テルル−セレン−窒素層の厚さは１００八から１０００
人の範囲が記録再生特性の観点から望ましく、窒素の含
有量は原子数パーセントで２パ一セント以上２０パーセ
ント未満が記録再生特性、耐候性の観点から望ましく、
セレンの含有量は原子数パーセントで２パーセントから
５０パーセントの範囲が耐候性の観点から望ましい。
テルル−セレン−窒素層には鉛、ヒ素、スズ、ゲルマニ
ウム、カドミウム、タリウム、アンチモン、イオウ、リ
ン、インジウム、ガリウム、曲鉛、ビスマス、アルミニ
ウム、銅、銀、マグネシウム、タンタル、金、パラジウ
ム、コバルトの群から選ばれた少なくとも１種の元素が
添加されていてもよい。この場合、ピットの形状を良好
に整える場合がある。ただし添加量は原子数パーセント
で２０パ一セント未満が望ましい。
成膜方法はスパッタリング法の他に、蒸着法、反応性蒸
着法、イオンブレーティング法、イオンビームデポジシ
ョン法等でもよい。
基板としてはポリカーボネート、ポリオレフィン、ポリ
メチルペンテン、アクリル、エポキシ樹脂等の合成樹脂
やガラスなど通常使用されているものが用いられる。
［作　用］ 基板とテルル−セレン−窒素層の間にフッ化物層を介在
させることによってピットが大きく拡がらなくなり、優
れた光記録媒体を得ることができる。これはテルル−セ
レン−窒素層の有無による表面エネルギーの差がフッ化
物層の形成により変化するためであると考えられる。
［実施例］ 以下、本発明の実施例について説明する。
ｉｏｏ’ｃで２時間アニール処理した内径１５＃、外径
１３０ｍ、厚さ１．２＃のポリカーボネート樹脂ディス
ク基板にフッ化マグネシウムを約５０人厚形成し、ひき
つづきこの上に、テルル−セレン合金ターゲットをアル
ゴンと窒素の混合カスでマグネトロンスパッタして、テ
ルルとセレンと窒素の比か原子数パーセントで９０対４
対Ｇのテルル−セレン−窒素層を約５０人厚形成した。
この光ディスクを９５°Ｃの窒素雰囲気中で１時間アニ
ールしたのち、波長８３００人における基板入用反射率
を測定したところ３４％であった。波長８３００への半
導体レーザ光を基板を通して入射して記録層子で１．６
珈φ程度に絞り、媒体線速度５．６ｍ／Ｓｅｃ、記録周
波数３．７７ＭＨｚ、記録パルス幅７０ｎＳｅＣ、記録
パワー６．５ｍ−の条件で記録し、０．７ｍＷで再生し
た。ハント幅３０　ＫＨｚのキャリアーとノイス゛との
比（Ｃ／Ｎ　）は５０ｄＢと良好であった。１この光デ
ィスクを７０°Ｃ１８０％の高温高湿度の環境に６０時
間保存した後、上記特性を調べたか変化はなく、耐候性
に優れた光記録媒体であることか確認された。
比較のためのフッ化マグネシウム層を設けない光ディス
クに比へて、４５ｄＢ以上のＣ／Ｎか得られる記録パワ
ー範囲はおよそ２倍大きくなり、記録パワー変動に対す
る余裕度の大きいことが確認された。又、トラッキング
やフォーカスのサーボも不安定になることはなかった。
［発明の効果］ 以上説明したように本発明の光記録媒体は耐候性がよく
かつ高感度で信号品質の良好なものである。
【図面の簡単な説明】
第１図は本発明の光記録媒体の１実施例を示す部分断面
図、第２図は従来の光記録媒体を示す部分断面図である
。

Claims (1)

    【特許請求の範囲】
  1. （１）基板と、レーザ光によつて一部が選択的に除去さ
    れて情報を記録する前記基板上に形成された記録層とか
    らなる光記録媒体において、前記記録層がフッ化物を主
    成分とする前記基板側に形成された層と、この層に隣接
    して前記基板の外方に形成されたテルル、セレンおよび
    窒素を主成分とする層とを少なくとも有していることを
    特徴とする光記録媒体。
JP61174496A 1986-04-30 1986-07-23 光記録媒体 Granted JPS6330291A (ja)