JPH10218657A - セメント組成物およびその製造方法 - Google Patents

セメント組成物およびその製造方法

Info

Publication number
JPH10218657A
JPH10218657A JP3830697A JP3830697A JPH10218657A JP H10218657 A JPH10218657 A JP H10218657A JP 3830697 A JP3830697 A JP 3830697A JP 3830697 A JP3830697 A JP 3830697A JP H10218657 A JPH10218657 A JP H10218657A
Authority
JP
Japan
Prior art keywords
cement
blast furnace
dust
chlorine
chlorine bypass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP3830697A
Other languages
English (en)
Other versions
JP3695728B2 (ja
Inventor
Seiki Daimon
正機 大門
Kazumi Kato
和己 加藤
Kiyoshi Hasegawa
清 長谷川
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chichibu Onoda Cement Corp
Original Assignee
Chichibu Onoda Cement Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chichibu Onoda Cement Corp filed Critical Chichibu Onoda Cement Corp
Priority to JP3830697A priority Critical patent/JP3695728B2/ja
Publication of JPH10218657A publication Critical patent/JPH10218657A/ja
Application granted granted Critical
Publication of JP3695728B2 publication Critical patent/JP3695728B2/ja
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

(57)【要約】 【課題】 従来セメント原料として再利用するしかなか
った塩素バイパスダストのさらなる有効活用に関する技
術を提供する。 【解決手段】 高炉スラグまたはフライアッシュの一種
以上を含むセメント９９．７〜９０重量部に対して塩素
バイパスダスト０．３〜１０重量部を添加して混合して
セメント組成物を製造する。

Description

【発明の詳細な説明】
【０００１】
【発明の属する技術分野】本発明は、塩素バイパスダス
トの有効活用に関するもので、さらに詳しくは、塩素バ
イパスダストを添加したセメント組成物およびその製造
方法に関するものである。
【０００２】
【従来の技術】従来、セメント原料や燃料中に含まれる
アルカリや塩素等の揮発成分をセメントキルンの系外へ
取り出す技術としては、本出願人が特公平５−５０４５
８号公報等で開示しているように塩素バイパスによって
セメントキルンから排ガスの一部を抽気して処理するセ
メントキルン排ガスの処理方法がある。
【０００３】本処理方法によれば、キルン排ガスを分級
器へ導いてダストの粒径に応じて分級し、この分級によ
って生じた粗粒ダストをキルンへ戻すと共に、微粒ダス
トを含んだ高温の排ガスをボイラへ導いて熱回収するよ
うにしたので、従来アルカリバイパスによって無駄に排
出していた熱量を有効に回収できるばかりか、アルカリ
バイパスによって排出していた粗粒ダストの回収ができ
るため、資源の有効利用が図れるという効果がある。
【０００４】
【発明が解決しようとする課題】しかしながら、上述し
たセメントキルン排ガスの処理方法によって排出される
塩素バイパスダストは、セメント原料として再利用して
はいるものの、他に有効活用されていないのが現状であ
る。したがって、本発明の目的は、塩素バイパスダスト
のさらなる有効活用に関する技術を提供しようとするも
のである。
【０００５】
【課題を解決するための手段】上述した本発明の目的
は、高炉スラグまたはフライアッシュの一種以上を含む
セメント９９．７〜９０重量部と塩素バイパスダスト
０．３〜１０重量部とからなることを特徴とするセメン
ト組成物によって達成される。
【０００６】また、高炉スラグまたはフライアッシュの
一種以上を含むセメント９９．７〜９０重量部に対して
塩素バイパスダスト０．３〜１０重量部を添加して混合
することを特徴とするセメント組成物の製造方法によっ
て達成される。
【０００７】
【発明の実施の形態】本発明では、セメントとして高炉
スラグまたはフライアッシュの一種以上を含むセメント
を用いた。これは塩素バイパススラグ中に含まれる塩化
カリウムが高炉スラグまたはフライアッシュの一種以上
を含むセメントの初期強度を改善し増進する効果が期待
できるからである。ここで、本発明の高炉スラグまたは
フライアッシュを含むセメントとしては高炉セメントま
たはフライアッシュセメントはもちろんのこと、ポルト
ランドセメントに高炉スラグまたはフライアッシュの一
種以上を別途添加したものも含まれる。
【０００８】ここで、塩素バイパスダストの添加量を
０．３〜１０重量部としたのは、０．３重量部より少な
いと、高炉スラグまたはフライアッシュの一種以上を含
むセメントの初期強度の増進効果がなく、また１０重量
部より多いと、塩素分が多くなり、コンクリートとして
の用途が制限されるからである。
【０００９】
【実施例】以下、本発明を実施例と比較例により、さら
に詳しく説明する。ここで、塩素バイパスダストとして
は分級後、集塵機により回収された微粒ダストを使用し
たが、これには５０重量％程度の塩化カリウムが含まれ
ていることを確認した。
【００１０】（実施例１）セメントとしては、市販の高
炉セメント（Ｂ種）を用い、これに、微粒ダストを０．
５，１，２，４，８重量％の割合で添加混合して試料と
した。次に、得られた試料をＪＩＳ Ｒ５２０１に規定
されている「セメントの物理的試験方法」に従い圧縮強
さ試験を行った結果を表１にまとめて示した。また、比
較例として、微粒ダストを添加しない場合についても表
１に示した。
【００１１】
【表１】
【００１２】表１の結果より明らかなように、本発明に
より微粒ダストを添加混合した試料は、添加しない場合
と比較して、材齢３日、７日といったセメントの初期の
強度に対する増進効果が認められた。さらに、材齢２８
日においても、従来の初期強度改善剤の欠点である強度
の低下も観察されなかった。
【００１３】（実施例２）セメントとして、市販のフラ
イアッシュセメント（Ｂ種）を用いた以外は、実施例１
と同様な試験を行った。その結果、実施例１の結果と同
様に、セメントの初期強度に対する増進効果が認められ
た。また、材齢２８日においても強度の低下は観察され
なかった。
【００１４】
【発明の効果】従来セメント原料として再利用するしか
なかった塩素バイパスダストのさらなる有効活用ができ
るという効果がある。

Claims (2)

    【特許請求の範囲】
  1. 【請求項１】 高炉スラグまたはフライアッシュの一種
    以上を含むセメント９９．７〜９０重量部と塩素バイパ
    スダスト０．３〜１０重量部とからなることを特徴とす
    るセメント組成物。
  2. 【請求項２】 高炉スラグまたはフライアッシュの一種
    以上を含むセメント９９．７〜９０重量部に対して塩素
    バイパスダスト０．３〜１０重量部を添加して混合する
    ことを特徴とするセメント組成物の製造方法。
JP3830697A 1997-02-06 1997-02-06 セメント組成物およびその製造方法 Expired - Fee Related JP3695728B2 (ja)