JPH09254340A - 透かし彫り偽造防止用紙 - Google Patents
透かし彫り偽造防止用紙Info
- Publication number
- JPH09254340A JPH09254340A JP8113056A JP11305696A JPH09254340A JP H09254340 A JPH09254340 A JP H09254340A JP 8113056 A JP8113056 A JP 8113056A JP 11305696 A JP11305696 A JP 11305696A JP H09254340 A JPH09254340 A JP H09254340A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- support
- engraving
- propylene
- engraved
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
彫り偽造防止用紙において、支持体層がプロピレン系樹
脂二軸延伸フィルム層を基材層とし、この基材層の表裏
面に無機微細粉末を含有するプロピレン系樹脂一軸延伸
フィルム層が設けられた積層延伸物であって、不透明度
が50〜100%であり、密度が0.70〜1.4g/
cm3 であり、彫刻が彫刻塗工層または支持体の一軸延
伸フィルムの深さまで施こされている透かし彫り偽造防
止用紙。 【効果】 彫刻塗工層から支持体の一軸延伸物層まで施
こされた彫刻画像が反射光では不鮮明であり且つ透過光
では鮮明な彫刻画像を示すので、偽造、改ざんがきわめ
て困難であり、また、彫刻塗工層が堅牢であるので、画
像彫刻後に画像を爪等で擦っても剥離しない、IDカー
ド等に好的な透かし彫り偽造防止用紙を提供する。
Description
ク、有価証券、IDカード類、パスポート等の改ざんさ
れにくい透かし彫り偽造防止用紙に関する。
カード類は偽造や改ざんされにくいことが要求され、か
かる偽造、改ざん防止技術としては次のものが挙げられ
る。 I群: (1)印刷物内に蛍光発色物質を存在させる。 (2)磁性インキを用いて印刷し、磁気作用によるイン
キの濃度の変化を視覚的に検知できるようにする(特開
平5−177919号公報)。 (3)フォトクロミックの感光色系を含む印刷インキを
用いて印刷を行う(特開昭60−79992号公報)。 (4)特定の反射分光特性を持つインキを用いて、或い
は反射率に所定値以上の差がある2種以上のインキを用
いて印刷する。
える印刷物(特開平5−177919号公報)。 (6)透かし模様(潜像)を施した印刷物(特開平6−
15794号)等のように、外観で偽造を見破るように
したもの。 II群: (7)複写すると文字、図柄の判読が困難となるような
細工を施した印刷物、或いは警告マークが複写紙上に現
れるようにしたもの(実開昭59−64271号公
報)。
ーと出るように、特殊な磁性インキを用いて印刷した印
刷物、或いは複写したのでは印刷の網点の粗密差が真券
と異なるように複写されるような印刷を施したもの(特
公昭56−19273号公報、特公平2−51742号
公報)、もしくは、肉眼では判読できない文字を印刷
し、隠蔽文字が判別機で読み取れるようにしたもの(特
開昭62−130874号公報)。
防止技術は、写真製版的に複写できるものが多く、完全
な偽造防止策とはなり難く、また、真券の印刷インキの
シート基材への接着力が弱く、使用中に印刷が剥がれ、
かえって偽造券と思われるために係るものを回収、取り
替える作業が必要であった。更に、真券であっても、使
用しているうちに皺が発生して判別機にかけた場合、使
用できないとして戻されることもしばしばであった。
れる支持体層と彫刻層とからなる用紙において、支持体
層の不透明度が70%以下、彫刻層の不透明度が40%
以上で、支持体層の不透明度が常に彫刻層の不透明度よ
り低い値であり、且つ支持体層と彫刻層の不透明度の差
が30%以上で、彫刻層から支持体層まで彫刻するよう
にしたことを特徴とする透かし彫り用紙は、識別しやす
いことと、支持体が透明なポリエチレンテレフタレート
フイルムの表裏にピグメント塗工層を設けたものであ
り、更に彫刻層もピグメント塗工層であり、用紙の製造
が複雑であるので用紙の入手が困難であることから改ざ
ん防止には優れているが、彫刻時に支持体の樹脂フイル
ムのバリ(ヒゲ)が発生しやすいことと、給排紙や使用
時に皺が発生しやすい欠点がある。
彫刻塗工層とからなる透かし彫り偽造防止用紙におい
て、支持体層に特定の積層延伸物を用いることにより、
上記欠点を改善した透かし彫り偽造防止用紙を提供する
ことである。
層と彫刻塗工層とからなる透かし彫り偽造防止用紙にお
いて、支持体層がプロピレン系樹脂二軸延伸フィルム層
を基材層とし、この基材層の表裏面に無機微細粉末を含
有するプロピレン系樹脂一軸延伸フィルム層が設けられ
た積層延伸物であって、かつ、 (1)不透明度(JIS P−8138)が50〜10
0% (2)密度(JIS P−8188)が0.70〜1.
4g/cm3 を満たすものであり、かつ、彫刻が彫刻塗工層または支
持体の一軸延伸物の深さまで施こされていることによる
透かし彫り偽造防止用紙、である。
フィルム積層物を支持体層として用いるので、配向の方
向性があり、かつ、腰強度があるので印刷時の給排紙が
容易で、かつ、皺になり難い。また、彫刻が、表面強度
の高い、かつ、強靱な一軸延伸物の深さまで施されるの
で、彫刻された透かし彫り偽造防止用紙の支持体層のバ
リ(ヒゲ)の発生がない。また、彫刻の深さにより彫刻
像が半透明ないし不透明の明暗のはっきりとした像とな
るので、裏側から入射する光りによって透かし彫り像が
鮮明に識別できる。
基材層とし、この基材層の表裏面に無機微細粉末を含有
するプロピレン系樹脂フィルムの一軸延伸層が設けられ
た積層延伸物であって、かつ、 (1)不透明度(JIS P−8138)が50〜10
0% (2)密度(JIS P−8188)が0.70〜1.
4g/cm3 を満たすものである。
単独重合体:プロピレンを主成分とし、これとエチレ
ン、ブテン−1、ヘキセン−1、ヘプテン−1、オクテ
ン−1、4−メチルペンテン−1等のα−オレフィンと
の共重合体;或いはこれらプロピレン重合体または共重
合体に無水マレイン酸、アクリル酸、メタクリル酸、ス
チレン、アクリル酸メチル、グリシジルメタクリレー
ト、2−ヒドロキシエチルメタクリレート等のビニル単
量体を0.1〜10重量%グラフト反応させた変性プロ
ピレン系樹脂等であって、融点が130〜180℃、結
晶化度が20〜75%のプロピレン系樹脂が使用でき
る。
リエチレン、線状低密度ポリエチレン、エチレン・酢酸
ビニル共重合体、エチレン・アクリル酸共重合体、エチ
レン・メタクリル酸共重合体の金属塩(K,Na,L
i,Zn,Al)、エチレン・アクリル酸アルキルエス
テル共重合体等の樹脂を30重量%以下、その他、安定
剤、紫外線吸収剤、核剤、分散剤等を2重量%以下含有
させてもよい。
3μmの炭酸カルシウム、焼成クレイ、けいそう土、バ
ーミキュライト、タルク、雲母、酸化チタン、硫酸バリ
ウム、アルミニウム粉等が使用でき、支持体層全体中に
10〜55重量%含有させて支持体層のプロピレン系樹
脂の不透明化を画る。好ましくは安価な炭酸カルシウ
ム、焼成クレイ、けいそう土等の体質顔料と、反射率の
高い酸化チタン、硫酸バリウム、酸化亜鉛、アルミニウ
ム粉等の反射性顔料との併用が好ましい。
30重量%、好ましくは6〜25重量%含有するプロピ
レン系樹脂フィルムを、プロピレン系樹脂の融点より低
い温度で縦方向に3〜7倍延伸し、次いでこの縦延伸フ
イルムの片面または両面に無機微細粉末を10〜55重
量%含有するプロピレン系樹脂フィルムを溶融ラミネー
トし、次いでこのラミネートフイルムを再加熱し、プロ
ピレン系樹脂の融点よりも15℃低い温度から融点より
も10℃高い温度域で縦方向に5〜12倍延伸し、次い
でこれをアニーリング処理することにより得られる。こ
こで融点とはプロピレン系樹脂のDSC曲線のピーク温
度をいう。ピークが2つ以上あるときは、高い方のピー
ク温度をいう。
融点以上とすることにより支持体層中の微細なボイドの
発生を抑えるか、少なくすることができる。又、一軸延
伸層と二軸延伸物層もしくは一軸延伸層の表面に、無機
微細粉末を0〜3重量%含有するプロピレン系樹脂やエ
チレン系樹脂のフイルム層を設けてもよい。このもの
は、延伸されていても、いなくてもよい。この支持体の
一軸延伸フイルム層は、印刷インクとの接着性を向上さ
せるためにコロナ放電処理、オゾン処理、プラズマ処理
等の酸化処理を施こすと良く、又、印刷インキとの密着
性を良好とするために、支持体の表面に帯電防止機能を
有する水溶性ポリマーを固型分量が0.5〜5g/m2
となるように塗布するのが好ましい。帯電防止機能を有
する水溶性ポリマーとしては、ポリエチレンイミン、ポ
リ(エチレンイミン−尿素)、ポリアミンポリアミドの
エチレンイミン付加物、窒素原子含有カチオン性もしく
は両性ポリマー等が挙げられる。
好ましくは60〜150μmの範囲である。支持体層の
二軸延伸基材層の肉厚は40〜150μm、好ましくは
40〜100μmで、一軸延伸層の肉厚は5〜30μ
m、好ましくは8〜20μmである。支持体の不透明度
は50〜100%、好ましくは65〜85%である。5
0%未満では彫刻の輪郭の鮮明さに欠ける。彫刻により
支持体の一軸延伸物の一部が削り去られるので、支持体
の不透明度が100%であっても、彫刻の部分の支持体
の不透明度は、30〜80%となり、支持体の裏面側か
ら光が入射すれば透かし彫り模様の輪郭がはっきりとす
る。
の周囲に微細なボイドを発生させて支持体を半透明〜不
透明とするために延伸前よりは支持体の密度が小さくな
り、通常その値は、0.70〜1.4g/cm3 、好ま
しくは0.90〜1.2g/cm3 である。密度が0.
70g/cm3 未満では、支持体の弾力性が大き過ぎ、
彫刻がしずらく、1.4g/cm3 を越えては、無機充
填剤の配合量を多くし、延伸倍率を低くする必要があ
り、支持体の成形が困難となる。支持体の面には、印刷
や印字を施こしてもよい。
重量%、無機微細粉末を80〜50重量%含有する層
で、不透明度が40%以上、好ましくは50〜100%
である。具体的には、バインダー樹脂、無機微細粉末、
必要により帯電防止剤、増粘剤、耐水化剤、消泡剤、防
腐剤、分散剤を分散媒に分散した塗工液を支持体の表面
に塗布し、乾燥することにより得られる。
体のような天然接着剤、スチレン・ブタジエン共重合
体、メチルメタクリレート・ブタジエン共重合体等の共
役ジエン系重合体ラテックス、アクリル又はメタクリル
酸アルキルエステルの共重合体ラテックス、澱粉、ポリ
ビニルアルコール、ポリウレタン系、またはポリエステ
ル系合成樹脂接着剤の一種類又は二種類以上組み合わせ
て使用することができる。特に耐擦過性の良好なポリエ
ステル系、またはポリウレタン系合成樹脂が好ましい。
5μmのカオリン、クレー、重質炭酸カルシウム、軽質
炭酸カルシウム、水酸化アルミニウム、二酸化チタン、
サチンホワイト、亜硫酸カルシウム、非晶質シリカ等の
無機顔料が挙げられるが、プラスチックピグメントとし
て知られるメラミンシアヌレート、メラミン等の有機顔
料或いは接着剤の性能を合わせ有しているバインダーピ
グメント等も挙げることができる。これらの中でも、耐
擦過性の上から、粒子が細かく、且つ少量の添加で不透
明度を与えるものが好ましく、二酸化チタンが特に好ま
しい。
コーター、ロールコーター、エアーナイフコーター、グ
ラビアコーター、ダイコーター等の公知の塗工設備が用
いられる。塗工量は、片面の塗工量が固型分量で5.0
〜30g/m2 、好ましくは10〜20g/m2 となる
ように行われる。塗工は支持体の片面でも、両面であっ
てもよい。かかる塗工量で、肉厚5〜30μm、好まし
くは10〜20μmの肉厚の彫刻塗工層が得られる。
着性を良好とするため、プライマー層を設けてもよい。
プライマー層は、透明、不透明いずれのものでも良い
が、彫像に細かい階調をつけるためには不透明の方が良
い場合もある。この場合は不透明度を高くするのに役立
つ。また、偽造防止のために、プライマー層を着色層と
してもよく、層の数を複数にしても良い。この場合、着
色層を支持体層と彫刻層のそれぞれの色と異なるように
すれば、より改ざんされにくくすることができる。更
に、プライマー層として、地紋印刷を入れて偽造防止す
るようにすることも可能である。
好ましくは1〜5μmである。本発明において、支持体
層にプライマー層を設ける場合には、支持体層とプライ
マー層の両方の不透明度を合せて測定した値を支持体層
の不透明度とする。次に、本発明の透かし彫り用紙の構
成例を図により説明する。図1は支持体層1の表面にプ
ライマー層3を介して彫刻層4を設けた透かし彫り用紙
の一例を示す断面拡大図で、このように構成された透か
し彫り用紙は、図2に示すように、画像部5を彫刻し、
その両側に背影部6,6を支持体1の一軸延伸フィルム
層1aまたは1bまで彫刻して、裏面から透過光を当て
ると、陰影がはっきりし画像が鮮明に視認できる。
(t)は、支持体層の不透明度、彫刻画像により異な
る。支持体の一軸延伸物1b層まで彫刻6が施こされる
場合は、tは3〜28μm、好ましくは5〜20μmで
ある。彫刻は支持体の一軸延伸物の延伸方向とは直角方
向に行うのがヒゲの発生をなくし、彫刻の外郭を明瞭と
する。また、図3は支持体層1の表面に明度の異なる、
もしくは色相の異なる着色プライマー層3を三層形成
し、その上に彫刻層4を設けた透かし彫り用紙の断面拡
大図、図4は支持体層1の裏面に筆記性良好なピグメン
ト塗工層2を設け、同じく表面に地紋印刷7を施し、そ
の上に着色プライマー層3を介して彫刻層4を設けた透
かし彫り用紙の断面拡大図であって、これらの透かし彫
り用紙は、図2に示すような彫刻5,6を施すことによ
り、透過光によって鮮明な画像を視認することができ
る。
説明する。尚、実施例及び比較例において部とあるの
は、すべて重量部を示す。無機微細粉末含有樹脂延伸フイルム積層物の製造 例 1 (1) メルトフローレート(MFR)1g/10分の
ホモポリプロピレン(融点164℃)80重量%、高密
度ポリエチレン8重量%、炭酸カルシウム12重量%の
混合物(A)を押出機で240℃で溶融混練した後、ダ
イよりシート状に押出し、冷却装置により冷却して、無
延伸シートを得た。このシートを、155℃に加熱した
後、縦方向に5倍延伸した。
プロピレン56重量%に平均粒径1.5μmの炭酸カル
シウム40重量%と平均粒径0.8μmのアナターゼ型
酸化チタン0.5重量%と高密度ポリエチレン3.5重
量%を混合した組成物(B)とを別々の押出機で溶融混
練し、(1)の5倍延伸シートの両面に(B)が外側に
なるようにダイ内で共押出して積層し、ついでこの積層
物を160℃に加熱したのち横方向に7.5倍の延伸を
行なって、三層積層フイルムを得た。 (3) この三層積層フイルムの表面をコロナ放電処理
して、(B)/(A)/(B)の各フイルムの肉厚が2
0/50/20ミクロンの三層構造の積層物を得た。
ミドのエピクロルヒドリン付加物の1:1水溶液を塗布
し、乾燥させて、肉厚0.5μmのプライマー層を形成
させた。この肉厚が100.5ミクロンの三層積層フイ
ルムの物性は表1に示す通りであった。
ポリプロピレン(融点164℃)89重量%と高密度ポ
リエチレン8重量%及び粒径1.5μmの炭酸カルシウ
ム粉末3重量%の混合物(A)を押出機で溶融混練した
後、ダイよりシート状に押出し、冷却装置により冷却し
て、無延伸シートを得た。このシートを、155℃に加
熱した後、縦方向に5倍延伸した。
プロピレン(C)と、MFRが4.0g/10分のポリ
プロピレン50.5重量%に平均粒径1.2μmの焼成
クレイ45重量%と粒径0.8μmの酸化チタン1.0
重量%と高密度ポリエチレン3.5重量%を混合した組
成物(B)とを別々の押出機で溶融混練し、ダイ内で積
層して共押出したシートを(1)の5倍延伸シートの両
面に(C)が外側になるように積層し、ついでこの五層
積層物を185℃に加熱したのち横方向に7.5倍の延
伸を行なって、五層のフイルムを得た。
ロナ放電処理し、(C)/(B)/(A)/(B)/
(C)の各フイルムの肉厚が5/30/80/30/5
ミクロンの五層構造の積層物を得た。この肉厚が150
ミクロンの五層積層フイルムの物性は表1に示す通りで
あった。
ン(融点164℃)92重量%と高密度ポリエチレン8
重量%の混合物(A)を押出機で溶融混練した後、ダイ
よりシート状に押出し、冷却装置により冷却して、無延
伸シートを得た。このシートを、155℃に加熱した
後、縦方向に5倍延伸した。 (2) MFRが4.0g/10分のホモポリプロピレ
ン(C)と、MFRが4.0g/10分のポリプロピレ
ン86.5重量%に平均粒径1.5μmの炭酸カルシウ
ム10重量%と高密度ポリエチレン3.5重量%を混合
した組成物(B)とを別々の押出機で溶融混練し、ダイ
内で積層して共押出したシートを(1)の5倍延伸シー
トの両面に(C)が外側になるように積層し、ついでこ
の五層積層物を185℃に加熱したのち横方向に7.5
倍の延伸を行なって、五層積層フイルムを得た。
ロナ放電処理して、(C)/(B)/(A)/(B)/
(C)の各フイルムの肉厚が5/20/50/20/5
ミクロンの五層構造の積層物を得た。この肉厚が100
ミクロンの五層積層フイルムの物性は表1に示す通りで
あった。 例 4 王子油化合成紙(株)製の一軸/二軸/一軸の積層構造
のプロピレン系樹脂のトレース合成紙“YUPO TP
G−75”(商品名;肉厚75μm)を用いた。
FPG−95”(商品名;肉厚95μm)を用いた。 例 6 王子油化合成紙(株)製の一軸/二軸/一軸の積層構造
のプロピレン系樹脂の合成紙“YUPO KPK−8
0”(商品名;肉厚80μm)を用いた。 例 7 東洋紡績(株)製の単層二軸延伸ポリプロピレン系合成
紙“トーヨーパールSU”(商品名;肉厚110μm)
を用いた。
を含有するプロピレン系樹脂二軸延伸フイルムよりなる
合成紙“パール”(商品名;肉厚150μm)を用い
た。 例 9 王子油化合成紙(株)製のフィラー含有ポリプロピレン
樹脂三層構造の二軸延伸フイルム“OYパール”(商品
名;肉厚100μm)を用いた。
0A)45部、二酸化チタン(石原産業(株)製 A−
220)35部、軽質炭酸カルシウム(白石工業(株)
製ブリリアント−15)20部を用い、顔料100部当
たり分散剤として特殊カルボン酸(花王(株)製 ポイ
ズ−530)0.1部を添加し、固形分濃度50%にな
る如く水を添加して高速攪拌用デリッターにおいて分散
後、さらに接着剤として水性ポリエステル樹脂(東洋紡
績(株)製 バイロナールMD1200)55部、水性
ポリウレタン樹脂(大日本インキ化学工業(株)製 A
P−40)45部を添加配合した。
加して混合し、最終的に固形分濃度が48%の塗工液を
製造した。 界面活性剤(大日本インキ化学工業(株)製 F−883) 0.15部 帯電防止剤(三洋化成工業(株)製 ケミスタット6120)5.0 部 耐水化剤 (サンノプコ(株)製 デナコールEX−512)0.4 部 この塗工液をガラス板上にバーコーターを用い、塗工量
が20g/m2 となるように塗布し、乾燥して皮膜を得
た。この皮膜(肉厚12μm)の不透明度は93%であ
った。
JR−600A)20部、二酸化チタン(石原産業
(株)製 A−220)30部、クレー(エンゲルハー
ド(株)製 ウルトラホワイト−90)50部を用い、
顔料100部当たり分散剤として特殊カルボン酸(花王
(株)製 ポイズ−530)0.15部を添加し、固形
分濃度60%になる如く水を添加して高速攪拌用デリッ
ターにおいて分散後、さらに接着剤として水性ポリエス
テル樹脂(東洋紡績(株)製 バイロナールMD124
5)65部、水性ポリウレタン樹脂(大日本インキ化学
工業(株)製 AP−40)35部を添加配合した。
加して混合し、最終的に固形分濃度が52%の塗工液を
製造した。 界面活性剤(大日本インキ化学工業(株)製 F−812) 0.1 部 帯電防止剤(三洋化成工業(株)製 ケミスタット6120)3.0 部 この塗工液をバーコーターを用い、ガラス板上に10g
/m2 の量塗工し、乾燥して6μmの皮膜を形成し、更
にこの皮膜上に前記塗工液1をバーコーターを用いて1
5g/m2 の量塗工し、乾燥して全膜厚13μmの積層
皮膜を得た。これをガラス板より剥がし、不透明度を測
定したところ、93%であった。
9で得た合成紙の片面に、塗工液1をバーコーター(熊
谷理器(株)製)を用いて塗工量が20g/m2 となる
よう2回塗布し、乾燥して肉厚12μmまたは13μm
の皮膜(彫刻塗工層)を形成させて透かし彫り偽造防止
用紙を得た。これら透かし彫り偽造防止用紙の彫刻塗工
層面に、パスポート番号、氏名、国籍の記入欄をオフセ
ット印刷した。ついで、用紙の彫刻塗工層面よりカード
彫刻機により支持体層の一軸延伸物1b層に達するまで
(t=3〜12μm)人物画像を一軸延伸物の延伸方向
とは直角方向である縦方向に彫刻を施こし、パスポート
を得た。
た。 (1)人物画像の透かし彫り画像の識別性 パスポートの支持体面側より照明を与えたとき、鮮明な
画像が視認できたものを良好(○)、識別可能なものを
普通(△)とし、輪郭が不鮮明なものを不良(×)とし
た。 (2)擦過性 彫刻画像を爪で擦った際、表面の脱落が見受けられず、
堅牢なものを良好(○)、表面の脱落が見受けられたも
のを不良(×)とした。 (3)ヒゲの発生の有無 彫刻画像の周辺に、刻り跡のヒゲ(バリ)がないものを
良好(○)、ヒゲがあるものを不良(×)とした。
0枚得たときの、パスポートの紙づまりの回数、および
複写後の原紙のパスポートの皺の発生の有無を調べた。 (比較例7)実施例7において、彫刻の深さを、支持体
の二軸延伸フイルム層(A)の略中央肉厚前後部に行っ
たほかは同様にしてパスポートを得た。得られた結果を
表1または2に示す。
刻塗工層から支持体の一軸延伸物層まで施こされた彫刻
画像が支持体側からの入射光で鮮明な彫刻画像を示すの
で、偽造、改ざんがきわめて困難となる。また、彫刻塗
工層が堅牢であるので、画像彫刻後に画像を爪等で擦っ
ても剥離することがない為、IDカードのような透かし
彫り偽造防止用紙として好適である。
断面拡大図。
断面拡大図。
示す断面拡大図。
Claims (3)
- 【請求項1】 支持体層と彫刻塗工層とからなる透かし
彫り偽造防止用紙において、支持体層がプロピレン系樹
脂二軸延伸フィルム層を基材層とし、この基材層の表裏
面に無機微細粉末を含有するプロピレン系樹脂一軸延伸
フィルム層が設けられた積層延伸物であって、かつ、 (1)不透明度(JIS P−8138)が50〜10
0% (2)密度(JIS P−8188)が0.70〜1.
4g/cm3 を満たすものであり、かつ、彫刻が彫刻塗工層または支
持体の一軸延伸フィルムの深さまで施こされていること
を特徴とする透かし彫り偽造防止用紙。 - 【請求項2】 彫刻のなされた方向が、支持体の一軸延
伸フィルム層の延伸方向に対して直角の方向になされて
いることを特徴とする請求項1記載の透かし彫り偽造防
止用紙。 - 【請求項3】 支持体の一軸延伸フィルム層の肉厚が各
々5〜30μmであり、基材層の二軸延伸フィルム層の
肉厚が40〜150μmであることを特徴とする請求項
1記載の透かし彫り偽造防止用紙。