JPH0489053A - 吸収性物品 - Google Patents
吸収性物品Info
- Publication number
- JPH0489053A JPH0489053A JP2204163A JP20416390A JPH0489053A JP H0489053 A JPH0489053 A JP H0489053A JP 2204163 A JP2204163 A JP 2204163A JP 20416390 A JP20416390 A JP 20416390A JP H0489053 A JPH0489053 A JP H0489053A
- Authority
- JP
- Japan
- Prior art keywords
- absorbent
- sheet
- absorption
- liquid
- diffusible
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
め要約のデータは記録されません。
Description
で代表される吸収性物品に関するものであり、更に詳し
くは、体液の吸収特性、特に吸収速度、拡散性、吸収体
からの液戻り阻止性及び漏れ防止性を向上させた高吸収
性の吸収性物品に関するものである。 〔従来の技術及び発明が解決しようとする課B]従来か
ら、体液の喋収性の向上を目的とした吸収性物品の提案
が数多く行われ、数多くの改善がなされてきた。そして
、これらの改善の大部分は、吸収速度の向上、吸収体か
ら表面への液戻りの阻止、漏れ防止及び身体に対するベ
タツキの低減にあった。 例えば、吸収体の素材に関して言えば、吸収体の素材と
して、物理的微細菟間で液を吸収、保持する親水性の吸
収紙やパルプなどに替えて、液を物理化学的な作用、即
ち、イオン浸透圧を利用して高吸収性ポリマーに液体を
吸収、保持させることによって吸収容量を向上させると
共に吸収後の液戻りを防止することが提案されている。 事実、この提案により、吸収性が向上し、現在はパルプ
と高吸水性ポリマーとを併用した吸収体が殆どの吸収性
物品に用いられている。しかし、これらの吸収性物品で
あっても依然として漏れ防止に関して十分なものとは言
えない。そして、このような事実は、吸収性物品に対す
る不満の第一が漏れにあることにより示唆されている。 即ち、イオン浸透圧によって液体を吸収、保持させるタ
イプの高吸水性ポリマーでは体液の吸収速度に限度があ
り、更に高吸水性ポリマーが体液に濡れないと体液を吸
収できないため、高吸水性ポリマーは、吸水速度の速い
パルプなどと併用して用いざるを得なかった。しかしな
がら、パルプを併用するにしても、パルプは、乾燥時に
はある程度の圧縮及び曲げ回復性を示すが、湿潤時には
極度に強度が低下し、殆どそれらの回復性を示さないた
め、湿潤したパルプに応力が加わると、パルプが圧縮変
形(以下「ヨレ」という)してその吸収空間が著しく減
少し、また、−旦吸収した体液がヨレに伴って容易に戻
ってしまい、また、ヨした後の再吸収速度が著しく低下
するため、高吸収性ポリマーがその吸水特性を十分に発
揮しないうちに吸収体がヨしてしまい、このヨレが漏れ
に繋がることが多くなっている。 そこで、このような吸収体の欠点を補うために、例えば
、実開昭56−6099号公報、実開昭61−2235
4号公報及び特開昭56−97748号公報等に記載の
技術が提案されている。 (1)実開昭56−6099号公報に記載の生理用ナプ
キンは、第5図に示す如く、液透過性の表面材1、親水
性繊維を主体とする吸収体2及び液不透過性のバックシ
ート3を備えて構成され、この吸収体2の内部若しくは
裏面側に保型性を有する弾性多孔体4(例えば、発泡フ
オーム等)を設けることにより上記吸収体2の変形を防
止したものである。 (2)また、実開昭61−22354号公報に記載のも
のは、第6図に示す如く、吸収体2として、親水性繊維
の代わりに弾性多孔体(例えば、ウレタンスケルトンフ
オーム、バインダー等により接合されたポリエステル繊
維集合体等)で置き換えられたものである。 (3)また、特開昭56−97748号公報に記載のも
のは、第7図に示す如く、吸収体2として弾性多孔体4
の気泡(セル)中に親水性繊維及び/又は吸水ポリマー
を均一に分散させたものである。 しかしながら、(1)の場合には、全体として生理用ナ
プキンの保型性が保たれるが、吸収体2に並設された弾
性多孔体4は、親水性が不十分で、体液を吸収保持する
場合に有効な骨格構造を有していないため、それ自体が
体液の吸収保持性を実質的に有しておらず、また、親水
性繊維を主体とする吸収体2自体に回復性がないため、
生理用ナプキンに応力が与えられると吸収体2にヨレ、
ヘタリを生してしまい、吸収体2が吸収効果を十分に発
揮することができない。 また、(2)の場合には、吸収体2として用いられる弾
性多孔体は変形、回復性に優れている反面、吸収体2と
しての弾性多孔体は、(])の場合と同様、液保持性が
劣悪であるため、このような吸収性物品は、吸収性物品
として到底実用に堪え得るものではなかった。 更に、(3)の場合には、(2)の場合に比べて、吸液
性、保液性に若干の向上は認められるものの、やはり吸
収体2の主体を成す弾性多孔体自体の液保持性が劣悪で
あるため、依然として吸収性物品としての性能は不十分
であった。 従って、現在のところ上述したパルプと高吸収性ポリマ
ーが併用された吸収性物品が吸収性物品の玉流となって
いるのが実状である。 また、現在、主流になっている上記吸収性物品は、吸収
体からの液戻りが存在しても、表面シートで液戻りを阻
止する工夫が数多く提案されている。これら表面シート
は、その素材を、従来、般に使用されている親水性素材
(例えば、レーヨンステーブル)に替えて、疎水性素材
(例えば、ポリプロピレンステーブル、ポリエチレンス
テーブル、ポリエステルステーブル等)からなる不織布
等を用い、使用者の身体の表面と吸収体との間に疎水雰
囲気の空間を形成することにより、表面のへタツキを低
減させたものである。特に、最近では、開孔を有する疎
水性のシート(フィルム)を表面シートとして用いたも
のが提案されている。 このような開孔シートは、表面シートを疎水性素材とし
て用いているため表面シート内での液体の保留が起こら
ずヘタツキ防止に対して効果的である反面、液の透過性
と液戻り防止性とは相反する関係にあって、これらを同
時に解決するには自ずと限度がある。つまり疎水雰囲気
空間が大きくなると開孔部が少なくなって液戻りを防止
することができるが、逆に、液が透過しなくなってしま
い、その空間の大きさのみを調整するだけでは液の透過
性と戻り防止性とを同時且つ効果的に作用させる゛こと
は困難である。 従って、本発明の目的は、身体から排泄された体液を素
速く吸収体全体に亘って吸収、拡散させ、吸収体、特に
高吸収性ポリマーの吸収機能を最大限に利用することが
でき、表面への液戻り及び液漏れを抑制することができ
る吸収性物品を提供することにある。 C課題を解決するための手段〕 本発明者らは、従来の吸収性物品に比べ、優れた吸収性
能を有し、表面への液戻りを著しく低減させ、表面での
ベタツキを改善し、漏れが極めて少なく、快適に使用す
ることができる吸収性物品を得るべく、鋭意検討を重ね
た結果、吸収体の一部を特定の拡散性吸収シートと特定
の吸収保持シートによって構成することにより上記目的
を達成し得ることを知見した。 即ち、本発明は、上記知見に基づいてなされたもので、
液体透過性の表面材、液体保持性の吸収体、及び液体不
透過性の防漏材を有する実質的に縦長の吸収性物品にお
いて、 上記吸収体は、拡散性吸収シート及び該拡散性吸収シー
トより裏面側に位置する吸収保持性シートを有し、 (a)上記拡散性吸収シートは、親水度(cosθ)が
0.5〜1で且つ長手方向のクレム吸収速度が40〔l
ll1l/分〕以上のシートからなり、また、(b)上
記吸収保持性シートは、毛管浸透圧4000〜I 50
00 [dyn/cffl)の繊維集合体からナルシー
トで、生理食塩水の吸収量が40〜70〔g/g〕で且
つその吸収速度が2(Idlo、3gポリマー・分〕以
上の高吸水ポリマーを、該繊維集合体に対して10〜1
00重量%挟持する積層シートからなる ことを特徴とする吸収性物品を提供するものである。 以下、第1図〜第16図を参照しながら本発明を説明す
る。尚、各回申、第1Mは本発明の吸収性物品の一実施
例の横方向の断面の一部を省略して示す断面図、第20
は本発明の吸収性物品の他の実施例を示す第1図相当図
、第3図は第1図に示す吸収保持シートを示す断面図、
第4図は第1図に示す表面ソートの一部を拡大して示す
部分斜視図である。 本発明の吸収性物品は、第1図に示す如く、液体通過性
の表面材(表面シート)l、液体保持性の吸収体2〜及
び液体不透過性の防漏材(防漏シート)3を有し、実質
的に縦長に形成されている。 そして、この吸収性物品の着用時には、上記表面ソート
1が肌に接する表面側に位置し、上記防漏シート3が下
着に接する裏面側に位置するようになしてあり、」二記
吸収体2が上記表面シート1と上記防漏シート3の間に
介在している。上記吸収体2は、第1図に示す如く、裏
面、全側面及び表面の周縁部が上記防漏シート3によっ
て被覆され、更にこれらの全面が上記表面シート1によ
って被覆され、上記吸収体2の表面においては、その中
央部が上記表面ノート1によって直接被覆されて体液を
吸収体2へ直接透過させるように構成されている。また
、上記表面シート1の裏面には、長手方向に3本の粘着
部4が筋状に形成され、剥離紙5によって保護されてい
る。尚、6は接合部である。 而して、本発明における吸収体2は、拡散性吸収シート
21及び該拡散性吸収シート21より裏面側に位置する
吸収保持シート22を有している。 上記拡散性吸収シート21は、親水性繊維からなる湿式
不織布を3枚積層して構成されている。 この拡散性吸収シートは、親水度(cosθ)が0.5
〜1で且つ長手方向のクレム吸収速度が40〔肛/分]
以上であり、より好ましくは親水度Cosθが0.6〜
1で、クレム吸収速度が50以上〔加/分〕である。親
水度(cosθ)は、シートに対する液体のなじみ性を
示す指標であり、また、クレム吸収速度は、シートに対
する液体の拡散性を示す指標である。親水度(cosθ
)が0.5未満若しくはクレム吸収速度が40(mm/
分〕未満になると液体の拡散性または吸収速度が低下し
、後述する高吸収性ポリマーの吸収機能を有効に発揮さ
せることができなくなる虞れがある。 本発明における拡散性吸収シート21として用いられる
材料は、上記特性を満足するソートであればよく、特に
制限されるものではない。好ましく用いられる材料とし
ては、例えば、ポリウレタン、ポリスチレン、ポリエチ
レン、ポリエステル、ポリビニルアルコール、ブタジェ
ンスチレンゴム(SBR)、ニトリルブタジェンゴム等
の合成高分子からなる発泡体、合成繊維(ポリエチレン
(PE)、ポリプロピレン(PP)、ポリエチレンテレ
フタレート(PET)等)を熱融着又は接着剤によって
接着してなる繊維集合体及び親水性繊維(レーヨン繊維
、パルプ繊維等)を熱圧着又は接着剤で接合してなる繊
維集合体等が挙げられる。 本発明における拡散性吸収シート21は、これを構成す
るソート素材が疎水性材料の場合には、界面活性剤によ
って親水性を付与して上記親水度(cosθ)及びクレ
ム吸収速度を向上させたものが好ましい。このような界
面活性剤としては、親油基と親水基とを有する親水性の
界面活性剤であれば特に制限されるものではないが、ア
ニオン系界面活性剤、エチレンオキサイドの付加モル数
の高い非イオン系界面活性剤が好ましい。好ましく用い
られる界面活性剤としては、例えば、スルホコハク酸エ
ステル、アルキルエーテルサルフェート、ポリオキンエ
チレンアルキルエーテル、ポリオキシエチレンアルキル
フェノールエーテル、グリセリン脂肪酸エステル等が挙
げられる。これらは単独でもこれらから適宜選択された
ものの混合物であってもよい。通常、ソートに対して0
.05〜1重量%で上記親水度(cosθ)を付与する
ことができるものが更に好ましい。 また、上記拡散性吸収シート21は、その素材自体が親
水性材料からなるものであれば、湿潤剤による処理の必
要がなく、また長時間の使用及び再吸収時における親水
性が安定していてより好ましい。好ましく用いられる親
水性材料としては、例えば、親水性繊維(パルプ繊維、
レーヨン繊維、ビニロン等)を融若若しくは接着剤等で
接合した湿式不織布が挙げられ、バルブとレーヨン繊維
の湿式混抄紙がより好ましい。更に、漏れ防止性及び吸
収性能を得るには、3デニール未満のレーヨン繊維とバ
ルブとの混合物で、該レーヨン繊維ノ混合率が30〜9
0%、即ち、混合重量比(レーヨン/パルプ)が30/
70〜90/10の湿式混抄紙が好ましい。またレーヨ
ン繊維は、その繊維断面の真円度が0.5以下であるこ
とが好ましく、0.4以下がより好ましい。 上記拡散性吸収シート21は、第1図、第2図に示す如
く、複数積層したものであっても単層であっても良く、
より好ましくは、クレム吸収速度の異なる2種以上の拡
散性吸収シートを複数積層したものである。複数層から
なる拡散性吸収シート21は、表面側(上層)よりも裏
面側(下層)になるに従いクレム吸収速度が大きくなる
速度勾配を有する方が身体に遠い下層側へ体液を拡げる
上で好ましい。 上記拡散性吸収ノートは、吸収保持ソートへの液透過性
が大きいほど好ましく、そのためには、液透過時間(測
定法は後述する)が200秒以下であることが好ましく
、]50秒以下炉上り好ましい。 また、上記拡散性吸収シート21は、体液を吸収体全体
に素速く拡げる必要があり、更に、より効果的に横漏れ
を防止するためには拡散性吸収ソト21の縦方向と横方
向の拡散性に差をもたせたものが好ましい。この場合、
この拡散性吸収ント21に生理食塩水を滴下した際の液
滴下1分後の液拡がり面の縦と横との長さの比(縦/横
)が1.2以上であることが好ましく、13〜3がより
好ましい。そして、この拡散性吸収ソート21は、その
縦方向を吸収性物品の縦方向に一致するようにすること
が好ましい。 更に、上記拡散性吸収シート21は、変形回復性を有し
ているものが好ましく、具体的には、液吸収時(WET
時)の圧縮残留歪が0.3以下であることが好ましい。 また、本発明における吸収保持性シート22は、毛管浸
透圧4000〜15000dyn/ciの繊維集合体か
らなるシー)22Aで、生理食塩水の吸収量40〜70
(g/g)で且つその吸収速度が2[’Id70.3
gポリマー・93以上の高吸収性ポリマー22Bを10
〜100重量%挟持させた積層シートからなるものであ
る(第3図番。照)。 即ち、上記高吸収ポリマー22Bを挟持する上記シート
22Aは、毛管浸透圧が4000〜15000 dyn
/cmであり、より好ましくは4000〜12000d
yn/cdである。毛管浸透圧が4000dyn/c+
f1未満になると、吸収保持シート22が上記拡散性吸
収シート21より液体を吸収し難くなり、また、150
00dyn10ffを趙えると、高吸収性ポリマー22
Bへの液体の移動がスムーズに行われず好ましくない。 また、上記高吸収ポリマー22Bは、生理食塩水の吸収
量40〜70 Cg/g〕であることが好ましい。この
吸収量が70 Cg/g]を超えると、膨潤時に高吸水
性ポリマーの表面が乾燥状態にならず、液拡散が効果的
に行われず、また40〔g/g)未満では、吸収量その
ものが不足して好ましくない。また、上記高吸収ポリマ
ー22Bは、その吸収速度が2[dlo、3gポリマー
・分〕以上であり、より好ましくは3[dlo、3gポ
リマー・93以上である。この吸収速度が2[dlo。 3gポリマー・分]未満では、液体を効果的に移動させ
ることができず、高吸収性ポリマーの吸収が不十分で、
水溜まりを吸収体の中に作ってしまい好ましくない。 上記高吸水性ポリマー22Bは繊維集合体からなるシー
ト22Aに対して10〜100重量%挟持され、より好
ましくは30〜80重量%である。 100重量%を超えると吸収後ゲルブロンキングを生し
、10重量%未満では保持液量が不十分になり好ましく
ない。これら高吸水性ポリマーはシートの間に均一に存
在させても、部分的に濃度が異なっても良い。吸収性物
品での液体の流れ方を考えると、シートの両端部に高吸
水性ポリマーの量を多くする構成が更に好ましい。 而して、上記毛管浸透圧、生理食塩水の吸収量及びその
吸収速度は、第9図、第10図に示す測定装置を用いて
下記の方法により測定し、この測定値に基づいて得られ
た値である。 ・毛管浸透圧(dyn/c+fl) 毛管浸透圧の測定には第9図に示す測定装置を用いた。 まず、吸収保持シートに使用する繊維集合体からなるシ
ートを縦250mm、幅20肛の測定片50にカントし
、測定片50を10枚用意する。次いで、支持体51が
弛まないように測定片50を垂下させて両端を固定する
。また、300X100X50mm(縦×横×深さ)の
直方体の容器52乙こ、生理食塩水53を40価の高さ
まで入れ、生理食塩水53中に試験片50を浸す。試験
片50を浸した後、60分後の最大液吸い上げ高さを測
定する。10枚の試験片50について同様の測定を行い
、これらの平均値を計算し、求められた平均値を平均最
大吸い上げ高さh6゜膠として下記の式に代入して毛管
浸透圧P (dyn/c4)を求めた。 ・毛管浸透圧 P−ρghb。 P;毛管浸透圧(dyn/c+Il) ρ;生理食塩水の比重(g / ctl )g ; 9
.8 X 102CI/S”h6゜;生理食塩水の60
分後の吸収高さ(c+n)・吸収量(g/g) 1gの高吸水性ポリマー22Bを大過剰の生理食塩水に
分散させ、充分に膨潤させた後に80メツシユの金網で
高吸水性ポリマー22Bを濾過し、その重量を測定し、
この測定値を吸収量とした。 ・吸収速度 吸収速度の測定には第10図に示す測定装置を用いた。 まず、測定台54と、ビユレット55中の生理食塩水5
3の液面を等高位にセフ)し、測定台54中の直径70
mmのガラスフィルター56上に0゜3gの高吸収性ポ
リマー22Bを均一に散布し、1分間に高吸収性ポリマ
ー22Bが吸収した生理食塩水53の容量を高吸収性ポ
リマー22Bの吸収速度(dlo、3gポリマー・分〕
とした。 また、上記吸収保持シート22に用いられる材料は、上
記条件を満足するものであれば、特に制限されるもので
はない。好ましく用いられる繊維集合体からなるシート
材料としては、例えば、合成繊維(ポリエチレン(PE
)、ポリプロピレン(PP)、ポリエチレンテレフタレ
ート(PET)等)を熱融着又は接着剤で接着してなる
繊維集合体、及び親水性繊維(レーヨン繊維、パルプ繊
維等)を熱圧着又は接着剤で接合してなる繊維集合体等
が挙げられる。 また、本発明における高吸水性ポリマー22Bは、イオ
ン浸透圧によって大量の液体を吸収保持し、加圧下でも
、漏出しない高分子量のポリアクリル酸塩架橋体等のポ
リマーが好ましく、微細空隙を有するシートから素速く
液体を吸収する機能が必要であり、しかも膨潤後にその
表面が乾燥状態に保たれ、液体の移動を妨げないものが
好ましまた、このような吸収機能は、高吸水性ポリマが
均一な架橋構造をもつものでは発現することが困難であ
り、架橋密度勾配をもつことが好ましい。架橋密度勾配
を有する高吸水性ポリマーとしてはポリアクリル酸塩を
骨格とし、中和条件がpH6〜7.5の範囲のものが好
ましい。高吸水性ポリマーに架橋密度勾配をもたせる方
法としては、水溶性ラジカル開始剤を含存するアクリル
酸塩の水溶液を、7保護コロイドの存在下で非水溶媒中
に分散、懸濁させて重合した後、得られたボロアクリル
酸塩の含水量を10〜40重量%にコントロールした後
、ポリアクリル酸塩の官能基と反応し得る架橋剤によっ
て更にポリアクリル酸塩を反応させて表面を更に架橋す
ることにより得ることができる。 このような架橋剤は、カルボキシル基と反応し得る2個
以上の官能基を有する水溶性の化合物が好ましく、この
ような架橋剤としては、例えば、エチレングリコールジ
グリシジルニーテニル、ポリエチレングリコールジグリ
シジルエーテル、グリセリントリグリシジルエーテル等
のポリグリシジルエーテル、エピクロルヒドリン、α−
メチルクロルヒドリン等のハロヒト′リンのハロエポキ
シ化物、グルタルアルデヒド、グリオキサール等のポリ
アルデヒド、ポリオール、ポリアミン類が挙げられ、好
ましくは、エチレングリコールジグリノジルエーテル等
のポリグリシジルエーテルが挙げられる。 また、上記吸収速度は、粒径により変化し、高吸水性ポ
リマーが微細になればなるほど、吸収速度が速くなるが
、この場合、吸収時のゲルブロンキングを生し易くなる
。ゲルブロッキングを生しさせない高吸収性ポリマーの
粒径としては、平均粒径20〜200μが好ましく、5
0〜150μがより好ましい。尚、ゲルブロッキングと
は、液体を保持した時に液体の拡散性が低下するするこ
とをいう。上記吸収保持シート22は、液体の吸収容量
及び液体を保持した時の液体の拡散性の両立を成し得る
ため、繊維集合体からなるシート22Aで高吸水性ポリ
マー22Aを挟持するサンドイッチにした構造のものが
好ましい(第3図参照)。 この場合、繊維集合体からなるソートは、少なくとも2
枚は必要であり、数枚重ねたものであっても良い。ポリ
マーがシートから脱落しないようにエンボス処理及びス
パイラルホットメルトによって固定等を行ったものが好
ましい。 このようなソート22Aの間に高吸水性ポリマー22B
を挟持した層は、−層で使用しても、数層組み合わせて
使用しても良く、生理用ナプキンの場合には、−層で十
分である。 本発明の吸収性物品は、上述の特定の拡散性吸収シート
21と吸収保持シート22との組合せることによって、
それぞれ単独では得られない相乗効果が発揮されて体液
の吸収性能が著しく向上したものになる。即ち、本吸収
性物品の一例である生理用ナプキンにおいては、拡散性
吸収ノート21が、極めて効果的に吸収保持シート22
全体に液体を拡げ、吸収保持シート22に体液をスムー
ズに移行させる一方、吸収保持ノート22が、高吸収ポ
リマー22Bによって最大限吸収保持できる環境にあっ
て身体から排泄されて拡散性吸収シート21を透過した
液体を素速くゲル化することができ、身体から排泄され
た体液を極めて素速く吸収拡散し、吸収した体液を素速
く封じ込めることができる。 また、本発明の吸収性物品においては、上記吸収体2を
効果的にに作用させるには表面シート1との組合せも重
要である。 上記吸収体2が高吸収量である場合、上記吸収体2から
の液体の表面への戻りを抑制し且つ体液を吸収体2へ素
速く導くことができる表面シート1が、吸収体2の吸収
保持効果をより一層発揮させ、漏れ防止力を高めること
ができて好ましい。 このような表面シート1としては、不織布の高い液透過
性と疎水性フィルムの体液の残留の阻止性を兼ね備えた
第4図に示すものが好ましい。同図に示す表面シートは
、二層からなる積層シートで、肌に接する側に位置する
フィルム層11と、吸収体2側番こ位置する親水性の繊
維集合体12との二層が一体化したものである。この表
面シートIは、表面側ほど広く開口する凹部IAを多数
有すると共に該凹部IAの傾斜壁部IBにおける上記フ
ィルム層11に開孔ICを有している。そして、この開
孔ICは上記繊維集合体層12によって閉塞されている
。また、上記凹部IAを形成する4面の傾斜壁部IBは
、いずれも上記凹部IAの開口を表面側ほど広くするよ
うに傾斜しているため、該表面シートlが圧縮されても
、上記開孔】Cが被われることがないように形成されて
いる。 上記表面シート1を用いることにより、身体から排泄さ
れた液体を素速く吸収体2に導くことができ、しかも、
液戻りを大量の液を吸収した後でも阻止することができ
る。従って、本発明の吸収性物品は、優れた吸収保持性
を有することから従来の吸収性物品と比較して、極薄で
極めて漏れが少なく身体へのフィント性が向上し、使用
者に快適な使用感を付与することができるものである。 〔作用〕 本発明の吸収性物品によれば、表面材を透過した体液が
吸収体の拡散性吸収シートによって素速く吸収体全面に
拡散すると共に内部へ透過し、透過した体液が吸収保持
シートの繊維集合体シートを素速く透過してその高吸収
性ポリマーに捕獲されて体液を吸収体内に封し込めるこ
とができる。 [実施例] 次に、本発明の吸収性物品を下記実施例に基づいて具体
的に説明する。尚、下記実施例においては、生理用ナプ
キンを例に挙げて説明するが、本発明は紙オムツ等にも
同様に適用することができる。 1、まず、本実施例及び比較例で用いられる拡散性吸収
ノート、吸収保持シート、及び表面シートを下記要領で
作製し、それぞれの機能を測定した。 (1)拡散性吸収シートの作製 ■拡散性吸収シート(A) 大さ1.7デニール、長さ7胴で繊維断面の真円度(測
定法は後述)が0,21の湿式用レーヨン繊維(商品名
:SAレーヨン、ダイワボウレーヨン■製)75部、パ
ルプ繊維25部、結合剤ポリビニルアルコール(以下P
VAと称す)(商品名:ゴーセノール P−250、日
本合成化学@) 10部をそれぞれ水中に分散し、これ
らを抄紙し、乾燥した後、秤量25gのパルプ・レーヨ
ン混抄紙(拡散性吸収シー) (A))を得た。尚、レ
ーヨン繊維の真円度は下記のように測定した。 ・真円度の測定 繊維の断面を電子顕微鏡で写真撮影した後、この撮影画
像を画像解析装置(日本アビオニクス社製Avio
EXCEL)にかけ、その解析結果に基づいて真円度を
下記の式を用いて計算して求めた。そして、+00の試
料についてそれぞれの真円度を同様に求めて、その平均
値を真円度の値とした。 真円度= 4×πXA A;繊維断面積L2
L;繊維断面の周囲長 ■拡散性吸収シート(B) 大さ1.7デニール、長さ7コで繊維断面の真円度が0
.21の湿式用SAシレー3フ0部、パルプ繊維50部
、結合剤PVA(ゴーセノールP−250)10部をそ
れぞれ水中に分散し、これらを抄紙し、乾燥した後、秤
量25gのパルプ・レーヨン混抄紙(拡散性吸収シート
(B))を得た。 ■拡散性吸収シート(C) 太さ1.7デニール、長さ711II11で繊維断面の
真円度が0.68の湿式用レーヨン(商品名:コロナ(
SB)レーヨン、ダイワボウレーヨン■)70部、パル
プ繊維30部、結合剤PVA(ゴーセノル P−250
)10部をそれぞれ水中に分散し、これらを抄紙し、乾
燥した後、秤量25gのパルプ・レーヨン混抄紙(拡散
性吸収シー)(C))を得た。 ■拡散性吸収シート(D) 太さ2デニール、秤量30gの湿式レーヨンスパンボン
ド不織布(商品名:TCF703、二相化学■製)を拡
散性吸収シート(D)とした。 ■拡散性吸収シート(E) 太さ2デニール、秤量50gの湿式レーヨンスパンボン
ド不織布(商品名:TCF405、二相化学■製)を拡
散性役収ノー) (E)とした。 ■拡散性吸収ソート(F) パルプを湿式抄紙として得た秤量25gの吸収性の紙を
拡散性吸収シート(F)とした。 ■拡散性吸収シート(G) 太さ1.7デニール 長さ7mmで繊維断面の真円度が
0.21の湿式用SAシレー3フ0部、パルプ繊維90
部、結合剤PVA(ゴーセノール P2S5)10部を
水中に分散し、これらを抄紙し、乾燥した後、秤量25
gのパルプ・レーヨン混抄紙(拡散性吸収シート(G)
)を得た。 ■拡散性吸収シート(H) 太さ3デニール、長さ7mで繊維断面の真円度が0.6
8の湿式用レーヨン(商品名:コロナ(SB)レーヨン
、ダイワボウレーヨン■)50部、パルプ繊維50部、
結合剤PVA(ゴーセノールP−250)10部を水中
に分散し、これらを抄紙、乾燥した後、秤量25gのパ
ルプ・レーヨン混抄紙(拡散性吸収シー)(H))を得
た。 ■拡散性吸収シート(1) 秤量300g/rd、厚み5aII11、密度o、o6
g/cnlの粉細パルプシートを拡散性吸収ソート(I
)とした。 (2)次いで、上記各拡散性吸収シートA−1について
、親水度cosθ、クレム吸収速度、液透過時間、液拡
がり面の縦、横の拡がり比(縦/横)、WET時の圧縮
残留歪を下記方法により測定し、それぞれの結果を後記
表−1に示した。 ■親水度(cosθ)、クレム吸収速度の測定親水度(
cosθ)、クレム吸収速度の測定は、第11図に示す
測定装置を用いて行った。 まず、拡散性吸収シートを縦250肝、幅20
トして測定片50′を作製した。次いで、この測定片5
0″を、第11財に示す如く、支持体51“に弛みがな
いように垂下させて上下両端を固定する。また300x
100x50mm(緬×横×深さ)の直方体の容器52
′に生理食塩水53゛を測定液として高さ40髄まで入
れ、この生理食塩水53′中に測定片50”を浸す。測
定片50°を浸した後、1分後に、測定片50′が液面
から吸収した吸収液の高さ、及び60分後における測定
片50′が液面から吸収した高さをそれぞれ測定した。 合計10点について同様のを測定し、その平均値を採っ
てそれぞれ1分後の吸収高さhl、及び60分後の生理
食塩水53°の吸収高さh6゜とする。ここで、]分後
の吸収高さhの値をクレム吸収速度り、 (wn/分
)とする。 次に生理食塩水53′をエタノール(E tOH)(試
薬特級:和光純薬工業■)に替え、上記と同様の手法で
60分後の測定片50°がEtOHを吸収した高さを測
定し、10点の測定片50゛の平均値をもって、60分
後のEtOHの吸収高さh6o”とする。下記の式によ
り生理食塩水53と測定片50” との親水度cosθ
(θ:生理食塩水と測定片との接触角)を下記の式によ
り計算して求めた。 尚、この親水度cosθの計算手法は、粉末法と呼ばれ
る手法を応用したものである。 hbox’r + X ρz 00゛θ= h6o×T2×ρ h°6゜;60分後のEtOHの吸収高さ(cm)71
;EtOHの表面張力(dyn)cnl)p、;EtO
Hの比重(g/cffl)hbo;60分後の生理食塩
水の吸収高さ(cm)T2 ;生理食塩水の表面張力(
dyn/cm)ρ2 ;生理食塩水の比重(g/cff
l)■液透過時間の測定 液透過時間の測定は、第12図に示す測定装置を用いて
行った。 まず、拡散性吸収ソートを縦50肛、横50−にカット
して測定片60を作製し、次いで、この測定片60を、
第12図に示す如く、内径35aIII+のガラス管6
1.61で上下両側から挟持固定した。この時、測定中
に液が横からしみ出さないように、シリコンゴム62を
介してクリンプで両側から固定する。測定液として下記
に示す割合で配合調整したグリセリン85%水溶液63
を20−戚ビーカー64に10g取り、静かに注入する
。グリセリン85%水溶液63を注入した後、ガラス管
61の開孔面積に対し50%以上測定片の面が現れるま
での時間を求め、これを液透過時間とした。 ・測定液(グリセリン85%水溶液)の調整グリセリン
(和光純薬工業■)85gにイオン交換水15gを混合
した後、食用青色1号(東京化成工業■)0.3gを添
加し青色に着色した。 ■液拡がり面の拡がり比(縦/横) 液拡がり面の拡がり比の測定は、第13図に示す測定装
置を用いて行った。 まず、拡散性吸収シートを縦120mm、横120鵬に
カットして測定片70を作製し、次いで、この測定片7
0を、第13図に示す如く、縦100論、横100m+
nの開孔を有する横110肛、横110m、厚さ10m
mのアクリル枠71.71で測定片70が弛まないよう
に両面から固定する。 次いで、生理食塩水をピペットに取り、測定片70の上
方101Wlから生理食塩水を1滴(0,04g)静か
に滴下する。液滴下1分後、測定片70の面上に拡がっ
た液の縦/横の最大長さをそれぞれ測定し、これらの測
定値を下記の式に用いて、液拡がり面の拡がり比を求め
た合計10点について同様の測定をし、その平均値をと
って液拡がり面における縦と横の比とした。尚、測定片
7oの縦方向は、生理用ナプキンの縦方向と一致するよ
うに拡散性吸収ノートを用いる。 液拡がり面の拡がり比(縦/横) ■WET時の圧縮残留歪 まず、拡散性吸収シートを50mmX50mmにカット
して測定片を作製し、この測定片について乾燥時の5g
/cn荷重時の厚み!。(μm)を求めた。次に測定片
を生理食塩水に1分間浸して湿潤状態にし、テンシロン
圧縮試験機を用いて圧縮速度5mm/min、圧縮面積
10cifl、半径17.8m+++の円抜で、最大荷
重300g/cIIlまで湿潤状態の測定片80を圧縮
し、圧縮後の測定片を等速度で回復させた。この時、5
g/ci荷重時の湿潤状態の厚みρ1 (μm)を求め
、下記の式により、試験片のWET時の圧縮残留歪を求
めた。 !。;乾燥時の5g/c+fl荷重時−の厚み(μm)
11;湿潤時圧縮後の5g/all荷重時の厚み(μm
)(3)吸収保持シートの作製 ■吸収保持ソート(A) パルプ繊維の湿式抄紙して得られた、毛管浸透圧500
0dyn/C′I11、秤量33g/allの吸収性紙
のTcこホットメルト トプコP618B(東洋ペトロ
ライト■製)をスパイラル形状で秤量10g/dで散布
した後、更に、下記方法で製造された高吸水性ポリマー
Aを秤量40g/cjで散布した。 次いで、上記高少水性ポリマー(A)に上記吸収性紙を
重ね、上記吸収性紙によって上記高吸水性ポリマーAが
挟持された吸収保持ソート(A)を得た。 ・高吸水性ポリマーAの製造方法 45重量%のモノマー濃度をもつ中和度α=07のアク
リル酸ナトリウムを重合させてポリマーを得、得られた
ポリマー中の水分を30重量%にコントロールし、次い
で、このポリマーにエチレングリコールジグリ7ジルエ
ーテルをその濃度が11000ppになるように添加し
て架橋勾配を有する平均粒径80μの架橋構造のポリマ
ーを得た。このポリマーの吸収性能は、生理食塩水の吸
収量50 (g/g)、吸収速度6.2 [m10.3
gポリマー・分〕であった。 ■吸収保持シート(B) 下記方法で製造した高吸水性ポリマー(B)を用いる以
外は、吸収保持シー) (A)と全く同様にして吸収保
持ノー) (B)を得た。 ・高吸水性ポリマー(B)の製造方法 高吸水性ポリマー(A)の製法と同様の操作を行って本
ポリマーを製造した。但し、エチレングリコールジグリ
シジルエーテルは、重合後に加えるのではなく、重合前
のモノマーの水溶液に添加し、この千ツマ−の重合時に
架橋させて均一な架橋構造のポリマーを得、得られたポ
リマーの平均粒径が80μであった。このポリマーを高
吸水性ポリマー(B)とした。このポリマーの吸収性能
は、生理食塩水の吸収量50(g/g)、吸収速度1.
8 [d/ 0.3 gポリマー・分〕であった。 ■吸収保持シート(C) 太さ3デニール、長さ7il!11で繊維断面の真円度
0.68の湿式用レーヨン(商品名コロナ(SB)レー
ヨン、ダイワボウレーヨン■)70部 バルブ繊維30
部、結合剤PVA(ゴーセノール P250)10部を
水中に分散し、抄紙して乾燥した後、秤量33g/rr
rの毛管浸透圧3000dyn/ポの吸収性シートを得
た。この吸収性シートの上に、ホットメルトトプコP6
18B(東洋ペトロライト■製)をスパイラル形状で秤
量10g/rrrで散布した後、高吸水性ポリマー(B
)を秤量40g/r+(で散布する。再び、毛管浸透圧
3000dyn/cffl、秤量33g/nfの吸収性
シートを重ねて吸収保持シート(C)を得た。 (4)表面シートの作製 0表面シート(A) アルキルホスフェートとソルビタン脂肪酸エステルとの
混合界面活性剤が0.34重量%付着したポリエチレン
/ポリプロピレン複合繊維(チッソ■製)を用いた秤量
25 g/rrfの乾式熱接着不織布に、低密度ポリエ
チレン(三井石油化学工業■製)を25μmラミネート
したものに、第4図に示す如く、凹部IAの形成密度が
52個/C1lである表面シー) (A)を得た。この
凹部IAにおける側壁部IBの開孔ICの大きさは0.
1〜21II112であった。 0表面ノート(B) 市販の生理用ナプキン(商品名二ロリエ、花王■製)の
表面シート(不織布)を表面シー)(B)とした。 0表面ソート (C) 面積0.18+m++2 (平均値)の開孔が多数分散
形成された低密度ポリエチレン(三片石油化学工業■製
)の疎水性シートを表面シート(C)とした。 実施例】 本実施例では、3枚の拡散性吸収シート21の一番上層
(肌当接面側)に拡散性吸収シート(B)を1枚、その
下側に拡散性吸収シート(A)を2枚重ね、更に、その
下側に吸収保持ノート(A)22を積層して幅75圓、
長さ195mmにカットして吸収体2を作製した。次い
で、この吸収体2、ポリエチレンをラミネートした防漏
シート3、表面ソート(A)1及びズレ止め用テープ4
を用いて第1図に示す生理用ナプキン(本発明品)1を
作製した。 実施例2 本実施例では、3枚の拡散性吸収シート21の一番上層
に拡散性吸収シート(C)を1枚、その下側に拡散性吸
収シー) (A)を2枚用いる以外は、全て実施例1と
同様にして第1図に示す生理用ナプキン(本発明品)2
を作製した。 実施例3 本実施例では、2枚の拡散性吸収シー)21の上層に拡
散性吸収シー) (D)を1枚、その下側に拡散性吸収
シート(E)を1枚重ね、更にその下側に吸収保持シー
)A22を積層して幅75m、長さ195mにカントし
て吸収体2を作製した。 次いで、ポリエチレンをラミネートした防漏シト3、表
面シー) (A)1及びズレ止め用テープ4を用い、第
2図に示す生理用ナプキン(本発明品)3を作製した。 実施例4 本実施例では、3枚の拡散性吸収シート21として、3
枚全てに拡散性吸収シート(A)を用いた以外は、全て
実施例1と同様にして第1図に示す生理用ナプキン(本
発明品)4を作製した。 実施例5 本実施例では、3枚の拡散性吸収シート21として、3
枚全てに拡散性吸収ノート(C)を用いた以外は、全て
実施例1と同様にして、第1図に示す生理用ナプキン(
本発明品)5を作製した。 実施例6 本実施例では、表面ソートとして、表面シート(B)を
用いた以外は、全て実施例1と同様にして第1図に示す
生理用ナプキン(本発明品)6を作製した。 実施例7 本実施例では、表面シートとして表面シート(C)を用
いた以外は、全て実施例1と同様にして第1図に示す生
理用ナプキン(本発明品)7を作製した。 比較例1 本比較例では、3枚の拡散性吸収シート21として、3
枚全てに拡散性吸収シートFを用いた以外は、全て実施
例1と同様にして第1図に示す生理用ナプキン(比較品
)1を作製した。 比較例2 本比較例では、3枚の拡散性吸収シート21として、3
枚全てに拡散性吸収ソート(G)を用いた以外は、全て
実施例1と同様にして第1図に示す生理用ナプキン(比
較品)2を作製した。 比較例3 本比較例では、3枚の拡散性吸収シート21として、3
枚全てに拡散性吸収シー) (H)を用いた以外は、全
て実施例1と同様にして第1図に示す生理用ナプキン(
比較品)3を作製した。 比較例4 本比較例では、第8図に示す如く、拡散性吸収シート2
1に吸収シート四)を用い、その下層に吸収保持シー)
(A)を積層して幅75閣、長さ195mにカットし
て吸収体2を作製した。この吸収体2、ポリエチレンラ
ミネート紙からなる防漏ソート3、表面ソー1−(A)
1及びズレ止め用テープ4を用い、第3114こ示す生
理用ナプキン(比較品)4を作製した。 比較例5 本比較例では、吸収保持シート22として吸収保持シー
トBを用いた以外は、全て実施例5と同様にして第1図
に示す生理用ナプキン(比較品)5を作製した。 比較例6 本比較例では、吸収保持シート22として吸収保持シー
) (C)を用いた以外は、全て実施例5と同様にして
第1回に示す生理用ナプキン(比較品)5を作製した。 比較例7 本比較例では、3枚の拡散性吸収シート21として、3
枚全てに拡散性吸収シート(F)を用いた以外は、全て
実施例6と同様にして第1図に示す生理用ナプキン(比
較品)7を作製した。 比較例8 本比較例では、3枚の拡散性吸収ノート21として3枚
全てに拡散性吸収シート(F)を用いた以外は、全て実
施例7と同様にして第1閲に示す生理用ナプキン(比較
品)8を作製した。 ■1次に、本実施例1〜7における本発明品1〜7及び
比較例1〜8における比較品1〜8それぞれの生理用ナ
プキンの吸収保持効果を観るために、下記に示す方法に
よって動的液戻り量(g)及び漏れ試験を各生理用ナプ
キンについて行い、それぞれの結果を後記表−2に示し
た。 (1)動的液戻り量 第14図に示すように、実施例及び比較例で得られた試
験用の生理用ナプキン80を水平に置き、直径10 m
mの注入口81のついたアクリル板82を載せる。試験
の生理用ナプキン80に5g/n(の荷重が掛かるよう
に、更に重り83を載せる(アクリル板82と重り83
との重量の総和を732gとする)。注入口81から脱
繊維馬脂(日本バイオテスト研究所株製)10gを注入
し、液か完全に注入されてから、20分間放置する。そ
の後、75cm幅X l 95m+nにカットした秤量
30g/rrfの吸収性紙を10枚、試験用の生理用ナ
プキン80の上面(肌当接面側)に重ね、第15図に示
す可動式女性腰部モデル90に、第16図に示すように
吸収紙を重ねた生理用ナプキン80を装着させ、ショー
ツをはかせた後、100歩/分(50m/分)の歩行速
度で1分間歩行させた。 歩行後、生理用ナプキン80と吸収紙10枚を取り出し
、吸収紙に吸収された脱繊維馬脂の重量を液戻り量(g
)として求めた。生理用ナプキン80は、10点につい
て測定し、その平均値を動的液戻り量とした。 (2)漏れ試験 実施例及び比較例で得られた試験用の生理用ナプキン8
0を、第15図に示す如く、可動式女性腰部モデル90
に装着させ、ショーツをはかせた後、100歩/分(5
0m/分)の歩行速度で10分間歩行させた。その後、
チューブ91によって脱繊維馬脂を歩行させながら3g
注入し、その後同じ速度で10分間歩行させ、更に、そ
の後脱繊維馬脂を3g注入した後、10分間歩行させ、
更に、脱繊維馬脂を3g旺入、10分間歩行を繰り返し
、それぞれの時点でサンプル数10枚のうちの漏れが発
生した枚数を数え、それぞれの結果を後記表−2に示し
た。 (3)後記表−2に示す結果によれば、特定の拡散性吸
収ソートと吸収保持ノートとの組み合わせた本発明品1
〜7は、それぞれのノート単独で用いたものでは得られ
ない相乗効果により著しく吸収性能が向上し、液戻り量
が少なく、極めて漏れの少ないことが判る。 また、本発明品1〜7は、特定の拡散性吸収ノートと特
定の吸収保持ノートとの組み合わせて液体を素早く吸収
させることができ、高吸収性ポリマーの特性を極めて効
果的に発揮させることができ、極薄に形成することがで
き、快適に着用する表−2 〔発明の効果〕 本発明の吸収性物品は、身体から排泄された体液を素速
く吸収体全体に亘って吸収、拡散させ、吸収体、特に高
吸収性ポリマーの吸収機能を最大限に利用することがで
き、表面への液戻り及び液漏れを抑制することができる
ものである。
プキンの横方向の断面の一部を省略して示す断面図、第
2図は本発明の吸収性物品の他の実施例を示す第1図相
当図、第3図は第1図に示す生理用ナプキンの吸収保持
シートを拡大して示す断面図、第4図は第1図に示す生
理用ナプキンの表面シートを拡大して示す斜視図、第5
図、第6図及び第7図それぞれ従来の生理用ナプキンを
示す第1図相当図、第8図は第1図に示す生理用ナプキ
ンの比較例を示す第1図相当図、第9図は毛管浸透圧の
測定に用いられる測定装置を示す斜視図、第10図は吸
収速度の測定に用いられる測定装置を示す断面図、第1
1図は親水度及びクレム吸収速度の測定に用いられる測
定装置を示す斜視図、第12回は液透過時間の測定に用
いられる測定装置を示す斜視図、第13図は液拡がり面
の拡がり比(縦/横)の測定に用いられる測定装置を示
す斜視図、第14図は動的液戻り量の測定に用いられる
測定装置を示す断面図、第15図は動的液戻り量の測定
及び漏れ試験に用いられる可動式女性腰部モデルを示す
斜視図、第16図は可動式女性腰部モデルに試験用の生
理用ナプキンを装着させた状態を示す斜視図である。 1、表面材 IA;凹部 1B;傾斜壁部 IC;開孔 2;吸収体 3;防漏材 11;フィルム層 12;繊維集合体層21;拡散
性吸収シート 22;吸収保持シート 22A;繊維集合体からなるシート 22B;高吸水性ポリマー
Claims (9)
- (1)液体透過性の表面材、液体保持性の吸収体、及び
液体不透過性の防漏材を有する実質的に縦長の吸収性物
品において、 上記吸収体は、拡散性吸収シート及び該拡散性吸収シー
トより裏面側に位置する吸収保持性シートを有し、 (a)上記拡散性吸収シートは、親水度(cosθ)が
0.5〜1で且つ長手方向のクレム吸収速度が40〔m
m/分〕以上のシートからなり、また、(b)上記吸収
保持性シートは、毛管浸透圧4000〜15000〔d
yn/cm^2〕の繊維集合体からなるシートで、生理
食塩水の吸収量が40〜70〔g/g〕で且つその吸収
速度が2〔ml/0.3gポリマー・分〕以上の高吸水
ポリマーを、該繊維集合体に対して10〜100重量%
挟持する積層シートからなる ことを特徴とする吸収性物品。 - (2)上記拡散性吸収性シートが親水性繊維からなる湿
式不織布である、請求項(1)記載の吸収性物品。 - (3)上記拡散性吸収性シートは、その表面側から裏面
側になるに従いクレム吸収速度が大きくなる速度勾配を
有する、請求項(1)または(2)記載の吸収性物品。 - (4)上記拡散性吸収シートは、グリセリン85%水溶
液を滴下した際の液透過時間が200秒以下である、請
求項(1)ないし(3)のいずれか一つに記載の吸収性
物品。 - (5)上記拡散性吸収性シートは、生理食塩水を滴下し
た際の液滴下1分後の液拡がり面における縦と横の比(
縦/横)が1.2以上である、請求項(1)ないし(4
)のいずれか一つに記載の吸収性物品。 - (6)上記拡散性吸収性シートは、液吸収時の圧縮残留
歪が0.3以下である、請求項(1)ないし(5)のい
ずれか一つに記載の吸収性物品。 - (7)上記拡散性吸収性シートは、レーヨン繊維とパル
プ繊維の混抄紙とからなり、該レーヨン繊維は3デニー
ル未満の繊維で且つ該混抄紙中のその混合率が30〜9
0%である、請求項(1)ないし(6)のいずれか一つ
に記載の吸収性物品。 - (8)上記レーヨン繊維は、その断面の真円度が0.5
以下である、請求項(7)記載の吸収性物品。 - (9)上記表面材は、肌に接する側に位置するフィルム
層と吸収体側に位置する親水性の繊維集合体層の二層が
一体化し、且つ表面側ほど広く開口する凹部を多数有す
ると共に少なくとも該凹部の傾斜壁部における上記フィ
ルム層に開孔を有する、請求項(1)ないし(8)のい
ずれか一つに記載の吸収性物品。