JPH0428741A - プロピレン樹脂組成物 - Google Patents
プロピレン樹脂組成物Info
- Publication number
- JPH0428741A JPH0428741A JP13324790A JP13324790A JPH0428741A JP H0428741 A JPH0428741 A JP H0428741A JP 13324790 A JP13324790 A JP 13324790A JP 13324790 A JP13324790 A JP 13324790A JP H0428741 A JPH0428741 A JP H0428741A
- Authority
- JP
- Japan
- Prior art keywords
- component
- parts
- weight
- general formula
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔発明の背景〕
〈産業上の利用分野〉
本発明は射出成形体とするのに好適なプロピレン樹脂組
成物に関し、特に剛性及び成形品の顔料分散性が改良さ
れた射出成形体を製造するのに好適なプロピレン樹脂組
成物に関するものである。
成物に関し、特に剛性及び成形品の顔料分散性が改良さ
れた射出成形体を製造するのに好適なプロピレン樹脂組
成物に関するものである。
〈従来の技術〉
プロピレン樹脂はその優れた力学特性や成形性などを生
かして各種の用途に適した成形体に成形されて使用され
ている。しかしながら、用途によってはさらに高い剛性
の成形体を要求される場合がある。
かして各種の用途に適した成形体に成形されて使用され
ている。しかしながら、用途によってはさらに高い剛性
の成形体を要求される場合がある。
それ故、プロピレン樹脂により高い剛性を付与するため
に、従来から種々の技術が提案されている。具体的には
タルク等の無機フィラー、カルボン酸の金属塩、芳香族
カルボン酸のアルミニウム塩、ベンジリデンソルビトー
ル類、芳香族燐酸塩などの増核剤を添加する方法などが
知られている。
に、従来から種々の技術が提案されている。具体的には
タルク等の無機フィラー、カルボン酸の金属塩、芳香族
カルボン酸のアルミニウム塩、ベンジリデンソルビトー
ル類、芳香族燐酸塩などの増核剤を添加する方法などが
知られている。
〈発明が解決しようとする課題〉
しかしながら、これら増核剤を添加する公知の剛性の向
上方法では、着色剤を添加すると十分な剛性の向上を発
揮することかできなくなる場合かある。
上方法では、着色剤を添加すると十分な剛性の向上を発
揮することかできなくなる場合かある。
く要 旨〉
本発明者らは上記課題に鑑みて鋭意研究を重ねた結果、
着色剤が混入された結晶性プロピレン重合体よりなるプ
ロピレン樹脂組成物を得る際に、特定な構造の有機リン
酸エステル化合物と、脂肪族金属塩またはアルキル乳酸
金属塩とを特定な割合で配合することにより優れた剛性
および顔料分散性を備えたプロピレン樹脂組成物が得ら
れ、該プロピレン樹脂組成物は射出成形体を製造するの
に好適な素材であるとの知見を得て、本発明を完成する
に至った。
着色剤が混入された結晶性プロピレン重合体よりなるプ
ロピレン樹脂組成物を得る際に、特定な構造の有機リン
酸エステル化合物と、脂肪族金属塩またはアルキル乳酸
金属塩とを特定な割合で配合することにより優れた剛性
および顔料分散性を備えたプロピレン樹脂組成物が得ら
れ、該プロピレン樹脂組成物は射出成形体を製造するの
に好適な素材であるとの知見を得て、本発明を完成する
に至った。
すなわち、本発明のプロピレン樹脂組成物は、結晶性プ
ロピレン重合体1. O0重量部に下記成分(A)〜(
C)を配合してなることを特徴とするものである。
ロピレン重合体1. O0重量部に下記成分(A)〜(
C)を配合してなることを特徴とするものである。
成分(A)二次に示す一般式(I)または−最大(TI
)にて表わされる有機リン酸エステル化合物0.01〜
5重量部 一般式(I) 一般式 (ただし、 上記−最大(1) 中のR1およびR−は同−又は異なる水素原子、又は炭
素数1〜8のアルキル基を、水素原子又は炭素数1〜4
のアルキル基を表わす。〕を、Yは水酸基又は水素原子
を、aは1又は0、bは1又は0、Cおよびdは同−又
は異なる0〜3の整数をそれぞれ表わす。) 成分(B):炭素数が6〜40で、金属がアルカリ金属
又はカルシウムである、脂肪族金属塩およびアルキル乳
酸金属塩から選ばれた化合物0.01〜5重量部 成分(C)、無機又は有機顔料0.001〜5重量部 く効 果〉 本発明のプロピレン樹脂組成物は、結晶性プロピレン重
合体に特定な構造の有機リン酸エステル化合物と、脂肪
族金属塩またはアルキル乳酸金属塩と、顔料とを特定な
割合で配合してなるもので、優れた剛性と顔料分散性と
を備えていることから、着色された射出成形体用素材と
して適したものであり、各種工業用部品、例えば家庭電
化製品の冷蔵庫などの部品、高剛性コンテナー、電子レ
ンジ用食品容器、自動車のバンパー、インストルメント
パネルなどの内装品、外装部品などの射出有色成形品と
して成形することができる。
)にて表わされる有機リン酸エステル化合物0.01〜
5重量部 一般式(I) 一般式 (ただし、 上記−最大(1) 中のR1およびR−は同−又は異なる水素原子、又は炭
素数1〜8のアルキル基を、水素原子又は炭素数1〜4
のアルキル基を表わす。〕を、Yは水酸基又は水素原子
を、aは1又は0、bは1又は0、Cおよびdは同−又
は異なる0〜3の整数をそれぞれ表わす。) 成分(B):炭素数が6〜40で、金属がアルカリ金属
又はカルシウムである、脂肪族金属塩およびアルキル乳
酸金属塩から選ばれた化合物0.01〜5重量部 成分(C)、無機又は有機顔料0.001〜5重量部 く効 果〉 本発明のプロピレン樹脂組成物は、結晶性プロピレン重
合体に特定な構造の有機リン酸エステル化合物と、脂肪
族金属塩またはアルキル乳酸金属塩と、顔料とを特定な
割合で配合してなるもので、優れた剛性と顔料分散性と
を備えていることから、着色された射出成形体用素材と
して適したものであり、各種工業用部品、例えば家庭電
化製品の冷蔵庫などの部品、高剛性コンテナー、電子レ
ンジ用食品容器、自動車のバンパー、インストルメント
パネルなどの内装品、外装部品などの射出有色成形品と
して成形することができる。
(I)構成成分
(1)結晶性プロピレン重合体
本発明のプロピレン樹脂組成物において主成分として用
いられる結晶性プロピレン重合体としては、プロピレン
単独重合体の他に、プロピレンと炭素数2〜18個、好
ましくは2〜9個の他のα−オレフィン、例えばエチレ
ン、1−ブテン、1−ペンテン、4−メチルペンテン−
1等や、酢酸ビニル等との共重合体などがある。具体的
には、ホモポリプロピレン、プロピレン・エチレンブロ
ック又はランダム共重合体、プロピレン・エチレン・ブ
テン共重合体などが好適な例であるが、これらに限定さ
れるものではない。特に好ましくは、ホモポリプロピレ
ン、プロピレン・エチレンブロック共重合体である。中
でもMFR(230℃、2、 16kg)か0.1〜1
00g/10分、好ましくは1〜90g/10分のもの
か最適である。
いられる結晶性プロピレン重合体としては、プロピレン
単独重合体の他に、プロピレンと炭素数2〜18個、好
ましくは2〜9個の他のα−オレフィン、例えばエチレ
ン、1−ブテン、1−ペンテン、4−メチルペンテン−
1等や、酢酸ビニル等との共重合体などがある。具体的
には、ホモポリプロピレン、プロピレン・エチレンブロ
ック又はランダム共重合体、プロピレン・エチレン・ブ
テン共重合体などが好適な例であるが、これらに限定さ
れるものではない。特に好ましくは、ホモポリプロピレ
ン、プロピレン・エチレンブロック共重合体である。中
でもMFR(230℃、2、 16kg)か0.1〜1
00g/10分、好ましくは1〜90g/10分のもの
か最適である。
これらプロピレン重合体は、通常チーグラー・ナツタ触
媒にて製造されるか、塩化マグネシウム等の担体に前記
触媒の一成分を担持させた担持型触媒を用いて製造した
ものをも使用することが出来る。
媒にて製造されるか、塩化マグネシウム等の担体に前記
触媒の一成分を担持させた担持型触媒を用いて製造した
ものをも使用することが出来る。
このような結晶性プロピレン重合体は市販されているも
のの中から適宜選択して使用することができる。
のの中から適宜選択して使用することができる。
(2)成 分A
本発明のプロピレン樹脂組成物において配合される成分
Aとしては、以下に示す一般式(1)または一般式(I
I)にて表わされる有機リン酸エステル化合物である。
Aとしては、以下に示す一般式(1)または一般式(I
I)にて表わされる有機リン酸エステル化合物である。
一般式(1)
一般式
(II)
(ただし、上記一般式(I)および(II)中のR1お
よびR2は同じ又は異なる水素原子、又は炭素数1〜8
、好ましくは1〜5のアルキル基を、Xは硫黄原子又は
−CH−(式中のR3は水素原子又は炭素数1〜4のア
ルキル基、好ましくは水素原子又は炭素数1〜2のアル
キル基を表わす。〕を、Yは水酸基又は水素原子を、a
は1又は0、bは1又はOscおよびdは同じ又は異な
る0〜3の整数をそれぞれ表わす。)。
よびR2は同じ又は異なる水素原子、又は炭素数1〜8
、好ましくは1〜5のアルキル基を、Xは硫黄原子又は
−CH−(式中のR3は水素原子又は炭素数1〜4のア
ルキル基、好ましくは水素原子又は炭素数1〜2のアル
キル基を表わす。〕を、Yは水酸基又は水素原子を、a
は1又は0、bは1又はOscおよびdは同じ又は異な
る0〜3の整数をそれぞれ表わす。)。
成分Aの有機リン酸エステル化合物の具体例を挙げれば
、次に示す化合物を好適な代表例として挙げることがで
きるが、これら化合物に限定されるものではない。
、次に示す化合物を好適な代表例として挙げることがで
きるが、これら化合物に限定されるものではない。
(3)成 分B
本発明のプロピレン樹脂組成物において配合される成分
Bとしては、炭素数が6〜40て、金属がアルカリ金属
又はカルシウムである、脂肪族金属塩およびアルキル乳
酸金属塩から選ばれた化合物であり、例えば、ステアリ
ン酸、ラウリン酸、オレイン酸、ヒドロキシステアリン
酸、ベヘニン酸、モンタン酸、ステアリル乳酸なとの、
リチウム塩、ナトリウム塩、カリウム塩、カルシウム塩
なとを挙げることかできる。具体的には、ステアリン酸
リチウム、ステアリン酸ナトリウム、ステアリン酸カリ
ウム、ヒドロキシステアリン酸リチウム、ヒドロキンス
テアリン酸ナトリウム、ラウリン酸ナトリウム、モンタ
ン酸ナトリウム、ステアリル乳酸リチウム、ステアリン
酸カルシウム、ヒドロキンステアリン酸カルシウム、ス
テアリル乳酸カルシウム等がある。
Bとしては、炭素数が6〜40て、金属がアルカリ金属
又はカルシウムである、脂肪族金属塩およびアルキル乳
酸金属塩から選ばれた化合物であり、例えば、ステアリ
ン酸、ラウリン酸、オレイン酸、ヒドロキシステアリン
酸、ベヘニン酸、モンタン酸、ステアリル乳酸なとの、
リチウム塩、ナトリウム塩、カリウム塩、カルシウム塩
なとを挙げることかできる。具体的には、ステアリン酸
リチウム、ステアリン酸ナトリウム、ステアリン酸カリ
ウム、ヒドロキシステアリン酸リチウム、ヒドロキンス
テアリン酸ナトリウム、ラウリン酸ナトリウム、モンタ
ン酸ナトリウム、ステアリル乳酸リチウム、ステアリン
酸カルシウム、ヒドロキンステアリン酸カルシウム、ス
テアリル乳酸カルシウム等がある。
これら成分Aと成分Bとの組合せにおける好適な組合せ
としては、成分Aとして上記化合物A1ないしA−5の
ような環状リン化合物を用いる場合にはアルカリ金属の
塩類を用いることか好ましい。また、上記化合物A−6
やA−7のような非環状リン化合物を用いる場合にはカ
ルシウム塩を用いることが好ましい。
としては、成分Aとして上記化合物A1ないしA−5の
ような環状リン化合物を用いる場合にはアルカリ金属の
塩類を用いることか好ましい。また、上記化合物A−6
やA−7のような非環状リン化合物を用いる場合にはカ
ルシウム塩を用いることが好ましい。
(4)成 分C
本発明のプロピレン樹脂組成物において配合される成分
Cの有機及び無機顔料としては、有機系として、縮合ア
ゾ系、イソインドリノン系、キナクリドン系、ペリノン
系、ペリレン系、キノフタロン系、アンスラキノン系、
フタロシアニン系、の顔料かあり、無機系として、酸化
チタン、チタンイエロー、亜鉛華、鉄黒、カーボン、弁
柄、群青等の顔料がある。
Cの有機及び無機顔料としては、有機系として、縮合ア
ゾ系、イソインドリノン系、キナクリドン系、ペリノン
系、ペリレン系、キノフタロン系、アンスラキノン系、
フタロシアニン系、の顔料かあり、無機系として、酸化
チタン、チタンイエロー、亜鉛華、鉄黒、カーボン、弁
柄、群青等の顔料がある。
(5)付加的成分り
本発明のプロピレン樹脂組成物中には、本発明の効果を
著しく損なわない限り、任意成分として他の付加的成分
りを配合することができる。
著しく損なわない限り、任意成分として他の付加的成分
りを配合することができる。
即ち、ヒンダードフェノール系、イオウ系、リン系等の
酸化防止剤、ヒンダードアミン系、トリアゾール系、ベ
ンゾフェノン系、ベンゾエート系、ニッケル系、サリチ
ル酸系等の光安定剤、そのほか、必要に応して、帯電防
止剤、滑剤、過酸化物、金属不活性化剤、核剤等を配合
することが出来る。
酸化防止剤、ヒンダードアミン系、トリアゾール系、ベ
ンゾフェノン系、ベンゾエート系、ニッケル系、サリチ
ル酸系等の光安定剤、そのほか、必要に応して、帯電防
止剤、滑剤、過酸化物、金属不活性化剤、核剤等を配合
することが出来る。
又、タルク、マイカ、ガラス繊維、硫酸バリウム、炭酸
カルシウム、チタン酸カリウム、ナイロン繊維等の無機
、有機系の充填材、さらには他の樹脂成分をブレンド、
又はアロイ化した系でも有効てある。
カルシウム、チタン酸カリウム、ナイロン繊維等の無機
、有機系の充填材、さらには他の樹脂成分をブレンド、
又はアロイ化した系でも有効てある。
(II)配合量比
上記結晶性プロピレン重合体成分に前記必須の配合成分
A−Cの配合量比は、成分Aの化合物の配合量はプロピ
レン重合体100重量部当り0.01〜5重量部、好ま
しくは、0.03〜2重量部である。上記範囲未満ては
剛性の改良効果が小さく、上記範囲を超えると不経済で
あるのみならず、ブリードが発生したり、金型汚染の問
題を生ずる。
A−Cの配合量比は、成分Aの化合物の配合量はプロピ
レン重合体100重量部当り0.01〜5重量部、好ま
しくは、0.03〜2重量部である。上記範囲未満ては
剛性の改良効果が小さく、上記範囲を超えると不経済で
あるのみならず、ブリードが発生したり、金型汚染の問
題を生ずる。
また、成分Bの配合量はプロピレン重合体100重量部
当り0.01〜5重量部、好ましくは0.03〜2重量
部である。上記範囲未満では、剛性、並びに顔料分散効
果が充分でなく、上記範囲を超えるとブリード、金型汚
染、変色の問題などを起し好ましくない。
当り0.01〜5重量部、好ましくは0.03〜2重量
部である。上記範囲未満では、剛性、並びに顔料分散効
果が充分でなく、上記範囲を超えるとブリード、金型汚
染、変色の問題などを起し好ましくない。
更に、成分Cの配合量は要求される成形品の色により決
まるものであるが、プロピレン重合体100重量部当り
、0.001〜5重量部、好ましくは0.01〜3重量
部である。
まるものであるが、プロピレン重合体100重量部当り
、0.001〜5重量部、好ましくは0.01〜3重量
部である。
([I)プロピレン樹脂組成物の製造
本発明のプロピレン樹脂組成物は上記各成分A〜Cを前
記配合量比の割合て配合する以外は通常の方法にて製造
することができる。
記配合量比の割合て配合する以外は通常の方法にて製造
することができる。
具体的に述べれば、パウダー状のプロピレン重合体に前
記成分A〜成分C1必要に応じて他の付加的成分りを入
れ、ヘンシェルミキサーにてブレンド後、押出機にて溶
融混合してペレットとする。
記成分A〜成分C1必要に応じて他の付加的成分りを入
れ、ヘンシェルミキサーにてブレンド後、押出機にて溶
融混合してペレットとする。
このペレットを射出成形機にて目的とする成形品に加工
する。このとき、成分Cは成形段階にて配合することが
できる。
する。このとき、成分Cは成形段階にて配合することが
できる。
[IV)プロピレン樹脂組成物
このようにして製造された本発明のブ、ロビレン樹脂組
成物は、射出成形加工して得られる射出成形体とするこ
とにより特にその効果を発揮することができ、そのよう
な射出成形体の具体例としては、家庭電化製品の冷蔵庫
なとの部品、高剛性コンテナー、電子レンジ用食品容器
、自動車のバンパー、インストルメントパネルなどの内
装品、外装部品などの射出有色成形品を挙げることがて
きる。
成物は、射出成形加工して得られる射出成形体とするこ
とにより特にその効果を発揮することができ、そのよう
な射出成形体の具体例としては、家庭電化製品の冷蔵庫
なとの部品、高剛性コンテナー、電子レンジ用食品容器
、自動車のバンパー、インストルメントパネルなどの内
装品、外装部品などの射出有色成形品を挙げることがて
きる。
本発明のプロピレン樹脂組成物について、より具体的に
説明するため、以下に実施例および比較例の実験例を示
すが、これら実験例は、本発明の目的を損わない限り、
これらに限定されるものではない。
説明するため、以下に実施例および比較例の実験例を示
すが、これら実験例は、本発明の目的を損わない限り、
これらに限定されるものではない。
また、本実験例において使用した化合物の略号は以下の
通りである。
通りである。
成分A
A−1文中A−1の化合物
A−5文中A−5の化合物
A−6文中A−6の化合物
成分B
S−L ステアリン酸リチウム
H5−L 12−ヒドロキシ−ステアリン酸リチウ
ム ステアリン酸ナトリウム ステアリン酸カルシウム ステアリル乳酸カルシウム S−〇 −N N−C 成分C B W CYB R 成分D IRIOIO: 11?168・ NAl0: 他の金属塩 カーボンブランク 酸化チタン フタロシアニンブルー ペリレンレッド テトラキス〔メチレン−3−(3’ 5′ −ジ−t−ブチル−4′ −ヒドロキシフェニル
)プロピオネート〕 メタン トリス(2,4−ジ−t−ブチルフ ェニル)フォスファイト リン酸ビス(4−t−ブチルフェニ ル)ナトリウム S−A:モノヒドロキシステアリン酸アルミニウム S−Z ニステアリン酸亜鉛 S−Mニステアリン酸マグネシウム 実施例1〜10及び比較例1〜9 MFRか10g/10分のホモポリプロピレン100重
量部に、第1表に示す配合剤を第1表に示す配合量で配
合し、ヘンシェルミキサーにてブレンドした後、内径3
011の押出機にて溶融混線(230℃)してベレット
とした。
ム ステアリン酸ナトリウム ステアリン酸カルシウム ステアリル乳酸カルシウム S−〇 −N N−C 成分C B W CYB R 成分D IRIOIO: 11?168・ NAl0: 他の金属塩 カーボンブランク 酸化チタン フタロシアニンブルー ペリレンレッド テトラキス〔メチレン−3−(3’ 5′ −ジ−t−ブチル−4′ −ヒドロキシフェニル
)プロピオネート〕 メタン トリス(2,4−ジ−t−ブチルフ ェニル)フォスファイト リン酸ビス(4−t−ブチルフェニ ル)ナトリウム S−A:モノヒドロキシステアリン酸アルミニウム S−Z ニステアリン酸亜鉛 S−Mニステアリン酸マグネシウム 実施例1〜10及び比較例1〜9 MFRか10g/10分のホモポリプロピレン100重
量部に、第1表に示す配合剤を第1表に示す配合量で配
合し、ヘンシェルミキサーにてブレンドした後、内径3
011の押出機にて溶融混線(230℃)してベレット
とした。
このベレットを射出成形機(240℃)にて長さ80關
、幅10mm、肉厚4111の試験片に成形した。この
試験片を用いて、曲げ弾性率(JIS−に7203)を
測定した。
、幅10mm、肉厚4111の試験片に成形した。この
試験片を用いて、曲げ弾性率(JIS−に7203)を
測定した。
また、このベレットを230℃にセットした圧縮成形機
にて圧縮して、スペーサー無しで薄いフィルムを成形し
た。そして、このフィルムの顔料分散を目視にて観察し
て判定した。その結果を第1表に示す。
にて圧縮して、スペーサー無しで薄いフィルムを成形し
た。そして、このフィルムの顔料分散を目視にて観察し
て判定した。その結果を第1表に示す。
なお、顔料分散の判定基準は、以下の四段階にて行なっ
た。
た。
A:極めて良好 B:良 好
C:若干不良 D=不 良
実施例11〜16及び比較例10〜16MFRが30
g / 10分、エチレン含量か3重量%のブロックコ
ポリマーを用いた以外は実施例1と同様の方法にて行な
った。その結果を第1表に示す。
g / 10分、エチレン含量か3重量%のブロックコ
ポリマーを用いた以外は実施例1と同様の方法にて行な
った。その結果を第1表に示す。
Claims (1)
- 【特許請求の範囲】 結晶性プロピレン重合体100重量部に下記成分(A)
〜成分(C)を配合してなることを特徴とするプロピレ
ン樹脂組成物。 成分(A):次に示す一般式( I )または一般式(II
)にて表わされる有機リン酸エステル化合物0.01〜
5重量部 一般式( I ) ▲数式、化学式、表等があります▼ 一般式(II) ▲数式、化学式、表等があります▼ (ただし、上記一般式( I )および(II) 中のR^1およびR^2は同一又は異なる水素原子、又
は炭素数1〜8のアルキル基を、Xは硫黄原子又は▲数
式、化学式、表等があります▼〔式中のR^3は 水素原子又は炭素数1〜4のアルキル基を表わす。〕を
、Yは水酸基又は水素原子を、aは1又は0、bは1又
は0、cおよびdは同一又は異なる0〜3の整数をそれ
ぞれ表わす。) 成分(B):炭素数が6〜40で、金属がアルカリ金属
又はカルシウムである、脂肪族金属塩およびアルキル乳
酸金属塩から選ばれた化合物0.01〜5重量部 成分(C):無機又は有機顔料0.001〜5重量部