JPH04193586A - 光記録媒体 - Google Patents
光記録媒体Info
- Publication number
- JPH04193586A JPH04193586A JP2326310A JP32631090A JPH04193586A JP H04193586 A JPH04193586 A JP H04193586A JP 2326310 A JP2326310 A JP 2326310A JP 32631090 A JP32631090 A JP 32631090A JP H04193586 A JPH04193586 A JP H04193586A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- recording layer
- substrate
- optical recording
- recording
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は光ディスク等の光記録媒体、特にCD規格に準
じた信号の記録再生が可能な追記型コンパクトディスク
に関する。
じた信号の記録再生が可能な追記型コンパクトディスク
に関する。
〔従来の技術及び発明が解決しようとする課題〕近年、
コンパクトディスク(CO)に記録機能を付加した追記
型CDの開発がなされつつある。これは市販のCDプレ
ーヤーで再生可能なことを狙っており、従ってCDの国
際規格を満たす必要がある。CD規格においては70%
以上という高い反射率が要求されるため、金、アルミニ
ウム等の反射率の高い金属反射層を含む媒体構成をとる
ことが多い。
コンパクトディスク(CO)に記録機能を付加した追記
型CDの開発がなされつつある。これは市販のCDプレ
ーヤーで再生可能なことを狙っており、従ってCDの国
際規格を満たす必要がある。CD規格においては70%
以上という高い反射率が要求されるため、金、アルミニ
ウム等の反射率の高い金属反射層を含む媒体構成をとる
ことが多い。
特開平2−87339号公報においては、基板上にレー
ザー光を吸収する色素をスピンコードした光吸収層を設
け、更にその上に金属反射層を積層した媒体の例が示さ
れている。この媒体は反射率をはじめ各種の信号レベル
がCD規格を満たしており。
ザー光を吸収する色素をスピンコードした光吸収層を設
け、更にその上に金属反射層を積層した媒体の例が示さ
れている。この媒体は反射率をはじめ各種の信号レベル
がCD規格を満たしており。
市販のCDプレーヤーで再生可能である。
ところで、この媒体に用いる色素はレーザー光を吸収す
る色素ではあるが、レーザー光の波長に吸収極大をもつ
ような色素ではない。もしレーザー光の波長に吸収極大
をもつような色素を用いると、レーザー光の吸収が大き
すぎて裏面の反射層からの反射光はほとんど利用できな
くなるため702以上の反射率を実現できないからであ
るミ従って実際には吸収極大がレーザー光波長がらばず
れた色素を用い1色素層の表裏両面での多重反射干渉効
果を利用して高反射率を得ている。干渉効果により高反
射率を得るためには、色素層の複素屈折率(n−ik)
及び膜厚の最適化が必要であるが、この場合の複素屈折
率(n−ik)及び膜厚の最適値は、n≧1.8、k≦
0.3、膜厚100nm−2100nであり、色素層膜
厚についてはかなり厚い膜となる。
る色素ではあるが、レーザー光の波長に吸収極大をもつ
ような色素ではない。もしレーザー光の波長に吸収極大
をもつような色素を用いると、レーザー光の吸収が大き
すぎて裏面の反射層からの反射光はほとんど利用できな
くなるため702以上の反射率を実現できないからであ
るミ従って実際には吸収極大がレーザー光波長がらばず
れた色素を用い1色素層の表裏両面での多重反射干渉効
果を利用して高反射率を得ている。干渉効果により高反
射率を得るためには、色素層の複素屈折率(n−ik)
及び膜厚の最適化が必要であるが、この場合の複素屈折
率(n−ik)及び膜厚の最適値は、n≧1.8、k≦
0.3、膜厚100nm−2100nであり、色素層膜
厚についてはかなり厚い膜となる。
このような膜厚をスピンコード法で形成すると。
基板上にあらかじめ設けられているトラッキング用のグ
ループが埋まってしまうため、トラックエラー信号が出
にくくなるという問題がある。この解決策として、埋ま
ってしまう分を考慮してグループを深く作っておくこと
が考えられるが、深いグループは射出形成などによる基
板作成の際、転写性が悪くなるという問題が生ずる。
ループが埋まってしまうため、トラックエラー信号が出
にくくなるという問題がある。この解決策として、埋ま
ってしまう分を考慮してグループを深く作っておくこと
が考えられるが、深いグループは射出形成などによる基
板作成の際、転写性が悪くなるという問題が生ずる。
また、膜厚の記録層をスピンコード法で形成するために
は、高濃度の色素塗布液をスピンコードする必要がある
。このため色素材料には、塗布溶媒に対する高い溶解性
が要求され、用いる色素材料が限定されてしまう。さら
に、低コストで媒体を製造する゛には、射出成形された
基板に下引き層を介さず直接記録層を形成することが望
ましい。
は、高濃度の色素塗布液をスピンコードする必要がある
。このため色素材料には、塗布溶媒に対する高い溶解性
が要求され、用いる色素材料が限定されてしまう。さら
に、低コストで媒体を製造する゛には、射出成形された
基板に下引き層を介さず直接記録層を形成することが望
ましい。
しかし、最もよく用いられるポリカーボネート樹脂基板
やアクリル樹脂基板は、耐溶剤性が低く、アルコール系
溶媒などの極く限られた溶媒しか塗布溶媒として使用で
きないという問題があり、色素材料及び塗布溶媒の選定
が難しい。
やアクリル樹脂基板は、耐溶剤性が低く、アルコール系
溶媒などの極く限られた溶媒しか塗布溶媒として使用で
きないという問題があり、色素材料及び塗布溶媒の選定
が難しい。
一方、媒体の生産性を考慮した場合にも、スピンコード
形成した記録層に真空製膜法により反射層を形成する方
法は、ウェットプロセスとドライプロセスの両方を用い
ているので、生産性が悪いという問題点がある。
形成した記録層に真空製膜法により反射層を形成する方
法は、ウェットプロセスとドライプロセスの両方を用い
ているので、生産性が悪いという問題点がある。
本発明は以上の問題点に鑑み、通常の追記型光記録媒体
(従来のコンピュータメモリ用、追記型光記録媒体)と
同程度の深さのグループを有する基板を用いても充分な
トラックニラ−信号が得られ、蒸着法やスパッタ法など
の従来より知られている真空製膜方法で容易に記録層形
成が可能である追記型CDの如き新規な光記録媒体を提
供するものである。
(従来のコンピュータメモリ用、追記型光記録媒体)と
同程度の深さのグループを有する基板を用いても充分な
トラックニラ−信号が得られ、蒸着法やスパッタ法など
の従来より知られている真空製膜方法で容易に記録層形
成が可能である追記型CDの如き新規な光記録媒体を提
供するものである。
上記目的を達成するため、本発明によれば、基板上に直
接または他の層シ介して記録層を設け、更にその上に直
接または他の層を介して光反射層を設けてなる光記録媒
体において、前記記録層が金属又は半金属の硫化物を主
成分とする無機材料により構成され、かつその複素屈折
率(n−ik)がn≧1゜8、k≦0.3なる条件を満
足することを特徴とする光記録媒体が提供される。
接または他の層シ介して記録層を設け、更にその上に直
接または他の層を介して光反射層を設けてなる光記録媒
体において、前記記録層が金属又は半金属の硫化物を主
成分とする無機材料により構成され、かつその複素屈折
率(n−ik)がn≧1゜8、k≦0.3なる条件を満
足することを特徴とする光記録媒体が提供される。
以下本発明の構成を詳述する。
本発明の光記録媒体の代表的な構成を第1図及び第2図
に示す。本発明の光記録媒体の最も簡単な構成のもので
は、第1図に示すように基板l上に記録層2が形成され
、その上に反射層3が形成されているが、第2図に示す
ように、必要に応じて基板1と記録層2との間に下引き
層4が、記録層2と反射層3との間に中間層5が、さら
に反射層3上に保護層6が形成されていてもよい。
に示す。本発明の光記録媒体の最も簡単な構成のもので
は、第1図に示すように基板l上に記録層2が形成され
、その上に反射層3が形成されているが、第2図に示す
ように、必要に応じて基板1と記録層2との間に下引き
層4が、記録層2と反射層3との間に中間層5が、さら
に反射層3上に保護層6が形成されていてもよい。
基板1の材料としては、透明プラスチック基板、ガラス
基板等を用いることができ、具体的には、例えば、ポリ
カーボネート樹脂、ポリオレフィン樹脂、アクリル樹脂
、エポキシ樹脂、石英ガラス、強化ガラス等を挙げるこ
とができる。なお、基板の表面には、トラッキング用案
内溝や案内ピット。
基板等を用いることができ、具体的には、例えば、ポリ
カーボネート樹脂、ポリオレフィン樹脂、アクリル樹脂
、エポキシ樹脂、石英ガラス、強化ガラス等を挙げるこ
とができる。なお、基板の表面には、トラッキング用案
内溝や案内ピット。
さらには、アドレス信号などのプリフォーマットが形成
されていてもよい。
されていてもよい。
記録層2は、金属又は半金属の硫化物を主成分とする無
機材料から構成され、その複屈折率(n−ik)はn≧
1.8、k≦0.3なる条件を満足する。記録層2の具
体的な材料例としては、 sb、s3、SnS、(sb
2S3)X(In2S3)y、(Sbz S3 )X
(GeS)y、(SnS)x (In2s、 )y、(
SnS)x(GeS)y、(SnS)zoy、(Sbz
S:、)xoy、(但し。
機材料から構成され、その複屈折率(n−ik)はn≧
1.8、k≦0.3なる条件を満足する。記録層2の具
体的な材料例としては、 sb、s3、SnS、(sb
2S3)X(In2S3)y、(Sbz S3 )X
(GeS)y、(SnS)x (In2s、 )y、(
SnS)x(GeS)y、(SnS)zoy、(Sbz
S:、)xoy、(但し。
40≦x(100,0<y≦60. X+!/=100
)等を挙げることが出来る。記録層2の膜厚は、材料の
複素屈折率(n−ik)の値により異なるが、記録層2
0表裏両面での多重反射干渉効果により高反射率の得ら
れるlOO〜200nm程度が好ましい。記録層2を基
板1又は下引き層4上に形成するには、蒸着法やスパッ
タ法などの従来より知られている真空製膜方法で容易に
行うことが出来る。
)等を挙げることが出来る。記録層2の膜厚は、材料の
複素屈折率(n−ik)の値により異なるが、記録層2
0表裏両面での多重反射干渉効果により高反射率の得ら
れるlOO〜200nm程度が好ましい。記録層2を基
板1又は下引き層4上に形成するには、蒸着法やスパッ
タ法などの従来より知られている真空製膜方法で容易に
行うことが出来る。
反射層3は、単体で高反射率の得られる金属。
半金属等を用いることができる。材料例としては、Au
、Ag、 Cu、 AQ、Cr、 Niなどを挙げるこ
とが出来、特に好ましくはAu、 AQが良い。また、
これらの金属は単独で用いてもよいし、合金として用い
てもよい。
、Ag、 Cu、 AQ、Cr、 Niなどを挙げるこ
とが出来、特に好ましくはAu、 AQが良い。また、
これらの金属は単独で用いてもよいし、合金として用い
てもよい。
下引き層4、中間層5は、■水又はガスなどのバリヤー
層、■記録層の保存安定性の向上、■反射率の向上、■
プレグルーブの形成などの機能を光記録媒体に付与する
ために設けられる。その材料例としては、前記■、■を
重視すれば高分子材料(アクリル樹脂、エポキシ樹脂な
ど)、無機化合物(Sin2、ZnS、 SiN、Ti
Nなど)が使用8来、前記■を重視すれば、無機化合物
(Sin、、ZnS、SiN、 TiN、AQN、 S
i、N4など)が使用でき、前記■を重視すれば紫外線
硬化樹脂、熱硬化性樹脂及び熱可塑性樹脂が使用できる
。下引き層4、中間層5の厚さは、材料の種類により異
なるが、0.01〜30碑ぐらいが適当である。
層、■記録層の保存安定性の向上、■反射率の向上、■
プレグルーブの形成などの機能を光記録媒体に付与する
ために設けられる。その材料例としては、前記■、■を
重視すれば高分子材料(アクリル樹脂、エポキシ樹脂な
ど)、無機化合物(Sin2、ZnS、 SiN、Ti
Nなど)が使用8来、前記■を重視すれば、無機化合物
(Sin、、ZnS、SiN、 TiN、AQN、 S
i、N4など)が使用でき、前記■を重視すれば紫外線
硬化樹脂、熱硬化性樹脂及び熱可塑性樹脂が使用できる
。下引き層4、中間層5の厚さは、材料の種類により異
なるが、0.01〜30碑ぐらいが適当である。
保護層6は、■記録層2をキズ、ホコリ、汚れなどから
保護し、■記録層2の保存安定性を向上させるなどのた
めに形成されるものである。保護層6の形成材料として
は、下引き層4、中間層5で挙げた材料をそのまま使用
することが出来る。保護層6の厚さは、下引き層4.中
間層5の場合と同様、材料の種類により異なるが、0.
1〜100m<らいが適当である。
保護し、■記録層2の保存安定性を向上させるなどのた
めに形成されるものである。保護層6の形成材料として
は、下引き層4、中間層5で挙げた材料をそのまま使用
することが出来る。保護層6の厚さは、下引き層4.中
間層5の場合と同様、材料の種類により異なるが、0.
1〜100m<らいが適当である。
なお、保護層6、下引き層4、中間層5の形成手段とし
ては、無機材料を形成させる場合には真空製膜方法(蒸
着法、スパッタ法など)、有機材料を形成させる場合に
は溶液塗工法(スピンナーコーティング、スプレーコー
ティング、浸漬コーティングなど)等の従来より知られ
ている方法が採用し得る。
ては、無機材料を形成させる場合には真空製膜方法(蒸
着法、スパッタ法など)、有機材料を形成させる場合に
は溶液塗工法(スピンナーコーティング、スプレーコー
ティング、浸漬コーティングなど)等の従来より知られ
ている方法が採用し得る。
本発明の光記録媒体は、記録層2を金属又は半金属の硫
化物を主成分とする無機材料からなり、その複屈折率(
n−ik)がn≧1.8、k≦0.3を満たすものによ
り構成しているので、基板1に記録層2を設け、この上
にAu、 i等の金属からなる反射層3を形成すること
により、CD規格の高反射率(R%≧70)を得ること
が可能である。さらに蒸着法やスパッタ法などの真空製
膜法により、記録層を容易に形成できるので、厚膜の記
録層を形成しても、スピンコードにより設けた膜のよう
に基板のグループを埋めることがなく、トラックエラー
信号が確保される。
化物を主成分とする無機材料からなり、その複屈折率(
n−ik)がn≧1.8、k≦0.3を満たすものによ
り構成しているので、基板1に記録層2を設け、この上
にAu、 i等の金属からなる反射層3を形成すること
により、CD規格の高反射率(R%≧70)を得ること
が可能である。さらに蒸着法やスパッタ法などの真空製
膜法により、記録層を容易に形成できるので、厚膜の記
録層を形成しても、スピンコードにより設けた膜のよう
に基板のグループを埋めることがなく、トラックエラー
信号が確保される。
また、本発明の光記録媒体は、レーザー光等の記録光照
射により記録層を相変化又は変形させて記録ピットを形
成することができ、本光記録媒体により、CD規格に準
じた信号の記録再生が可能であることが確認された。
射により記録層を相変化又は変形させて記録ピットを形
成することができ、本光記録媒体により、CD規格に準
じた信号の記録再生が可能であることが確認された。
以下本発明を実施例により更に詳細に説明する。
(実施例1〜4)
表面に溝幅0.81a、溝深さ700人、トラックピッ
チ1.6.のプレグルーブが設けられたポリカーボネー
ト射出成形ディスク基板を用意し、5b2s、、SnS
、(Sbz Si )s s (Inz s、 )3s
、(SnS)、 s (In2 Sl )3 sの記録
層を抵抗加熱方式の真空蒸着装置を用いて1000〜2
000人の膜厚で形成した。これらの記録層の複素屈折
率は、理論値の分光特性とのフィッティングによりいず
れもn≧1.8、k≦0.3であることが確認された。
チ1.6.のプレグルーブが設けられたポリカーボネー
ト射出成形ディスク基板を用意し、5b2s、、SnS
、(Sbz Si )s s (Inz s、 )3s
、(SnS)、 s (In2 Sl )3 sの記録
層を抵抗加熱方式の真空蒸着装置を用いて1000〜2
000人の膜厚で形成した。これらの記録層の複素屈折
率は、理論値の分光特性とのフィッティングによりいず
れもn≧1.8、k≦0.3であることが確認された。
次に、これらの記録層の上に上記と同じ装置を用いて、
Auを約1000人の膜厚で設け、実施例1〜実施例4
の光記録媒体を作成した。
Auを約1000人の膜厚で設け、実施例1〜実施例4
の光記録媒体を作成した。
(比較例)
上記実施例と同じ基板上に下式で表わされるシアニン色
素をメタノールと1,2−ジクロルエタンの混合溶媒を
用いてスピンコードすることにより、厚さ約1400人
の色素層を形成した。この色素層上にAuの反射層を上
記実施例と同じ条件で作製し、比較例の光記録媒体とし
た。用いた色素層の吸収スペクトルを第3図に示す。
素をメタノールと1,2−ジクロルエタンの混合溶媒を
用いてスピンコードすることにより、厚さ約1400人
の色素層を形成した。この色素層上にAuの反射層を上
記実施例と同じ条件で作製し、比較例の光記録媒体とし
た。用いた色素層の吸収スペクトルを第3図に示す。
これらの光記録媒体に線速1’、3m/s、記録レーザ
ーパワー6閣V、再生レーザーパワー0.5mす(波長
780nm)でEFM信号を記録じ、再生信号波形及び
トラックエラー信号を観測した。その結果を表−1に示
す。
ーパワー6閣V、再生レーザーパワー0.5mす(波長
780nm)でEFM信号を記録じ、再生信号波形及び
トラックエラー信号を観測した。その結果を表−1に示
す。
表−1
上記表から明らかなように、本発明の光記録媒体は、C
D規格を満足する信号レベル(I、□/Itop≧0.
6.0.3≦I3/Itop≦0.6)が得られ、反射
率も70%以上を有していた。さらに本発明の各実施例
では比較例に比へ大きなトラックエラー信号が得られ、
本発明の効果が確認された。
D規格を満足する信号レベル(I、□/Itop≧0.
6.0.3≦I3/Itop≦0.6)が得られ、反射
率も70%以上を有していた。さらに本発明の各実施例
では比較例に比へ大きなトラックエラー信号が得られ、
本発明の効果が確認された。
本発明によれば、記録層に金属又は半金属の硫化物を主
成分とする無機材料からなりその複屈折率が前記の条件
を満たすものを用いたことにより、通常の深さのグルー
プを有する成形性の良い基板を用いても充分なトラック
エラー信号が得られる追記型CDの如き光記録媒体を提
供することが出来る。
成分とする無機材料からなりその複屈折率が前記の条件
を満たすものを用いたことにより、通常の深さのグルー
プを有する成形性の良い基板を用いても充分なトラック
エラー信号が得られる追記型CDの如き光記録媒体を提
供することが出来る。
また、本発明の光記録媒体においては、蒸着法やスパッ
タ法のような真空製膜方法により、容易に記録層を形成
することが出来るので、記録層、反射層をドライプロセ
ス工程で連続成膜することにより生産性を上げることが
できる。
タ法のような真空製膜方法により、容易に記録層を形成
することが出来るので、記録層、反射層をドライプロセ
ス工程で連続成膜することにより生産性を上げることが
できる。
第1図及び第2図は、それぞ九本発明による光記録媒体
の構成例を示す断面図、第3図は色素層の吸収スペクト
ル図である。 1・・基板 2・・・記録層 3・・・反射層 4・・・下引き層 5・・中間層 6・保護層
の構成例を示す断面図、第3図は色素層の吸収スペクト
ル図である。 1・・基板 2・・・記録層 3・・・反射層 4・・・下引き層 5・・中間層 6・保護層
Claims (2)
- (1)基板上に直接または他の層を介して記録層を設け
、更にその上に直接または他の層を介して光反射層を設
けてなる光記録媒体において、前記記録層が金属又は半
金属の硫化物を主成分とする無機材料により構成され、
かつその複素屈折率(n−ik)がn≧1.8、k≦0
.3なる条件を満足することを特徴とする光記録媒体。 - (2)前記記録層がイオウ以外の成分元素として、Sb
、Sn、In、Ge、Oから選ばれる元素を少なくとも
一つ以上含有することを特徴とする請求項(1)記載の
光記録媒体。