JPH01113394A - フォトクロミック化合物 - Google Patents
フォトクロミック化合物Info
- Publication number
- JPH01113394A JPH01113394A JP62267865A JP26786587A JPH01113394A JP H01113394 A JPH01113394 A JP H01113394A JP 62267865 A JP62267865 A JP 62267865A JP 26786587 A JP26786587 A JP 26786587A JP H01113394 A JPH01113394 A JP H01113394A
- Authority
- JP
- Japan
- Prior art keywords
- group
- photochromic
- polymerization
- compound
- benz
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は、衣料、装飾品用フォトクロミック材料、記録
材料用フォトクロミック材料または光学機器用として有
用な新規フォトクロミック化合物に関する。
材料用フォトクロミック材料または光学機器用として有
用な新規フォトクロミック化合物に関する。
7オトクロミツク物質のなかで、スピロ炭素を有スるイ
ンドリノスピロピラン化合物は、発消色速度に優れ、モ
ル吸光係数も大きく、バラエティ−に富んだ色調の変化
を示すことより、数多くの研究が報告されている。
ンドリノスピロピラン化合物は、発消色速度に優れ、モ
ル吸光係数も大きく、バラエティ−に富んだ色調の変化
を示すことより、数多くの研究が報告されている。
しかし、前述のスピロピラン化合物は耐久性に大きな問
題点が有る。その原因は、ピラン骨格のa、C二重結合
が容易に1重項酸素の攻撃を受け、分解するためである
。これに対し、オキサジン骨格のO,N二重結合は、酸
素分解反応に対して強固である。
題点が有る。その原因は、ピラン骨格のa、C二重結合
が容易に1重項酸素の攻撃を受け、分解するためである
。これに対し、オキサジン骨格のO,N二重結合は、酸
素分解反応に対して強固である。
そこで、本発明はこのように問題点を解決するもので、
その目的とするところは、発消色速度を任意に制御が可
能であり、モル吸光係数が大きく1バラエティ−に富ん
だ色調の変化を示し、耐久性に富んだフォトクロミック
化合物を提供することにある。
その目的とするところは、発消色速度を任意に制御が可
能であり、モル吸光係数が大きく1バラエティ−に富ん
だ色調の変化を示し、耐久性に富んだフォトクロミック
化合物を提供することにある。
すなわち本発明は、下記一般式で示されるフォトクロミ
ック化合物に関する。
ック化合物に関する。
♂
〔式中 R1〜R14は、水素、アルキル基、アルコキ
シ基、ベンジル基、アリール基s /”10 ケン。
シ基、ベンジル基、アリール基s /”10 ケン。
ニトロ基、アルフキジアルキル基、シアノ基、アルキル
アミノ基、カルボキシ基、カルボキシアルキル基、So
、M (Mはアルカリ金属)、R2とR3とで飽和炭化
水素環もしくは不飽和炭化水素環、重合もしくは縮合可
能な置換基から選ばれる同種または異種の一種以上のt
ita基を示す。〕本発明のフォトクロミック化合物は
、オキサジン骨格のO,N二重結合が、−重項酸素の攻
撃に対して、反応し難い為、耐久性が向上する。また、
置換基が電子吸引基、電子供与基と様々であるため、深
色効果、浅色効果による色調の変化を可能である。さら
に、分子中に重合や縮合が可能なwt、a基を付与した
場合、他の成分との反応や、自分自身との反応により、
ポリマー化され、フォトクロミック物質の流出を防ぐこ
とも可能となる。
アミノ基、カルボキシ基、カルボキシアルキル基、So
、M (Mはアルカリ金属)、R2とR3とで飽和炭化
水素環もしくは不飽和炭化水素環、重合もしくは縮合可
能な置換基から選ばれる同種または異種の一種以上のt
ita基を示す。〕本発明のフォトクロミック化合物は
、オキサジン骨格のO,N二重結合が、−重項酸素の攻
撃に対して、反応し難い為、耐久性が向上する。また、
置換基が電子吸引基、電子供与基と様々であるため、深
色効果、浅色効果による色調の変化を可能である。さら
に、分子中に重合や縮合が可能なwt、a基を付与した
場合、他の成分との反応や、自分自身との反応により、
ポリマー化され、フォトクロミック物質の流出を防ぐこ
とも可能となる。
このように、本発明では、前述の問題点を解決するに至
った。
った。
本発明の7オトクロミツク物質は、合成樹脂や紙への練
り込み法や浸漬法、昇華転写法、コーティング材料(プ
ライマー、バインダー、)1−ドコートなど)へ溶解も
しくは分散させ基材に塗布する方法、高分子を溶解した
溶液へ溶解もしくは分散させ、フィルムにする方法、他
のモノマーやコポリマーに入れ、重合もしくは共重合す
る方法など適用方法は様々である。
り込み法や浸漬法、昇華転写法、コーティング材料(プ
ライマー、バインダー、)1−ドコートなど)へ溶解も
しくは分散させ基材に塗布する方法、高分子を溶解した
溶液へ溶解もしくは分散させ、フィルムにする方法、他
のモノマーやコポリマーに入れ、重合もしくは共重合す
る方法など適用方法は様々である。
また、本発明における重合もしくは縮合可能な置換基と
は、ビニル基、アリル基、アクリル基。
は、ビニル基、アリル基、アクリル基。
メタクリル基、エポキシ基などの重合性置換基や水酸基
、メルカプト基、ハロゲンなどのように他成分と縮合反
応可能な置換基などがあげられる。
、メルカプト基、ハロゲンなどのように他成分と縮合反
応可能な置換基などがあげられる。
フォトクロミック化合物のざリマー化反応としては、ラ
ジカル重合、イオン重合、異性化重合、環化重合、脱離
重合9重縮合、付加縮合反応などがあり、フォトクロミ
ック物質のみのポリマー化や他成分と7オトクロミツク
物質との共重合などの適用方法がある。
ジカル重合、イオン重合、異性化重合、環化重合、脱離
重合9重縮合、付加縮合反応などがあり、フォトクロミ
ック物質のみのポリマー化や他成分と7オトクロミツク
物質との共重合などの適用方法がある。
さらに、フォトクロミック物質と酸化防止剤。
−重項酸素クエンチャー、紫外線吸収剤を加えることは
フォトクロミック物質の寿命延長や色調変化に効果的で
ある。
フォトクロミック物質の寿命延長や色調変化に効果的で
ある。
以下、実施例により、本発明を更に詳しく説明するが、
本発明は、これ等に限定されるものではない。
本発明は、これ等に限定されるものではない。
実施例1
1’、3’、3’−1リメチル−7−メトキシスピロ(
2H−(1,4)ベンゾオキサジン−2゜2′−ベンズ
(e)インドリン〕の合成及びその応用例。
2H−(1,4)ベンゾオキサジン−2゜2′−ベンズ
(e)インドリン〕の合成及びその応用例。
1.2,3.3−テトラメチルベンズ(8)インドリウ
ムのヨウ素塩五57 ? (cLo 1 mot)及び
2−ニトロソ−5−メトキシフェノール1.53? (
CL 01 mo4 )とをエタノール100dに加え
た後、さらにトリエチルアミン1.212P([LOl
2 mol )を添加し、窒素気流中5時間還流を行
なった。溶媒除去後、水を加え、塩化メチレンで抽出を
行なった。この塩化メチレン溶液を、活性炭で処理した
後、溶媒除去をし、分取液体クロマトグラフィーで目的
とする1 / 、 5 / 、 5/ )リメ
チル−7−メトキシスピロ(2H−(1’ e4′)
ベンゾオキサジン−2,2′−ベンズ〔e〕インドリン
〕を1.37 f (収率58%)得た。
ムのヨウ素塩五57 ? (cLo 1 mot)及び
2−ニトロソ−5−メトキシフェノール1.53? (
CL 01 mo4 )とをエタノール100dに加え
た後、さらにトリエチルアミン1.212P([LOl
2 mol )を添加し、窒素気流中5時間還流を行
なった。溶媒除去後、水を加え、塩化メチレンで抽出を
行なった。この塩化メチレン溶液を、活性炭で処理した
後、溶媒除去をし、分取液体クロマトグラフィーで目的
とする1 / 、 5 / 、 5/ )リメ
チル−7−メトキシスピロ(2H−(1’ e4′)
ベンゾオキサジン−2,2′−ベンズ〔e〕インドリン
〕を1.37 f (収率58%)得た。
得られたオキサジン化合物11 ? eメタクリル酸メ
チル4992及びA’lBN[LI L/とを60℃で
20時間かけて重合を行ない、得られたポリマーを厚さ
11圓のフィルムとなるよう成形した。
チル4992及びA’lBN[LI L/とを60℃で
20時間かけて重合を行ない、得られたポリマーを厚さ
11圓のフィルムとなるよう成形した。
このフィルムは、室内では無色で、紫外線を照射すると
紫色に着色した。
紫色に着色した。
フォトクロミック性能の評価は次のようにして行ない表
1に示した。
1に示した。
(1)透過率
光照射前後の400〜700rLrrLの平均透過率を
表1に示した。なお、光照射の光源は500W超高圧水
銀灯(ウシオX気社製)を用い、測定時の温度は25℃
とした。
表1に示した。なお、光照射の光源は500W超高圧水
銀灯(ウシオX気社製)を用い、測定時の温度は25℃
とした。
(2)耐久性
キセノンロングライフフェードメーター(スガ試験機社
製IFAL−25AX)に50時間後ノ透過率の性能評
価を行い表1に示した。
製IFAL−25AX)に50時間後ノ透過率の性能評
価を行い表1に示した。
実施例2
1/ (p−アリルベンジル) 3/、3/−ジ
メチル−5,7−シメトキシスピロ(2H−(1,4)
ベンゾオキサジン−2,2′−ベンズ〔e〕インドリン
〕の合成及びその応用例。
メチル−5,7−シメトキシスピロ(2H−(1,4)
ベンゾオキサジン−2,2′−ベンズ〔e〕インドリン
〕の合成及びその応用例。
すa=t、+1−4
2.5.5−)リメチルペンズ(e)インドレニン2.
09r(101mot)とP−りOコメチルスチレン1
.525 f (α01 mot)とヒドロキノンII
L21及びエタノール10Wlを封管し、80℃で4時
間反応させた後、生成物をエーテルで洗浄し、1−(P
−アリルベンジル)*2+!’y5−トリメチルベンズ
(e)インドリウムの塩素塩の結晶をLO7y(収率8
5%)で得た。
09r(101mot)とP−りOコメチルスチレン1
.525 f (α01 mot)とヒドロキノンII
L21及びエタノール10Wlを封管し、80℃で4時
間反応させた後、生成物をエーテルで洗浄し、1−(P
−アリルベンジル)*2+!’y5−トリメチルベンズ
(e)インドリウムの塩素塩の結晶をLO7y(収率8
5%)で得た。
上記塩素塩1.808 ? (5X 1 o−”mot
) と2−二トロン−3,5−ジメトキシフェノール
Q、77 ? (5X 10−3mot)ヒドロキノン
α1fとをエタノール50dに加えた後、さらにトリエ
チルアミン0.606F(6X10−3 mot)を添
加し、窒素気流中5時間還流を行りた。溶媒除去後、水
を加え、塩化メチレンで抽出を行なった。この塩化メチ
レン溶液を、活性炭で処理した後、溶媒除去をし、分取
液体クロマトグラフィーで目的とする1′−(P−アリ
ルベンジル) 3/、3/−ジメチル−5,7−シメ
トキシスビロ(2’H−(1,4)ペンジオキサジン−
2,2′−ベンズ〔e〕インドリン〕を1.1039
(収率45%)で得た。
) と2−二トロン−3,5−ジメトキシフェノール
Q、77 ? (5X 10−3mot)ヒドロキノン
α1fとをエタノール50dに加えた後、さらにトリエ
チルアミン0.606F(6X10−3 mot)を添
加し、窒素気流中5時間還流を行りた。溶媒除去後、水
を加え、塩化メチレンで抽出を行なった。この塩化メチ
レン溶液を、活性炭で処理した後、溶媒除去をし、分取
液体クロマトグラフィーで目的とする1′−(P−アリ
ルベンジル) 3/、3/−ジメチル−5,7−シメ
トキシスビロ(2’H−(1,4)ペンジオキサジン−
2,2′−ベンズ〔e〕インドリン〕を1.1039
(収率45%)で得た。
得られたオキサジン化合物α1f、2.2−ビス(3,
5−ジブロモ−4−メタクリロオキシエトキフェニル)
プロパン25v、スチレン202、ジエチレングリコー
ルビスアリルカーボネート5 t 、 tart−ブチ
ルパーオキネオデカネートα52とを混合し、酢酸ビニ
ル−ポリエチレン共重合体のガスケット及び2枚のフラ
ットなガラス型より構成される中心厚2間のモールドに
注入し、40℃50時間、60℃8時間、80℃2時間
で重合を行なった。得られた、フラット板は、室内では
無色で、紫外線を照射すると赤紫色に着色した。
5−ジブロモ−4−メタクリロオキシエトキフェニル)
プロパン25v、スチレン202、ジエチレングリコー
ルビスアリルカーボネート5 t 、 tart−ブチ
ルパーオキネオデカネートα52とを混合し、酢酸ビニ
ル−ポリエチレン共重合体のガスケット及び2枚のフラ
ットなガラス型より構成される中心厚2間のモールドに
注入し、40℃50時間、60℃8時間、80℃2時間
で重合を行なった。得られた、フラット板は、室内では
無色で、紫外線を照射すると赤紫色に着色した。
フォトクロミック性能の評価は実施例1の評価方法と同
様に行ない結果を表1に示した。
様に行ない結果を表1に示した。
実施例3
実施例1で得られた、1’ 、!’ 、5’−)リ
メチル−7−メトキシスビロ[:2H−(114)−ベ
ンゾオキサジン−2,2′−ベンズ(e)インドリン)
20 F’をジエチレングリコール80fに溶かした
溶液を100℃に加熱し、この溶液に、厚さ2囚のジエ
チレングリコールビスアリカーボネート樹脂製フラット
板を30分間浸漬し、イソプロピルアルコールにて洗浄
した。このフラット板に、真空蒸着により、Si、O,
、zro、。
メチル−7−メトキシスビロ[:2H−(114)−ベ
ンゾオキサジン−2,2′−ベンズ(e)インドリン)
20 F’をジエチレングリコール80fに溶かした
溶液を100℃に加熱し、この溶液に、厚さ2囚のジエ
チレングリコールビスアリカーボネート樹脂製フラット
板を30分間浸漬し、イソプロピルアルコールにて洗浄
した。このフラット板に、真空蒸着により、Si、O,
、zro、。
SiO□の順序でそれぞれ光学的膜厚2/4(λ=52
0ルrrL)の膜を設げた。
0ルrrL)の膜を設げた。
フォトクロミック性能の評価は実施例1の評価方法と同
様に行ない結果を表1に示した。
様に行ない結果を表1に示した。
実施例4
実施例1で碍られた、1/ 、3/ 、3/−トリ
メチル−7−メドキシスビロ(2a−(it4)ベンゾ
オキサジン−2,2′−ベンズ(e)インドリン〕11
を、r−グリシドキプロピル′トリメトキシシラン28
ノ、エタノール64r、[L05規定塩酸71.フロコ
ントロール剤0.02 S’ e塩化第1スズ107f
で調整したコーテイング液に溶かした。
メチル−7−メドキシスビロ(2a−(it4)ベンゾ
オキサジン−2,2′−ベンズ(e)インドリン〕11
を、r−グリシドキプロピル′トリメトキシシラン28
ノ、エタノール64r、[L05規定塩酸71.フロコ
ントロール剤0.02 S’ e塩化第1スズ107f
で調整したコーテイング液に溶かした。
この溶液を、アクリル板に塗布し、100℃で3時間乾
燥をした(膜厚5μm)。
燥をした(膜厚5μm)。
フォトクロミック性能の評価は実施例1の評価方法と同
様に行ない結果を表1に示した。
様に行ない結果を表1に示した。
以上に述べたように本発明は、オキサジン骨格を有する
ために、耐久性に優れている。書た、分子中に重合もし
くは縮合可能な置換基を有する化合物は、他成分もしく
は自分自身でポリマー化させることにより、フォトクロ
ミック物質の流出という問題点を解決することが可能で
ある。
ために、耐久性に優れている。書た、分子中に重合もし
くは縮合可能な置換基を有する化合物は、他成分もしく
は自分自身でポリマー化させることにより、フォトクロ
ミック物質の流出という問題点を解決することが可能で
ある。
このため、本発明は、サングラス、窓ガラス。
記録材料、繊維、装飾品への応用が可能である。
以上
Claims (1)
- 【特許請求の範囲】 下記、一般式で示されることを特徴とするフォトクロミ
ック化合物。 ▲数式、化学式、表等があります▼ 〔式中、R^1〜R^1^4は、水素、アルキル基、ア
ルコキシ基、ベンジル基、アリール基、ハロゲン、ニト
ロ基、アルコキシアルキル基、シアノ基、アルキルアミ
ノ基、カルボキシ基、カルボキシアルキル基、SO_3
M(Mはアルカリ金属)、R^2とR^3とで飽和炭化
水素環もしくは不飽和炭化水素環、重合もしくは縮合可
能な置換基から選ばれる同種または異種の一種以上の置
換基を示す。