JP7282211B2 - 不織布、その製造方法、該不織布を含む物品、及び該不織布を使用した衛生用品 - Google Patents
不織布、その製造方法、該不織布を含む物品、及び該不織布を使用した衛生用品 Download PDFInfo
- Publication number
- JP7282211B2 JP7282211B2 JP2021570454A JP2021570454A JP7282211B2 JP 7282211 B2 JP7282211 B2 JP 7282211B2 JP 2021570454 A JP2021570454 A JP 2021570454A JP 2021570454 A JP2021570454 A JP 2021570454A JP 7282211 B2 JP7282211 B2 JP 7282211B2
- Authority
- JP
- Japan
- Prior art keywords
- nonwoven fabric
- weight
- spunbond
- nonwoven
- elastomeric propylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
不織布であり、
前記不織布全体100重量%を基準にし、
1.0~8.0重量%の共単量体含量を有する7.0~17.0重量%のエラストマープロピレン共重合体と、
0.025~1.0重量%のアミド系化合物と、
0.375~1.0重量%のTiO2と、
残量のプロピレンホモ重合体と、を含む溶融紡糸フィラメント纎維集合体であり、
前記不織布の坪量(basis weight)は、15~30gsmであるとき、前記不織布のハンドル・オ・メーター(HOM)測定値が、縦方向(MD:machine direction)に、3.3gf以下であり、横方向(CD:cross direction)に、1.5gf以下である不織布が提供される。
不織布全体100重量%を基準にし、
1.0~8.0重量%の共単量体含量を有する7.0~17.0重量%のエラストマープロピレン共重合体、0.025~1.0重量%のアミド系化合物含有プロピレン重合体、及び0.375~1.0重量%のTiO2含有プロピレン重合体をブレンディングして溶融紡糸し、複数のフィラメント纎維を得る段階と、
前記複数のフィラメント纎維をコンベアベルト上で延伸して積層させ、不織布ウェブを形成する段階と、
前記積層された不織布ウェブを、145~165℃の温度で熱接着させ、前述の不織布を製造する段階と、を含む不織布の製造方法が提供される。
前述の不織布を含む物品が提供される。
前述の不織布を、バックシート(back sheet)、トップシート(top sheet)またはサイドギャザー(side gather)の材料として使用した衛生用品が提供される。
不織布全体100重量%を基準にし、ポリプロピレン重合体86.5重量%、1.0重量%のTiO2含有プロピレン重合体を押出機に投入し、混錬機で均質にブレンディングした。さらには、12重量%のエチレン・プロピレンランダム共重合体(エチレン含量:1.8重量%)、及び0.5重量%の脂肪酸アミド化合物含有プロピレン重合体を押出機に投入し、前記混錬機で均質にブレンディングし、ブレンディング組成物を製造した。前記ブレンディング組成物を、ノズルを介して溶融紡糸することにより、約1.75デニール太の複数のフィラメント纎維を得た。
前記4層に積層された不織布ウェブを、148℃温度のエンブロールと、152℃温度のスイミングロールとの間の代わりに、152℃温度のエンブロールと、156℃温度のスイミングロールとの間を通過させながら熱接着させたことを除いては、実施例1と同一方法を遂行し、積層型スパンボンド不織布を製造した。
前記4層に積層された不織布ウェブを、148℃温度のエンブロールと、152℃温度のスイミングロールとの間の代わりに、156℃温度のエンブロールと、160℃温度のスイミングロールとの間を通過させながら熱接着させたことを除いては、実施例1と同一方法を遂行し、積層型スパンボンド不織布を製造した。
前記複数のフィラメント纎維を、4,200Paのキャビン圧力に設定した条件の代わりに、3,700Paのキャビン圧力に設定した条件下で、多孔性コンベアベルト上で延伸して4層に積層し、不織布ウェブを形成したことを除いては、実施例1と同一方法を遂行し、積層型スパンボンド不織布を製造した。
前記複数のフィラメント纎維を、4,200Paのキャビン圧力に設定した条件の代わりに、3,200Paのキャビン圧力に設定した条件下で、多孔性コンベアベルト上で延伸して4層に積層し、不織布ウェブを形成したことを除いては、実施例1と同一方法を遂行し、積層型スパンボンド不織布を製造した。
不織布全体100重量%を基準にし、ポリプロピレン重合体87.35重量%、0.15重量%のTiO2含有プロピレン重合体を押出機に投入し、混錬機で均質にブレンディングした。さらには、12重量%のエチレン・プロピレンランダム共重合体(エチレン含量:1.8重量%)、及び0.5重量%の脂肪酸アミド化合物含有プロピレン重合体を押出機に投入し、前記混錬機で均質にブレンディングし、ブレンディング組成物を製造した。前記ブレンディング組成物を、ノズルを介して溶融紡糸することにより、約1.75デニール太の複数のフィラメント纎維を得た。
実施例1~5及び比較例1によって製造された積層型スパンボンド不織布の物性を、次のような方法で評価した。その結果を下記[表1]に示した。
(2)ストリップ引っ張り強度(@MD方向&@CD方向):WSP 110.4
(3)ハンドル・オ・メーター(HOM;@MD方向&@CD方向):WSP 90.3
(4)均一度:不織布の裏に黒紙を接触させたとき、前記不織布前面で観察される不織布全体面積を基準にした黒色が占める面積;肉眼評価
Claims (15)
- 不織布であり、
前記不織布全体100重量%を基準にし、
1.0~8.0重量%の共単量体含量を有する7.0~17.0重量%のエラストマープロピレン共重合体と、
0.025~1.0重量%のアミド系化合物と、
0.375~1.0重量%のTiO2と、
残量のプロピレンホモ重合体と、を含む溶融紡糸フィラメント纎維集合体であり、
前記不織布の坪量が15~30gsmであるとき、前記不織布のハンドル・オ・メーター(HOM)測定値が、縦方向(MD)に、3.3gf以下であり、横方向(CD)に、1.5gf以下である、不織布。 - 前記不織布の坪量が15~25gsmである、請求項1に記載の不織布。
- 前記共単量体がエチレンである、請求項1に記載の不織布。
- 第1項において、
前記エラストマープロピレン共重合体がエラストマープロピレンランダム共重合体である、請求項1に記載の不織布。 - 前記不織布が2層以上のスパンボンド不織布を含む、請求項1に記載の不織布。
- 前記不織布が、スパンボンド不織布/スパンボンド不織布、スパンボンド不織布/スパンボンド不織布/スパンボンド不織布、スパンボンド不織布/メルトブローン不織布/スパンボンド不織布、スパンボンド不織布/スパンボンド不織布/スパンボンド不織布/スパンボンド不織布、またはそれら組み合わせを含む、請求項1に記載の不織布。
- 前記不織布の坪量が15~30gsmであるとき、前記不織布のストリップ引っ張り強度が、縦方向(MD)に、39N/5cm以下であり、横方向(CD)に、17N/5cm以下である、請求項1に記載の不織布。
- 不織布全体100重量%を基準にし、
1.0~8.0重量%の共単量体含量を有する7.0~17.0重量%のエラストマープロピレン共重合体、0.025~1.0重量%のアミド系化合物含有プロピレン重合体、及び0.375~1.0重量%のTiO2含有プロピレン重合体をブレンディングし、溶融紡糸し、複数のフィラメント纎維を得る段階と、
前記複数のフィラメント纎維をコンベアベルト上で延伸して積層させ、不織布ウェブを形成する段階と、
前記積層された不織布ウェブを、145~165℃の温度で熱接着させ、請求項1に記載の不織布を製造する段階と、を含む、不織布の製造方法。 - 前記共単量体がエチレンである、請求項8に記載の不織布の製造方法。
- 前記エラストマープロピレン共重合体が、エラストマープロピレンランダム共重合体である、請求項8に記載の不織布の製造方法。
- 前記不織布ウェブを形成する段階において、前記複数のフィラメント纎維をコンベアベルト上で、3,000~4,200Paの圧力で延伸する工程を含む、請求項8に記載の不織布の製造方法。
- 前記不織布ウェブを形成する段階において、前記複数のフィラメント纎維をコンベアベルト上で、2層以上積層する工程を含む、請求項8に記載の不織布の製造方法。
- 前記不織布の坪量が15~30gsmであるとき、前記不織布のストリップ引っ張り強度が、縦強度が縦方向(MD)に、39N/5cm以下であり、横方向(CD)に、17N/5cm以下である、請求項8に記載の不織布の製造方法。
- 請求項1に記載の不織布を含む、物品。
- 請求項1に記載の不織布を、バックシート、トップシートまたはサイドギャザーの材料として使用した、衛生用品。