JP6960336B2 - 研磨用組成物 - Google Patents
研磨用組成物 Download PDFInfo
- Publication number
- JP6960336B2 JP6960336B2 JP2017545787A JP2017545787A JP6960336B2 JP 6960336 B2 JP6960336 B2 JP 6960336B2 JP 2017545787 A JP2017545787 A JP 2017545787A JP 2017545787 A JP2017545787 A JP 2017545787A JP 6960336 B2 JP6960336 B2 JP 6960336B2
- Authority
- JP
- Japan
- Prior art keywords
- polishing composition
- polishing
- abrasive grains
- average particle
- polyhydric alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
実施例1〜実施例27、及び比較例1〜比較例8の研磨用組成物の組成について説明する。なお、各研磨用組成物の組成を表1〜表6にも示す。表1〜表6において、各成分の重量%は、研磨用組成物(原液)全体に対する重量%を表す。
研磨装置(SPP800S、岡本工作機械製作所製)を用い、研磨パッド(SUPREME(登録商標) RN−H、ニッタ・ハース株式会社製)に、31倍に希釈された実施例1〜実施例27及び比較例1〜比較例8の研磨用組成物を1000mL/分の割合で供給して、4分間、シリコンウェーハの研磨を行った。用いたシリコンウェーハは、直径が300mmのP型半導体のものであり、結晶方位が(100)であった。このときの研磨条件としては、シリコンウェーハにかける圧力が0.012MPa、研磨定盤の回転速度が40rpm、キャリアの回転速度が39rpmであった。
上記の実施例1〜実施例27及び比較例1〜比較例8について、ウェーハ欠陥検査・レビュー装置(レーザーテック株式会社製の「MAGICS M5640」)を用いて欠陥数の測定を行った。測定時のウェーハ欠陥検査・レビュー装置の最高感度は、D37mVに設定した。
上記の実施例1〜実施例27及び比較例1〜比較例8について、ウェーハ表面検査装置(日立エンジニアリング社製の「LS6600」)を用いて、ヘイズ値の測定を行った。
上記の実施例1〜実施例27及び比較例1〜比較例8について、動的光散乱法を用いて、研磨用組成物を測定対象物として、研磨用組成物中の粒子の平均粒子径の測定を行った。測定には、大塚電子株式会社製の粒径測定システム「ELS−Z2」を用いた。
研磨用組成物が砥粒、アルカリ化合物及び変性PVAを含む実施例1及び比較例1を比較すると、配合する砥粒の径が小さい(平均粒子径:50nm)実施例1は、砥粒の径が大きい(平均粒子径:70nm)比較例1よりも、シリコンウェーハの欠陥数及びヘイズ値が著しく良好となることが分かる。
Claims (5)
- 請求項1に記載の研磨用組成物において、
さらに、非イオン性界面活性剤を含む、研磨用組成物。 - 請求項1〜請求項3のいずれか一項に記載の研磨用組成物において、
さらに、多価アルコールを含む、研磨用組成物。 - 請求項4に記載の研磨用組成物において、
前記多価アルコールは、メチルグルコシドのアルキレンオキシド誘導体である、研磨用組成物。