JP6922720B2 - 耐汚染性付与剤、コーティング剤、及び物品 - Google Patents
耐汚染性付与剤、コーティング剤、及び物品 Download PDFInfo
- Publication number
- JP6922720B2 JP6922720B2 JP2017245029A JP2017245029A JP6922720B2 JP 6922720 B2 JP6922720 B2 JP 6922720B2 JP 2017245029 A JP2017245029 A JP 2017245029A JP 2017245029 A JP2017245029 A JP 2017245029A JP 6922720 B2 JP6922720 B2 JP 6922720B2
- Authority
- JP
- Japan
- Prior art keywords
- mass
- parts
- group
- stain resistance
- polysiloxane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
FOXの式:1/Tg=W1/Tg1+W2/Tg2+・・・
(Tg:求めるべきガラス転移温度、W1:成分1の重量分率、Tg1:成分1のホモポリマーのガラス転移温度)
測定装置:高速GPC装置(東ソー株式会社製「HLC−8220GPC」)
カラム:東ソー株式会社製の下記のカラムを直列に接続して使用した。
「TSKgel G5000」(7.8mmI.D.×30cm)×1本
「TSKgel G4000」(7.8mmI.D.×30cm)×1本
「TSKgel G3000」(7.8mmI.D.×30cm)×1本
「TSKgel G2000」(7.8mmI.D.×30cm)×1本
検出器:RI(示差屈折計)
カラム温度:40℃
溶離液:テトラヒドロフラン(THF)
流速:1.0mL/分
注入量:100μL(試料濃度4mg/mLのテトラヒドロフラン溶液)
標準試料:下記の単分散ポリスチレンを用いて検量線を作成した。
東ソー株式会社製「TSKgel 標準ポリスチレン A−500」
東ソー株式会社製「TSKgel 標準ポリスチレン A−1000」
東ソー株式会社製「TSKgel 標準ポリスチレン A−2500」
東ソー株式会社製「TSKgel 標準ポリスチレン A−5000」
東ソー株式会社製「TSKgel 標準ポリスチレン F−1」
東ソー株式会社製「TSKgel 標準ポリスチレン F−2」
東ソー株式会社製「TSKgel 標準ポリスチレン F−4」
東ソー株式会社製「TSKgel 標準ポリスチレン F−10」
東ソー株式会社製「TSKgel 標準ポリスチレン F−20」
東ソー株式会社製「TSKgel 標準ポリスチレン F−40」
東ソー株式会社製「TSKgel 標準ポリスチレン F−80」
東ソー株式会社製「TSKgel 標準ポリスチレン F−128」
東ソー株式会社製「TSKgel 標準ポリスチレン F−288」
東ソー株式会社製「TSKgel 標準ポリスチレン F−550」
攪拌機、温度計、滴下ロート、冷却管及び窒素ガス導入口を備えた反応容器に、メチルトリメトキシシラン(以下、「MTMS」と略記する。)1,421質量部を仕込んで、60℃まで昇温した。次いで、前記反応容器中にiso−プロピルアシッドホスフェート(SC有機化学株式会社製「Phoslex A−3」)0.17質量部と脱イオン水207質量部との混合物を5分間で滴下した後、80℃の温度で4時間撹拌して加水分解縮合反応させた。
上記の加水分解縮合反応によって得られた縮合物を、温度40〜60℃及び40〜1.3kPaの減圧下(メタノールの留去開始時の減圧条件が40kPaで、最終的に1.3kPaとなるまで減圧する条件をいう。以下、同様。)で蒸留し前記反応過程で生成したメタノール及び水を除去することによって、数平均分子量1,000のMTMSの縮合物(a1’−1)を含有する液(有効成分70質量%)1,000質量部を得た。
なお、前記有効成分とは、MTMS等のシランモノマーのメトキシ基が全て縮合反応した場合の理論収量(質量部)を、縮合反応後の実収量(質量部)で除した値〔シランモノマーのメトキシ基が全て縮合反応した場合の理論収量(質量部)/縮合反応後の実収量(質量部)〕により算出したものである。
攪拌機、温度計、滴下ロート、冷却管及び窒素ガス導入口を備えた反応容器に、n−ブタノール(以下、「BuOH」と略記する。)150質量部、フェニルトリメトキシシラン(以下、「PTMS」と略記する。)88質量部、ジメチルジメトキシシラン(以下、「DMDMS」と略記する。)233質量部を仕込んで80℃まで昇温した。
次いで、同温度でメチルメタクリレート(以下、「MMA」と略記する。)84質量部、ブチルメタクリレート(以下、「BMA」と略記する。)16質量部、ブチルアクリレート(以下、「BA」と略記する。)13質量部、3−メタクリルオキシプロピルトリメトキシシラン(以下、「MPTS」と略記する。)7質量部、BuOH12質量部及びtert−ブチルパーオキシ−2−エチルヘキサノエート(以下、「TBPEH」と略記する。)2.4質量部を含有する混合物を、前記反応容器中へ4時間で滴下し、滴下終了後、更に同温度で20時間反応させて加水分解性シリル基を有する数平均分子量が10,200のビニル重合体(a2−1)の有機溶剤溶液を得た。
次いで、iso−プロピルアシッドホスフェート(SC有機化学株式会社製「Phoslex A−3」、以下「A−3」と略記する。)0.04質量部と脱イオン水94質量部との混合物を、5分間で滴下し、更に同温度で10時間攪拌して加水分解縮合反応させることで、ビニル重合体(a2−1)の有する加水分解性シリル基と、前記PTMS及びDMDMS由来のポリシロキサンの有する加水分解性シリル基及びシラノール基とが結合した複合樹脂を含有する液を得た。
次いで、この液に合成例1で得られたMTMSの縮合物(a1’−1)398質量部、脱イオン水 67質量部を添加し、同温度で10時間攪拌して加水分解縮合反応させたものを、合成例1と同様の条件で蒸留することによって生成したメタノール及び水を除去し、次いで、BuOH 250質量部を添加し、不揮発分が60.1質量%の耐汚染性付与剤(1)を1,000質量部得た。
攪拌機、温度計、滴下ロート、冷却管及び窒素ガス導入口を備えた反応容器に、BuOH 150質量部、PTMS 99質量部、DMDMS 263質量部を仕込んで80℃まで昇温した。
次いで、同温度でMMA 42質量部、BMA 8質量部、BA 7質量部、MPTS 4質量部、BuOH 6質量部及びTBPEH 1.2質量部を含有する混合物を、前記反応容器中へ5時間で滴下し、滴下終了後、更に同温度で20時間反応させて加水分解性シリル基を有する数平均分子量が10,300のビニル重合体(a2−2)の有機溶剤溶液を得た。
次いで、A−3 0.04質量部と脱イオン水 106質量部との混合物を、5分間で滴下し、更に同温度で10時間攪拌して加水分解縮合反応させることで、ビニル重合体(a2−2)の有する加水分解性シリル基と、前記PTMS及びDMDMS由来のポリシロキサンの有する加水分解性シリル基及びシラノール基とが結合した複合樹脂を含有する液を得た。
次いで、この液に合成例1で得られたMTMSの縮合物(a1’−1)447質量部、脱イオン水 76質量部を添加し、同温度で10時間攪拌して加水分解縮合反応させたものを、合成例1と同様の条件で蒸留することによって生成したメタノール及び水を除去し、次いで、BuOH 250質量部を添加し、不揮発分が60.0質量%の耐汚染性付与剤(2)を1,000質量部得た。
攪拌機、温度計、滴下ロート、冷却管及び窒素ガス導入口を備えた反応容器に、BuOH 150質量部、PTMS 105質量部、DMDMS 277質量部を仕込んで80℃まで昇温した。
次いで、同温度でMMA 21質量部、BMA 4質量部、BA 3質量部、MPTS 2質量部、BuOH 3質量部及びTBPEH 0.6質量部を含有する混合物を、前記反応容器中へ6時間で滴下し、滴下終了後、更に同温度で20時間反応させて加水分解性シリル基を有する数平均分子量が10,000のビニル重合体(a2−3)の有機溶剤溶液を得た。
次いで、A−3 0.04質量部と脱イオン水 112質量部との混合物を、5分間で滴下し、更に同温度で10時間攪拌して加水分解縮合反応させることで、ビニル重合体(a2−3)の有する加水分解性シリル基と、前記PTMS及びDMDMS由来のポリシロキサンの有する加水分解性シリル基及びシラノール基とが結合した複合樹脂を含有する液を得た。
次いで、この液に合成例1で得られたMTMSの縮合物(a1’−1)472質量部、脱イオン水 80質量部を添加し、同温度で10時間攪拌して加水分解縮合反応させたものを、合成例1と同様の条件で蒸留することによって生成したメタノール及び水を除去し、次いで、BuOH 250質量部を添加し、不揮発分が60.1質量%の耐汚染性付与剤(3)を1,000質量部得た。
攪拌機、温度計、滴下ロート、冷却管及び窒素ガス導入口を備えた反応容器に、BuOH 150質量部、PTMS 108質量部、DMDMS 286質量部を仕込んで80℃まで昇温した。
次いで、同温度でMMA 8質量部、BMA 2質量部、BA 1質量部、MPTS 1質量部、BuOH 2質量部及びTBPEH 0.3質量部を含有する混合物を、前記反応容器中へ6時間で滴下し、滴下終了後、更に同温度で20時間反応させて加水分解性シリル基を有する数平均分子量が10,300のビニル重合体(a2−4)の有機溶剤溶液を得た。
次いで、A−3 0.05質量部と脱イオン水 115質量部との混合物を、5分間で滴下し、更に同温度で10時間攪拌して加水分解縮合反応させることで、ビニル重合体(a2−4)の有する加水分解性シリル基と、前記PTMS及びDMDMS由来のポリシロキサンの有する加水分解性シリル基及びシラノール基とが結合した複合樹脂を含有する液を得た。
次いで、この液に合成例1で得られたMTMSの縮合物(a1’−1)487質量部、脱イオン水 82質量部を添加し、同温度で10時間攪拌して加水分解縮合反応させたものを、合成例1と同様の条件で蒸留することによって生成したメタノール及び水を除去し、次いで、BuOH 250質量部を添加し、不揮発分が60.2質量%の耐汚染性付与剤(4)を1,000質量部得た。
実施例2で使用した、MMA 42質量部、BMA 8質量部、BA 7質量部、MPTS 4質量部、BuOH 6質量部及びTBPEH 1.2質量部を含有する混合物の代わりに、MMA 18質量部、BMA 14質量部、BA 7質量部、アクリル酸(以下、「AA」と略記する。)1質量部、MPTS 2質量部、BuOH 6質量部及びTBPEH 0.9質量部を含有する混合物を使用した以外は、実施例2と同様の操作を行い、不揮発分が60.0%の耐汚染性付与剤(5)を1,000質量部得た。
実施例2で使用した、MMA 42質量部、BMA 8質量部、BA 7質量部、MPTS 4質量部、BuOH 6質量部及びTBPEH 1.2質量部を含有する混合物の代わりに、MMA 12質量部、シクロヘキシルメタクリレート 15質量部、2−エチルヘキシルアクリレート 32質量部、MPTS 1質量部、BuOH 6質量部及びTBPEH 0.6質量部を含有する混合物を使用した以外は、実施例2と同様の操作を行ない、不揮発分が60.2%の耐汚染性付与剤(6)を1,000質量部得た。
攪拌機、温度計、滴下ロート、冷却管及び窒素ガス導入口を備えた反応容器に、BuOH 150質量部、ジフェニルジメトキシシラン(以下、「DPDMS」と略記する。)133質量部、DMDMS 350質量部を仕込んで80℃まで昇温した。
次いで、同温度でMMA 18質量部、BMA 14質量部、BA 7質量部、AA 1質量部、MPTS 2質量部、BuOH 6質量部及びTBPEH 0.9質量部を含有する混合物を、前記反応容器中へ5時間で滴下し、滴下終了後、更に同温度で10時間反応させて加水分解性シリル基を有する数平均分子量が20,000のビニル重合体(a2−7)の有機溶剤溶液を得た。
次いで、A−3 0.05質量部と脱イオン水 134質量部との混合物を、5分間で滴下し、更に同温度で10時間攪拌して加水分解縮合反応させることで、ビニル重合体(a2−7)の有する加水分解性シリル基と、前記DPDMS及びDMDMS由来のポリシロキサンの有する加水分解性シリル基及びシラノール基とが結合した複合樹脂を含有する液を得た。
次いで、この液に合成例1で得られたMTMSの縮合物(a1’−1)309質量部、脱イオン水 52質量部を添加し、同温度で15時間攪拌して加水分解縮合反応させたものを、合成例1と同様の条件で蒸留することによって生成したメタノール及び水を除去し、次いで、BuOH 250質量部を添加し、不揮発分が60.0質量%の耐汚染性付与剤(7)を1,000質量部得た。
攪拌機、温度計、滴下ロート、冷却管及び窒素ガス導入口を備えた反応容器に、BuOH 150質量部、PTMS 249質量部、DMDMS 263質量部を仕込んで80℃まで昇温した。
次いで、同温度でMMA 18質量部、BMA 14質量部、BA 7質量部、AA 1質量部、MPTS 2質量部、BuOH 6質量部及びTBPEH 0.9質量部を含有する混合物を、前記反応容器中へ5時間で滴下し、滴下終了後、更に同温度で10時間反応させて加水分解性シリル基を有する数平均分子量が20,100のビニル重合体(a2−8)の有機溶剤溶液を得た。
次いで、A−3 0.05質量部と脱イオン水 147質量部との混合物を、5分間で滴下し、更に同温度で10時間攪拌して加水分解縮合反応させることで、ビニル重合体(a2−8)の有する加水分解性シリル基と、前記PTMS及びDMDMS由来のポリシロキサンの有する加水分解性シリル基及びシラノール基とが結合した複合樹脂を含有する液を得た。
次いで、この液に3−グリシドキシプロピルトリメトキシシラン 76質量部、合成例1で得られたMTMSの縮合物(a1’−1)231質量部、脱イオン水 56質量部を添加し、同温度で15時間攪拌して加水分解縮合反応させたものを、合成例1と同様の条件で蒸留することによって生成したメタノール及び水を除去し、次いで、BuOH 250質量部を添加し、不揮発分が60.0質量%の耐汚染性付与剤(8)を1,000質量部得た。
攪拌機、温度計、滴下ロート、冷却管及び窒素ガス導入口を備えた反応容器に、BuOH 150質量部、PTMS 414質量部、DMDMS 263質量部を仕込んで80℃まで昇温した。
次いで、同温度でMMA 18質量部、BMA 14質量部、BA 7質量部、AA 1質量部、MPTS 2質量部、BuOH 6質量部及びTBPEH 0.9質量部を含有する混合物を、前記反応容器中へ6時間で滴下し、滴下終了後、更に同温度で10時間反応させて加水分解性シリル基を有する数平均分子量が19,600のビニル重合体(a2−9)の有機溶剤溶液を得た。
次いで、A−3 0.07質量部と脱イオン水 192質量部との混合物を、5分間で滴下し、更に同温度で10時間攪拌して加水分解縮合反応させることで、ビニル重合体(a2−9)の有する加水分解性シリル基と、前記PTMS及びDMDMS由来のポリシロキサンの有する加水分解性シリル基及びシラノール基とが結合した複合樹脂を含有する液を得た。
次いで、この液に合成例1で得られたMTMSの縮合物(a1’−1)154質量部、脱イオン水 26質量部を添加し、同温度で5時間攪拌して加水分解縮合反応させたものを、合成例1と同様の条件で蒸留することによって生成したメタノール及び水を除去し、次いで、BuOH 250質量部を添加し、不揮発分が60.1質量%の耐汚染性付与剤(9)を1,000質量部得た。
攪拌機、温度計、滴下ロート、冷却管及び窒素ガス導入口を備えた反応容器に、BuOH 150質量部、PTMS 33質量部、DMDMS 88質量部を仕込んで80℃まで昇温した。
次いで、同温度でMMA 294質量部、BMA 55質量部、BA 46質量部、MPTS 25質量部、BuOH 42質量部及びTBPEH 8.4質量部を含有する混合物を、前記反応容器中へ3時間で滴下し、滴下終了後、更に同温度で20時間反応させて加水分解性シリル基を有する数平均分子量が11,000のビニル重合体(Ra2−1)の有機溶剤溶液を得た。
次いで、A−3 0.01質量部と脱イオン水 35質量部との混合物を、5分間で滴下し、更に同温度で10時間攪拌して加水分解縮合反応させることで、ビニル重合体(Ra2−1)の有する加水分解性シリル基と、前記PTMS及びDMDMS由来のポリシロキサンの有する加水分解性シリル基及びシラノール基とが結合した複合樹脂を含有する液を得た。
次いで、この液に合成例1で得られたMTMSの縮合物(a1’−1)149質量部、脱イオン水 25質量部を添加し、同温度で10時間攪拌して加水分解縮合反応させたものを、合成例1と同様の条件で蒸留することによって生成したメタノール及び水を除去し、次いで、BuOH 250質量部を添加し、不揮発分が60.0質量%の比較用樹脂組成物(R1)を1,000質量部得た。
攪拌機、温度計、滴下ロート、冷却管及び窒素ガス導入口を備えた反応容器に、BuOH 150質量部、PTMS 66質量部、DMDMS 175質量部を仕込んで80℃まで昇温した。
次いで、同温度でMMA 168質量部、BMA 31質量部、BA 26質量部、MPTS 14質量部、BuOH 24質量部及びTBPEH 4.8質量部を含有する混合物を、前記反応容器中へ4時間で滴下し、滴下終了後、更に同温度で20時間反応させて加水分解性シリル基を有する数平均分子量が10,200のビニル重合体(Ra2−2)の有機溶剤溶液を得た。
次いで、A−3 0.03質量部と脱イオン水 70質量部との混合物を、5分間で滴下し、更に同温度で10時間攪拌して加水分解縮合反応させることで、ビニル重合体(Ra2−2)の有する加水分解性シリル基と、前記PTMS及びDMDMS由来のポリシロキサンの有する加水分解性シリル基及びシラノール基とが結合した複合樹脂を含有する液を得た。
次いで、この液に合成例1で得られたMTMSの縮合物(a1’−1)298質量部、脱イオン水 50質量部を添加し、同温度で10時間攪拌して加水分解縮合反応させたものを、合成例1と同様の条件で蒸留することによって生成したメタノール及び水を除去し、次いで、BuOH 250質量部を添加し、不揮発分が60.0質量%の比較用樹脂組成物(R2)の溶液1,000質量部を得た。
攪拌機、温度計、滴下ロート、冷却管及び窒素ガス導入口を備えた反応容器に、BuOH 150質量部、PTMS 111質量部、DMDMS 292質量部を仕込んで80℃まで昇温した。
次いで、同温度でA−3 0.05質量部と脱イオン水 118質量部との混合物を、5分間で滴下し、更に同温度で10時間攪拌して加水分解縮合反応させることで、前記PTMS及びDMDMS由来のポリシロキサンを含有する液を得た。
次いで、この液に合成例1で得られたMTMSの縮合物(a1’−1)497質量部、脱イオン水 84質量部を添加し、同温度で10時間攪拌して加水分解縮合反応させたものを、合成例1と同様の条件で蒸留することによって生成したメタノール及び水を除去し、次いで、BuOH 250質量部を添加し、不揮発分が60.0質量%の比較用樹脂組成物(R3)の溶液1,000質量部を得た。
攪拌機、温度計、滴下ロート、冷却管及び窒素ガス導入口を備えた反応容器に、BuOH 150質量部、PTMS 41質量部、DMDMS 263質量部を仕込んで80℃まで昇温した。
次いで、同温度でMMA 42質量部、BMA 8質量部、BA 7質量部、MPTS 4質量部、BuOH 6質量部及びTBPEH 1.2質量部を含有する混合物を、前記反応容器中へ5時間で滴下し、滴下終了後、更に同温度で20時間反応させて加水分解性シリル基を有する数平均分子量が10,400のビニル重合体(Ra2−4)の有機溶剤溶液を得た。
次いで、A−3 0.04質量部と脱イオン水 90質量部との混合物を、5分間で滴下し、更に同温度で10時間攪拌して加水分解縮合反応させることで、ビニル重合体(Ra2−4)の有する加水分解性シリル基と、前記PTMS及びDMDMS由来のポリシロキサンの有する加水分解性シリル基及びシラノール基とが結合した複合樹脂を含有する液を得た。
次いで、この液に合成例1で得られたMTMSの縮合物(a1’−1)501質量部、脱イオン水 85質量部を添加し、同温度で10時間攪拌して加水分解縮合反応させたものを、合成例1と同様の条件で蒸留することによって生成したメタノール及び水を除去し、次いで、BuOH 250質量部を添加し、不揮発分が60.0質量%の比較用樹脂組成物(R4)の溶液1,000質量部を得た。
攪拌機、温度計、滴下ロート、冷却管及び窒素ガス導入口を備えた反応容器に、BuOH 150質量部、PTMS 332質量部、DMDMS 350質量部を仕込んで80℃まで昇温した。
次いで、同温度でMMA 42質量部、BMA 8質量部、BA 7質量部、MPTS 4質量部、BuOH 6質量部及びTBPEH 1.2質量部を含有する混合物を、前記反応容器中へ6時間で滴下し、滴下終了後、更に同温度で20時間反応させて加水分解性シリル基を有する数平均分子量が10,000のビニル重合体(Ra2−5)の有機溶剤溶液を得た。
次いで、A−3 0.07質量部と脱イオン水 195質量部との混合物を、5分間で滴下し、更に同温度で10時間攪拌して加水分解縮合反応させることで、ビニル重合体(Ra2−5)の有する加水分解性シリル基と、前記PTMS及びDMDMS由来のポリシロキサンの有する加水分解性シリル基及びシラノール基とが結合した複合樹脂を含有する液を得た。
次いで、この液に3−グリシドキシプロピルトリメトキシシラン 153質量部、脱イオン水 35質量部を添加し、同温度で10時間攪拌して加水分解縮合反応させたものを、合成例1と同様の条件で蒸留することによって生成したメタノール及び水を除去し、次いで、BuOH 250質量部を添加し、不揮発分が60.0質量%の比較用樹脂組成物(R5)の溶液1,000質量部を得た。
攪拌機、温度計、滴下ロート、冷却管及び窒素ガス導入口を備えた反応容器に、BuOH 690質量部を仕込んで80℃まで昇温した。
次いで、同温度でMMA 193質量部、BMA 36質量部、BA 30質量部、MPTS 17質量部、BuOH 28質量部及びTBPEH 5.5質量部を含有する混合物を、前記反応容器中へ3時間で滴下し、滴下終了後、更に同温度で20時間反応させて数平均分子量が10,300のビニル重合体(Ra2−6)の有機溶剤溶液を得た。
次いで、比較例3で得た比較用樹脂組成物(R3)808質量部と不揮発分が28.0質量%のビニル重合体(Ra2−6)の有機溶剤溶液 192質量部とを混合し、同温度で1時間攪拌することで不揮発分が53.8質量%の比較用樹脂組成物(R6)の溶液1,000質量部を得た。
上記で得られた耐汚染性付与剤及び比較用樹脂組成物の保存安定性を、50℃において、30日間保存したものの粘度(いわゆる経時粘度)を分子とし、初期粘度を分母とする粘度比で評価した。粘度測定は、E型粘度計(東京計器株式会社製)を用いて25℃にて行った。また、サンプルの保存は、得られた硬化性樹脂組成物をガラス製チュ−ブに入れて、50℃の環境下で30日間静置せしめることによって行った。この粘度比が1に近い値であるほど、保存安定性が優れているということを意味しており、粘度比が0.9以上1.1以下で保存安定性が非常に優れている樹脂であるものと判定した。
水性樹脂(1)(DIC株式会社製「バーノックWD−551」、アクリル系水性樹脂)100質量部、硬化剤(1)(DIC株式会社製「バーノックDNW−5500」、ポリイソシアネート硬化剤)30質量部及び耐汚染性付与剤(1)0.5質量部を混合し、コーティング剤(1)を得た。
下記表4〜6に示す配合に変更した以外は実施例10と同様に操作することにより、コーティング剤(2)〜(15)を得た。
下記表7及び8に示す配合に変更した以外は実施例10と同様に操作することにより、コーティング剤(R1)〜(R9)を得た。
上記で得られたコーティング剤を、株式会社エンジニアリングテストサービス製のクロメート処理されたアルミ板上にアクリルポリオール・ポリイソシアネート白色塗料が塗装された塗装板を水研ぎして得られた白色塗板上に、硬化塗膜の膜厚が30μmとなるように塗装し、23℃の環境下で1週間乾燥させて評価用クリア硬化塗膜を得た。
上記で得られた硬化塗膜の初期状態目視で観察し、下記の基準で塗膜外観を評価した。
○:ブツ等の異物や白化の発生が認められない。
△:若干のブツ等の異物や白化の発生が認められる。
×:著しいブツ等の異物や白化の発生が認められる。
上記で得られた硬化塗膜を、大阪府高石市のDIC株式会社堺工場内において1ヶ月間、3ヶ月間、6ヶ月間の曝露試験を行った。
ここで、曝露試験後の未洗浄の試験塗膜と、曝露試験前の試験塗膜との色差(ΔE)を、コニカミノルタセンシング株式会社製の「CM−3500d」を用いて評価した。前記色差(ΔE)が小さいほど、耐汚染性が良好であることを示す。
水性樹脂(1):DIC株式会社製「バーノックWD−551」、アクリル系水性樹脂
水性樹脂(2):DIC株式会社製「セラネートWSA−1070」、ポリシロキサンアクリル複合系水性樹脂
水性樹脂(3):DIC株式会社製「ハイドランWLS−210」、ウレタン系水性樹脂
硬化剤(1):DIC株式会社製「バーノックDNW−5500」、水分散性ポリイソシアネート硬化剤
硬化剤(2):DIC株式会社製「ウォーターゾールWSA−950」、加水分解性シリル基含有硬化剤
Claims (5)
- 一般式(1)又は(2)で表される構造単位(U1)、及び一般式(3)で表される構造単位(U2)を有するポリシロキサン(a1)と重合体(a2)とが一般式(4)で表される結合により結合した複合樹脂(A)が、媒体中に溶解又は分散している耐汚染性付与剤であって、前記複合樹脂(A)中の前記ポリシロキサン(a1)が75〜99質量%であり、前記ポリシロキサン(a1)中の前記構造単位(U1)が10〜55質量%であることを特徴とする耐汚染性付与剤。
- 前記構造単位(U1)が、フェニルトリメトキシシランまたはジフェニルジメトキシシラン由来の構造単位である請求項1記載の耐汚染性付与剤。
- 請求項1又は2記載の耐汚染性付与剤を含有することを特徴とするコーティング剤。
- 水性樹脂を含有する請求項3記載のコーティング剤。
- 請求項3又は4記載のコーティング剤の塗膜を有することを特徴とする物品。